JP2002017598A - Bathroom washing place and method for manufacturing the same - Google Patents
Bathroom washing place and method for manufacturing the sameInfo
- Publication number
- JP2002017598A JP2002017598A JP2000200653A JP2000200653A JP2002017598A JP 2002017598 A JP2002017598 A JP 2002017598A JP 2000200653 A JP2000200653 A JP 2000200653A JP 2000200653 A JP2000200653 A JP 2000200653A JP 2002017598 A JP2002017598 A JP 2002017598A
- Authority
- JP
- Japan
- Prior art keywords
- thermoplastic elastomer
- washing place
- layer
- bathroom washing
- bathroom
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は浴室洗い場とその製
造法に関するものである。The present invention relates to a bathroom washing place and a method for manufacturing the same.
【０００２】[0002]
【従来の技術】従来、浴室内に設置される浴室洗い場は
ポリプロピレンなどの熱可塑性樹脂や、不飽和ポリエス
テル樹脂とガラス繊維を用いた繊維強化プラスチック
（以下ＦＲＰという）であったり硬質磁性タイルであっ
た。これらの浴室洗い場は高耐久性、高級感、重厚感あ
るものとするために表面をできるだけ硬く、また高剛性
化する傾向にあった。2. Description of the Related Art Conventionally, a bathroom washing place installed in a bathroom is made of thermoplastic resin such as polypropylene, fiber reinforced plastic (hereinafter referred to as FRP) using unsaturated polyester resin and glass fiber, or hard magnetic tile. Was. These bathroom washing places tend to have a hard surface as much as possible and high rigidity in order to provide high durability, high-grade feeling and solid feeling.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら幼児や足
腰の弱った高齢者などの場合には、不安定であり浴室洗
い場で滑ったり転倒したりして身体を強く打ち付けたり
することがある。この様な場合に、浴室洗い場が硬くか
つ剛性の大きなものであると怪我をする危険が伴う。そ
こで、浴室洗い場全体を軟質材で形成することが考えら
れるが、このように浴室洗い場全体を軟質材で形成する
と、浴室洗い場自身が形状保持できなくなってしまう。However, in the case of an infant or an elderly person with weak legs, the body is unstable and may hit the body strongly by slipping or falling in the bathroom washing place. In such a case, if the bathroom washing place is hard and rigid, there is a risk of injury. Therefore, it is conceivable to form the entire bathroom washing area with a soft material. However, if the entire bathroom washing area is formed of a soft material in this way, the shape of the bathroom washing area itself cannot be maintained.
【０００４】また、浴室内には人体からの垢、石鹸かす
などの汚れ成分が充満しており、日常の浴室洗い場の手
入れが大変である。さらに、浴室内は高湿度であり、細
菌やカビの増殖には最適な環境である。手入れを少しで
も怠ると、浴室洗い場の表面には細菌やカビが増殖しや
すく不潔になりやすい。[0004] Further, the bathroom is full of dirt components such as dirt and soap scum from the human body, and daily cleaning of the bathroom is difficult. Furthermore, the bathroom has high humidity, making it an ideal environment for the growth of bacteria and mold. With little care, bacteria and mold can easily grow and become dirty on the surface of the bathroom.
【０００５】また、軟質の浴室洗い場を製造し提供する
に際して、これを量産性のよいものとし、安価に浴槽を
提供できるようにすることが求められる。[0005] Further, when manufacturing and providing a soft bathroom washing place, it is required to improve the mass productivity and to provide a bathtub at low cost.
【０００６】[0006]
【課題を解決するための手段】本発明は上記課題を解決
するために、樹脂材料からなるバックアップ基材に対し
て、表面自由エネルギーが熱可塑性エラストマーより小
さい物質を含む前記熱可塑性エラストマー層からなる軟
質材を表面層として積層し一体化した浴室洗い場として
ある。In order to solve the above-mentioned problems, the present invention comprises the above-mentioned thermoplastic elastomer layer containing a substance having a surface free energy smaller than that of the thermoplastic elastomer with respect to a backup substrate made of a resin material. This is a bathroom washing place where soft materials are laminated as a surface layer and integrated.
【０００７】上記発明によれば、樹脂材料からなるバッ
クアップ基材によって浴室洗い場自体の形状が保持され
るとともに、表面層が熱可塑性エラストマー層の軟質材
料により形成されているため、たとえば幼児や高齢者な
どが洗い場で転倒してもその衝撃を軟質材料により良好
に吸収でき、安全性を向上させることができる。さら
に、表面自由エネルギーが小さい物質を熱可塑性エラス
トマー層が含んでいるため表面層の撥水性が向上し、汚
れ成分に対し低活性となり防汚性が向上する。また、そ
れらの汚れ成分を餌とする細菌やカビの増殖も抑制され
る。According to the above invention, the shape of the bathroom washing space itself is maintained by the backup base material made of the resin material, and the surface layer is formed of the soft material of the thermoplastic elastomer layer. Even if it falls down in the washing place, the impact can be better absorbed by the soft material, and the safety can be improved. Furthermore, since the thermoplastic elastomer layer contains a substance having a small surface free energy, the water repellency of the surface layer is improved, the activity of the surface layer is reduced, and the antifouling property is improved. In addition, the growth of bacteria and fungi that feed on these dirt components is also suppressed.
