JP2001140826A - Stainless nail and its manufacturing method - Google Patents
Stainless nail and its manufacturing methodInfo
- Publication number
- JP2001140826A JP2001140826A JP32236299A JP32236299A JP2001140826A JP 2001140826 A JP2001140826 A JP 2001140826A JP 32236299 A JP32236299 A JP 32236299A JP 32236299 A JP32236299 A JP 32236299A JP 2001140826 A JP2001140826 A JP 2001140826A
- Authority
- JP
- Japan
- Prior art keywords
- stainless steel
- nail
- steel nail
- resin
- stainless
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】この発明はステンレス釘およ
びその製造方法、詳しくは腐食、特にすきま腐食に対し
ての防錆効果の高いステンレス釘およびその製造方法に
関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a stainless steel nail and a method of manufacturing the same, and more particularly to a stainless steel nail having a high rust prevention effect against corrosion, particularly crevice corrosion, and a method of manufacturing the same.
【０００２】[0002]
【従来の技術】釘は、打ち込みにより例えば複数枚の木
板同士を継ぎ合わせる金具であり、通常、細長い胴部の
元側の端に平たい頭部が鍛造されている。釘の先端部
は、その用途に応じて、例えば四角形，六角形，丸形な
どに成形されている。ところで、特殊な釘としてステン
レス釘がある。これは、ステンレス鋼（主にＳＵＳ３０
４）の線材を、釘の形状に付形したものである。ステン
レス釘は、通常の鉄釘に比べて硬く、錆びにくいとい
う、ステンレス鋼の特長を有している。したがって、そ
の用途には、高い防錆性を生かして、例えば雨露にさら
され、または、水中に浸漬されたりして、釘が錆びやす
い環境下にある部材間の継ぎ合わせに利用されている。2. Description of the Related Art A nail is a metal fitting for joining, for example, a plurality of wooden boards together by driving, and a flat head is usually forged at a base end of an elongated body. The tip of the nail is formed into, for example, a square, a hexagon, a round, or the like according to its use. By the way, there is a stainless steel nail as a special nail. This is made of stainless steel (mainly SUS30
The wire rod of 4) is shaped like a nail. Stainless steel nails have the characteristics of stainless steel that they are harder and less rust than ordinary iron nails. Therefore, in its use, it is used for joining seams in an environment where nails are easily rusted by, for example, being exposed to rain or being immersed in water, taking advantage of high rust prevention properties.
【０００３】[0003]
【発明が解決しようとする課題】このように、釘をあつ
かう業者にあっては、今日まで、ステンレス釘は防錆に
優れた釘であるという認識が一般的であった。しかしな
がら、最近になって、このようなステンレス釘であって
も、比較的短期間で錆が発生したという、施工現場から
のデータが報告されている。そのデータの中には、適用
場所が錆の発生しやすい場所という悪条件ではあるもの
の、わずか２年間程度で、釘の胴部の直径の半分以上が
腐食してしまうという事例も報告されている。そこで、
この発明者はその原因を追求するべく、長年にわたり鋭
意研究を行なってきた。その結果、ステンレス釘の腐食
の主な原因は、すきま腐食であることを突き止めた。す
なわち、図７の従来手段に係るステンレス釘の使用状態
の拡大断面図に示すように、ステンレス釘１００と、釘
止めされる部材１０１に穿設された釘孔１０１ａ内壁と
のすきまの内外で濃淡電池が構成されて、このステンレ
ス釘１００の胴部１０２の一部分１０２ａが錆びていた
のである。図７において、１０３は釘止め用の基台であ
る。As described above, it has been generally recognized among those who deal with nails that stainless steel nails are excellent in rust prevention until now. However, data from construction sites has recently been reported that even such stainless steel nails generated rust in a relatively short period of time. According to the data, there are cases where more than half of the diameter of the nail body corrodes in just two years, even under the bad condition that the application place is susceptible to rust. . Therefore,
The inventor of the present invention has been conducting intensive research for many years to pursue the cause. As a result, they found that the main cause of corrosion of stainless steel nails was crevice corrosion. That is, as shown in the enlarged sectional view of the use state of the stainless steel nail according to the conventional means in FIG. 7, the density of the inside and outside of the clearance between the stainless steel nail 100 and the inner wall of the nail hole 101a formed in the member 101 to be nailed is changed. The battery was constructed, and a part 102a of the body 102 of the stainless nail 100 was rusted. In FIG. 7, reference numeral 103 denotes a base for nailing.
【０００４】[0004]
【発明の目的】この発明は、安価で防錆効果の高いステ
ンレス釘およびその製造方法を提供することを、その目
的としている。SUMMARY OF THE INVENTION An object of the present invention is to provide a stainless steel nail which is inexpensive and has a high rust prevention effect, and a method for manufacturing the same.
