JP2001278171A - Bicycle crank - Google Patents
Bicycle crankInfo
- Publication number
- JP2001278171A JP2001278171A JP2001047779A JP2001047779A JP2001278171A JP 2001278171 A JP2001278171 A JP 2001278171A JP 2001047779 A JP2001047779 A JP 2001047779A JP 2001047779 A JP2001047779 A JP 2001047779A JP 2001278171 A JP2001278171 A JP 2001278171A
- Authority
- JP
- Japan
- Prior art keywords
- crank
- core
- casting
- mold
- core material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、自転車用クランク
に関する。特に内部に芯材を有した自転車用クランクを
鋳造により製造して軽量化した自転車用クランクに関す
るものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a bicycle crank. More particularly, the present invention relates to a bicycle crank which is manufactured by casting a bicycle crank having a core material therein to reduce its weight.
【０００２】[0002]
【従来の技術】自転車はできるだけ軽量化することが望
まれているが、そのためにすべての自転車用部品につい
ても可能な限り軽量化することが好ましい。そこで、自
転車用クランクについても、例えば、特公平２−１８６
５２号公報のように管を成形して製造し、クランク内部
を中空構造として軽量化したものが知られている。2. Description of the Related Art It is desired to reduce the weight of a bicycle as much as possible. For this purpose, it is preferable to reduce the weight of all bicycle parts as much as possible. Therefore, regarding bicycle cranks, for example, Japanese Patent Publication No. 2-186
As disclosed in Japanese Patent Application Publication No. 52-52, there has been known a method in which a pipe is formed and manufactured, and the inside of the crank is made hollow to reduce the weight.
【０００３】中実ブランクから押出し鍛造により内部に
空洞を形成する方法も提案されている（特開平５−１１
６６７０号公報）。この中空クランクは、パイプ又はク
ランク素材を溶接又は塑性変形により行うものであった
ので、クランク形状の設計の自由度が少ない。更に材料
力学上必要のない部分があっても成形ができない等の理
由から形状が制約される。更に、デザイン上からの要請
があっても、加工の制約から外見に高級感等を出しにく
い問題があった。A method has been proposed in which a cavity is formed inside a solid blank by extrusion forging (JP-A-5-11).
No. 6670). Since this hollow crank is formed by welding or plastically deforming a pipe or a crank material, the degree of freedom in designing the crank shape is small. Further, the shape is restricted because, for example, molding is not possible even if there is an unnecessary part in material mechanics. Furthermore, even if there is a request from the design, there is a problem in that it is difficult to give a high-grade appearance to the appearance due to processing restrictions.
【０００４】一方、自転車のクランクを軽合金で鋳造法
により製造する製造方法は知られている（例えば、特開
昭５８−９３５５４号公報）。鋳造法によれば、前記形
状の制約からは解放されるが内部を空洞化することは小
部品であるクランクでは困難であり、かつ機械的強度も
劣る。このため、内部にパイプ等を一体に鋳込んだもの
も提案されている（実開昭４８−７９４８号公報、実開
昭６１−１３１３９１号公報等）。しかしながら、鋳造
したものは一般に機械的強度が弱いといわれている。On the other hand, a manufacturing method for manufacturing a bicycle crank by a casting method using a light alloy is known (for example, Japanese Patent Application Laid-Open No. 58-93554). According to the casting method, the shape is released from the above-mentioned restrictions, but it is difficult to hollow the inside with a crank which is a small part, and the mechanical strength is also poor. For this reason, pipes or the like integrally cast therein have been proposed (Japanese Utility Model Laid-Open No. 48-7948, Japanese Utility Model Laid-Open No. 61-131391). However, it is generally said that a cast product has low mechanical strength.
【０００５】[0005]
【発明が解決しようとする課題】本発明は、以上のよう
な技術的背景で発明されたものであり、次の目的を達成
することにある。SUMMARY OF THE INVENTION The present invention has been made in view of the above technical background, and has as its object to achieve the following objects.
