JP2001303156A - Ornament, and metallic material for ornament - Google Patents
Ornament, and metallic material for ornamentInfo
- Publication number
- JP2001303156A JP2001303156A JP2000120589A JP2000120589A JP2001303156A JP 2001303156 A JP2001303156 A JP 2001303156A JP 2000120589 A JP2000120589 A JP 2000120589A JP 2000120589 A JP2000120589 A JP 2000120589A JP 2001303156 A JP2001303156 A JP 2001303156A
- Authority
- JP
- Japan
- Prior art keywords
- less
- metal material
- group
- decorative
- main component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、装飾品及び装飾品
用金属材料に関し、例えばナイフ、フォーク、スプーン
等に適用することができる。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to decorative articles and metal materials for decorative articles, and can be applied to, for example, knives, forks, spoons and the like.
【０００２】[0002]
【従来の技術】従来の装飾品用金属材料として、金合金
及びプラチナ合金などが使用されることがある。そのう
ち、銀白色を呈するものには、主にＫ１４、Ｋ１８、ホ
ワイトゴールド、９０％若しくは９５％プラチナ（Ｐ
ｔ）とパラジウム（Ｐｄ）やコバルト（Ｃｏ）等を合金
にしたものがある。ここでいう装飾品とは、何かを加え
ることによって、その物を実質以上に美しくした物をい
い、例えば、装飾品としてのナイフ、フォーク、スプー
ン等が挙げられる。2. Description of the Related Art As a conventional metal material for decorative articles, a gold alloy, a platinum alloy and the like are sometimes used. Among them, those exhibiting silver white are mainly K14, K18, white gold, 90% or 95% platinum (P
t) and an alloy of palladium (Pd), cobalt (Co), or the like. Here, the decorative article refers to an article that is made more beautiful by adding something, and examples thereof include a knife, a fork, and a spoon.
【０００３】金やプラチナは材料単価が非常に高いもの
であり、プラチナを９０％以上含有し、他に白色系の色
を維持する貴金属を添加した材料も単価が非常に高いも
のとなる。そのため、これに代わる安価な白色系の装飾
品用金属材料として、銀が使用されることが多い。[0003] Gold and platinum have very high unit prices of materials, and materials containing 90% or more of platinum and added with a noble metal for maintaining a white color also have very high unit prices. Therefore, silver is often used as an inexpensive alternative metal material for white ornaments.
【０００４】[0004]
【発明が解決しようとする課題】しかしながら、銀から
なる装飾品は、金やプラチナに比べて耐蝕性が悪く、使
用していく間に酸化して黒ずんだ銀色になってしまうの
で、その黒ずみを除去するといった手入れが必要とな
り、金やプラチナ系の材料と比べて不便である。However, decorative articles made of silver have poor corrosion resistance compared to gold and platinum, and oxidize during use to become dark silver. It requires care such as removal, which is inconvenient compared to gold and platinum-based materials.
【０００５】また、耐蝕性の悪い点を補うために、銀か
らなる装飾品にロジウム等のメッキを施すことも考えら
れるが、比較的にメッキが剥がれやすく、メッキが剥が
れてしまうと上述したように表面が酸化して黒ずんだ銀
色になってしまう。従って、メッキを施した場合でもプ
ラチナに類似した銀白色を維持することは困難である。[0005] Further, in order to compensate for the poor corrosion resistance, it is conceivable to apply a plating of rhodium or the like to a decorative article made of silver. The surface oxidizes and becomes dark silver. Therefore, it is difficult to maintain silvery white similar to platinum even when plating is performed.
【０００６】本発明は上記のような事情を考慮してなさ
れたものであり、その目的は、従来に比して耐蝕性に優
れた金属材料からなる装飾品及び装飾品用金属材料を提
供することにある。The present invention has been made in view of the above circumstances, and an object of the present invention is to provide a decorative article made of a metal material having excellent corrosion resistance as compared with the related art and a metal material for the decorative article. It is in.
