JP2000318015A - Recovered pet bottle crushed matter and extrusion molding of pet pipe using pet resin as raw material - Google Patents

Abstract

PROBLEM TO BE SOLVED: To produce a PET pipe make of mainly recovered PET bottle crushed matter and has excellent physical properties, which has been difficult to produce heretofore, for the purpose of improving the recycle ratio of recovered PET bottles to a large extent. SOLUTION: A lubricant having an ester bond is added to a PET resin based on recovered PET bottle crushed matter and this PET resin is molded into a PET pipe by using a single screw or twin-screw extruder having a screw structure wherein a ratio in the number of threads of [supply zone]:[compression zone]: [metering zone] of a screw is [30-40]:[1]:[1-15].

Description

DETAILED DESCRIPTION OF THE INVENTION

[0001]

[0001] The present invention relates to an extrudable resin composition obtained by using a recovered PET bottle (component, polyethylene terephthalate resin) and a pet resin (polyethylene terephthalate resin) as a raw material and adding an ester lubricant specified in the present invention. The present invention relates to a method for extruding a pet pipe having an excellent appearance and excellent appearance.

[0002]

2. Description of the Related Art PET fibers and PET films with improved crystallization and mechanical strength by stretch orientation are the main axes of the market, and the market is constituted by the use of PET bottles by stretch blow molding. ing.

[0003] These processing methods all use a crystallinity of a pet resin to achieve an improvement in strength by stretching orientation. Behind the development of the processing methods by these stretching methods, pipes that do not use stretching are used. Extrusion molding has been hindered by the difficulty of extrusion technology, and has not been developed at all.

[0004] In Japan, the “Act on the Separation and Collection of Containers and Packaging and the Promotion of Recycling” was fully enforced in April 2000, but at the present time (April 1999) a huge amount of plastic bottles are recycled. Amount (1998: Japan 50
10,000 tons, 1.5 million tons in North America, more than 3.5 million tons worldwide)
With regard to material recycling, there has been no development of promising new processing technologies other than fibers, films and blow molding by conventional drawing techniques.

[0005]

SUMMARY OF THE INVENTION It is an object of the present invention to improve the current state of the recycling of plastic bottles as described above, and to propose a method for effectively utilizing a larger amount of collected PET bottles. Specifically, an object of the present invention is to provide a method for extruding a PET resin pipe having an excellent appearance using a collected PET bottle as a main material, which has been considered difficult in the prior art.

[0006]

Means for Solving the Problems The present inventor has conducted intensive studies in view of the above-mentioned problems, and as a result, it has been found that a 100: 0 weight ratio to a 60:40 weight ratio of a crushed material of a collected PET bottle and a pet resin is used alone or in combination. When the mixture is extruded into a pipe, a single-screw or twin-screw extruder having a screw structure specified in the present invention is used, and the extrudability is significantly improved by adding an ester lubricant specified in the present invention. The present inventors have found that it is possible to extrude a pet pipe having an excellent appearance and completed the present invention. That is, the present invention relates to a method for collecting 100 to 60 pulverized collected PET bottles.
Parts by weight and 0 to 40 parts by weight of a polyethylene terephthalate resin, an ester of an aliphatic monohydric alcohol having 4 to 50 carbon atoms and an aliphatic fatty acid having 4 to 50 carbon atoms, a polyhydric alcohol and 4 to 50 carbon atoms A composition comprising 0.001 to 15 parts by weight of a lubricant having an ester bond selected from the group consisting of an ester with an aliphatic fatty acid and a mixture of two or more thereof is supplied to the screw with a [feed zone]: [compression zone]. : The ratio of the number of peaks in the [quantification zone] is [3 to 40]: [1]: [1 to 1]
5] is a method for extruding a pet pipe having an excellent appearance by using a single-screw or twin-screw extruder having a screw structure, which has remarkably improved extrudability.

[0007]

BEST MODE FOR CARRYING OUT THE INVENTION In the present invention, a single or blend of 100 to 60 parts by weight of a crushed and dried recovered PET bottle and 0 to 40 parts by weight of a polyethylene terephthalate resin is used as a raw material. The general structure of PET resin (polyethylene terephthalate resin) is given by the following general formula

[0008]

Embedded image

As shown in the above, it is a polymer having an ester bond.

