JP2001294824A - Pressure sensitive adhesive tape for fixing articles - Google Patents
Pressure sensitive adhesive tape for fixing articlesInfo
- Publication number
- JP2001294824A JP2001294824A JP2000113434A JP2000113434A JP2001294824A JP 2001294824 A JP2001294824 A JP 2001294824A JP 2000113434 A JP2000113434 A JP 2000113434A JP 2000113434 A JP2000113434 A JP 2000113434A JP 2001294824 A JP2001294824 A JP 2001294824A
- Authority
- JP
- Japan
- Prior art keywords
- adhesive tape
- sensitive adhesive
- block copolymer
- isoprene block
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、例えば冷蔵庫のド
ア等を仮止めする際に用いられる、物品固定用粘着テー
プに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an adhesive tape for fixing an article, which is used, for example, for temporarily fixing a refrigerator door or the like.
【０００２】[0002]
【従来の技術】従来の物品固定用粘着テープは、粘着剤
層がアクリル系粘着剤又はゴム架橋系粘着剤により構成
されている。2. Description of the Related Art In a conventional adhesive tape for fixing an article, an adhesive layer is constituted by an acrylic adhesive or a rubber cross-linking adhesive.
【０００３】[0003]
【発明が解決しようとする課題】しかし、アクリル系粘
着剤は、家電製品の被着部分に対する接着性が高すぎ、
再剥離に際し被着体の印刷、塗装面をむしりとったり、
凝集破壊によりのり残り現象が生じるという問題があっ
た。他方、ゴム架橋系粘着剤は、凝集力を高めるにはか
なりの量の架橋剤添加が必要になり、結果的に被着体に
よっては汚染が生じやすいという欠点があった。However, acrylic pressure-sensitive adhesives have too high an adhesiveness to the parts to be adhered to home electric appliances,
When removing, printing on the adherend, peeling off the painted surface,
There is a problem that a cohesion failure causes a residue phenomenon. On the other hand, the rubber cross-linking type pressure-sensitive adhesive requires a considerable amount of a cross-linking agent to be added in order to increase the cohesive force, and as a result, there is a drawback that contamination tends to occur depending on the adherend.
【０００４】[0004]
【発明が解決しようとする課題】本発明は、常温におけ
る粘着物性に優れ、架橋剤の使用の有無にかかわらず、
十分な凝集力を保持するため、のり残り現象が生じ難い
物品固定用粘着テープを提供することを目的とする。DISCLOSURE OF THE INVENTION The present invention has excellent adhesive properties at room temperature, regardless of the use of a crosslinking agent.
An object of the present invention is to provide an article-fixing pressure-sensitive adhesive tape in which a residual phenomenon is unlikely to occur in order to maintain a sufficient cohesive force.
【０００５】[0005]
【課題を解決するための手段】本発明は、天然ゴム及び
／又はポリイソプレンゴムと水添スチレン−イソプレン
ブロック共重合体とをエラストマー成分として含有する
粘着剤層が設けられている物品固定用粘着テープに関す
る（１）。SUMMARY OF THE INVENTION The present invention provides an adhesive for fixing an article provided with an adhesive layer containing a natural rubber and / or a polyisoprene rubber and a hydrogenated styrene-isoprene block copolymer as an elastomer component. (1) related to tape.
【０００６】また、本発明は、エラストマー成分として
更にスチレン−イソプレンブロック共重合体を含有す
る、前記物品固定用粘着テープ（１）に関する（２）。The present invention also relates to (2) the pressure-sensitive adhesive tape for fixing articles, which further comprises a styrene-isoprene block copolymer as an elastomer component.
【０００７】更に、本発明は、エラストマー成分の全重
量を基準として、２０〜９０重量％が天然ゴム及び／又
はポリイソプレンゴムであり、５〜７０重量％が水添ス
チレン−イソプレンブロック共重合体であり、５〜５０
重量％がスチレン−イソプレンブロック共重合体であ
る、前記物品固定用粘着テープ（２）に関する（３）。Further, the present invention relates to a rubber composition comprising 20 to 90% by weight of natural rubber and / or polyisoprene rubber, and 5 to 70% by weight of hydrogenated styrene-isoprene block copolymer based on the total weight of the elastomer component. And 5 to 50
(3) The pressure-sensitive adhesive tape (2) for fixing articles, wherein the weight% is a styrene-isoprene block copolymer.
