JP2001354858A - Curable composition and method for identifying the same - Google Patents
Curable composition and method for identifying the sameInfo
- Publication number
- JP2001354858A JP2001354858A JP2000175010A JP2000175010A JP2001354858A JP 2001354858 A JP2001354858 A JP 2001354858A JP 2000175010 A JP2000175010 A JP 2000175010A JP 2000175010 A JP2000175010 A JP 2000175010A JP 2001354858 A JP2001354858 A JP 2001354858A
- Authority
- JP
- Japan
- Prior art keywords
- curable composition
- indicator
- manufacturer
- identifying
- reaction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明が属する技術分野】本発明は、シーリング材や接
着剤、塗料等の識別機能を付与した硬化性組成物及びそ
の識別方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a curable composition provided with a discriminating function for a sealing material, an adhesive, a paint, and the like, and a method for discriminating the same.
【０００２】[0002]
【従来の技術】一般に、建築物等は、その設計段階にお
いて各部における使用材料やその製造メーカーが予め指
定されており、万一問題が発生した場合には、設計図面
や見積書を調べることにより、問題発生箇所の使用材料
や製造メーカーを特定して、責任の所在を明確にすると
ともに、原因究明とその対策を迅速に行えるようになさ
れている。また、例えば使用材料が施工途中で変更され
るなど、設計通りに施工が行われないことにより、所期
の特性が十分に得られない場合もあるので、原因究明時
には、現場検証を行って実際に使用している材料を検証
して、原因究明とその対策を講じている。2. Description of the Related Art In general, for a building or the like, the materials used in each part and the manufacturer of the building are specified in advance at the design stage, and in the event of a problem, by examining the design drawings and quotes, In addition to identifying the materials used and the manufacturer at the location where the problem occurs, the responsibility is clarified, and the cause of the problem and its countermeasures can be promptly determined. In addition, the expected characteristics may not be obtained sufficiently because the construction is not performed as designed, for example, when the material used is changed during construction. The materials used in the inspection are verified to determine the cause and take countermeasures.
【０００３】[0003]
【発明が解決しようとする課題】ところで、前述のよう
に、施工途中等において使用材料が変更された場合で
も、定形材料の場合には、その品番等に基づいて製造メ
ーカー等を特定することが可能であるが、例えばシーリ
ング材や接着剤、塗料等の硬化性組成物のような不定形
材料においては、容器に入っている段階では、容器の表
示から製造メーカーを特定できるものの、一旦使用され
ると、製造メーカーまでは容易には特定できず、万一漏
水や接着不良等の問題が発生した場合には、原因究明と
その対策が遅れるという問題があった。例えば、シーリ
ング材では、その主成分の素材（ポリマー）が同じであ
れば、各製造メーカーとも基本的な配合資材は似通って
おり、施工後における製造メーカーの判別は、現場にお
いて瞬時に判断することは困難で、赤外分光分析や元素
分析等の精密な機器分析等を行っても容易ではなかっ
た。However, as described above, even when the material used is changed during construction or the like, in the case of a fixed-form material, it is necessary to specify a manufacturer or the like based on the product number or the like. Although it is possible, in the case of amorphous materials such as curable compositions such as sealing materials, adhesives, and paints, the manufacturer can be identified from the label on the container when the container is in the container, but it is used once. Then, it is not easy to identify even the manufacturer, and if a problem such as water leakage or poor adhesion occurs, there is a problem that the investigation of the cause and the countermeasures are delayed. For example, in the case of sealing materials, if the main component (polymer) is the same, the basic compounding materials are similar for each manufacturer, and the determination of the manufacturer after construction should be made immediately on site. Is difficult, and it is not easy even if a precise instrumental analysis such as infrared spectroscopy or elemental analysis is performed.
【０００４】本発明の目的は、使用後においても製造メ
ーカー等を容易に特定可能な識別機能を付与した硬化性
組成物及びその識別方法を提供することである。[0004] It is an object of the present invention to provide a curable composition having an identification function capable of easily specifying a manufacturer or the like even after use, and a method for identifying the same.
