JP2001212916A - Decorative sheet with protective film - Google Patents
Decorative sheet with protective filmInfo
- Publication number
- JP2001212916A JP2001212916A JP2000028533A JP2000028533A JP2001212916A JP 2001212916 A JP2001212916 A JP 2001212916A JP 2000028533 A JP2000028533 A JP 2000028533A JP 2000028533 A JP2000028533 A JP 2000028533A JP 2001212916 A JP2001212916 A JP 2001212916A
- Authority
- JP
- Japan
- Prior art keywords
- protective film
- decorative sheet
- layer
- protective
- density polyethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、保管、運搬、施工
時等において、化粧シートの表面が汚れたり傷ついたり
艶が変化したりするのを防止するために、化粧シートの
表面に保護フィルムが剥離可能に貼着された化粧シート
に関する。BACKGROUND OF THE INVENTION The present invention relates to a protective film formed on a surface of a decorative sheet to prevent the surface of the decorative sheet from being stained, damaged, or changed in gloss during storage, transportation, construction and the like. The present invention relates to a decorative sheet that is detachably attached.
【０００２】[0002]
【従来の技術】従来、保護フィルム付き化粧板として
は、例えば、特開昭６２−１３６３９号公報に記載され
ているものが知られている。この保護フィルム付き化粧
板は、化粧板の表面に、裏面に粘着剤が貼着された保護
フィルムを重ね、この化粧板と保護フィルムとを押さえ
ロールと受けロールとで構成される圧着ロールにて加圧
して、化粧板の表面に保護フィルムを貼着することによ
り作製されるものである。上記化粧板のように、保護フ
ィルムを化粧板の表面に積層するには、粘着剤層を備え
た保護フィルムを使用して、保護フィルムの粘着剤層を
化粧板の表面に重ねて加圧して貼着するものであり、裏
面に粘着剤を備えた保護フィルムを作製する工程と、加
圧により化粧板の表面に保護フィルムを貼着する工程が
必要となるため、製造工程が煩雑になるとともに、粘着
剤を備えた保護フィルムを使用するためにコスト高にな
るという欠点がある。2. Description of the Related Art Conventionally, as a decorative plate with a protective film, for example, a decorative plate described in JP-A-62-13639 is known. This decorative plate with a protective film, a protective film with an adhesive stuck on the back surface is superimposed on the surface of the decorative plate, and the decorative plate and the protective film are pressed with a pressure roll composed of a holding roll and a receiving roll. It is produced by applying pressure and adhering a protective film to the surface of the decorative board. To laminate the protective film on the surface of the decorative board, as in the decorative board, use a protective film provided with an adhesive layer, apply the pressure-sensitive adhesive layer of the protective film on the surface of the decorative board, and apply pressure. It is necessary to perform a process of producing a protective film having an adhesive on the back surface and a process of attaching the protective film to the surface of the decorative plate by applying pressure, which complicates the manufacturing process. However, there is a disadvantage that the use of a protective film provided with an adhesive increases costs.
【０００３】また、保護フィルム付き化粧シートとして
は、例えば、特開平１１−２７７７０８号公報に記載さ
れているものが知られている。この保護フィルム付き化
粧シートは、化粧シートと密着する面に物理的に粗面を
設けた保護フィルムを、加熱して軟化させた化粧シート
の意匠表面に当接させて重ね合わせ、ローラーで加圧す
る方法等により作製されるものであり、化粧シートと密
着する面に物理的に粗面を設けた保護フィルムを作製す
る工程と、加熱して軟化させた化粧シートの意匠表面と
圧着して積層する工程が必要があるために、工程が煩雑
となるとともにコスト高になるという欠点がある。ま
た、加熱して軟化させた化粧シートの表面に保護フィル
ムを積層するため、耐熱性の劣る保護フィルムは使用し
にくいという欠点がある。As a decorative sheet with a protective film, for example, a decorative sheet described in Japanese Patent Application Laid-Open No. H11-277708 is known. This decorative sheet with a protective film, a protective film having a rough surface physically provided on the surface in close contact with the decorative sheet, is brought into contact with the design surface of the decorative sheet which has been softened by heating, and superposed, and is pressed with a roller. It is produced by a method or the like, and a step of producing a protective film having a physically roughened surface on a surface that is in close contact with the decorative sheet, and laminating by pressing the decorative surface of the decorative sheet heated and softened. Since a process is required, there is a disadvantage that the process is complicated and the cost is increased. In addition, since the protective film is laminated on the surface of the decorative sheet that has been softened by heating, there is a disadvantage that a protective film having poor heat resistance is difficult to use.
【０００４】[0004]
【発明が解決しようとする課題】本発明の目的は、化粧
シートの表面に保護フィルムをきわめて簡単で効率的な
方法により積層することが可能であるので、低コストで
製造することができる保護フィルム付き化粧シートを提
供することにある。SUMMARY OF THE INVENTION It is an object of the present invention to provide a protective film which can be manufactured at a low cost because a protective film can be laminated on the surface of a decorative sheet by a very simple and efficient method. Provided is a decorative sheet with the same.