【０００８】また、本発明は、粘着剤層が、エラストマ
ー成分１００重量部に対し、粘着付与樹脂１０〜１５０
重量部を含有する、前記物品固定用粘着テープ（１）〜
（３）に関する（４）。In the present invention, the pressure-sensitive adhesive layer may contain 10 to 150 tackifier resins per 100 parts by weight of the elastomer component.
The above-mentioned pressure-sensitive adhesive tape for fixing articles, which contains parts by weight.
(4) concerning (3).
【０００９】更に、本発明は、天然ゴム及び／又はポリ
イソプレンゴムと水添スチレン−イソプレンブロック共
重合体とをエラストマー成分として含有する粘着剤組成
物に関する（５）。Further, the present invention relates to a pressure-sensitive adhesive composition containing a natural rubber and / or a polyisoprene rubber and a hydrogenated styrene-isoprene block copolymer as an elastomer component (5).
【００１０】また、本発明は、スチレン−イソプレンブ
ロック共重合体を含有する、前記粘着剤組成物（５）に
関する（６）。The present invention also relates to (6) the pressure-sensitive adhesive composition (5) containing a styrene-isoprene block copolymer.
【００１１】[0011]
【発明の実施の態様】本発明に係る「天然ゴム」とは、
天然シス−１，４−ポリイソプレンを主成分としている
ものであり、市販されているものがいずれも使用可能で
ある。なお、２本ロールのゴム練りロールかバンバリー
ミキサー等を用いての素練りにより、ムーニー粘度を５
０〜８０にしたものを用いるのが好ましい。なお、本明
細書における「ムーニー粘度」とは、ＪＩＳ Ｋ６３０
０（未加硫ゴム物理試験方法）に従い測定されたものを
いう。また、天然ゴムを変性させたものを用いてもよ
く、例えば、メチルメタクリレートやスチレン等をグラ
フト変性したものや、塩素や無水マレイン酸を付加した
もの、エポキシ変性したもの等が挙げられる。BEST MODE FOR CARRYING OUT THE INVENTION The "natural rubber" according to the present invention is
It is mainly composed of natural cis-1,4-polyisoprene, and any commercially available one can be used. The Mooney viscosity was reduced to 5 by mastication using a two-roll rubber kneading roll or a Banbury mixer.
It is preferable to use a value between 0 and 80. In this specification, “Mooney viscosity” refers to JIS K630.
0 (measured according to the unvulcanized rubber physical test method). Further, those obtained by modifying natural rubber may be used, and examples thereof include those obtained by graft modification of methyl methacrylate or styrene, those added with chlorine or maleic anhydride, and those modified by epoxy.
【００１２】本発明に係る「ポリイソプレンゴム」と
は、天然ゴムと同様の化学構造を有するものであり、通
常５０００００〜２００００００程度の数平均分子量を
有するものが好ましくは用いられる。また、ムーニー粘
度が５０〜８０であるものを用いるのがより好ましい。
商品としては、ＪＳＲ製のＩＲ２２００や日本ゼオン社
製のニポールＩＲ−２２００が挙げられる。The "polyisoprene rubber" according to the present invention has a chemical structure similar to that of natural rubber, and usually has a number average molecular weight of about 5,000,000 to 2,000,000. Further, it is more preferable to use one having a Mooney viscosity of 50 to 80.
Commercial products include IR2200 manufactured by JSR and Nipol IR-2200 manufactured by Zeon Corporation.
【００１３】また、天然ゴムとポリイソプレンゴムは、
それぞれ単独でも、混合して用いてもよい。Further, natural rubber and polyisoprene rubber are
Each of them may be used alone or in combination.
【００１４】本発明に係る「水添スチレン−イソプレン
ブロック共重合体」としては、好ましくは、スチレン含
量が１０〜３０重量％であり、メルトインデックス（Ｊ
ＩＳＫ７２１０準拠、２００℃、１０kg荷重）が０〜１
００ｇ／１０分のものである。市販品としては、クラレ
社製のセプトン２００２、２００３、２０２３、２０６
３、２００５が挙げられる。The "hydrogenated styrene-isoprene block copolymer" according to the present invention preferably has a styrene content of 10 to 30% by weight and a melt index (J).
