JP2002052899A - Surface decorated fitting of every kind and surface decorating processing method - Google Patents

Abstract

PROBLEM TO BE SOLVED: To form a uniform and stable picture pattern/character pattern/mark pattern to a fitting of every kind made of a metal without damaging an aesthetic feeling and a value feeling as surface decoration. SOLUTION: A substrate treatment process is constituted of a grinding process for applying under-grinding processing to the surface of a fitting base material (1) of every kind, a first washing process for washing the surface after grinding, a quality inspection process for inspecting quality after grinding and a second washing process for washing the surface after the surface finish processing due to the mirror surface processing to the surface after quality inspection. In addition to the substrate treatment process, a surface decorating processing process is constituted of a plating treatment process, a forming treatment process, a plating layer peeling process, a peel liquid washing process, a drying process and a washing process. In the forming treatment process, a film member 2 (mask part 4) having the shape corresponding to a pattern part 3 is bonded to the surface of a plating layer in the fitting base material (1) of every kind and, after bonding, sand blasting processing (Q) is applied to peel the plating layer M other than the mask part 4 and the residual part is formed as the pattern part 3.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0001]

BACKGROUND OF THE INVENTION The present invention is used for handrails in washrooms, toilets, bathrooms, etc., for water supplies such as bathroom tubs, kitchen faucets, etc., and also for outer walls, retaining walls, indoor walls, etc. of building bodies. Surface decoration characterized by applying decorative patterns on the surfaces of decorative panels, tableware, vases, containers, etc., and various internal and external equipment such as bumpers in automobiles and other various equipment. The present invention relates to various accessories provided with a surface treatment method and a surface decoration processing method.

[0002]

2. Description of the Related Art Conventionally, handrails for washrooms, toilets, bathrooms, etc.
Plumbing products, decorative boards, tableware, vases, containers, etc., as well as interior and exterior accessory equipment and other various accessories in automobiles, etc., are configured as those made of metal such as stainless steel, brass, aluminum, etc. The surface is plated to have a mirror-like shape, a hairline shape, or the like so as to prevent rust or other occurrences and to be used for a long time. However, in order to add a pattern to such a plated product, if the surface is damaged to a considerable extent, the plating process layer will be degraded and the value of a good-looking product will be reduced by half. Also. For this reason, conventionally, the surface of such a plated product has been kept in a mirror-like, hairline-like or the like after treatment, and a product having a concrete, interesting pattern is provided. It had not been done.

[0003]

For these reasons, for example, a picture pattern, a character pattern,
If surface decorations such as symbol patterns are to be applied, it is conceivable to first apply a plating member on the surface of the various materials of the equipment and then stick a seal member printed with a pattern pattern, character pattern, symbol pattern, etc. on a part. Can be However, in the case of using such a seal member, the seal member is turned up from the surface of the various equipment and is easily peeled off due to repetition of moisture and drying, so that the surface decoration as a picture pattern, a character pattern, a symbol pattern, etc. There is a problem that the beauty and value are impaired.

Accordingly, the present invention has been made in view of the above-mentioned various circumstances, and includes, for example, a toilet, a toilet,
Handrails such as bathrooms, bathtubs in bathrooms, water supplies such as faucets in kitchens,
Furthermore, on the surface of decorative panels used for the outer wall, retaining wall, indoor wall, etc. of the frame, or the surface of tableware, vases, containers, etc., and various internal and external accessories such as bumpers in automobiles and other various equipment For example, uniform and stable patterns and characters on the surface of various materials such as stainless steel, brass, aluminum, etc. -It is an object of the present invention to provide various accessories having a surface decoration capable of forming a symbol pattern and the like and a surface decoration processing method thereof.

[0005]