【０００５】[0005]
【課題を解決するための手段及びその作用】本発明に係
る硬化性組成物は、識別機能を付与する指示薬を配合し
てなるものである。このような硬化性組成物において
は、それに配合した指示薬に基づいて硬化性組成物の製
造メーカーや組成等を特定することが可能となる。この
ため、この硬化性組成物を使用した建築物等において
は、施工後における建築物の検査時に、実際に使用され
ている硬化性組成物の硬化物に含まれる指示薬を調べる
ことで、設計通りの硬化性組成物が使用されているか否
を容易に検査できる。また、万一硬化性組成物を使用し
た部分に何らかの問題が発生した場合においても、実際
に使用されている硬化性組成物の硬化物に含まれる指示
薬を調べることで、設計通りの硬化性組成物が使用され
ているか否かを判別できるとともに、設計通りの硬化性
組成物が使用されていない場合でも、使用されている硬
化性組成物の製造メーカー等を特定して、問題発生の原
因究明や対策を迅速に行うことが可能となる。Means for Solving the Problems and Action Thereof The curable composition according to the present invention comprises an indicator for imparting a discriminating function. In such a curable composition, it is possible to specify a manufacturer, a composition, and the like of the curable composition based on an indicator blended therein. For this reason, in a building or the like using this curable composition, at the time of inspection of the building after construction, by examining the indicator contained in the cured product of the curable composition actually used, as designed. It can be easily inspected whether or not the curable composition is used. Also, in the event that any problem occurs in the part where the curable composition is used, by examining the indicator contained in the cured product of the curable composition actually used, the curable composition as designed It is possible to determine whether the product is used or not, and even when the curable composition as designed is not used, identify the manufacturer of the curable composition used and investigate the cause of the problem And measures can be taken promptly.
【０００６】指示薬としては、臭い成分を含むもの、蛍
光染顔料、炎色反応を呈する金属塩化合物、呈色反応を
呈する化合物、電気伝導を呈する導電性材料などを採用
するがことが可能である。臭い成分を含む場合には、硬
化性組成物の硬化物の臭いに基づいて、蛍光染顔料を含
む場合には、暗室にて紫外線ランプ（ブラックライト）
を近づけたときの蛍光色に基づいて、炎色反応を呈する
金属塩化合物である場合には、硬化性組成物の硬化物の
一部を切り取って燃やしたときの炎の色に基づいて、呈
色反応を呈する化合物である場合には、呈色反応試薬を
接触させたときにおける発色に基づいて、電気伝導を呈
する導電性材料からなる場合には、硬化性組成物の硬化
物の導電性を測定することで、製造メーカー等をそれぞ
れ特定することになる。As the indicator, it is possible to employ an indicator containing an odor component, a fluorescent dye / pigment, a metal salt compound exhibiting a flame reaction, a compound exhibiting a color reaction, a conductive material exhibiting electric conduction, and the like. . In the case of containing an odor component, based on the odor of the cured product of the curable composition, and in the case of containing a fluorescent dye, an ultraviolet lamp (black light) in a dark room
In the case of a metal salt compound exhibiting a flame reaction based on the fluorescent color when approached, is based on the color of the flame when a part of the cured product of the curable composition is cut and burned. In the case of a compound that exhibits a color reaction, based on the color development when the color reaction reagent is brought into contact, if it is made of a conductive material that exhibits electrical conduction, the conductivity of the cured product of the curable composition is determined. By the measurement, the manufacturer and the like are specified.
