JP2001113620A - Water section product - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a water section product having no possibility of peeling of short fibers even in the case when it is under wet condition and which can be stably handled by suppressing slip when it is used and wherein appearance and feeling of quality can be improved by providing an electrostatic flocked body with excellent adhesiveness of the short fibers, flocking properties and water resistance. SOLUTION: An electrostatic flocked body wherein the surface of a base material 2 comprising a polypropylene resin is coated with an adhesive member 7 comprising a primer 7b and an adhesive material 7a applied on the primer 7b and short fibers 8 are electrostatically flocked through the adhesive member 7, is provided.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a plumbing device such as a bath chair, a transfer table, a bath mat, and a porcelain used as a stool or the like in a bathroom or a washing tub.

[0002]

2. Description of the Related Art FIG. 10 is a perspective view of a bath chair which is a conventional plumbing product. In the figure, reference numeral 21 denotes a bath chair made of polypropylene resin, which comprises a base 22 on which a user sits, and four legs 23 suspended from the lower surface of the base 22. A suction cup 24 made of a soft synthetic resin is attached to each lower end.

[0003] When the bath chair 21 is used in a bathroom, the bath chair 21 is placed on a floor of a bathroom washing place, for example, and the pedestal 22 is pressed from above. The suction cups 24 are attached to the floor of the washing place by suction. Next, the user sits on the platform 22 to wash his body and the like.

[0004]

In the conventional bath chair 21 as described above, since the suction cups 24 attached to the legs 23 are attached to the floor of a bathroom washroom or the like, the bathroom is slippery. Also, stable use can be obtained. However, in the bath chair 21 made of plastic, since the upper surface of the base 22 on which the user sits is formed substantially flat, when the user sits on the bath chair 21 to wash his / her body, Hot water, soap and foam attached to the body or the bath chair 21 make the surface, particularly the upper surface, of the base 22 slippery, and especially for persons with physical disabilities, the elderly and children, the surface of the base 22 slips. It was a serious problem because it could fall.

Therefore, it is conceivable to form the upper surface of the base 22 into a shape that wraps around the user's hips. However, the surface is smooth because it is made of plastic. It did not come to a resolution. Moreover, the smoothness of the surface of the base 22 is not particularly bad texture, but in some cases, it may be felt hard.

Further, in Japanese Patent Publication No. Sho 60-223, a primer layer is formed on a propylene resin substrate with a composition obtained by adding an ethylene vinyl acetate copolymer and / or an epoxy rubber to a chlorinated polyolefin,
There is disclosed an electrostatic flocking product in which an adhesive layer is formed on a primer layer, and further, short fibers are electrostatically flocking in the adhesive layer.

However, this electrostatic flocking product is used in the interior of automobiles, and is not used in places that always come into contact with water. Although short fibers may not be peeled off when the surface is scratched with a nail, etc., it may be possible to maintain good quality, but when wet, the short fibers are easily peeled off when the surface of the electrostatic flocking product is scratched. There is a risk that it will.

SUMMARY OF THE INVENTION The present invention has been made to solve the above-mentioned problems, and is intended to solve the above-mentioned problems. However, an object of the present invention is to provide a plumbing product that can be handled with good stability while suppressing slippage during use without stripping of short fibers, and can also improve the appearance and texture.

[0009]

In a plumbing product according to the present invention, an adhesive member comprising a primer and an adhesive applied on the primer is applied to a surface of a base material made of a polypropylene resin, and the adhesive member is provided. And a short fiber is provided with an electrostatic flocking body through which the short fibers are electrostatically flocking.

In the plumbing product according to the present invention, the adhesive is a mixture of a urethane paint and a urethane adhesive.

In the plumbing product according to the present invention, the adhesive is a mixture in which a urethane paint and a urethane adhesive are mixed in substantially the same ratio.

In the plumbing product according to the present invention, the urethane paint is a urethane two-pack paint.

In the plumbing product according to the present invention, the urethane adhesive is a urethane one-component adhesive.

[0014]

DESCRIPTION OF THE PREFERRED EMBODIMENTS Embodiment 1 1 is a plan view of Embodiment 1 of the present invention, FIG. 2 is a front view thereof, FIG. 3 is a right side view of FIG. 1, FIG. 4 is a sectional view taken along line AA of FIG. 1, and FIG.
It is an enlarged view of a part. In the figure, reference numeral 1 denotes a bath chair, which is a plumbing product, and comprises a base 2 having a substantially rectangular planar shape and a pair of legs 3 fixed to the lower surface of the base 2.

