JP2001234697A - Bendable panel for formwork - Google Patents
Bendable panel for formworkInfo
- Publication number
- JP2001234697A JP2001234697A JP2000043730A JP2000043730A JP2001234697A JP 2001234697 A JP2001234697 A JP 2001234697A JP 2000043730 A JP2000043730 A JP 2000043730A JP 2000043730 A JP2000043730 A JP 2000043730A JP 2001234697 A JP2001234697 A JP 2001234697A
- Authority
- JP
- Japan
- Prior art keywords
- tunnel
- fabric
- formwork
- panel
- bending strength
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、下水道、導水路、
道路等のトンネル部の修繕工事に、モルタルやコンクリ
ートを被覆するときに用いる、型枠パネルに関する。TECHNICAL FIELD The present invention relates to a sewer, a headrace,
The present invention relates to a formwork panel used when covering mortar or concrete for repair work of a tunnel section such as a road.
【０００２】[0002]
【従来の技術】下水道、導水路、道路等のトンネル部
は、コンクリートやレンガ等で作られているが、年月の
経過とともに表層部の劣化が進行し、崩壊やコンクリー
トが剥落する危険性が増大する。従って、崩壊や剥落の
可能性が高いところでは、劣化部を除去し、コンクリー
トやモルタルで再被覆する修繕工事が行われている。2. Description of the Related Art Tunnels such as sewers, headraces, roads, etc. are made of concrete, brick, etc., but the deterioration of the surface layer progresses with the passage of time, and there is a risk of collapse and concrete falling off. Increase. Therefore, where there is a high possibility of collapse or peeling, repair work is performed to remove the deteriorated portion and re-cover with concrete or mortar.
【０００３】このコンクリートやモルタルを被覆する時
に、型枠を使用しない施工方法として吹付けやコテ塗り
がある。吹付け施工の場合、各部位により充填密度に差
が生じたり、天井部の付着が悪いこと、粉塵で作業環境
が悪いこと等の問題がある。また、コテ塗り施工の場合
は、作業効率に問題がある。[0003] When the concrete or mortar is coated, there are spraying and ironing as construction methods that do not use a mold. In the case of spraying, there are problems such as a difference in packing density depending on each part, poor adhesion of a ceiling portion, and a bad working environment due to dust. In the case of ironing, there is a problem in work efficiency.
【０００４】一方、型枠を用いる方法として、トンネル
の断面形状に対応するセントルを組み立て、セントルと
トンネル壁の間隙にコンクリートやモルタルを充填する
方法が行われている。しかしながら、トンネルには様々
な断面形状があるため、セントルをその都度トンネルの
形状にあわせて作らなければならず、更には充填物が硬
化後セントルを取り除く作業が必要であるため、工事規
模が小さい場合や被覆厚みが薄い場合は、経済的にも工
期面でもこの方法は効率の良い方法ではなかった。On the other hand, as a method using a formwork, a method of assembling a centur corresponding to the cross-sectional shape of a tunnel and filling concrete or mortar in a gap between the centur and the tunnel wall has been used. However, since the tunnel has various cross-sectional shapes, it is necessary to make the centrum in accordance with the shape of the tunnel each time, and furthermore, it is necessary to remove the centur after the filling is hardened, so the construction scale is small. In the case where the thickness of the coating is small, this method is not efficient in terms of cost and work period.
【０００５】[0005]
【発明が解決しようとする課題】本発明の目的は、上記
のような従来技術の問題点を解決し、吹付けやコテ塗り
作業をなくし、更にはセントルを設置することなく、迅
速にトンネル被覆を行うことができる技術を提供するこ
とにある。SUMMARY OF THE INVENTION It is an object of the present invention to solve the above-mentioned problems of the prior art, eliminate the need for spraying and ironing work, and quickly install a tunnel coating without installing a centrifuge. It is an object of the present invention to provide a technology capable of performing the above.