【０００７】本発明に係る硬化性組成物の識別方法は、
指示薬を配合してなる硬化性組成物を建築物の必要箇所
に使用し、建築物の施工後に硬化性組成物の硬化物に含
まれる指示薬に基づいて使用されている硬化性組成物を
識別するものである。識別方法においては、硬化性組成
物の硬化物に配合されている指示薬に基づいて、建築物
に使用されている硬化性組成物を特定することが可能と
なり、施工後における建築物の検査時に、設計通りの硬
化性組成物が使用されているか否を容易に検査でき、ま
た漏水等の問題発生時には、使用されている硬化性組成
物の製造メーカー等を特定して、問題発生の原因究明や
対策を迅速に行うことが可能となる。硬化性組成物とし
ては、前述した硬化性組成物を好適に利用できる。The method for identifying a curable composition according to the present invention comprises:
A curable composition containing an indicator is used in a necessary part of a building, and after the construction of the building, the curable composition used based on the indicator contained in the cured product of the curable composition is identified. Things. In the identification method, it is possible to specify the curable composition used in the building based on the indicator that is blended in the cured product of the curable composition, and when inspecting the building after construction, Whether the curable composition as designed is used can be easily inspected, and when a problem such as water leakage occurs, the manufacturer of the curable composition used is specified, and the cause of the problem can be investigated. Measures can be taken promptly. As the curable composition, the aforementioned curable composition can be suitably used.
【０００８】[0008]
【発明の実施の形態】以下、本発明の実施の形態につい
て説明する。本発明に係る硬化性組成物は、識別機能を
付与する指示薬を硬化性組成物に配合してなるものであ
る。硬化性組成物とは、シーリング材や接着剤、塗料な
どのように、施工時には液状やゲル状を呈するが、施工
後には乾燥や化学反応などにより硬化するものの総称
で、本発明では、特に建築材料として使用されるシーリ
ング材を例示する。シーリング材としては、変成シリコ
ーン系、ポリウレタン系、ポリサルファイド系、ポリイ
ソブチレン系、シリコーン系あるいはアクリル系など周
知のシーリング材に適用できる。Embodiments of the present invention will be described below. The curable composition according to the present invention is obtained by blending an indicator imparting an identification function into the curable composition. The curable composition is a general term for a material such as a sealing material, an adhesive, or a paint that exhibits a liquid or gel state at the time of construction, but is cured by drying or a chemical reaction after the construction. An example of a sealing material used as a material will be described. Well-known sealing materials such as modified silicone, polyurethane, polysulfide, polyisobutylene, silicone and acrylic can be used as the sealing material.
【０００９】指示薬は、それに基づいて硬化性組成物の
製造メーカーや組成等を特定するため、臭いや味などの
特性、分光特性、炎色反応や呈色反応などの化学的特
性、導電率や誘電率などの電気的特性の一種又は２種以
上で構成されている。具体的には、臭い成分を含むも
の、蛍光染顔料、炎色反応を呈する金属塩化合物、呈色
反応を呈する化合物、導電性材料などを好適に採用でき
る。The indicator specifies the maker and composition of the curable composition based on the indicator. Therefore, characteristics such as odor and taste, spectral characteristics, chemical characteristics such as flame reaction and color reaction, conductivity, It is composed of one or more of electrical characteristics such as a dielectric constant. Specifically, those containing an odor component, fluorescent dyes and pigments, metal salt compounds exhibiting a flame reaction, compounds exhibiting a color reaction, and conductive materials can be suitably used.
【００１０】また、指示薬としては、硬化性組成物と反
応せず、硬化性組成物の本来の特性を阻害しないものを
採用することになる。また、簡単な検査方法により製造
メーカー等を特定できること、容易に識別できること、
硬化後においてもその特性を維持できること、などの特
性を有する素材を選定することが好ましい。更に、指示
薬の配合割合は、多すぎると硬化性組成物の特性を低下
させ、少なすぎると指示薬としての識別機能を果たさな
くなるので、指示薬による識別機能が十分に得られる範
囲で、極力少ない配合量に設定することが好ましい。
尚、指示薬は、粉末状や液状のものを直接的に硬化性組
成物に混合してもよいし、硬化性組成物との化学反応等
を極力防止するため、マイクロカプセル等に充填したも
のを混合してもよい。[0010] As the indicator, one that does not react with the curable composition and does not inhibit the original properties of the curable composition is used. In addition, the manufacturer and the like can be specified by a simple inspection method, it can be easily identified,
It is preferable to select a material having such characteristics that the characteristics can be maintained even after curing. Furthermore, if the compounding ratio of the indicator is too large, the properties of the curable composition are deteriorated, and if it is too small, the discriminating function as the indicator is not fulfilled. It is preferable to set
The indicator may be a powdery or liquid one directly mixed with the curable composition, or a filler filled in microcapsules or the like to minimize a chemical reaction with the curable composition. You may mix.