0-1 based on ISK7210, 200 ° C, 10kg load)
00 g / 10 min. Commercially available products include Septon 2002, 2003, 2023, and 206 manufactured by Kuraray.
3, 2005.
【００１５】本発明に係る「スチレン−イソプレンブロ
ック共重合体」としては、特に限定されないが、スチレ
ン含量が１０〜３０重量％であり、メルトインデックス
（ＪＩＳ Ｋ７２１０準拠、２００℃、５kg荷重）が１
〜２０ｇ／１０分であるものが好ましい。市販品として
は、例えば、シェル化学社製クレイトンＤ−１１０７、
日本ゼオン社製のクインタック３６２０、３５２０、３
４６０が挙げられる。The “styrene-isoprene block copolymer” according to the present invention is not particularly limited, but has a styrene content of 10 to 30% by weight and a melt index (according to JIS K7210, 200 ° C., 5 kg load) of 1%.
It is preferably 20 g / 10 min. Commercially available products include, for example, Clayton D-1107 manufactured by Shell Chemical Company,
Zeon Co., Ltd. Quintac 3620, 3520, 3
460.
【００１６】本発明に係る「粘着付与樹脂」は、特に限
定されないが、ロジン系、テルペン系、石油系、スチレ
ン系、フェノール系、各種の水添樹脂等が挙げられる。The "tackifying resin" according to the present invention is not particularly limited, and examples thereof include rosin-based, terpene-based, petroleum-based, styrene-based, phenol-based and various hydrogenated resins.
【００１７】その他、各種添加剤、例えば、老化防止剤
（フェノール系、アミン系、ベンズイミダゾール系
等）、紫外線吸収剤（ベンゾフェノン系、トリアゾール
系等）、凝集力付与のための架橋剤（チウラム系、フェ
ノール系等を被着体を強く汚染しない範囲の量で）、充
填剤（シリカ等）を使用してもよい。また、用途によっ
ては、変性ゴム、液状ゴム、液状樹脂、オイル等を添加
してもよい。In addition, various additives such as antioxidants (phenol-based, amine-based, benzimidazole-based, etc.), ultraviolet absorbers (benzophenone-based, triazole-based, etc.), crosslinking agents for imparting cohesive strength (thiuram-based) Phenols or the like in an amount that does not strongly contaminate the adherend) and a filler (silica or the like) may be used. Further, depending on the use, modified rubber, liquid rubber, liquid resin, oil, etc. may be added.
【００１８】本発明に係る「物品固定用粘着テープ」の
基材は、特に限定されず、従来の粘着テープの基材が使
用可能である。例えば、ポリエチレン、ポリエステル、
ポリプロピレン等のような合成樹脂フィルムが挙げられ
る。また、厚さに関しては、用途にもよるが、家電製品
のようなものを仮止めする際には、２０〜５０μm程度
であることが好ましい。The substrate of the "adhesive tape for fixing articles" according to the present invention is not particularly limited, and a conventional substrate of an adhesive tape can be used. For example, polyethylene, polyester,
Synthetic resin films such as polypropylene are exemplified. Further, the thickness is preferably about 20 to 50 μm when temporarily fixing a home electric appliance or the like, though it depends on the application.
【００１９】物品固定用粘着テープの製造方法は、従来
の粘着テープの製造方法と同様であり、例えばコンマコ
ーター、リバースロールコーター、リバースグラビヤコ
ーターなど均一に塗工できる塗工装置を用いて、基材上
に粘着剤組成物溶液を塗布し、その後溶媒を蒸発させ
る。なお、溶媒や溶解量に関しては、汎用の溶剤型粘着
剤の場合と同様であり、溶媒としては、例えば、トルエ
ン、ヘキサン、シクロヘキサン等の有機溶剤が挙げら
れ、溶解量は、通常１０〜３０重量％である。また、粘
着剤層の厚さは、好ましくは２０〜４０μmである。The method for producing the pressure-sensitive adhesive tape for fixing articles is the same as the conventional method for producing an adhesive tape. For example, using a coating apparatus such as a comma coater, a reverse roll coater, or a reverse gravure coater, which can apply uniformly, is used. The pressure-sensitive adhesive composition solution is applied onto the material, and then the solvent is evaporated. The solvent and the amount of dissolution are the same as in the case of a general-purpose solvent-type pressure-sensitive adhesive, and examples of the solvent include organic solvents such as toluene, hexane, and cyclohexane. %. The thickness of the pressure-sensitive adhesive layer is preferably 20 to 40 μm.
