JP2001187010A - Laminated sheet for cleaning - Google Patents
Laminated sheet for cleaningInfo
- Publication number
- JP2001187010A JP2001187010A JP37441699A JP37441699A JP2001187010A JP 2001187010 A JP2001187010 A JP 2001187010A JP 37441699 A JP37441699 A JP 37441699A JP 37441699 A JP37441699 A JP 37441699A JP 2001187010 A JP2001187010 A JP 2001187010A
- Authority
- JP
- Japan
- Prior art keywords
- film
- water
- sheet
- hydrolysis
- cleaning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、清掃用シートに関
し、特に、使用後に水中に投棄した場合に分解する清掃
用積層シートに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a cleaning sheet, and more particularly, to a cleaning laminate sheet which is decomposed when discarded in water after use.
【０００２】[0002]
【従来の技術】従来、清掃時において、濡れたところを
拭き取り、使用後はそのまま水に流すことができる清掃
用シートが知られている。この清掃用シートは、水解紙
にバインダーとして水溶性高分子、添加剤にアルカリ金
属や溶剤等が使用されており、従来技術として、バイン
ダーとしてＰＶＡを含有する不織布に含有液を含浸させ
たウエット水解紙（特開平３−２１３５９６号公報）、
特定のＣＭＣ塩と粉末有機酸をバインダーとした水解紙
（特開平６−２２０７９３号公報）、グリセリン、ＰＥ
Ｇ等の保湿剤を含有する水解紙（特開平９−１５４７６
４号公報）、ＰＶＡをバインダーとして硫酸塩等を含浸
させた清拭用ウエット水解紙（特開平９−２１５６２５
号公報）、特定のカルボキシメチルセルロース塩（ＣＭ
Ｃ塩）をバインダーとした水解紙（特開平１０−９６１
８７号公報）等が開示されている。これらの清掃用シー
トは、清掃用として使用に耐える強度があり、また、使
用後に水中に投棄すると崩壊するので水洗トイレ等にフ
ラッシュアウトが可能なものであるため、広く用いられ
ている。2. Description of the Related Art Heretofore, there has been known a cleaning sheet which can wipe off a wet portion at the time of cleaning, and can be poured directly into water after use. This cleaning sheet uses a water-soluble polymer as a binder in hydrolyzed paper and an alkali metal or a solvent as an additive. As a conventional technology, a wet hydrolyzate obtained by impregnating a nonwoven fabric containing PVA as a binder with a liquid is used. Paper (JP-A-3-213596),
Hydrolysis paper using a specific CMC salt and a powdered organic acid as a binder (JP-A-6-220793), glycerin, PE
Water disintegration paper containing a humectant such as G (Japanese Patent Laid-Open No. 9-15476)
No. 4), wet hydrolyzed paper for wiping impregnated with sulfate or the like using PVA as a binder (JP-A-9-215625)
Publication), a specific carboxymethylcellulose salt (CM
Water disintegration paper using C salt) as a binder (JP-A-10-961)
No. 87) and the like. These cleaning sheets are widely used because they have strength enough to be used for cleaning, and can be flushed out in flush toilets and the like because they collapse when discarded in water after use.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、これら
の清掃用シートは水への吸収性、浸透性が良好であるた
め、少し多めの水を拭き取ると清掃用シートの取り扱い
側（手で触れる面）より水がしみ出して拭いている手が
汚れてしまうという問題点があった。特に、トイレの汚
水などを拭き取る際は、多くの人より不満点として挙げ
られていた。そこで、上記問題点を解決するために、水
溶性フィルムと不織布を積層させるものが提案されてい
る。例えば、特開平１０−２１６０６０号公報で開示さ
れているように、加水分解度９０〜９９．９モル％の部
分ケン化ポリビニルアルコールフィルムが不織布に積層
された清掃用シートが提案されている。しかしながら、
これによると、濡れた所の掃除ではフィルムが不織布よ
りはがれてしまうという問題があり、さらに加水分解度
９７モル％の部分ケン化ポリビニルアルコールを使用す
ると、水中に投棄しても容易に溶解せず、トイレを詰ま
らせてしまう等の問題があった。However, these cleaning sheets have good absorbency and permeability to water. Therefore, when a little more water is wiped off, the cleaning sheet is handled on the handling side (the surface to be touched by hand). There is a problem in that the water that oozes out and the wiping hands become dirty. In particular, many people complained of wiping out toilet sewage and the like. Then, in order to solve the above-mentioned problems, a device in which a water-soluble film and a nonwoven fabric are laminated has been proposed. For example, as disclosed in JP-A-10-216060, a cleaning sheet in which a partially saponified polyvinyl alcohol film having a degree of hydrolysis of 90 to 99.9 mol% is laminated on a nonwoven fabric has been proposed. However,
According to this, there is a problem that the film is peeled off from the nonwoven fabric when cleaning a wet place. Further, when partially saponified polyvinyl alcohol having a hydrolysis degree of 97 mol% is used, it does not easily dissolve even when discarded in water. There is a problem that the toilet is clogged.
