JP2001057931A - Deodorizing antibacterial sheet - Google Patents

Deodorizing antibacterial sheet

Info

Publication number
JP2001057931A
JP2001057931A JP11234830A JP23483099A JP2001057931A JP 2001057931 A JP2001057931 A JP 2001057931A JP 11234830 A JP11234830 A JP 11234830A JP 23483099 A JP23483099 A JP 23483099A JP 2001057931 A JP2001057931 A JP 2001057931A
Authority
JP
Japan
Prior art keywords
sheet
antibacterial
nonwoven fabric
water
antifungal agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP11234830A
Other languages
Japanese (ja)
Inventor
Haruyoshi Funae
Mitsuo Yoshida
光男 吉田
晴芳 船江
Original Assignee
Mitsubishi Paper Mills Ltd
三菱製紙株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitsubishi Paper Mills Ltd, 三菱製紙株式会社 filed Critical Mitsubishi Paper Mills Ltd
Priority to JP11234830A priority Critical patent/JP2001057931A/en
Publication of JP2001057931A publication Critical patent/JP2001057931A/en
Application status is Pending legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To prepare a deodorizing antibacterial sheet that has good wetback nature and deodorant function and suppresses decomposition of excrements with antibacterial nature to prevent gas production by decomposition. SOLUTION: A sheet united by applying thermal-embossed processing to a water- absorbing polymer between nonwoven fabric sheets containing an antibacterial mildewproof agent that prevents development of odor caused by components eluting into water and an adsorbent is sealed between a liquid permeable and a liquid impermeable sheet. It is desirable in this case that the antibacterial mildewproof agent is a metallic salt of an organic compound and that it is a deodorizing antibacterial sheet of wet nonwoven fabric holding a particular nitrogen-containing heterocyclic ring or a metallic salt of an organic compound containing sulfur atom. It is also preferable to be a deodorizing antibacterial sheet made of nonwoven fabric containing an antibacterial mildewproof agent that is a metallic salt of an organic compound containing a particular nitrogen-containing heterocyclic ring or a metallic salt of an organic compound containing sulfur atom and a water-insoluble polymer compound. The metallic salt is preferably to contain at least one or more of silver salt, copper salt and zinc salt. The use of the sheet as those for human nursing and for animals is desirable.

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】本発明は、人や動物に使用されるベッド用シーツ等の日用品に関するものである。 The present invention relates to are those related to daily necessities bed sheets or the like to be used in humans and animals. さらに詳しくは、脱臭抗菌に効果が有るシートに関するものである。 More particularly, the present invention relates to effect there is a sheet on deodorant antibacterial.

【0002】 [0002]

【従来の技術】人あるいは動物が尿等を排泄した場合には、不快な臭気の発生原因となるばかりかベッド、床等を汚染し、菌類の繁殖を促す源となっている。 If the Background of the Invention person or animal is excreted urine, etc., only one bed becomes a cause of unpleasant odors, contaminate the floor or the like, it has become a source to encourage the growth of fungi. 特に犬、 In particular dog,
猫等の排泄物の臭気は大であり、床等に飛散しやすい。 Odor of excrement such as cat is a large, easy to scattered on the floor.
従来の動物用シートや介護用シートは、粉末状の吸水性ポリマー等を不織布、紙、フィルム等の支持基体上に、 Conventional animal sheets and nursing sheet, the powdery water-absorbing polymers such as nonwoven fabric, paper, on a supporting substrate such as a film,
層状に散布したもの、バインダーで支持基体に固定化したもの、支持基体間に封入したもの等が知られている。 Those sprayed in layers, those immobilized to the support substrate with a binder, such as those enclosed between the supporting substrate is known.

【0003】従来のシートの問題点としては、単に粉末状の吸水性ポリマーを基材に散布したものは運搬中や取り扱い時に吸水性ポリマーが偏在化しやすい。 [0003] The problem of the conventional sheet, the water-absorbing polymer tends to unevenly distributed at or during handling transport is merely were sprayed with powdery water absorbent polymer to the substrate. バインダーで固定したものは排泄物の吸収能が低下する場合が有る。 Those fixed with binder there may absorption capacity of excrement is reduced.

【0004】又、従来のシートは脱臭機能が不十分なものが多く、排泄物の菌類による分解で発生するガスによる臭気が経時で周囲に充満する事が多々ある。 [0004] In addition, conventional sheet many things deodorization function is insufficient, odor due to the gas generated by the decomposition by fungi of excrement is often able to fill around with the passage of time. 例えば、 For example,
特開平6−253966号公報には水分移動上部布層、 Moisture transport upper fabric layer in JP-A-6-253966,
水分分散中間部層、漏れ防止布層の下部布層を接合して一体化したものが開示されているが、脱臭性、抗菌性は考慮されていない。 Water dispersible intermediate portion layer is formed by integrating by bonding the lower fabric layer of leakproof fabric layer is disclosed, deodorization, antibacterial properties is not considered. 特開平9−187482号公報には、吸水加工された、抗菌性を有する熱可塑性繊維層と防水層が積層された複合シートが開示されている。 JP-A-9-187482, is hygroscopic treatment, composite sheet thermoplastic fiber layer and the waterproof layer is laminated with antimicrobial properties is disclosed. しかしながら、抗菌性を有する熱可塑性繊維のみで吸着剤を使用していないので初期の脱臭性に劣る。 However, poor initial deodorization does not use an adsorbent only thermoplastic fibers having antimicrobial properties.

【0005】 [0005]

【発明が解決しようとする課題】本発明は、充分な脱臭機能を有し、抗菌により排泄物の分解を抑え、分解によるガスの発生を防止する、シート全面で均一で多量の液体吸収性、脱臭抗菌特性を有する脱臭抗菌シートの提供を可能ならしめたものである。 The present invention 0005] has a sufficient deodorizing function to suppress the decomposition of excreta by antimicrobial, to prevent the generation of gas by decomposition, a large amount of the liquid absorbent in a uniform sheet over the entire surface, those which made possibly to provide the deodorant antimicrobial sheet having a deodorant antimicrobial properties.

【0006】 [0006]

【課題を解決するための手段】本発明者らは、上記の問題解決につき鋭意検討を重ねた結果、本発明に到達したものである。 Means for Solving the Problems The present inventors have found, after intensive studies on solving the above problems, it is the present invention has been completed. 即ち、本発明は、抗菌防黴剤と吸着剤を含有する少なくとも2枚の不織布の間に吸水性ポリマーを熱エンボス加工で封入したシートを液体透過性のシートと液体不透過性のシートとの間に入れ、少なくとも両端部の全面ヒートシール加工により一体化したものであり、水中へ溶出する成分により抗菌防黴性が発現する脱臭抗菌シートである。 That is, the present invention provides antibacterial antifungal agent and at least two non-woven fabrics sheets water-absorbing polymeric sheets sealed by heat embossing the liquid-permeable sheet and a liquid impermeable between containing adsorbent inserted between, it is obtained by integrating the entire surface by heat sealing process at least two ends, a deodorizing antibacterial sheet antibacterial antifungal properties are expressed by components eluted into water.

【0007】本発明は、抗菌防黴剤が有機化合物の金属塩である脱臭抗菌シートである。 [0007] The present invention, the antibacterial antifungal agent is deodorizing antibacterial sheet is a metal salt of an organic compound.

【0008】本発明は、有機化合物が、ベンズイミダゾール化合物、メルカプトピリジン−N−オキシド化合物、イソチアゾリン化合物、ベンゾチアゾール化合物もしくはベンゾチアゾリン化合物から選ばれる少なくとも1種の化合物である脱臭抗菌シートである。 [0008] The present invention relates to organic compounds, benzimidazole compounds, mercaptopyridine--N- oxide compounds, isothiazoline compounds, deodorizing antibacterial sheet is at least one compound selected from benzothiazole compounds or benzothiazoline compounds.

【0009】本発明は、金属塩が銀塩、銅塩、亜鉛塩の少なくとも1種を含有する脱臭抗菌シートである。 [0009] The present invention is a deodorant antimicrobial sheet metal salt containing silver salts, copper, at least one zinc salt.

【0010】本発明は、吸着剤がゼオライト系化合物である脱臭抗菌シートである。 [0010] The present invention is a deodorant antimicrobial sheet adsorbing agent is a zeolite-based compound.

【0011】本発明は、不織布が、有機化合物の金属塩よりなる抗菌防黴剤を含有する繊維状物質を含む脱臭抗菌シートである。 [0011] The present invention, nonwoven fabric, a deodorizing antibacterial sheet comprising a fibrous material containing an antibacterial antifungal agent of a metal salt of an organic compound.

【0012】本発明は、不織布が湿式不織布である脱臭抗菌シートである。 [0012] The present invention is a deodorant antibacterial sheet non-woven fabric is a wet-laid nonwoven fabric.

【0013】本発明は、人の介護用シートとして使用される脱臭抗菌シートである。 [0013] The present invention is a deodorant antibacterial sheet to be used as a long-term care for the seat of the people.

【0014】本発明は、動物用シートとして使用される脱臭抗菌シートである。 [0014] The present invention is a deodorant antimicrobial sheet used as an animal sheet.

【0015】 [0015]

【発明の実施の形態】本発明における脱臭抗菌シートは、抗菌防黴剤と吸着剤を含有する不織布の間に吸水性ポリマーを熱エンボス加工で封入したシートと抗菌防黴剤と吸着剤を含有する不織布が、液体透過性のシートと液体不透過性のシートの間に入っており、少なくとも両端部が全面にヒートシール加工で一体化されており、特に抗菌防黴剤が有機化合物の金属塩よりなり、ペット用トイレに敷いたり、ペット用の寝床に敷いたり、人の介護用シートとして寝具上に敷いて使用する。 Deodorizing antibacterial sheet according DETAILED DESCRIPTION OF THE INVENTION The present invention contains an antibacterial antifungal agent and the sheet and the antibacterial antifungal agent of the water-absorbing polymer between the nonwoven containing sealed by heat embossing the adsorbent adsorbent to nonwoven, has entered between the sheet of the sheet and a liquid impermeable liquid permeable, at least both end portions are integrated by heat-sealing process on the entire surface, in particular a metal salt of an antibacterial antifungal agent is an organic compound more now, or laid pet toilet, or laid in bed for pets, use laid on the bedding as long-term care for the seat of the people.

【0016】液体透過性のシートの役割は、液体をその表面から吸収し、内部の不織布に渡す役割と、流動性の排泄物を保持する役割を持っており、織物、編物、不織布等が使用される。 The role of the sheet of liquid permeable absorbs liquid from the surface, and roles to pass to the inside of the nonwoven fabric, has a role to hold a flow of excretion, use woven, knitted, non-woven fabric or the like It is. 価格、液体透過性等で選択されるが、スパンボンド法、サーマルボンド法、カード法、エアーレイ法、湿式法等の不織布が挙げられる。 Price, is selected by a liquid permeable like, spunbonding, thermal bonding, carding method, airlaid method, and non-woven fabric of wet process. 液体透過性の改良のためにシート表面に界面活性剤等で親水化処理を行ったり、使用時の肌触りや柔らかさを出すために高圧水流で処理したスパンレース加工不織布が好ましく用いられる。 And go to a hydrophilic treatment with a surfactant or the like on the sheet surface for liquid permeability improvement, spunlace process nonwoven fabric treated with high-pressure water in order to give texture and softness during use is preferably used. シートを構成する繊維径はあまり小さいのは液体透過性に劣るので、1〜8デニール程度が好ましい。 Since it is fiber diameter constituting the sheet too small is inferior in liquid permeability, approximately 1-8 denier being preferred. 厚さは、液体透過性から薄いものがよいが、強度と復元力等の使用感により選択される。 Thickness is good as thin a liquid permeable, is selected by a sense of the strength and resiliency, and the like. 通常は、目付は1 Usually, the basis weight 1
0〜50g/m 2 、厚さは10〜100μm程度のものが使用される。 0~50g / m 2, thickness is used of about 10 to 100 [mu] m. 好ましくはヒートシール性が良好なものが加工性が簡便であるので好ましく選択される。 Preferably those heat sealable is good is preferably selected so workability is simple.

【0017】特に人の介護用として使用する場合には、 [0017] In the case of particular use for the care of people,
液体透過性のシートの表面を疎水性の繊維等とするほうが患者との接触面の水分を出来るだけ少なくして不快感を防止するのに効果的である。 The liquid permeable surface sheet is better to hydrophobic fibers such as is effective to prevent discomfort to minimize moisture contact surface with the patient. 動物の場合でも同様に疎水性にすることで足や体の表面に尿等が付着して周囲を汚染するのを防止する効果が有る。 There is an effect to prevent the contamination of the surroundings to adhere urine or the like on the surface of the foot and body by the similarly hydrophobic even if the animal.

【0018】疎水性の繊維としてはポリエステルやポリプロピレン等が挙げられる。 Examples of the hydrophobic fibers include polyester, polypropylene, or the like. 親水性の繊維としては、パルプ、レーヨン、綿、親水性ナイロン等が挙げられる。 As hydrophilic fibers, pulp, rayon, cotton, hydrophilic nylon and the like.
好ましくは疎水性不織布と親水性不織布をスパンレース等で積層したシートが使用出来る。 Preferably the sheet can be used by laminating a hydrophobic non-woven fabric and a hydrophilic nonwoven spunlace like.