【０００５】[0005]
【課題を解決するための手段】基材層と意匠層を有する
化粧シートの使用状態での表面側に保護フィルムが剥離
可能に積層された保護フィルム付き化粧シートにおい
て、保護フィルムがポリオレフィン樹脂の押出ラミネー
ションにより形成された構成とすることにより、ロール
状の化粧シートを使用して押出ラミネーションによりポ
リオレフィン樹脂からなる保護フィルムを高速で積層す
ることができ、保護フィルムを化粧シートに積層する工
程の簡略化が可能となるため、低コストの保護フィルム
付き化粧シートとすることができる。また、保管、運
搬、施工時等において化粧シートの使用状態での表面側
となる面が汚れたり傷付いたり艶が変化したりするのを
防止できるとともに、施工完了後には保護フィルムを化
粧シートから簡単に剥離することができる。Means for Solving the Problems In a decorative sheet with a protective film in which a protective film is releasably laminated on a surface side of a decorative sheet having a base layer and a design layer in use, the protective film is formed by extruding a polyolefin resin. By adopting the structure formed by lamination, a protective film made of polyolefin resin can be laminated at high speed by extrusion lamination using a roll-shaped decorative sheet, and the process of laminating the protective film on the decorative sheet can be simplified. Therefore, a low-cost decorative sheet with a protective film can be obtained. In addition, it is possible to prevent the surface on the surface side in use of the decorative sheet from being stained, scratched or changed in gloss during storage, transportation, construction, etc., and after the construction is completed, remove the protective film from the decorative sheet. It can be easily peeled off.
【０００６】上記の保護フィルム付き化粧シートにおい
て、保護フィルムが低密度ポリエチレンからなる構成と
することにより、押出ラミネーションされた低密度ポリ
エチレンからなる保護フィルムが、使用状態での表面側
となる意匠層面ないしはプラスチック基材層面に対して
適度の接着強度を有し且つ優れた剥離性を有するもので
ある。また、低密度ポリエチレンは押出ラミネーション
加工適性が優れるので高速で加工することが可能である
とともに、低密度ポリエチレンが比較的安価であるため
低コストの保護フィルム付き化粧シートとすることがで
きる。In the decorative sheet with a protective film described above, the protective film is made of low-density polyethylene, so that the protective film made of low-density polyethylene that has been extruded and laminated is a design layer surface or a surface side that is a surface side in use. It has an appropriate adhesive strength to the surface of the plastic substrate layer and has excellent releasability. In addition, low-density polyethylene has excellent suitability for extrusion lamination processing, so that it can be processed at high speed. In addition, since low-density polyethylene is relatively inexpensive, a low-cost decorative sheet with a protective film can be obtained.
【０００７】上記の保護フィルム付き化粧シートにおい
て、保護フィルムが１５〜４０μｍの厚さである構成と
することにより、化粧シート面から容易に剥離でき、且
つ化粧シートの表面を保護するのに十分な強度が得られ
るとともに、厚さを薄くすることにより低コスト化が可
能となる。また、１工程のポリエチレンの押出ラミネー
ションにより保護フィルムを化粧シートの表面に積層す
ることができるので押出ラミネーションの効率化が可能
となる。In the above decorative sheet with a protective film, the protective film has a thickness of 15 to 40 μm, so that it can be easily peeled off from the decorative sheet surface and is sufficient to protect the surface of the decorative sheet. The strength can be obtained, and the cost can be reduced by reducing the thickness. Further, since the protective film can be laminated on the surface of the decorative sheet by one-step extrusion lamination of polyethylene, the efficiency of extrusion lamination can be improved.
【０００８】上記の保護フィルム付き化粧シートにおい
て、意匠層が印刷絵柄層と保護層からなる構成とするこ
とにより、低密度ポリエチレンの押出ラミネーションに
より保護フィルムを化粧シートの意匠層面に積層した際
に、保護フィルムが意匠層の保護層面に接着されるの
で、保護層を形成する樹脂の種類により保護フィルムを
保護層面から容易に剥離できる強度に調整することが可
能となるとともに、保護層が印刷絵柄層の全面を被覆し
ているので保護フィルムを剥離する際に印刷絵柄層を形
成するインキが点状に剥離してくるのを防止できる。In the decorative sheet with a protective film described above, the design layer is constituted by a printed pattern layer and a protective layer, so that when the protective film is laminated on the decorative layer surface of the decorative sheet by extrusion lamination of low density polyethylene, Since the protective film is adhered to the protective layer surface of the design layer, it is possible to adjust the strength of the protective film so that the protective film can be easily peeled off from the protective layer surface depending on the type of resin forming the protective layer, and the protective layer is formed of a printed pattern layer. Since the entire surface of the protective film is covered, it is possible to prevent the ink forming the print pattern layer from peeling off in dots when the protective film is peeled off.
【０００９】上記の保護フィルム付き化粧シートにおい
て、基材層が紙、紙とプラスチックの積層体、プラスチ
ックフィルムからなる構成とすることにより、襖、水回
りないしはキッチン用扉、収納用扉、壁面、ドア面材等
として使用できる保護フィルム付き化粧シートとするこ
とができる。In the above decorative sheet with a protective film, the base material layer is made of paper, a laminate of paper and plastic, and a plastic film, so that a sliding door, a water or kitchen door, a storage door, a wall surface, A decorative sheet with a protective film that can be used as a door face material or the like can be provided.
【００１０】[0010]
【発明の実施の形態】以下、図面を引用して本発明の実
施の形態を説明する。図１は本発明の第１実施形態の構
成を示す断面図、図２は本発明の第２実施形態の構成を
示す断面図、図３は本発明の第３実施形態の構成を示す
断面図、図４は本発明の第４実施形態の構成を示す断面
図、図５は化粧シートに保護フィルムを積層する工程の
概略を示す図であって、１は保護フィルム、２は保護
層、３は印刷絵柄層、４は紙基材層、５は低密度ポリエ
チレン層、６は紙層、7,8 はプラスチック基材層、11は
Ｔダイ、12は冷却ロール、13は加圧ロール、14は給紙
部、15は排紙部をそれぞれ表す。Embodiments of the present invention will be described below with reference to the drawings. FIG. 1 is a cross-sectional view illustrating a configuration of a first embodiment of the present invention, FIG. 2 is a cross-sectional view illustrating a configuration of a second embodiment of the present invention, and FIG. 3 is a cross-sectional view illustrating a configuration of a third embodiment of the present invention. FIG. 4 is a cross-sectional view showing a configuration of a fourth embodiment of the present invention, and FIG. 5 is a view schematically showing a process of laminating a protective film on a decorative sheet, wherein 1 is a protective film, 2 is a protective layer, Is a print pattern layer, 4 is a paper base layer, 5 is a low-density polyethylene layer, 6 is a paper layer, 7, 8 is a plastic base layer, 11 is a T die, 12 is a cooling roll, 13 is a pressure roll, 14 Denotes a paper feed unit, and 15 denotes a paper discharge unit.