【０００８】[0008]
【発明の実施の形態】本発明の請求項１記載の発明は、
樹脂材料からなるバックアップ基材に対して、表面自由
エネルギーが熱可塑性エラストマーより小さい物質を含
む前記熱可塑性エラストマー層からなる軟質材を表面層
として積層し一体化した浴室洗い場である。BEST MODE FOR CARRYING OUT THE INVENTION
This is a bathroom washing place where a soft material composed of the thermoplastic elastomer layer containing a substance having a surface free energy smaller than that of the thermoplastic elastomer is laminated as a surface layer on a backup substrate composed of a resin material, and integrated.
【０００９】そして、樹脂材料からなるバックアップ基
材によって浴室洗い場自体の形状が保持されるととも
に、表面層が熱可塑性エラストマー層の軟質材料により
形成されているため、たとえば幼児や高齢者などが洗い
場で転倒してもその衝撃を軟質材料により良好に吸収で
き、安全性を向上させることができる。さらに、表面自
由エネルギーが小さい物質を熱可塑性エラストマー層が
含んでいるため表面層の撥水性が向上し、汚れ成分に対
し低活性となり防汚性が向上する。また、それらの汚れ
成分を餌とする細菌やカビの増殖も抑制される。Since the shape of the bathroom washing place itself is maintained by the backup base material made of the resin material, and the surface layer is formed of the soft material of the thermoplastic elastomer layer, for example, infants and the elderly can be used in the washing place. Even if the vehicle falls, the impact can be better absorbed by the soft material, and the safety can be improved. Furthermore, since the thermoplastic elastomer layer contains a substance having a small surface free energy, the water repellency of the surface layer is improved, the activity of the surface layer is reduced, and the antifouling property is improved. In addition, the growth of bacteria and fungi that feed on these dirt components is also suppressed.
【００１０】また、請求項２記載の発明は、樹脂材料か
らなるバックアップ基材と表面自由エネルギーが熱可塑
性エラストマーより小さい物質を含む前記熱可塑性エラ
ストマー層との間に第二の弾性層を有する軟質材を表面
層として積層し一体化した浴室洗い場である。[0010] The invention according to claim 2 is a soft material having a second elastic layer between a backup substrate made of a resin material and the thermoplastic elastomer layer containing a substance having a surface free energy smaller than that of the thermoplastic elastomer. This is a bathroom washing area where materials are laminated as a surface layer and integrated.
【００１１】そして、樹脂材料からなるバックアップ基
材と表面層である熱可塑性エラストマー層との間に第二
の弾性層を有する軟質材を積層し一体化することによ
り、浴室洗い場表面をよりいっそう軟らかく、安全にす
ることができる。[0011] A soft material having a second elastic layer is laminated and integrated between a backup base material made of a resin material and a thermoplastic elastomer layer as a surface layer, so that the surface of the bathroom washing place is softened further. , Can be secure.
【００１２】また、請求項３記載の発明は、バックアッ
プ基材の樹脂材料がＦＲＰからなる浴室洗い場である。Further, the invention according to claim 3 is a bathroom washing place in which the resin material of the backup base material is made of FRP.
【００１３】そして、ＦＲＰは不飽和ポリエステル樹脂
などの熱硬化性樹脂とガラス繊維を混合して硬化させた
ものであり、軽くて高剛性のため、強度の大きい浴室洗
い場が可能となる。The FRP is obtained by mixing and curing a thermosetting resin such as an unsaturated polyester resin and glass fiber, and is light and has high rigidity, so that a bathroom washing place with high strength can be realized.
【００１４】また、請求項４記載の発明は、塩素元素を
含まない化学構造を有する表面自由エネルギーが熱可塑
性エラストマーより小さい物質を含む該熱可塑性エラス
トマー層からなる軟質材を表面層として積層し一体化し
た浴室洗い場である。Further, according to the present invention, a soft material composed of a thermoplastic elastomer layer having a chemical structure containing no chlorine element and having a surface free energy smaller than that of the thermoplastic elastomer is used as a surface layer. It is a bathroom wash area.
【００１５】そして、熱可塑性エラストマー層が塩素元
素を含まないため、サーマルリサイクル時に塩化水素ガ
スやダイオキシンといった人体に悪影響を及ぼす排ガス
が生成しない。このため、環境に優しいクリーンな浴室
洗い場が可能となる。[0015] Since the thermoplastic elastomer layer does not contain chlorine element, exhaust gas such as hydrogen chloride gas and dioxin which adversely affects the human body is not generated during thermal recycling. For this reason, an environment-friendly clean bathroom washing place becomes possible.
【００１６】また、請求項５記載の発明は、弾性層が発
泡層である浴室洗い場である。The invention according to claim 5 is a bathroom washing place wherein the elastic layer is a foamed layer.
【００１７】そして、このようにすれば軟質材層をより
いっそう軟らかくすることができ、安全性や快適性がさ
らに向上する。[0017] By doing so, the soft material layer can be further softened, and the safety and comfort are further improved.
