JP2001098424A - Covering yarn body - Google Patents
Covering yarn bodyInfo
- Publication number
- JP2001098424A JP2001098424A JP27614199A JP27614199A JP2001098424A JP 2001098424 A JP2001098424 A JP 2001098424A JP 27614199 A JP27614199 A JP 27614199A JP 27614199 A JP27614199 A JP 27614199A JP 2001098424 A JP2001098424 A JP 2001098424A
- Authority
- JP
- Japan
- Prior art keywords
- fiber
- covering
- yarn
- metal
- molten
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は、被検知体として利
用可能なカバリング糸条体に関し、特に、溶融繊維を溶
融して、金属繊維と合成繊維とを溶着して成るカバリン
グ糸条体に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a covering thread usable as an object to be detected, and more particularly to a covering thread formed by melting a molten fiber and welding a metal fiber and a synthetic fiber. It is.
【0002】[0002]
【従来の技術】従来から、スーパーマーケットやレンタ
ルビデオ屋、音楽CD販売店等では、万引き防止のため
に、被検知体としてアモルファス金属を用いたセキュリ
ティラベルを商品に直接貼付、あるいはセキュリティラ
ベルが貼付された透明袋に商品を挿入しておき、店の出
口付近に磁界の変化を検知する磁気システムによって商
品の盗難を監視していた。2. Description of the Related Art Conventionally, in a supermarket, a rental video store, a music CD store, etc., in order to prevent shoplifting, a security label using an amorphous metal as an object to be detected is directly attached to a product or a security label is attached. The product was inserted into a transparent bag, and the theft of the product was monitored near a store exit by a magnetic system that detects a change in the magnetic field.
【0003】しかしながら、このセキュリティラベル
は、一般に商品の外側に貼付されているため、容易にそ
の存在を知られることとなり、特に衣料品などにおいて
は、簡単に商品から剥がすことができたり、また、セキ
ュリティラベルが貼付された透明袋から衣料品などを簡
単に取り出すことができるので、実効が上がらず、あま
り利用されていないというのが実状であった。[0003] However, since this security label is generally affixed to the outside of a product, its existence can be easily known, and particularly in the case of clothing, the security label can be easily peeled off from the product. Since the clothing and the like can be easily taken out of the transparent bag to which the security label is attached, the effect has not been improved, and the fact is that it is not used much.
【0004】[0004]
【発明が解決しようとする課題】本発明は上述の実状に
鑑みてなされたもので、その目的とするところは、被検
知体として利用可能でありながら、しかもその存在を気
付かれにくくしたカバリング糸条体に関するものであ
り、特に衣料品などのタグ取付用として有効に利用でき
るものである。SUMMARY OF THE INVENTION The present invention has been made in view of the above situation, and has as its object to provide a covering yarn which can be used as an object to be detected and whose presence is hardly noticed. The present invention relates to a strip, and can be effectively used particularly for attaching a tag to clothing or the like.
【0005】[0005]
【課題を解決するための手段】即ち、本発明は、金属繊
維に溶融繊維を巻き付け、更に該溶融繊維の上から合成
繊維によってカバリングした後、加熱処理により溶融繊
維を溶融させ、金属繊維と合成繊維とを溶着して成るこ
とに特徴を有する。また、金属繊維が、鉄、コバルト、
ニッケル、モリブデン、バナジウム、クロム、銅からな
る群より選ばれた少なくとも1種を主要な組成としてい
ること、金属繊維の線径が、10〜200μmφである
ことにそれぞれ特徴を有する。That is, the present invention relates to a method for winding a molten fiber around a metal fiber, further covering the molten fiber with a synthetic fiber, and then melting the molten fiber by a heat treatment to form a composite fiber with the metal fiber. It is characterized by being fused with fibers. The metal fibers are iron, cobalt,
It is characterized in that at least one selected from the group consisting of nickel, molybdenum, vanadium, chromium, and copper has a main composition, and the wire diameter of the metal fiber is 10 to 200 μmφ.
【0006】[0006]
【発明の実施の形態】前記構成において、本発明のカバ
リング糸条体は、金属繊維と合成繊維とが、溶融繊維を
溶融することにより溶着されているので、カバリングし
ている合成繊維が移動したり剥離したりすることがな
く、また、カットした場合、カット端からの金属繊維の
飛び出しも防止することができる。DESCRIPTION OF THE PREFERRED EMBODIMENTS In the above construction, the covering thread of the present invention has the metal fiber and the synthetic fiber welded by melting the molten fiber, so that the covering synthetic fiber moves. It does not peel or peel off, and when cut, it is possible to prevent the metal fibers from jumping out of the cut end.