【0019】液体不透過性のシートとしては、液体を遮断する効果の有るものであれば何でもよいが、例えばポリエチレン、ポリプロピレン、ポリ塩化ビニル、ポリエステル等のフィルム、織布、不織布、紙等にラミネートしたラミネートシートが挙げられる。 [0019] Liquid impermeable sheet is be anything having the effect of blocking the liquid, for example a laminate of polyethylene, polypropylene, polyvinyl chloride, films such as polyester, woven fabric, nonwoven fabric, a paper or the like like laminate sheet that is. 通常は、目付は1 Usually, the basis weight 1
0〜50g/m 2 、厚さは10〜100μm程度のものが使用される。 0~50g / m 2, thickness is used of about 10 to 100 [mu] m. 好ましくはヒートシール性の良好なものが加工性が簡便であるので好ましく選択される。 Preferably it is preferably selected so having good heat sealability is simple processability.

【0020】本発明で使用する吸着剤は、粘土系、ゼオライト系、酸性白土系、活性白土系、ベントナイト系、 The adsorbent used in the present invention, clay, zeolite, acid clay type, activated clay based, bentonite,
活性炭系等の無機化合物系や酸性基や塩基性基を有する高分子化合物等が利用出来る。 Polymer compounds having a inorganic compound or an acidic group or a basic group activated carbon or the like is available. 好ましいのは、アンモニア、トリメチルアミン、硫化水素、エチルメルカプタン等の吸着に有効である粘土系のアルミノケイ酸亜鉛系である。 Preferred are ammonia, trimethylamine, a clay-based aluminosilicate zinc in is effective for adsorption such as hydrogen sulfide, ethyl mercaptan. 具体的には水沢化学工業社製のミズカナイトA More specifically, Mizusawa Chemical Industry Co., Ltd. of Mizukanaito A
P、ミズカナイトAG、ミズカナイトHP、ミズカナイトHG、ミズカナイトMPが挙げられる。 P, Mizukanaito AG, Mizukanaito HP, Mizukanaito HG, include Mizukanaito MP.

【0021】本発明で使用する吸水性ポリマーには、架橋ポリアクリル酸ソーダ、酢酸ビニル−アクリル酸エステル共重合体、酢酸ビニル−マレイン酸メチル共重合体、イソブチレン−無水マレイン酸共重合体、デンプン−アクリルニトリルグラフト共重合体、ポリエチレンオキサイド架橋物等が有る。 [0021] water-absorbing polymer used in the present invention, crosslinked sodium polyacrylate, vinyl acetate - acrylic acid ester copolymer, vinyl acetate - methyl maleate copolymer, isobutylene - maleic anhydride copolymer, starch - acrylonitrile graft copolymer, polyethylene oxide crosslinked product, etc. there.

【0022】吸水性ポリマーの使用量は、特に限定されないが、一般的には脱臭抗菌シートに対して3〜100 [0022] The amount of the water-absorbing polymer is not particularly limited, in general, with respect deodorant antimicrobial sheet 3-100
g/m 2 、好ましくは5〜50g/m 2になるような高吸水性のポリマーが選択される。 g / m 2, and preferably is superabsorbent polymers such that 5 to 50 g / m 2 selection. 吸水性ポリマーの使用により尿の戻りを防止する機能、ウエットバック性が向上するほか、吸収量が増えるので臭いの発生する菌類の増殖防止に効果が大きい。 Function to prevent urine back by the use of the water-absorbing polymer, in addition to improved wetback properties, the effect is large growth prevention of fungal generated by the odor because absorption increases.

【0023】抗菌防黴剤と吸着剤を含有する不織布は、 The nonwoven fabric containing an adsorbent and antibacterial antifungal agent,
不織布同士の貼り合わせで不織布の間に抗菌防黴剤と吸着剤をポリエチレンやポリ酢酸ビニル等のバインダー粒子と併用して熱圧処理で封入したり、抗菌防黴剤と高分子化合物を含有するする抗菌防黴剤の組成物を塗布、含浸等で含有させた不織布と他の不織布の間に吸着剤とバインダー粒子を封入したものが使用出来る。 Or encapsulated by the heat pressure treatment of the adsorbent with an antibacterial antifungal agent between at bonding nonwoven nonwoven together in combination with binder particles, such as polyethylene or polyvinyl acetate, containing an antimicrobial antifungal agent and the polymer compound the composition of the antimicrobial antifungal agent applied, those filled with adsorbent and binder particles between the nonwoven fabric and another nonwoven fabric which contains impregnation or the like can be used. 吸着剤の量は、その種類により異なるが、臭気物質の吸着効果からは不織布の重量比で5%以上の使用が好ましく、より好ましくは10%以上である。 The amount of the adsorbent varies depending on its type, from the adsorption effect of odorants preferred use of more than 5% by weight of the nonwoven fabric, more preferably 10% or more. 不織布の使用方法は、封入シート単独か、好ましくは重ねて使用される。 Using the nonwoven fabric, or encapsulating sheet alone, is preferably superimposed used.

【0024】不織布が湿式不織布の場合は、抗菌防黴剤を含有する繊維状物質を抄造時に他の繊維と一緒に使用し、吸着剤は内填することで不織布に含有させる事が出来るので簡単であり好ましい。 [0024] When the nonwoven fabric is wet-laid nonwoven fabric, easy since the fibrous material containing an antibacterial antifungal agent used in conjunction with other fibers during papermaking, the adsorbent can be contained in the nonwoven fabric by inner Hama in is preferable. また、内填することで吸着剤の有効面積の減少が少ないので脱臭効果の点でも好ましい。 Also, it preferred in terms of the deodorizing effect since reduction is less effective area of ​​the adsorbent by inner Hama. 吸着剤の量はその種類により異なるが、臭気物質の吸着効果からは不織布の重量比で3%以上の含有量が好ましく、より好ましくは10%以上である。 The amount of the adsorbent may vary depending on the type, from the adsorption effect of the odorant preferably a content of 3% or more by weight of the nonwoven fabric, more preferably 10% or more. 不織布の使用方法は、重ねて複数枚で使用したり、クレープ加工で不織布にしわを付けた方が表面積が増え、吸水量が増える他にウエットバック性も向上するので好ましい。 Using the nonwoven fabric, or used in plural overlapping, nonwoven who gave a wrinkled surface area increased to at creping, wet back property in addition to water absorption is also increased preferably improved.

【0025】吸水性ポリマーを封入する時の熱エンボス加工は、例えば表面に凹凸を設けた金属ロールとエンボスロールや鏡面ロール、樹脂ロール間に不織布を通す事で不織布表面に凹凸を付けたり不織布同士を一体化する加工法である。 The hot embossing when encapsulating the water-absorbing polymer, for example, a metal roll and an embossing roll and mirror roll having irregularities on the surface, with an uneven surface of the nonwoven fabric by passing the nonwoven fabric between the resin roll or nonwoven together it is a processing method to integrate. エンボスロール表面の温度は、不織布やシートに使用する繊維や樹脂で異なるが、70〜200 Temperature of the embossing roll surface will vary with fibers and resin used to nonwoven fabric or sheet, 70 and 200
℃程度が一般的である。 About ℃ is common.

【0026】抗菌防黴剤と吸着剤を含有する不織布の間に吸水性ポリマーを熱エンボス加工により封入し、一体化することで吸水性ポリマーの極近隣に抗菌防黴剤が存在しやすくなり、尿等を介して両者が接触することで抗菌剤が溶出して吸水性ポリマーが吸収している尿等の中での菌類の繁殖が抑えられることになる。 [0026] Antibacterial antifungal agent and a water-absorbing polymer between the nonwoven fabric containing an adsorbent enclosed by heat embossing, tends to exist antibacterial antifungal agent to the poles close to the water-absorbing polymer by integrating, both so that breeding of fungi in such urine absorbent polymeric antimicrobial agent is eluted is absorbed is suppressed by contacting through the urine and the like. 加えてエンボス加工の方が全面熱加工よりも不織布表面の液体吸収速度の低下が少ないという効果も有る。 Additionally towards the embossing even there the effect of reduced fluid absorption rate of the nonwoven fabric surface than entire thermal processing is smaller.

【0027】抗菌防黴剤と吸着剤を含有する不織布の間に吸水性ポリマーを熱エンボス加工により封入して一体化したシートを液体透過性のシートと液体不透過性のシートの間に入れて一体化する時のヒートシール加工は、 [0027] The antibacterial antifungal agent and a sheet of water-absorbing polymer and integrated sealed by heat embossing between the nonwoven fabric containing an adsorbent placed between sheets of the sheet and a liquid impermeable liquid permeable heat seal processing at the time of integration is,
鏡面金属ロール同士や鏡面金属ロールとエンボスロールとの間を通す事で複数のシートや不織布を一体化する加工法である。 It is a processing method for integrating a plurality of sheets or non-woven fabric by passing between a mirror surface metallic rolls or between the specular metal roll and the embossing roll. ロール表面の温度は、不織布やシートに使用する繊維や樹脂で異なるが、一般的には80〜200 Temperature of the roll surface varies with fibers and resin used in the nonwoven fabric or sheet, generally from 80 to 200
℃程度である。 It is about ℃.

【0028】本発明の抗菌防黴剤として金属塩で用いられる有機化合物は、好ましくは基本的に防黴性を有し、 The organic compound used in the metal salt as the antibacterial antifungal agent of the present invention preferably has an essentially antifungal,
特に以下の含窒素複素環、硫黄原子の少なくともいずれかを含む化合物から選択される。 In particular the following nitrogen-containing heterocyclic ring, selected from the compounds containing at least one sulfur atom.

【0029】本発明で使用する抗菌防黴剤としては、現在市販されているビグアナイド系、アルコール系、フェノール系、アニリド系、ヨウ素系、イミダゾール系、チアゾール系、イソチアゾロン系、トリアジン系、ニトリル系、フッ素系、トロポリン系、有機金属系、無機金属系のものはいずれも使用可能である。 [0029] as an antibacterial antifungal agent used in the present invention, biguanide on the market today, alcohol, phenol, anilide, iodine, imidazole, thiazole, isothiazolone, triazine, nitrile, fluorine-based, tropolin based, organometallic, any one of inorganic metallic usable.

【0030】例えば、ピロール系、ピリジン系、ピリミジン系、ピラゾール系、イミダゾール系、ベンズイミダゾール系、1,3,5−トリアジン系、ヘキサヒドロ− [0030] For example, pyrrole, pyridine, pyrimidine, pyrazole, imidazole, benzimidazole, 1,3,5-triazine, hexahydro -
1,3,5−トリアジン系、トリアゾール系、イソオキサゾール系、チアゾール系、ベンゾチアゾール系、チアゾロン系、ベンゾチアゾロン系、イソチアゾロン系、ベンゾイソチアゾロン系、テトラヒドロチアジアジンチオン系などを基本骨格とするものが挙げられ、さらに、それらのアルキルアリル誘導体、メルカプト誘導体などが挙げられるが、なかでも、ベンズイミダゾール化合物、 1,3,5 triazine, triazole, isoxazole, thiazole, benzothiazole, thiazolone system, benzothiazolone type, an isothiazolone, benzisothiazolone system, tetrahydrothienyl Asian renal blood on system and those having a basic skeleton the recited further their alkyl allyl derivatives, and mercapto derivatives, inter alia, benzimidazole compounds,
メルカプトピリジン−N−オキシド化合物、イソチアゾロン化合物、ベンゾチアゾール化合物、ベンゾチアゾロン化合物から選ばれる少なくとも一種の化合物が特に好ましい。 Mercaptopyridine--N- oxide compounds, isothiazolone compounds, benzothiazole compounds, at least one compound selected from benzothiazolone compounds are particularly preferred. これらの具体例としては、例えば、2−(4− Specific examples thereof include 2- (4-
チアゾリル)−ベンズイミダゾール、2−(カルボメトキシアミノ)−ベンズイミダゾール、2−メルカルトピリジン−N−オキシド、1,2−ベンゾイソチアゾリン−3−オン、5−クロロ−2−メチル−4−イソチアゾリン−3−オン、2−メチル−4−イソチアゾリン−3 Thiazolyl) - benzimidazole, 2- (carbomethoxy amino) - benzimidazole, 2- Mel cult pyridine -N- oxide, 1,2-benzisothiazolin-3-one, 5-chloro-2-methyl-4-isothiazolin -3 - one, 2-methyl-4-isothiazolin -3
−オン、2−n−オクチル−4−イソチアゾリン−3− - one, 2-n-octyl-4-isothiazolin-3
オン、1,2−ベンゾチアゾロン、2−(4−チオシアノメチルチオ)ベンゾチアゾールなどを挙げることができる。 One, 1,2-benzothiazolone, such as 2- (4-thiocyanomethylthio) benzothiazole and the like.

【0031】特に、ベンズイミダゾール化合物、メルカプトピリジン−N−オキシド化合物、イソチアゾロン化合物、ベンゾチアゾール化合物もしくはベンゾチアゾロン化合物のうちの少なくとも1種類が効果の点で好ましい。 [0031] In particular, benzimidazole compounds, mercaptopyridine--N- oxide compounds, isothiazolone compounds, at least one of the benzothiazole compound or benzothiazolone compounds are preferable in terms of effects.