【０００４】本発明は、前記従来の問題点に鑑みてなさ
れたものであって、濡れた所の清掃時に手を濡らすこと
なく、使用後は水中で容易に溶解することができる清掃
用積層シートを提供することを目的とする。SUMMARY OF THE INVENTION The present invention has been made in view of the above-mentioned conventional problems, and does not wet hands when cleaning wet places and can be easily dissolved in water after use. The purpose is to provide.
【０００５】[0005]
【課題を解決するための手段】本発明は、前記目的を達
成するため、清掃用積層シートを、水解性シートと２種
類の親水性フィルムとを積層させて一体的に構成したこ
とを特徴とするものである。また、前記２種類の親水性
フィルムは、ポリ酢酸ビニルの加水分解度が異なるもの
であって、第１フィルムとする加水分解度９０〜９６モ
ル％の部分ポリビニルアルコールフィルムと、第２フィ
ルムとする加水分解度６５〜８９モル％の部分ポリビニ
ルアルコールフィルムからなり、第２フィルムは第１フ
ィルムと前記水解性シートとの間に配置されることが好
ましい。In order to achieve the above object, the present invention is characterized in that the cleaning laminated sheet is integrally formed by laminating a water-disintegrable sheet and two kinds of hydrophilic films. Is what you do. The two types of hydrophilic films differ in the degree of hydrolysis of polyvinyl acetate, and are a first film and a partial polyvinyl alcohol film having a degree of hydrolysis of 90 to 96 mol%, and a second film. It is preferable that the second film is disposed between the first film and the water-decomposable sheet, and is composed of a partial polyvinyl alcohol film having a degree of hydrolysis of 65 to 89 mol%.
【０００６】本発明によれば、水解性シートと２種類の
親水性フィルムとを積層させることにより、清掃用シー
トに水をしみ込ませても手を濡らすことなく、使用後は
水中で容易に溶解することができる。また、２種類の親
水性フィルムはポリ酢酸ビニルの加水分解度が異なるも
のであって、第１フィルムを加水分解度９０〜９６モル
％の部分ポリビニルアルコールフィルムとすることによ
り、水がしみ込みづらくなり手を濡らすことがなく清掃
が可能となり、第２フィルムを加水分解度６５〜８９モ
ル％の部分ポリビニルアルコールフィルムとして、該第
２フィルムを第１フィルムと前記水解性シートとの間に
配置することにより、前記第２フィルムと第１フィルム
と水解性シートが分離することなく濡れた所の清掃を行
うことができる。According to the present invention, by laminating a water-disintegrable sheet and two types of hydrophilic films, even if the cleaning sheet is impregnated with water, it does not wet the hands and easily dissolves in water after use. can do. Further, the two types of hydrophilic films have different degrees of hydrolysis of polyvinyl acetate, and the first film is a partial polyvinyl alcohol film having a degree of hydrolysis of 90 to 96 mol%, so that water does not easily permeate. Cleaning becomes possible without wetting the hand, and the second film is disposed between the first film and the water-disintegrable sheet as a partial polyvinyl alcohol film having a degree of hydrolysis of 65 to 89 mol%. Thereby, the wet place can be cleaned without separating the second film, the first film, and the water-disintegrable sheet.