【0007】また、溶融繊維としては、特に制限はない
が、好ましくは低融点タイプのナイロンやポリエステル
を挙げることができ、その融点は80〜120℃が好ま
しい。溶融繊維を溶融させる際の加熱処理は特にどのよ
うな手段でもよく、また、加熱温度は、用いられる溶融
繊維の融点にもよるが、90〜140℃が好ましい。も
ちろん、用いられている溶融繊維の融点以上の加熱温度
が必要なことは言うまでもない。The molten fibers are not particularly limited, but preferably include low-melting type nylons and polyesters, and the melting point is preferably from 80 to 120 ° C. Heat treatment for melting the molten fiber may be performed by any means, and the heating temperature is preferably 90 to 140 ° C., although it depends on the melting point of the molten fiber used. Needless to say, a heating temperature higher than the melting point of the molten fiber used is required.
【0008】次に、前記構成において、金属繊維として
は、特に、鉄、コバルト、ニッケル、モリブデン、バナ
ジウム、クロム、銅からなる群より選ばれた少なくとも
1種を主要な組成としている強磁性の合金が好ましい。
なお、該組成中には、ケイ素(Si)やホウ素(B)が
含まれていてもよい。また、金属繊維の線径は、10〜
200μmφが好ましく、10μmφより小さいと、磁
性材料としての効果が希薄になり、更に切断しやすくな
る可能性がある。また、200μmφより大きいと糸条
体としての取り扱いが困難になる可能性がある。Next, in the above structure, the metal fiber is preferably a ferromagnetic alloy having at least one selected from the group consisting of iron, cobalt, nickel, molybdenum, vanadium, chromium, and copper as a main composition. Is preferred.
The composition may contain silicon (Si) or boron (B). The wire diameter of the metal fiber is 10 to
200 μmφ is preferable, and if it is smaller than 10 μmφ, the effect as a magnetic material is diminished, and there is a possibility that cutting is further facilitated. On the other hand, if it is larger than 200 μmφ, it may be difficult to handle as a filament.
【0009】金属繊維に溶融繊維を巻き付け、更に該溶
融繊維の上からカバリングする合成繊維としては、金属
繊維の磁気特性を阻害しないものが好ましく、例えば、
ポリエステル、ポリアミド、ポリウレタン等の繊維が挙
げられる。また、カバリングとしては、通常のシングル
カバリング、ダブルカバリング等が挙げられるが、ダブ
ルカバリングの場合、2本を合糸した後、同時に同方向
へカバリングしてもよい。更に、カバリングする合成繊
維は、先染めにより着色したものでもよく、本発明を取
り付ける商品の色に合わせて適宜選択することができ
る。[0009] As the synthetic fiber to be wound around the metal fiber and covered from above the molten fiber, those which do not hinder the magnetic properties of the metal fiber are preferable.
Fibers such as polyester, polyamide, and polyurethane are exemplified. Examples of the covering include ordinary single covering and double covering. In the case of double covering, two covers may be combined and then covered in the same direction at the same time. Further, the synthetic fibers to be covered may be colored by yarn dyeing, and can be appropriately selected according to the color of the product to which the present invention is attached.
【0010】[0010]
【実施例】以下、図面及び実施例を挙げて更に詳細に説
明する。なお、以下の実施例は本発明の一実施例であ
り、本発明を限定するものではない。DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, the present invention will be described in more detail with reference to the drawings and embodiments. The following embodiment is an embodiment of the present invention and does not limit the present invention.
【0011】図1は、本発明のカバリング糸条体1を示
した図であり、また、図2は、図1のX−X断面図を示
した図である。本発明のカバリング糸条体1は、金属繊
維4が溶着部5を介して合成繊維2、3でカバリングさ
れたものであり、例えば図1のように合成繊維2、3
は、2本を合糸した後、同時に同方向へカバリングした
ダブルカバリングとなっている。なお、本発明において
は、図3に示したように、あらかじめ金属繊維4に溶融
繊維6を巻き付けておき、この溶融繊維6の上から合成
繊維2、3をカバリングした後、加熱処理により溶融繊
維を溶融させ、金属繊維4と合成繊維2、3とを溶着し
ている。FIG. 1 is a view showing a covering thread 1 of the present invention, and FIG. 2 is a view showing a sectional view taken along line XX of FIG. The covering thread 1 of the present invention is obtained by covering the metal fibers 4 with the synthetic fibers 2 and 3 via the welded portions 5, and for example, as shown in FIG.
