JP2001155547A - Flameproof insulating paper - Google Patents
Flameproof insulating paperInfo
- Publication number
- JP2001155547A JP2001155547A JP33669499A JP33669499A JP2001155547A JP 2001155547 A JP2001155547 A JP 2001155547A JP 33669499 A JP33669499 A JP 33669499A JP 33669499 A JP33669499 A JP 33669499A JP 2001155547 A JP2001155547 A JP 2001155547A
- Authority
- JP
- Japan
- Prior art keywords
- flame
- insulating paper
- retardant
- flame retardant
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】この発明は、民生用電気器
具、車載用電気器具等の絶縁材料として用いられる難燃
絶縁紙に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a flame-retardant insulating paper used as an insulating material for consumer electric appliances, vehicle electric appliances and the like.
【０００２】[0002]
【従来の技術】従来、民生用電気器具、車載用電気器具
等の絶縁材料としては、ポリエステルフィルム、プレス
ボード又はバルカナイズドファイバ板等が用いられてき
た。これらの絶縁材料は、ＪＩＳ Ｃ２３１８、Ｃ２３
０５及びＣ２３１５に品質基準が示され、用途に応じて
各材料が選択されている。ポリエステルフィルムは、高
い絶縁性と強度が得られるが、耐熱温度が低く、発熱体
の近くでは使用できない欠点がある。一方、プレスボー
ドは紙基材のため、打ち抜き加工性に適しており、２５
０℃以下であれば加熱変性することなく使用することが
できるが、これ以上の高温条件下で使用する場合は難燃
剤を添加する必要がある。また、バルカナイズドファイ
バ板は、セルロース系プラスチックを用いて製造され、
強度と電気特性が良好であるが、打ち抜き加工及び曲げ
加工には適さず、プレスボード同様、高温条件下での使
用に際しては難燃剤の添加が必要である。2. Description of the Related Art Hitherto, polyester films, press boards, vulcanized fiber boards, and the like have been used as insulating materials for consumer electric appliances, vehicle electric appliances, and the like. These insulating materials are JIS C2318, C23
05 and C2315 indicate quality standards, and each material is selected according to the application. The polyester film has high insulation properties and strength, but has a drawback that it cannot be used near a heating element because of its low heat resistance temperature. On the other hand, the press board is suitable for punching workability because it is a paper base material.
If it is 0 ° C. or lower, it can be used without heat denaturation, but if it is used under higher temperature conditions, it is necessary to add a flame retardant. The vulcanized fiber board is manufactured using a cellulosic plastic,
Although it has good strength and electrical properties, it is not suitable for punching and bending, and requires the addition of a flame retardant when used under high temperature conditions, like a press board.
【０００３】従来、プレスボード及びバルカナイズドフ
ァイバ板に用いられる難燃剤として、塩素化ポリオレフ
ィンと三酸化アンチモンを併用したものが用いられてき
た。ところが、近年の環境問題に対する関心の高まりか
ら、焼却時にダイオキシンの発生源となりうる塩素化ポ
リオレフィンの使用は敬遠されている。また、アンチモ
ンは発ガン性が指摘され、環境庁の水質基準の要監視項
目に加えられ、製造時に工業廃水への流出が規制されつ
つある。また、日本も批准している「廃棄物の移動に関
するバーゼル条約」において、アンチモンを含有する廃
棄物を国外へ移動することは禁止されている。Hitherto, a combination of chlorinated polyolefin and antimony trioxide has been used as a flame retardant for press boards and vulcanized fiber boards. However, the use of chlorinated polyolefins, which can be a source of dioxin during incineration, has been shunned due to the growing interest in environmental issues in recent years. In addition, antimony has been pointed out as a carcinogen, has been added to the monitoring requirements of the Environment Agency's water quality standards, and its outflow to industrial wastewater during production is being regulated. The Basel Convention on the Movement of Waste, which Japan has ratified, prohibits the transfer of antimony-containing waste outside the country.