【０００７】[0007]
【課題を解決するための手段】上記課題を解決するた
め、本発明に係る装飾品は、Ａｇを主成分とし、Ｐｄを
０．１ｗｔ％以上５．０ｗｔ％以下含有し、Ａｌ、Ａ
ｕ、Ｐｔ、Ｃｕ、Ｔａ、Ｃｒ、Ｔｉ、Ｃｏ、Ｓｉからな
る群から選ばれた１又は複数の元素を合計で０．１ｗｔ
％以上５．０ｗｔ％以下含有する金属材料からなること
を特徴とする。Means for Solving the Problems In order to solve the above-mentioned problems, the decorative article according to the present invention contains Ag as a main component, contains Pd in an amount of 0.1 wt% to 5.0 wt%, and contains Al, A
u, Pt, Cu, Ta, Cr, Ti, Co, and one or more elements selected from the group consisting of Si in a total amount of 0.1 wt.
% Or more and 5.0 wt% or less.
【０００８】上記装飾品によれば、Ａｇを主成分とし、
Ｐｄを含有し、且つ、Ａｌ、Ａｕ、Ｐｔ、Ｃｕ、Ｔａ、
Ｃｒ、Ｔｉ、Ｃｏ、Ｓｉからなる群から選ばれた１又は
複数の元素を所定量含有するため、従来の銀からなる装
飾品に比べて耐蝕性を向上させることができる。[0008] According to the decorative article, Ag is a main component,
Containing Pd, and Al, Au, Pt, Cu, Ta,
Since one or more elements selected from the group consisting of Cr, Ti, Co, and Si are contained in a predetermined amount, the corrosion resistance can be improved as compared with a conventional decorative article made of silver.
【０００９】また、本発明に係る装飾品は、Ａｇを主成
分とし、Ｉｒを０．１ｗｔ％以上５．０ｗｔ％以下含有
し、Ｃｕ、Ａｌ、Ｔｉからなる群から選ばれた１又は複
数の元素を合計で０．１ｗｔ％以上５．０ｗｔ％以下含
有する金属材料からなることを特徴とする。[0009] The decorative article according to the present invention contains Ag as a main component, contains Ir in an amount of 0.1 wt% or more and 5.0 wt% or less, and has at least one selected from the group consisting of Cu, Al and Ti. It is characterized by comprising a metal material containing a total of 0.1 wt% or more and 5.0 wt% or less of elements.
【００１０】また、本発明に係る装飾品は、Ａｇを主成
分とし、Ｐｔを０．１ｗｔ％以上５．０ｗｔ％以下含有
し、Ｃｕ、Ａｌ、Ｔｉからなる群から選ばれた１又は複
数の元素を合計で０．１ｗｔ％以上５．０ｗｔ％以下含
有する金属材料からなることを特徴とする。[0010] The decorative article according to the present invention contains Ag as a main component, contains Pt in a range of 0.1 wt% to 5.0 wt%, and one or more selected from the group consisting of Cu, Al, and Ti. It is characterized by comprising a metal material containing a total of 0.1 wt% or more and 5.0 wt% or less of elements.
【００１１】また、本発明に係る装飾品は、Ａｇを主成
分とし、Ｒｕを０．１ｗｔ％以上５．０ｗｔ％以下含有
し、Ｃｕ、Ａｌ、Ｔｉからなる群から選ばれた１又は複
数の元素を合計で０．１ｗｔ％以上５．０ｗｔ％以下含
有する金属材料からなることを特徴とする。Further, the decorative article according to the present invention contains Ag as a main component, contains 0.1 wt% or more and 5.0 wt% or less of Ru, and has at least one selected from the group consisting of Cu, Al and Ti. It is characterized by comprising a metal material containing a total of 0.1 wt% or more and 5.0 wt% or less of elements.
