JP2001172893A - Pulp sheet for forming deodorant product - Google Patents
Pulp sheet for forming deodorant productInfo
- Publication number
- JP2001172893A JP2001172893A JP36265699A JP36265699A JP2001172893A JP 2001172893 A JP2001172893 A JP 2001172893A JP 36265699 A JP36265699 A JP 36265699A JP 36265699 A JP36265699 A JP 36265699A JP 2001172893 A JP2001172893 A JP 2001172893A
- Authority
- JP
- Japan
- Prior art keywords
- pulp
- pulp sheet
- sheet
- forming
- bleached
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、脱臭性能にすぐれ
た綿状パルプやパルプ粉末、パルプ細片等を形成するた
めのパルプシートに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a pulp sheet for forming floc pulp, pulp powder, pulp fragments and the like having excellent deodorizing performance.
【０００２】[0002]
【従来の技術】木材チップやバガス（砂とうきびのしぼ
り粕）を蒸解液で蒸解することによってパルプを製造す
ることは広く行われている。このようなパルプの製造方
法においては、得られるパルプの白色度を高めるため
に、未漂白（未晒）パルプを次亜塩素酸塩や二酸化塩素
等の塩素系漂白剤を用いて漂白することにより、漂白パ
ルプ（晒しパルプ）とすることも知られている。一方、
パルプを解繊して綿状パルプを製造することは知られて
おり、このような綿状パルプは、おむつ等の吸収性物品
における尿等の体液吸収材料として使用されている。2. Description of the Related Art Pulp is widely produced by digesting wood chips and bagasse (sand and cane squeezed cake) with a cooking liquor. In such a pulp manufacturing method, unbleached (unbleached) pulp is bleached using a chlorine bleach such as hypochlorite or chlorine dioxide in order to increase the whiteness of the obtained pulp. It is also known to use bleached pulp (bleached pulp). on the other hand,
It is known to disintegrate pulp to produce cotton-like pulp, and such cotton-like pulp is used as a body fluid absorbing material such as urine in absorbent articles such as diapers.
【０００３】[0003]
【発明が解決しようとする課題】本発明は、脱臭性能に
すぐれた綿状パルプ等の脱臭製品を形成するための原料
となるパルプシートを提供することをその課題とする。SUMMARY OF THE INVENTION An object of the present invention is to provide a pulp sheet as a raw material for forming a deodorized product such as floc pulp having excellent deodorizing performance.
【０００４】[0004]
【課題を解決するための手段】本発明者らは、前記課題
を解決すべく鋭意研究を重ねた結果、本発明を完成する
に至った。即ち、本発明によれば、塩素系漂白剤を用い
て漂白された漂白パルプから形成された坪量１５０〜３
５０ｇ／ｍ2のパルプシート中に硫酸第１鉄を含む水溶
液を含浸させた後乾燥してなる脱臭製品形成用パルプシ
ートが提供される。Means for Solving the Problems The present inventors have conducted intensive studies to solve the above-mentioned problems, and as a result, have completed the present invention. That is, according to the present invention, a basis weight of 150 to 3 formed from bleached pulp bleached using a chlorine-based bleaching agent.
Provided is a pulp sheet for forming a deodorized product, which is obtained by impregnating a 50 g / m 2 pulp sheet with an aqueous solution containing ferrous sulfate and then drying.
【０００５】[0005]
【発明の実施の形態】本発明で用いるパルプシートは、
塩素系漂白剤を用いて漂白された漂白パルプから形成さ
れたものである。この場合、塩素系漂白剤には、塩素、
二酸化塩素、亜塩素酸ナトリウム、次亜塩素酸ナトリウ
ム等が包含される。パルプとしては、木材パルプの他、
バガスパルプ（砂とうきび粕からのパルプ）等の非木材
パルプが用いられる。パルプシートは、パルプを抄紙
し、乾燥することによって得られる。パルプシートにお
いて、その坪量は、１５０〜３５０ｇ／ｍ2、好ましく
は２００〜３００ｇ／ｍ2である。程度である。DETAILED DESCRIPTION OF THE INVENTION The pulp sheet used in the present invention is as follows.
It is formed from bleached pulp bleached using a chlorine bleach. In this case, chlorine bleach contains chlorine,
Chlorine dioxide, sodium chlorite, sodium hypochlorite and the like are included. In addition to wood pulp,
Non-wood pulp such as bagasse pulp (pulp from sand and cane meal) is used. The pulp sheet is obtained by paper-making and drying pulp. The pulp sheet has a basis weight of 150 to 350 g / m 2 , preferably 200 to 300 g / m 2 . It is about.