【００２０】本発明の「物品固定用粘着テープ」は、対
ＳＵＳ粘着力が３．０〜１０．０(N/１５mm）であるこ
とが好ましく、４．０〜７．０(N/１５mm）であること
がより好ましい。また、保持力は、０．３mm以下が好ま
しく、０．２mm以下がより好ましい。The "adhesive tape for fixing articles" of the present invention preferably has an adhesive strength to SUS of 3.0 to 10.0 (N / 15 mm), and 4.0 to 7.0 (N / 15 mm). Is more preferable. Further, the holding force is preferably 0.3 mm or less, and more preferably 0.2 mm or less.
【００２１】粘着力の測定：ＪＩＳ Ｚ−０２３７に記
載の方法に従って測定を実施した。なお以下の測定は特
に指定が無い限り２３℃６５％ＲＨの雰囲気で行った。
また、被着体は清浄な面を用いた。幅１５mmの粘着テー
プをＪＩＳで規定されている、ＳＵＳ３０４のステンレ
ス板に貼付し、ＪＩＳ Ｚ−０２３７記載の圧着条件に
従って圧着後、引き剥がし角度＝１８０°および速度＝
３００mm/minでの引き剥がし力（N/１５mm）を測定し
た。Measurement of Adhesion: Measurement was carried out according to the method described in JIS Z-0237. The following measurements were performed in an atmosphere at 23 ° C. and 65% RH unless otherwise specified.
The adherend had a clean surface. An adhesive tape having a width of 15 mm is affixed to a SUS304 stainless steel plate specified by JIS, and after being crimped according to the crimping conditions described in JIS Z-0237, a peeling angle = 180 ° and a speed =
The peeling force (N / 15 mm) at 300 mm / min was measured.
【００２２】保持力の測定：ガラス板に、貼付面積１２
mm×２０mmの粘着テープを貼付し、ローラー圧着後、試
料粘着テープの一端に荷重１kgをかけ、６０分後のテー
プ片のずれ距離を測定した。Measurement of holding force: affixed area 12 on glass plate
After applying an adhesive tape of mm × 20 mm and pressing the roller, a load of 1 kg was applied to one end of the sample adhesive tape, and the displacement distance of the tape piece after 60 minutes was measured.
【００２３】熱湿貼り跡試験：一般に電化製品で使用さ
れるアクリル樹脂塗料を用いた白色塗装板に試料粘着テ
ープを貼付して圧着後、４０℃×７５％ＲＨ雰囲気にて
２４時間放置したのち、常態雰囲気下に１時間放置し手
による剥離後の被着体の表面状態を目視にて評価した。 ○：貼り跡なし △：微小貼り跡確認 ×：貼り跡
ありHot-wet adhesion test: A sample adhesive tape was applied to a white painted plate using an acrylic resin paint generally used for electric appliances, pressed and then left standing at 40 ° C. × 75% RH for 24 hours. Then, the surface condition of the adherend after being left in a normal atmosphere for 1 hour and peeled by hand was visually evaluated. ○: No sticking mark △: Minor sticking mark confirmed ×: Sticking mark found
【００２４】コード仮止め試験：試験台にＳＵＳ３０４
板を固定し、針金で束ねた１６０ｇのビニルコードに対
して幅１９mmの粘着テープの貼付部分が上下になるよう
にＳＵＳ表面に仮止めした。これを４０℃雰囲気中で２
４時間放置したのち、常態雰囲気下に１時間放置し手に
よる剥離後のＳＵＳへののり残りを目視にて評価した。 ○：のり残りなし ×：のり残りあり（粘着剤の凝集破
壊）Code temporary fixing test: SUS304 on test table
The plate was fixed, and temporarily fixed to the SUS surface such that the portion to which a 19 mm-wide adhesive tape was attached to a 160 g vinyl cord bundled with wires was placed vertically. In an atmosphere of 40 ° C.