However, since it is an ester bond, the water content and the 270 ° C.
There is a disadvantage that hydrolysis and thermal decomposition rapidly proceed due to a high processing temperature of before and after and the molecular weight is reduced. Therefore, in addition to the above general formula, there is also a considerable structure in which an ester bond is hydrolyzed to have a terminal carboxylic acid group of -COOH. In particular, it is generally known that the presence of a terminal structure of —COOH in a resin impairs lubricity with a metal in an extruder.

Moreover, the grade of the PET resin used for molding the PET bottle has an intrinsic viscosity IV value of 0.7 to 0.7.
It is a low molecular weight grade of 0.8. A crushed product of a plastic bottle molded with this resin is extruded at a high temperature of 260 to 270 ° C., and the molecular weight is further reduced by thermal decomposition and hydrolysis.

Accordingly, in the region of the melting zone in the extruder, the pet resin having a lower molecular weight fraction and a lower melt viscosity easily causes a back pressure flow or a leakage flow in the direction opposite to the propulsion flow in the extrusion direction. Then, a surging phenomenon appears and the extrusion flow fluctuates, so that the outer diameter and the inner diameter of the pipe periodically change. Furthermore, these unusual abnormal flows generate flow marks on the pipe surface, resulting in poor appearance.

On the other hand, in the extrusion molding of the collected PET bottle pulverized material and PET resin, a solid zone is formed from the hopper side.
The phase changes from the melting zone to the solid zone in the sizing die into three phases. The three phases drive the screw by the same motor that drives the screw to propel the pet resin. However, in the ordinary extrusion molding of PVC or polyethylene, the inside of the machine is the propulsion and transportation of only one solid phase, and the extrusion of pets is basically different from the extrusion of these resins. Is another cause of the surging phenomenon.

In order to solve these difficult technical problems, as the extruder, the compression zone of the screw is set to a very short crest compared to the feed zone so that the melting zone of the pet resin is moved in the direction of the tip die. It is necessary to have a special screw structure that can be displaced, which significantly narrows the pet's melting zone and significantly improves extrusion. Therefore, the first condition that the screw structure defined in the present invention is required. That is, in order to manufacture the target pet pipe in the present invention, the ratio of the number of peaks of the [supply zone]: [compression zone]: [measurement zone] of the screw of the extruder is [3 to 40]:
[1]: It is an essential condition that [1 to 15] is satisfied.

In the present invention, an ester-type lubricant is required in addition to the screw structure described above. Ester bond selected from the group consisting of an ester of an aliphatic monohydric alcohol and an aliphatic fatty acid having 4 to 50 carbon atoms, an ester of a polyhydric alcohol and an aliphatic fatty acid having 4 to 50 carbon atoms, and a mixture of two or more thereof 0.001 to 15 parts by weight of a lubricant having

Since the pet resin has an ester bond, an ester-type lubricant is required as a chemical condition showing compatibility, and the compatibility results in an increase in the apparent melt viscosity of the pet resin. On the other hand, C4 ~
Fragments of C50 long chain alkyl groups enhance the sliding effect, especially on the solid phase portion of the sizing die. The three phases of solid → melt → solid are promoted as described above for pets mainly composed of crushed collected PET bottles, but sizing that rapidly solidifies from the low viscosity melt in the solution area of the die of the extruder die In the die area, because of the still high temperature solid zone, the lubricity of the solid pet inside the long sizing die is very closely related to the extrudability. The lubricity of the high temperature solid pet of the sizing die is an important factor influencing the extrudability of the pet pipe. For this purpose, a long-chain alkyl group is required in the structure of the lubricant. The fatty acid constituting the ester type lubricant used in the present invention needs to have a C4 to C50 alkyl group fragment, and for example, an animal or plant-derived fat or oil such as butyric acid, lauric acid, stearic acid, or lignoceric acid, or an ester wax. Other than those existing in the above, those obtained by chemical synthesis can also be used. A single one or a mixture of two or more thereof can be used.

The alcohol constituting the ester type lubricant used in the present invention may be a C4-C50 monovalent alkyl alcohol, or ethanediol, propanediol, propanetriol, butanediol, trimethylolpropane, sorbitan. And polyhydric alcohols such as sorbitol, polyglycerol, polyethylene glycol, polypropylene glycol, pentaerythritol and dipentaerythritol. These alcohols can be used alone or in a mixture of two or more.