【００１１】指示薬として、臭い成分を含むものを使用
する場合には、硬化性組成物の臭いから製造メーカー等
を特定化し、識別することになる。臭いの種類は任意に
設定できるが、不快な臭いを放つものは避けることが好
ましい。また、液状のものを使用してもよいし、固形の
ものを使用してもよい。このような臭い成分を含む指示
薬を用いると、臭いを嗅ぐだけで硬化性組成物の製造メ
ーカー等をその場で容易に識別することができるので好
ましい。When an indicator containing an odor component is used as the indicator, a manufacturer or the like is specified and identified from the odor of the curable composition. The type of odor can be set arbitrarily, but it is preferable to avoid those that emit an unpleasant odor. Moreover, a liquid thing may be used and a solid thing may be used. It is preferable to use an indicator containing such an odor component, because the manufacturer of the curable composition can be easily identified on the spot simply by smelling the odor.
【００１２】指示薬として、蛍光染顔料を含むものを使
用する場合には、暗室にて紫外線ランプ（ブラックライ
ト）を近づけたときの蛍光色により、製造メーカー等を
特定することになる。蛍光染顔料としては、任意の組成
からなる蛍光増白剤或いは集光性蛍光染料を採用でき
る。蛍光増白剤は、ブラックライトに近づけることによ
り青紫〜青緑色などに発光し、集光性蛍光染料はレッ
ド、オレンジ、バイオレットなどのいずれかに発光す
る。尚、硬化性組成物が塗料の場合には、指示薬の配合
により塗料の色が微妙に変化することが考えられるの
で、蛍光染顔料を指示薬として使用しないことが好まし
い。When an indicator containing a fluorescent dye or pigment is used as an indicator, a manufacturer or the like is specified by a fluorescent color when an ultraviolet lamp (black light) is approached in a dark room. As the fluorescent dye / pigment, a fluorescent brightener or a condensing fluorescent dye having an arbitrary composition can be employed. The fluorescent whitening agent emits light in blue-violet to blue-green or the like by approaching black light, and the light-collecting fluorescent dye emits light in any of red, orange, violet, and the like. In the case where the curable composition is a paint, it is considered that the color of the paint may slightly change due to the blending of the indicator. Therefore, it is preferable not to use a fluorescent dye or pigment as the indicator.
【００１３】指示薬として、炎色反応を呈する金属塩化
合物を使用する場合には、硬化性組成物を燃やしたとき
の炎の色により、製造メーカー等を特定することにな
る。炎色反応を呈する金属塩化合物としては、リチウ
ム、ナトリウム、カリウム、ルビジウム、セシウム、カ
ルシウム、ストロンチウム、バリウム、銅、インジウム
などの金属塩が知られているが、安全面や入手容易性な
どから銅塩化合物を採用することが好ましい。このよう
な炎色反応を呈する指示薬を用いると、検査器具等を用
いることなく、容易に識別することが可能となるので好
ましい。When a metal salt compound exhibiting a flame reaction is used as an indicator, a manufacturer or the like is specified by the color of the flame when the curable composition is burned. As metal salt compounds exhibiting a flame reaction, metal salts such as lithium, sodium, potassium, rubidium, cesium, calcium, strontium, barium, copper, and indium are known. It is preferable to employ a salt compound. It is preferable to use an indicator exhibiting such a flame reaction because it can be easily identified without using an inspection instrument or the like.