【０００５】[0005]
【課題を解決するための手段】請求項１に記載の発明
は、ステンレス鋼を形状加工して得られたステンレス釘
において、釘表面が、絶縁性を有する防錆膜によって被
覆されたステンレス釘である。According to the present invention, there is provided a stainless steel nail obtained by shaping stainless steel, wherein the surface of the nail is coated with a stainless steel nail having an insulating property. is there.
【０００６】釘の素材は、ステンレス鋼であれば限定さ
れない。例えば、請求項２のＳＵＳ３０４などが挙げら
れる。その他、ＳＵＳ４１０などのクロム含有率が１３
％以内のマルテンサイト系ステンレス鋼でもよいし、ま
たＳＵＳ４３０といったクロム含有率が１６％以上のフ
ェライト系ステンレス鋼でもよい。さらには、このマル
テンサイト系の強度と、このオーステナイト系の耐酸性
を兼ね備えたＰＨステンレス鋼などでもよい。なお、こ
のフェライト系のステンレス鋼からなる釘には、さらに
高い防錆効果が得られる可能性を有している。[0006] The material of the nail is not limited as long as it is stainless steel. For example, SUS304 of claim 2 is cited. In addition, chromium content such as SUS410 is 13
% Martensitic stainless steel, or a ferritic stainless steel having a chromium content of 16% or more, such as SUS430. Further, PH stainless steel having martensite-based strength and austenitic-based acid resistance may be used. The ferrite-based stainless steel nail has a possibility of obtaining a higher rust prevention effect.
【０００７】また、釘の形状、種類、寸法などは限定さ
れない。汎用の釘は、尖った先端を有する胴部と、この
胴部の元側の端に、平坦な頭部が一体形成されたもので
ある。ただし、頭部がない胴部だけの釘でもよい。釘の
種類としては、例えば、先端が丸いボールポイント，先
端部が傾斜カットされたベベルド・スクエアポイント，
ボールスティクポイント，ブリードクリンチドポイン
ト，バタフライポイント，チゼルポイント，クリンチポ
イント，カップドポイント，ダイヤモンドポイント，ダ
ックビルポイント，ドルポイント（２８度〜４４度），
フィッシュマウスポイント，Ｊ−クリンチポイント，ロ
ングポイント，ショートポイント，ニードルポイント，
ペンシルポイント，パイロットポイント，シャープポイ
ント，シャードスクエアポイント，サイドポイント，ウ
ェッジポイントなどが挙げられる。釘により継ぎ合わさ
れる部材も限定されない。例えば、各種の木材，石材，
プラスチック材，コンクリート材，金属材，セラミック
スなどが挙げられる。なお、請求項３の瓦などであって
もよい。[0007] The shape, type, size, and the like of the nail are not limited. A general-purpose nail has a body having a sharp tip, and a flat head integrally formed at the base end of the body. However, a nail having only a torso without a head may be used. Types of nails include, for example, a ball point with a rounded tip, a beveled square point with a beveled tip,
Ball stick point, bleed clinched point, butterfly point, chisel point, clinch point, cupped point, diamond point, duck bill point, dollar point (28 degrees to 44 degrees),
Fish mouse point, J-clinch point, long point, short point, needle point,
Pencil points, pilot points, sharp points, shard square points, side points, wedge points, and the like. The members joined by the nails are not limited. For example, various kinds of wood, stone,
Examples include plastic materials, concrete materials, metal materials, and ceramics. The roof tile according to claim 3 may be used.
【０００８】ステンレス釘の表面うち、この防錆膜で覆
われる部分は限定されない。釘全体でもよいし、その一
部でもよい。一部を被覆する場合、すきま腐食を防ぐた
めに、少なくとも釘の胴部を被覆する必要がある。ま
た、頭部の裏面の部分にもすきま腐食が起きるおそれが
あるので、この部分も覆った方がよい。防錆膜の厚さは
限定されない。ただし、通常は３〜２０μｍ程度であ
る。防錆膜の素材は、絶縁性を有していれば限定されな
い。例えば、塗料でもよいし、コーティング材でもよ
い。ここでいう絶縁性を有する塗料としては、油性塗
料，繊維素塗料，樹脂塗料（天然樹脂，合成樹脂を含
む），ゴム弾性塗料などが挙げられる。油性塗料として
は、例えば顔料をボイル油で溶いて作製した調合ペイン
ト，樹脂と乾燥油とを加熱してテレビン油などで溶いた
油性ワニス，顔料を油性ワニスで溶いた油性エナメル，
錆止め顔料をボイル油で溶いた錆止めペイントなどが挙
げられる。[0008] The portion of the surface of the stainless steel nail that is covered with the antirust film is not limited. The whole nail or a part thereof may be used. When coating a part, it is necessary to cover at least the body of the nail to prevent crevice corrosion. Also, crevice corrosion may occur on the back surface of the head, so it is better to cover this portion. The thickness of the rust prevention film is not limited. However, it is usually about 3 to 20 μm. The material of the rust prevention film is not limited as long as it has insulating properties. For example, it may be a paint or a coating material. Examples of the paint having insulation properties include an oil paint, a fiber paint, a resin paint (including a natural resin and a synthetic resin), and a rubber elastic paint. Examples of the oil-based paint include a prepared paint prepared by dissolving a pigment in boiling oil, an oil-based varnish obtained by heating a resin and a drying oil and dissolving with a turpentine oil, an oil-based enamel obtained by dissolving a pigment in an oil-based varnish,
A rust preventive paint obtained by dissolving a rust preventive pigment in boil oil is exemplified.