Means for Solving the Problems To solve the above-mentioned problems, various kinds of equipment having a surface decoration according to the present invention include: The plating, M, and symbol patterns are removed by sandblasting or peeling off the plating layer M around the mask portion 4 while leaving the mask portion 4 in the shape of the provided pattern, character, symbol, etc. The pattern portion 3 is formed by the plating layer M having the remaining contour such as. The pattern portion 3 can be formed by a mask portion 4 made of a film member 2 in the form of a picture pattern, a character pattern, a symbol pattern, etc. attached to the surface of various accessory material materials. On the surface of the protective plating layer 5,
Preferably, a transparent protective plating layer 5 can be formed. On the other hand, in the surface decoration processing method for various accessories provided with surface decoration according to the present invention, a base treatment step (A, B, D, E) of mirror-finishing the surface of a stainless steel base, and a rhodium plating layer or A plating step F for forming a plating layer M such as a gold plating layer, and forming a mask portion 4 in the form of a picture pattern, a character pattern, a symbol pattern, etc. on the surface of the various material materials on which the plating layer M is formed. Then, a forming process step G in which the plating layer M around the mask portion 4 is scratched to a matte state by sandblasting, and a plating layer stripping step H in which the plating layer M is stripped with a stripping solution after the forming process. And a stripping solution washing step I for removing the stripping solution, a drying step J for drying, and a washing step K for washing the surface after drying. Brass·
A base treatment step (A, B, D, E) of mirror-finish the surface of the aluminum base, a plating treatment step F of forming a nickel plating layer after forming a copper plating layer, and various types of plating layers M formed. A mask portion 4 in the form of a picture pattern, character pattern, symbol pattern, etc. is formed on the surface of the equipment material, and the plating layer M around the mask portion 4 is scratched by sandblasting to a matte state of matte. A forming step G, a cleaning step K for cleaning the forming surface, and a protective plating layer for protecting the surface of the forming surface after the cleaning, preferably a transparent protective plating layer 5.
For example, the method may include a protective plating process L for forming a chrome plating layer, a gold plating layer, and the like. Surface treatment process (A, B, D,
E) and a plating step F for forming a gold plating layer M
And forming a mask portion 4 in the form of a picture pattern, a character pattern, a symbol pattern, etc. on the surface of the various component material materials on which the plating layer M is formed, and removing the plating layer M around the mask portion 4 by a stripping solution. Layer stripping step H for stripping, stripping solution washing step I for removing the stripping agent, and drying step J for drying
And a cleaning step K for cleaning the surface after drying. The undercoating process (A, B, D, E) is a polishing process A using a lower polishing process on the surface of the various dough materials.
And a first cleaning step B for cleaning the polished surface, a surface finishing processing D by mirror finishing on the surface, and a second cleaning step E for cleaning the surface after the surface finishing. Mask part 4 in the forming process
Is formed by exfoliating the release paper 7 covering the adhesive 6 formed on one side of the film member 2 in the shape of a picture pattern, a character pattern, a symbol pattern, and the like, exposing the adhesive 6 and then performing various operations. It can be attached to the surface of the equipment material.

[0006] In the various accessories having the surface decoration according to the present invention configured as described above, the plating layer M around the mask portion 4 in the form of a picture pattern, a character pattern, a symbol pattern, etc. is sandblasted. The pattern portion 3, which is formed by being peeled off by the above, makes a picture pattern, a character pattern, a symbol pattern, and the like appear on the matte stainless steel surface. The pattern portion 3 remaining by peeling off the plating layer M around the mask portion 4 in the shape of a picture pattern, a character pattern, a symbol pattern, or the like with a peeling liquid is provided on the glossy stainless steel surface. Make patterns and sign patterns appear. The film member 2 is
The contours of picture patterns, character patterns, symbol patterns, and the like by the plating layer M as the pattern portion 3 are clearly expressed. The protective plating layer 5 formed on the surface after the formation of the pattern portion 3 protects the entire matte stainless surface including the pattern portion 3. On the other hand, in the surface decoration processing method of various equipment with surface decoration,
Undercoating process (A, B, D, E), plating process F,
The surface decoration processing method including the forming process step G, the plating layer stripping step H, the stripping solution cleaning step I, the drying step J, and the cleaning step K is performed in a uniform matte stainless steel surface through a series of these steps. Then, a pattern portion 3 such as a picture pattern, a character pattern, a symbol pattern, and the like by the plating layer M is formed on the surface of various equipment fabric materials. Base treatment process (A, B, D,
E), a plating process F, a forming process G, a cleaning process K, and a protective plating process L each include a surface decoration processing method. A pattern part 3 such as a picture pattern, a character pattern, a symbol pattern, etc. is formed on the surface of various equipment material materials.
In addition, the protective plating process L protects the surface of the various component material materials after the formation of the pattern portion 3 from rust, discoloration, cracks, and the like. The surface decoration processing method including the base treatment steps (A, B, D, and E), the plating step F, the plating layer stripping step H, the stripping solution cleaning step I, the drying step J, and the cleaning step K is a series of these processes. Through the process, the pattern portions 3 such as a picture pattern, a character pattern, and a symbol pattern appear on the glossy stainless steel surface. The undercoating process (A, B, D, E), which includes the polishing process A, the first cleaning process B, the surface finishing process D, and the second cleaning process E, involves damaging the surface of various equipment fabric materials. Process beautifully and improve product yield. The release paper 7 covering the surface of the adhesive 6 of the film member 2 forming the mask portion 4 is peeled off and released.
By exposing the surface, it can be attached to an arbitrary position on the surface of the various dough materials.