【０００６】本発明の目的は、鋳造により製造したので
設計の自由度の多い自転車用クランクを提供することに
ある。An object of the present invention is to provide a bicycle crank having a high degree of freedom in design because it is manufactured by casting.
【０００７】本発明の他の目的は、軽量化した鋳造によ
って製造された自転車用クランクを提供することにあ
る。Another object of the present invention is to provide a bicycle crank manufactured by lightweight casting.
【０００８】本発明の更に他の目的は、鋳造したクラン
ク素材を型鍛造したので、軽量化した上で十分な強度を
得ることができる自転車用クランクを提供することにあ
る。It is still another object of the present invention to provide a bicycle crank capable of obtaining sufficient strength while being light in weight, since a cast crank material is forged.
【０００９】[0009]
【課題を解決するための手段】本発明は、前記目的を達
成するために次の手段を採用する。The present invention employs the following means to achieve the above object.
【００１０】第１の本発明は、自転車用クランクであっ
て、前記クランクの鋳造により形成された母材金属より
比重が軽い中実の芯材を前記クランク内部に有し、前記
クランクの重さが前記クランクの前記母材金属の材料の
みで形成された形状のクランクよりも軽いことを特徴と
するものである。According to a first aspect of the present invention, there is provided a bicycle crank having a solid core material having a specific gravity lower than that of a base metal formed by casting the crank inside the crank. Is lighter than a crank having a shape formed of only the base metal material of the crank.
【００１１】第２の本発明は、第１の本発明の自転車用
クランクであって、前記芯材は、多孔質体からなるもの
である。この多孔質体は、内部に気孔、空洞、空間等を
有したもの、すなわち独立気泡を有するもの、気泡が連
続する連続気泡（気孔）を有し、鋳造に耐えうるような
耐熱性があり、機械的強度を備えたものであれれば良
い。According to a second aspect of the present invention, there is provided the bicycle crank according to the first aspect of the present invention, wherein the core is made of a porous material. This porous body has pores, cavities, spaces, etc. inside, that is, those having closed cells, continuous cells (pores) in which bubbles are continuous, and has heat resistance enough to withstand casting, Any material having mechanical strength may be used.
【００１２】第３の本発明は、第１の発明又は第２の発
明の自転車用クランクであって、前記芯材は火山ガラス
とからなることを特徴とする。A third aspect of the present invention is the bicycle crank according to the first or second aspect, wherein the core is made of volcanic glass.
【００１３】[0013]
【発明の実施の形態】［本発明の実施の形態１］本発明
の実施の形態１について図面を参照して説明する。図１
に本発明の左クランク１の背面図を示す。左クランク１
はアルミ合金で作られており、図１に示すように、ペダ
ルを取り付けるペダル軸端部４側が細く、クランク軸
（図示せず。）に取り付けるクランク軸端部２側が断面
が太くなるように形成されている。左クランク１の太さ
をこのように、位置により変化させることによって、断
面積の大きさを変えることにより左クランクに加わる応
力をどの断面においてもほぼ一定にするように強度設計
されている。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS [First Embodiment of the Present Invention] A first embodiment of the present invention will be described with reference to the drawings. FIG.
FIG. 1 shows a rear view of the left crank 1 of the present invention. Left crank 1
Is made of an aluminum alloy, and as shown in FIG. 1, the pedal shaft end portion 4 side to which the pedal is attached is thin, and the crank shaft end portion 2 side to be attached to the crankshaft (not shown) has a thicker cross section. Have been. By changing the thickness of the left crank 1 depending on the position as described above, the strength is designed so that the stress applied to the left crank is made substantially constant in any cross section by changing the size of the cross-sectional area.