In the ester comprising these alcohols and C4 to C50 fatty acids, the esterification rate is 3
It needs to be 3% or more. Esterification rate of 33
%, The compatibility with the pet resin in the molten state is inferior, and the smooth transport of the pet resin in the melting zone cannot be obtained. Specific examples of the lubricant having the ester bond include stearyl stearate, myristyl lignoserate, sorbitan behenate, glycerin monostearate and the like. Further, the alcohol, polyhydric alcohol or aliphatic fatty acid constituting these esters does not exert an effect as a lubricant on the production of a pet pipe mainly composed of the recovered PET bottle of the present invention.

[0019]

The present invention will now be described by way of examples, which are not intended to limit the invention. Preparation of collected PET bottles Collected PET bottles are milled by Orient Co., Ltd. VMNT
It was pulverized at −50 to obtain a pulverized product having an average flake size of 5 to 7 mm and an apparent specific gravity of 0.36 g / ml. This crushed product,
The product was dried at 130 ° C. under a high vacuum for 5 hours and stored in a dry box to obtain a crushed PET bottle used in the next example.

Example 1 100 parts by weight of a collected PET bottle pulverized product and 2.8 parts by weight of stearyl stearate (Rikemar SL800 (manufactured by Riken Vitamin Co., Ltd., esterification ratio: about 94%)) as a lubricant were used in a small high-speed rotary mixer. Stir and mix for 30 minutes. Under the following conditions, a pipe having an outer diameter of 76 mm and an inner diameter of 66 mm was extruded. As a result, the resin pressure in the melting zone is 60 k
g / cm ² , extrudability was good, there was no surging phenomenon, the dimensions of the formed pipe were constant, no flow mark was observed, and a normal good appearance pet pipe could be produced. .

Extruder: A single screw having a shaft diameter of 40 mm. Screw structure: The ratio of the number of peaks of [feed zone]: [compression zone]: [measurement zone] is 20: 1: 10. L / D = 3
0. Motor power consumption 7.5kw. Screw rotation speed: 130 rpm. Extrusion temperature: cylinder temperature 270 ° C, extruder die temperature 270 ° C, sizing die temperature 180 ° C.

Example 2 80 parts by weight of recovered PET bottle pulverized product and PET resin [P
A500 (manufactured by Mitsubishi Rayon Co., Ltd .: IV value 0.76] 2
0 parts by weight and 3.4 parts by weight of a millisillignocerate [Kawawax L (G) (produced by Kawaken Fine Chemical Co., Ltd., esterification ratio: about 94%)] as a lubricant are mixed by stirring with a small high-speed rotary mixer for 30 minutes. did. Under the following conditions,
A pipe having a diameter of 41 mm and an inner diameter of 41 mm was extruded. As a result, the resin pressure in the melting zone was constant at 54 kg / cm ² , the extrudability was good, and there was no surging phenomenon.
The dimensions of the molded pipe were constant and no flow mark was observed, and a pet pipe having a normal good appearance could be produced.

Extruder: A screw having two shafts and a shaft diameter of 40 mm. Screw structure: The ratio of the number of peaks of [feed zone]: [compression zone]: [measurement zone] is 20: 1: 10. L / D = 3
0. Motor power consumption 7.5kw. Screw rotation speed: 110 rpm. Extrusion temperature: cylinder temperature 270 ° C, extruder die temperature 270 ° C, sizing die temperature 180 ° C.

Example 3 90 parts by weight of a collected PET bottle pulverized product and PET resin [P
A280 (manufactured by Mitsubishi Rayon Co., Ltd .: IV value 0.80] 1
0 parts by weight and 3.0 parts by weight of sorbitan tribehenate [Likemar B-150 (manufactured by Riken Vitamin Co., Ltd., esterification ratio: about 65%)] as a lubricant were mixed by stirring with a small high-speed rotary mixer for 30 minutes. This was carried out under the same conditions as in Example 1 with an outer diameter of 7 mm.
A 6 mm pipe having an inner diameter of 66 mm was extruded. As a result, the resin pressure in the melting zone was constant at 58 kg / cm ² , the extrudability was good, and there was no surging phenomenon.
The dimensions of the molded pipe were constant and no flow mark was observed, and a pet pipe having a normal good appearance could be produced.