【０００９】繊維素塗料としては、硝化綿に樹脂を加え
て溶剤で溶いたラッカ，顔料をラッカで溶いたエナメ
ル，合成樹脂をラッカで溶いたハイソリッドラッカなど
が挙げられる。また、樹脂塗料の一種である合成樹脂塗
料には、溶剤系、水系および無溶剤系が存在する。この
うち、溶剤系としては、ポリエステルを変成したアルキ
ド樹脂塗料（例えばメラミン樹脂などとアルキド樹脂と
を混合させたアミノアルキド樹脂塗料，酸硬化アミノア
ルキド樹脂塗料など），塩化ビニルまたは酢酸ビニルか
らなるビニル樹脂塗料（塩化ビニル，酢酸ビニルの共重
合樹脂を含む），エポキシ樹脂に硬化剤を加えたもの
で、低温焼き付けされるエポキシ樹脂塗料，ジイソシア
ネートと多価アルコールとの樹脂であるウレタン樹脂塗
料などが挙げられる。さらに、水系としては、酢酸ビニ
ルやアクリル樹脂を乳状化したものに顔料を加えたエマ
ルジョンペント等が挙げられる。そして、無溶剤系とし
ては、エポキシ樹脂やアクリル樹脂の粉体に顔料を加え
た静電吹付け塗料，塩化ビニル樹脂に顔料とガラスビー
ズを加えたトラフィックペイントなどが挙げられる。Examples of the cellulose paint include lacquer obtained by adding a resin to nitrified cotton and dissolving with a solvent, enamel dissolving pigment with lacquer, and high solid lacquer dissolving a synthetic resin with lacquer. In addition, synthetic resin paints, which are one type of resin paints, include solvent-based, water-based, and solvent-free paints. Among these, as the solvent system, alkyd resin coatings obtained by modifying polyester (for example, amino alkyd resin coating obtained by mixing melamine resin and alkyd resin, acid-curing amino alkyd resin coating), vinyl chloride or vinyl acetate Resin paints (including copolymer resins of vinyl chloride and vinyl acetate), epoxy resins with curing agents added, epoxy resin paints that are baked at low temperatures, and urethane resin paints that are resins of diisocyanate and polyhydric alcohol No. Further, examples of the aqueous system include an emulsion pent obtained by adding a pigment to a material obtained by emulsifying vinyl acetate or an acrylic resin. Examples of the solventless system include an electrostatic spray paint obtained by adding a pigment to an epoxy resin or an acrylic resin powder, and a traffic paint obtained by adding a pigment and glass beads to a vinyl chloride resin.
【００１０】なお、この塗料は、塗装後、乾燥されて固
化されることで塗膜となる。この乾燥には２つの種類が
ある。ひとつは、ラッパやニスなどのように溶剤などを
揮発させる乾燥である。揮発後に残った成分が流動性を
失って塗膜となる。これは、速乾性を有するが、溶剤を
加えれば元の液体にもどってしまう。もうひとつは、合
成樹脂などが重合または架橋などの化学反応による乾燥
である。すなわち、高分子物質となって流動性を失う。
この乾燥では、一度固化してしまえば元の状態にはもど
ることがない。[0010] The paint is dried and solidified after coating to form a coating film. There are two types of this drying. One is drying for volatilizing a solvent or the like like a wrapper or a varnish. The components remaining after volatilization lose fluidity to form a coating film. It has a fast drying property, but returns to the original liquid when a solvent is added. The other is drying of a synthetic resin or the like by a chemical reaction such as polymerization or crosslinking. That is, it becomes a polymer substance and loses fluidity.
In this drying, once solidified, it does not return to its original state.