After leaving it for 4 hours, it was left for 1 hour in a normal atmosphere, and the residue on SUS after peeling by hand was visually evaluated. ○: No glue residue ×: Glue residue (cohesive failure of adhesive)
【００２５】[0025]
【実施例】実施例１ 帝人(株)製のＰＥＴ３８番〔商品名：ビューレックスＡ
１５〕を基材とする。天然ゴムをオープンロールで素練
りし、ムーニー粘度ＭＬ＝６０±２の素練りゴムを得
た。この素練りゴム５０部、水添スチレン−イソプレン
ブロック共重合体としてＳＥＰＳ〔商品名：セプトン
２０６３ クラレ製〕５０部、粘着付与樹脂として水添
脂肪族系石油樹脂〔商品名：マルカレッツＨ−９２５Ｃ
丸善石油製〕５０部、老化防止剤としてビスフェノール
系〔商品名：アンテージ Ｗ−５００〕２部を上記固形
分が１６％になるようトルエンに溶解し、これを粘着剤
とした。次に、この粘着剤を上記ＰＥＴフィルム上に、
乾燥後の厚さが３０μmになるように塗布し、１２０℃
で２分間加熱乾燥して、粘着テープを作製した。EXAMPLES Example 1 PET No. 38 manufactured by Teijin Limited [trade name: Burex A]
15] as a base material. Natural rubber was masticated with an open roll to obtain a masticated rubber having Mooney viscosity ML = 60 ± 2. 50 parts of this masticated rubber was used as a hydrogenated styrene-isoprene block copolymer as SEPS [trade name: Septon
2063 Kuraray] 50 parts, hydrogenated aliphatic petroleum resin [trade name: Marcarez H-925C] as tackifying resin
50 parts of Maruzen Petroleum Co., Ltd. and 2 parts of a bisphenol-based anti-aging agent (trade name: Antage W-500) were dissolved in toluene so that the solid content was 16%, and this was used as an adhesive. Next, this adhesive was placed on the PET film,
Apply so that the thickness after drying becomes 30 μm,
For 2 minutes to produce an adhesive tape.
【００２６】実施例２ 天然ゴムの配合部数を３０部、ＳＥＰＳを７０部にした
以外は、実施例１と同様にして粘着テープを作製した。 Example 2 An adhesive tape was produced in the same manner as in Example 1, except that the number of natural rubber was 30 parts and the SEPS was 70 parts.
【００２７】実施例３ 天然ゴムの配合部数を７０部、ＳＥＰＳを３０部にした
以外は、実施例１と同様にして粘着テープを作製した。 Example 3 An adhesive tape was produced in the same manner as in Example 1 except that the number of natural rubber was 70 parts and the SEPS was 30 parts.
【００２８】実施例４ 天然ゴムの配合部数を４５部、ＳＥＰＳを４５部にし、
スチレン−イソプレンブロック共重合体〔クレイトンＤ
−１１０７日本ゼオン製〕１０部を加えた以外は、実施
例１と同様にして粘着テープを作製した。 Example 4 The mixing ratio of natural rubber was 45 parts and SEPS was 45 parts.
Styrene-isoprene block copolymer [Clayton D
-1107 Nippon Zeon Co., Ltd.] was prepared in the same manner as in Example 1 except that 10 parts were added.
【００２９】実施例５ 天然ゴムの配合部数を３０部、ＳＥＰＳを２０部にし、
スチレン−イソプレンブロック共重合体５０部を加えた
以外は、実施例１と同様にして粘着テープを作製した。 Example 5 The compounding number of natural rubber was 30 parts and SEPS was 20 parts.
An adhesive tape was produced in the same manner as in Example 1 except that 50 parts of a styrene-isoprene block copolymer was added.
【００３０】比較例１ 天然ゴムの配合部数を１００部、ＳＥＰＳを除いた以外
は、実施例１と同様にして粘着テープを作製した。 Comparative Example 1 An adhesive tape was produced in the same manner as in Example 1 except that the number of natural rubber was 100 parts and SEPS was omitted.
