【特許請求の範囲】
【請求項１】 既設管中に挿入され、加熱されることにより該既設管の内面に密着させる更正管であって、単独重合体のガラス転移温度が−１４０〜−２０℃であるアルキル（メタ）アクリレートモノマー５０重量％以上及びその他のアクリル系モノマー５０重量％以下を含有してなるアクリル系モノマー成分１００重量部及び多官能性モノマー成分０．０１〜３０重量部を共重合したアクリル系共重合体１０重量％超４０重量％以下に、塩化ビニルモノマー又は塩化ビニルモノマー及びその他の共重合性モノマー９０重量％未満６０重量％以上をグラフト共重合してなる平均重合度４００〜２５００の複合塩化ビニル系樹脂１００重量部に対し、該複合塩化ビニル系樹脂と相溶し得る熱可塑性エラストマー３〜３０重量部が添加されてなる塩化ビニル系樹脂組成物を溶融混練して得られることを特徴とする塩化ビニル系樹脂更生管。
【請求項２】
熱可塑性エラストマーが、アクリロニトリル−ブタジエン共重合体、エチレン−酢酸ビニル共重合体及びエチレン−酢酸ビニル−一酸化炭素共重合体からなる群より選択される１種もしくは２種以上を含有する熱可塑性エラストマーであることを特徴とする請求項１に記載の塩化ビニル系樹脂更生管。
[Claims]
(1) A correction pipe that is inserted into an existing pipe and is brought into close contact with the inner surface of the existing pipe by being heated,100 parts by weight of an acrylic monomer component containing 50% by weight or more of an alkyl (meth) acrylate monomer having a glass transition temperature of -140 to -20 ° C of a homopolymer and 50% by weight or less of another acrylic monomer. More than 10% by weight to 40% by weight or less of an acrylic copolymer obtained by copolymerizing 0.01 to 30 parts by weight of a functional monomer component, and less than 60% by weight of a vinyl chloride monomer or less than 90% by weight of a vinyl chloride monomer and other copolymerizable monomers. % To 100 parts by weight of a composite vinyl chloride resin having an average degree of polymerization of 400 to 2500 obtained by graft copolymerization with 3 to 30 parts by weight of a thermoplastic elastomer compatible with the composite vinyl chloride resin. BecomeObtained by melt-kneading vinyl chloride resin compositionCharacterized byVinyl chloride resin rehabilitation pipe.
(2)
A thermoplastic elastomer, wherein the thermoplastic elastomer contains one or more selected from the group consisting of acrylonitrile-butadiene copolymer, ethylene-vinyl acetate copolymer and ethylene-vinyl acetate-carbon monoxide copolymer 2. The method according to claim 1, whereinVinyl chloride resin rehabilitation pipe.
【０００５】
【課題を解決するための手段】
請求項１に記載の発明（以下、「本発明１」と記す）による塩化ビニル系樹脂更生管は、既設管中に挿入され、加熱されることにより該既設管の内面に密着させる更正管であって、単独重合体のガラス転移温度が−１４０〜−２０℃であるアルキル（メタ）アクリレートモノマー５０重量％以上及びその他のアクリル系モノマー５０重量％以下を含有してなるアクリル系モノマー成分１００重量部及び多官能性モノマー成分０．０１〜３０重量部を共重合したアクリル系共重合体１０重量％超４０重量％以下に、塩化ビニルモノマー又は塩化ビニルモノマー及びその他の共重合性モノマー９０重量％未満６０重量％以上をグラフト共重合してなる平均重合度４００〜２５００の複合塩化ビニル系樹脂１００重量部に対し、該複合塩化ビニル系樹脂と相溶し得る熱可塑性エラストマー３〜３０重量部が添加されてなる塩化ビニル系樹脂組成物を溶融混練して得られることを特徴とする。尚、ここで言う（メタ）アクリレートとはアクリレート又はメタクリレートを意味する。
[0005]
[Means for Solving the Problems]
The vinyl chloride-based resin rehabilitation pipe according to the invention of claim 1 (hereinafter referred to as “the present invention 1”) is a rehabilitation pipe that is inserted into an existing pipe and is brought into close contact with the inner surface of the existing pipe by being heated. And 100% by weight of an acrylic monomer component containing 50% by weight or more of an alkyl (meth) acrylate monomer having a glass transition temperature of -140 to -20 ° C of a homopolymer and 50% by weight or less of another acrylic monomer. Parts and more than 10% by weight of an acrylic copolymer obtained by copolymerizing 0.01 to 30 parts by weight of a polyfunctional monomer component and 40% by weight or less, and 90% by weight of a vinyl chloride monomer or a vinyl chloride monomer and other copolymerizable monomers. Less than 60% by weight or more is graft copolymerized, and 100 parts by weight of the composite vinyl chloride resin having an average degree of polymerization of 400 to 2500 is added to the composite vinyl chloride resin. Characterized in that it is obtained a thermoplastic elastomer 3 to 30 parts by weight, which are added the vinyl chloride resin composition capable of fat is compatible with melt-kneading. In addition, (meth) acrylate here means acrylate or methacrylate.
請求項２に記載の発明（以下、「本発明２」と記す）による塩化ビニル系樹脂更生管は、上記本発明１の塩化ビニル系樹脂更生管において、熱可塑性エラストマーが、アクリロニトリル−ブタジエン共重合体、エチレン−酢酸ビニル共重合体及びエチレン−酢酸ビニル−一酸化炭素共重合体からなる群より選択される１種もしくは２種以上を含有する熱可塑性エラストマーであることを特徴とする。
The invention of claim 2 (hereinafter, "the present invention 2" and referred) vinyl chloride by resin rehabilitating pipe, in vinyl chloride resin rehabilitating pipe of the present invention 1, a thermoplastic elastomer, acrylonitrile - butadiene copolymerization A thermoplastic elastomer containing one or more members selected from the group consisting of a copolymer, an ethylene-vinyl acetate copolymer and an ethylene-vinyl acetate-carbon monoxide copolymer.
【００７４】
【発明の効果】
以上述べたように、本発明の更生管は、上記記載の塩化ビニル系樹脂組成物からなるので、優れた機械的強度と耐衝撃性を高水準で兼備すると共に、施工性にも優れるものであり、既設管の更生（修復）用として好適に用いられる。
[0074]
【The invention's effect】
As described above, the rehabilitating pipe of the present invention, since the vinyl chloride resin compositions described above, as well as combine high levels of excellent mechanical strength and impact resistance, but also excellent in workability Yes, it is suitable for rehabilitating (restoring) existing pipes.