【０００７】[0007]
【発明の実施の形態】以下、図面を参照して本発明の実
施形態を詳細に説明する。図１は本発明の実施形態に係
る清掃用積層シートの構成を示す説明図、図２は前記清
掃用積層シートの詳細断面図である。本実施形態は、図
１、図２に示すように、水解性シート４と２種類の親水
性フィルムとを積層させて一体的に構成した清掃用積層
シートである。前記２種類の親水性フィルムは、ポリ酢
酸ビニルの加水分解度が異なるものであって、第１フィ
ルム２とする加水分解度９０〜９６モル％の部分ポリビ
ニルアルコールフィルムと、第２フィルム３とする加水
分解度６５〜８９モル％の部分ポリビニルアルコールフ
ィルムからなり、第２フィルム３は第１フィルム２と前
記水解性シート４との間に配置されるている。Embodiments of the present invention will be described below in detail with reference to the drawings. FIG. 1 is an explanatory view showing a configuration of a cleaning laminated sheet according to an embodiment of the present invention, and FIG. 2 is a detailed sectional view of the cleaning laminated sheet. This embodiment is a cleaning laminated sheet integrally formed by laminating a water-disintegrable sheet 4 and two types of hydrophilic films, as shown in FIGS. 1 and 2. The two types of hydrophilic films differ in the degree of hydrolysis of polyvinyl acetate, and are referred to as a first film 2, a partial polyvinyl alcohol film having a degree of hydrolysis of 90 to 96 mol%, and a second film 3. It is composed of a partial polyvinyl alcohol film having a degree of hydrolysis of 65 to 89 mol%, and the second film 3 is disposed between the first film 2 and the hydrolyzable sheet 4.
【０００８】実施例１は、２種類の親水性フィルム、す
なわち、ポリ酢酸ビニルの加水分解度９２モル％の部分
ポリビニルアルコールフィルムで構成された第１フィル
ム２と、ポリ酢酸ビニルの加水分解度８０モル％の部分
ポリビニルアルコールフィルムで構成された第２フィル
ム３と、水解性シート４との３層を積層させて一体的に
構成した清掃用積層シート１である。前記第２フィルム
３は、前記第１フィルム２と前記水解性シート４との間
に配置されている。前記水解性シート４は、目付２５ｇ
／ｍ2の水解紙が用いられている。前記第１フィルム
２、第２フィルム３、水解性シート４はシールヒート方
式により、積層一体化されている。In Example 1, a first film 2 composed of two kinds of hydrophilic films, that is, a partial polyvinyl alcohol film having a hydrolysis degree of polyvinyl acetate of 92 mol%, and a hydrolysis degree of polyvinyl acetate of 80% was used. This is a cleaning laminated sheet 1 integrally formed by laminating three layers of a second film 3 composed of a mol% partial polyvinyl alcohol film and a water-disintegrable sheet 4. The second film 3 is disposed between the first film 2 and the water-disintegrable sheet 4. The water-disintegrable sheet 4 has a basis weight of 25 g.
/ M 2 of water-disintegrated paper is used. The first film 2, the second film 3, and the water-disintegrable sheet 4 are laminated and integrated by a seal heat method.
【０００９】ここで、シールヒート方式について説明す
る。第１フィルム２、第２フィルム３、そして水解性シ
ート４を重ね合わせ、約１２０℃で４〜１０ｍ／ｍｉｎ
の速度で連続的にヒートシールを行う。この時、温度が
高すぎるとポリ酢酸ビニル加水分解物の水溶性が悪くな
り、温度が低すぎると十分なシール強度が得られない。
また、シール速度が遅すぎると加熱時間が長くなりポリ
酢酸ビニル加水分解物の水溶性が悪くなる。また、シー
ル速度が早すぎると加熱時間が短くなり十分なシール強
度が得られない。Here, the seal heat method will be described. The first film 2, the second film 3, and the water-disintegrable sheet 4 are superimposed, and at about 120 ° C., 4 to 10 m / min.
Heat sealing is performed continuously at a speed of At this time, if the temperature is too high, the water solubility of the polyvinyl acetate hydrolyzate deteriorates, and if the temperature is too low, sufficient sealing strength cannot be obtained.
On the other hand, if the sealing speed is too slow, the heating time becomes longer, and the water solubility of the polyvinyl acetate hydrolyzate becomes worse. On the other hand, if the sealing speed is too fast, the heating time becomes short, and sufficient sealing strength cannot be obtained.
【００１０】その他の方式として、キャスティング方式
があり、この方式は、ポリ酢酸ビニル加水分解物の水溶
液を回転乾燥ドラムへスリットを通して流延し、水解性
シートを圧着させるものである。この時、ポリ酢酸ビニ
ル水溶液の濃度、温度を微妙にコントロールする必要が
ある。したがって、ヒートシール方式の方が生産性、コ
ストの点で好ましい。As another method, there is a casting method, in which an aqueous solution of a polyvinyl acetate hydrolyzate is cast through a slit to a rotary drying drum, and a water-disintegrable sheet is pressed. At this time, it is necessary to delicately control the concentration and temperature of the aqueous polyvinyl acetate solution. Therefore, the heat sealing method is preferable in terms of productivity and cost.