【０００６】[0006]
【課題を解決するための手段】本発明に従えば、上記の
目的を達成するものとして、曲げ強度が１５Ｎ／ｍｍ 2
以上のスレートボードの両面に高弾性繊維のファブリッ
クを貼り付け、湾曲可能にしたことを特徴とする型枠用
パネルが提供される。According to the present invention, the above-mentioned object is achieved.
To achieve the purpose, the bending strength is 15 N / mm Two
Fabrics of high-elastic fiber on both sides of the slate board
For formwork characterized by being able to bend and bendable
Panels are provided.
【０００７】[0007]
【発明の実施の形態】本発明のパネルは、湾曲し得ると
ともに高い曲げ強度と耐荷重性能を有するので、工事現
場において、直接、トンネルに合った形状に組み立て、
これを型枠としてトンネル壁との間隙にコンクリートや
モルタルを被覆するのに用いることができ、したがっ
て、吹付け作業やコテ塗り作業を行うことなく、また、
セントルの設置を必要とせずにトンネルの迅速な補修工
事が可能となる。DESCRIPTION OF THE PREFERRED EMBODIMENTS The panel of the present invention can be bent and has high bending strength and load-bearing performance.
This can be used as a formwork to cover the gap with the tunnel wall with concrete or mortar, and therefore without spraying or ironing,
Rapid repair work of tunnels is possible without the need for installation of a center.
【０００８】本発明は、国内外で製造され簡単に入手で
きるスレートボードを利用して上記のような機能を発揮
する型枠用パネルを実現させたものである。すなわち、
本発明の型枠用パネルは、薄いため軽いこと、製品自体
が無機質で比較的高い曲げ強度や耐溶剤性を有している
こと等により加工がし易いというスレートボードの特性
を活かしながら、該ボードの表裏両面にガラス繊維や炭
素繊維（カーボン繊維）のような高弾性繊維のファブリ
ックを貼り付けることにより、曲げ強度や耐荷重性能を
大幅に増加させた湾曲可能な新しいタイプのパネルであ
る。The present invention has realized a formwork panel that exhibits the above-described functions by using a slate board that is easily manufactured and manufactured in Japan and overseas. That is,
The formwork panel of the present invention is thin and light, and the product itself is inorganic and has relatively high bending strength and solvent resistance. This is a new type of bendable panel that has greatly increased bending strength and load-bearing performance by attaching a fabric of high elastic fiber such as glass fiber or carbon fiber (carbon fiber) to both sides of the board.
【０００９】現場で用いられる形式の型枠パネルは従来
からも幾つか提示されているが、それらはいずれも厚く
て重質な型枠パネルで構造物の一部を補強または代替す
る目的で使用されるものであり、薄くて軽いながら充分
な強度を有し湾曲できるようにしてトンネルのような構
造物の補修に使用されるようなものは見当たらない。例
えば、特願平８−５０１４８２には、コンクリート製パ
ネルにガラス繊維を埋め込み運搬可能にして現場で取り
付けられる型枠パネルが記載されているが、このパネル
は湾曲させて使うことは全く考慮されておらず、本発明
のようにスレートボードの両面にガラス繊維や炭素繊維
のような高弾性繊維のファブリックを貼り付け湾曲可能
とした技術とは全く異なるものである。Several formwork panels of the type used in the field have been proposed in the past, but all of them are thick and heavy formwork panels used to reinforce or replace part of the structure. There is no material that is thin and light, yet has sufficient strength and can be bent to be used for repairing a structure such as a tunnel. For example, Japanese Patent Application No. 8-501482 describes a formwork panel which can be transported by embedding glass fiber in a concrete panel and attached on site, but this panel is completely considered to be curved. However, this is completely different from the technique in which a high elastic fiber fabric such as glass fiber or carbon fiber is attached to both sides of a slate board and can be bent as in the present invention.