【0032】また、本発明の脱臭抗菌シートで使用される抗菌防黴剤の金属塩の例としては銀、銅、亜鉛、錫、 Further, silver as an example of a metal salt of an antibacterial antifungal agent used in the deodorant antimicrobial sheet of the present invention, copper, zinc, tin,
マンガン、コバルト、鉄塩等が挙げられる。 Manganese, cobalt, iron salts, and the like. 効果の点で好ましくは銀、銅、亜鉛塩から選択され、特に銀、銅、 In view of the effects, preferably selected silver, copper, zinc salt, in particular silver, copper,
亜鉛塩の3種が複合されたものがより好ましい。 That three zinc salts are combined are more preferred.

【0033】本発明では、含窒素複素環、硫黄原子の少なくともいずれかを含む有機化合物の金属塩である抗菌防黴剤を繊維構造内もしくは表面に強固かつ密に形成させ、有効に機能させる為には、繊維が適度な膨潤性、イオン浸透性、イオン捕獲性を有することが必要である。 [0033] In the present invention, nitrogen-containing heterocyclic ring, an antibacterial antifungal agent is a metal salt of an organic compound containing at least one sulfur atom is firmly and tightly formed in the fiber structure or within the surface, in order to function effectively the fiber moderate swelling, ion permeability, it is necessary to have an ionic captive.

【0034】このような繊維として、いわゆるイオン交換繊維が用いられ、例えばポリスチレン、ポリアクリル、ポリアミド、ポリエチレン、セルロース等のベースポリマーにスルホン酸基、ホスホン酸基、カルボン酸基等を適度に導入する事によって得られる。 [0034] As such a fiber, so-called ion-exchange fibers are used, such as polystyrene, polyacrylic, polyamide, polyethylene, sulfonic acid groups in the base polymer such as cellulose, a phosphonic acid group, appropriately introducing carboxylic acid groups, etc. obtained by things.

【0035】また通常パルプと称せられる天然のセルロース系繊維を部分的に化学変性することにより好ましく利用出来る。 Further cellulosic fibers of natural is called a normal pulp partially preferably available by chemical modification. 化学変性処理としては、硫酸化、リン酸化、硝酸化、カルボキシメチル化、カルボキシエチル化、カルボキシプロピル化処理が挙げられる。 The chemical modification treatment, sulfation, phosphorylation, nitration, carboxymethylated, carboxyethyl reduction include carboxypropyl process. 中でも、 Among them,
カルボキシメチル化処理はプロセスが容易で、経済性、 Carboxymethylation process process is easy, economical,
安全性も良く、かつ膨潤性、イオン浸透性等に優れており本発明の実施に極めて好適であり、特に該セルロース系繊維の部変性物の置換度が0.5以下のものが好ましい。 Safety is also good, and swelling, are very suitable for the practice of the present invention has excellent ion permeability, etc., in particular the degree of substitution of parts modified product of the cellulosic fibers is preferably from 0.5 or less.

【0036】本発明で好ましく使用されるカルボキシメチル変性繊維状物質の素材となるパルプとしては、適度にカルボキシメチル化された木材パルプ(針葉樹パルプ、広葉樹パルプなど)は、本発明の実施に好適であるが、この他、レーヨンなどの再生セルロースも同様に使用可能である。 [0036] As the material to become pulp carboxymethyl-modified fibrous material preferably used in the present invention, moderately carboxymethylated wood pulp (softwood pulp, hardwood pulp, etc.), suitable for the practice of the present invention there, this addition can be used as well regenerated cellulose such as rayon. さらには、前記主旨に沿って適度に変性されたイオン交換能を有する合成繊維、アルギン酸繊維や可溶性ポリマーの湿式紡糸繊維であっても良い。 Furthermore, the synthetic fibers having ion exchange capacity which is suitably modified along the gist may be wet spun fibers of alginate fibers and soluble polymers. また、本発明における抗菌・防黴能を有する有機金属複合塩を含有するポリマー液から製造された湿式紡糸繊維であっても良い。 Further, it may be a wet spinning fibers produced from the polymer solution containing an organic metal complex salt having an antibacterial Bokabino in the present invention.

【0037】本発明における繊維状物質の好ましい一具体例としては、天然セルロース系繊維のカルボキシメチル化加工によって達成される。 [0037] As one preferred embodiment of the fibrous material in the present invention is achieved by carboxymethylation processing of natural cellulosic fibers.

【0038】本発明で用いられる各種のカルボキシメチル基置換度を持つ繊維状物質は、置換度が大きくなるにつれて、金属イオン捕獲能は高まり、したがって、本発明における抗菌・防黴能を有する有機金属複合塩の充填密度は高くなるが、高置換度では膨潤が過度に進み、繊維強度の低下および、ひいては可溶化に至る。 The present invention fibrous material with a variety of carboxymethyl substitution degree to be used in, as the degree of substitution increases, the increased metal ion capturing ability, therefore, an organic metal having antibacterial Bokabino in the present invention While packing density of the composite salt is increased, the high degree of substitution swelling proceeds excessively, lowering of fiber strength and leads to thus solubilize. 一般的に、置換度はおよそ0.6で可溶性となる。 Generally, the degree of substitution is soluble at about 0.6. 強度低下はあるが置換度はおよそ0.5が繊維形状が維持できる上限レベルである。 Some reduction in strength although the degree of substitution is the upper limit level of approximately 0.5 can be sustained fibrous form.

【0039】このようにして作られた極度に高濃度化された抗菌防黴剤を含有する繊維状物質と吸着剤を用いた本発明における不織布を封入した袋を適用した場合は、 In the case of applying the bag encapsulating a nonwoven in this way with extremely fibrous materials containing high concentrations of antimicrobial antifungal agent, produced by the present invention using the adsorbent,
抗菌防黴剤が適度に水溶解性が有り、優れた抗菌防黴機能による腐敗防止効果や吸着剤の脱臭効果により悪臭が軽減される。 Antibacterial antifungal agent moderately water solubility there, malodor is reduced by deodorizing effect of excellent anti-corruption effect and adsorbent by antibacterial antifungal functions. 特に吸水性ポリマー近隣に存在する抗菌防黴剤が効果的に尿中に溶解して菌類の繁殖を抑える。 In particular the antibacterial antifungal agent present in the water-absorbing polymer close effectively suppress the growth of fungi was dissolved in the urine.

【0040】本発明において、最も効果的に抗菌防黴機能を発揮する有機化合物の複合塩の作製方法について述べる。 [0040] In the present invention, it describes a method for manufacturing the most effective composite salt of an organic compound which exhibits an antibacterial antifungal functions.

【0041】基本的には、カルボキシメチルセルロースに対して添加する金属塩組成を、計算量配合することによって達成できるし、また、銀電極もしくは白金電極を用いた電位計測により、各イオンとの反応をモニターできる。 [0041] Basically, the metal salt composition to be added relative to the carboxymethyl cellulose, to be achieved by calculating the amount, also by the potential measurement using a silver electrode or a platinum electrode, the reaction between the ions It can be monitored.

【0042】一例として、2−メルカプトピリジン−N [0042] As an example, 2-mercaptopyridine -N
−オキシドの複合塩の作製方法を例示すれば、銀、銅、 - To exemplify a method for manufacturing a composite salt of oxide, silver, copper,
亜鉛の複合系に2−メルカプトピリジン−N−オキシドを添加することにより得られる。 The composite system of the zinc obtained by adding 2-mercaptopyridine -N- oxide. 銀25モル%、銅25 Silver 25 mol%, copper 25
モル%、亜鉛50モル%と2−メルカプトピリジン−N Mol%, zinc 50 mol% with 2-mercaptopyridine -N
−オキシドの複合塩を形成させるための具体例を挙げれば、 Na型カルボキシメチルセルロース(DS=0.4)固形分 100g 水 5000g 硝酸銀 10mmol 硫酸銅 15mmo l 硝酸亜鉛 30mm ol 水 1000g 2−メルカプトピリジン−N−オキシドナトリウム0.1m/l溶液1000g となる。 - As a specific example for forming a composite salt of oxide, Na-type carboxymethyl cellulose (DS = 0.4) solid 100g water 5000g silver nitrate 10mmol copper sulfate 15Mmo l zinc nitrate 30 mm ol water 1000 g 2-mercaptopyridine -N - the oxide sodium 0.1 m / l solution 1000 g. また、本発明の好ましい1実施態様として、硝酸銀添加後、以下、2−メルカプトピリジン−N−オキシド化合物添加→硫酸銅添加→2−メルカプトピリジン−N−オキシド化合物添加→硝酸亜鉛添加→2−メルカプトピリジン−N−オキシド化合物添加など、各種の添加方法により行うことができる。 Furthermore, as one preferred embodiment of the present invention, after the silver nitrate addition, hereinafter, 2-mercaptopyridine--N- oxide compound added → copper sulfate added → 2-mercaptopyridine--N- oxide compound added → zinc nitrate added → 2-mercapto pyridine -N- oxide compound added can be carried out by various additives methods.

【0043】含窒素有機複素環化合物およびチオール化合物、チオン化合物などの含硫黄化合物の多くは、同様の思想で形成できる。 The nitrogen-containing organic heterocyclic compounds and thiol compounds, many sulfur-containing compounds such as thione compounds can be formed by the same idea.

【0044】イソチアゾリン−3−オン系化合物も同様に可能であり、また、イミダゾール誘導体にも、それ自身(抗菌)防黴作用があるものが多い。 The isothiazolin-3-a-one system likewise possible compounds, also imidazole derivative itself (antibacterial) Some are often antifungal action. この場合、水への溶解度は低く、水溶液の形で添加することはできないが、水混和性の有機溶剤、例えば、アルコール類、グリコール類などの溶剤には可溶であり、それらの溶液として添加することにより、金属塩を繊維状物質内に形成できる。 In this case, the solubility in water is low, can not be added in the form of an aqueous solution, a water-miscible organic solvent, for example, in solvents such as alcohols, glycols are soluble, added as a solution thereof by the metal salt can be formed in the fibrous material.

【0045】本発明における抗菌防黴剤を含有する繊維状物質は、そのもの自体や他の有機繊維や無機繊維と混合して粒状物として適用することもできるが、繊維状物質単独や、他の各種繊維と混抄して不織布にして使用することが、より実用的である。 The fibrous material containing an antibacterial antifungal agent according to the present invention can also be mixed with itself itself or other organic fibers and inorganic fibers is applied as granules, fibrous material alone or, in other it is more practical to use in the various fibers and 混抄 to nonwoven. さらに、前述したとおり、本発明における繊維状物質中に、抗菌防黴剤を高濃度に吸着させて、いわゆるマスターバッチ的に本発明における繊維状物質を適用することは、より効果的であり、且つ、操業上でも大きな利点がある。 Further, as described above, the fibrous material of the present invention, an antibacterial antifungal agent is adsorbed at a high concentration, applying the fibrous material in the present invention is a so-called master batch to be more effective, and, there is a great advantage even on operations.

【0046】本発明における抗菌防黴剤を含有する繊維状物質と併用される有機繊維や無機繊維は、有機繊維としては、植物繊維、動物繊維、再生繊維、半合成繊維および合成繊維から選ばれる繊維を単独あるいは混合したものが使用され、無機繊維としては、ガラス繊維、炭素繊維、セラミック繊維およびウイスカーから選ばれる繊維を単独あるいは混合したものが使用される。 The organic fibers and inorganic fibers used in combination with fibrous material containing an antibacterial antifungal agent according to the present invention, the organic fibers are selected from vegetable fibers, animal fibers, regenerated fibers, semisynthetic fibers and synthetic fibers those fibers alone or mixed is used as the inorganic fibers, glass fibers, carbon fibers, those alone or mixed fibers selected from ceramic fibers and whiskers are used.

【0047】植物繊維としては、針葉樹パルプ、広葉樹パルプなどの木材パルプや藁パルプ、竹パルプ、ケナフパルプなどの木本類、草本類、綿、麻(亜麻、ラミー) [0047] Examples of the plant fibers, softwood pulp, wood pulp and straw pulp, such as hardwood pulp, bamboo pulp, woody plants, such as kenaf, grasses, cotton, hemp (flax, ramie)
等を含み、吸水性からは好ましい。 It comprises like, preferable in water absorption. さらに、古紙、損紙などから得られるパルプ繊維も含まれる。 Also included paper, also pulp fibers obtained from such spoilage. 動物繊維としては、絹、羊毛などの繊維が挙げられる。 As the animal fibers, silk, include fibers such as wool.

【0048】再生繊維としては、レーヨン、キュプラが、半合成繊維としては、アセテート、トリアセテート、プロミックスが、合成繊維としては、ナイロン、アクリル、ビニロン、ビニリデン、ポリ塩化ビニル、ポリエステル、ポリエチレン、ポリプロピレン、ベンゾエート、ポリクラール、フェノール系などの繊維が挙げられる。 [0048] As playback fibers, rayon, cuprammonium is, as a semi-synthetic fibers include acetates, triacetates, promix is, as the synthetic fibers, nylon, acrylic, vinylon, vinylidene, polyvinyl chloride, polyester, polyethylene, polypropylene, benzoate, polychlal, include fibers such as phenolic.

【0049】本発明における抗菌防黴剤を含有する繊維状物質の比率は、含有する抗菌防黴剤の種類や比率によるが、粒状物や不織布を構成する全繊維状物質中で、 The proportion of fibrous material containing an antibacterial antifungal agent according to the present invention, depending on the type and proportion of the antibacterial antifungal agent containing a total fibrous material that constitutes the particulate material or nonwoven fabric,
0.1〜100重量部、好ましくは0.5〜70重量部である。 0.1 parts by weight, preferably 0.5 to 70 parts by weight. 0.1重量部未満であると、十分な抗菌防黴機能が発揮されず、長期にわたる効果が得にくい。 If it is less than 0.1 part by weight, not exhibited sufficient antibacterial antifungal function, prolonged effect may not obtained. また、 Also,
70重量部を超えるとコスト面から望ましくない。 More than 70 parts by weight, the undesirable cost.