【００１１】本発明の第１実施形態は、図１に示すよう
に、紙基材層４の一方の面に印刷絵柄層３と保護層２か
らなる意匠層が形成された構成の化粧シートＡの保護層
２の面に低密度ポリエチレンからなる保護フィルム１が
押出ラミネーションにより剥離可能に積層された構成で
ある。第１実施形態の保護フィルム付き化粧シートは襖
紙等に使用することができ、保管時、運搬時、施工時に
意匠層面が汚れたり傷が付いたり艶が変化したりするの
を防止できる。In the first embodiment of the present invention, as shown in FIG. 1, a decorative sheet A having a structure in which a design layer composed of a printed picture layer 3 and a protective layer 2 is formed on one surface of a paper base layer 4 is shown. The protective film 1 made of low-density polyethylene is laminated on the surface of the protective layer 2 so as to be peelable by extrusion lamination. The decorative sheet with a protective film of the first embodiment can be used for fusuma paper or the like, and can prevent the design layer surface from being stained, scratched, or changed in gloss during storage, transportation, or construction.
【００１２】本発明の第２実施形態は、図２に示すよう
に、紙基材層４の一方の面に印刷絵柄層３と保護層２か
らなる意匠層が形されるとともに紙基材層４の他方の面
にポリエチレン層５を介して紙層６が積層された構成の
化粧シートＢの保護層２の面に低密度ポリエチレンから
なる保護フィルム１が押出ラミネーションにより剥離可
能に積層された構成である。第２実施形態の保護フィル
ム付き化粧シートは襖紙等に使用した際に、保管、運
搬、施工時に意匠層面が汚れたり傷が付いたり艶が変化
したりするのを防止できるとともに、ポリエチレン層５
により防湿効果も得られるので吸湿による反りの発生を
防止する効果も得られる。In the second embodiment of the present invention, as shown in FIG. 2, a design layer comprising a printed picture layer 3 and a protective layer 2 is formed on one surface of a paper base layer 4 and a paper base layer is formed. 4, a protective film 1 made of low-density polyethylene is laminated on the surface of the protective layer 2 of the decorative sheet B having a paper layer 6 laminated on the other surface via a polyethylene layer 5 so as to be peelable by extrusion lamination. It is. When the decorative sheet with the protective film of the second embodiment is used for fusuma paper or the like, it is possible to prevent the surface of the design layer from being stained, scratched, or changed in gloss during storage, transportation, and construction, and to prevent the polyethylene layer 5 from changing.
As a result, a moisture-proof effect can be obtained, and an effect of preventing the occurrence of warpage due to moisture absorption can also be obtained.
【００１３】本発明の第３実施形態は、図３に示すよう
に、プラスチック基材層７の一方の面に印刷絵柄層３と
保護層２からなる意匠層が形成された構成の化粧シート
Ｃの保護層２の面に低密度ポリエチレンからなる保護フ
ィルム１が押出ラミネーションにより剥離可能に積層さ
れた構成である。プラスチック基材層７としては着色し
たプラスチックフィルムが一般的に使用される。第３実
施形態の保護フィルム付き化粧シートは壁面、ドア面
材、収納扉等に使用でき、意匠層面が汚れたり傷が付い
たりするのを防止できるとともに、防湿性を付与するこ
とができる。In a third embodiment of the present invention, as shown in FIG. 3, a decorative sheet C having a configuration in which a design layer composed of a printed picture layer 3 and a protective layer 2 is formed on one surface of a plastic base material layer 7. The protective film 1 made of low-density polyethylene is laminated on the surface of the protective layer 2 so as to be peelable by extrusion lamination. As the plastic base material layer 7, a colored plastic film is generally used. The decorative sheet with a protective film of the third embodiment can be used for a wall surface, a door surface material, a storage door, and the like, and can prevent the design layer surface from being stained or scratched, and can impart moisture resistance.
【００１４】本発明の第４実施形態は、図４に示すよう
に、プラスチック基材層８の一方の面に印刷絵柄層３か
らなる意匠層が形成された構成の化粧シートＤのプラス
チック基材層８の面に低密度ポリエチレンからなる保護
フィルム１が押出ラミネーションにより剥離可能に積層
された構成である。第４実施形態の保護フィルム付き化
粧シートは、印刷絵柄層３の面にて合板等の基板に接着
した状態で、保護フィルム１が積層されたプラスチック
基材層８の面が外面となるようにして使用されるもので
あり、保管、運搬、施工時に、プラスチック基材層８と
なるプラスチックフィルム表面の鏡面光沢ないしは艶消
光沢が損なわれたり、プラスチックフィルム表面に傷が
付いたりするのを防止することができる。プラスチック
基材層８としては無着色透明のプラスチックフィルムが
使用される。In the fourth embodiment of the present invention, as shown in FIG. 4, a plastic substrate of a decorative sheet D having a design layer composed of a printed picture layer 3 formed on one surface of a plastic substrate layer 8. The protective film 1 made of low-density polyethylene is laminated on the surface of the layer 8 so as to be peelable by extrusion lamination. In the decorative sheet with a protective film of the fourth embodiment, the surface of the plastic base material layer 8 on which the protective film 1 is laminated becomes the outer surface in a state where the surface of the printed pattern layer 3 is adhered to a substrate such as plywood. In storage, transportation, and construction, it is possible to prevent the specular gloss or matte gloss of the plastic film surface serving as the plastic base material layer 8 from being impaired, and to prevent the plastic film surface from being damaged. be able to. As the plastic base material layer 8, a non-colored transparent plastic film is used.