【００１１】なお、この塗料中には、分散剤，可塑剤，
乾燥剤，硬化剤，増粘剤，光沢付与剤，平坦化剤，たれ
防止剤，皮張り防止剤，防腐剤，防かび剤，紫外線吸収
剤などを添加してもよい。この塗料に顔料などの着色剤
を添加すれば、防錆膜で被覆された本発明のステンレス
釘と、被覆されていない従来のステンレス釘とを簡単に
見分けることができる。さらに、流動性の保持や成長に
利用される溶剤または希釈剤としては、水，アルコール
（エタノール他），エステル（酢酸エチル他），ケトン
（アセトン他），炭化水素（トルエン，キシレン他）な
どを採用することができる。また、ステンレス釘の表面
に塗料を塗る方法は限定されない。例えば、上記エポキ
シ樹脂塗料のように、ステンレス釘を塗料を貯めた貯液
槽の液面下に浸漬させた後、これを引き上げて、自然乾
燥または２００℃前後の低温で焼き付ける方法などが挙
げられる。その他、脱水槽の塗料中にステンレス釘を浸
漬させ、その後、この脱水槽を高速回転させて、ステン
レス釘の表面から余分な塗料を遠心力で分離させる方法
などが挙げられる。この他にも、エアスプレー塗装法，
刷毛塗り法，静電塗装法などが挙げられる。塗布は１回
だけでもよいし、繰り返し行なってもよい。なお、通
常、ステンレス釘に塗料を塗装する前には、ステンレス
釘と塗料との密着性を良くするために、ステンレス釘の
洗浄および脱脂といった前処理が施される。ただし、こ
の前処理は必ずしも必要ではない。なお、これらの事項
は、請求項７にも該当する。In this paint, a dispersant, a plasticizer,
A drying agent, a curing agent, a thickening agent, a glossing agent, a flattening agent, an anti-sagging agent, an anti-skinning agent, a preservative, a fungicide, an ultraviolet absorber and the like may be added. If a coloring agent such as a pigment is added to the paint, the stainless steel nail of the present invention coated with a rust preventive film can be easily distinguished from the conventional stainless steel nail not coated. Further, as solvents or diluents used for maintaining and growing fluidity, water, alcohols (ethanol, etc.), esters (ethyl acetate, etc.), ketones (acetone, etc.), hydrocarbons (toluene, xylene, etc.), etc. Can be adopted. Further, the method of applying the paint on the surface of the stainless steel nail is not limited. For example, as in the case of the epoxy resin paint, a method in which a stainless steel nail is immersed under the liquid surface of a liquid storage tank storing the paint, and then pulled up and naturally dried or baked at a low temperature of about 200 ° C. . In addition, there is a method in which a stainless steel nail is immersed in the paint of a dehydration tub, and then the dehydration tub is rotated at a high speed to separate excess paint from the surface of the stainless steel nail by centrifugal force. In addition, the air spray coating method,
A brush coating method, an electrostatic coating method and the like can be mentioned. The application may be performed only once or may be performed repeatedly. Normally, before applying paint to the stainless steel nail, pretreatment such as cleaning and degreasing of the stainless steel nail is performed to improve the adhesion between the stainless steel nail and the paint. However, this pre-processing is not always necessary. These matters also correspond to claim 7.
【００１２】請求項２に記載の発明は、上記ステンレス
釘が、ＳＵＳ３０４製である請求項１に記載のステンレ
ス釘である。このＳＵＳ３０４のステンレス鋼には、軟
質２号（Ｗ２），１／２硬質（１／２Ｈ）などがある。[0012] The invention according to claim 2 is the stainless steel nail according to claim 1, wherein the stainless steel nail is made of SUS304. The stainless steel of SUS304 includes soft No. 2 (W2), 1/2 hard (1 / 2H) and the like.
【００１３】請求項３に記載の発明は、上記ステンレス
釘が瓦止め用の釘である請求項１または請求項２に記載
のステンレス釘である。According to a third aspect of the present invention, there is provided the stainless steel nail according to the first or second aspect, wherein the stainless steel nail is a nail for roofing.
【００１４】請求項４に記載の発明は、上記防錆膜が樹
脂系の塗料からなる請求項１〜請求項３のうちのいずれ
か１項に記載のステンレス釘である。According to a fourth aspect of the present invention, there is provided the stainless steel nail according to any one of the first to third aspects, wherein the rust preventive film is made of a resin-based paint.
【００１５】請求項５に記載の発明は、上記樹脂系の塗
料がアルキド樹脂である請求項４に記載のステンレス釘
である。According to a fifth aspect of the present invention, there is provided the stainless steel nail according to the fourth aspect, wherein the resin paint is an alkyd resin.