Is a double covering in which two yarns are combined and then covered in the same direction at the same time. In the present invention, as shown in FIG. 3, the molten fiber 6 is wound around the metal fiber 4 in advance, the synthetic fibers 2 and 3 are covered from above the molten fiber 6, and then the molten fiber 6 is heated. Is melted, and the metal fiber 4 and the synthetic fibers 2 and 3 are welded.
【0012】(実施例1)金属繊維として、コバルト
(Co)、鉄(Fe)、ケイ素(Si)、ホウ素(B)
を含有する金属繊維(線径100μmφ)を用い、溶融
繊維として、低融点ナイロン糸(200d、融点120
℃)を該金属繊維に撚り数450回で巻き付けた。更
に、この低融点ナイロン糸の上から合成繊維として、先
染めにより着色したナイロン66(1260d、下撚り
300T/m)を2本合糸した後、同時に同方向へダブ
ルカバリングした。得られた糸条体を130〜140℃
で加熱処理し、低融点ナイロン糸を溶融させ、金属繊維
とナイロン66とを溶着して本発明のカバリング糸条体
を得た。(Example 1) As metal fibers, cobalt (Co), iron (Fe), silicon (Si), boron (B)
And a low melting point nylon yarn (200d, melting point 120
° C) was wound around the metal fiber with 450 twists. Further, two pieces of nylon 66 (1260d, 300 T / m lower twist) colored by yarn dyeing were combined as a synthetic fiber from above the low melting point nylon yarn, and double covered simultaneously in the same direction. 130 to 140 ° C.
To melt the low-melting nylon yarn, and weld the metal fiber and nylon 66 to obtain a covering yarn of the present invention.
【0013】[0013]
【発明の効果】以上説明したように、本発明によれば、
特に衣料品などのタグ取付用として有効に利用でき、し
かもその存在を気付かれにくくした、被検知体であるカ
バリング糸条体を提供することができる。As described above, according to the present invention,
In particular, it is possible to provide a covering thread, which is a detection object, which can be effectively used for attaching a tag to clothing or the like and whose presence is hardly noticed.
【図1】本発明のカバリング糸条体を示した図である。FIG. 1 is a view showing a covering thread of the present invention.
【図2】図1のX−X断面図を示した図である。FIG. 2 is a view showing a cross-sectional view taken along line XX of FIG. 1;
【図3】金属繊維のまわりに溶融繊維を巻き付けた状態
を示す図である。FIG. 3 is a diagram showing a state in which a molten fiber is wound around a metal fiber.
1 カバリング糸条体 2 合成繊維 3 合成繊維 4 金属繊維 5 溶着部 6 溶融繊維 DESCRIPTION OF SYMBOLS 1 Covering thread 2 Synthetic fiber 3 Synthetic fiber 4 Metal fiber 5 Welding part 6 Molten fiber
フロントページの続き (51)Int.Cl.7 識別記号 FI テーマコート゛(参考) G08B 13/24 G08B 13/24 Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat II (reference) G08B 13/24 G08B 13/24
Claims (3)
溶融繊維の上から合成繊維によってカバリングした後、
加熱処理により溶融繊維を溶融させ、金属繊維と合成繊
維とを溶着して成ることを特徴とするカバリング糸条
体。After winding a molten fiber around a metal fiber and further covering the molten fiber with a synthetic fiber,
A covering thread formed by melting a molten fiber by a heat treatment and welding a metal fiber and a synthetic fiber.
ル、モリブデン、バナジウム、クロム、銅からなる群よ
り選ばれた少なくとも1種を主要な組成としていること
を特徴とする請求項1に記載のカバリング糸条体。2. The metal fiber according to claim 1, wherein the metal fiber has at least one selected from the group consisting of iron, cobalt, nickel, molybdenum, vanadium, chromium, and copper as a main composition. Covering thread.
mφであることを特徴とする請求項1又は2に記載のカ
バリング糸条体。3. The metal fiber has a wire diameter of 10 to 200 μm.
The covering thread according to claim 1, wherein the diameter is mφ.