As shown in FIG. 1, the pedestal 2 is made of a polypropylene resin, which is a plastic, has a substantially rectangular planar shape with four chamfered corners, and has a front shape with left, right, left and rear edges. It is formed in a substantially dish shape curved upward so as to enclose the buttocks and the like. In the vicinity of the center of the base 2, a plurality of holes 4 are provided for draining, each having a small circular shape in plan view, and the plan shape is substantially circular along the front side of the left and right sides along each side. An arc-shaped, elongated hole-shaped holding portion 5 for carrying is provided. Further, an intersecting groove 6 into which the pair of legs 3 is fitted is provided on the lower surface side of the base 2.

As shown in FIG. 5, at least the surface of the platform 2, which is in contact with the seat when the user is seated on the bath chair 1, for example, except for the lower surface, is applied to the surface of the platform 2. A pile 8 of short fibers (for example, 0.8 mm long) made of, for example, nylon fiber, is provided via an adhesive member 7 composed of a primer 7b and a bonding material 7a in which a paint and an adhesive are mixed and applied to the surface of the primer 7b. Has been planted. This flocking process is an electrostatic process fixed type, which is one of the flocking processes, and the process is as follows. The surface of the base portion 2 of the polypropylene blow molded product, which is the base material, on which the flocking process is to be performed is wiped and cleaned with a cloth containing toluene (degreasing treatment). The primer 7b of the adhesive member 7 is applied by spraying to the cleaned work surface of the base 2. After the application, it is left at room temperature for about 10 minutes and dried. An adhesive 7a in which the paint of the adhesive member 7 and the adhesive are mixed in a substantially equal ratio is applied to the processed surface of the base 2 by spraying. After the application, the short fiber pile 8 is electrostatically implanted on the adhesive member 7 (adhesive 7a). (Electrostatic flocking uses static electricity, and the surface of the base 2 to which the adhesive member 7 is applied is
This is an electric flocking method in which the charged pile 8 is attached by electrostatic attraction. After the electrostatic flocking, heat and dry at 80 ° C. for 60 minutes.

Here, the adhesive 7a as one component of the adhesive member 7 is, for example, a product name of a urethane two-pack type paint:
R240, a urethane paint manufactured by Nippon Bee Chemical Co., Ltd., and a trade name: Sungrip NO. 2926, a urethane adhesive manufactured by Sanwa Kogyo Kogyo Co., Ltd. in a mixture of approximately the same amount (here, 1: 1). This is because if the urethane paint is too much more than the urethane adhesive, the adhesion will be good but the surface hardening will be fast and the workability will be poor. On the other hand, if the urethane adhesive is too much more than the urethane, the coating film becomes thicker and the flocking property (piercing) of the pile 8 is improved, but the adhesiveness is deteriorated and the pile 8 is easily peeled, and the water resistance is not satisfactory. The primer 7b as the other component of the adhesive member 7 is, for example, trade name: KBK
65K2K, a modified acrylic resin-based primer manufactured by Nippon NS Co., Ltd. is desirable. Incidentally, a chlorinated modified polyolefin resin primer may be used.

The pair of legs 3 is formed, for example, in a substantially inverted U-shape by a cylindrical metal material, and is formed of a rubber-like elastic body at both ends thereof. A substantially trapezoidal foot 9 fitted to the end is attached. The legs 3 intersect at substantially the center of the respective upper surfaces, and the upper surface including the intersection is fitted into the groove 6 provided on the lower surface of the base 2, and the plurality of screws 10 Fixed. An adjusting unit 11 for adjusting the height of the base 2 is provided below each leg 3. The feet 9 made of rubber-like elastic material are non-slip when installed on the floor of a bathroom, for example, in a washing room. Instead of the feet 9, a suction cup made of a soft synthetic resin and adsorbed on the floor is used. It may be. Further, the adjustment unit 11 may be omitted.

When the bath chair 1 is used in the bathroom, for example, in the first embodiment thus configured, first, the bath chair 1 is installed at a desired position on the bathroom, for example, on the floor of a washing room. Next, the user sits on the base 2 of the bath chair 1. At this time, when the installation position is to be changed, each of the holding portions 5 provided on the base portion 2 is grasped by hand, lifted and moved. Next, the user cleans the body and the like. At this time, the hot water, soap and foams used for washing may be removed from the user's body or bath chair 1.
The pile 8 is electrostatically planted on the surface of the platform 2 where the user comes in contact when sitting on the bath chair 1, so that friction occurs between the user and the pile 8 and The surface (upper surface) of the portion 2 becomes less slippery, and slip off from the base portion 2 is prevented.