【００１５】なお、第１〜第３実施形態においては意匠
層を印刷絵柄層３と保護層２により形成した構成につい
て説明したが、印刷絵柄層３が全面のベタインキ層を含
む絵柄からなる場合は保護層２をなくした構成とするこ
ともできる。意匠層を印刷絵柄層３のみにて形成した構
成の場合は、積層された保護フィルム１は印刷絵柄層３
との界面で剥離するものである。第４実施形態では、印
刷絵柄層３は絵柄インキ層と全面ベタインキ層により形
成されるのが普通である。In the first to third embodiments, the configuration in which the design layer is formed by the print pattern layer 3 and the protective layer 2 has been described. However, in the case where the print pattern layer 3 is formed of a pattern including a solid ink layer on the entire surface, It is also possible to adopt a configuration in which the protective layer 2 is omitted. In the case of a configuration in which the design layer is formed only of the print pattern layer 3, the laminated protective film 1 is formed of the print pattern layer 3.
At the interface with the surface. In the fourth embodiment, the printed picture layer 3 is usually formed by a picture ink layer and a solid ink layer on the entire surface.
【００１６】保護フィルム１を形成する樹脂としては、
低密度ポリエチレン、中密度ポリエチレン、高密度ポリ
エチレン、エチレン−プロピレン共重合体、エチレン−
酢酸ビニル共重合体、エチレン−アクリル酸共重合体、
エチレン−アクリル酸エステル共重合体、アイオノマー
等が使用できるが、高圧法低密度ポリエチレン、線状低
密度ポリエチレン、シングルサイト触媒を用いて重合し
たエチレン−αオレフィン共重合体等の低密度ポリエチ
レンを使用するのが好ましい。低密度ポリエチレンとし
ては、密度が０．９１６〜０．９２５、メルトインデッ
クスが５〜１３のものが好適に使用できる。上記の低密
度ポリエチレンを使用することにより、優れた押出ラミ
ネーシヨン適性が得られるとともに、化粧シートの意匠
層面への適度の接着強度が得られるので、化粧シートの
意匠層面から容易に剥離できる保護フィルムを形成する
ことができる。また、１回の押出ラミネーシヨンにより
１０〜８０μｍの厚さに低密度ポリエチレンからなる保
護フィルムを化粧シート面に形成することが可能である
が、化粧シート面からの剥離性、コスト、押出ラミネー
シヨンの作業性等を考慮すると、保護フィルムの厚さを
１５〜４０μｍとするのが好ましい。The resin forming the protective film 1 includes:
Low-density polyethylene, medium-density polyethylene, high-density polyethylene, ethylene-propylene copolymer, ethylene-
Vinyl acetate copolymer, ethylene-acrylic acid copolymer,
Ethylene-acrylate copolymers, ionomers, etc. can be used, but low-density polyethylenes such as high-pressure low-density polyethylene, linear low-density polyethylene, and ethylene-α-olefin copolymers polymerized using a single-site catalyst are used. Is preferred. As the low-density polyethylene, those having a density of 0.916 to 0.925 and a melt index of 5 to 13 can be suitably used. By using the above low-density polyethylene, excellent extrusion lamination suitability can be obtained, and appropriate adhesive strength to the design layer surface of the decorative sheet can be obtained, so that the protective film can be easily peeled from the design layer surface of the decorative sheet. Can be formed. Further, it is possible to form a protective film made of low-density polyethylene to a thickness of 10 to 80 μm on the decorative sheet surface by one extrusion lamination, but the exfoliation from the decorative sheet surface, cost, and extrusion lamination are also possible. In consideration of the workability and the like, the thickness of the protective film is preferably set to 15 to 40 μm.
【００１７】なお、化粧シートの意匠層面ないしはプラ
スチック基材層面に保護フィルムを形成する方法とし
て、化粧シート面に低密度ポリエチレン層を押出ラミネ
ーションする際に別に作製したプラスチックフィルムを
積層する方法、ないしは、多層押出装置を備えた押出ラ
ミネーターを使用して多層押出ラミネーションを行うこ
とにより多層プラスチックフィルムからなる保護フィル
ムを形成する方法とすることもできる。上記の方法にて
化粧シート面に保護フィルムを形成する場合、化粧シー
トの意匠層面ないしはプラスチック基材層面と保護フィ
ルム間の接着強度の調節を容易に行うことができる。As a method of forming a protective film on the surface of the decorative sheet or the surface of the plastic substrate layer of the decorative sheet, a method of laminating a plastic film separately produced when extruding a low-density polyethylene layer on the surface of the decorative sheet, or A method of forming a protective film composed of a multilayer plastic film by performing multilayer extrusion lamination using an extrusion laminator equipped with a multilayer extrusion device. When the protective film is formed on the decorative sheet surface by the above method, the adhesive strength between the design layer surface or the plastic substrate layer surface of the decorative sheet and the protective film can be easily adjusted.