【００１４】また、左クランク１の裏側両角部には面取
部１１（図２参照）が形成されている。左クランク１の
クランク軸端部２には、左クランク１をクランク軸に取
り付けるためのクランク軸取付穴５が形成されている。
このクランク軸取付穴５は、クランクを挿入することに
よって、クランク軸に左クランク１が取り付けられる。
また、左クランク１のペダル取付側のペダル軸端部４に
は、ペダル取付穴６が形成されている。このペダル取付
穴６にペダルのペダル軸（図示せず）の一端が取り付け
られる。A chamfered portion 11 (see FIG. 2) is formed at both corners on the rear side of the left crank 1. The crankshaft end 2 of the left crank 1 has a crankshaft mounting hole 5 for mounting the left crank 1 to the crankshaft.
The left crank 1 is mounted on the crankshaft by inserting a crank into the crankshaft mounting hole 5.
A pedal mounting hole 6 is formed in the pedal shaft end 4 of the left crank 1 on the pedal mounting side. One end of a pedal shaft (not shown) of the pedal is mounted in the pedal mounting hole 6.
【００１５】図２は、左クランク１の平面図である。図
３は、左クランク１を図１のIII−III線で切断したとき
の断面図である。クランク中央部３を中心にペダル軸端
部４側と、クランク軸端部２側に渡って芯材７が形成さ
れている。芯材（芯ともいう。）７は、左クランク１を
構成する金属より比重が軽く、加圧に耐えうるように圧
縮荷重に強いものであれば軽石等が良い。本例では、酸
化珪素、酸化アルミニウムを主成分とする火山ガラスを
発泡させた中空発泡体を用いた。FIG. 2 is a plan view of the left crank 1. FIG. FIG. 3 is a sectional view when the left crank 1 is cut along the line III-III in FIG. A core 7 is formed over the pedal shaft end 4 and the crank shaft end 2 with the crank center 3 as the center. The core material (also referred to as a core) 7 is preferably a pumice stone as long as it has a specific gravity lower than that of the metal constituting the left crank 1 and is strong against a compressive load so as to withstand pressurization. In this example, a hollow foam obtained by foaming volcanic glass containing silicon oxide and aluminum oxide as main components was used.
【００１６】図４は、左クランク１の正面図である。芯
材７の断面構造は、図５に示す。図５は、図４における
ａ−ａ，ｂ−ｂ，ｃ−ｃ，ｄ−ｄ切断線での各矢視断面
図である。図５（ａ）はａ−ａ矢視断面図、図５（ｂ）
はｂ−ｂ矢視断面図、図５（ｃ）はｃ−ｃ矢視断面図、
図５（ｄ）はｄ−ｄ矢視断面図である。クランク中央部
３の内部の芯材７により、軽量化が図られている。更
に、芯材７は、曲げ等の機械的応力に対しても一定の役
割を果たす。FIG. 4 is a front view of the left crank 1. The cross-sectional structure of the core 7 is shown in FIG. FIG. 5 is a cross-sectional view taken along arrows aa, bb, cc, and dd in FIG. 4. FIG. 5A is a sectional view taken along the line aa, and FIG.
FIG. 5C is a cross-sectional view taken along arrow cc, FIG.
FIG. 5D is a cross-sectional view taken along the line dd. The weight is reduced by the core material 7 inside the crank central portion 3. Further, the core 7 plays a certain role against mechanical stress such as bending.
【００１７】クランク中央部３の肉厚が実質的に同じに
なるように構成されている。芯材７の断面構造は、クラ
ンク軸端部２側では円を切断した半円形の形を成してい
る。ペダル軸端部４側では長方形の変形した扁平であ
る。芯材７の断面積は連続的に小さくなり、両端部では
厚さが最小になっている。すなわち、芯材７の形状は、
概略いわゆる船底型の形状を成している。The central portion 3 of the crank is configured to have substantially the same thickness. The cross-sectional structure of the core 7 has a semicircular shape obtained by cutting a circle on the crankshaft end 2 side. The side of the pedal shaft end 4 is rectangular and deformed flat. The cross-sectional area of the core 7 is continuously reduced, and the thickness is minimized at both ends. That is, the shape of the core 7 is
It has a so-called ship bottom shape.