【００１６】請求項６に記載の発明は、上記防錆膜の厚
さが３〜２０μｍである請求項１〜請求項５のうちのい
ずれか１項に記載のステンレス釘である。好ましい防錆
膜の厚さは３〜２０μｍである。３μｍ未満では長期間
の防錆効果が期待できないという不都合が生じる。ま
た、２０μｍを超えると製造コストが高くなるという不
都合が生じる。According to a sixth aspect of the present invention, there is provided the stainless steel nail according to any one of the first to fifth aspects, wherein the thickness of the rust preventive film is 3 to 20 μm. The preferred thickness of the rust preventive film is 3 to 20 μm. If it is less than 3 μm, there is a disadvantage that a long-term rust prevention effect cannot be expected. On the other hand, if it exceeds 20 μm, there is a disadvantage that the manufacturing cost increases.
【００１７】請求項７に記載の発明は、ステンレス鋼か
らなる釘の表面を、絶縁性を有する防錆膜によって被覆
するステンレス釘の製造方法である。A seventh aspect of the present invention is a method for manufacturing a stainless steel nail in which the surface of a stainless steel nail is coated with an insulating rust-proof film.
【００１８】請求項８に記載の発明は、上記防錆膜は、
釘の表面に樹脂系の塗料を塗布し、その後、これを乾燥
させて固化した請求項７に記載のステンレス釘の製造方
法である。The invention according to claim 8 is characterized in that the rust-preventive film is
8. The method for producing a stainless steel nail according to claim 7, wherein a resin-based paint is applied to the surface of the nail, and then dried and solidified.
【００１９】[0019]
【作用】この発明によれば、ステンレス釘の表面が絶縁
性を有する防錆膜により被覆されているので、ステンレ
ス釘によって被釘止め部材（例えば請求項３の瓦）を釘
止めして、これを例えば長期間にわたって雨露にさらし
たとしても、すきま腐食によりステンレス釘が錆びるこ
とはない。これは、防錆膜が絶縁膜となっているため
で、ステンレス釘と、釘止めされる部材に穿たれた釘孔
内壁とのすきまの内外で濃淡電池が形成されることがな
いからである。そして、このような効果を有する釘を比
較的安価に製造することができる。According to the present invention, since the surface of the stainless steel nail is covered with the rustproof film having an insulating property, the member to be nailed (for example, the roof tile of claim 3) is nailed by the stainless steel nail. For example, even if the steel nail is exposed to rain for a long period of time, the stainless steel nail does not rust due to crevice corrosion. This is because the rust-preventive film is an insulating film, and the density battery is not formed inside and outside the gap between the stainless nail and the nail hole inner wall formed in the member to be nailed. . And the nail which has such an effect can be manufactured comparatively cheaply.
【００２０】[0020]
【発明の実施の形態】以下、この発明の実施例を図面を
参照して説明する。なお、ここでは屋根瓦を屋根に止め
るステンレス釘を例にとる。図１は、この発明の一実施
例に係る釘の一部断面図を含む拡大正面図である。図２
は、この発明の一実施例に係るステンレス釘の使用状態
の拡大断面図である。Embodiments of the present invention will be described below with reference to the drawings. Here, a stainless nail for fixing a roof tile to the roof is taken as an example. FIG. 1 is an enlarged front view including a partial cross-sectional view of a nail according to an embodiment of the present invention. FIG.
FIG. 1 is an enlarged sectional view of a use state of a stainless steel nail according to one embodiment of the present invention.
【００２１】図１において、１０はこの発明の一実施例
に係る瓦止め用のステンレス釘であり、このステンレス
釘１０は、オーステナイト系ステンレス鋼（ＳＵＳ３０
４）製の線材を加工して作製されている。この釘１０
は、胴部１１の元部側の端に、頭部１２が鍛造されてい
る。胴部１１の寸法は、直径２．５ｍｍ，長さ６５ｍｍ
である。また、頭部１２の寸法は、外径９．０ｍｍ，厚
さ０．８ｍｍである。この一実施例のステンレス釘１０
の特長は、釘表面の全域が、絶縁性を有する有色または
無色の防錆膜１３によって被覆されている点である。防
錆膜１３の素材はアルキド樹脂が採用されている。その
膜厚ｔは５μｍである。図２に示すように、このステン
レス釘１０は、瓦１４に穿設された釘孔１４ａを介し
て、この瓦１４を建物の屋根板１５に固定するための釘
である。In FIG. 1, reference numeral 10 denotes a stainless steel nail for roof tiles according to an embodiment of the present invention. The stainless steel nail 10 is made of austenitic stainless steel (SUS30).
4) It is manufactured by processing a wire rod. This nail 10
The head 12 is forged at the end of the body 11 on the base side. The dimensions of the body 11 are 2.5 mm in diameter and 65 mm in length.