【００１８】また、請求項６記載の発明は、前記表面自
由エネルギーが熱可塑性エラストマーより小さい物質が
有機珪素化合物からなる請求項１または２記載の浴室洗
い場である。The invention according to claim 6 is the bathroom washing place according to claim 1 or 2, wherein the substance whose surface free energy is smaller than that of the thermoplastic elastomer comprises an organosilicon compound.
【００１９】そして、有機珪素化合物を熱可塑性エラス
トマー層に添加することにより熱可塑性エラストマー層
の表面は撥水性が大幅に向上し、汚れ成分に対し低活性
となるため防汚性が向上する。さらに、汚れ成分の浴室
洗い場表面への汚れの付着が少なくなるため、それらを
餌とする細菌やカビの増殖も抑制される。By adding the organosilicon compound to the thermoplastic elastomer layer, the surface of the thermoplastic elastomer layer has significantly improved water repellency and low activity against dirt components, thereby improving antifouling properties. Furthermore, since the adhesion of the dirt components to the surface of the bathroom washing area is reduced, the growth of bacteria and molds that feed on them is suppressed.
【００２０】また、請求項７記載の発明は、樹脂材料か
らなるバックアップ基材に対して、有機珪素化合物と抗
菌剤とを含む熱可塑性エラストマー層からなる軟質材を
表面層として積層し一体化した浴室洗い場である。According to the present invention, a soft material comprising a thermoplastic elastomer layer containing an organosilicon compound and an antibacterial agent is laminated and integrated as a surface layer on a backup substrate comprising a resin material. It is a bathroom washroom.
【００２１】また、請求項８記載の発明は、樹脂材料か
らなるバックアップ基材と、有機珪素化合物と抗菌剤と
を含む熱可塑性エラストマー層との間に第二の弾性層を
有する軟質材を表面層として積層し一体化した浴室洗い
場である。According to an eighth aspect of the present invention, a soft material having a second elastic layer between a backup base made of a resin material and a thermoplastic elastomer layer containing an organic silicon compound and an antimicrobial agent is provided on the surface. This is a bathroom washing area that is laminated and integrated as a layer.
【００２２】そして、熱可塑性エラストマー層からなる
浴室洗い場の表面層は有機珪素化合物を含むことによ
り、防汚性が向上し汚れ成分が付着しにくくなる。さら
に、抗菌剤を含有することにより、浴室洗い場表面での
細菌、ぬめり、カビなどの増殖が抑制される。さらに、
樹脂材料からなるバックアップ基材と表面層である熱可
塑性エラストマー層との間に第二の弾性層を有する軟質
材を積層し一体化することにより、浴室洗い場表面をよ
りいっそう軟らかく、安全にすることができる。The surface layer of the bathroom washing place comprising the thermoplastic elastomer layer contains an organosilicon compound, so that the antifouling property is improved and the dirt component is hardly adhered. Further, by containing an antibacterial agent, the growth of bacteria, slime, mold, etc. on the surface of the bathroom washing place is suppressed. further,
By laminating and integrating a soft material having a second elastic layer between a backup base material made of a resin material and a thermoplastic elastomer layer that is a surface layer, the surface of the bathroom washing place is made more soft and safe. Can be.
【００２３】また、請求項９記載の発明は、抗菌剤とし
て無機系抗菌剤の少なくとも一種、および有機系抗菌剤
の少なくとも一種からなる請求項７または８記載の浴室
洗い場である。According to a ninth aspect of the present invention, there is provided a bathroom washing place according to the seventh or eighth aspect, wherein the antibacterial agent comprises at least one of inorganic antibacterial agents and at least one of organic antibacterial agents.
【００２４】そして、無機系抗菌剤の作用により主とし
て細菌の増殖を抑制し、さらには細菌の増殖に起因する
悪臭の発生、酵母の増殖に起因するぬめりの発生も抑制
する。また、有機系抗菌剤の作用により主としてカビの
増殖を抑制する。このように、カビ、細菌などの増殖を
抑制し、健康的で清潔な浴室洗い場が可能となる。The action of the inorganic antibacterial agent mainly suppresses the growth of bacteria, and further suppresses the generation of offensive odors caused by the growth of bacteria and the generation of slimming caused by the growth of yeast. In addition, the action of the organic antibacterial agent mainly suppresses the growth of mold. In this way, the growth of mold, bacteria and the like is suppressed, and a healthy and clean bathroom washing place becomes possible.
【００２５】また、請求項１０記載の発明は、樹脂材料
からなるバックアップ基材に対して、表面自由エネルギ
ーが熱可塑性エラストマーより小さい物質を含む前記熱
可塑性エラストマー層からなる軟質材を表面層として積
層し一体化した浴室洗い場において、軟質材からなる表
面層は真空成形によりバックアップ基材と積層し一体化
する浴室洗い場の製造法である。According to a tenth aspect of the present invention, a soft material comprising the thermoplastic elastomer layer containing a substance having a surface free energy smaller than that of the thermoplastic elastomer is laminated as a surface layer on a backup substrate comprising a resin material. This is a method for manufacturing a bathroom washing place in which a surface layer made of a soft material is laminated and integrated with a backup base material by vacuum forming.
【００２６】そして、軟質材からなる表面層を真空成形
によりバックアップ基材と積層一体化することにより浴
室洗い場を簡単に安価に製造することができる。Further, the surface layer made of a soft material is laminated and integrated with the backup substrate by vacuum forming, so that a bathroom washing place can be easily and inexpensively manufactured.