【００１０】本発明の型枠パネルは、一定の曲げ強度
（１５Ｎ／ｍｍ2）以上のスレートボードの表裏両面に
高弾性繊維（例えば、ガラス繊維や炭素繊維）のファブ
リックを貼り付けて得られるものであり、表面または裏
面の一方にそのようなファブリックを貼り付けてもトン
ネルの補修工事に用いられる湾曲可能な型枠パネルは得
られない。The formwork panel of the present invention is obtained by adhering a fabric of high elasticity fiber (for example, glass fiber or carbon fiber) on both sides of a slate board having a certain bending strength (15 N / mm 2 ) or more. Even if such a fabric is stuck to one of the front and back surfaces, a bendable formwork panel used for tunnel repair work cannot be obtained.
【００１１】スレートボードを、トンネルの形状に合わ
せるため湾曲させると、スレートボードの外側には引張
力が作用し内側には圧縮力が作用するので、組み立て時
には湾曲させるためにボード外側の補強が必要となり、
また、型枠組み立て後、間隙にコンクリートやモルタル
を充填するときには、内側に引張力が作用するため、内
側の補強も必要となるからである。When the slate board is curved to conform to the shape of the tunnel, a tensile force acts on the outside of the slate board and a compressive force acts on the inside, so that the outside of the board needs to be reinforced to bend during assembly. Becomes
Further, when the gap is filled with concrete or mortar after assembling the formwork, a tensile force acts on the inner side, so that the inner side also needs to be reinforced.
【００１２】本発明に用いるスレートボードは、加工上
１５Ｎ／ｍｍ2以上の曲げ強度が必要であり、ＪＩＳ
Ａ ５４３０に適合するフレキシブル板または軟質フレ
キシブル板が好ましいが、１５Ｎ／ｍｍ2以上の曲げ強
度があればＪＩＳ規格適合品に限定するわけではない。
スレートボードは３、４、５、６、８ｍｍの厚みのもの
がＪＩＳで規格化されているが、本発明に用いるボード
の厚みとしては３〜１０ｍｍのものが好ましい。The slate board used in the present invention requires a bending strength of 15 N / mm 2 or more in processing.
A flexible plate or a soft flexible plate conforming to A5430 is preferable, but a flexural strength of 15 N / mm 2 or more is not limited to a product conforming to the JIS standard.
Slate boards having a thickness of 3, 4, 5, 6, or 8 mm are standardized by JIS, and a board used in the present invention preferably has a thickness of 3 to 10 mm.
【００１３】スレートボードの厚みにより耐荷重やたわ
み量が異なる。すなわち薄いものはたわみ量が大きくな
るが耐荷重は低くなり、厚みが増すごとにたわみ量は小
さく、耐荷重は大きくなる。したがってトンネルの形状
や被覆厚みによってスレートボードの厚みを選択すれば
よいが、場合によってはパネルを重ね合わせて使用し、
耐荷重性をさらに高めることも可能である。The load resistance and the amount of deflection vary depending on the thickness of the slate board. That is, the thinner the larger the amount of deflection but the lower the load resistance, and the larger the thickness, the smaller the amount of deflection and the greater the load resistance. Therefore, the thickness of the slate board may be selected according to the shape of the tunnel and the thickness of the coating.
It is also possible to further increase the load resistance.
【００１４】スレートボードの幅および長さについても
ＪＩＳで規格化されており、９１０×１８２０および１
０００×２０００ｍｍが一般的であるが、本発明を実施
する上では、特に幅および長さについては制限しない。
すなわち、トンネルの形状によって大きめの型枠ボード
であれば切断して使用することも可能であり、または、
あらかじめトンネルの形状に合わせて切断したスレート
ボードに、補強用のファブリックを貼り付けたものを使
用できる。The width and length of the slate board are also standardized by JIS, and 910 × 1820 and 1
Although the size is generally 000 × 2000 mm, the width and length are not particularly limited in practicing the present invention.