[0007]

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS An embodiment of the present invention will be described below with reference to the drawings.
Is formed from a cloth material of a hollow or solid metal bar made of, for example, stainless steel, brass, aluminum, or the like, which is attached to a wall P of a bathroom, a toilet, a bathroom, or the like, a door, or the like as a housing-related equipment. It is a handrail that was done. As shown in FIG. 1, the handrail 1 has a substantially U-shape as a whole from a long handle 1 </ b> A and short mounting legs 1 </ b> B formed by bending both ends of the handle 1 </ b> A sideways. It is formed so that it becomes. Then, for example, a film member 2 having an outline of a flower pattern is attached to the surface of the handle 1A near the mounting leg 1B, and the film member 2 is peeled off after performing a sandblasting process described below from above. On the surface of the handle portion 1A matted in a matte shape, a pattern portion 3 having an outline of a floral pattern, for example, a pattern portion 3 having a shine by a gold plating layer having a residual gold color to be described later is formed.

As shown in FIG. 2, the film member 2 is formed such that a mask portion 4 in the shape of, for example, a floral pattern is cut in an endless line shape in the plane, and the film portion 2 is formed on the surface of the handle portion 1A. A release paper 7 that can be peeled off after the adhesive 6 is applied is attached on the side of the application surface. Therefore, when attaching the film member 2 to the surface of the handle 1A, the release paper 7 is peeled from the film member 2 to expose the adhesive 6, and then the film member 2 itself is attached to the surface of the handle 1A. Wear it. In FIG. 2, although the contour is shown as simulating the contour, the contour is not limited to this, and may be, for example, a punch type.

In sand blasting, an abrasive Q such as glass beads or fine sand having a small particle size is forcibly sprayed through a nozzle or the like on the surface of a handrail 1 made of a metal bar such as stainless steel, brass or aluminum. A part of the surface of the handrail fabric itself, that is, a part other than the decorative part, which is a part excluding the pattern part 3, is a matte state of the satin finish. As a specific method of this sandblasting, there are, for example, a gravity type, a siphon type, a direct pressure type, etc. as an air method for spraying the abrasive Q using the injection energy of compressed air, and a centrifugal projection method without using compressed air, a rotary method. There is a type in which the abrasive Q supplied from the center of the impeller to be struck by centrifugal force from the outer periphery of the impeller. Further, there is a flat-hit type in which the abrasive Q is allowed to fall naturally in a wide width like a waterfall and hits and accelerates the abrasive Q using an impeller having a wide width in the middle thereof.

The shape and outline of the pattern portion 3 itself may be, for example, an outline pattern of animals, vehicles, characters, symbols, etc., in addition to the outline pattern of the floral pattern. Instead of forming the pattern, the entire surface of the pattern may be formed, and in any case, the pattern has a shine by a gold plating layer, a rhodium plating layer, or the like, which will be described later, which exhibits a gold color or the like. Further, in the present embodiment, the handrail 1 is described as a housing-related equipment, but as other housing-related equipment, for example, a handrail such as a washroom, a toilet, a bathroom, or the like.
It may be a plumbing device used for a bathtub in a bathroom, a faucet in a kitchen or the like, or an outer wall, a retaining wall, an indoor wall or the like of a frame. Further, it may be an interior or exterior accessory such as a bumper in an automobile or the like, and in any case, the material is not limited to these, and the material of the material is not limited to metal, but may be plastic or the like. It can be anything.

Next, an example of the surface decoration processing method will be described. As shown in FIG. 3, before the surface decoration processing step is performed, the following base treatment steps (A, B, C, D, E) are performed. Keep going. That is, the base treatment process (A, B, C, D,
E) First, in the polishing step A, after polishing the surface of a base material such as a stainless steel base, which is to be various accessories such as the handrail 1, by under-polishing, and then in the first cleaning step B, an ultrasonic cleaning machine And ultrasonic cleaning by immersion in a cleaning solution. Then, in the quality inspection step C, a quality inspection after polishing is performed by using a quality inspection device such as an optical microscope or by visual inspection. In the surface finishing step D, the surface after the quality inspection is subjected to mirror finishing using, for example, a buff of 800-1000 finish, etc., and in the second cleaning step E, the surface after the surface finishing is ultrasonically cleaned. And ultrasonic cleaning by immersion in a cleaning solution. As a cleaning liquid for this ultrasonic cleaning device, for example, a temperature of about 10
Use a trichlorethylene solution at about 0 ° C.