【0050】本発明における抗菌防黴剤を含有する繊維状物質と併用される繊維の少なくとも30%は針葉樹パルプや広葉樹パルプ、レーヨン等の吸水性繊維が好ましい。 [0050] At least 30% of the fibers used in combination with fibrous material containing an antibacterial antifungal agent according to the present invention is softwood pulp and hardwood pulp, is absorbent fibers such as rayon preferred.

【0051】本発明における抗菌防黴剤を含有する繊維状物質を他の併用される各種繊維と混抄して使用する場合、必要に応じて、各種の繊維状バインダーを用いることができる。 [0051] When the fibrous material containing an antibacterial antifungal agent of the present invention used with various fibers and 混抄 is another combination, it is possible to optionally use various fibrous binder.

【0052】本発明に用いられる繊維状バインダーは、 [0052] Fibrous binder for use in the present invention,
芯鞘タイプ(コアシェルタイプ)、並列タイプ(サイドバイサイドタイプ)などの複合繊維が挙げられる。 Core-sheath type (core-shell type), and a composite fiber, such as a parallel type (side-by-side type). 例えば、ポリプロピレン(芯)とポリエチレン(鞘)の組み合わせ(商品名:ダイワボウNBF−H:大和紡績社製)、ポリプロピレン(芯)とエチレンビニルアルコール(鞘)の組み合わせ(商品名:ダイワボウNBF− For example, a combination of polypropylene (core) and polyethylene (sheath) (trade name: Daiwabo NBF-H: manufactured by Daiwa Spinning Co., Ltd.), a combination of polypropylene (core) and ethylene vinyl alcohol (sheath) (trade name: Daiwabo NBF-
E:大和紡績社製)、ポリプロピレン(芯)とポリエチレン(鞘)の組み合わせ(商品名:チッソESC:チッソ社製)、高融点ポリエステル(芯)と低融点ポリエステル(鞘)の組み合わせ(商品名:メルテイ4080: E: manufactured by Daiwa Spinning Co., Ltd.), combined (trade name of polypropylene (core) and polyethylene (sheath): Chisso ESC: Chisso Corporation), the combination of high melting point polyester (core) and low melting point polyester (sheath) (trade name: Merutei 4080:
ユニチカ社製)などが挙げられる。 Unitika Co., Ltd.) and the like. また、ビニロンバインダー繊維(VPB107×1:クラレ社製)などの熱水溶融タイプなども使用できる。 Further, vinylon binder fibers: thermal water melt type, such as (VPB107 × 1 manufactured by Kuraray Co., Ltd.) can also be used.

【0053】繊維状のバインダーの繊維径は特に限定されないが、0.3〜5デニールであることが好ましく、 [0053] Although the fiber diameter of the fibrous binder is not particularly limited, but is preferably 0.3 to 5 denier,
より好ましくは1〜2デニールである。 More preferably from 1 to 2 denier.

【0054】良好な引張り強度、折り適性を抄造段階で付与させるために繊維状のバインダーを配合することにより、不織布の内部強度を強くでき、抄造後の接着剤の付与工程、スリット工程でテンションが加わった際に起こり易い断紙や、スリット工程、プリーツ加工工程でこすられた時に起こり易い面剥けを抑える役割を果たす。 [0054] good tensile strength, by blending the fibrous binder for the folding aptitude granted papermaking step, can strongly internal strength of the nonwoven fabric, the process application of adhesive after papermaking, the tension in the slitting step easy and paper break occurs when applied, serves to slitting step, it suppresses the picking prone surfaces occur when rubbed by pleating step.

【0055】本発明における抗菌防黴剤を含有する繊維状物質を使用した湿式不織布を湿式抄紙法で製造する際、地合を良好にするためには、各種繊維をパルパーなどの分散タンク内で分散水に均一に分散する必要があり、そのために界面活性剤を用いることが望ましい。 [0055] The wet-laid nonwoven fabric using a fibrous material containing an antibacterial antifungal agent of the present invention when producing a wet paper-making method, in order to improve the formation, the various fibers in the dispersion tank such as pulper must be uniformly dispersed in the dispersing water, it is desirable to use a surfactant for this purpose.

【0056】界面活性剤は、アニオン系、カチオン系、 [0056] surfactants, anionic, cationic,
ノニオン系、両性に分類される。 Nonionic, are classified as amphoteric. アニオン系界面活性剤としては、例えば、カルボン酸塩、硫酸エステル塩、スルホン酸塩、リン酸エステル塩などが挙げられる。 Examples of the anionic surfactant, for example, carboxylates, sulfates, sulfonates, and the like phosphoric acid ester salts. カチオン系界面活性剤としては、アミン塩、アンモニウム塩などが挙げられる。 Examples of the cationic surfactants, amine salts, and ammonium salts. ノニオン系界面活性剤としては、エーテル型、エステル型、アミノエーテル型などが挙げられる。 Examples of the nonionic surfactant, ether type, ester type, and the like amino ether type. 両性界面活性剤としては、ベタイン型などが挙げられる。 Examples of the amphoteric surfactant, and the like betaine type.

【0057】均一に混合分散した繊維の分散安定性を向上させるために、アニオン性のポリアクリルアミド系粘剤を繊維分散液、または抄紙ヘッドに添加することにより、湿式抄造後のシートの地合はさらに向上する。 [0057] In order to uniformly improve the dispersion stability of the mixed dispersion fibers, by adding an anionic polyacrylamide viscosity agent fiber dispersion, or to the paper making head, after the wet papermaking formation of the sheet further improved.

【0058】本発明の抗菌防黴剤と吸着剤を含有する湿式不織布は、一般紙や湿式不織布を製造するための湿式抄紙機、例えば、長網抄紙機、円網抄紙機、傾斜ワイヤー式抄紙機を単独で1層であっても、同機種同士、異機種を組み合わせた2層以上の多層であっても良い。 [0058] wet-laid nonwoven fabric containing an antibacterial antifungal agent and the adsorbent of the present invention, generally paper and wet-laid nonwoven fabric wet paper making machine for the manufacture of, for example, Fourdrinier, cylinder paper machine, inclined-wire paper making even in one layer of the machine alone, with each other the same model, it may be two or more layers that combine heterogeneous. 又、 or,
抄紙機のワイヤーに水不透過部分を設けて抄くことにより、孔を開けて水はけ性をコントロールすることもできる。 By combing it provided water impermeable portion to the wire of the paper machine, it is also possible to control the drainage property perforated. 特に不織布を積層で使用する場合には速やかに下層の不織布まで液体が浸透するので好ましい。 Particularly preferred as the liquid to the underlying nonwoven fabric to penetrate quickly when using the nonwoven fabric laminate.

【0059】乾燥には、シリンダードライヤー、エアードライヤー、赤外線ドライヤーなどの乾燥機を用いることが可能である。 [0059] for drying, it is possible to use cylinder dryer, air dryer, the dryer, such as an infrared dryer. また、水はけ性を改良させるために、 Further, in order to improve drainage properties,
孔あけ加工を施しても良い。 It may be subjected to drilling.

【0060】シリンダードライヤーでの乾燥時に不織布を弛ませたクレープ状にすると見かけの表面積が増えるので保持出来る液体や臭気の吸収性が増大し、好ましい。 [0060] With the dry creped which slackened a nonwoven fabric of a cylinder dryer absorbing liquid or odor can hold the surface area of ​​an apparent increase is increased, preferred.

【0061】本発明の抗菌防黴剤と吸着剤を含有する不織布は、取り扱いのし易さなどの用途により、さらに強度、腰を向上させるために、液体の吸収性を損なわない範囲で各種バインダーを付与することが可能である。 [0061] nonwoven fabric containing an antimicrobial antifungal agent and the adsorbent of the present invention, by applications such as to ease of handling, further strength, in order to improve the waist, various binders in a range that does not impair the absorption of the liquid it is possible to impart.

【0062】バインダーとしては、例えば、アクリル系ラテックス、酢ビ系ラテックス、ウレタン系ラテックス、エポキシ系ラテックス、ポリエステル系ラテックス、SBR系ラテックス、NBR系ラテックス、エポキシ系バインダー、フェノール系バーンダー、PVA、デンプン、一般的に製紙工程で使用される紙力剤などが挙げられ、これらを単独、もしくは架橋剤と併用して使用できる。 [0062] As the binder, for example, acrylic latex, vinyl acetate latex, urethane latex, epoxy-based latex, polyester latex, SBR latex, NBR latex, epoxy-based binder, a phenolic Banda, PVA, starch, generally such as paper strength agents used are exemplified by the papermaking process, it can be used in combination singly or crosslinking agent.

【0063】本発明の抗菌防黴剤と吸着剤を含有する不織布の目付は特に限定しないが、加工のしやすさ、使いやすさからは15〜500g/m 2が一般的であり、好ましくは20〜300g/m 2である。 [0063] basis weight of the nonwoven fabric containing an antibacterial antifungal agent and the adsorbent of the present invention is not particularly limited, processing ease, from ease of use is generally 15~500g / m 2 is preferably it is a 20~300g / m 2. 使用に際して適当に不織布を重ねての使用が吸水性の点で好ましい。 Use of appropriately superimposed nonwoven in use is preferable in terms of water absorption.

【0064】また、本発明の有機化合物の金属塩よりなる抗菌防黴剤と接着剤としての高分子化合物と混合した組成物を不織布に塗布か含浸することも可能である。 [0064] It is also possible to the composition antibacterial antifungal agent of a metal salt of an organic compound mixed with a polymer compound as an adhesive of the present invention is impregnated or coated on the nonwoven fabric. 接着剤は市販の各種水溶性高分子化合物や水不溶性高分子化合物が使用される。 Adhesives commercially available various water-soluble polymer compound and water-insoluble polymer compound is used.

【0065】水不溶性高分子化合物としては、ウレタン系高分子化合物、スチレン−ブタジェン系高分子化合物、アクリル系高分子化合物、アクリロニトリル−ブタジェン系高分子化合物、エステル系高分子化合物、スチレン系高分子化合物、アミド系高分子化合物、塩化ビニル系化合物、酢酸ビニル系化合物、フッソ系化合物、シリコン系化合物、エチレン系高分子化合物やプロピレン系高分子化合物等のオレフィン系高分子化合物等が挙げられる。 [0065] As the water-insoluble polymer compound, a urethane-based polymer compound, a styrene - butadiene-based polymer compounds, acrylic polymer compounds, acrylonitrile - butadiene-based polymer compound, an ester-based polymer compound, a styrene-based polymer compound , amide-based polymer compounds, vinyl chloride compounds, vinyl acetate compounds, fluorine compounds, silicon compounds, olefinic polymer compounds such as ethylene-based polymer compound and the propylene polymer compounds.

【0066】水溶性高分子化合物としてはポリビニルアルコール系、デンプン系、ポリ酢酸ビニル系、ポリエチレンオキサイド、変性セルロース等が挙げられる。 [0066] As the water-soluble polymer compounds polyvinyl alcohol, starch-based, polyvinyl acetate, polyethylene oxide, modified cellulose, and the like.

【0067】水不溶性高分子化合物に自己乳化性を付与したり、乳化剤で水に分散させたものを乾燥した場合には膜の不連続部分が発生しやすく、抗菌防黴剤のような異種のものを加えた場合には特に顕著であり、その不連続部分より抗菌防黴剤の成分が移動しやすくなり、良好な抗菌防黴性が発現すると予想される。 [0067] or impart self-emulsifying property in water-insoluble polymer compound, a discontinuous portion of the film is likely to occur when dry are dispersed in water with an emulsifier, a heterologous like antibacterial antifungal agent is particularly pronounced when added things, tends to move the component of the antibacterial antifungal agent than its discontinuity, good antibacterial antifungal properties are expected to express.

【0068】特に、好ましい自己乳化型の水不溶性高分子化合物としては、ウレタン系高分子化合物、スチレン−ブタジェン系高分子化合物、アクリル系高分子化合物である。 [0068] In particular, preferred the self-emulsifying water-insoluble polymer compound, a urethane-based polymer compound, a styrene - butadiene polymer compound, an acrylic polymer compound.

【0069】抗菌防黴剤に付与する接着剤量は、抗菌防黴剤固形分に対して80重量%未満が好ましい。 [0069] amount of adhesive to be applied to the antibacterial antifungal agent is preferably less than 80 wt% with respect to the antibacterial antifungal agent solids. 80重量%を超えると、接着性は強くなるものの抗菌防黴性が低下する。 If more than 80 wt%, adhesion antibacterial antifungal of stronger ones decreases.

【0070】本発明における抗菌防黴剤の組成物には必要に応じて各種の顔料、染料等を混合することが出来る。 [0070] Various pigments as necessary to the composition antibacterial antifungal agent of the present invention, it is possible to mix the dyes.