【００１８】保護フィルムを低密度ポリエチレンの押出
ラミネーションにより成形する際の押出条件としては、
樹脂温度は通常の低密度ポリエチレンの押出ラミネーシ
ョン時の温度よりも低い２３０〜３００℃程度の比較的
低い温度で押出ラミネーションを行うのが好ましい。化
粧シートの意匠層面と低密度ポリエチレンからなる保護
フィルム間の接着強度は押出ラミネーション時の樹脂温
度により変化し、押出ラミネーション時の樹脂温度を高
くすると保護フィルムと意匠層面との接着強度を強くす
ることができ、低くすると接着強度を弱くすることがで
きる。したがって、意匠層を形成する樹脂の種類、必要
とする保護フィルムと意匠層面間の接着強度により押出
ラミネーション時の低密度ポリエチレンの樹脂温度を調
節するのが好ましい。保護フィルムと化粧シートの意匠
層面間の接着強度は、押出ラミネーション時の樹脂温度
以外に押出ラミネーションの厚さ、加工速度、ニップ圧
等により微調整することもできる。低密度ポリエチレン
からなる保護フィルムを押出ラミネーションにより意匠
層面に積層することにより、保護フィルムと意匠層面間
の接着強度を１０〜３０ｇ／２５ｍｍ幅（１８０度剥
離、引張速度２００ｍｍ／分）とすることができ、保護
フィルムを化粧シートの意匠層面から容易に剥離するこ
とができる。また、低密度ポリエチレンからなる保護フ
ィルムを押出ラミネーションによりプラスチック基材層
８面に積層した場合においても、保護フィルムとプラス
チック基材層８間の接着強度を上記と同程度の強度とす
ることができる。The extrusion conditions for forming the protective film by extrusion lamination of low-density polyethylene include:
It is preferable to perform extrusion lamination at a relatively low resin temperature of about 230 to 300 ° C., which is lower than the temperature during extrusion lamination of ordinary low-density polyethylene. The adhesive strength between the decorative layer surface of the decorative sheet and the protective film made of low-density polyethylene changes depending on the resin temperature during extrusion lamination, and increasing the resin temperature during extrusion lamination increases the adhesive strength between the protective film and the decorative layer surface. If it is lowered, the adhesive strength can be reduced. Therefore, it is preferable to control the resin temperature of the low-density polyethylene during extrusion lamination depending on the type of resin forming the design layer and the required adhesive strength between the protective film and the design layer surface. The adhesive strength between the protective film and the decorative layer surface of the decorative sheet can be finely adjusted by the thickness of the extrusion lamination, the processing speed, the nip pressure and the like, in addition to the resin temperature at the time of the extrusion lamination. By laminating a protective film made of low-density polyethylene on the surface of the design layer by extrusion lamination, the adhesive strength between the protective film and the surface of the design layer can be set to 10 to 30 g / 25 mm width (180 degree peeling, 200 mm / min tensile speed). The protective film can be easily peeled off from the design layer surface of the decorative sheet. Further, even when a protective film made of low-density polyethylene is laminated on the surface of the plastic substrate layer 8 by extrusion lamination, the adhesive strength between the protective film and the plastic substrate layer 8 can be made approximately the same as above. .
【００１９】印刷絵柄層３を形成するインキの樹脂とし
ては、化粧シートの印刷に通常使用されているセルロー
ス系樹脂、アクリル系樹脂、塩化ビニル系樹脂、ポリア
ミド系樹脂等の熱可塑性樹脂、およびウレタン系樹脂、
アクリルウレタン系樹脂等の２液硬化型樹脂が使用でき
る。保護層２を形成する樹脂としては、上記のインキに
使用されるのと同種の樹脂を使用できる。特に化粧シー
トの意匠層面の耐磨耗性、耐汚染性等を必要とする場合
にはウレタンアクリレート、ポリエステルアクリレー
ト、エポキシアクリレート等からなる電離放射線硬化性
樹脂を使用することもできる。また、化粧シートの意匠
性を高めるために意匠層面に微細凹凸からなる各種形状
のエンボスを施してもよい。Examples of the resin of the ink for forming the print pattern layer 3 include thermoplastic resins such as cellulose resins, acrylic resins, vinyl chloride resins, polyamide resins, etc., which are generally used for printing decorative sheets. Resin,
Two-component curable resins such as acrylic urethane resins can be used. As the resin for forming the protective layer 2, the same type of resin as that used for the above-described ink can be used. In particular, when the decorative layer surface of the decorative sheet requires abrasion resistance, stain resistance, and the like, an ionizing radiation curable resin made of urethane acrylate, polyester acrylate, epoxy acrylate, or the like can be used. Further, in order to enhance the design property of the decorative sheet, the design layer surface may be embossed in various shapes composed of fine irregularities.
【００２０】紙基材層４としては、クラフトパルプ、サ
ルフアイトパルプ等の化学パルプからなる紙、樹脂を混
抄ないしは含浸した紙間強化紙、自己消火性の水酸化ア
ルミニウムを主体とし、クレー、カオリン、タルク、二
酸化チタン等を填料として１０〜８０重量％混抄した難
燃紙等が使用できる。紙基材層４に積層する紙層６とし
てはクラフト紙、純白等の強度の優れた紙が使用でき
る。The paper base layer 4 is mainly composed of paper made of chemical pulp such as kraft pulp or sulphite pulp, paper-reinforced paper mixed or impregnated with resin, self-extinguishing aluminum hydroxide, clay, kaolin , Talc, titanium dioxide or the like as a filler can be used as a flame-retardant paper. As the paper layer 6 to be laminated on the paper base material layer 4, kraft paper or paper having excellent strength such as pure white can be used.