【００１２】また、本発明に係る装飾品は、Ａｇを主成
分とし、Ｒｈを０．１ｗｔ％以上５．０ｗｔ％以下含有
し、Ｃｕ、Ａｌ、Ｔｉからなる群から選ばれた１又は複
数の元素を合計で０．１ｗｔ％以上５．０ｗｔ％以下含
有する金属材料からなることを特徴とする。Further, the decorative article according to the present invention contains one or more selected from the group consisting of Cu, Al and Ti, containing Ag as a main component, containing 0.1 wt% or more and 5.0 wt% or less of Rh. It is characterized by comprising a metal material containing a total of 0.1 wt% or more and 5.0 wt% or less of elements.
【００１３】本発明に係る装飾品用金属材料は、Ａｇを
主成分とした装飾品用金属材料であって、Ｐｄを０．１
ｗｔ％以上５．０ｗｔ％以下含有し、Ａｌ、Ａｕ、Ｐ
ｔ、Ｃｕ、Ｔａ、Ｃｒ、Ｔｉ、Ｃｏ、Ｓｉからなる群か
ら選ばれた１又は複数の元素を合計で０．１ｗｔ％以上
５．０ｗｔ％以下含有することを特徴とする。The decorative metal material according to the present invention is a decorative metal material containing Ag as a main component and having a Pd of 0.1.
wt% to 5.0wt%, Al, Au, P
It is characterized in that one or more elements selected from the group consisting of t, Cu, Ta, Cr, Ti, Co, and Si are contained in a total amount of 0.1 wt% or more and 5.0 wt% or less.
【００１４】また、本発明に係る装飾品用金属材料は、
Ａｇを主成分とした装飾品用金属材料であって、Ｉｒを
０．１ｗｔ％以上５．０ｗｔ％以下含有し、Ｃｕ、Ａ
ｌ、Ｔｉからなる群から選ばれた１又は複数の元素を合
計で０．１ｗｔ％以上５．０ｗｔ％以下含有することを
特徴とする。Further, the metal material for decorative articles according to the present invention comprises:
A decorative metal material containing Ag as a main component and containing Ir in an amount of 0.1 wt% or more and 5.0 wt% or less;
It is characterized in that one or more elements selected from the group consisting of l and Ti are contained in a total amount of 0.1 wt% or more and 5.0 wt% or less.
【００１５】また、本発明に係る装飾品用金属材料は、
Ａｇを主成分とした装飾品用金属材料であって、Ｐｔを
０．１ｗｔ％以上５．０ｗｔ％以下含有し、Ｃｕ、Ａ
ｌ、Ｔｉからなる群から選ばれた１又は複数の元素を合
計で０．１ｗｔ％以上５．０ｗｔ％以下含有することを
特徴とする。Further, the metal material for decorative articles according to the present invention comprises:
A metal material for decorative articles mainly composed of Ag, containing Pt in an amount of 0.1 wt% or more and 5.0 wt% or less, and containing Cu, A
It is characterized in that one or more elements selected from the group consisting of l and Ti are contained in a total amount of 0.1 wt% or more and 5.0 wt% or less.
【００１６】また、本発明に係る装飾品用金属材料は、
Ａｇを主成分とした装飾品用金属材料であって、Ｒｕを
０．１ｗｔ％以上５．０ｗｔ％以下含有し、Ｃｕ、Ａ
ｌ、Ｔｉからなる群から選ばれた１又は複数の元素を合
計で０．１ｗｔ％以上５．０ｗｔ％以下含有することを
特徴とする。Further, the metal material for decorative articles according to the present invention comprises:
A metal material for decorative articles containing Ag as a main component, containing 0.1 wt% or more and 5.0 wt% or less of Ru;
It is characterized in that one or more elements selected from the group consisting of l and Ti are contained in a total amount of 0.1 wt% or more and 5.0 wt% or less.