【０００４】その他、紙基材用難燃剤としては、壁紙用
にスルファミン酸グアニジン、メチロール化スルファミ
ン酸グアニジンが用いられているが、水溶性のため耐水
性に劣り、電気絶縁性の低下を引き起こす。また、水酸
化アルミニウムや水酸化マグネシウム等も使用されてい
るが、これらは加熱すると水分を放出するため電気絶縁
用途には適さない。硫酸、リン酸及び五酸化リンについ
ても難燃剤としての効果が知られているが、セルロース
を分解してしまうため紙基材には使用することができな
い。[0004] In addition, guanidine sulfamate and methylolated guanidine sulfamate are used as wallpaper flame retardants for wallpaper, but they are poor in water resistance due to water solubility and cause a decrease in electrical insulation. Although aluminum hydroxide and magnesium hydroxide are also used, they release moisture when heated, so they are not suitable for electric insulation. Sulfuric acid, phosphoric acid, and phosphorus pentoxide are also known as flame retardants, but cannot be used for paper substrates because they degrade cellulose.
【０００５】特開昭５２−３９９３１号には、メラミン
付加ポリリン酸アンモニウムと水酸化アルミニウムとの
混合物を難燃剤とした難燃紙が開示されているが、加熱
時に水酸化アルミニウムから水が発生し、さらにメラミ
ン付加ポリリン酸アンモニウムの水に対する溶解度が高
いため絶縁紙としての用途には適さない。特開平８−４
９１９６号及び特開平８−４９１９７号にはポリリン酸
アンモニウムをメラミンで被覆した難燃剤を使用した難
燃紙が開示されているが、加熱時にポリリン酸アンモニ
ウムがセルロースから水を奪うので、難燃紙の強度が低
下するという欠点がある。以上の状況から、塩素化ポリ
オレフィン及び三酸化アンチモンを併用した難燃剤に代
替するものが求められているが、これに代わる難燃剤は
見出されていないのが現状である。Japanese Unexamined Patent Publication (Kokai) No. 52-39931 discloses a flame-retardant paper using a mixture of melamine-added ammonium polyphosphate and aluminum hydroxide as a flame retardant, but water is generated from the aluminum hydroxide during heating. Furthermore, the solubility of melamine-added ammonium polyphosphate in water is high, so that it is not suitable for use as insulating paper. JP-A-8-4
No. 9196 and JP-A-8-49197 disclose flame retardant papers using a flame retardant in which ammonium polyphosphate is coated with melamine. However, since ammonium polyphosphate deprives cellulose of water when heated, flame retardant paper is used. However, there is a disadvantage that the strength of the steel is reduced. Under the circumstances described above, a substitute for a flame retardant using a combination of a chlorinated polyolefin and antimony trioxide has been demanded, but no flame retardant has been found to replace this.
【０００６】[0006]
【発明が解決しようとする課題】本発明の課題は、ハロ
ゲン又はアンチモンを使用することなく、十分な難燃性
と電気絶縁性を有する難燃絶縁紙を提供することであ
る。難燃性については、ＪＩＳ Ｋ６９１１及びＵＬ
（米国保険業者研究所）規格に示されるＶ−０の水準を
目標とした。また、絶縁性等の品質基準はＪＩＳ Ｃ２
３０５に示されたプレスボード２種の基準に準拠したも
のを目標とした。SUMMARY OF THE INVENTION An object of the present invention is to provide a flame-retardant insulating paper having sufficient flame retardancy and electrical insulation without using halogen or antimony. For flame retardancy, see JIS K6911 and UL
(U.S.A. Insurers Institute) The target was the level of V-0 indicated in the standard. In addition, quality standards such as insulation are JIS C2
The objective was to comply with the two types of press boards shown in 305.
【０００７】[0007]
【課題を解決するための手段】本発明の主題は、木材パ
ルプを主体とする紙基材にポリリン酸メラミン粒子、リ
ン酸メラミン粒子及び硫酸メラミン粒子から成る群から
選択される少なくとも１種の難燃剤を１０〜５０重量％
含有する難燃絶縁紙である。本発明の別の主題は、更に
ホウ酸ナトリウム及びケイ酸ナトリウムから成る群から
選択される少なくとも１種のガラス系難燃剤を０．５〜
１５．０重量％含有する上記難燃絶縁紙である。これら
の難燃絶縁紙は、ＵＬ規格Ｖ−０と同等又はそれ以上の
難燃性を有し、その他の品質もプレスボード２種の水準
を示す。SUMMARY OF THE INVENTION The subject of the present invention is that a paper substrate based on wood pulp has at least one difficulties selected from the group consisting of melamine polyphosphate particles, melamine phosphate particles and melamine sulfate particles. 10 to 50% by weight of flame retardant
Contains flame-retardant insulating paper. Another subject of the invention is the addition of at least one glass-based flame retardant selected from the group consisting of sodium borate and sodium silicate to 0.5 to 0.5 g.