It is. The head 12 has an outer diameter of 9.0 mm and a thickness of 0.8 mm. Stainless steel nail 10 of this embodiment
Is characterized in that the entire surface of the nail surface is covered with a colored or colorless rust preventive film 13 having an insulating property. Alkyd resin is adopted as the material of the rust prevention film 13. The thickness t is 5 μm. As shown in FIG. 2, the stainless steel nail 10 is a nail for fixing the roof tile 14 to a roof panel 15 of a building via a nail hole 14a formed in the roof tile 14.
【００２２】次に、図３〜図６を参照して、この防錆膜
１３により被覆されたステンレス釘１０の製造を、２つ
の異なる装置を用いて説明する。図３は、この発明の一
実施例に係るステンレス釘の製造装置の縦断面図であ
る。図４は、この発明の一実施例に係るステンレス釘の
製造装置の正面図である。図５は、この発明の一実施例
に係るステンレス釘の他の製造装置の縦断面図である。
図６は、この発明の一実施例に係るステンレス釘の他の
製造装置の使用状態を示す説明図である。Next, with reference to FIGS. 3 to 6, the production of the stainless steel nail 10 covered with the antirust film 13 will be described using two different devices. FIG. 3 is a longitudinal sectional view of a stainless steel nail manufacturing apparatus according to one embodiment of the present invention. FIG. 4 is a front view of an apparatus for manufacturing a stainless steel nail according to one embodiment of the present invention. FIG. 5 is a longitudinal sectional view of another apparatus for manufacturing a stainless steel nail according to one embodiment of the present invention.
FIG. 6 is an explanatory view showing a use state of another manufacturing apparatus of the stainless nail according to the embodiment of the present invention.
【００２３】図３および図４には、この発明の一実施例
に係る第１の塗装装置２０を示す。これはバレル回転式
の装置である。第１の塗装装置２０は、蓋２１ａ付きの
８角バレル２１と、この８角バレル２１の両端面の中心
部から外方へ突出した一対の回転軸部２１ｂの片側に連
結された変速機２２と、この変速機２２の内部の変速ギ
ヤ（図外）に噛合されるギヤ（図外）が出力軸２３ａに
固着された回転モータ２３とを有している。図４中の２
４は、他側の回転軸部２１ｂを回転自在に支える軸受で
ある。変速機２２を介して、回転モータ２３の出力軸２
３ａを回転させると、８角バレル２１がそのバレル軸線
を中心に４０ｒｐｍで数分間回転される（図３および図
４の矢印参照）。これにより、あらかじめバレル内に投
入された多数本のステンレス釘１０と、所定比率の溶剤
および有色顔料（無色の場合には添加されない）を含む
所定量のアルキド樹脂ａとが、この８角バレル２１内で
攪拌混合され、その結果、ステンレス釘１０の釘表面の
全域に略均一の厚さｔ（５μｍ）でアルキド樹脂ａが塗
布される。その後、８角バレル２１内から樹脂で塗装さ
れたステンレス釘１０を取り出し、次いで例えば自然乾
燥などによりアルキド樹脂ａを固化させて塗膜となる。
よって、表面全体が防錆膜１３により被われたステンレ
ス釘１０が製造される。このため、従来製法にあった焼
き付け乾燥工程が不要となる。FIGS. 3 and 4 show a first coating apparatus 20 according to an embodiment of the present invention. This is a barrel rotating type device. The first coating apparatus 20 includes an octagonal barrel 21 with a lid 21a, and a transmission 22 connected to one side of a pair of rotary shafts 21b protruding outward from the center of both end faces of the octagonal barrel 21. And a rotation motor 23 having a gear (not shown) meshed with a transmission gear (not shown) inside the transmission 22 fixed to an output shaft 23a. 2 in FIG.
Reference numeral 4 denotes a bearing that rotatably supports the other rotating shaft portion 21b. The output shaft 2 of the rotary motor 23 is transmitted via the transmission 22.
Rotating 3a causes octagonal barrel 21 to rotate about its barrel axis at 40 rpm for several minutes (see arrows in FIGS. 3 and 4). As a result, a large number of stainless nails 10 previously charged in the barrel and a predetermined amount of alkyd resin a containing a predetermined ratio of a solvent and a colored pigment (not added in the case of colorlessness) are combined with the octagon barrel 21. As a result, the alkyd resin a is applied to the entire area of the nail surface of the stainless steel nail 10 with a substantially uniform thickness t (5 μm). After that, the stainless steel nail 10 coated with resin is taken out from the inside of the octagon barrel 21, and then the alkyd resin a is solidified by, for example, natural drying to form a coating film.
Accordingly, the stainless nail 10 whose entire surface is covered with the rust-preventive film 13 is manufactured. For this reason, the baking and drying step which is required in the conventional manufacturing method is not required.