【００１７】また、本発明に係る装飾品用金属材料は、
Ａｇを主成分とした装飾品用金属材料であって、Ｒｈを
０．１ｗｔ％以上５．０ｗｔ％以下含有し、Ｃｕ、Ａ
ｌ、Ｔｉからなる群から選ばれた１又は複数の元素を合
計で０．１ｗｔ％以上５．０ｗｔ％以下含有することを
特徴とする。Further, the decorative metal material according to the present invention comprises:
A metal material for decorative articles containing Ag as a main component, containing 0.1 wt% or more and 5.0 wt% or less of Rh, Cu, A
It is characterized in that one or more elements selected from the group consisting of l and Ti are contained in a total amount of 0.1 wt% or more and 5.0 wt% or less.
【００１８】[0018]
【発明の実施の形態】以下、本発明の実施の形態につい
て説明する。第１の実施の形態による装飾品は、Ａｇを
主成分とし、Ｐｄを０．１重量％（ｗｔ％）以上５．０
ｗｔ％以下含有し、Ａｌ、Ａｕ、Ｐｔ、Ｃｕ、Ｔａ、Ｃ
ｒ、Ｔｉ、Ｃｏ、Ｓｉからなる群から選ばれた１又は複
数の元素を合計で０．１ｗｔ％以上５．０ｗｔ％以下含
有する金属材料から構成されている。Embodiments of the present invention will be described below. The decorative article according to the first embodiment has Ag as a main component and Pd in an amount of 0.1% by weight (wt%) or more to 5.0.
wt% or less, Al, Au, Pt, Cu, Ta, C
It is composed of a metal material containing a total of one or more elements selected from the group consisting of r, Ti, Co, and Si in a range of 0.1 wt% or more and 5.0 wt% or less.
【００１９】ここで、本発明は、各種の装飾品に適用す
ることが可能であり、具体的には、装飾品としてのナイ
フ、フォーク、スプーン、栓抜き、押ピン、アイストン
グ、アイスペール用取手、マドラー、ナプキンリング、
箸置き、文房具類、ペーパーウェート、ペーパーナイ
フ、ペンスタンド、筆記用具、カードスタンド等に適用
することが可能である。但し、これらの具体例は単なる
例示であり、本発明を他の装飾品に適用することも可能
である。以下、装飾品については同様である。Here, the present invention can be applied to various decorative articles, and specifically, for knives, forks, spoons, bottle openers, push pins, ice tongs, and ice pail as decorative articles. Handle, muddler, napkin ring,
The present invention can be applied to chopstick rests, stationery, paper weights, paper knives, pen stands, writing utensils, card stands, and the like. However, these specific examples are merely examples, and the present invention can be applied to other decorative articles. Hereinafter, the same applies to decorative articles.
【００２０】上記第１の実施の形態によれば、Ｐｄを含
有し、且つ、Ａｌ、Ａｕ、Ｐｔ、Ｃｕ、Ｔａ、Ｃｒ、Ｔ
ｉ、Ｃｏ、Ｓｉからなる群から選ばれた１又は複数の元
素を所定量含有するため、従来の銀からなる装飾品に比
べて耐蝕性を向上させることができる。また、この金属
材料は銀白色を有すると共に装飾品として使用可能な硬
度を有している。According to the first embodiment, Pd is contained and Al, Au, Pt, Cu, Ta, Cr, T
Since a predetermined amount of one or more elements selected from the group consisting of i, Co, and Si is contained, the corrosion resistance can be improved as compared with a conventional decorative article made of silver. This metal material has a silvery white color and a hardness that can be used as a decorative product.
【００２１】第２の実施の形態による装飾品は、Ａｇを
主成分とし、Ｉｒを０．１ｗｔ％以上５．０ｗｔ％以下
含有し、Ｃｕ、Ａｌ、Ｔｉからなる群から選ばれた１又
は複数の元素を合計で０．１ｗｔ％以上５．０ｗｔ％以
下含有する金属材料により構成されている。The decorative article according to the second embodiment contains Ag as a main component, contains Ir in an amount of 0.1 wt% to 5.0 wt%, and one or more selected from the group consisting of Cu, Al, and Ti. Is a metal material containing a total of 0.1 wt% or more and 5.0 wt% or less.