In the surface decoration processing step, first, a plating layer M such as a rhodium plating layer or a gold plating layer is formed by a plating step F using a well-known electrolytic plating tank. Then, a mask portion 4 is formed by sticking a film member 2 in the form of a picture pattern, a character pattern, a symbol pattern, or the like on the surface of the various component material materials on which the plating layer M is formed. That is, as shown in FIG.
Is formed on the surface of the film member 2, for example, and the release paper 7 is peeled off from the film member 2 to expose the adhesive 6, and then the film member 2 itself is gripped. Adhere to the surface of 1A (see FIGS. 4 (a) and 4 (b)).

In the forming step G, the plating layer M around the mask portion 4 is scratched by sandblasting to a matte state of matte. That is, an abrasive Q having a small particle size is forcibly sprayed by a nozzle or the like toward the mask portion 4 having a contour of, for example, a flower pattern of the film member 2 by a sandblasting device (not shown), and the film portion 2 is covered with the mask portion 4. After the plating layer M on the surface of the handle portion 1A except for a certain portion is made matte (see FIG. 4C), the film member 2 is removed. Therefore, on the surface of the handle portion 1A, the portion other than the portion covered with the film member 2 is matted in a matt-like shape, so that the floral pattern-shaped pattern portion 3 as shown in the mask portion 4 remains.

In the next plating layer stripping step H, first, the plating layer M is stripped by using a stripping solution in order to leave the mask portion 4 after the forming process as it is. Then, after removing the stripping agent in the stripping solution cleaning step I,
The cleaning liquid is dried and removed in the drying step J, and the mask surface 4 is removed by cleaning the dried surface in, for example, an ultrasonic wave in the cleaning step K. As a result, a two-tone product is formed by contrasting the metal plating color with the stainless steel base color in which the pattern portion 3 having the metallic luster plating layer M is formed on the matte surface.

FIGS. 5 and 6 show another embodiment of the present invention, in which a surface treatment step (A, B, C, D, E) for mirror-finishing the surface of a brass or aluminum substrate is performed. Thereafter, a copper plating layer is formed in a plating step F, and a nickel plating layer is further formed thereon. Then, in the forming processing step G, a mask portion 4 in the form of a picture pattern, a character pattern, a symbol pattern, etc. is formed on the surface of the various material base material on which the nickel plating layer is formed, and plating around the mask portion 4 is performed. The layer M is scratched by sandblasting to a matte state of matte. After the forming process, the forming process surface is cleaned by a cleaning process K using an ultrasonic cleaner or the like using a trichlorethylene solution having a temperature of about 100 ° C., for example. For example, a transparent protective plating layer 5 is preferably formed by a chrome plating layer or a gold plating layer, which preferably has a transparent thickness.

FIG. 7 shows another embodiment of the present invention, in which a plating treatment step is performed after a base treatment step (A, B, C, D, E) for mirror-finishing the surface of a stainless steel base. In F, a gold plating layer M is formed. Then, a mask portion 4 in the form of a picture pattern, a character pattern, a symbol pattern, or the like is formed on the surface of the various material base materials on which the plating layer M is formed. The surface of the stainless steel base is exposed by immersing the plating layer M in a release agent solution containing a release agent, or by peeling off by washing with a release agent solution. Then, after removing the stripping liquid agent in the stripping liquid washing step I, drying is performed in the drying step J,
For example, the mask portion 4 is removed by cleaning the dried surface in a cleaning step K using an ultrasonic cleaning device or the like using a trichloroethylene solution having a temperature of about 100 ° C., so that the pattern portion 3 remains.

[0017]

Since the present invention is constructed as described above, for example, handrails in washrooms, toilets, bathrooms, etc., plumbers in bathrooms, faucets in kitchens, etc., as well as outer walls, Metal, plastic such as stainless steel, brass, aluminum, etc. used for decorative boards used for walls, indoor walls, etc., or for various accessories such as tableware, vases, containers, etc. It can form uniform and stable picture patterns, character patterns, symbol patterns, etc. without deteriorating the beauty and value as surface decoration for various equipment such as products, and those products have good appearance It gives a striking impression.