【００２４】次に、図５および図６を参照して、この発
明の一実施例に係る第２の塗装装置３０を示す。これは
遠心分離式の塗装装置である。この第２の塗装装置３０
は、多孔質の内槽３１と、孔が穿設されていない外槽３
２と、内槽３１の底板の中心部に出力軸３３ａの先端が
固着された回転モータ３３とを有している。この槽３
１，３２内にアルキド樹脂ａを比較的多量に貯液し、こ
の状態で内槽３１の内部に多数本のステンレス釘１０を
投入して、これらの釘１０を所定比率の溶剤に溶けたア
ルキド樹脂ａの液中に、所定時間浸漬させる。その後、
外槽３２の底板に設けられた排水孔３２ａを開口し、ア
ルキド樹脂ａを抜き取ってから、回転モータ３３により
内槽３１を１０００ｒｐｍで数分間だけ高速回転させ
る。これにより、ステンレス釘１０の表面に付着した余
分なアルキド樹脂ａが、その遠心力によって外方へ吹き
飛ばされる。その後、例えば自然乾燥することで、同様
に釘表面の全領域が防錆膜１３により被覆されたステン
レス釘１０が安価に製造される。なお、アルキド樹脂ａ
を有色にした場合には、仮に従来の釘の中に混ざって
も、ひと目でこの実施例のステンレス釘１０を見分ける
ことができる。Next, referring to FIGS. 5 and 6, a second coating apparatus 30 according to one embodiment of the present invention is shown. This is a centrifugal type coating device. This second coating device 30
Is a porous inner tank 31 and an outer tank 3 having no holes.
2 and a rotary motor 33 to which the tip of an output shaft 33a is fixed at the center of the bottom plate of the inner tank 31. This tank 3
Alkyd resin a is stored in a relatively large amount in each of the first and second 32, and in this state, a large number of stainless steel nails 10 are charged into the inner tank 31, and these nails 10 are dissolved in a predetermined ratio of an alkyd resin. It is immersed in the liquid of the resin a for a predetermined time. afterwards,
The drainage hole 32a provided in the bottom plate of the outer tank 32 is opened, the alkyd resin a is extracted, and then the inner tank 31 is rotated by the rotating motor 33 at 1000 rpm for several minutes at a high speed. As a result, excess alkyd resin a attached to the surface of the stainless steel nail 10 is blown outward by the centrifugal force. Thereafter, for example, by natural drying, the stainless nail 10 in which the entire area of the nail surface is similarly covered with the rust prevention film 13 is manufactured at low cost. The alkyd resin a
Is colored, the stainless steel nail 10 of this embodiment can be identified at a glance even if it is mixed in a conventional nail.
【００２５】このステンレス釘１０は、通常の釘と同様
のあつかいで保管および使用することができる。図２に
は、このステンレス釘１０を用いて、瓦１４を屋根１５
に固定した状態を示している。このように、ステンレス
釘１０の表面が絶縁性を有する防錆膜１３により被覆さ
れているので、ステンレス釘１０によって瓦１４を釘止
めして、これを屋根の上で、数年間もの長い間雨露にさ
らしても、すきま腐食によってこのステンレス釘１０が
錆びることはない。これは、防錆膜１３が絶縁膜とな
り、ステンレス釘１０と、瓦１４の釘孔１４ａとのすき
まの内外で濃淡電池が形成されないためである。また、
防錆膜１３には顔料が含まれているので、この発明品と
従来品とをひと目で見分けることができる。また、ステ
ンレス釘か否かは、従前どおり磁石に着磁するかどうか
で簡単に判断することができる。The stainless steel nail 10 can be stored and used in the same manner as a normal nail. FIG. 2 shows that the stainless steel nail 10 is used to attach the tile 14 to the roof 15.
Shows the state fixed to. As described above, since the surface of the stainless steel nail 10 is covered with the rust-preventive film 13 having an insulating property, the tile 14 is nailed by the stainless steel nail 10 and the roof is exposed to the rain for many years for several years. The stainless steel nail 10 will not rust due to crevice corrosion. This is because the rust preventive film 13 becomes an insulating film, and no concentration battery is formed inside and outside the gap between the stainless steel nail 10 and the nail hole 14a of the roof tile 14. Also,
Since the rust preventive film 13 contains a pigment, the invention product and the conventional product can be distinguished at a glance. Further, whether or not a stainless steel nail can be easily determined based on whether or not the magnet is magnetized as before.
【００２６】ここで、実際に、従来の防錆膜により被覆
されていないステンレス釘と、上記一実施例の防錆膜で
被覆されたステンレス釘とについて、いぶし瓦片を木材
片に釘止めしたミニサンプルにつき、そのすきま腐食試
験の結果を報告する。なお、従来のステンレス釘は、防
錆膜が被覆されていない一実施例のステンレス釘と同一
素材、同一寸法のものとする。この試験にあたっては、
各ミニサンプルを６０℃に保持されたＣｌ− ＋ＳＯ ４
２− 雰囲気中に６４日間だけ暴露し、両者のすきま腐
食の状態を対比した。その結果、従来のステンレス釘で
は、胴部の一部表面に赤錆が発生した。これに対して、
防錆膜により被われた一実施例のステンレス釘の場合に
は、腐食はまったく発生していなかった。Here, actually, a conventional rust-preventive film is coated.