【００２２】上記第２の実施の形態においても第１の実
施の形態と同様の効果を得ることができる。すなわち、
この金属材料は従来の銀からなる装飾品に比べて耐蝕性
に優れ、また、銀白色を有すると共に装飾品として使用
可能な硬度を有している。The same effects as in the first embodiment can be obtained in the second embodiment. That is,
This metal material has better corrosion resistance than a conventional decorative article made of silver, has a silvery white color, and has a hardness that can be used as a decorative article.
【００２３】第３の実施の形態による装飾品は、Ａｇを
主成分とし、Ｐｔを０．１ｗｔ％以上５．０ｗｔ％以下
含有し、Ｃｕ、Ａｌ、Ｔｉからなる群から選ばれた１又
は複数の元素を合計で０．１ｗｔ％以上５．０ｗｔ％以
下含有する金属材料から構成されている。The decorative article according to the third embodiment contains Ag as a main component, contains Pt in a range of 0.1 wt% to 5.0 wt%, and has at least one selected from the group consisting of Cu, Al and Ti. Of a total of 0.1 wt% or more and 5.0 wt% or less.
【００２４】上記第３の実施の形態においても第１の実
施の形態と同様の効果を得ることができる。すなわち、
この金属材料は従来の銀からなる装飾品に比べて耐蝕性
に優れ、また、銀白色を有すると共に装飾品として使用
可能な硬度を有している。The same effects as in the first embodiment can be obtained in the third embodiment. That is,
This metal material has better corrosion resistance than a conventional decorative article made of silver, has a silvery white color, and has a hardness that can be used as a decorative article.
【００２５】第４の実施の形態による装飾品は、Ａｇを
主成分とし、Ｒｕを０．１ｗｔ％以上５．０ｗｔ％以下
含有し、Ｃｕ、Ａｌ、Ｔｉからなる群から選ばれた１又
は複数の元素を合計で０．１ｗｔ％以上５．０ｗｔ％以
下含有する金属材料から構成されている。The decorative article according to the fourth embodiment contains Ag as a main component, contains 0.1 wt% or more and 5.0 wt% or less of Ru, and has at least one selected from the group consisting of Cu, Al, and Ti. Of a total of 0.1 wt% or more and 5.0 wt% or less.
【００２６】上記第４の実施の形態においても第１の実
施の形態と同様の効果を得ることができる。すなわち、
この金属材料は従来の銀からなる装飾品に比べて耐蝕性
に優れ、また、銀白色を有すると共に装飾品として使用
可能な硬度を有している。The same effects as those of the first embodiment can be obtained in the fourth embodiment. That is,
This metal material has better corrosion resistance than a conventional decorative article made of silver, has a silvery white color, and has a hardness that can be used as a decorative article.
【００２７】第５の実施の形態による装飾品は、Ａｇを
主成分とし、Ｒｈを０．１ｗｔ％以上５．０ｗｔ％以下
含有し、Ｃｕ、Ａｌ、Ｔｉからなる群から選ばれた１又
は複数の元素を合計で０．１ｗｔ％以上５．０ｗｔ％以
下含有する金属材料から構成されている。The decorative article according to the fifth embodiment contains Ag as a main component, contains 0.1 wt% or more and 5.0 wt% or less of Rh, and one or more selected from the group consisting of Cu, Al, and Ti. Of a total of 0.1 wt% or more and 5.0 wt% or less.
【００２８】上記第５の実施の形態においても第１の実
施の形態と同様の効果を得ることができる。すなわち、
この金属材料は従来の銀からなる装飾品に比べて耐蝕性
に優れ、また、銀白色を有すると共に装飾品として使用
可能な硬度を有している。The same effects as those of the first embodiment can be obtained in the fifth embodiment. That is,
This metal material has better corrosion resistance than a conventional decorative article made of silver, has a silvery white color, and has a hardness that can be used as a decorative article.