The flame-retardant insulating paper contains 15.0% by weight. These flame-retardant insulating papers have a flame retardancy equal to or higher than UL standard V-0, and the other qualities also show the level of two press boards.
【０００８】[0008]
【発明の実施の形態】本発明の難燃絶縁紙は、木材パル
プを主体とした製紙原料に、粉末状の難燃剤を添加分散
した原料を湿式抄紙することにより製造される。本発明
で用いられる木材パルプは、針葉樹クラフトパルプ、広
葉樹クラフトパルプ、サルファイトパルプ等の化学パル
プ、ストーングラインドパルプ、サーモメカニカルパル
プ等の機械パルプ、新聞、コート紙、上質紙等から得ら
れる再生パルプ等の一般的な製紙用パルプを適宜配合す
ることが可能である。また、必要に応じて、ケナフ、
竹、麻等の非木材パルプ、ガラス繊維、ポリエステル繊
維等の非セルロース繊維を配合することも可能である。BEST MODE FOR CARRYING OUT THE INVENTION The flame-retardant insulating paper of the present invention is produced by wet-papermaking a raw material obtained by adding and dispersing a powdery flame retardant to a papermaking raw material mainly composed of wood pulp. Wood pulp used in the present invention is a chemical pulp such as softwood kraft pulp, a hardwood kraft pulp, a sulfite pulp, a mechanical pulp such as a stone grind pulp, a thermomechanical pulp, a recycled pulp obtained from newspaper, coated paper, woodfree paper, or the like. It is possible to appropriately mix common papermaking pulp such as pulp. Also, if necessary, kenaf,
Non-wood pulp such as bamboo and hemp, and non-cellulose fibers such as glass fiber and polyester fiber can also be blended.
【０００９】本発明の難燃剤はリン酸メラミン粒子、ポ
リリン酸メラミン粒子及び硫酸メラミン粒子であり、こ
れらは市販品を用いることができる。例えば、リン酸メ
ラミン粒子としてＴ−７２０２（三和ケミカル）、ポリ
リン酸メラミン粒子としてＭＰＰ（三和ケミカル）、及
び硫酸メラミン粒子としてアピノン９０１等がある。こ
れらの難燃剤を単独で用いてもよいし、又は２種以上を
混合して用いてもよい。これらの難燃剤を、難燃絶縁紙
中の含有量（乾燥時）が１０〜５０重量％、好ましくは
１５〜３０重量％になるように添加する。この含有量が
１０重量％未満の場合には、十分な難燃性が得られず、
ＵＬ規格のＶ−０基準を満たすことができない。また、
この含有量を５０重量％より多くしても、難燃効果は頭
打ちとなり、一般に製紙原料に比べて高価である難燃剤
を高配合することは経済的に無意味になる。The flame retardant of the present invention is melamine phosphate particles, melamine polyphosphate particles and melamine sulfate particles, and commercially available products can be used. For example, melamine phosphate particles include T-7202 (Sanwa Chemical), melamine polyphosphate particles include MPP (Sanwa Chemical), and melamine sulfate particles include Apinone 901. These flame retardants may be used alone or in combination of two or more. These flame retardants are added so that the content (when dried) in the flame retardant insulating paper becomes 10 to 50% by weight, preferably 15 to 30% by weight. If the content is less than 10% by weight, sufficient flame retardancy cannot be obtained,
The V-0 standard of the UL standard cannot be satisfied. Also,
Even if the content is more than 50% by weight, the flame retardant effect reaches a plateau, and it is economically meaningless to mix a flame retardant which is generally expensive compared to papermaking raw materials.