That is, it is also possible to cut and use a large form board depending on the shape of the tunnel, or
A slate board cut in advance according to the shape of the tunnel and a reinforcing fabric attached to the slate board can be used.
【００１５】本発明の型枠パネルにおいて用いる高弾性
繊維のファブリック（fabric）とは、高弾性繊維を織
り、編み、または絡み合わせることにより作られた生地
状の二次元構造物であって、一般に７００００Ｎ／ｍｍ
2以上の弾性率を有するものを指称する。ファブリック
としては、具体的には、繊維が交差して目に見える大き
さの網目を形成したものや繊維が密に織製等されて畳地
やマット地程度に密集したようなシートも使用可能であ
る。ファブリックを構成する繊維密度が高ければ、パネ
ルの補強効果は大きくなるが経済的に不利になるので、
用途に応じて適当な繊維密度のファブリックを選択す
る。The high elastic fiber fabric used in the formwork panel of the present invention is a fabric-like two-dimensional structure made by weaving, knitting or intertwining the high elastic fibers, and is generally a fabric. 70000N / mm
A material having an elastic modulus of 2 or more is referred to. As the fabric, specifically, a fabric in which the fibers intersect to form a mesh of visible size or a sheet in which the fibers are densely woven, etc. and are densely packed in a tatami mat or mat fabric can be used It is. If the fiber density of the fabric is high, the reinforcing effect of the panel will be large, but it will be economically disadvantageous,
Select a fabric with an appropriate fiber density according to the application.
【００１６】本発明の型枠用パネルにおいてスレートボ
ードに貼り付けるファブリックとして好ましいのは、ガ
ラス繊維や炭素繊維であるが、これらに限定されるもの
ではない。例えばアラミドや超高密度ポリエチレン等か
ら成る繊維のファブリックであっても、上記のような弾
性率を有するものであれば本発明の目的を十分達成し得
る。In the formwork panel of the present invention, glass fabric or carbon fiber is preferable as the fabric to be attached to the slate board, but is not limited thereto. For example, a fiber fabric made of aramid, ultra-high-density polyethylene, or the like can sufficiently achieve the object of the present invention as long as it has the above elastic modulus.
【００１７】スレートボードに貼り付けるファブリック
の材質は必ずしも裏表同一のものではくても良い。炭素
繊維のファブリックは、ガラス繊維のファブリックに比
べて引張強さや弾性率が高いために、補強効果が優れて
いるが、単価が高くなる。したがって、より大きな引張
力を受ける面に炭素繊維のファブリックを用い、反対面
にガラス繊維ファブリックを使い原価を下げることも可
能である。本発明の型枠用パネルには各種の市販の繊維
ファブリックを用いることができる。The material of the fabric to be attached to the slate board may not necessarily be the same on both sides. Carbon fiber fabrics have a higher tensile strength and elastic modulus than glass fiber fabrics, and thus have an excellent reinforcing effect, but have a higher unit price. Therefore, it is possible to reduce the cost by using a carbon fiber fabric for the surface receiving the higher tensile force and using a glass fiber fabric for the opposite surface. Various commercially available fiber fabrics can be used for the formwork panel of the present invention.
【００１８】ガラス繊維ファブリックの例としては、カ
ネボウからテキストグラスＫＳシリーズとして市販され
ているもの、日東紡績（株）からガラスクロスＷＬ、ガ
ラス組布ＫＣ、ガラスマットＭＣシリーズなどとして市
販されているものが挙げられるが、これらに限定される
ものではない。Examples of glass fiber fabrics include those commercially available from Kanebo as Text Glass KS Series, and those commercially available from Nitto Boseki Co., Ltd. as Glass Cloth WL, Glass Braid KC, Glass Mat MC Series, and the like. But are not limited to these.