【００２９】尚、本発明は上記実施の形態に限定され
ず、種々変更して実施することが可能である。The present invention is not limited to the above embodiment, but can be implemented with various modifications.
【００３０】[0030]
【発明の効果】以上説明したように本発明によれば、Ａ
ｇを主成分とし、Ｐｄを含有し、且つ、Ａｌ、Ａｕ、Ｐ
ｔ、Ｃｕ、Ｔａ、Ｃｒ、Ｔｉ、Ｃｏ、Ｓｉからなる群か
ら選ばれた１又は複数の元素を所定量含有する。したが
って、従来に比して耐蝕性に優れた金属材料からなる装
飾品及び装飾品用金属材料を提供することができる。As described above, according to the present invention, A
g as a main component, containing Pd, and Al, Au, P
Contains a predetermined amount of one or more elements selected from the group consisting of t, Cu, Ta, Cr, Ti, Co, and Si. Therefore, it is possible to provide a decorative article and a decorative metal material made of a metal material having excellent corrosion resistance as compared with the related art.
Claims (20)
ｉからなる群から選ばれた複数の元素を合計で０．１ｗ
ｔ％以上５．０ｗｔ％以下含有する金属材料からなるこ
とを特徴とする装飾品。1. An alloy containing Ag as a main component, Pd in an amount of 0.1 wt% or more and 5.0 wt% or less, Al, Au, Pt, Cu, Ta, Cr, Ti, Co, and S.
a total of 0.1 w of a plurality of elements selected from the group consisting of
A decorative article comprising a metal material containing t% or more and 5.0 wt% or less.
ｉからなる群から選ばれた１の元素を０．１ｗｔ％以上
５．０ｗｔ％以下含有する金属材料からなることを特徴
とする装飾品。2. An alloy containing Ag as a main component, Pd in an amount of 0.1 wt% or more and 5.0 wt% or less, and Al, Au, Pt, Cu, Ta, Cr, Ti, Co, and S.
A decorative article comprising a metal material containing 0.1 wt% or more and 5.0 wt% or less of one element selected from the group consisting of i.
合計で０．１ｗｔ％以上５．０ｗｔ％以下含有する金属
材料からなることを特徴とする装飾品。3. An alloy containing Ag as a main component, containing Ir in an amount of 0.1 wt% or more and 5.0 wt% or less, and a plurality of elements selected from the group consisting of Cu, Al, and Ti in a total amount of 0.1 wt% or more. A decorative article comprising a metal material containing not more than 0.0 wt%.
０．１ｗｔ％以上５．０ｗｔ％以下含有する金属材料か
らなることを特徴とする装飾品。4. An alloy containing Ag as a main component, containing Ir in an amount of 0.1 wt% or more and 5.0 wt% or less, and containing one element selected from the group consisting of Cu, Al, and Ti in an amount of 0.1 wt% or more and 5.0 wt%. %. A decorative article comprising a metallic material containing not more than 10%.
合計で０．１ｗｔ％以上５．０ｗｔ％以下含有する金属
材料からなることを特徴とする装飾品。5. An alloy containing Ag as a main component, Pt in an amount of 0.1 wt% or more and 5.0 wt% or less, and a plurality of elements selected from the group consisting of Cu, Al, and Ti in a total amount of 0.1 wt% or more. A decorative article comprising a metal material containing not more than 0.0 wt%.
０．１ｗｔ％以上５．０ｗｔ％以下含有する金属材料か
らなることを特徴とする装飾品。6. An alloy containing Ag as a main component, containing Pt in a range of 0.1 wt% to 5.0 wt%, and containing one element selected from the group consisting of Cu, Al, and Ti in a range of 0.1 wt% to 5.0 wt%. %. A decorative article comprising a metallic material containing not more than 10%.