【００１８】クランク軸端部２には、クランク軸取付穴
５が設けられている。クランク軸取付穴５の内面にはフ
ランジ８が内面側に突出して設けられ、そのフランジ８
の裏面側に連接して、雌のセレーション９が設けられて
いる。セレーション９は、図１に示すように本例は８歯
である。歯の数が少ないと、回転結合の結合強度が不足
し、歯の数が多すぎると、加工が困難でコスト上昇につ
ながり、組立時に回転方向の割り出し位置決め作業もミ
スが出易くなる。The crankshaft end 2 is provided with a crankshaft mounting hole 5. A flange 8 is provided on the inner surface of the crankshaft mounting hole 5 so as to protrude toward the inner surface.
A female serration 9 is provided in connection with the back side of the female serration. The serration 9 has eight teeth in this example as shown in FIG. If the number of teeth is small, the connection strength of the rotational connection is insufficient, and if the number of teeth is too large, machining is difficult and leads to an increase in cost, and errors are likely to occur in the indexing and positioning operation in the rotation direction during assembly.
【００１９】クランク軸取付穴５のセレーション９より
裏面側の部分は、テーパー孔である芯出し部１０（ガイ
ド部ともいう。）として構成されている。芯出し部１０
は、裏面側に広がる円筒のテーパ穴形状であり、本例で
はテーパ角は２〜３°に形成されている。芯出し部１０
のテーパ面は、クランク軸（図示せず。）の芯出し部１
０のテーパ面に密着させて両者の芯を正確に一致させる
と共に両者を一体に強力に連結する。The portion of the crankshaft mounting hole 5 on the back side from the serration 9 is formed as a centering portion 10 (also referred to as a guide portion) which is a tapered hole. Centering part 10
Is a cylindrical tapered hole shape spreading on the back surface side, and in this example, the taper angle is formed at 2 to 3 °. Centering part 10
Is a centering portion 1 of a crankshaft (not shown).
The two cores are brought into close contact with each other by being brought into close contact with the 0 tapered surface, and the two are integrally and strongly connected.
【００２０】［左クランク１の製造方法１］前記した左
クランク１は、次の製造方法により製造される。図６は
左クランク１の鋳造状態を示す鋳造金型の断面図であ
る。金型２０と金型２１との間に溶融金属を流し込む溶
融空間２２が金型２０と金型２１の中に区画されてい
る。溶融空間２２は、左クランク１とほぼ対応した形を
して区画された空間であるが、溶融金属の収縮を考慮し
て若干大きい。溶融空間２２には、芯材７が挿入配置さ
れている。[Method 1 of Manufacturing Left Crank 1] The left crank 1 described above is manufactured by the following method. FIG. 6 is a sectional view of a casting mold showing a casting state of the left crank 1. A molten space 22 into which the molten metal is poured between the mold 20 and the mold 21 is defined in the mold 20 and the mold 21. The melting space 22 is a space defined so as to substantially correspond to the left crank 1, but is slightly larger in consideration of shrinkage of the molten metal. The core material 7 is inserted and arranged in the melting space 22.
【００２１】芯材７は、発泡性の火山ガラスを焼いて作
ったものである。芯材７は、耐火物で作られた中子型３
０で焼いて作られる。図７は、中子型を示す斜軸投影図
である。中子型３０は、二つに分割された型で作られて
いる。中子型３０の内部には、芯材７に対応する内部空
間３１、及び注入口３２が形成されている。この注入口
３２から内部空間３１に砂状の火山ガラスを投入する。
火山ガラスを所定の圧力で付き固めた後、中子型３０と
共に焼結炉（図示せず）に投入し、火山ガラスが硬化す
る硬化温度まで昇温させる。The core 7 is made by baking foaming volcanic glass. The core 7 is a core 3 made of refractory.