【００２７】[0027]
【実施例】以下本発明の具体的な一実施例について説明
する。DESCRIPTION OF THE PREFERRED EMBODIMENTS A specific embodiment of the present invention will be described below.
【００２８】本発明におけるバックアップ基体の樹脂材
料としては、熱可塑性樹脂としてポリエチレン、ポリプ
ロピレン、アクリロニトリル・ブタジエン・スチレン共
重合物などが挙げられるが、これに限定するものではな
い。また、熱硬化性樹脂としてフェノール樹脂、尿素樹
脂、メラミン樹脂、ウレタン樹脂、不飽和ポリエステル
樹脂、エポキシ樹脂、熱硬化性アクリル樹脂などが挙げ
られるが、これに限定するものではない。また、ＦＲＰ
用樹脂としては上記熱硬化性樹脂が使用可能であり、成
形法としてはハンドレイアップ成形法、ホットプレス成
形法、注型法、レジントランスファーモールデイング法
などを用いることが可能である。Examples of the resin material of the backup substrate in the present invention include, but are not limited to, thermoplastic resins such as polyethylene, polypropylene and acrylonitrile-butadiene-styrene copolymer. Examples of the thermosetting resin include a phenol resin, a urea resin, a melamine resin, a urethane resin, an unsaturated polyester resin, an epoxy resin, and a thermosetting acrylic resin, but are not limited thereto. Also, FRP
As the resin for use, the above-mentioned thermosetting resin can be used, and as a molding method, a hand lay-up molding method, a hot press molding method, a casting method, a resin transfer molding method, or the like can be used.
【００２９】熱可塑性エラストマーとしては、スチレン
系、オレフィン系、ウレタン系、エステル系、アミド
系、塩化ビニル系などが挙げられるが、これに限定する
ものではない。Examples of the thermoplastic elastomer include, but are not limited to, styrene, olefin, urethane, ester, amide, and vinyl chloride.
【００３０】発泡層としては、ポリエチレン、ポリプロ
ピレン、ポリスチレン、ポリウレタンなどが挙げられる
が、これに限定するものではない。Examples of the foamed layer include, but are not limited to, polyethylene, polypropylene, polystyrene, and polyurethane.
【００３１】本発明の有機珪素化合物としては、ジメチ
ルポリシロキサン、メチルフェニルポリシロキサン、ジ
フェニルポリシロキサンなどのシリコーン化合物。それ
らのシリコーン化合物をアルキッド変性、ポリエステル
変性、アクリル変性、エポキシ変性した変性シリコーン
化合物などが挙げられるが、これに限定するものではな
い。As the organosilicon compound of the present invention, silicone compounds such as dimethylpolysiloxane, methylphenylpolysiloxane and diphenylpolysiloxane. These silicone compounds include, but are not limited to, alkyd-modified, polyester-modified, acryl-modified, and epoxy-modified silicone compounds.
【００３２】本発明における抗菌剤としては、無機系抗
菌剤として、硝酸銀、硫酸銀、塩化銀など。銀、銅、亜
鉛あるいは錫を担持したゼオライト。および銀、銅、亜
鉛あるいは錫を担持したシリカゲルなどが挙げられる
が、これに限定するものではない。The antibacterial agent in the present invention includes silver nitrate, silver sulfate, silver chloride and the like as inorganic antibacterial agents. Zeolite supporting silver, copper, zinc or tin. And silica gel supporting silver, copper, zinc or tin, but not limited thereto.
【００３３】有機系抗菌剤としては、１０、１０’−オ
キシビスフェノキサアルシンなどフェニルエーテル誘導
体、シクロフルアニドなどＮ−ハロアルキルチオ系化合
物、２−（４−チアゾリル）ベンズイミダゾール（以下
ＴＢＺと略称する）等イミダゾール誘導体、２、３、
５、６テトラクロル−４−（メチルスルホリル）ピリジ
ンなど第４級アンモニウム塩などが挙げられるが、これ
に限定するものではない。Examples of the organic antibacterial agent include phenyl ether derivatives such as 10,10'-oxybisphenoxaarsine, N-haloalkylthio compounds such as cyclofluanide, and 2- (4-thiazolyl) benzimidazole (hereinafter abbreviated as TBZ). Imidazole derivatives, 2, 3, etc.
Examples include, but are not limited to, quaternary ammonium salts such as 5,6 tetrachloro-4- (methylsulfolyl) pyridine.
【００３４】（実施例１）ハンドレイアップ成形法によ
り、不飽和ポリエステル樹脂を用いたＦＲＰによりバッ
クアップ基材を作成した。表層として１．５mm厚のポリ
オレフィン系熱可塑性エラストマーと１０mm厚のポリウ
レタン発泡層とを用い、真空成形によりバックアップ基
材と積層一体化し目的とする浴室洗い場を得た。Example 1 A backup base material was prepared by FRP using an unsaturated polyester resin by a hand lay-up molding method. A 1.5 mm-thick polyolefin-based thermoplastic elastomer and a 10 mm-thick polyurethane foam layer were used as a surface layer, and were laminated and integrated with a backup substrate by vacuum molding to obtain a desired bathroom washing place.