【００３１】比較例２ ＳＥＰＳの配合部数を１００部、天然ゴムを除いた以外
は、実施例１と同様にして粘着テープを作製した。 Comparative Example 2 An adhesive tape was prepared in the same manner as in Example 1 except that the amount of SEPS was 100 parts and natural rubber was omitted.
【００３２】比較例３ 天然ゴムの配合部数を５０部、ＳＥＰＳの替わりにスチ
レン−イソプレンブロック共重合体５０部を加えた以外
は、実施例１と同様にして粘着テープを作製した。 Comparative Example 3 An adhesive tape was produced in the same manner as in Example 1 except that the blending number of natural rubber was 50 parts and 50 parts of a styrene-isoprene block copolymer was added instead of SEPS.
【００３３】[0033]
【表１】 [Table 1]
───────────────────────────────────────────────────── フロントページの続き (72)発明者 吉住 和彦 東京都文京区関口二丁目３番３号 ニチバ ン株式会社内 Ｆターム(参考） 4J004 AA04 AA05 AA06 AA07 AA12 AB01 CA04 CA06 CC02 DB01 EA01 FA08 4J040 BA201 BA202 CA011 CA012 CA091 CA092 DB031 DB032 DM011 DM012 DN031 DN032 DN071 DN072 EB021 EB022 JA01 JB09 KA23 KA26 MA02 MA10 MB03 NA06 NA12 NA19 ────────────────────────────────────────────────── ─── Continued on the front page (72) Inventor Kazuhiko Yoshizumi 2-3-3 Sekiguchi, Bunkyo-ku, Tokyo Nichiban Co., Ltd. F-term (reference) 4J004 AA04 AA05 AA06 AA07 AA12 AB01 CA04 CA06 CC02 DB01 EA01 FA08 4J040 BA201 BA202 CA011 CA012 CA091 CA092 DB031 DB032 DM011 DM012 DN031 DN032 DN071 DN072 EB021 EB022 JA01 JB09 KA23 KA26 MA02 MA10 MB03 NA06 NA12 NA19
Claims (6)
と水添スチレン−イソプレンブロック共重合体とをエラ
ストマー成分として含有する粘着剤層が設けられている
物品固定用粘着テープ。1. An article-fixing adhesive tape provided with an adhesive layer containing a natural rubber and / or a polyisoprene rubber and a hydrogenated styrene-isoprene block copolymer as an elastomer component.
イソプレンブロック共重合体を含有する、請求項１記載
の物品固定用粘着テープ。2. A styrene-elastomer as an elastomer component.
The pressure-sensitive adhesive tape for fixing an article according to claim 1, comprising an isoprene block copolymer.
て、２０〜９０重量％が天然ゴム及び／又はポリイソプ
レンゴムであり、５〜７０重量％が水添スチレン−イソ
プレンブロック共重合体であり、５〜５０重量％がスチ
レン−イソプレンブロック共重合体である、請求項２記
載の物品固定用粘着テープ。3. A rubber composition comprising 20 to 90% by weight of natural rubber and / or polyisoprene rubber, 5 to 70% by weight of hydrogenated styrene-isoprene block copolymer, based on the total weight of the elastomer component. The pressure-sensitive adhesive tape for fixing an article according to claim 2, wherein -50% by weight is a styrene-isoprene block copolymer.
量部に対し、粘着付与樹脂１０〜１５０重量部を含有す
る、請求項１〜３のいずれか一項記載の物品固定用粘着
テープ。4. The pressure-sensitive adhesive tape for fixing an article according to claim 1, wherein the pressure-sensitive adhesive layer contains 10 to 150 parts by weight of a tackifier resin based on 100 parts by weight of the elastomer component.
と水添スチレン−イソプレンブロック共重合体とをエラ
ストマー成分として含有する粘着剤組成物。5. An adhesive composition comprising a natural rubber and / or a polyisoprene rubber and a hydrogenated styrene-isoprene block copolymer as an elastomer component.
重合体を含有する、請求項５記載の粘着剤組成物。6. The pressure-sensitive adhesive composition according to claim 5, further comprising a styrene-isoprene block copolymer.