As described above, since the pile 8 is electrostatically planted on the surface of the base 2 at least when the user is seated on the bath chair 1, the user can use the bath chair 1.
When washing the body or the like while sitting on the floor, even if the hot water, soap, foam and the like used for washing adhere to the user's body or the bath chair 1, friction occurs between the user and the pile 8 The difficulty of sliding on the surface of the base 2 is maintained,
It is possible to prevent the slide from falling off the base 2. Also,
By the pile 8 on which the electrostatic flocking is performed, a soft texture can be obtained on the surface of the pedestal portion 2 so that the sitting comfort is improved and the aesthetic appearance can be improved.

Further, since the adhesive member 7 is composed of the adhesive 7a and the primer 7b in which urethane paint and urethane adhesive are mixed at substantially the same ratio, the adhesion between the adhesive 7a and the primer 7b is improved. The flocking property with the pile 8 is improved. As a result, the base portion 2 which is an electrostatic flocking body in which the pile 8 is electrostatically planted via the adhesive member 7 is peeled even when the flocked portion of the platform portion 2 is scratched with a nail or the like in handling. It is possible to obtain the bath chair 1 having good adhesion to the base portion 2 and good flocking ability without having to do so. The bath chair 1 is used in a wet place such as a bathroom. Even in such a case, the pile 8 does not peel off, and the bath chair 1 having excellent water resistance can be obtained.

Embodiment 2 FIG. 6 is a plan view of a second embodiment of the present invention, FIG. 7 is a front view and a right side view thereof,
In the second embodiment, in the bath chair 1 according to the first embodiment, the side surface shape is substantially L above the rear portion of the base portion 2.
The backrest 1 is connected via a pair of connecting portions 13 formed in a letter shape.
2 is provided.

The backrest 12 is made of a plastic polypropylene resin, and has a substantially elliptical front shape and is formed in an arc shape such that the planar shape wraps around the user's back. The upper part of the backrest 12 has a backrest 12.
A carrying grip 14 having an elongated hole-like planar shape is provided along the length direction of the pair. On the back side of the backrest 12, a groove 15 into which upper end portions of a pair of connecting portions 13 are fitted. Are provided near the left and right ends of the backrest 12 so as to be orthogonal to the length direction of the backrest 12. At least on the surface of the backrest 12 that contacts when the user is seated on the bath chair 1, for example, on the surface except for the substantially back side, the pile 8 is electrostatically attached via the adhesive member 7, similarly to the base 2. Hair transplanted.

The pair of connecting portions 13 are formed, for example, in a substantially L-shape by a cylindrical metal material. The upper ends of the connecting portions 13 are fitted into the grooves 15 of the backrest 12, and a plurality of screws 16 are used. The lower end of each connecting portion 13 is fixed to the lower surface near the intersection of the pair of legs 3 with a plurality of screws 17.
It is fixed by.

With such a configuration, substantially the same operation and effect as those of the first embodiment can be obtained. Even when the user sits down on the bath chair 1 and cleans his / her body, the base 2
In addition, the pile 8 electrostatically planted on the surface of the backrest 12 makes it hard to slip, and can prevent a user from slipping off the bath chair 1. In addition, the surfaces of the base 2 and the backrest 12 have a soft texture and the sitting comfort is improved, and the bath chair 1 that can improve the aesthetic appearance can be obtained. Further, the pile 8 was electrostatically implanted with the pile 8 via the adhesive member 7 constituted by the adhesive 7a and the primer 7b in which the urethane paint and the urethane adhesive were mixed at a substantially equal ratio. The base portion 2 and the backrest 12 are in a wet state while the pile 8 is not peeled off even when the flocked portion is scratched with a nail or the like in handling, and the bath chair 1 with good adhesion and flocking properties is obtained. Even when used in a place, the pile 8 does not peel off, so that the bath chair 1 with excellent water resistance can be obtained.

Therefore, the base 2 and the backrest 12 of the bath chair 1, which is an electrostatic flocking body in which the pile 8 is electrostatically planted with the pile 8 on the surface that contacts when the user sits on the bath chair 1, at least, In the flocking, by using the adhesive member 7 composed of the adhesive 7a and the primer 7b in which the urethane paint and the urethane adhesive are mixed at a substantially equal ratio, the adhesiveness and the flocking property of the pile 8 are improved.
Even in a wet state, the pile 8 does not peel off and becomes excellent in water resistance, and its flocking process makes its surface less slippery. Therefore, such an electrostatic flocked body is suitable for a plumbing product. You can see that. The effect of the electrostatic flocking is specifically described below using examples.