【0071】本発明における抗菌防黴剤の組成物の作成例として銀、銅、亜鉛の複合系の抗菌防黴剤およびポリウレタン系高分子化合物について述べる。 [0071] Silver as an example of creating a composition antibacterial antifungal agent of the present invention, copper, the composite antibacterial antifungal agent and a polyurethane-based polymer compound of zinc described. 一例として、 As an example,
自己乳化型ポリウレタン系高分子化合物を使った例を用いて説明する。 It will be described with reference to examples using a self-emulsifiable polyurethane-based polymer compound. 1)水100gを用意する。 1) providing a water 100g. 2)硝酸銀0.1mol相当量を添加する。 2) adding silver nitrate 0.1mol significant amount. 3)硫酸銅0.05mol相当量を添加する。 3) adding copper sulfate 0.05mol significant amount. 4)硝酸亜鉛0.1mol相当量を添加する。 4) adding zinc nitrate 0.1mol equivalent amount. 5)室温下で十分に撹拌する。 5) To stirred thoroughly at room temperature. 6)2−メルカプトピリジン−N−オキシドナトリウム塩の0.4mol/l液1000gを撹拌しながら少しずつ添加する。 6) while stirring 0.4 mol / l solution 1000g mercaptopyridine -N- oxide sodium salt added in portions. 銀電極もしくは白金電極を用いて、電位計測すると、反応終了点を検知することができる。 Using a silver electrode or a platinum electrode, when potential measurement, it is possible to detect the reaction end point. 7)添加終了後、30分間撹拌し、十分に反応させる。 After 7) completion of the addition, stirred for 30 minutes to sufficiently react. 8)自己乳化型ポリウレタン系高分子化合物の40重量%水分散液を200g添加する。 8) the 40 wt% aqueous dispersion of the self-emulsifiable polyurethane-based polymer compound is added 200 g.

【0072】上記の手順により、本発明における抗菌防黴剤組成物Dであるメルカプトピリジン−N−オキシドの銀塩、銅塩および亜鉛塩と水不溶性高分子化合物よりなる分散液が得られる。 [0072] By the above procedure, a silver salt of mercaptopyridine--N- oxide is an antibacterial antifungal agent composition D, dispersions consisting copper salt and zinc salt and a water-insoluble polymer compound obtained in the present invention. そのままの液状でも抗菌防黴剤組成物の塗料として不織布に含浸、塗布等が可能である。 Impregnating the non-woven fabric as a paint antibacterial antifungal agent composition in neat liquid form, it is possible coating.

【0073】本発明における抗菌防黴剤の不織布単位面積当たりの含有量は、抗菌防黴剤の組成によるが、一般的には0.05g/m 2以上であり、0.1g/m 2以上が好ましい。 [0073] content per nonwoven unit area of the antibacterial antifungal agent according to the present invention, depending on the composition of the antimicrobial antifungal agent, generally at 0.05 g / m 2 or more, 0.1 g / m 2 or more It is preferred.

【0074】抗菌防黴剤が0.05g/m 2より少ないと使用の初期から充分な抗菌性、防黴性が得られにくい。 [0074] The antibacterial antifungal agent is less than 0.05 g / m 2 sufficient antimicrobial from the initial use, difficult antifungal property can be obtained. 抗菌防黴性の必要持続期間により適宜含有量を選択出来るが、数日以上の使用では0.1g/m 2以上が必要である。 You can select an appropriate amount as required duration of antibacterial antifungal, but the use of more than a few days is necessary 0.1 g / m 2 or more.

【0075】本発明における抗菌防黴剤の組成物は、作成したものをそのまま不織布に塗布又は含浸しても良いが、抗菌防黴剤の組成物の安定性向上や接着性を高めるために、塗布する前に各種接着剤を付与することや着色のための少量の顔料や染料の付与も可能である。 [0075] The composition of the antimicrobial antifungal agent in the present invention include, but are those prepared may be coated or impregnated directly into the nonwoven, in order to increase the stability improved and adhesiveness of the composition of an antibacterial antifungal agent, applying a small amount of pigment or dye for various adhesive imparting it or colored prior to application is also possible.

【0076】本発明における抗菌防黴剤の組成物を含浸又は塗布する不織布は、カード法等による乾式不織布、 [0076] nonwoven fabric is impregnated or coated with the composition of the antimicrobial antifungal agent in the present invention, dry nonwoven fabric by card method,
スパンボンド、メルトブローン等による不織布、湿式不織布、及びそれらのスパンレース加工不織布が使用される。 Spunbond, nonwoven according meltblown such as wet-laid nonwoven fabric, and their spunlace process nonwoven fabric is used.

【0077】使用される不織布の目付は特に制限は無いが、20〜500g/m 2が一般的であり、好ましくは20〜300g/m 2である。 [0077] basis weight of the nonwoven fabric used is not particularly limited but, 20 to 500 g / m 2 is generally preferably 20 to 300 g / m 2.

【0078】本発明の脱臭抗菌シートの作成方法の一例を挙げると、抗菌防黴剤と吸着剤を含有する、伸縮率1 [0078] As an example of how to create a deodorizing antibacterial sheet of the present invention, containing an adsorbent and an antibacterial antifungal agent, expansion ratio 1
0〜20%でクレープ加工された、50〜100g/m Was creped at 0~20%, 50~100g / m
2の2枚の不織布の間に吸水性ポリマーを加熱エンボス加工により封入したシートと抗菌防黴剤と吸着剤を含有する、伸縮率10〜20%でクレープ加工された、30 2 of the two nonwoven fabric sheet and an antimicrobial fungicide and the water-absorbing polymer is sealed by heat embossing between the containing adsorbent, which is creped with expansion ratio 10-20%, 30
〜60g/m 2の1〜4枚の不織布を重ね合わせ、上下に液体透過性のシートと液体不透過性のシートを重ねて両端部の全面に加熱エンボス加工で一体化した後、適当な長さでヒートシール、切断して脱臭抗菌シートを作成する。 Superposing 1-4 sheets of nonwoven to 60 g / m 2, was integrated by heat embossing on the entire surface of both ends vertically stacked sheets of the liquid-permeable sheet and the liquid impermeable, suitable lengths heat seal, cut and create a deodorizing antibacterial sheet of. 吸水性ポリマー封入シートを液体透過性のシート側にする方が瞬間吸水性から好ましい。 How to the water-absorbing polymer encapsulated sheet to the sheet side of the liquid permeable preferably from the moment water absorption.

【0079】吸水性ポリマー封入する時や液体透過性のシートと液体不透過性のシートの間に不織布を入れて一体化する時の加熱エンボス加工での温度は、不織布やシートに使用する繊維や樹脂で異なるが、80〜200℃ [0079] Temperature in the heating embossing when integrating put absorbent when and liquid permeable polymer enclosing the sheet and the liquid impermeable nonwoven fabric between the sheets, the Ya fibers used in the nonwoven fabric or sheet different but, 80~200 ℃ in resin
程度が一般的である。 The degree is common.

【0080】本発明の脱臭抗菌シートに適当な間隔で超音波加熱器等で部分的に溶着することによりしわや不織布の偏りを防止出来るので好ましい。 [0080] preferred because partly the bias of wrinkles or non-woven fabric can be prevented by welding at appropriate intervals deodorant antimicrobial sheet of the present invention an ultrasonic heater or the like.

【0081】本発明では、吸水性ポリマーの近隣に抗菌防黴剤が存在するので吸水性ポリマーが吸収した尿と接触している抗菌防黴剤の水可溶成分が尿中へ溶出して菌類の繁殖を抑えるために臭いの発生が少なくなるが、更に近辺に存在する吸着剤が一部で発生した臭いを吸着するので脱臭効果が大きくなると予想される。 [0081] In the present invention, close to the water soluble component of the antibacterial antifungal agent water-absorbing polymer in contact with absorbed urine since the antibacterial antifungal agent is present in the water-absorbing polymer is eluted into urine fungus Although the occurrence of odor is reduced in order to suppress the breeding are expected because the deodorizing effect is increased further adsorbent present in the vicinity adsorbs odor generated by some.

【0082】本発明の脱臭抗菌シートの用途として好ましくは人の介護用シートとして使用される場合であり、 [0082] a case preferably as application of deodorant antimicrobial sheet of the present invention is used as a care sheet for human,
臭気を抑え、患者の不快感を軽減するものである。 Reduce the odor, it is intended to reduce the discomfort of the patient.

【0083】本発明の脱臭抗菌シートの用途として好ましくは動物用シートとして使用される場合であり、臭気や黴を抑え、動物に付着した液体が飛散するのを軽減するものである。 [0083] Preferably the application of the deodorant antimicrobial sheet of the present invention are when used as an animal sheet, suppress odor and mold, in which liquid that has adhered to the animal is reduced from dispersing.

【0084】 [0084]

【実施例】以下に実施例を挙げて本発明を具体的に説明するが、本発明は実施例に限定されるものではない。 EXAMPLES The following examples illustrate the present invention in detail, but the present invention is not limited to the examples. なお、実施例中の「部」および「%」は、それぞれ「重量部」および「重量%」を示す。 Incidentally, "parts" and "%" in the examples each represent "parts by weight" and "% by weight".

【0085】製造例A 前記の発明の実施の形態の記載に準じて、カルボキシメチル基置換度0.22(DS=0.22)の変性NBK [0085] analogously as described in the embodiment of Preparation A above invention, the modified carboxymethyl substitution degree 0.22 (DS = 0.22) NBK
Pに、銀/2−メルカプトピリジン−N−オキシドよりなる抗菌防黴剤を含有する繊維状物質を作製した(以下、CP22AgMPと略記する)。 The P, to produce a fibrous material containing an antibacterial antifungal agent consisting of silver / 2-mercaptopyridine--N- oxide (hereinafter, abbreviated as CP22AgMP). 即ち、上記の変性NBKP分散液(固形分1000g)に硝酸銀0.5m In other words, silver nitrate 0.5m above modified NBKP dispersion (solids 1000 g)
olを加え、pHを5.5に調節してから、30分間撹拌する。 ol was added, the pH was adjusted to 5.5 and stirred for 30 minutes. 0.1M/lの2−メルカプトピリジン−N− Of 0.1M / l 2- mercaptopyridine -N-
オキシドナトリウム液を、変性NBKP分散液に加えられた硝酸銀と等モル相当量を添加した。 The oxide of sodium solution, and the silver nitrate and an equimolar equivalent amount was added to the modified NBKP dispersion was added. 30分間撹拌してから、硫酸でpHを4まで下げた後、脱水した。 After stirring for 30 minutes, after which the pH was lowered to 4 with sulfuric acid and dried. 脱水パルプに、再び500mlの水を加え、撹拌水洗して脱水した。 Dehydrated pulp, adding 500ml of water again, and dried by stirring with water. これを、銀/2−メルカプトピリジン−N−オキシドよりなる抗菌防黴剤を含有するカルボキシメチル基置換度0.22(DS=0.22)の変性NBKPとした。 This was a modification of the carboxymethyl substitution degree of 0.22, containing an antibacterial antifungal agent consisting of silver / 2-mercaptopyridine--N- oxide (DS = 0.22) NBKP.

【0086】比較例1で使用する不織布 2m 3の分散タンクにアクリル酸ソーダ系アニオン性界面活性剤(日本アクリル化学社製、プライマル850) [0086] Comparative Example sodium acrylate system dispersion tank nonwoven 2m 3 for use in 1 anionic surfactant (Nippon acrylic Chemical Co., Primal 850)
を全繊維に対して1%になるように添加し、NBKP Was added at 1% of the total fibers, NBKP
(カナダ標準濾水度480ml)、高叩解NBKP(カナダ標準濾水度200ml)、ポリエステル繊維(2デニール×5mm:帝人社製)、水中溶解温度が70℃のビニロンバインダー繊維(VPB107;1デニール× (Canadian Standard Freeness 480 ml), a high beating NBKP (Canadian Standard Freeness 200 ml), polyester fibers (2 denier × 5 mm: manufactured by Teijin Ltd.), the temperature of dissolution in water is 70 ° C. vinylon binder fibers (VPB107; 1 denier ×
3mm:クラレ社製)を各々60:5:30:5の比率で配合し、合成アルミノ珪酸亜鉛(水沢化学工業社製、 3 mm: manufactured by Kuraray Co., Ltd.) each 60: 5: 30: blended at a ratio of 5, the synthetic aluminosilicates, zinc (Mizusawa Chemical Industry Co.,
ミズカナイトA)を全繊維に対して20%になるように添加し、分散濃度0.2%で30分間分散した後、乾燥重量で60g/m 2になるように円網抄紙機で抄紙後、表面温度130℃のシリンダードライヤーで乾燥、クレープ加工(伸縮率10%)して比較例1で使用する湿式不織布を作製した。 Was added Mizukanaito A) so that 20% of the total fibers, was dispersed for 30 minutes at dispersion concentration of 0.2%, after paper in cylinder paper machine so that 60 g / m 2 by dry weight, dried cylinder dryer having a surface temperature of 130 ° C., to produce a wet-laid nonwoven fabric to be used in the creping (expansion ratio of 10%) to Comparative example 1. 同様にして乾燥重量が30g/m 2の湿式不織布を作製した。 Dry weight to prepare a wet-laid nonwoven fabric of 30 g / m 2 in the same manner.