Stainless steel nails that have not been
For coated stainless steel nails and smashed tile pieces on wood
For a mini-sample nailed to a piece, the crevice corrosion test
Report the results of the experiment. Conventional stainless steel nails are
Same as stainless steel nail of one example without rust film coating
The material shall be of the same dimensions. In this test,
Each mini sample was treated with Cl held at 60 ° C.− + SO 4
2- Exposure to atmosphere for only 64 days
Eating conditions were compared. As a result, with conventional stainless steel nails
Red rust occurred on some surfaces of the body. On the contrary,
In case of stainless steel nail of one embodiment covered with rust prevention film
Had no corrosion at all.
【００２７】[0027]
【発明の効果】この発明によれば、ステンレス釘の表面
を絶縁性を有する防錆膜によって被覆するようにしたの
で、すきま腐食によってステンレス釘が錆びてしまうこ
とを防ぐことができる。しかも、この防錆対策を安価に
行なうことができる。According to the present invention, since the surface of the stainless steel nail is covered with the insulating rust preventive film, the stainless steel nail can be prevented from being rusted by crevice corrosion. Moreover, this rust prevention measure can be performed at low cost.
【図面の簡単な説明】[Brief description of the drawings]
【図１】この発明の一実施例に係る釘を拡大して示す正
面図である。FIG. 1 is an enlarged front view showing a nail according to an embodiment of the present invention.
【図２】この発明の一実施例に係るステンレス釘の使用
状態を拡大して示す断面図である。FIG. 2 is an enlarged sectional view showing a use state of the stainless steel nail according to one embodiment of the present invention.
【図３】この発明の一実施例に係るステンレス釘の製造
装置の縦断面図である。FIG. 3 is a longitudinal sectional view of a stainless steel nail manufacturing apparatus according to one embodiment of the present invention.
【図４】この発明の一実施例に係るステンレス釘の製造
装置の正面図である。FIG. 4 is a front view of an apparatus for manufacturing a stainless steel nail according to one embodiment of the present invention.
【図５】この発明の一実施例に係るステンレス釘の他の
製造装置の縦断面図である。FIG. 5 is a longitudinal sectional view of another apparatus for manufacturing a stainless steel nail according to one embodiment of the present invention.
【図６】この発明の一実施例に係るステンレス釘の他の
製造装置の使用状態を示す説明図である。FIG. 6 is an explanatory view showing a use state of another manufacturing apparatus of the stainless nail according to the embodiment of the present invention.
【図７】従来手段に係るステンレス釘の使用状態を拡大
して示す断面図である。FIG. 7 is an enlarged sectional view showing a use state of a stainless steel nail according to a conventional means.
１０ ステンレス釘、 １３ 防錆膜、 １４ 瓦、 ａ アルキド樹脂。 10 Stainless steel nail, 13 Rust prevention film, 14 Roof tile, a Alkyd resin.
Claims (8)
テンレス釘において、 釘表面が、絶縁性を有する防錆
膜によって被覆されたステンレス釘。1. A stainless steel nail obtained by shaping stainless steel, wherein the nail surface is covered with an insulating rust preventive film.
ある請求項１に記載のステンレス釘。2. The stainless steel nail according to claim 1, wherein said stainless steel nail is made of SUS304.
請求項１または請求項２に記載のステンレス釘。3. The stainless steel nail according to claim 1, wherein the stainless steel nail is a nail for roof tiles.
項１〜請求項３のうちのいずれか１項に記載のステンレ
ス釘。4. The stainless steel nail according to claim 1, wherein the rust preventive film is made of a resin-based paint.
請求項４に記載のステンレス釘。5. The stainless steel nail according to claim 4, wherein the resin-based paint is an alkyd resin.
請求項１〜請求項５のうちのいずれか１項に記載のステ
ンレス釘。6. The stainless steel nail according to claim 1, wherein the thickness of the rust preventive film is 3 to 20 μm.
性を有する防錆膜によって被覆するステンレス釘の製造
方法。7. A method for manufacturing a stainless steel nail, wherein the surface of the nail made of stainless steel is covered with an insulating rust preventive film.
を塗布し、その後、これを乾燥させて固化した請求項７
に記載のステンレス釘の製造方法。8. The rust-preventive film is obtained by applying a resin-based paint to the surface of a nail, and then drying and solidifying the resin-based paint.
The method for producing a stainless steel nail according to item 1.