【０００６】本発明により脱臭製品形成用のパルプシー
トを製造するには、先ず、前記パルプシートを硫酸第１
鉄（ＦｅＳＯ4）を含む水溶液と接触させる。この水溶
液において、その硫酸第１鉄の濃度は特に制約されない
が、通常、０．５〜２０％、好ましくは５〜１５％程度
である。In order to manufacture a pulp sheet for forming a deodorized product according to the present invention, first, the pulp sheet is treated with sulfuric acid
It is brought into contact with an aqueous solution containing iron (FeSO 4 ). In this aqueous solution, the concentration of ferrous sulfate is not particularly limited, but is usually about 0.5 to 20%, preferably about 5 to 15%.
【０００７】前記硫酸第１鉄を含む水溶液には、その安
定化剤として、水溶性のカルボン酸又はその塩を含有さ
せることができる。カルボン酸又はその塩としては、Ｌ
−アスコルビン酸、エルソルビン酸、グリコール酸、ヒ
ドロキシ酢酸、酒石酸、コハク酸、クエン酸、リンゴ
酸、フマル酸、エチレンジアミンテトラカルボン酸（Ｅ
ＤＴＡ）及びそれらのナトリウム塩やカルシウム塩等が
挙げられる。カルボン酸又はその塩の添加量は、硫酸第
１鉄１００重量部当り、１０〜１５０重量部、好ましく
は１５〜１００重量部、より好ましくは２０〜８０重量
部の割合である。このカルボン酸は、硫酸第１鉄に対し
てキレート化能を有する。The aqueous solution containing ferrous sulfate may contain a water-soluble carboxylic acid or a salt thereof as a stabilizer. As the carboxylic acid or a salt thereof, L
-Ascorbic acid, elsorbic acid, glycolic acid, hydroxyacetic acid, tartaric acid, succinic acid, citric acid, malic acid, fumaric acid, ethylenediaminetetracarboxylic acid (E
DTA) and their sodium salts and calcium salts. The amount of the carboxylic acid or a salt thereof added is 10 to 150 parts by weight, preferably 15 to 100 parts by weight, more preferably 20 to 80 parts by weight, per 100 parts by weight of ferrous sulfate. This carboxylic acid has a chelating ability for ferrous sulfate.
【０００８】前記硫酸第１鉄を含む水溶液を用いるパル
プシートの処理においては、そのシート中に含まれる塩
素分が効果的に除去される。本発明者らの研究によれ
ば、前記塩素系漂白剤を用いて得られる漂白パルプのシ
ートには、微量の塩素分が含まれ、この塩素分は硫酸第
１鉄を含む水溶液と接触させると、塩素ガスとして除去
されることが確認された。塩素分は、ダイオキシン原因
物質であるので本発明のパルプシートに含まれるのは好
ましくないが、前記処理によりほぼ完全に除去されるの
で、本発明の方法は非常に有利である。In the treatment of a pulp sheet using the aqueous solution containing ferrous sulfate, chlorine contained in the sheet is effectively removed. According to the study of the present inventors, a sheet of bleached pulp obtained using the chlorine-based bleaching agent contains a trace amount of chlorine, and when the chlorine is brought into contact with an aqueous solution containing ferrous sulfate. , Was confirmed to be removed as chlorine gas. Since chlorine is a dioxin-causing substance, it is not preferable to include it in the pulp sheet of the present invention. However, the process of the present invention is very advantageous because it is almost completely removed by the treatment.
【０００９】前記硫酸第１鉄を含む水溶液を用いるパル
プシートを処理により、その硫酸第１鉄が含浸されたパ
ルプシートが得られる。次に、このパルプシートは、乾
燥される。その乾燥温度は、特に制約されず、常温〜１
００℃でよい。前記のようにして得られるパルプシート
は、硫酸第１鉄を含有するもので、アンモニアや有機ア
ミンに対して高い反応性を有する。このパルプシートに
おいて、その硫酸第１鉄の含有量は、０．５〜３０％、
好ましくは１〜２０％である。By treating a pulp sheet using the aqueous solution containing ferrous sulfate, a pulp sheet impregnated with the ferrous sulfate is obtained. Next, the pulp sheet is dried. The drying temperature is not particularly limited, and is from room temperature to 1
00 ° C may be sufficient. The pulp sheet obtained as described above contains ferrous sulfate and has high reactivity to ammonia and organic amines. In this pulp sheet, the ferrous sulfate content is 0.5 to 30%,
Preferably it is 1 to 20%.
【００１０】本発明のパルプシートは、高い吸水性と同
時に、アンモニアや有機アミンに対して高い反応性を有
し、綿状パルプや、パルプ粉末、パルプ細片等を得るた
めの原料として好適のものである。本発明のパルプシー
ト、から綿状パルプを製造するには、これを乾燥状態で
綿状に解繊すればよい。この場合の解繊装置としては、
公知のもの、例えば（株）瑞光製、モデルＦＦ−２７０
等を用いることができる。パルプ細片を作るには、前記
パルプシートをシュレッダー等で裁断すればよい。ま
た、パルプ粉末を作るには、前記パルプシートを粉砕す
ればよい。The pulp sheet of the present invention has high water absorbency and high reactivity to ammonia and organic amines, and is suitable as a raw material for obtaining floc pulp, pulp powder, pulp chips and the like. Things. In order to produce fluffy pulp from the pulp sheet of the present invention, the pulp may be fibrillated in a dry state. In this case, as a defibrating device,
Known products, for example, Model FF-270, manufactured by Zumiko Co., Ltd.