【００１９】また、本発明に使用される炭素繊維のファ
ブリックの例としては阪神大震災以降、ビルや橋脚等補
強工事に使用され、東邦レーヨンや東レ、三菱化学等か
らベスファイト、トレカ、リベラーク等商品名で市販さ
れているものが挙げられるが、これらに限定するわけで
はない。Examples of the carbon fiber fabric used in the present invention are used for reinforcing works such as buildings and piers after the Great Hanshin Earthquake, and products such as Vesfight, Trading Card, Riverark from Toho Rayon, Toray, Mitsubishi Chemical, etc. But are not limited to those marketed by name.
【００２０】高弾性繊維のファブリックをスレートボー
ドに貼り付けるための接着剤は、エポキシ樹脂やアクリ
ル樹脂接着剤が好ましいが、これに限定されるものでは
なく、他の合成樹脂系接着剤や無機質接着剤を使用する
こともできる。The adhesive for attaching the high-elastic fiber fabric to the slate board is preferably an epoxy resin or an acrylic resin adhesive, but is not limited thereto, and may be other synthetic resin adhesives or inorganic adhesives. Agents can also be used.
【００２１】[0021]
【実施例】以下、実施例により本発明の特徴を具体的に
説明するが、本発明はこれらの実施例によって制限され
るものではない。 実施例１ ＪＩＳＡ５４３０に適合する厚さ５ｍｍのスレートボー
ド（曲げ強度２５Ｎ／ｍｍ2）に東邦レーヨン製炭素繊
維ベスファイトＫ６、またはカネボウ製ガラス繊維ＫＳ
５３８０をエポキシ接着剤で貼り付け、曲げ強度および
たわみ量（破壊時のたわみ量）を測定した。被試験パネ
ルのサイズは、長さ５０ｃｍ×幅１８ｃｍとした。EXAMPLES Hereinafter, the features of the present invention will be described specifically with reference to examples, but the present invention is not limited to these examples. Example 1 A 5 mm thick slate board (bending strength 25 N / mm 2 ) conforming to JIS A5430 was placed on a carbon fiber vesfite K6 manufactured by Toho Rayon or a glass fiber KS manufactured by Kanebo.
5380 was attached with an epoxy adhesive, and the bending strength and the amount of flexure (the amount of flexure at break) were measured. The size of the panel under test was 50 cm long × 18 cm wide.
【００２２】試験にはＪＩＳＡ１４０８に規定されてい
る建築用ボード類の曲げ試験機を用いた。スパン間距離
は４０ｃｍで行い、引張力の働く方を表側として配置し
た。なお、実際にトンネル部を補修するに当たっては、
この表側の方にグラウト材が充填される。試験結果を表
１に示す。For the test, a bending tester for architectural boards specified in JIS A1408 was used. The distance between the spans was set at 40 cm, and the side on which the tensile force worked was arranged on the front side. When actually repairing the tunnel,
The grout material is filled on the front side. Table 1 shows the test results.
【００２３】[0023]
【表１】 [Table 1]
【００２４】比較例と実験例を比べると炭素繊維マ
ットを張ることにより曲げ強さや破壊たわみ量が大幅に
向上しているのがわかる。比較例は引張力の働くほう
へ炭素繊維を貼り付けているため、曲げ強さや破壊たわ
み量が大きくなっているが、圧縮側に炭素繊維を貼り付
けても比較例に示すとおりほとんど効果がない。A comparison between the comparative example and the experimental example shows that the flexural strength and the amount of deflected fracture are greatly improved by stretching the carbon fiber mat. In the comparative example, since the carbon fiber is attached to the side where the tensile force works, the bending strength and the amount of deflected deflection are large, but even if the carbon fiber is attached to the compression side, there is almost no effect as shown in the comparative example. .