【００１４】指示薬として、呈色反応を呈する化合物を
使用する場合には、呈色反応試薬を接触させたときにお
ける発色に基づいて、製造メーカー等を特定することに
なる。呈色反応を呈する化合物と反応試薬とは、錯生成
反応や酸化還元反応やジアゾ化合物と芳香核とのカップ
リングなどを生じて発色を示すものであれば、任意のも
のを採用できる。When a compound exhibiting a color reaction is used as the indicator, the manufacturer or the like is specified based on the color development when the color reaction reagent is brought into contact. As the compound exhibiting a color reaction and the reaction reagent, any compounds can be used as long as they exhibit color formation by causing a complex formation reaction, an oxidation-reduction reaction, coupling between a diazo compound and an aromatic nucleus, and the like.
【００１５】指示薬として、電気伝導を呈する導電性材
料を使用する場合には、硬化性組成物の硬化物の導電性
を測定することで、製造メーカー等を特定することにな
る。導電性材料としては、アルミニウム、銅、鉄、ニッ
ケルなどの周知の金属材料或いは炭素を採用できる。特
に、金属材料が、安価に入手可能なので好適である。When a conductive material exhibiting electric conductivity is used as the indicator, the manufacturer or the like is specified by measuring the conductivity of the cured product of the curable composition. As the conductive material, a known metal material such as aluminum, copper, iron, and nickel, or carbon can be used. In particular, metal materials are preferred because they are available at low cost.
【００１６】このような硬化性組成物は、例えば建築物
の各部に使用されるが、硬化後においても、指示薬によ
り硬化性組成物の製造メーカ等を特定できるので、施工
後における建築物の検査時に、設計通りの硬化性組成物
が使用されているか否を容易に検査できる。また、漏水
等の問題発生時においても、使用されている硬化性組成
物の製造メーカー等を特定して、問題発生の原因究明や
対策を迅速に行うことが可能となる。Such a curable composition is used, for example, in various parts of a building. However, even after curing, the manufacturer of the curable composition can be specified by an indicator. At times, it can be easily checked whether the curable composition as designed is used. In addition, even when a problem such as water leakage occurs, it is possible to identify the manufacturer of the curable composition being used and to quickly investigate the cause of the problem and take countermeasures.
【００１７】次に、指示薬を配合した実施例について説
明する。 １．臭い成分を含む指示薬の評価 硬化性組成物としてのシーリング材に指示薬としての臭
い成分（香料）を配合し、遊星式試験機を用いて一様に
なるまで混合してなる実施例１〜６のシーリング材を調
製する。シーリング材として、変成シリコーン系シーリ
ング材（ペンギンシール２５５０ＬＭ（サンスター技研
（株）製））を用い、香料として、エチルバニリン（宇
部興産（株）製）、エアーケム４７０（第１工業製薬
（株）製）、ケイ皮酸エチル（長谷川香料（株）製）の
３種類の香料を用い、シーリング材に対してそれぞれ
０．０３重量％配合した実施例１〜３と、０．３重量％
配合した実施例４〜６を調製した。また、比較例１とし
て、香料を配合していないものを硬化性組成物として用
いた。Next, an example in which an indicator is blended will be described. 1. Evaluation of Indicator Containing Odor Component An odor component (perfume) as an indicator was blended with a sealing material as a curable composition and mixed until uniform using a planetary tester. Prepare sealing material. As a sealing material, a modified silicone sealing material (Penguin Seal 2550LM (manufactured by Sunstar Giken Co., Ltd.)) is used, and as a fragrance, ethyl vanillin (manufactured by Ube Industries, Ltd.) and Airchem 470 (Daiichi Kogyo Seiyaku Co., Ltd.) Examples 1 to 3 in which 0.03% by weight was added to the sealing material using three kinds of fragrances, namely ethyl cinnamate (manufactured by Hasegawa Corporation) and 0.3% by weight.
Formulated Examples 4-6 were prepared. As Comparative Example 1, a composition containing no fragrance was used as a curable composition.