It is made by baking at 0. FIG. 7 is an oblique axis projection view showing the core type. The core mold 30 is made of a mold divided into two. Inside the core mold 30, an internal space 31 corresponding to the core material 7 and an injection port 32 are formed. Sand-like volcanic glass is injected from the injection port 32 into the internal space 31.
After the volcanic glass is hardened with a predetermined pressure, it is put into a sintering furnace (not shown) together with the core mold 30, and the temperature is raised to a hardening temperature at which the volcanic glass hardens.
【００２２】この加熱により、火山ガラスが硬化した
後、中子型３０内の火山ガラスを硬化させて芯材７を作
る。芯材７が硬化すると、中子型３０を割って空間３１
の中から芯材７を取り出す。取り出した芯材７の注入口
３２の部分は、必要ないのでこの部分を切断する。After the volcanic glass is cured by this heating, the volcanic glass in the core mold 30 is cured to form the core material 7. When the core material 7 is hardened, the core mold 30 is broken and the space 31
Take out the core material 7 from the inside. Since the portion of the injection hole 32 of the removed core material 7 is unnecessary, this portion is cut.
【００２３】溶融空間２２は、金型２０、金型２１の間
に区画形成される。これを図６に示すように、常法によ
り溶融空間２２に位置決めする。溶融空間２２に芯材７
を正確に位置決めするために、発泡スチロール等で作ら
れたスペーサ２６で芯材７は位置決めされる。溶融空間
２２は、湯道２７を介して注湯口２８に連通されてい
る。The melting space 22 is defined between the mold 20 and the mold 21. This is positioned in the melting space 22 by a conventional method as shown in FIG. Core material 7 in melting space 22
The core 7 is positioned by a spacer 26 made of styrene foam or the like in order to accurately position the core material 7. The melting space 22 communicates with a pouring port 28 via a runner 27.
【００２４】溶融されたアルミ合金が注湯口２８から注
湯されて、湯道２７を通り溶融空間２２に入る。また、
溶融された金属は重力により溶融空間２２に圧力をかけ
る。この鋳造法は、溶融金属に圧力を加えずに重力のみ
の圧力を溶融空間２２に加圧するものであり、普通の鋳
込みを行う金型鋳造法、いわゆる重力金型鋳造と呼ばれ
ている鋳造方法である。The molten aluminum alloy is poured from a pouring port 28 and enters a melting space 22 through a runner 27. Also,
The molten metal applies pressure to the melting space 22 by gravity. In this casting method, a pressure of only gravity is applied to the molten space 22 without applying pressure to the molten metal, and a mold casting method for performing ordinary casting, a casting method called a so-called gravity mold casting. It is.
【００２５】鋳造後にクランク素材２９を金型２０、金
型２１から取り出す。しかしながら、鋳造のみでは内部
の金属組織に巣等が発生することがある。この鋳造後
に、芯材７をクランク素材２９内に入れた状態のまま型
鍛造を行う。型鍛造は、半密閉型鍛造用の半密閉金型３
５に載置して熱間鍛造する。After casting, the crank blank 29 is taken out of the mold 20 and the mold 21. However, cavities and the like may occur in the internal metal structure only by casting. After this casting, die forging is performed with the core 7 placed in the crank blank 29. Die forging is a semi-closed mold for semi-closed die forging.
5 and hot forged.