Etc. can be used. In order to produce pulp strips, the pulp sheet may be cut with a shredder or the like. Further, in order to produce pulp powder, the pulp sheet may be ground.
【００１１】[0011]
【実施例】次に本発明を実施例によりさらに詳細に説明
する。Next, the present invention will be described in more detail with reference to examples.
【００１２】実施例１ 次亜塩素酸ナトリウムで漂白されたバガスパルプからの
パルプシート（坪量：２６０ｇ／ｍ2、寸法：１０ｃｍ
×１０ｃｍ）を、硫酸第１鉄・７水和物（ＦｅＳＯ4・
７Ｈ2Ｏ）を濃度１０％で含む水溶液中に浸漬した後、
これを水中から取出し、これを４０℃の恒温槽に入れて
乾燥してパルプシートを得た。Example 1 Pulp sheet from bagasse pulp bleached with sodium hypochlorite (basis weight: 260 g / m 2 , size: 10 cm)
× 10 cm) was replaced with ferrous sulfate heptahydrate (FeSO 4.
7H 2 O) after immersion in an aqueous solution containing 10%
This was taken out from the water, placed in a constant temperature bath at 40 ° C., and dried to obtain a pulp sheet.
【００１３】実施例２ 実施例１において、水溶液中にクエン酸を濃度１０％で
添加した以外は同様にして実験を行ってパルプシートを
得た。Example 2 A pulp sheet was obtained in the same manner as in Example 1, except that citric acid was added to the aqueous solution at a concentration of 10%.
【００１４】参考例１ 前記実施例２で得たパルプシートに、アンモニア水（濃
度：２．４％）０．５ｃｃを滴下したところ、そのアン
モニア水は迅速に吸収され、また、そのアンモニア水を
吸収したパルプには、アンモニア臭は全く感じられなか
った。Reference Example 1 When 0.5 cc of aqueous ammonia (concentration: 2.4%) was dropped on the pulp sheet obtained in Example 2, the aqueous ammonia was quickly absorbed, and the aqueous ammonia was removed. The absorbed pulp did not show any ammonia odor.
【００１５】[0015]
【発明の効果】本発明のパルプシートを用いることによ
り、脱臭性能にすぐれた綿状パルプや、パルプ粉末、パ
ルプ細片等を容易に得ることができる。本発明のパルプ
シートを用いて得られる綿状パルプは、不織布原料とて
用いられる他、紙おむつや生理用品等の原料として用い
ることができる。本発明のパルプシートから得られるパ
ルプ粉末やパルプ細片も、前記綿状パルプと同様に用い
ることができる。By using the pulp sheet of the present invention, it is possible to easily obtain cotton-like pulp, pulp powder, pulp chips and the like having excellent deodorizing performance. The cotton-like pulp obtained by using the pulp sheet of the present invention can be used not only as a raw material for nonwoven fabrics but also as a raw material for disposable diapers, sanitary products and the like. Pulp powder and pulp chips obtained from the pulp sheet of the present invention can be used in the same manner as the flocculent pulp.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ａ６１Ｆ 13/472 Ｆターム(参考） 3B029 BA12 BD22 4C003 HA01 4C080 AA06 CC08 CC09 CC12 HH05 JJ06 KK08 LL10 MM02 NN24 QQ03 4L055 AA06 AC05 AD03 AD04 AD06 AG08 AG34 AH50 BE10 EA08 FA30 GA26 GA50 ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 7 Identification code FI theme coat ゛ (Reference) A61F 13/472 F-term (Reference) 3B029 BA12 BD22 4C003 HA01 4C080 AA06 CC08 CC09 CC12 HH05 JJ06 KK08 LL10 MM02 NN24 QQ03 4L055 AA06 AC05 AD03 AD04 AD06 AG08 AG34 AH50 BE10 EA08 FA30 GA26 GA50
Claims (2)
ルプから形成された坪量１５０〜３５０ｇ／ｍ2のパル
プシート中に硫酸第１鉄を含む水溶液を含浸させた後乾
燥してなる脱臭製品形成用パルプシート。1. A pulp sheet having a basis weight of 150 to 350 g / m 2 formed from bleached pulp bleached using a chlorine bleach is impregnated with an aqueous solution containing ferrous sulfate and then dried. Pulp sheet for forming deodorized products.
む請求項１の脱臭製品形成用パルプシート。2. The pulp sheet for forming a deodorized product according to claim 1, wherein the aqueous solution contains a carboxylic acid or a salt thereof.