【００１８】そして、ポリエチレン製バックアップ材を
用いて作製した深さ１０ｍｍ、幅１０ｍｍの目地に、実
施例１〜６及び比較例１のシーリング材をそれぞれ充填
した後、２３℃、５０％ＲＨ下で７日間養生を行い、硬
化後、シーリング材を切断して、その切断面の臭いを嗅
いで、臭いにより実施例１〜６と比較例１との識別を行
った。その結果、香料の配合割合が０．３重量％の実施
例４〜６はいうまでもなく、香料の配合割合が０．０３
重量％の実施例１〜３についても、香料の臭いを確認す
ることができ、香料の入っていない比較例１とを容易に
識別できた。After filling the sealing materials of Examples 1 to 6 and Comparative Example 1 into joints having a depth of 10 mm and a width of 10 mm prepared by using a backup material made of polyethylene, the joints were kept at 23 ° C. and 50% RH. After curing for 7 days and curing, the sealing material was cut, and the odor of the cut surface was smelled. Examples 1 to 6 and Comparative Example 1 were distinguished by the odor. As a result, needless to say, Examples 4 to 6 in which the blending ratio of the fragrance was 0.3% by weight, the blending ratio of the fragrance was 0.03%.
Also in Examples 1 to 3 by weight, the odor of the fragrance could be confirmed, and it could be easily distinguished from Comparative Example 1 containing no fragrance.
【００１９】２．炎色反応を呈する指示薬の評価 硬化性組成物としての変成シリコーン系シーリング材
（ペンギンシール２５５０ＬＭ（サンスター技研（株）
製））に対して、指示薬としての塩化第二銅の粉体を
２，５，１０重量％になるように配合し、遊星式試験機
を用いて一様になるまで混合して、実施例７〜９のシー
リング材を調製した。比較例２として、塩化第二銅の粉
体を配合していない変成シリコーン系シーリング材（ペ
ンギンシール２５５０ＬＭ（サンスター技研（株）
製））を用いた。2. Evaluation of an indicator exhibiting a flame reaction A modified silicone-based sealing material as a curable composition (Penguin seal 2550LM (Sunstar Giken Co., Ltd.)
)) Was mixed with 2,5,10% by weight of cupric chloride as an indicator and mixed until uniform using a planetary tester. 7 to 9 sealing materials were prepared. As Comparative Example 2, a modified silicone-based sealing material containing no cupric chloride powder (Penguin Seal 2550LM (Sunstar Giken Co., Ltd.)
Manufactured)).
【００２０】そして、ポリエチレン製バックアップ材を
用いて作製した深さ２ｍｍ、幅３０ｍｍの目地に、実施
例７〜９及び比較例２のシーリング材をそれぞれ充填し
た後、２３℃、５０％ＲＨ下で７日間養生を行い、硬化
後、シーリング材を切断して、シーリング材をガスバー
ナーもしくはライターの炎に近づけて、シーリング材を
燃焼させて、炎色反応による実施例７〜９と比較例２と
の識別を行った。その結果、塩化第二銅を含む実施例７
〜９はいずれの割合の場合についても、オレンジ色の炎
の中に銅特有の緑色が混じるが、塩化第二銅が含まれて
いない比較例２の炎はオレンジ色のみであり、炎色によ
り両者を容易に識別できた。Then, after filling the sealing materials of Examples 7 to 9 and Comparative Example 2 into joints having a depth of 2 mm and a width of 30 mm prepared using a backup material made of polyethylene, respectively, at 23 ° C. and 50% RH. After curing for 7 days, after curing, the sealing material was cut off, the sealing material was brought close to the flame of a gas burner or lighter, the sealing material was burned, and Examples 7 to 9 and Comparative Example 2 by flame reaction were performed. Was identified. As a result, Example 7 containing cupric chloride
In each of the cases of Nos. 9 to 9, the green color peculiar to copper is mixed in the orange flame, but the flame of Comparative Example 2 containing no cupric chloride is only orange, and Both could be easily identified.