【００２６】図８は、下金型３６にクランク素材２９を
入れた状態を示す断面図である。下金型３６にクランク
素材２９を載置する。このクランク素材２９を所要温度
に加熱して下金型３６に載置した後、上金型３７により
加圧して鍛造加工を行う。この熱間鍛造により、鋳造さ
れたクランク素材２９は、長さ、厚さ、肉厚、表面が精
度良く加工され、クランク素材２９の材質が鍛錬され均
質化され機械強度も強化される。FIG. 8 is a sectional view showing a state where the crank blank 29 is put in the lower mold 36. The crank blank 29 is placed on the lower mold 36. After the crank blank 29 is heated to a required temperature and placed on the lower mold 36, the upper blank 37 is pressurized to perform forging. By this hot forging, the length, thickness, thickness, and surface of the cast crank material 29 are accurately processed, and the material of the crank material 29 is forged and homogenized to enhance the mechanical strength.
【００２７】この熱間鍛造による芯材７は、クランク素
材２９内に入れられた状態で鍛造されるので芯材７は潰
されることはなく芯材７の形状は確保される（図９参
照）。この後、図１から図５に示す左クランク１の形状
に、切削、研削、研磨等の機械加工をして完成させる。The core 7 formed by the hot forging is forged in a state of being placed in the crank blank 29, so that the core 7 is not crushed and the shape of the core 7 is secured (see FIG. 9). . Thereafter, the shape of the left crank 1 shown in FIGS. 1 to 5 is completed by machining such as cutting, grinding, and polishing.
【００２８】[0028]
【実施例】芯材７は次のものを用いた。EXAMPLE The following core material 7 was used.
【００２９】商品名：「テラバルーン」、株式会社カル
シード（千葉県市原市五井南海岸８番２号）製 成分（重量％）：ＳiＯ2（７７．３）、Ａｌ2Ｏ3（１
２．８）、Ｆｅ2Ｏ3()１．７）、ＣａＯ（１．０）、Ｍ
ｇＯ（０．１）、Ｎａ2Ｏ（３．２）、Ｋ2Ｏ（２．
９）、ＴｉＯ2（０．２）、その他（０．９） 粒度（μm）：９．４１（１０％）、２７．７１（５０
％）、７１．３２（９０％） 密度：軽装密度０．３０、重装密度（０．４６）、粒子
密度（１．１４） 耐熱温度（度Ｃ）：１,１００ ［その他の実施の形態］前記実施の形態では、芯材に火
山ガラスを用いていたが、天然の軽石、発泡石膏等のよ
うに母材の金属より比重が軽く、溶融金属に対する耐熱
性があり、かつ鍛造の圧力に耐えうる圧縮強度があるも
のであれば他の芯材料でも良い。また、発泡材は、内部
空間が独立した発泡体、または砥石の気孔のように内部
空間がつながっている連続気泡体などの何れでも良く、
これらを本発明では多孔質体という。Trade name: "Terra Balloon", Calseed Co., Ltd. (No. 8-2, Goi-minamikaigan, Ichihara-shi, Chiba) Ingredients (% by weight): SiO 2 (77.3), Al 2 O 3 (1
2.8), Fe 2 O 3 () 1.7), CaO (1.0), M
gO (0.1), Na 2 O (3.2), K 2 O (2.
9), TiO 2 (0.2), others (0.9) Particle size (μm): 9.41 (10%), 27.71 (50)
%), 71.32 (90%) Density: light packing density 0.30, heavy packing density (0.46), particle density (1.14) Heat resistance temperature (degree C): 1,100 [Other embodiments] In the above embodiment, volcanic glass was used as the core material, but the specific gravity is lower than that of the base metal, such as natural pumice, foamed gypsum, etc., and it has heat resistance to the molten metal, and the forging pressure is reduced. Other core materials may be used as long as they have a compressive strength that can withstand. In addition, the foam material may be any of a foam having an independent internal space, or an open-cell body in which the internal space is connected like pores of a grindstone,
These are referred to as porous bodies in the present invention.
【００３０】[0030]
【発明の効果】本発明のクランクは、クランク中芯に母
材金属より比重が軽いものを用いたのでクランクが軽量
になる。また、鋳造によりクランクを製造するので、形
状をどのようにでもデザインでき、設計の自由度が増え
るので、外観に高級感を出しやすい。The crank of the present invention has a lower specific gravity than that of the base metal, so that the weight of the crank is reduced. In addition, since the crank is manufactured by casting, the shape can be designed in any manner, and the degree of freedom of design is increased, so that it is easy to give a high-quality appearance to the appearance.