[0027]

EXAMPLES Examples 1 and 2 and Comparative Examples 1 to 7 <Preparation of Electrostatic Flocked Body> The surface of a plate member of a blow-molded polypropylene article as a substrate is degreased (wipe clean with a cloth containing toluene). Then, the primers shown in Table 1 were applied by spraying, left at room temperature for about 10 minutes, and dried. Then, an adhesive having a ratio shown in Table 1 was applied by spraying, and a pile of nylon fibers was electrostatically planted. And it dried by heating at 80 degreeC for 60 minutes, and each electrostatic flocking body of Example 1, 2 and Comparative Examples 1-6 was created. In Example 2, after the paint and the adhesive were mixed in the adhesive, the mixture was allowed to stand for 1 hour and then applied to the substrate. Further, in Comparative Example 4, the adhesive was trade name: Fabric-two (A),
Mikasa Paint Co., Ltd. used a two-part urethane solvent-based paint, and Comparative Example 5 used an adhesive of trade name: F-445, a one-part acrylic emulsion-type adhesive and primer of Showa Kogyo Co., Ltd. Name: SP-1350, a one-pack acrylic / polyolefin modified primer manufactured by Toa Gosei Co., Ltd. In Comparative Example 6, the adhesive was trade name: FA-4
D, a one-pack type acrylic emulsion adhesive and primer manufactured by Toa Gosei Co., Ltd. were the same as the primer of Comparative Example 5. Further, in Comparative Example 7, the flocking was omitted and the polypropylene base was used. In Comparative Example 3, since the adhesive was made of only the urethane two-pack type paint manufactured by Nippon Bee Chemical Co., Ltd., the pile could not be planted, and thus could not be formed as an electrostatic flocking.

[0028]

[Table 1]

<Nail Scratch Test> Next, in each of the electrostatically implanted body of Examples 1 and 2 and Comparative Examples 1 to 6, a test finger and a human nail of a Gakushin type friction tester (JIS L 0823 II type) were used. The nail scratch test (Test 1 and Test 2) was performed according to the following test method.

[Method Using Gakushin Type Friction Tester: Test 1] The tip 32 of the test finger 31 of the Gakushin type friction tester shown in FIG. 8 was placed in a normal (dry state) or 40 ° C. water for 24 hours. After standing for a period of time, it was vertically applied to the flocking surface of the moist electrostatic flocking body and reciprocated at a load of 200 g at a speed of 12 cm / sec one way. The number of times of reciprocation is 100 times and 300 times when the electrostatic flocking body is in a normal state (dry state), and 1 when the electrostatic flocking body is in a wet state.
00 and 200 times. Note that this test 1 was performed in Example 1.
And Comparative Examples 4 to 6.

[Method Using Human Nail: Test 2] Grasp the electrostatic flocking body with one hand and place the thumb of the grasped hand on the flocking surface of the normal (dry) or wet static flocking body And scratched once parallel to the surface. In addition, the test in a wet state was performed in Example 1 and Comparative Examples 4 to 6.

After the completion of Test 1, the flocked surface of the electrostatic flocking was observed, and the evaluation of the scratching strength was performed based on the presence or absence of peeling of the pile and the scratch marks. The evaluation criteria are as follows, and the obtained results are shown in Table 1. Grade 5 (◎): Scarring scarcely was observed. Grade 4 (◎): Scratch marks are observed, but the amount is small and inconspicuous. Grade 3 (O): Scratch marks are clearly observed, but are less noticeable. Grade 2 (x): Scratch marks are clearly observed and conspicuous. Grade 1 (x): Scratch marks are noticeable. However, “◎” and “○” are levels that can be used, and “×” is a level that poses a problem in use.

In Test 2, the flocked surface of the electrostatic flocking during the test was observed, and the scratching strength was evaluated based on the presence or absence of peeling of the pile. The evaluation criteria are as follows, and the obtained results are shown in Table 1. ：: Almost no peeling. Δ: peeled off slightly. ×: easily peeled. However, "○" is a level that can be used,
“△” and “×” are levels that are problematic in use.