【００１１】上記構成によれば、第１フィルム２をポリ
酢酸ビニルの加水分解度９０〜９６モル％とすることに
より、スプレーした洗剤等を拭き取るときに手を濡らす
ことなく、かつ使用後はトイレで水洗することができ
る。ここで、加水分解度が９０モル％未満では、洗剤を
拭き取り中に溶けてしまい防漏できず、加水分解度が９
６モル％を超えたのでは、使用後に水に溶けないのでト
イレに流せないことになる。According to the above construction, the first film 2 has a degree of hydrolysis of polyvinyl acetate of 90 to 96 mol%, so that hands are not wet when wiping the sprayed detergent and the like, and the toilet is used after use. Can be washed with water. Here, if the degree of hydrolysis is less than 90 mol%, the detergent is dissolved during wiping and cannot be prevented from leaking.
If it exceeds 6 mol%, it will not dissolve in water after use, and will not be able to be flushed into the toilet.
【００１２】また、第１フィルム２と水解性シート４だ
けでは、濡れたときに容易に剥がれてしまうため、第２
フィルム３をポリ酢酸ビニルの加水分解度６５〜８９モ
ル％とすることにより、第１フィルム２と水解性シート
４を濡れても強固に接着させることができる。これによ
ると洗剤や水等で濡れることにより第２フィルム３が溶
けて糊の役目を果たすことになる。ここで、加水分解度
が８９モル％を超えたのでは、水解性シート４との接着
が十分ではなく、また、加水分解度が６５モル％未満で
は、溶解速度が速すぎて接着力が弱く、何れも清掃中に
剥がれてしまうことになる。In addition, since the first film 2 and the water-disintegrable sheet 4 are easily separated when wet,
By setting the degree of hydrolysis of the film 3 to 65 to 89 mol% of the polyvinyl acetate, the first film 2 and the hydrolyzable sheet 4 can be firmly adhered to each other even when wet. According to this, the second film 3 is melted by being wet with a detergent, water, or the like, and functions as a paste. Here, if the degree of hydrolysis exceeds 89 mol%, the adhesion to the water-decomposable sheet 4 is not sufficient, and if the degree of hydrolysis is less than 65 mol%, the dissolution rate is too fast and the adhesion is weak. , Will be peeled off during cleaning.
【００１３】したがって、実施例１の清掃積層シートに
よれば、水解性シートと２種類の親水性フィルムとを積
層させることにより、清掃用シートに水をしみ込ませて
も手を濡らすことなく、使用後は水中で容易に溶解する
ことができる。Therefore, according to the cleaning laminate sheet of Example 1, the water-disintegrable sheet and the two types of hydrophilic films are laminated so that the hands can be used without dampening the hands even if the cleaning sheet is impregnated with water. Thereafter, it can be easily dissolved in water.
【００１４】実施例２は、２種類の親水性フィルム、す
なわち、ポリ酢酸ビニルの加水分解度９５モル％の部分
ポリビニルアルコールフィルムで構成された第１フィル
ムと、ポリ酢酸ビニルの加水分解度８５モル％の部分ポ
リビニルアルコールフィルムで構成された第２フィルム
と、水解性シートとの３層を積層させて一体的に構成し
た清掃用積層シートである。前記第２フィルムは、前記
第１フィルムと前記水解性シートとの間に配置されてい
る。前記水解性シートは、目付３０ｇ／ｍ2の水解紙が
用いられている。前記第１フィルム、第２フィルム、水
解性シートはシールヒート方式により、積層一体化され
ている。In Example 2, a first film composed of two kinds of hydrophilic films, that is, a partial polyvinyl alcohol film having a hydrolysis degree of polyvinyl acetate of 95 mol%, and a hydrolysis degree of polyvinyl acetate of 85 mol% was used. % Is a cleaning laminated sheet integrally formed by laminating three layers of a second film composed of a partially polyvinyl alcohol film and a water-disintegrable sheet. The second film is disposed between the first film and the water-disintegrable sheet. As the water disintegratable sheet, water disintegrated paper having a basis weight of 30 g / m 2 is used. The first film, the second film, and the water-disintegrable sheet are laminated and integrated by a seal heat method.
【００１５】以上の構成によれば、実施例２も実施例１
と同様の効果を奏する。According to the above configuration, the second embodiment is also the first embodiment.
It has the same effect as.