【００２１】プラスチック基材層７としては、ポリ塩化
ビニル、中密度ポリエチレン、高密度ポリエチレン、ポ
リプロピレン、エチレン−プロピレン共重合体、ポリエ
チレンテレフタレート、ポリカーボネート、ポリエチレ
ンナフタレート、ポリアクリル酸エステル、ポリメタク
リル酸エステル、エチレン−ビニルアルコール共重合体
等の樹脂からなるプラスチックフィルムが使用できる。
プラスチック基材層７としては化粧シートの意匠を形成
するのに適した色調に着色した着色フィルムが一般に使
用される。プラスチック基材層８としては、ポリプロピ
レン、ポリエチレンテレフタレート、ポリカーボネー
ト、ポリエチレンナフタレート、ポリアクリル酸エステ
ル、ポリメタクリル酸エステル、エチレン−ビニルアル
コール共重合体等の樹脂からなる無着色透明プラスチッ
クフィルムが主に使用される。The plastic base material layer 7 is made of polyvinyl chloride, medium density polyethylene, high density polyethylene, polypropylene, ethylene-propylene copolymer, polyethylene terephthalate, polycarbonate, polyethylene naphthalate, polyacrylate, polymethacrylate. And a plastic film made of a resin such as an ethylene-vinyl alcohol copolymer.
As the plastic substrate layer 7, a colored film colored in a color tone suitable for forming a design of a decorative sheet is generally used. As the plastic base material layer 8, a non-colored transparent plastic film made of a resin such as polypropylene, polyethylene terephthalate, polycarbonate, polyethylene naphthalate, polyacrylate, polymethacrylate, ethylene-vinyl alcohol copolymer is mainly used. Is done.
【００２２】化粧シートの意匠層面に低密度ポリエチレ
ンからなる保護フィルムを積層するには通常の熱溶融押
出ラミネーターが使用される。図５に示すように、給紙
部14から意匠層を形成したロール状の化粧シートを繰り
出し、Ｔダイ11から押し出される溶融した皮膜状の低密
度ポリエチレンを化粧シートの意匠層面に積層し、冷却
ロール13が溶融ポリエチレン層に接するように加圧ロー
ル12と冷却ロール13間で加圧し、化粧シートの意匠層面
に低密度ポリエチレンからなる保護フィルムを積層した
後に、排紙部15にて巻き上げることにより保護フィルム
付き化粧シートを作製することができる。第４実施形態
のようにプラスチック基材層面に保護フィルムを積層す
る構成についても、プラスチック基材層面に低密度ポリ
エチレンを押出ラミネーションすることにより作製する
ことができる。For laminating a protective film made of low-density polyethylene on the surface of the decorative layer of the decorative sheet, an ordinary hot melt extrusion laminator is used. As shown in FIG. 5, a roll-shaped decorative sheet on which a design layer is formed is fed out from the paper supply unit 14, and a low-density polyethylene in the form of a melted film extruded from the T-die 11 is laminated on the design layer surface of the decorative sheet, and cooled. By pressurizing between the pressure roll 12 and the cooling roll 13 so that the roll 13 is in contact with the molten polyethylene layer, a protective film made of low-density polyethylene is laminated on the design layer surface of the decorative sheet, and then wound up at the paper discharge unit 15. A decorative sheet with a protective film can be produced. The configuration in which the protective film is laminated on the plastic substrate layer surface as in the fourth embodiment can also be manufactured by extruding low-density polyethylene on the plastic substrate layer surface.
【００２３】実施例１ 坪量１００ｇ／ｍ2 の紙（Ｄ−５−Ｂ、サンファイバ
ー）の表面側に、硝化綿系樹脂からなるインキにてグラ
ビア印刷により和紙模様の印刷絵柄層を形成し、印刷絵
柄層面に硝化綿系樹脂からなる透明インキを使用してグ
ラビア印刷により全面にベタ刷りして保護層を形成し
て、表面から順に保護層と印刷絵柄層と紙基材層とから
なる化粧シートを作製した。作製した化粧シートの保護
層面に、密度が０．９１８、メルトインデックスが６の
低密度ポリエチレンを、樹脂温度を２７０℃に設定して
５０ｍ／分の速度でニップ圧を１３６ｋｇ／ｃｍ2 の条
件で押出ラミネーションして、３０μｍの厚さの低密度
ポリエチレンからなる保護フィルムを積層した保護フィ
ルム付き化粧シートを作製した。得られた保護フィルム
付き化粧シートの保護フィルムと硝化綿系樹脂からなる
保護層間の接着強度は２０ｇ／２５ｍｍ幅（１８０度剥
離、引張速度２００ｍｍ／分）であり、保護フィルムを
化粧シートの保護層面から簡単に剥離することができ
た。Example 1 On a surface side of paper (D-5-B, sun fiber) having a basis weight of 100 g / m 2 , a print pattern layer of Japanese paper pattern was formed by gravure printing with an ink composed of a nitrified cotton resin. Using a transparent ink made of a nitrifying cotton-based resin on the printed pattern layer surface, solid printing is performed over the entire surface by gravure printing to form a protective layer, and in order from the surface, a protective layer, a printed pattern layer, and a paper base layer are formed. A decorative sheet was produced. A low-density polyethylene having a density of 0.918 and a melt index of 6 was applied to the protective layer surface of the prepared decorative sheet at a resin temperature of 270 ° C. at a speed of 50 m / min and a nip pressure of 136 kg / cm 2 . Extrusion lamination produced a decorative sheet with a protective film in which a protective film made of low-density polyethylene having a thickness of 30 μm was laminated. The adhesive strength between the protective film of the decorative sheet with the protective film thus obtained and the protective layer made of a nitrified cotton resin is 20 g / 25 mm width (180 degree peeling, 200 mm / min of pulling speed). Could be easily peeled off.