As apparent from Table 1, in Test 1, Comparative Examples 4 to 6 were at a level relatively usable in a dry state, but at a level that was problematic in use in a wet state. On the other hand, in Example 1 using the adhesive member composed of the adhesive and the modified acrylic resin-based primer in which the urethane paint and the urethane adhesive were mixed at almost the same ratio, either the dry state or the wet state was used. It was at a level that could be used even in cases. Thus, the first embodiment
By using the adhesive member for the flocking process, it is possible to obtain an electrostatic flocking body having good adhesion and flocking properties, and it is also excellent in water resistance, so that the electrostatic flocking body is suitable for plumbing goods I understand.

In Test 2, Comparative Examples 4 to 6 were at a level relatively usable in a dry state.
In the wet state, the level was a problem in use. Also,
Comparative Examples 1 and 2 in which the ratios of the adhesives were different were at a level where there was a problem in use even in a dry state. On the other hand, in Example 1 using the adhesive member composed of the adhesive and the modified acrylic resin-based primer in which the urethane paint and the urethane adhesive were mixed at almost the same ratio, either the dry state or the wet state was used. It was at a level that could be used even in cases.
Thus, by using the adhesive member having the adhesive in which the urethane paint and the urethane adhesive of Example 1 are mixed in the same amount in the flocking process, an electrostatic flocking body having good adhesion and flocking properties can be obtained. In addition, it is clear that this electrostatic flocking body is suitable as a water-drainable product because of its excellent water resistance. Also, in Example 2, which is different from Example 1 in the step of being left for one hour at the time of mixing the adhesive, it was at a level that could be used in a dry state. This allows
It can also be seen that the adhesive can be electrostatically planted without being cured even after mixing or after being left for one hour, and the workability is good.

<Slip Resistance Test> Next, a slip resistance test (test) was performed on each of the electrostatic flocking bodies of Example 1 and Comparative Example 7 using the slip resistance test apparatus 40 shown in FIG. 3) was performed. [Slip Resistance Test Method: Test 3] As shown in FIG. 9, the slip resistance test method is provided so as to face the normal (dry) or wet electrostatic flocking body 41 and is in contact with the flocking surface of the electrostatic flocking body 41. A weight 44 was placed on an intermediate jig 42 of a slip resistance test apparatus 40 having a rubber plate 43 adhered to the lower surface, and the intermediate jig 42 was gently pulled by a tension gauge 45 to measure the amount of force at the start of sliding. . The rubber plate 43 has a rubber hardness of 3
A hard nitrile rubber having a hardness of 0 and a soft foamed polyethylene having a rubber hardness of 10 have a load of 1 kg (intermediate jig 42 + weight 44 + weight of rubber plate 43).
The test was performed three times for each of 3 kg and 5 kg. Reference numeral 46 denotes a fixing block for fixing the electrostatic flocking body 41.

After the measurement, the average of three measurements and the formula μ = F / W
(Μ = sliding resistance value, F = average value of force at the beginning of sliding, W
= Load) to evaluate the slip resistance and evaluate the difficulty of sliding. Further, the obtained sliding resistance value of Example 1 was divided by the sliding resistance value of Comparative Example 7 to obtain an effect magnification, and the sliding resistance effect was evaluated by an average value of the respective values. The results obtained are shown in Table 2.

[0038]

[Table 2]

As is clear from Table 2, in Comparative Example 7 where the base material was as-is, the slip resistance value was low regardless of the load even when the rubber plate 43 was made of nitrile rubber or foamed polyethylene in the dry state. However, it was a slippery level which was a problem in use. Also, in the wet state, in the case of nitrile rubber, the slip resistance value is lower than that in the dry state and is a considerably slippery level which is a problem in use, and in the case of foamed polyethylene, the slip resistance value is higher than in the dry state Although it was a value, it was a slippery level that was a problem in use. Therefore, it can be seen that Comparative Example 7 as it is is not suitable as a plumbing product. On the other hand, in Example 1 in which the flocking process was performed, even when the rubber plate 43 was made of nitrile rubber or foamed polyethylene in the dry state, the slip resistance value was high irrespective of each load, and it could be used. Level. In the wet state, the slip resistance was lower than that in the dry state, but higher than that in Comparative Example 7. Accordingly, it is understood that the electrostatic flocking body of Example 1 is hard to slide in a wet state and is suitable for a plumbing product.