【００３５】（実施例２）ハンドレイアップ成形法によ
り、不飽和ポリエステル樹脂を用いたＦＲＰによりバッ
クアップ基材を作成した。表層として１．５mm厚のポリ
オレフィン系熱可塑性エラストマーを用い、真空成形に
よりバックアップ基材と積層一体化し目的とする浴室洗
い場を得た。Example 2 A back-up substrate was prepared by FRP using an unsaturated polyester resin by a hand lay-up molding method. A 1.5 mm-thick polyolefin-based thermoplastic elastomer was used as a surface layer, which was laminated and integrated with a backup substrate by vacuum molding to obtain a desired bathroom washing place.
【００３６】（実施例３）ハンドレイアップ成形法によ
り、不飽和ポリエステル樹脂を用いたＦＲＰによりバッ
クアップ基材を作成した。ジメチルポリシロキサンを
０．５％、ゼオライト銀系抗菌剤を０．５％および有機
系抗菌剤であるＴＢＺを０．５％分散させた１．５mm厚
のポリオレフィン系熱可塑性エラストマーと１５mm厚の
ポリウレタン発泡層とを用い、真空成形によりバックア
ップ基材と積層一体化し目的とする浴室洗い場を得た。Example 3 A backup substrate was prepared by FRP using an unsaturated polyester resin by a hand lay-up molding method. 1.5 mm thick polyolefin-based thermoplastic elastomer in which 0.5% of dimethylpolysiloxane, 0.5% of silver zeolite antibacterial agent and 0.5% of TBZ which is an organic antibacterial agent are dispersed, and 15 mm thick polyurethane Using the foamed layer, the backup base material was laminated and integrated by vacuum molding to obtain a desired bathroom washing place.
【００３７】図１は本発明の一実施例における浴室洗い
場を示す模式図である。１は浴室洗い場であり、２は浴
槽である。この浴室洗い場１は、図１の部分拡大断面図
に示しているようにＦＲＰに代表されるバックアップ基
材３とポリウレタンに代表される発泡層４と熱可塑性エ
ラストマー層５と、熱可塑性エラストマー層中に分散さ
れているジメチルポリシロキサンに代表される有機珪素
化合物６とゼオライト銀に代表される無機系抗菌剤７と
ＴＢＺに代表される有機系抗菌剤８で構成されている。FIG. 1 is a schematic view showing a bathroom washing place in one embodiment of the present invention. 1 is a bathroom washing place, and 2 is a bathtub. As shown in the partially enlarged sectional view of FIG. 1, the bathroom washing place 1 includes a backup base material 3 typified by FRP, a foamed layer 4 typified by polyurethane, a thermoplastic elastomer layer 5, and a thermoplastic elastomer layer 5. And an organic antibacterial agent 8 typified by an organic silicon compound 6 typified by dimethylpolysiloxane, an inorganic antibacterial agent typified by silver zeolite 7 and TBZ.
【００３８】各実施例で得た浴室洗い場の撥水性を協和
界面科学（株）製接触角測定装置（ＣＡ−Ｚ型）で測定
した。その結果を（表１）に示す。The water repellency of the bathroom washing area obtained in each example was measured with a contact angle measuring device (model CA-Z) manufactured by Kyowa Interface Science Co., Ltd. The results are shown in (Table 1).
【００３９】[0039]
【表１】 [Table 1]
【００４０】各実施例で得た浴室洗い場の抗菌性能およ
びカビ抵抗性について試験を行った。前記浴室洗い場か
ら５０mm×５０mmの試料を切りだしそれぞれに菌液（黄
色ブドウ球菌および大腸菌）１ccを滴下し、３７℃で２
４時間培養した。その後、滅菌済みリン酸緩衝液にて菌
を洗い出した。この洗い出した液中の生菌数を、菌数測
定用培地を用いて混釈平板法にて測定した。その結果を
（表２）に示す。A test was conducted on the antibacterial performance and the mold resistance of the bathroom washer obtained in each of the examples. A 50 mm × 50 mm sample was cut out from the bathroom washing place, and 1 cc of a bacterial solution (Staphylococcus aureus and Escherichia coli) was added dropwise to each sample.
The cells were cultured for 4 hours. Thereafter, the bacteria were washed out with a sterilized phosphate buffer. The viable cell count in the washed-out liquid was measured by a pour plate method using a cell count medium. The results are shown in (Table 2).
【００４１】[0041]
【表２】 [Table 2]
【００４２】寒天培地上においた各試料（５０mm×５０
mm）にアスペルギルス・ニガー菌液を噴霧し、２５℃で
７日間培養した。その結果を（表３）に示す。Each sample (50 mm × 50) placed on an agar medium
mm) was sprayed with Aspergillus niger bacterial solution and cultured at 25 ° C. for 7 days. The results are shown in (Table 3).
【００４３】[0043]
【表３】 [Table 3]
【００４４】（表１）から明らかなように、実施例３の
浴室洗い場は実施例１および２の浴室洗い場に比較し、
著しい撥水性の向上が確認された。As is clear from Table 1, the bathroom washing place of Example 3 is compared with the bathroom washing places of Examples 1 and 2.