That is, in the various accessories provided with the surface decoration according to the present invention, the pattern, character, symbol, and the like provided on the surface of the various accessory fabric material on which the plating layer M is formed. This is because the patterned portion 3 remains by removing the plating layer M around the mask portion 4 by sand blasting or a stripping solution while leaving the mask portion 4 that has been removed. For example, a picture pattern, a character pattern, a symbol pattern, or the like can be easily made to appear on the surface of the substrate, and the pattern does not significantly damage the fabric material and the plating layer M.

The pattern portion 3 is formed by a mask portion 4 of a film member 2 in the form of a picture pattern, a character pattern, a symbol pattern, etc., which is adhered to the surface of various equipment fabric materials.
It is possible to clearly express the outline of a satin pattern, character pattern, symbol pattern, etc. on the surface of various equipment.

After the pattern portion 3 is formed, a protective plating layer 5 is formed on the surface.
Is formed, the surfaces of various accessories after the formation of the pattern portion 3 can be easily protected from rust, discoloration, cracks, and the like.

On the other hand, in the surface decoration processing method for various accessories having the surface decoration according to the present invention, a surface treatment step (A, B, D, E) of mirror-finishing the surface of the stainless steel substrate.
And a plating layer M such as a rhodium plating layer or a gold plating layer.
And a plating process F to form a pattern, a character pattern, and the like on the surface of various equipment fabric materials on which the plating layer M is formed.
A forming process G for forming a mask portion 4 in the shape of a symbol pattern or the like and scratching the plating layer M around the mask portion 4 to a matte state of a matte finish by sandblasting; A plating layer stripping step H for stripping the plating layer M, a stripping solution washing step I for removing the stripping solution, a drying step J for drying, and a washing step K for washing the surface after drying. It is possible to easily form a glossy pattern portion 3 such as a picture pattern pattern, a character pattern, a symbol pattern, etc., with a satin pattern on the surface of the surface as a background.

A base treatment step (A, B, D, E) for mirror-finishing the surface of the brass / aluminum base, a plating treatment step F for forming a nickel plating layer after forming a copper plating layer, and a plating layer M A mask portion 4 in the form of a picture pattern, a character pattern, a symbol pattern, etc. is formed on the surface of the formed various equipment material, and a plating layer M around the mask portion 4 is formed.
Forming process G for sanding the matted state to a matte state by sand blasting, cleaning process K for cleaning the formed surface, and transparent chrome plating layer or gold plating for surface protection on the formed surface after cleaning. Since the method comprises a protective plating process L for forming a layer, the matte brass / aluminum surface of the various equipment includes metal such as a picture pattern, a character pattern, a symbol pattern, etc. different from the brass / aluminum surface. The glossy and beautiful pattern portion 3 can be easily formed. In addition, the protective plating process L can protect the surface of the various component fabric materials after the formation of the pattern portion 3 from rust, discoloration, cracks, and the like.

A base treatment step (A, B, D, E) for mirror-finishing the surface of a stainless steel base, a plating treatment step F for forming a gold plating layer M, and various equipment on which the plating layer M is formed A mask portion 4 in the shape of a picture pattern, character pattern, symbol pattern, etc. is formed on the surface of the cloth material, and the mask portion 4 is formed.
The method includes a plating layer stripping step H for stripping the surrounding plating layer M with a stripping solution, a stripping solution washing step I for removing the stripping solution, a drying step J for drying, and a washing step K for washing the surface after drying. , In the glossy stainless steel surface of various equipment
It is possible to easily form a glossy and beautiful pattern portion 3 by gold plating such as a character pattern and a symbol pattern.

The undercoating process (A, B, D, E) includes a polishing process A by under-polishing the surface of the various dough materials, a first cleaning process B for cleaning the polished surface, and a surface process. And a second cleaning step E for cleaning the surface after the surface finishing, so that the surface of the various material materials can be treated beautifully without damaging the product, and the product yield can be improved. Can be improved.

In the forming process G, the mask portion 4 is formed by peeling off the release paper 7 from the film member 2 in the form of a picture pattern, a character pattern, a symbol pattern, etc. and exposing the pressure-sensitive adhesive 6 to various equipment. Since it is to be adhered to the surface of the article material, it can be easily adhered to an arbitrary position for forming the pattern portion 3 on the surface of various equipment.

[Brief description of the drawings]

FIG. 1 is a perspective view illustrating a handrail according to an embodiment of the present invention.

FIG. 2 is a perspective view showing an example of a film member forming a mask portion.

FIG. 3 is a flowchart sequentially showing steps of a surface decoration processing method in the case of a stainless steel base.