合計で０．１ｗｔ％以上５．０ｗｔ％以下含有する金属
材料からなることを特徴とする装飾品。7. An alloy containing Ag as a main component, containing 0.1 wt% or more and 5.0 wt% or less of Ru, and a total of 0.1 wt% or more of a plurality of elements selected from the group consisting of Cu, Al, and Ti. A decorative article comprising a metal material containing not more than 0.0 wt%.
０．１ｗｔ％以上５．０ｗｔ％以下含有する金属材料か
らなることを特徴とする装飾品。8. An alloy containing Ag as a main component, containing 0.1 wt% or more and 5.0 wt% or less of Ru, and 0.1 wt% or more and 5.0 wt% of one element selected from the group consisting of Cu, Al, and Ti. %. A decorative article comprising a metallic material containing not more than 10%.
合計で０．１ｗｔ％以上５．０ｗｔ％以下含有する金属
材料からなることを特徴とする装飾品。9. An alloy containing Ag as a main component, containing 0.1 wt% or more and 5.0 wt% or less of Rh, and a total of 0.1 wt% or more of a plurality of elements selected from the group consisting of Cu, Al, and Ti. A decorative article comprising a metal material containing not more than 0.0 wt%.
０．１ｗｔ％以上５．０ｗｔ％以下含有する金属材料か
らなることを特徴とする装飾品。10. An alloy containing Ag as a main component, containing 0.1 wt% or more and 5.0 wt% or less of Rh, and 0.1 wt% or more and 5.0 wt% of one element selected from the group consisting of Cu, Al, and Ti. %. A decorative article comprising a metallic material containing not more than 10%.
であって、 Ｐｄを０．１ｗｔ％以上５．０ｗｔ％以下含有し、 Ａｌ、Ａｕ、Ｐｔ、Ｃｕ、Ｔａ、Ｃｒ、Ｔｉ、Ｃｏ、Ｓ
ｉからなる群から選ばれた複数の元素を合計で０．１ｗ
ｔ％以上５．０ｗｔ％以下含有することを特徴とする装
飾品用金属材料。11. A decorative metal material mainly containing Ag, containing Pd in an amount of 0.1 wt% or more and 5.0 wt% or less; Al, Au, Pt, Cu, Ta, Cr, Ti, and Co. , S
a total of 0.1 w of a plurality of elements selected from the group consisting of
A metal material for decorative articles, wherein the metal material contains at least t% and at most 5.0% by weight.
であって、 Ｐｄを０．１ｗｔ％以上５．０ｗｔ％以下含有し、 Ａｌ、Ａｕ、Ｐｔ、Ｃｕ、Ｔａ、Ｃｒ、Ｔｉ、Ｃｏ、Ｓ
ｉからなる群から選ばれた１の元素を０．１ｗｔ％以上
５．０ｗｔ％以下含有することを特徴とする装飾品用金
属材料。12. A decorative metal material mainly containing Ag, containing Pd in an amount of 0.1 wt% or more and 5.0 wt% or less, and containing Al, Au, Pt, Cu, Ta, Cr, Ti, and Co. , S
A metal material for decorative articles, comprising one element selected from the group consisting of i and 0.1 wt% or more and 5.0 wt% or less.
であって、 Ｉｒを０．１ｗｔ％以上５．０ｗｔ％以下含有し、 Ｃｕ、Ａｌ、Ｔｉからなる群から選ばれた複数の元素を
合計で０．１ｗｔ％以上５．０ｗｔ％以下含有すること
を特徴とする装飾品用金属材料。13. A metal material for decorative articles containing Ag as a main component, containing Ir in a range of 0.1 wt% to 5.0 wt%, and a plurality of elements selected from the group consisting of Cu, Al, and Ti. A total of 0.1 wt% or more and 5.0 wt% or less.