【００１０】本発明の難燃絶縁紙の抄造に際して、難燃
性及び絶縁性に影響を与えない範囲で、サイズ剤、歩留
まり向上剤、紙力向上剤、定着剤、消泡剤及び染料等の
内添薬品、並びにタルク、カオリン、炭酸カルシウム及
び二酸化チタン等の内添填料を適宜製紙原料に添加して
もよい。本発明の難燃絶縁紙の坪量は、用途に合わせて
５０〜５００ｇ／ｍ２の範囲で適宜変更可能であり、密
度についても、用途に合わせて０．７〜１．２ｇ／ｃｍ
３の範囲で適宜変更可能である。When the flame-retardant insulating paper of the present invention is formed,
Sizing agent and yield within the range that does not affect the properties and insulation
Such as ballistic improvers, paper strength improvers, fixing agents, defoamers and dyes
Internal additives, talc, kaolin, calcium carbonate and
And internal fillers such as titanium dioxide, etc.
Is also good. The basis weight of the flame-retardant insulating paper of the present invention depends on the application.
50-500 g / m2Can be changed appropriately within the range of
0.7-1.2g / cm
3Can be changed as appropriate within the range.
【００１１】本発明においては、より高度な難燃性が必
要とされる場合には、更にガラス系難燃剤を含浸法又は
塗工法により、難燃絶縁紙中の含有量（乾燥時）が０．
５〜１５重量％、好ましくは０．５〜５重量％となるよ
うに添加してもよい。このガラス系難燃剤としては、ホ
ウ酸ナトリウム又はケイ酸ナトリウムが好ましい。この
含有量が０．５重量％未満の場合には、難燃性能を更に
向上させる効果を期待することができない。またこの含
有量が１５重量％より多い場合には難燃効果は頭打ちに
なる。また、ガラス系難燃剤は遊離のナトリウムイオン
の影響により電気絶縁性に悪影響を及ぼす傾向があるた
め、５重量％より多い添加は望ましくない。In the present invention, when a higher degree of flame retardancy is required, the content (when dried) in the flame retardant insulating paper is further reduced by impregnation or coating with a glass-based flame retardant. .
You may add so that it may become 5 to 15 weight%, preferably 0.5 to 5 weight%. As the glass flame retardant, sodium borate or sodium silicate is preferable. If the content is less than 0.5% by weight, the effect of further improving the flame retardancy cannot be expected. When the content is more than 15% by weight, the flame retardant effect reaches a plateau. Further, since the glass-based flame retardant tends to have a bad influence on the electric insulation due to the influence of free sodium ions, it is not desirable to add more than 5% by weight.
【００１２】ガラス系難燃剤の添加方法に特に制限はな
く、サイズプレス法、ゲートロールコート法又はグラビ
アロールコート法等により付与される。この際に難燃性
及び絶縁性に影響を与えない範囲で、デンプンやポリビ
ニルアルコール等の紙力向上剤、表面サイズ剤、耐水化
剤及び染料等を適宜配合して表面処理してもよい。The method for adding the glass-based flame retardant is not particularly limited, and is applied by a size press method, a gate roll coating method, a gravure roll coating method, or the like. At this time, a surface treatment may be carried out by appropriately blending a paper strength improver such as starch or polyvinyl alcohol, a surface sizing agent, a water-proofing agent, a dye and the like within a range that does not affect the flame retardancy and the insulating property.
【００１３】[0013]
【実施例】以下、実施例及び比較例により本発明を具体
的に説明するが、本発明はこれらによって限定されるも
のでない。なお、実施例中の「％」は全て「重量％」、
「ｘ／ｙ」は「ｘとｙの重量比」を示す。また、難燃性
及び絶縁性については下記の方法で試験した。 難燃性： ＵＬ（米国保険業者研究所）−９４規格及び
ＪＩＳ−Ｋ６９１１の難燃性試験に準拠した。これらの
規格に従い、難燃性を非難燃、ＨＢ、Ｖ−１（バーナー
で着火後、３０秒以内に消炎する。）、Ｖ−０（バーナ
ーで着火後、１０秒以内に消炎する。）の順に格付けし
た。 絶縁性： ＪＩＳ−Ｃ２１１１に準拠して、絶縁破壊試
験を行った。試験結果が５ｋｖ／ｍｍ以上であれば絶縁
性は良好である。EXAMPLES The present invention will now be described specifically with reference to examples and comparative examples, but the present invention is not limited to these examples. In the examples, “%” is all “% by weight”,
“X / y” indicates “weight ratio between x and y”. Further, the flame retardancy and the insulation were tested by the following methods. Flame retardancy: Complied with UL (U.S.A. Insurance Institute) -94 standard and JIS-K6911 flame retardancy test. According to these standards, the flame retardancy is non-flammable, HB, V-1 (extinguishes flame within 30 seconds after ignition with burner), and V-0 (extinction within 10 seconds after ignition with burner). It was ranked in order. Insulation: A dielectric breakdown test was performed according to JIS-C2111. If the test result is 5 kv / mm or more, the insulation is good.