【００１６】以下に、前記実施例１、２とともに、比較
例１〜３の構成を示すとともに、下記の６例の評価テス
トを図３に示す。 〇実施例１：第１フィルム 加水分解度９２モル％の部分ポリビニルアルコ ールフィルム 第２フィルム 加水分解度８０モル％の部分ポリビニルアルコ ールフィルム 水解シート 目付２５ｇ／ｍ2の水解紙 〇実施例２：第１フィルム 加水分解度９５モル％の部分ポリビニルアルコ ールフィルム 第２フィルム 加水分解度８５モル％の部分ポリビニルアルコ ールフィルム 水解シート 目付２５ｇ／ｍ2の水解紙 〇比較例１：水解シートのみ 目付２５ｇ／ｍ2の水解紙 〇比較例２：第１フィルム 加水分解度８０モル％の部分ポリビニルアルコ ールフィルム 第２フィルム 加水分解度８０モル％の部分ポリビニルアルコ ールフィルム 水解シート 目付２５ｇ／ｍ2の水解紙 〇比較例３：第１フィルム 加水分解度９９モル％の部分ポリビニルアルコ ールフィルム 第２フィルム 加水分解度９９モル％の部分ポリビニルアルコ ールフィルム 水解シート 目付２５ｇ／ｍ2の水解紙 〇比較例４：第１フィルム 加水分解度９９モル％の部分ポリビニルアルコ ールフィルム 第２フィルム 加水分解度８５モル％の部分ポリビニルアルコ ールフィルム 水解シート 目付３０ｇ／ｍ2の水解紙The structures of Comparative Examples 1 to 3 are shown below together with Examples 1 and 2, and evaluation tests of the following six examples are shown in FIG. 〇Example 1: First film Partial polyvinyl alcohol film having a degree of hydrolysis of 92 mol% Second film Partial polyvinyl alcohol film having a degree of hydrolysis of 80 mol% Hydrolysis sheet Hydrolysis paper having a basis weight of 25 g / m 2 〇Example 2: First Film Partial polyvinyl alcohol film having a degree of hydrolysis of 95 mol% Second film Partial polyvinyl alcohol film having a degree of hydrolysis of 85 mol% Hydrolysis sheet Hydrolysis paper having a basis weight of 25 g / m 2 〇Comparative Example 1: Only hydrolysis sheet having a basis weight of 25 g / m 2 Water disintegration paper 〇Comparative example 2: First film Partial polyvinyl alcohol film with a hydrolysis degree of 80 mol% Second film Hydrolysis paper Partial polyvinyl alcohol film with a hydrolysis degree of 80 mol% Water disintegration sheet Water disintegration paper with a basis weight of 25 g / m 2 〇Comparative example 3: First film Partial polyvinyl alcohol with a degree of hydrolysis of 99 mol% Rufirumu second film degree of hydrolysis 99 mol% partially polyvinyl alcohol Rufirumu hydrolyzate sheet basis weight 25 g / m 2 of water-decomposable paper 〇 Comparative Example 4: the first film a degree of hydrolysis of 99 mol% portion of polyvinyl alcohol Rufirumu second film hydrolysis degree 85 mol% partial polyvinyl alcohol film Hydrolysis sheet Hydrolysis paper with a basis weight of 30 g / m 2
【００１７】なお、実施例、比較例の評価は以下の方法
により評価したものである。 〇清掃時の手の濡れ アクリル板上にスプレーした約１ｇの水を、 シート（１６×１４ｃｍ）で拭き取り、 以下の基準で評価した。 〇：拭いた手がほとんど濡れない ×：濡れる 〇清掃時のフィルムの剥がれ アクリル板上にスプレーした約１ｇの水を、 シート（１６×１４ｃｍ）で拭き取り、 以下の基準で評価した。 〇：フィルムの剥がれ無し △：一部剥がれる ×：剥がれる 〇シートの水解性 水洗トイレにシート（１６×１４ｃｍ）を ５枚入れ、水をフラッシュアウトした後の シートの水解性を以下の基準で評価した。 〇：便器内にシートが残っていない ×：シートが残っているThe evaluations of the examples and comparative examples were evaluated by the following methods.濡 れ Hand wetness during cleaning About 1 g of water sprayed on an acrylic plate was wiped off with a sheet (16 × 14 cm), and evaluated according to the following criteria. 〇: The wiped hand hardly gets wet ×: Wet 〇 Peeling of film at the time of cleaning About 1 g of water sprayed on an acrylic plate was wiped off with a sheet (16 × 14 cm) and evaluated according to the following criteria. 〇: No peeling of film △: Partially peeled ×: Peeled 〇 Water disintegration of sheet Five sheets (16 × 14 cm) were placed in a flush toilet, and the water disintegration of the sheet after flushing out water was evaluated according to the following criteria. did. 〇: No sheet left in toilet bowl ×: Sheet left