【００３１】また、鋳造したブランクを型鍛造したの
で、軽量化した上で十分な強度を得ることができる。更
に、内部に芯材を配置したので、型鍛造でも芯材の形状
が潰れることはない。Further, since the cast blank is die-forged, sufficient strength can be obtained while reducing the weight. Further, since the core material is disposed inside, the shape of the core material does not collapse even in die forging.
【図１】図１は、本発明の左クランク１の背面図であ
る。FIG. 1 is a rear view of a left crank 1 according to the present invention.
【図２】図２は、本発明の左クランク１の平面図であ
る。FIG. 2 is a plan view of the left crank 1 of the present invention.
【図３】図３は、左クランク１の側面から見た断面図で
ある。FIG. 3 is a cross-sectional view of the left crank 1 as seen from the side.
【図４】図４は、左クランク１の正面図である。FIG. 4 is a front view of the left crank 1. FIG.
【図５】図５は、図４におけるａ−ａ，ｂ−ｂ，ｃ−
ｃ，ｄ−ｄ切断線での各矢視断面図である。図５（ａ）
はａ−ａ矢視断面図、図５（ｂ）はｂ−ｂ矢視断面図、
図５（ｃ）はｃ−ｃ矢視断面図、図５（ｄ）はｄ−ｄ矢
視断面図である。FIG. 5 is a diagram showing aa, bb, and c- in FIG.
It is each arrow sectional drawing in a c, dd cutting line. FIG. 5 (a)
FIG. 5B is a cross-sectional view taken along the line bb, FIG.
FIG. 5C is a cross-sectional view taken along the line cc, and FIG. 5D is a cross-sectional view taken along the line dd.
【図６】図６は、左クランク１の鋳造状態を示す断面図
である。FIG. 6 is a sectional view showing a casting state of the left crank 1.
【図７】図７は、芯型を示す斜軸投影図である。FIG. 7 is an oblique axis projection view showing a core type.
【図８】図８は、半密閉金型３５にクランク素材２９を
入れた状態を示す断面図である。FIG. 8 is a cross-sectional view showing a state where the crank blank 29 is put in a semi-closed mold 35.
【図９】図９は、鍛造加工後のクランク素材２９を示す
図である。FIG. 9 is a view showing a crank blank 29 after forging.
１…左クランク ２…クランク軸端部 ３…クランク中央部 ４…ペダル軸端部 ５…クランク軸取付穴 ７…芯材 ２９…クランク素材 ３０…芯型 ３５…半密閉金型 DESCRIPTION OF SYMBOLS 1 ... Left crank 2 ... Crank shaft end part 3 ... Crank center part 4 ... Pedal shaft end part 5 ... Crank shaft mounting hole 7 ... Core material 29 ... Crank material 30 ... Core mold 35 ... Semi-sealed mold
Claims (3)
が軽い中実の芯材を前記クランク内部に有し、 前記クランクの重さが前記クランクの前記母材金属の材
料のみで形成された形状のクランクよりも軽いことを特
徴とする自転車用クランク。1. A crank for a bicycle, comprising a solid core material having a specific gravity lighter than a base metal formed by casting the crank inside the crank, wherein the weight of the crank is equal to the weight of the crank. A bicycle crank characterized by being lighter than a crank having a shape formed only of a base metal material.
あって、 前記芯材は、多孔質体からなることを特徴とする自転車
用クランク。2. The bicycle crank according to claim 1, wherein the core is made of a porous material.
ンクであって、 前記芯材は火山ガラスとからなることを特徴とする自転
車用クランク。3. The bicycle crank according to claim 1, wherein the core material is made of volcanic glass.