FIG. 4 shows a forming process.
(A) is a cross-sectional view at the time of sticking the film member, (b) is a cross-sectional view after sticking the film member, (c) is a cross-sectional view at the time of sandblasting, and (d) is a cross-sectional view at the time of removing the film member. .

FIG. 5 is a flow chart showing another embodiment of the present invention and sequentially showing steps of a surface decoration processing method in the case of brass and aluminum base.

6A and 6B show a forming process in the case of a brass or aluminum base, wherein FIG. 6A is a cross-sectional view at the time of sandblasting, FIG. 6B is a cross-sectional view at the time of removing a film member, and FIG. It is sectional drawing after a processing process.

FIG. 7 shows another embodiment of the present invention, and is a flowchart sequentially showing steps of a surface decoration processing method in the case of a stainless steel base.

[Explanation of symbols]

DESCRIPTION OF SYMBOLS 1 ... Handrail 1A ... Handle part 1B ... Mounting leg part 2 ... Film member 3 ... Pattern part 4 ... Mask part 5 ... Protective plating layer 6 ... Adhesive 7 ... Release paper P ... Wall surface Q ... Abrasive M ... Plating layer A ... Polishing step B: First cleaning step C: Quality inspection step D: Surface finishing step E: Second cleaning step F: Plating step G: Forming step H: Plating layer peeling step I: Stripping liquid cleaning step J: Drying process K: Cleaning process L: Protective plating process

Claims (8)

[Claims] 1. A plating layer around a mask portion except for a mask portion in the form of a picture pattern, a character pattern, a symbol pattern, etc., provided on the surface of a cloth material for various accessories on which a plating layer is formed. Various types of equipment having a surface decoration, wherein a pattern portion is formed by a plating layer having a contour such as a picture pattern, a character pattern, and a symbol pattern formed by processing or peeling with a stripping liquid. 2. The surface according to claim 1, wherein the pattern portion is formed by a mask portion made of a film member in the form of a picture pattern, a character pattern, a symbol pattern, or the like, which is adhered to the surface of various equipment material materials. Various accessories with decoration. 3. The various accessories having a surface decoration according to claim 1, wherein a protective plating layer is formed on the surface after the pattern portion is formed. 4. A base treatment step of mirror-finishing the surface of a stainless steel base, a plating step of forming a plating layer such as a rhodium plating layer or a gold plating layer, and a surface of various equipment fabric materials on which the plating layer is formed. Forming a mask portion in the shape of a picture pattern, a character pattern, a symbol pattern, etc., and forming a plating layer around the mask portion by sandblasting so that the matting state of the matte surface is damaged, and after the forming process Surface decoration processing of various equipment including a plating layer stripping step of stripping a plating layer with a stripping solution, a stripping solution washing step of removing a stripping solution, a drying step of drying, and a washing step of washing the surface after drying Method. 5. A base material processing step of mirror-finishing the surface of a brass / aluminum base, a plating step of forming a nickel plating layer after forming a copper plating layer, and various equipment fabric materials on which the plating layer is formed. Forming a mask part in the shape of a picture pattern, character pattern, symbol pattern, etc. on the surface of the surface, and forming a plating layer around the mask part by sandblasting to scratch the matte state of the satin finish, and forming processing A surface decoration processing method for various equipment, comprising: a cleaning step of cleaning a surface; and a protective plating step of forming a protective plating layer for surface protection on the forming surface after the cleaning. 6. A surface treatment process for mirror-finishing the surface of a stainless steel substrate, a plating process for forming a gold plating layer, and a pattern / character pattern on a surface of various equipment fabric materials on which the plating layer is formed. Forming a mask portion in the shape of a symbol pattern and the like, a plating layer stripping step of stripping a plating layer around the mask portion with a stripping solution, a stripping solution washing step of removing the stripping solution, and a drying step of drying; A surface decoration processing method for various accessories, comprising a cleaning step of cleaning the surface after drying. 7. The undercoating process includes: a polishing process by under-polishing on the surface of various accessory fabric materials; a first cleaning process of cleaning the polished surface; and a surface finishing process by mirror finishing on the surface. And a second cleaning step of cleaning the surface after surface finishing. 8. The method of forming a mask portion in the forming process includes peeling off a release paper covering an adhesive surface formed on one surface of a film member in the form of a picture pattern, a character pattern, a symbol pattern, or the like. The surface decoration processing method for various accessories according to any one of claims 4 to 7, wherein the surface is exposed and then attached to the surface of the various accessory fabric material.