【００２４】実施例２ 厚さ４５μｍの黄色に着色した２軸延伸ポリエチレンテ
レフタレートフィルム（Ｚ−２１０、三菱ポリエステ
ル）の一方の面にウレタン系樹脂からなるインキを使用
してグラビア印刷により木目模様の印刷絵柄層を形成
し、印刷絵柄層面にポリエステルアクリレートからなる
紫外線硬化性樹溶液をコーテイングし溶剤を揮散させた
後に紫外線を照射して硬化させて紫外線硬化性樹脂から
なる厚さ２μｍの保護層を形成することにより、保護層
と印刷絵柄層とプラスチック基材層からなる化粧シート
を作製した。作製した化粧シートの保護層面に、樹脂温
度を３００℃に設定した以外は、実施例１と同じ条件で
低密度ポリエチレンからなる保護フィルムを積層するこ
とにより保護フィルム付き化粧シートを作製した。得ら
れた保護フィルム付き化粧シートの保護フィルムと紫外
線硬化性樹脂からなる保護層間の接着強度は１５ｇ／２
５ｍｍ幅（１８０度剥離、引張速度２００ｍｍ／分）で
あり、保護フィルムを化粧シートの保護層面から簡単に
剥離することができた。Example 2 Printing of a grain pattern by gravure printing on one surface of a biaxially stretched polyethylene terephthalate film (Z-210, Mitsubishi Polyester) colored yellow with a thickness of 45 μm using a urethane resin. A pattern layer is formed, and a UV curable resin solution made of polyester acrylate is coated on the surface of the printed pattern layer to evaporate the solvent, and then irradiated with ultraviolet light to be cured to form a protective layer having a thickness of 2 μm made of an ultraviolet curable resin. Thereby, a decorative sheet including the protective layer, the printed picture layer, and the plastic base material layer was produced. A decorative film with a protective film was produced by laminating a protective film made of low-density polyethylene on the protective layer surface of the produced decorative sheet under the same conditions as in Example 1 except that the resin temperature was set to 300 ° C. The adhesive strength between the protective film of the obtained decorative sheet with a protective film and the protective layer made of an ultraviolet curable resin is 15 g / 2.
It was 5 mm wide (180 degree peeling, 200 mm / min tensile speed), and the protective film could be easily peeled off from the protective layer surface of the decorative sheet.
【００２５】[0025]
【発明の効果】基材層と意匠層を有する化粧シートの使
用状態での表面側に保護フィルムが剥離可能に積層され
た保護フィルム付き化粧シートにおいて、保護フィルム
がポリオレフィン樹脂の押出ラミネーションにより形成
された構成とすることにより、ロール状の化粧シートを
使用して押出ラミネーションによりポリオレフィン樹脂
からなる保護フィルムを高速で積層することができ、保
護フィルムを化粧シートに積層する工程の簡略化が可能
となるため、低コストの保護フィルム付き化粧シートと
することができる。また、保管、運搬、施工時等におい
て化粧シートの使用状態での表面側となる面が汚れたり
傷付いたり艶が変化したりするのを防止できるととも
に、施工完了後には保護フィルムを化粧シートから簡単
に剥離することができる。According to the present invention, in a decorative sheet having a protective film, a protective film is releasably laminated on a surface side of a decorative sheet having a base layer and a design layer in use, wherein the protective film is formed by extrusion lamination of a polyolefin resin. With this configuration, a protective film made of a polyolefin resin can be laminated at a high speed by extrusion lamination using a roll-shaped decorative sheet, and the process of laminating the protective film on the decorative sheet can be simplified. Therefore, a low-cost decorative sheet with a protective film can be obtained. In addition, it is possible to prevent the surface on the surface side in use of the decorative sheet from being stained, scratched or changed in gloss during storage, transportation, construction, etc., and after the construction is completed, remove the protective film from the decorative sheet. It can be easily peeled off.
【００２６】上記の保護フィルム付き化粧シートにおい
て、保護フィルムが低密度ポリエチレンからなる構成と
することにより、押出ラミネーションされた低密度ポリ
エチレンからなる保護フィルムが、使用状態での表面側
となる意匠層面ないしはプラスチック基材層面に対して
適度の接着強度を有し且つ優れた剥離性を有するもので
ある。また、低密度ポリエチレンは押出ラミネーション
加工適性が優れるので高速で加工することが可能である
とともに、低密度ポリエチレンが比較的安価であるため
低コストの保護フィルム付き化粧シートとすることがで
きる。In the decorative sheet with a protective film described above, the protective film is made of low-density polyethylene, so that the protective film made of low-density polyethylene extruded by lamination can be used as a surface of a design layer or a surface layer in a use state. It has an appropriate adhesive strength to the surface of the plastic substrate layer and has excellent releasability. In addition, low-density polyethylene has excellent suitability for extrusion lamination processing, so that it can be processed at high speed. In addition, since low-density polyethylene is relatively inexpensive, a low-cost decorative sheet with a protective film can be obtained.
【００２７】上記の保護フィルム付き化粧シートにおい
て、保護フィルムが１５〜４０μｍの厚さである構成と
することにより、化粧シート面から容易に剥離でき、且
つ化粧シートの表面を保護するのに十分な強度が得られ
るとともに、厚さを薄くすることにより低コスト化が可
能となる。また、１工程のポリエチレンの押出ラミネー
ションにより保護フィルムを化粧シートの表面に積層す
ることができるので押出ラミネーションの効率化が可能
となる。In the decorative sheet with a protective film described above, the protective film has a thickness of 15 to 40 μm, so that the protective film can be easily peeled off from the decorative sheet surface and sufficient to protect the surface of the decorative sheet. The strength can be obtained, and the cost can be reduced by reducing the thickness. Further, since the protective film can be laminated on the surface of the decorative sheet by one-step extrusion lamination of polyethylene, the efficiency of extrusion lamination can be improved.