【００２１】３．蛍光染顔料を用いた指示薬の評価 蛍光増白剤として、クマリン系蛍光増白剤 Whitefluor
Ｂ（住友化学工業（株）製）、オキサゾール系蛍光増
白剤 Whitefluor PSN conc （住友化学工業（株）
製）、クマリン系蛍光増白剤 ケイコールＥ（日本曹達
（株）製）、ピラゾリン系蛍光増白剤 ケイコールＣ
（日本曹達（株）製）、蛍光増白剤 Kayalight Ｂ
（日本化薬（株）製）を、トルエンに対して１：９９の
割合でそれぞれ混合し、５種類の蛍光増白剤１％溶液を
調製した。3. Evaluation of indicator using fluorescent dye / pigment As a fluorescent whitening agent, coumarin-based fluorescent whitening agent Whitefluor
B (Sumitomo Chemical Co., Ltd.), oxazole-based fluorescent whitening agent Whitefluor PSN conc (Sumitomo Chemical Co., Ltd.)
Co., Ltd.), Coumarin-based fluorescent whitening agent Keikoru E (manufactured by Nippon Soda Co., Ltd.), pyrazoline-based fluorescent whitening agent Keikoru C
(Manufactured by Nippon Soda Co., Ltd.), Kayalight B optical brightener
(Manufactured by Nippon Kayaku Co., Ltd.) were mixed with toluene at a ratio of 1:99, respectively, to prepare five types of 1% solutions of fluorescent whitening agents.
【００２２】そして、１００重量部の変成シリコーン系
シーリング材（ペンギンシール２５５０ＬＭ（サンスタ
ー技研（株）製））に対して、前記蛍光増白剤１％溶液
を１重量部の配合し、蛍光増白剤０．０１重量％の配合
物を遊星式試験機を用いて一様になるまで混合した実施
例１０〜１４のシーリング材と、蛍光増白剤１％溶液を
５重量部の配合し、蛍光増白剤０．０５重量％の配合物
を遊星式試験機を用いて一様になるまで混合した実施例
１５〜１９のシーリング材とを調製した。比較例３とし
て、蛍光増白剤を配合していない変成シリコーン系シー
リング材（ペンギンシール２５５０ＬＭ（サンスター技
研（株）製））を用いた。Then, 1 part by weight of the above-mentioned 1% solution of the fluorescent whitening agent was added to 100 parts by weight of the modified silicone-based sealing material (Penguin Seal 2550LM (manufactured by Sunstar Giken Co., Ltd.)) to give A sealant of Examples 10 to 14 in which a blend of 0.01% by weight of a whitening agent was mixed using a planetary tester until uniformity was mixed with 5 parts by weight of a 1% solution of an optical brightener, The sealing materials of Examples 15 to 19 were prepared by mixing a blend of 0.05% by weight of the optical brightener using a planetary tester until the blend was uniform. As Comparative Example 3, a modified silicone-based sealing material (Penguin Seal 2550LM (manufactured by Sunstar Giken Co., Ltd.)) containing no fluorescent whitening agent was used.
【００２３】そして、ポリエチレン製バックアップ材を
用いて作製した深さ１０ｍｍ、幅１０ｍｍの目地に、実
施例１０〜１９及び比較例３のシーリング材をそれぞれ
充填した後、２３℃、５０％ＲＨ下で７日間養生を行
い、硬化後、暗室にてシーリング材表面に紫外線ランプ
（ブラックライト）を近づけて、実施例１０〜１９と比
較例３との識別を行った。その結果、実施例１０〜１９
は蛍光を発するのに対して、比較例３は発光せず両者を
容易に識別できた。After filling the sealing materials of Examples 10 to 19 and Comparative Example 3 into joints having a depth of 10 mm and a width of 10 mm produced using a backup material made of polyethylene, the joints were each stored at 23 ° C. and 50% RH. After curing for 7 days and curing, an ultraviolet lamp (black light) was approached to the surface of the sealing material in a dark room to discriminate Examples 10 to 19 from Comparative Example 3. As a result, Examples 10-19
Emits fluorescence, whereas Comparative Example 3 does not emit light, and both can be easily identified.