A remarkable improvement in water repellency was confirmed.
【００４５】（表２）から明らかなように、実施例３の
浴室洗い場は実施例１および２の浴室洗い場に比較し、
黄色ブドウ球菌および大腸菌に対する著しい抗菌効果を
得ることができた。As is clear from Table 2, the bathroom washing place of Example 3 is compared with the bathroom washing places of Examples 1 and 2.
Significant antibacterial effects on Staphylococcus aureus and E. coli could be obtained.
【００４６】（表３）から明らかなように、実施例３の
浴室洗い場は実施例１および２の浴室洗い場に比較し、
良好な抗カビ効果を得ることができた。As is clear from (Table 3), the bathroom washing place of Example 3 is compared with the bathroom washing places of Examples 1 and 2.
A good antifungal effect could be obtained.
【００４７】[0047]
【発明の効果】以上のように、本発明の浴室洗い場とそ
の製造法によれば、次の効果が得られる。As described above, according to the bathroom washing place and the method of manufacturing the same according to the present invention, the following effects can be obtained.
【００４８】請求項１記載の発明によれば、樹脂材料か
らなるバックアップ基材に対して、表面自由エネルギー
が熱可塑性エラストマーより小さい物質を含む前記熱可
塑性エラストマー層からなる軟質材を表面層として積層
し一体化した浴室洗い場とすることにより、樹脂材料か
らなるバックアップ基材によって浴室洗い場自体の形状
が保持されるとともに、表面層が熱可塑性エラストマー
層の軟質材料により形成されているため、たとえば幼児
や高齢者などが洗い場で転倒してもその衝撃を軟質材料
により良好に吸収でき、安全性を向上させることができ
る。さらに、表面自由エネルギーが小さい物質を熱可塑
性エラストマー層が含んでいるため表面層の撥水性が向
上し、汚れ成分に対し低活性となり防汚性が向上する。
また、それらの汚れ成分を餌とする細菌やカビの増殖も
抑制される。According to the first aspect of the present invention, a soft material composed of the thermoplastic elastomer layer containing a substance having a surface free energy smaller than that of the thermoplastic elastomer is laminated as a surface layer on a backup substrate composed of a resin material. By making the bathroom washing place integrated, the shape of the bathroom washing place itself is maintained by the backup base material made of the resin material, and the surface layer is formed of the soft material of the thermoplastic elastomer layer. Even if an elderly person falls down in the washing place, the impact can be better absorbed by the soft material, and safety can be improved. Furthermore, since the thermoplastic elastomer layer contains a substance having a small surface free energy, the water repellency of the surface layer is improved, the activity of the surface layer is reduced, and the antifouling property is improved.
In addition, the growth of bacteria and fungi that feed on these dirt components is also suppressed.
【００４９】また、請求項２記載の発明によれば、樹脂
材料からなるバックアップ基材と表面自由エネルギーが
熱可塑性エラストマーより小さい物質を含む前記熱可塑
性エラストマー層との間に第二の弾性層を有する軟質材
を表面層として積層し一体化した浴室洗い場とすること
により、浴室洗い場表面をよりいっそう軟らかく、安全
にすることができる。According to the second aspect of the present invention, the second elastic layer is provided between the backup base material made of a resin material and the thermoplastic elastomer layer containing a substance having a surface free energy smaller than that of the thermoplastic elastomer. By forming a bathroom washing place by laminating and integrating soft materials having the same as a surface layer, the surface of the bathroom washing place can be made softer and safer.
【００５０】また、請求項３記載の発明によれば、バッ
クアップ基材の樹脂材料がＦＲＰからなる浴室洗い場と
することにより、不飽和ポリエステル樹脂などの熱硬化
生樹脂とガラス繊維を混合分散して加熱硬化させたＦＲ
Ｐは軽くて高剛性のため、強度の大きい浴室洗い場を得
ることができる。According to the third aspect of the present invention, the resin material of the backup base material is a bathroom washing place made of FRP, so that a thermosetting raw resin such as an unsaturated polyester resin and glass fiber are mixed and dispersed. Heat cured FR
Since P is light and has high rigidity, a strong bathroom washing place can be obtained.
【００５１】また、請求項４記載の発明によれば、塩素
元素を含まない化学構造を有する熱可塑性エラストマー
層からなる軟質材を表面層として積層し一体化した浴室
洗い場とすることにより、サーマルリサイクル時に塩化
水素ガスやダイオキシンといった人体に悪影響を及ぼす
は燃焼排ガスが生成しない、環境に優しいクリーンな浴
室洗い場を得ることができる。According to the fourth aspect of the present invention, a bathroom washing place is formed by laminating and integrating a soft material comprising a thermoplastic elastomer layer having a chemical structure containing no chlorine element as a surface layer, thereby providing thermal recycling. It is possible to obtain a clean bathroom that is environmentally friendly and does not generate combustion exhaust gas, which sometimes has an adverse effect on the human body such as hydrogen chloride gas and dioxin.
【００５２】また、請求項５記載の発明によれば、弾性
層が発泡層である浴室洗い場とすることにより、軟質材
層をよりいっそう軟らかくすることができ、安全性およ
び快適性がさらに向上する。According to the fifth aspect of the present invention, the soft material layer can be further softened by providing a bathroom washing place where the elastic layer is a foamed layer, and safety and comfort are further improved. .