【００２８】上記の保護フィルム付き化粧シートにおい
て、意匠層が印刷絵柄層と保護層からなる構成とするこ
とにより、低密度ポリエチレンの押出ラミネーションに
より保護フィルムを化粧シートの意匠層面に積層した際
に、保護フィルムと意匠層を構成する保護層面と接着強
度を保護層を形成する樹脂の種類により保護フィルムを
意匠層面から容易に剥離できる強度に調整することが可
能となるとともに、保護層が印刷絵柄層の全面を被覆し
ているので保護フィルムを意匠層面から剥離する際に印
刷絵柄層を形成するインキが点状に剥離してくるのを防
止できる。In the above decorative sheet with a protective film, the design layer is composed of a printed picture layer and a protective layer, so that when the protective film is laminated on the design layer surface of the decorative sheet by extrusion lamination of low density polyethylene, The protective film and the protective layer surface constituting the design layer and the adhesive strength can be adjusted to a strength that allows the protective film to be easily peeled off from the design layer surface by the type of the resin forming the protective layer, and the protective layer is a printed picture layer. Since the entire surface of the protective film is covered, it is possible to prevent the ink forming the printed picture layer from peeling off in dots when the protective film is peeled from the surface of the design layer.
【００２９】上記の保護フィルム付き化粧シートにおい
て、基材層が紙、紙とプラスチックの積層体、プラスチ
ックフィルムからなる構成とすることにより、襖、水回
りないしはキッチン用扉、収納用扉、壁面、ドア面材等
として使用できる保護フィルム付き化粧シートとするこ
とができる。In the decorative sheet with a protective film described above, the base material layer is made of paper, a laminate of paper and plastic, and a plastic film, so that the sliding door, water or kitchen door, storage door, wall surface, A decorative sheet with a protective film that can be used as a door face material or the like can be provided.
【図１】本発明の第１実施形態の構成を示す断面図。FIG. 1 is a sectional view showing a configuration of a first embodiment of the present invention.
【図２】本発明の第２実施形態の構成を示す断面図。FIG. 2 is a sectional view showing a configuration of a second embodiment of the present invention.
【図３】本発明の第３実施形態の構成を示す断面図。FIG. 3 is a sectional view showing a configuration of a third embodiment of the present invention.
【図４】本発明の第４実施形態の構成を示す断面図。FIG. 4 is a sectional view showing a configuration of a fourth embodiment of the present invention.
【図５】化粧シートに保護フィルムを積層する工程の概
略を示す図。FIG. 5 is a view schematically showing a step of laminating a protective film on a decorative sheet.
１ 保護フィルム ２ 印刷絵柄層 ３ 紙基材層 ４ 保護層 ５ ポリエチレン層 ６ 紙層 ７，８ プラスチック基材層 11 Ｔダイ 12 冷却ロール 13 加圧ロール 14 処理機 15 給紙部 16 排紙部 Ａ，Ｂ，Ｃ，Ｄ 化粧シート DESCRIPTION OF SYMBOLS 1 Protective film 2 Print picture layer 3 Paper base layer 4 Protective layer 5 Polyethylene layer 6 Paper layer 7,8 Plastic base layer 11 T die 12 Cooling roll 13 Pressure roll 14 Processing machine 15 Paper feed section 16 Paper discharge section A , B, C, D decorative sheet
───────────────────────────────────────────────────── フロントページの続き (72)発明者 増田 洋史 東京都新宿区市谷加賀町一丁目１番１号 大日本印刷株式会社内 (72)発明者 中川 均 東京都新宿区市谷加賀町一丁目１番１号 大日本印刷株式会社内 Ｆターム(参考） 4F100 AJ06E AK01D AK03C AK06C AT00A BA03 BA04 BA05 BA07 BA10A BA10C BA10D DG10A EJ17C EJ91C GB07 HB00B HB31B HB31E JL00 JL01 JL10B JN01E YY00C 4F206 AC03 AD05 AD06 AF00 AG01 AG03 JA07 JB02 JB12 ──────────────────────────────────────────────────続 き Continuing on the front page (72) Inventor Hiroshi Masuda 1-1-1, Ichigaya-Kagacho, Shinjuku-ku, Tokyo Inside Dai Nippon Printing Co., Ltd. (72) Inventor Hitoshi Nakagawa 1-1-1, Ichigaga-cho, Shinjuku-ku, Tokyo No. 1 Dai Nippon Printing Co., Ltd. F-term (reference) 4F100 AJ06E AK01D AK03C AK06C AT00A BA03 BA04 BA05 BA07 BA10A BA10C BA10D DG10A EJ17C EJ91C GB07 HB00B HB31B HB31E JL00 JL01 JL10B00 J0301 J0301
Claims (6)
用状態での表面側に保護フィルムが剥離可能に積層され
た保護フィルム付き化粧シートにおいて、前記保護フィ
ルムがポリオレフィン樹脂の押出ラミネーションにより
形成された構成からなることを特徴とする保護フィルム
付き化粧シート。1. A decorative sheet with a protective film having a protective film releasably laminated on a surface side in use of a decorative sheet having a base layer and a design layer, wherein the protective film is formed by extrusion lamination of a polyolefin resin. A decorative sheet with a protective film, comprising:
からなることを特徴とする請求項１記載の保護フィルム
付き化粧シート。2. The decorative sheet with a protective film according to claim 1, wherein the protective film is made of low density polyethylene.
さであることを特徴とする請求項１または２に記載の保
護フィルム付き化粧シート。3. The decorative sheet with a protective film according to claim 1, wherein the protective film has a thickness of 15 to 40 μm.
ることを特徴とする請求項１〜３のいずれかに記載の保
護フィルム付き化粧シート。4. The decorative sheet with a protective film according to claim 1, wherein the design layer comprises a printed picture layer and a protective layer.
積層体からなることを特徴とする請求項１〜４のいずれ
かに記載の保護フィルム付き化粧シート。5. The decorative sheet with a protective film according to claim 1, wherein the base layer is made of paper or a laminate of paper and plastic.
なることを特徴とする請求項１〜４のいずれかに記載の
保護フィルム付き化粧シート。6. The decorative sheet with a protective film according to claim 1, wherein the base layer is made of a plastic film.