【００２４】[0024]
【発明の効果】本発明に係る硬化性組成物及びその識別
方法によれば、硬化性組成物に対して識別機能を付与す
る指示薬を配合しているので、施工後における建築物の
検査時に、実際に使用されている硬化性組成物の硬化物
を調べることで、設計通りの硬化性組成物が使用されて
いるか否を容易に検査できる。また、万一この硬化性組
成物を使用した部分に何らかの問題が発生した場合にお
いても、実際に使用されている硬化性組成物の硬化物を
調べることで、設計通りの硬化性組成物が使用されいる
か否かを判別できるとともに、設計通りの硬化性組成物
が使用されていない場合でも、使用されている硬化性組
成物の製造メーカー等を特定して、問題発生の原因究明
や対策を迅速に行うことが可能となる。According to the curable composition and the method for identifying the same according to the present invention, an indicator for imparting an identification function to the curable composition is blended. By checking the cured product of the curable composition actually used, it can be easily inspected whether the curable composition as designed is used. Also, even in the event that any problem occurs in the portion where the curable composition is used, the curable composition as designed can be used by examining the cured product of the curable composition actually used. In addition to being able to determine whether or not the curable composition as designed is not used, identify the manufacturer of the curable composition used, and quickly investigate the cause of the problem and take countermeasures. Can be performed.
【００２５】指示薬が臭い成分を含む場合、指示薬が炎
色反応を呈する金属塩化合物である場合、指示薬が蛍光
染顔料を含む場合、指示薬が呈色反応を呈する化合物で
ある場合、指示薬が電気伝導を呈する導電性材料からな
る場合には、大がかりな機械器具を用いることなく、手
軽に硬化性組成物を識別でき特定することが可能にな
る。When the indicator contains an odorous component, when the indicator is a metal salt compound exhibiting a flame color reaction, when the indicator contains a fluorescent dye / pigment, when the indicator is a compound exhibiting a color reaction, the indicator is electrically conductive. In the case where the curable composition is made of a conductive material, the curable composition can be easily identified and specified without using a large-scale mechanical device.
フロントページの続き Ｆターム(参考） 4H017 AA04 AB15 AC01 AC07 AC10 AC18 AD05 AD06 AE03 4J002 BB181 BG001 CK021 CN021 CP031 DA078 DA088 DA098 DD057 DD067 DD077 ED059 EH129 FD096 FD118 FD209 GJ02 Continued on the front page F term (reference) 4H017 AA04 AB15 AC01 AC07 AC10 AC18 AD05 AD06 AE03 4J002 BB181 BG001 CK021 CN021 CP031 DA078 DA088 DA098 DD057 DD067 DD077 ED059 EH129 FD096 FD118 FD209 GJ02
Claims (7)
る硬化性組成物。1. A curable composition containing an indicator for imparting an identification function.
載の硬化性組成物。2. The curable composition according to claim 1, wherein the indicator is an odor component.
又は２記載の硬化性組成物。3. The method according to claim 1, wherein the indicator is a fluorescent dye or pigment.
Or the curable composition according to 2.
合物である請求項１〜３のいずれか１項記載の硬化性組
成物。4. The curable composition according to claim 1, wherein the indicator is a metal salt compound exhibiting a flame reaction.
ある請求項１〜４のいずれか１項記載の硬化性組成物。5. The curable composition according to claim 1, wherein the indicator is a compound that exhibits a color reaction.
料である請求項１〜５のいずれか１項記載の硬化性組成
物。6. The curable composition according to claim 1, wherein the indicator is a conductive material exhibiting electric conductivity.
築物の必要箇所に使用し、建築物の施工後に硬化性組成
物の硬化物に含まれる指示薬に基づいて使用されている
硬化性組成物を識別することを特徴とする硬化性組成物
の識別方法。7. A curable composition containing an indicator is used in a required part of a building, and a curable composition is used based on an indicator contained in a cured product of the curable composition after construction of the building. A method for identifying a curable composition, comprising identifying the composition.