【００５３】また、請求項６記載の発明によれば、熱可
塑性エラストマーより表面自由エネルギーが小さい物質
が有機珪素化合物である浴室洗い場とすることにより、
熱可塑性エラストマー層の表面すなわち浴室洗い場表面
の撥水性が大幅に向上し、汚れ成分に対し低活性となる
ため防汚性が向上する。さらに、汚れ成分の浴室洗い場
表面への汚れの付着が少なくなるため、それらを餌とす
る細菌やカビの増殖も抑制される。According to the sixth aspect of the present invention, a bathroom washing place in which the substance having a lower surface free energy than the thermoplastic elastomer is an organosilicon compound is provided.
The water repellency of the surface of the thermoplastic elastomer layer, that is, the surface of the bathroom washing place, is greatly improved, and the activity of soil components is low, so that the antifouling property is improved. Furthermore, since the adhesion of the dirt components to the surface of the bathroom washing area is reduced, the growth of bacteria and molds that feed on them is suppressed.
【００５４】また、請求項７記載の発明によれば、樹脂
材料からなるバックアップ基材に対して、有機珪素化合
物と抗菌剤とを含む熱可塑性エラストマー層からなる軟
質材を表面層として積層し一体化した浴室洗い場とする
ことにより、また、請求項８記載の発明によれば、樹脂
材料からなるバックアップ基材と有機珪素化合物と抗菌
剤とを含む熱可塑性エラストマー層との間に第二の弾性
層を有する軟質材を表面層として積層し一体化した浴室
洗い場とすることにより、熱可塑性エラストマー層から
なる浴室洗い場の表面層は有機珪素化合物を含むことに
より、防汚性が向上し汚れ成分が付着しにくくなる。さ
らに、抗菌剤を含有することにより、浴室洗い場表面で
の細菌、ぬめり、カビなどの増殖が抑制される。さら
に、樹脂材料からなるバックアップ基材と表面層である
熱可塑性エラストマー層との間に第二の弾性層を有する
軟質材を積層し一体化することにより、浴室洗い場表面
をよりいっそう軟らかく、安全にすることができる。According to the seventh aspect of the present invention, a soft material made of a thermoplastic elastomer layer containing an organic silicon compound and an antibacterial agent is laminated as a surface layer on a backup base made of a resin material, and integrated. According to the invention of claim 8, the second elasticity is provided between the backup base material made of a resin material and the thermoplastic elastomer layer containing the organic silicon compound and the antibacterial agent. The surface layer of the bathroom washing area composed of a thermoplastic elastomer layer contains an organosilicon compound, thereby improving the antifouling property and reducing the amount of dirt components. It becomes difficult to adhere. Further, by containing an antibacterial agent, the growth of bacteria, slime, mold, etc. on the surface of the bathroom washing place is suppressed. Furthermore, by laminating and integrating a soft material having a second elastic layer between a backup base material made of a resin material and a thermoplastic elastomer layer as a surface layer, the surface of the bathroom washing place is softer and safer. can do.
【００５５】また、請求項９記載の発明によれば、抗菌
剤として無機系抗菌剤の少なくとも一種、および有機系
抗菌剤の少なくとも一種からなる浴室洗い場とすること
により、無機系抗菌剤の作用により主として細菌の増殖
を抑制し、さらには細菌の増殖に起因する悪臭の発生、
酵母の増殖に起因するぬめりの発生も抑制する。また、
有機系抗菌剤の作用により主としてカビの増殖を抑制す
る。このように、カビ、細菌などの増殖を抑制し、健康
的で清潔な浴室洗い場が可能となる。According to the ninth aspect of the present invention, by providing a bathroom washing place comprising at least one of an inorganic antibacterial agent and at least one of an organic antibacterial agent as an antibacterial agent, the action of the inorganic antibacterial agent can be improved. Mainly suppresses the growth of bacteria, furthermore the generation of offensive odors due to the growth of bacteria,
It also suppresses the occurrence of slime caused by yeast growth. Also,
The growth of mold is mainly suppressed by the action of the organic antibacterial agent. In this way, the growth of mold, bacteria and the like is suppressed, and a healthy and clean bathroom washing place becomes possible.
【００５６】また、請求項１０記載の発明のように、樹
脂材料からなるバックアップ基材に対して、表面自由エ
ネルギーが熱可塑性エラストマーより小さい物質を含む
前記熱可塑性エラストマー層からなる軟質材を表面層と
して積層し一体化した浴室洗い場において、軟質材から
なる表面層は真空成形によりバックアップ基材と積層し
一体化して浴室洗い場を製造することにより、簡単に安
価に製造することができる。According to the tenth aspect of the present invention, a soft material composed of the thermoplastic elastomer layer containing a substance having a surface free energy smaller than that of the thermoplastic elastomer is applied to the backing substrate composed of a resin material. In the bathroom washing area integrated and integrated as above, the surface layer made of a soft material can be easily and inexpensively manufactured by stacking and integrating the backup material with the backup base material by vacuum forming to manufacture the bathroom washing area.