【0087】実施例1〜5で使用する不織布 比較例1のNBKPの一部を、上記製造例Aで得られた本発明における繊維状物質であるCP22AgMPに、 [0087] The part of NBKP nonwoven Comparative Example 1 used in Example 1-5, the CP22AgMP a fibrous material in the present invention obtained in Preparation Example A,
表1記載の配合量で置き換えた外は、比較例1で使用する不織布と同様にして、実施例1〜5で抗菌防黴剤と吸着剤を含有する不織布として使用する、乾燥重量が60 Table 1 outer was replaced with the amount of description, as in the nonwoven fabric used in Comparative Example 1, used as a nonwoven fabric containing an adsorbent and an antibacterial antifungal agent in Examples 1-5, the dry weight is 60
g/m 2と30g/m 2の湿式不織布を作製した。 The wet nonwoven fabric g / m 2 and 30 g / m 2 was produced.

【0088】製造例B 製造例Aと同様であるが、前記の発明の実施の形態の記載に準じて、CP22AgMPの代わりに、カルボキシメチル基置換度0・40(DS=0・40)の変性NB [0088] is similar to Production Example B Production Example A, is prepared analogously as described in the embodiment of the invention, instead of CP22AgMP, modified carboxymethyl substitution degree 0 · 40 (DS = 0 · 40) NB
KPに(銀、銅、亜鉛)/2−メルカプトピリジン−N KP to (silver, copper, zinc) / 2-mercaptopyridine -N
−オキシドよりなる抗菌防黴剤を含有する繊維状物質を作製した(以下、CP40Ag25Cu25Zn50M - to prepare a fibrous material containing an antibacterial antifungal agent comprising from oxide (hereinafter, CP40Ag25Cu25Zn50M
Pと略記する。 Abbreviated as P. なお、金属原子の次の数字は、モル%比を表わす)。 Incidentally, the next number of the metal atoms represents a mole% ratio). 即ち、上記の変性NBKP分散液(固形分1000g)に硝酸銀0.25mol、硫酸銅0.25 That is, the modified NBKP dispersion (solids 1000 g) of silver nitrate 0.25 mol, copper sulfate 0.25
mol、硝酸亜鉛0.5molを加え、pHを5.5に調節してから、30分間撹拌する。 mol, zinc nitrate 0.5mol addition, the pH was adjusted to 5.5 and stirred for 30 minutes. 0.1M/lの2− Of 0.1M / l 2-
メルカプトピリジン−N−オキシドナトリウム液を、 Mercaptopyridine -N- oxide sodium solution,
1.75mol相当量を添加した。 1.75mol considerable amount was added. 30分間撹拌してから、硫酸でpHを4まで下げた後、脱水した。 After stirring for 30 minutes, after which the pH was lowered to 4 with sulfuric acid and dried. 脱水パルプに、再び500mlの水を加え、撹拌水洗して脱水し、CP40Ag25Cu25Zn50MPを得た。 Dehydrated pulp, adding 500ml of water again and stirred rinsed and dehydrated, to obtain a CP40Ag25Cu25Zn50MP.

【0089】実施例6〜10で使用する不織布 比較例1のNBKPの一部を、上記製造例Bで得られた本発明における繊維状物質であるCP40Ag25Cu [0089] The part of NBKP nonwoven Comparative Example 1 used in Examples 6-10, a fibrous material in the present invention obtained in Production Example B CP40Ag25Cu
25Zn50MPに、表1記載の配合量で置き換えた外は、比較例1と同様にして、実施例6〜10で抗菌防黴剤と吸着剤を含有する不織布として使用する、乾燥重量が60g/m 2と30g/m 2の湿式不織布を作製した。 The 25Zn50MP, outside was replaced with the blending amount shown in Table 1, in the same manner as in Comparative Example 1, used as a nonwoven fabric containing an adsorbent and an antibacterial antifungal agent in Examples 6-10, a dry weight of 60 g / m 2 and 30g / m 2 of wet-laid nonwoven fabric was produced.

【0090】製造例C 前記の発明の実施の形態の記載に準じて、銀/2−メルカプトピリジン−N−オキシドを含有させた、有機化合物の金属塩よりなる抗菌防黴剤とウレタン系高分子化合物とアクリル系高分子化合物を含む抗菌防黴剤の組成物を作製した(以下、AgMP−UA0.3と略記する)。 [0090] analogously as described in the embodiment of Preparation C the invention, the silver / 2-mercaptopyridine--N- oxide was contained, antibacterial antifungal agent of a metal salt of an organic compound and a urethane polymer the compound and compositions of the antibacterial antifungal agent containing an acrylic polymer was prepared (hereinafter, abbreviated as AgMP-UA0.3). 即ち、水に硝酸銀0.1molを加え、攪拌する。 In other words, silver nitrate 0.1mol added to water and stirred. 0.1mol/lの2−メルカプトピリジン−N− Of 0.1mol / l 2- mercaptopyridine -N-
オキシドナトリウム液を、加えられた硝酸銀と等モル相当量を添加し、30分間撹拌する。 The oxide of sodium solution, was added silver nitrate and an equimolar equivalent amount was added and stirred for 30 minutes. これに自己乳化型ウレタン系高分子化合物(大日本インキ化学工業社製、ハイドランHW−350)の水分散液を加え、5分間攪拌した後、同重量の自己架橋型アクリル系高分子化合物(大日本インキ化学工業社製、ボンコート3256)の水分散液を加え、銀/2−メルカプトピリジン−N−オキシドの抗菌防黴剤のウレタン系高分子化合物に対する重量比を0.3とした。 This self-emulsifying urethane polymer compound (produced by Dainippon Ink and Chemicals, Inc., Hydran HW-350) was added an aqueous dispersion of, after stirring for 5 minutes, the weight of self-crosslinking acrylic polymer compound (Large Nippon ink chemical industry Co., Boncoat 3256) aqueous dispersion were added, and the weight ratio of urethane polymer compound antibacterial antifungal agent of a silver / 2-mercaptopyridine--N- oxide and 0.3. 尚、括弧内金属原子の次の数字は、モル%比を表わし、最後尾の数字は水不溶性高分子化合物に対する抗菌防黴剤の重量比を表わす。 Note that the following numbers in parentheses metal atom represents a mole% ratio, the last digit represents the weight ratio of the antimicrobial antifungal agents for water-insoluble polymeric compound.

【0091】製造例D 製造例Cと同様であるが、前記の発明の実施の形態の記載に準じて、AgMP−UA0.3の代わりに、(銀、 [0091] is similar to Production Example D Production Example C, and according to the description of an embodiment of the invention, instead of AgMP-UA0.3, (silver,
銅、亜鉛)/2−メルカプトピリジン−N−オキシドの抗菌防黴剤を含有した自己乳化型ウレタン系高分子化合物(ハイドランHW−350)と自己架橋型アクリル系高分子化合物(ボンコート3256)の水分散液を作製した。 Copper, water zinc) / 2-mercaptopyridine--N- oxide self-emulsifying urethane polymer compound containing an antibacterial antifungal agent (Hydran HW-350) a self-crosslinking acrylic polymer compound (Voncoat 3256) to prepare a dispersion. 即ち、硝酸銀0.25mol、硫酸銅0.25m In other words, silver nitrate 0.25mol, copper sulfate 0.25m
ol、硝酸亜鉛0.5mol及びそれらの総モル相当量である1.75molの2−メルカプトピリジン−N− ol, of 1.75mol a zinc nitrate 0.5mol and the total molar equivalent amounts of their 2-mercaptopyridine -N-
オキシドナトリウム水溶液を添加、攪拌し、自己乳化型ウレタン系高分子化合物水分散液を添加、攪拌後、同重量の自己架橋型アクリル系化合物水分散液を添加、攪拌して、(銀、銅、亜鉛)/2−メルカプトピリジン−N Added oxide aqueous sodium stirred, adding a self-emulsifying urethane polymer compound aqueous dispersion after stirring, adding the same weight of self-crosslinking acrylic compound aqueous dispersion was stirred, (silver, copper, zinc) / 2-mercaptopyridine -N
−オキシドの抗菌防黴剤と自己乳化型ウレタン系高分子化合物と自己架橋型アクリル系高分子化合物との重量比を0.3とした(以下、Ag25Cu25Zn50MP - the weight ratio between the antibacterial antifungal agent and a self-emulsifiable urethane polymer compound oxide with self-crosslinking acrylic polymer compound was 0.3 (hereinafter, Ag25Cu25Zn50MP
−UA0.3と略記する)。 Abbreviated as -UA0.3). 尚、括弧内金属原子の次の数字は、モル%比を表わし、最後尾の数字は水不溶性高分子化合物に対する抗菌防黴剤の重量比を表す。 Note that the following numbers in parentheses metal atom represents a mole% ratio, the last digit represents the weight ratio of the antimicrobial antifungal agents for water-insoluble polymeric compound.

【0092】実施例11、12で使用する不織布 5デニールのポリアクリル繊維50重量%と6デニールのポリエチレン−ポリプロピレン複合繊維50重量%からなる混合ウエブを熱処理した乾式不織布(目付60g [0092] As used in the Examples 11 and 12 the nonwoven 5 denier polyacrylic fibers 50% by weight of 6 denier polyethylene - dry nonwoven fabric was heat-treated mixture web of polypropylene composite fiber 50 wt% (basis weight 60g
/m 2 、厚さ300μm)に上記製造例C、Dで得られた本発明の抗菌防黴剤の組成物を抗菌防黴剤が5g/m / M 2, a thickness of 300 [mu] m) in Production Example C, an antibacterial antifungal agent composition antibacterial antifungal agent of the present invention obtained in D is 5 g / m
2の乾燥塗布量になるようにサイズプレス装置で含浸し、110℃で乾燥して実施例11、12で使用する抗菌防黴剤と吸着剤を含有する不織布を得た。 Impregnated with a size press apparatus so that the second dry coating amount to give a nonwoven fabric containing an adsorbent and an antibacterial antifungal agent used in dried Examples 11 and 12 at 110 ° C.. 尚、塗布適性を向上させるために抗菌防黴剤の組成物にセルロースエーテル(信越化学工業社製、メトローズSH3000 Incidentally, the cellulose ethers in the composition of the antibacterial antifungal agent for improving the coatability (Shin-Etsu Chemical Co., Ltd., Metolose SH3000
0)水溶液を適量添加して含浸した。 0) aqueous solution was impregnated by adding an appropriate amount of. 以下の実施例、比較例でも同様にしてセルロースエーテルを必要に応じて適量添加して含浸した。 The following examples were impregnated with suitable amount as needed cellulose ether in the same manner in Comparative Example.

【0093】実施例13で使用する不織布 実施例12で使用する不織布の製造で、Ag25Cu2 [0093] In the manufacture of nonwoven fabric used in the nonwoven Example 12 used in Example 13, Ag25Cu2
5Zn50MP−UA0.3の代わりに、塩化ベンザルコニウム含有アクリル系高分子化合物(ボンコート32 Instead of 5Zn50MP-UA0.3, benzalkonium chloride-containing acrylic polymer compound (Voncoat 32
56)を使用して塩化ベンザルコニウムの含浸量が5g 56) Use the impregnation amount of benzalkonium chloride 5g
/m 2になるように含浸、乾燥して実施例13で使用する抗菌防黴剤と吸着剤を含有する不織布を得た。 Impregnation such that / m 2, to obtain the antibacterial antifungal agent used a nonwoven fabric containing adsorbent dried to Example 13. なお、 It should be noted that,
塩化ベンザルコニウム含有アクリル系高分子化合物は、 Benzalkonium containing acrylic polymer compound chloride,
製造例Cで用いた自己乳化型ウレタン系高分子化合物と自己架橋型アクリル系高分子化合物を固形で10gに対して、0.1mol/lの塩化ベンザルコニウム液120 Against 10g self-emulsifying urethane polymer compound and a self-crosslinking acrylic polymer compound used in Production Example C a solid, 0.1 mol / l of benzalkonium chloride solution 120
mlを加え、pH5.5に調整後、撹拌して作製した。 ml and the mixture was adjusted to pH 5.5, was prepared by stirring.

【0094】比較例2で使用する不織布 実施例11で用いた乾式不織布(目付60g/m 2 、厚さ300μm)を何も含浸しないでそのままで比較例2 [0094] dry nonwoven fabric used in the nonwoven Example 11 used in Comparative Example 2 (basis weight 60 g / m 2, thickness 300 [mu] m) without anything impregnating Comparative intact Example 2
の不織布とした。 It was a non-woven fabric.

【0095】比較例3で使用する不織布 実施例11で得られた抗菌防黴剤を含浸した不織布上にポリエチレン−酢酸ビニル系バインダー粒子(平均粒子経20μm)を30g/m2散布、赤外線ヒーターで1 [0095] Polyethylene on the nonwoven fabric impregnated with an antibacterial antifungal agent obtained in nonwoven examples 11 used in Comparative Example 3 - vinyl acetate binder particles (average particle through 20 [mu] m) to 30 g / m @ 2 sprayed 1 with an infrared heater
20℃に加熱後比較例1で使用する不織布を載せて加圧して比較例3で使用する不織布を作製した。 Pressurized put the nonwoven fabric to be used in the heating after Comparative Example 1 to 20 ° C. and to produce a nonwoven fabric used in Comparative Example 3.