When the rubber plate 43 was made of harder nitrile rubber, the slip resistance effect was about 1.7 times in a dry state and about 2.0 times in a wet state. Also, the rubber plate 4
When No. 3 was soft foamed polyethylene, the ratio was about 2.3 times in the dry state and about 1.5 times in the wet state.
This shows that the electrostatic flocking body has a high slip resistance effect and is suitable for a plumbing product.

In the above-described first and second embodiments, the case where the pair of legs 3 intersect at substantially the center of the respective upper surfaces and are mounted on the lower surface of the base 2 has been described. A substantially U-shaped leg may be attached to the front and rear or left and right sides of the lower surface of the base 2, or one leg may be attached to each of the four corners of the lower surface of the base 2, as shown in the conventional example of FIG. Alternatively, a leg may be integrally formed with the base 2.

In the first and second embodiments, the case where the electrostatic flocking is used for the bath chair 1 used in the bathroom washing place has been described as an example. However, the present invention is not limited to this. Water that is desirable to prevent slippage, such as a transfer chair or bath mat, which is installed on the edge of the bath chair or bath tub used in the bath tub and sits on a turntable seat to facilitate access to the bath tub An electrostatic flocking body can also be used as a surrounding product.

[0043]

As described above, the plumbing product according to the present invention is
On the surface of the substrate composed of polypropylene resin,
Since the adhesive member made of the primer and the adhesive applied on the primer is applied, and the short fibers are electrostatically implanted through the adhesive member, the electrostatic flocking body is provided, so that even when in a wet state, slipping during use is possible. And can be handled with good stability. In addition, a soft texture can be obtained on the surface on which the electrostatic flocking is performed, the touch feeling is improved, and the appearance can be improved.

In the plumbing product according to the present invention, the adhesive is a mixture of a urethane paint and a urethane adhesive, and the ratio is almost the same. Becomes better. In this way, even when the flocked portion is scratched with a nail or the like in handling, a short-fiber does not peel off and a plumbing product with good adhesion and flocking properties is obtained. A plumbing product having excellent water resistance without peeling can be obtained.

In the plumbing product according to the present invention, since the urethane paint is a urethane two-pack type paint and the urethane adhesive is a urethane one-pack adhesive, the above-mentioned effects can be obtained.

[Brief description of the drawings]

FIG. 1 is a plan view of a first embodiment of the present invention.

FIG. 2 is a front view of FIG.

FIG. 3 is a right side view of FIG. 1;

FIG. 4 is a sectional view taken along line AA of FIG. 1;

FIG. 5 is an enlarged view of a portion B in FIG. 4;

FIG. 6 is a plan view of Embodiment 2 of the present invention.

FIG. 7 is a front view and a right side view of FIG. 6;

FIG. 8 is a plan view and a side view of a test finger of a Gakushin type friction tester used in a nail scratch test.

FIG. 9 is a schematic diagram of a slip resistance test device used in a slip resistance test and an operation explanatory diagram thereof.

FIG. 10 is a perspective view of a bath chair which is a conventional plumbing product.

[Explanation of symbols]

 DESCRIPTION OF SYMBOLS 1 Bath chair 2 Base part 3 Leg part 7 Adhesive member 7a Adhesive material 7b Primer 8 Pile 9 Foot part 12 Backrest 13 Connecting part 41 Electrostatic flocking

──────────────────────────────────────────────────の Continued on the front page (51) Int.Cl. ⁷ Identification symbol FI Theme coat ゛ (Reference) B32B 27/32 B32B 27/32 Z F term (Reference) 2D032 DA03 DA09 3B095 AC03 AC06 CA05 4D075 CA15 DA23 DB36 DC38 EA41 EB38 4F100 AK07A AK46 AK51B AK51G BA03 BA07 BA10A BA10C CB00 CB00B CC00B DG03C DG08C EH46B EH61 EJ62C EJ65B GB08 JB07 JK06 JL11

Claims (5)

[Claims] 1. An adhesive member comprising a primer and an adhesive applied on the primer is applied to the surface of a base material made of a polypropylene resin, and short fibers are electrostatically implanted through the adhesive member. A plumbing product comprising an electrostatic flocking. 2. The adhesive according to claim 1, wherein the adhesive is a mixture of a urethane paint and a urethane adhesive.
Plumbing product as described. 3. The plumbing product according to claim 1, wherein the adhesive is a mixture in which a urethane paint and a urethane adhesive are mixed at a substantially equal ratio. 4. The plumbing product according to claim 1, wherein the urethane paint is a urethane two-pack paint. 5. The plumbing product according to claim 1, wherein the urethane adhesive is a urethane one-component adhesive.