【００１８】[0018]
【発明の効果】以上説明した通り本発明によれば、水解
性シートと２種類の親水性フィルムとを積層させること
により、清掃用シートに水をしみ込ませても手を濡らす
ことなく、使用後は水中で容易に溶解することができ
る。また、２種類の親水性フィルムはポリ酢酸ビニルの
加水分解度が異なるものであって、第１フィルムを加水
分解度９０〜９６モル％の部分ポリビニルアルコールィ
ルムとすることにより、水がしみ込みづらくなり手を濡
らすことがなく清掃が可能となり、第２フィルムを加水
分解度６５〜８９モル％の部分ポリビニルアルコールフ
ィルムとして、該第２フィルムを第１フィルムと前記水
解性シートとの間に配置することにより、前記第２フィ
ルムと第１フィルムと水解性シートが分離することなく
濡れた所の清掃を行うことができる。As described above, according to the present invention, by laminating a water-disintegrable sheet and two kinds of hydrophilic films, even if the cleaning sheet is impregnated with water, the hand is not wetted and used. Can be easily dissolved in water. Further, the two types of hydrophilic films differ in the degree of hydrolysis of polyvinyl acetate, and the first film is made of a partial polyvinyl alcohol film having a degree of hydrolysis of 90 to 96 mol%, so that water does not easily permeate. Cleaning becomes possible without wetting the hand, and the second film is disposed between the first film and the water-disintegrable sheet as a partial polyvinyl alcohol film having a degree of hydrolysis of 65 to 89 mol%. Thereby, the wet place can be cleaned without separating the second film, the first film, and the water-disintegrable sheet.
【図１】本発明の実施形態に係る清掃用積層シートの構
成を示す説明図である。FIG. 1 is an explanatory diagram showing a configuration of a cleaning laminated sheet according to an embodiment of the present invention.
【図２】前記清掃用積層シートの詳細断面図である。FIG. 2 is a detailed sectional view of the cleaning laminated sheet.
【図３】実施形態に係る実施例１、２と比較例１〜３の
性能評価テストを示すものである。FIG. 3 shows performance evaluation tests of Examples 1 and 2 and Comparative Examples 1 to 3 according to the embodiment.
１ 清掃用積層シート ２ 第１フィルム ３ 倍２フィルム ４ 水解性シート DESCRIPTION OF SYMBOLS 1 Laminated sheet for cleaning 2 First film 3 times 2 film 4 Water disintegrable sheet
───────────────────────────────────────────────────── フロントページの続き (72)発明者 小泉 茂 東京都墨田区本所一丁目３番７号 ライオ ン株式会社内 Ｆターム(参考） 2D037 AE03 AE17 3B074 AA04 AA08 AB01 AC00 BB01 ────────────────────────────────────────────────── ─── Continuation of the front page (72) Inventor Shigeru Koizumi 1-3-7 Honjo, Sumida-ku, Tokyo F-term in Lion Corporation (reference) 2D037 AE03 AE17 3B074 AA04 AA08 AB01 AC00 BB01
Claims (2)
とを積層させて一体的に構成したことを特徴とする清掃
用積層シート。1. A cleaning laminated sheet wherein a water-disintegrable sheet and two types of hydrophilic films are laminated and integrally formed.
酸ビニルの加水分解度が異なるものであって、第１フィ
ルムとする加水分解度９０〜９６モル％の部分ポリビニ
ルアルコールフィルムと、第２フィルムとする加水分解
度６５〜８９モル％の部分ポリビニルアルコールフィル
ムからなり、第２フィルムは第１フィルムと前記水解性
シートとの間に配置されることを特徴とする請求項１に
記載の清掃用積層シート。2. The two types of hydrophilic films differ in the degree of hydrolysis of polyvinyl acetate, and include a partial polyvinyl alcohol film having a degree of hydrolysis of 90 to 96 mol% as a first film; The cleaning according to claim 1, wherein the film is composed of a partial polyvinyl alcohol film having a degree of hydrolysis of 65 to 89 mol%, and the second film is disposed between the first film and the water-disintegrable sheet. For laminated sheet.