であって、 Ｉｒを０．１ｗｔ％以上５．０ｗｔ％以下含有し、 Ｃｕ、Ａｌ、Ｔｉからなる群から選ばれた１の元素を
０．１ｗｔ％以上５．０ｗｔ％以下含有することを特徴
とする装飾品用金属材料。14. A metal material for decorative articles containing Ag as a main component, containing Ir in an amount of 0.1 wt% or more and 5.0 wt% or less, and one element selected from the group consisting of Cu, Al, and Ti. A metal material for decorative articles, comprising 0.1 wt% or more and 5.0 wt% or less.
であって、 Ｐｔを０．１ｗｔ％以上５．０ｗｔ％以下含有し、 Ｃｕ、Ａｌ、Ｔｉからなる群から選ばれた複数の元素を
合計で０．１ｗｔ％以上５．０ｗｔ％以下含有すること
を特徴とする装飾品用金属材料。15. A metal material for decorative articles containing Ag as a main component, containing Pt in a range of 0.1 wt% or more and 5.0 wt% or less, and a plurality of elements selected from the group consisting of Cu, Al, and Ti. A total of 0.1 wt% or more and 5.0 wt% or less.
であって、 Ｐｔを０．１ｗｔ％以上５．０ｗｔ％以下含有し、 Ｃｕ、Ａｌ、Ｔｉからなる群から選ばれた１の元素を
０．１ｗｔ％以上５．０ｗｔ％以下含有することを特徴
とする装飾品用金属材料。16. A metal material for decorative articles containing Ag as a main component, containing Pt in a range of 0.1 wt% to 5.0 wt%, and one element selected from the group consisting of Cu, Al and Ti. A metal material for decorative articles, comprising 0.1 wt% or more and 5.0 wt% or less.
であって、 Ｒｕを０．１ｗｔ％以上５．０ｗｔ％以下含有し、 Ｃｕ、Ａｌ、Ｔｉからなる群から選ばれた複数の元素を
合計で０．１ｗｔ％以上５．０ｗｔ％以下含有すること
を特徴とする装飾品用金属材料。17. A decorative metal material containing Ag as a main component, containing 0.1 wt% to 5.0 wt% of Ru, and a plurality of elements selected from the group consisting of Cu, Al, and Ti. A total of 0.1 wt% or more and 5.0 wt% or less.
であって、 Ｒｕを０．１ｗｔ％以上５．０ｗｔ％以下含有し、 Ｃｕ、Ａｌ、Ｔｉからなる群から選ばれた１の元素を
０．１ｗｔ％以上５．０ｗｔ％以下含有することを特徴
とする装飾品用金属材料。18. A metal material for decorative articles containing Ag as a main component, containing at least 0.1 wt% and not more than 5.0 wt% of Ru, and one element selected from the group consisting of Cu, Al and Ti. A metal material for decorative articles, comprising 0.1 wt% or more and 5.0 wt% or less.
であって、 Ｒｈを０．１ｗｔ％以上５．０ｗｔ％以下含有し、 Ｃｕ、Ａｌ、Ｔｉからなる群から選ばれた複数の元素を
合計で０．１ｗｔ％以上５．０ｗｔ％以下含有すること
を特徴とする装飾品用金属材料。19. A metal material for decorative articles mainly composed of Ag, containing 0.1 wt% to 5.0 wt% of Rh, and a plurality of elements selected from the group consisting of Cu, Al, and Ti. A total of 0.1 wt% or more and 5.0 wt% or less.
であって、 Ｒｈを０．１ｗｔ％以上５．０ｗｔ％以下含有し、 Ｃｕ、Ａｌ、Ｔｉからなる群から選ばれた１の元素を
０．１ｗｔ％以上５．０ｗｔ％以下含有することを特徴
とする装飾品用金属材料。20. A metal material for decorative articles containing Ag as a main component, containing 0.1 wt% or more and 5.0 wt% or less of Rh, and one element selected from the group consisting of Cu, Al, and Ti. A metal material for decorative articles, comprising 0.1 wt% or more and 5.0 wt% or less.