【００２５】実施例２ 厚みの異なるスレートボードにガラス繊維および炭素繊
維をエポキシ樹脂で両面に貼り付け、１週間の養生後、
破壊たわみ量および曲げ強さを測定した。試験には、Ｊ
ＩＳＡ１４０８に規定されている建築用ボード類の曲げ
強さを測定する試験機を用いた。なお、試験時に引張力
が働く方に表側を配置した。実施例１と同じく、用いた
ガラスファブリックはカネボウ製テキストグラスＫＳ５
３８０であり、炭素繊維ファブリックは東邦レイヨン製
ベスファイトＫ６である。Example 2 Glass fibers and carbon fibers were attached to both sides of epoxy resin on slate boards of different thicknesses, and after curing for one week,
The fracture deflection and flexural strength were measured. For the test, J
A tester for measuring the bending strength of architectural boards specified in ISA1408 was used. In addition, the front side was arrange | positioned in the direction where a tensile force acts at the time of a test. As in Example 1, the glass fabric used was Kanebo Text Glass KS5.
380, and the carbon fiber fabric is Vesfight K6 manufactured by Toho Rayon.
【００２６】ガラス繊維ファブリックは、スレートボー
ド１ｍ2あたり８４ｇをエポキシ樹脂接着剤で貼り付け
た。また、炭素繊維ファブリックはスレートボード１ｍ
2あたり６５ｇをエポキシ樹脂接着剤で貼り付けた。比
較例は加工前のスレートボードの値を示す。測定結果を
表２にまとめる。実施例Ａ−１、Ｂ−１、Ｃ−１および
Ｄ−１は、それぞれ、比較例Ａ、Ｂ、ＣおよびＤの両面
にガラス繊維ファブリックを貼り付けたものであり、ま
た、実施例Ａ−２、Ｂ−２、Ｃ−２およびＤ−２は、そ
れぞれ、比較例Ａ、Ｂ、ＣおよびＤの表側に炭素繊維フ
ァブリック、裏側にガラス繊維ファブリックを貼り付け
たものである。As for the glass fiber fabric, 84 g per 1 m 2 of the slate board was stuck with an epoxy resin adhesive. The carbon fiber fabric is slate board 1m
65 g per 2 was attached with an epoxy resin adhesive. The comparative example shows the value of the slate board before processing. Table 2 summarizes the measurement results. Examples A-1, B-1, C-1 and D-1 were obtained by attaching glass fiber fabrics to both sides of Comparative Examples A, B, C and D, respectively. 2, B-2, C-2, and D-2 are obtained by attaching a carbon fiber fabric to the front side and a glass fiber fabric to the back side of Comparative Examples A, B, C, and D, respectively.
【００２７】[0027]
【表２】 [Table 2]
【００２８】スレートボードの表裏両面にカーボン繊維
またはガラス繊維のファブリックを貼り付けた本発明の
パネルは破壊時のたわみ量が大きく湾曲性が増し、且つ
最大荷重および曲げ強度も増大していることが理解され
る。The panel of the present invention in which carbon fiber or glass fiber fabrics are adhered to both the front and back surfaces of the slate board has a large amount of flexure at the time of breakage, increases the curability, and also increases the maximum load and bending strength. Understood.
───────────────────────────────────────────────────── フロントページの続き Ｆターム(参考） 2D055 AA02 DA01 JA00 KA00 LA16 4F100 AD11B AD11C AE10A AG00B AG00C AK53G BA03 BA06 BA10B BA10C BA13 CB00 DG01B DG01C DG11B DG11C GB90 JK04A JK07B JK07C JK13A YY00A ──────────────────────────────────────────────────の Continued on the front page F term (reference) 2D055 AA02 DA01 JA00 KA00 LA16 4F100 AD11B AD11C AE10A AG00B AG00C AK53G BA03 BA06 BA10B BA10C BA13 CB00 DG01B DG01C DG11B DG11C GB90 JK04A JK07B JK07 JK07A
Claims (1)
トボードの両面に高弾性繊維のファブリックを貼り付
け、湾曲可能にしたことを特徴とする型枠用パネル。1. A panel for formwork, characterized in that a fabric of high elasticity fiber is stuck on both sides of a slate board having a bending strength of 15 N / mm 2 or more to enable bending.