【００１４】実施例１ 濾水度４００ｍ１（カナダ標準法）の針葉樹クラフトパ
ルプ（ＮＢＫＰ）とポリリン酸メラミン（商品名：ＭＰ
Ｐ、三和ケミカル製）を含有する紙料を酸性抄紙によ
り、ポリリン酸メラミンが２０重量％含有された、坪量
２００ｇ／ｍ２、密度１．２ｇ／ｃｍ３の難燃絶縁紙を
作成した。実施例２ 実施例１の方法で得た難燃絶縁紙に、ホウ酸ナトリウム
（ガラス系難燃剤、商品名：ＦＲ６５０Ｋ、アドコスミ
ック（株）製）水溶液をその付着量が３％となるように
サイズプレス法で付着させ、難燃絶縁紙を作成した。[0014]Example 1 Coniferous Kraft paper with a freeness of 400m1 (Canadian standard method)
Lup (NBKP) and melamine polyphosphate (trade name: MP
P, manufactured by Sanwa Chemical Co., Ltd.)
Weight, containing 20% by weight of melamine polyphosphate
200g / m2, Density 1.2g / cm3The flame retardant insulating paper
Created.Example 2 Sodium borate was added to the flame-retardant insulating paper obtained by the method of Example 1.
(Glass-based flame retardant, trade name: FR650K, Adcosumi
Solution) so that the amount of adhesion is 3%.
It was attached by the size press method to make a flame-retardant insulating paper.
【００１５】比較例１ 濾水度４００ｍ１のＮＢＫＰとポリリン酸メラミン（Ｍ
ＰＰ）を含有する紙料を酸性抄紙により、ポリリン酸メ
ラミンが８重量％含有された、坪量２００ｇ／ｍ２、密
度１．２ｇ／ｃｍ３の難燃絶縁紙を作成した。比較例２ 比較例１で作成した難燃絶縁紙に、ホウ酸ナトリウム
（ガラス系難燃剤、商品名：ＦＲ６５０Ｋ、アドコスミ
ック（株）製）水溶液をその付着量が１０％となるよう
に、サイズプレス法で付着させ、難燃絶縁紙を作成し
た。比較例３ 濾水度４００ｍ１のＮＢＫＰ、塩素化ポリオレフィン及
び三酸化アンチモンを含有する紙料を酸性抄紙により、
塩素化ポリオレフィンが１９．５重量％、三酸化アンチ
モンが０．５重量％含有された、坪量２００ｇ／ｍ２、
密度１．２ｇ／ｃｍ３の難燃絶縁紙を作成した。[0015]Comparative Example 1 NBKP with a freeness of 400 ml and melamine polyphosphate (M
PP) -containing stock is subjected to acidic papermaking to prepare polyphosphate
200g / m grammage containing 8% by weight of lamin2, Dense
Degree 1.2g / cm3Made flame retardant insulating paper.Comparative Example 2 Sodium borate was added to the flame retardant insulating paper prepared in Comparative Example 1.
(Glass-based flame retardant, trade name: FR650K, Adcosumi
(Manufactured by KK Co., Ltd.) so that the attached amount becomes 10%.
To make a flame retardant insulating paper
Was.Comparative Example 3 NBKP with freeness of 400m1, chlorinated polyolefin and
Paper containing antimony and antimony trioxide by acid papermaking
19.5% by weight of chlorinated polyolefin, anti trioxide
200g / m basis weight containing 0.5% by weight of mont2,
Density 1.2g / cm3Made flame retardant insulating paper.