【0096】実施例11〜13で使用する不織布と比較例2で使用する不織布上に吸着剤(ミズカナイトM)とポリエチレン−酢酸ビニル系バインダー粒子(平均粒子径20μm)の重量比10:20の混合物を30g/m Weight ratio mixture 10:20 of vinyl acetate binder particles (average particle size 20 [mu] m) - [0096] Polyethylene nonwoven fabric used in Examples 11-13 adsorbent onto the nonwoven fabric used in Comparative Example 2 (Mizukanaito M) a 30g / m
2散布、赤外線ヒーターで120℃に加熱後各々に実施例11〜13で使用する不織布と比較例2で使用する不織布を載せて加圧して実施例11〜13、比較例2で使用する抗菌防黴剤と吸着剤を含有する不織布を作製した。 2 spraying, carried pressurized put the nonwoven fabric used in Comparative Example 2 with the nonwoven fabric to be used in the heating after each Examples 11-13 to 120 ° C. in an infrared heater Example 11-13, antibacterial used in Comparative Example 2 to produce a nonwoven fabric containing a mildew agent and the adsorbent.

【0097】実施例1〜13、及び比較例1〜4 ポリプロピレン製乾式不織布(目付15g/m 2 )、とポリエチレン製フルム(目付15g/m 2 )の縦42c [0097] Vertical 42c of Examples 1-13 and Comparative Examples 1-4 Polypropylene dry nonwoven fabric (basis weight 15 g / m 2), and polyethylene Furumu (basis weight 15 g / m 2)
m×横62cmの長方形シートを重ねて、その3辺をヒートシールして内寸が41cm×61cmの袋(以下袋Aと記す)を作製した。 Overlapping rectangular sheets of m × horizontal 62cm, inner size and heat-sealing the three sides to prepare a bag (hereinafter referred to as a bag A) of 41cm × 61cm. 実施例1〜10、比較例1で使用する目付60g/ 2の不織布2枚の間に吸水性ポリマー(アクリル系、平均粒子径100μm)を30g/m Examples 1 to 10, the water-absorbing polymer (acrylic, average particle size 100 [mu] m) between two nonwoven having a basis weight of 60 g / 2 used in Comparative Example 1 to 30 g / m
2全面に散布した後110℃エンボス加工により一体化してシートにした。 And to the sheet and integrated by a 110 ° C. embossing it was sprayed into 2 entirely. 袋Aの中に前記の吸水性ポリマーを封入して一体化した40cm×60cmのシート1枚と実施例1〜10で使用する目付30g/m 2の不織布4 Having a basis weight of 30 g / m 2 for use with 40 cm × 60cm sheet one in Example 1 to 10 were integrated by sealing the water-absorbing polymer in the bag A nonwoven fabric 4
0cm×60cmを4枚入れて4辺の端部(幅1.5c End of the four put four sides of the 0 cm × 60cm (width 1.5c
m)を120℃ヒートシール加工して実施例1〜10の脱臭抗菌シートを得た。 m) the 120 ° C. heat sealing process to obtain a deodorant antimicrobial sheet of Examples 1 to 10. 実施例11〜13で使用する抗菌防黴剤と吸着剤を含有する不織布、比較例2で使用する吸着剤を含有する不織布および比較例3で使用する抗菌防黴剤を含有する不織布各々2枚の間に吸水性ポリマー(架橋ポリアクリル酸ソーダ系、平均粒子径10μ Nonwoven fabric containing an adsorbent and an antibacterial antifungal agent used in Examples 11-13, nonwoven each two containing antibacterial antifungal agent used in nonwovens and Comparative Example 3 containing the adsorbent used in Comparative Example 2 water-absorbing polymer (crosslinked sodium polyacrylate based between the average particle diameter of 10μ
m)を30g/m 2全面に散布した後エンボス加工により一体化してシートにした。 It was sheet m) and integrated by embossing after sprayed 30 g / m 2 over the entire surface. 袋Aの中に前記の吸水性ポリマーを封入して一体化した40cm×60cmのシート1枚と実施例11〜13で使用する抗菌防黴剤と吸着剤を含有した不織布40cm×60cmを2枚を入れて4辺の端部(幅1.5cm)を120℃ヒートシール加工して実施例11〜13の脱臭抗菌シートを得た。 Two said nonwoven 40 cm × 60cm containing an antibacterial antifungal agent and adsorbent used water-absorbing polymer in the sheet one and Examples 11-13 of 40 cm × 60cm that integrates enclosed in the bag A to obtain a deodorant antimicrobial sheet of examples 11-13 was 120 ° C. the heat sealing process the ends of the four sides (width 1.5 cm) put. 同様にして比較例1で使用する、目付60g/m 2の不織布の間に吸水性ポリマーを封入して一体化した40cm× Similarly used in Comparative Example 1, 40 cm × was integrated by encapsulating the water-absorbing polymer during the non-woven fabric having a basis weight 60 g / m 2
60cmのシート1枚と比較例1で使用する目付30g Basis weight 30g used in Comparative Example 1 and one sheet of 60cm
/m 2の不織布40cm×60cmを4枚を袋Aに入れて4辺の端部(幅1.5cm)を120℃ヒートシール加工して比較例1の脱臭抗菌シートを得た。 / M 2 of the 4 sheets of nonwoven fabric 40 cm × 60cm end of four sides bagged A (width 1.5 cm) 120 ° C. The heat sealing process to obtain the deodorant antimicrobial sheet of Comparative Example 1. 同様にして比較例2で使用する不織布の間に吸水性ポリマーを封入して一体化した40cm×60cmのシート1枚と比較例2で使用する不織布40cm×60cmを2枚袋Aに入れて4辺の端部(幅1.5cm)を120℃ヒートシール加工して比較例2の脱臭抗菌シートを得た。 4 Put nonwoven 40 cm × 60cm used in Comparative Example 2 the water-absorbing polymer and one sheet of 40 cm × 60cm that is integrated with enclosed between the nonwoven fabric used in Comparative Example 2 In the same manner the two bags A to obtain a deodorant antimicrobial sheet of Comparative example 2 end sides (width 1.5 cm) 120 ° C. the heat sealing process to. 同様にして比較例3で使用する吸水性ポリマーを封入して一体化した40cm×60cmのシート1枚と比較例3で使用する不織布40cm×60cmを2枚袋Aに入れて4 4 Put nonwoven 40 cm × 60cm used in Comparative Example 3 and one sheet of 40 cm × 60cm that the water-absorbing polymer used and integrated by sealing in Comparative Example 3 in the same manner into two bags A
辺の端部(幅1.5cm)を全面に120℃ヒートシール加工して比較例3の脱臭抗菌シートを得た。 To obtain a deodorant antimicrobial sheet of Comparative Example 3 end sides (width 1.5 cm) to 120 ° C. heat sealing process on the entire surface. 比較例4 Comparative Example 4
は実施例11で使用する抗菌防黴剤と吸着剤を含有した目付60g/m 2の不織布2枚の間に吸水性ポリマー3 Example 11 basis weight 60 g / m 2 nonwoven two water-absorbing polymer 3 between containing an antibacterial antifungal agent and the adsorbent for use in
0g/m 2を散布しただけでエンボス加工せずに使用し、抗菌防黴剤と吸着剤を含有した目付30g/m 2の不織布を4枚と共に袋Aに入れて4辺の端部(幅1.5 Used without embossing only were sprayed with 0 g / m 2, 4 sides of the end portion in the bag A with 4 sheets of basis weight 30 g / m 2 nonwoven fabric containing an adsorbent and an antibacterial antifungal agent (width 1.5
cm)を120℃ヒートシール加工して比較例4の脱臭抗菌シートを得た。 cm) the 120 ° C. heat sealing process to obtain a deodorant antimicrobial sheet of Comparative Example 4.

【0098】前記の実施例1〜10で使用する抗菌防黴剤と吸着剤を含有する不織布、実施例11〜13で使用する抗菌防黴剤を含有する不織布、および比較例1〜4 [0098] nonwoven fabric containing an adsorbent and an antibacterial antifungal agent used in Examples 1 to 10 above, a nonwoven fabric containing an antimicrobial antifungal agent used in Examples 11-13, and Comparative Examples 1 to 4
で使用する不織布について、抗菌性を測定した。 In the nonwoven fabric to be used to measure the antibacterial properties. 得られた結果を表1および表2に示す。 The results obtained are shown in Table 1 and Table 2.

【0099】実施例1〜13、及び比較例1〜4で得られた脱臭抗菌シートの脱臭性を犬の尿で評価した。 [0099] it was evaluated Examples 1-13, and the deodorization of the deodorizing antibacterial sheet obtained in Comparative Examples 1 to 4 in dog urine. 得られた結果を表1および表2に示す。 The results obtained are shown in Table 1 and Table 2.

【0100】実施例1〜13、及び比較例1〜4で得られた脱臭抗菌シートのウエットバック性を純水で評価した。 [0100] it was evaluated Examples 1-13, and the wet back of the deodorant antimicrobial sheet obtained in Comparative Examples 1 to 4 with pure water. 得られた結果を表1および表2に示す。 The results obtained are shown in Table 1 and Table 2.

【0101】<抗菌性>大腸菌(E−coli IF0 [0101] <antibacterial> E. coli (E-coli IF0
3301)を液体培地(ペプトン・イースト)で24時間前培養し、希釈して2×10 8セル/mlの試験液を調整した。 The 3301) and precultured for 24 hours in a liquid medium (peptone-yeast), to prepare a test solution diluted to 2 × 10 8 cells / ml. 上記実施例および比較例で使用する不織布の試験片2cm×2cmを用意し、水道水で流水水洗後、 Providing a test specimen 2 cm × 2 cm of the nonwoven fabric used in the above Examples and Comparative Examples, after running water washing with tap water,
それぞれをペトリ皿上に配置し、上記試験液を5滴(約0.1ml)滴下し、乾燥しないようにカバーをして3 Each was placed on a Petri dish and 5 drops of the test solution (approximately 0.1 ml) was added dropwise, and the cover so as not to dry 3
8℃で24時間経時した。 For 24 hours over time at 8 ℃. 経時後、試験片のそれぞれをNutrient Broth寒天培地上に押し当て、 After aging, pressed against each test specimen on Nutrient Broth agar medium,
試験片上の菌を転写させて剥離し、38℃で24時間培養し、観察した。 The cells on the specimen was peeled by transferring, for 24 hours at 38 ° C., it was observed. 評価は、次のとおりとした。 Evaluation was as follows. 評価グレード −− ほぼ完全に殺菌し、菌の成育がない。 Evaluation grade - almost completely sterilized, there is no growth of fungus. − 2cm×2cm転写面に5コロニー以下の成育はあるが、殆ど完全に殺菌。 - a 2 cm × 2 cm transfer surface there is a growth of less than 5 colonies, but almost completely sterilized. + 2cm×2cm転写面に100コロニー以下で良好な抗・殺菌作用。 + 2 cm × 2 cm transferring good anti-bactericidal action at 100 colony below surface. ++ 2cm×2cm転写面に効果は認められるが、 ++ but the effect is observed in 2cm × 2cm transfer surface,
弱いか、少ない。 Weak or less. +++ 2cm×2cm転写面に実質的効果なし。 +++ substantially no effect on the 2 cm × 2 cm transfer surface.

【0102】<犬尿での脱臭性>実施例1〜13、比較例1〜3で得られた脱臭抗菌シートについて、各々40 [0102] Examples 1 to 13 <deodorizing Dogs Urine>, the deodorant antimicrobial sheet obtained in Comparative Examples 1 to 3, each 40
cm×30cmに切断して2枚の試験シートを作成した。 And cut into cm × 30cm was created two of the test sheet. 一方の試験シートの中心部に犬の尿を各20mlしみ込ませ、ポリエチレン製ビニール袋に入れて38℃、 Center of one of the test sheets impregnated each 20ml dog urine, placed in 38 ° C. in a polyethylene plastic bag,
24時間静置した。 It was allowed to stand for 24 hours. 他方の試験シートも同様にポリエチレン製ビニール袋に入れて同様に38℃、24時間静置した。 Similarly 38 ° C. Also other test sheets were placed in polyethylene plastic bags similar, and allowed to stand 24 hours. 各試験シートについて20名が下記の評価グレードで脱臭性を評価し、その平均を最終評価とした。 20 people for each test sheet was evaluated deodorization evaluation grades below, and the average and final evaluation. 未処理シートは全て○であった。 Untreated sheet was all ○. 評価グレード ○ 臭い無し ○〜△ 殆ど臭い無し △ やや臭い有り × 臭い多い No evaluation grade ○ no smell ○ ~ △ almost smell △ smell often slightly smell there ×

【0103】<ウエットバック性>実施例1〜13、比較例1〜4の脱臭抗菌シートの液体透過性不織布側を上にして置き、半径5cmの円内に純水5gを吸収させる。 [0103] <wetback properties> Examples 1 to 13, placed in the top liquid-permeable nonwoven fabric side of the deodorizing antibacterial sheet of Comparative Examples 1 to 4, to absorb the pure water 5g within a circle of radius 5 cm. 10秒後に重量を測定した濾紙(5C;東洋濾紙社製、11cm径)を載せ、ポリ塩化ビニル板を介して1 10 seconds filter paper and weighed after (5C; Toyo Roshi Co., 11cm diameter) loaded with, via a polyvinyl chloride plate 1
0kgの重りを載せて1分後に重りとポリ塩化ビニル板を取り除いて濾紙の重量を測定する。 Put a weight of 0kg remove the weight and polyvinyl chloride plates after 1 minute measuring the weight of the filter paper. 試験前後の濾紙の重量から吸水量を算出する。 Calculating the water absorption from the weight of the filter paper before and after the test. 少ない方が良。 Less it is good.

【0104】 [0104]

【表1】 [Table 1]

【0105】 [0105]

【表2】 [Table 2]

【0106】表1および表2の結果から、次のことが解る。 [0106] Table 1 and the results in Table 2, indicate the followings.