【図１】本発明の一実施例における浴室洗い場の模式図FIG. 1 is a schematic view of a bathroom washing place in one embodiment of the present invention.
１ 浴室洗い場 ２ 浴槽 ３ バックアップ基材 ４ 発泡層 ５ 熱可塑性エラストマー層 ６ 有機珪素化合物 ７ 無機系抗菌剤 ８ 有機系抗菌剤 DESCRIPTION OF SYMBOLS 1 Bathroom washing place 2 Bathtub 3 Backup base material 4 Foam layer 5 Thermoplastic elastomer layer 6 Organosilicon compound 7 Inorganic antibacterial agent 8 Organic antibacterial agent
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ｃ０８Ｌ 101/00 Ｃ０８Ｌ 101/00 // Ｂ２９Ｋ 21:00 Ｂ２９Ｋ 21:00 105:12 105:12 Ｂ２９Ｌ 9:00 Ｂ２９Ｌ 9:00 31:58 31:58 (72)発明者 今坂 喜信 大阪府門真市大字門真1006番地 松下電器 産業株式会社内 (72)発明者 ▲よし▼田 博明 大阪府門真市大字門真1006番地 松下電器 産業株式会社内 Ｆターム(参考） 2D032 GA00 4F208 AA45 AC03 AG03 AG20 AH48 MA01 MB01 MG07 MG11 4J002 BB151 BD031 BP011 CK021 CL001 CP032 DA076 DA106 DA116 DD076 DF036 DG046 ED056 EN136 EV006 EV326 FD186 GC00 ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛ (Reference) C08L 101/00 C08L 101/00 // B29K 21:00 B29K 21:00 105: 12 105: 12 B29L 9: 00 B29L 9:00 31:58 31:58 (72) Inventor Yoshinobu Imasaka 1006 Kadoma, Kadoma City, Osaka Prefecture Matsushita Electric Industrial Co., Ltd. F-term (reference) in Matsushita Electric Industrial Co., Ltd.
Claims (10)
して、表面自由エネルギーが熱可塑性エラストマーより
小さい物質を含む前記熱可塑性エラストマー層からなる
軟質材を表面層として積層し一体化した浴室洗い場。1. A bathroom washing place in which a soft material made of a thermoplastic elastomer layer containing a substance having a surface free energy smaller than that of a thermoplastic elastomer is laminated as a surface layer on a backup base made of a resin material and integrated therewith.
面自由エネルギーが熱可塑性エラストマーより小さい物
質を含む前記熱可塑性エラストマー層との間に第二の弾
性層を有する軟質材を表面層として積層し一体化した浴
室洗い場。2. A soft material having a second elastic layer is laminated as a surface layer between a backup base material made of a resin material and the thermoplastic elastomer layer containing a substance having a surface free energy smaller than that of the thermoplastic elastomer. Bathroom washroom.
材からなる請求項１または２記載の浴室洗い場。3. The bathroom washing place according to claim 1, wherein the resin material is a backup base material which is FRP.
まない化学構造を有する請求項１ないし３のいずれか１
項記載の浴室洗い場。4. The thermoplastic elastomer layer according to claim 1, wherein the thermoplastic elastomer layer has a chemical structure containing no chlorine element.
Bathroom washing area described in the section.
室洗い場。5. The bathroom according to claim 2, wherein the elastic layer is a foam layer.
ストマーより小さい物質は有機珪素化合物からなる請求
項１または２記載の浴室洗い場。6. The bathroom washing place according to claim 1, wherein the substance whose surface free energy is smaller than that of the thermoplastic elastomer comprises an organosilicon compound.
して、有機珪素化合物と抗菌剤とを含む熱可塑性エラス
トマー層からなる軟質材を表面層として積層し一体化し
た浴室洗い場。7. A bathroom washing place in which a soft material comprising a thermoplastic elastomer layer containing an organosilicon compound and an antibacterial agent is laminated as a surface layer on a backup substrate made of a resin material and integrated therewith.
有機珪素化合物と抗菌剤とを含む熱可塑性エラストマー
層との間に第二の弾性層を有する軟質材を表面層として
積層し一体化した浴室洗い場。8. A backup substrate made of a resin material,
A bathroom washing place in which a soft material having a second elastic layer is laminated as a surface layer and integrated with a thermoplastic elastomer layer containing an organic silicon compound and an antibacterial agent.
種、および有機系抗菌剤の少なくとも一種からなる請求
項７または８記載の浴室洗い場。9. The bathroom washing place according to claim 7, wherein the antibacterial agent comprises at least one of an inorganic antibacterial agent and at least one of an organic antibacterial agent.
対して、表面自由エネルギーが熱可塑性エラストマーよ
り小さい物質を含む前記熱可塑性エラストマー層からな
る軟質材を表面層として積層し一体化した浴室洗い場に
おいて、軟質材からなる表面層は真空成形によりバック
アップ基材と積層し一体化する浴室洗い場の製造法。10. A bathroom washing place in which a soft material composed of a thermoplastic elastomer layer having a surface free energy smaller than that of a thermoplastic elastomer is laminated and integrated with a backup substrate composed of a resin material as a surface layer, A method of manufacturing a bathroom washroom where a surface layer made of a soft material is laminated and integrated with a backup substrate by vacuum forming.