【００１６】これらの難燃絶縁紙の難燃性及び絶縁性を
測定し、その結果を表１に示す。The flame retardancy and insulation properties of these flame-resistant insulating papers were measured, and the results are shown in Table 1.
【表１】 [Table 1]
【００１７】表１から明らかなように、実施例１及び２
の難燃絶縁紙は難燃性及び絶縁性の双方が優れている。
難燃剤の含有率が１０％未満である比較例１の難燃絶縁
紙では難燃性が十分ではなく、ガラス系難燃剤の付着量
を増加して難燃性を向上させた比較例２の難燃絶縁紙は
絶縁性が十分ではない。また、比較例３の難燃絶縁紙は
難燃性及び絶縁性共に優れるが、三酸化アンチモンを含
有しているため、使用後の廃棄が困難である。As is clear from Table 1, Examples 1 and 2
Is excellent in both flame retardancy and insulating properties.
The flame-retardant insulating paper of Comparative Example 1 in which the content of the flame retardant was less than 10% did not have sufficient flame retardancy, and the flame-retardant insulating paper of Comparative Example 2 in which the amount of the glass-based flame retardant was increased to improve the flame retardancy was used. Flame retardant insulating paper does not have sufficient insulation. Further, the flame-retardant insulating paper of Comparative Example 3 is excellent in both flame retardancy and insulating properties, but is difficult to dispose after use since it contains antimony trioxide.
【００１８】[0018]
【発明の効果】本発明の難燃絶縁紙は、難燃規格Ｖ−０
と同等又はそれ以上の難燃性を有し、かつ現在電気絶縁
材料として用いられているプレスボード及びバルカナイ
ズドファイバー板に相当する電気絶縁性を有する。ま
た、本発明の難燃絶縁紙は難燃剤にハロゲン（塩素）及
びアンチモン等の環境に悪影響を与える可能性のある成
分を含まないため、使用後廃棄物として環境に与える負
荷が小さい。従って、本発明の工業的意義は大きい。The flame-retardant insulating paper of the present invention has a flame-retardant standard V-0.
It has the same or higher flame retardancy as that of the press boards, and has electrical insulation properties equivalent to press boards and vulcanized fiber boards currently used as electrical insulation materials. In addition, the flame-retardant insulating paper of the present invention does not contain components that may have an adverse effect on the environment, such as halogen (chlorine) and antimony, in the flame retardant, so that the burden on the environment as waste after use is small. Therefore, the present invention has great industrial significance.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ｃ０９Ｋ 21/12 Ｃ０９Ｋ 21/12 21/14 21/14 Ｄ２１Ｈ 17/51 Ｄ２１Ｈ 17/51 21/34 21/34 Ｆターム(参考） 4H028 AA09 AA40 BA02 BA06 4J002 AH001 DJ007 DK007 EU186 FB076 FD136 FD137 GQ01 4L055 AG05 AG23 AG30 AG35 AG96 AH26 BE08 EA32 FA19 GA02 GA44 5G305 AA03 AB25 AB35 BA15 BA18 BA21 CA43 CA60 CC14 CD13──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛ (Reference) C09K 21/12 C09K 21/12 21/14 21/14 D21H 17/51 D21H 17/51 21/34 21 / 34 F-term (reference) 4H028 AA09 AA40 BA02 BA06 4J002 AH001 DJ007 DK007 EU186 FB076 FD136 FD137 GQ01 4L055 AG05 AG23 AG30 AG35 AG96 AH26 BE08 EA32 FA19 GA02 GA44 5G305 AA03 AB25 AB35 BA15 BA18 BA21 CA43 CA13 CD
Claims (2)
ン粒子及び硫酸メラミン粒子から成る群から選択される
少なくとも１種の難燃剤を１０〜５０重量％含有する難
燃絶縁紙。1. A flame-retardant insulating paper containing 10 to 50% by weight of at least one flame retardant selected from the group consisting of melamine polyphosphate particles, melamine phosphate particles and melamine sulfate particles.
ウムから成る群から選択される少なくとも１種のガラス
系難燃剤を０．５〜１５．０重量％含有する請求項１に
記載の難燃絶縁紙。2. The flame-retardant insulating paper according to claim 1, further comprising 0.5 to 15.0% by weight of at least one glass-based flame retardant selected from the group consisting of sodium borate and sodium silicate. .