【0107】製造例Aに記載した抗菌防黴剤(CP22 [0107] Antibacterial antifungal agents described in Preparation A (CP22
AgMP)を含む本発明における繊維状物質を、不織布の構成繊維の一つであるNBKPの一部に置き換えて使用した実施例1〜5の場合、抗菌防黴剤を含まない比較例1に比べて、抗菌性および犬尿での脱臭性とも優れていた。 The fibrous material in the present invention including AgMP), the case of Examples 1 to 5 was used to replace a part of NBKP, which is one of the constituent fiber of the nonwoven fabric, compared with Comparative Example 1 containing no antimicrobial antifungal agent Te, it was superior to the deodorization of an antimicrobial and dog urine. . その配合量は、5部置き換えで効果が認められ、置き換え量が増えるに従って効果は大きくなる。 The amount thereof, effect was observed by replacing 5 parts, the effect increases as the amount of replacement is increased. 効果は20部以上の置き換えで完全な抗菌性が得られる結果である。 Effect is the result of complete antimicrobial is obtained by replacing more than 20 parts.

【0108】製造例Bに記載した抗菌防黴剤(CP40 [0108] Antibacterial antifungal agents described in Preparation B (CP40
Ag25Cu25Zn50MP)を含む本発明における繊維状物質を、不織布の構成繊維の一つであるNBKP The fibrous material in the present invention including Ag25Cu25Zn50MP), which is one of the constituent fiber of the nonwoven fabric NBKP
の一部に置き換えて使用した実施例6〜10の場合、抗菌防黴剤を含まない比較例1に比べて、抗菌性および犬尿での脱臭性に効果が有ることが解った。 For Examples 6 to 10 was used to replace a part of, as compared with Comparative Example 1 containing no antimicrobial fungicide effect it has been found that there deodorization of an antimicrobial and dog urine. その配合量は、5部置き換えでも充分に効果が認められ、10部以上で完全な抗菌性が得られる結果であり、製造例Aの抗菌防黴剤(CP22AgMP)よりも少量でも効果の有る結果であった。 Results the amount thereof, observed sufficiently effective even replace 5 parts, the result of complete antimicrobial is obtained at least 10 parts, having the effect even in a small amount than the antibacterial antifungal agent of preparation A (CP22AgMP) Met.

【0109】製造例C,Dで得られた抗菌防黴剤と水不溶性高分子化合物からなる抗菌防黴剤組成物を不織布に含浸した実施例11、12は、抗菌防黴剤の乾燥重量は5.0g/m 2である。 [0109] Production Example C, Examples 11 and 12 impregnated with antibacterial antifungal agent composition consisting obtained antibacterial antifungal agent and a water-insoluble polymer compound D in nonwoven fabric, the dry weight of the antimicrobial antifungal agent it is 5.0g / m 2. 水不溶性高分子化合物に対する抗菌防黴剤の重量比が同じ0.3の銀系の抗菌防黴剤使用の実施例11は、銀、銅、亜鉛系抗菌防黴剤使用の実施例12と比較して明らかに抗菌性、犬尿での脱臭性は劣っている結果であった。 Comparative water-insoluble polymer compound Example 11 in a weight ratio of the antimicrobial antifungal agents used antibacterial antifungal agent of a silver-based in the same 0.3 against silver, copper, and Example 12 using zinc antibacterial antifungal agent clearly, antibacterial and, deodorizing properties at dog urine was the result of poor. 実施例13は抗菌防黴剤として塩化ベンザルコニウムを使用しており、実施例11よりも更に抗菌性、犬尿での脱臭性が劣っており、実使用で効果の得られる下限であった。 Example 13 is using benzalkonium chloride as an antibacterial antifungal agent, further antimicrobial than Example 11, and poor deodorizing Dogs urine was lower obtained effective in practical use . 抗菌防黴剤を使用していない比較例2は抗菌性、犬尿での脱臭性は無い結果であった。 Comparative Example 2 Antimicrobial not using an antibacterial antifungal agent, it was not the result deodorizing Dogs urine.

【0110】比較例3は実施例11で吸着剤を使用しない場合であるが、犬尿での脱臭性は、吸着剤が無いために液体中での菌の繁殖は殆ど抑えられるが、尿中の一部の繁殖や固体状の排出物内部の菌の繁殖は抑えられず、 [0110] While Comparative Example 3 is a case that does not use the adsorbent in Example 11, the deodorizing Dogs urine, although growth of bacteria in the liquid can be almost suppressed because no adsorbent, urinary breeding of some breeding and solid effluent internal bacteria not suppressed,
脱臭性は実施例11より比較例3の方が劣る結果になったと予想される。 Deodorization is expected to become inferior results found the following Comparative Example 3 than in Example 11.

【0111】実施例1〜10、比較例1はウエットバック性はすべて良好であり、実施例11〜13、比較例2、3では、乾式不織布を使用していることと、不織布の積層に用いたバインダー粒子の影響でウエットバック性は低下した。 [0111] Examples 1-10, Comparative Example 1 are all wet back property was good, Examples 11-13, Comparative Examples 2 and 3, and that are using the dry nonwoven fabric, use a laminate of the nonwoven fabric wetback properties under the influence of stomach binder particles decreased.

【0112】比較例4は実施例11で吸水性ポリマーをエンボス加工しないで散布しただけの場合であるが、使用する不織布の抗菌性は実施例11と同等であるが、犬尿での脱臭性は吸水性ポリマーと抗菌防黴剤との間隔が広がった事や吸水性ポリマーが動きやすく偏在しやすい事により悪くなっている。 [0112] While Comparative Example 4 is a case of the water-absorbing polymer in Example 11 only was sprayed without embossing, although antimicrobial nonwoven fabric used is the same as in Example 11, deodorizing Dogs Urine are worsened by easily localized easy movement is water-absorbing polymer and that the distance between the antibacterial antifungal agent spread and water-absorbing polymer. ウエットバック性も吸水性ポリマーが偏在しやすいので劣った。 Wet-back property also water-absorbing polymer is inferior because easy to uneven distribution.

【0113】 [0113]

【発明の効果】本発明に使用される抗菌防黴剤と吸着剤を含有した不織布間に吸水性ポリマーを加熱エンボス加工で一体化したシートと抗菌防黴剤を含有した不織布とを封入した袋は抗菌性、脱臭性、ウエットバック性が良好である。 Bag encapsulating and nonwoven fabric containing seat and antimicrobial antifungal agent with an integrated water-absorbing polymer between nonwoven containing a heating embossing an antibacterial antifungal agent and adsorbent used with the present invention antimicrobial, deodorant, wetback is good. エンボス加工により吸水性ポリマーを覆っている不織布に含有されている抗菌防黴剤と吸水性ポリマーが近接しているので吸水性ポリマーが吸収した尿中へ抗菌防黴剤の一部が溶出して菌類の繁殖をおさえやすくなっているためと予想される。 A part of the antibacterial antifungal agent in the urine of water-absorbing polymer has absorbed since the antibacterial antifungal agent and water-absorbing polymer contained in the non-woven fabric covering the water-absorbing polymer are close is eluted by embossing it is expected that because it is easy to suppress the growth of fungi. 又、吸着剤は、初期の臭いを吸着するほかに一部の抗菌防黴剤と接触していない尿中で菌類の繁殖により臭いの有るガスが発生した場合に吸着する効果が有ると予想される。 Also, the adsorbent can be expected the effect of adsorption when there odor gas by breeding fungi in urine that is not in contact with a portion of the antibacterial antifungal agent in addition to adsorb initial odor occurs there that. 特に犬等のペットに使用した場合には脱臭性に対する効果は良好である。 In particular effect on the deodorizing properties when used in pet such as a dog it is good.
特に含窒素複素環か硫黄原子を含有する有機化合物の金属塩である抗菌防黴剤を含有した繊維状物質を使用した場合や抗菌防黴剤と水不溶性高分子化合物との組成物を含有した不織布を使用した場合は抗菌性、脱臭性に効果が大きい。 Particularly contained composition and when using a fibrous material containing an antibacterial antifungal agent is a metal salt of an organic compound or an antibacterial antifungal agent and a water-insoluble polymer containing a nitrogen-containing heterocyclic ring or a sulfur atom antimicrobial when using the nonwoven fabric properties, the effect is large deodorizing. また、本発明において、抗菌防黴剤を含有して最も効果的に機能を発揮する繊維状物質は、セルロース系繊維の部分変性物がカルボキシメチル変性されたものである。 Further, in the present invention, fibrous material which exhibits works best contain an antibacterial antifungal agent are those partially denatured products of the cellulosic fibers are carboxymethyl-modified. このような繊維状物質よりなるパルプを用いると、パルプを構成するセルロース繊維中に高密度で充填できるので、極めて抗菌防黴剤含有量の高いパルプが得られ、優れた効果を発揮する。 With the pulp made from such fibrous materials, it is possible to fill a high density cellulosic fibers constituting the pulp obtained extremely high antibacterial antifungal agent content pulp, exhibits an excellent effect. 金属塩として銀、銅、 Silver as a metal salt, copper,
亜鉛塩を組み合わせて使用すると、連続して長期に抗菌性や防黴性効果等を発揮する。 When used in combination with zinc salts, long to exert antibacterial and antifungal effects, etc. in succession. その理由は、各金属塩は水溶解度が異なるのでそれらの組み合わせで連続して効果を発揮できる為と予想される。 The reason is that each metal salt is expected for water solubility can be exhibited an effect in succession a combination thereof is different. 抗菌防黴剤と水不溶性高分子化合物よりなる抗菌防黴剤組成物の場合は耐久性をそれらの重量比や種類により好ましく設計することができる。 If antibacterial antifungal agent and an antibacterial antifungal agent composition comprising water-insoluble polymeric compound can be preferably designed by a weight ratio and types durability.

Claims (9)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 抗菌防黴剤と吸着剤を含有する少なくとも2枚の不織布の間に吸水性ポリマーを熱エンボス加工により封入したシートを液体透過性のシートと液体不透過性のシートとの間に入れ、少なくとも両端部の全面ヒートシール加工により一体化したものであり、水中へ溶出する成分により抗菌防黴性が発現することを特徴とする脱臭抗菌シート。 [Claim 1] between the antimicrobial antifungal agent and at least two non-woven fabrics sheets water-absorbing polymeric sheets sealed by heat embossing the liquid-permeable sheet and a liquid impermeable between containing adsorbent put, is obtained by integrating the entire surface by heat sealing process at least two ends, deodorant antimicrobial sheet, characterized in that the antibacterial antifungal properties are expressed by components eluted into water.
  2. 【請求項2】 抗菌防黴剤が有機化合物の金属塩であることを特徴とする請求項1記載の脱臭抗菌シート。 2. A deodorizing antibacterial sheet according to claim 1, wherein the antibacterial antifungal agent characterized in that it is a metal salt of an organic compound.
  3. 【請求項3】 有機化合物が、ベンズイミダゾール化合物、メルカプトピリジン−N−オキシド化合物、イソチアゾリン化合物、ベンゾチアゾール化合物もしくはベンゾチアゾリン化合物から選ばれる少なくとも1種の化合物である請求項2記載の脱臭抗菌シート。 Wherein the organic compound is a benzimidazole compound, mercaptopyridine--N- oxide compounds, isothiazoline compounds, deodorant antimicrobial sheet of claim 2, wherein at least one compound selected from benzothiazole compounds or benzothiazoline compounds.
  4. 【請求項4】 金属塩が銀塩、銅塩、亜鉛塩の少なくとも1種を含有することを特徴とする請求項2記載の脱臭抗菌シート。 4. A deodorizing antibacterial sheet according to claim 2, wherein the metal salt is characterized silver salts, copper, that contains at least one zinc salt.
  5. 【請求項5】 吸着剤がゼオライト系化合物であることを特徴とする請求項1記載の脱臭抗菌シート。 5. A deodorizing antibacterial sheet according to claim 1, wherein the adsorbent is a zeolite-based compound.
  6. 【請求項6】 不織布が、有機化合物の金属塩よりなる抗菌防黴剤を含有する繊維状物質を含むことを特徴とする請求項1記載の脱臭抗菌シート。 6. A non-woven fabric, the deodorizing antibacterial sheet according to claim 1, characterized in that it comprises a fibrous material containing an antibacterial antifungal agent of a metal salt of an organic compound.
  7. 【請求項7】 不織布が湿式不織布であることを特徴とする請求項6記載の脱臭抗菌シート。 Deodorant antimicrobial sheet of claim 6, wherein 7. A nonwoven fabric characterized in that it is a wet-laid nonwoven fabric.
  8. 【請求項8】 脱臭抗菌シートが、人の介護用シートとして使用されることを特徴とする請求項1〜7のいずれか1項に記載の脱臭抗菌シート。 8. A deodorizing antibacterial sheet, deodorant antimicrobial sheet according to any one of claims 1 to 7, characterized in that it is used as a care sheet for human.
  9. 【請求項9】 脱臭抗菌シートが、動物用シートとして使用されることを特徴とする請求項1〜7のいずれか1 9. deodorizing antibacterial sheet, any of claims 1 to 7, characterized in that it is used as an animal sheet 1
    項に記載の脱臭抗菌シート。 Deodorant antibacterial sheet according to the item.
JP11234830A 1999-08-23 1999-08-23 Deodorizing antibacterial sheet Pending JP2001057931A (en)