Example 4 70 parts by weight of a collected PET bottle pulverized product and PET resin [P
A210 (manufactured by Mitsubishi Rayon Co., Ltd .: IV value 0.76] 3
0 parts by weight and 3.0 parts by weight of glycerin monostearate [Likemar S-100 (manufactured by Riken Vitamin Co., Ltd., esterification ratio: about 33%)] as a lubricant were mixed by stirring with a small high-speed rotary mixer for 30 minutes. A pipe having an outer diameter of 76 mm and an inner diameter of 66 mm was extruded under the same conditions as in Example 1. As a result, the resin pressure in the melting zone was constant at 63 kg / cm ² , the extrudability was good, there was no surging phenomenon, the dimensions of the molded pipe were constant, no flow mark was observed, and the ordinary good appearance Was able to manufacture a pet pipe.

Comparative Example 1 100 parts by weight of a collected PET bottle pulverized product and 3.0 parts by weight of diglycerin stearate [Likemar S-72 (manufactured by Riken Vitamin Co., Ltd., esterification ratio: about 40%)] as a lubricant were miniaturized at high speed. The mixture was stirred and mixed with a rotary mixer for 30 minutes. Under the following conditions, a pipe having an outer diameter of 76 mm and an inner diameter of 66 mm was extruded. As a result, (1) almost no extrudate was produced, (2) the resin pressure in the die portion of the extruder was constantly fluctuated as ²⁰ to 5 kg / cm ^2, and (3) even a small amount of extrudate was extremely surging, so that pipe molding was not possible. Extruder: A screw having a shaft diameter of 40 mm. Screw structure: The ratio of the peak number of [feed zone]: [compression zone]: [measurement zone] is 6: 13: 7 and an extruder for PVC is used. L / D = 30. Motor power consumption 7.5k
w. Screw rotation speed: 130 rpm. Extrusion temperature: cylinder temperature 270 ° C, extruder die temperature 270 ° C, sizing die temperature 180 ° C. This phenomenon is caused by the fact that the intrinsic viscosity IV value of the PET resin constituting the collected PET bottle is lowered, and the compression zone of the screw is long, so that the melting zone of the PET resin is long, and the flow of the extrudate becomes extremely unstable. It is thought that it became.

COMPARATIVE EXAMPLE 2 100 parts by weight of a collected PET bottle pulverized product and 3.0 parts by weight of stearyl alcohol [VLTN-6 (G) (manufactured by Kawaken Fine Chemicals Co., Ltd., esterification rate: 0%)] as a lubricant were miniaturized at a high speed. The mixture was stirred and mixed with a rotary mixer for 30 minutes. A pipe having an outer diameter of 76 mm and an inner diameter of 66 mm was extruded under the same conditions as in Example 1. As a result, the resin pressure at the die portion of the extruder greatly fluctuated to 70 to 5 kg / cm ² , the surging phenomenon was severe, flow marks were frequently generated on the pipe surface, and a normal pet pipe could not be manufactured. Stearyl alcohol has proven unsuitable as a lubricant.

Comparative Example 3 80 parts by weight of a crushed recovered PET bottle and PET resin [P
A280 (Mitsubishi Rayon Co., Ltd .: IV value 0.80] 2
3.3 parts of 0 parts by weight and purified stearic acid [F-3 (Kawaken Fine Chemical Co., Ltd., esterification rate 0%)] as a lubricant
Parts by weight and mixed with a small high-speed rotary mixer for 30 minutes. Under the same conditions as in Example 1, the outer diameter was 76 mm and the inner diameter was 66.
mm pipe was extruded. As a result, the resin pressure in the melting zone fluctuates greatly from 70 to 10 kg / cm ² ,
The extruded amount was extremely small, and a surging phenomenon and flow marks on the surface of the pipe were extremely frequent, so that extrusion of a pet pipe was impossible. Stearic acid has proven unsuitable as a lubricant.

[0029]

According to the present invention, it is possible to manufacture a PET pipe by using an extruder for a collected PET bottle, and it is possible to greatly improve the recycling rate of the PET bottle, and it is expected to greatly contribute to society.

 ──────────────────────────────────────────────────続 き Continued on the front page F term (reference) 4F207 AA24 AA50 AB07 AG08 AR15 KA01 KA17 KF01 KF02 KK12 KK13 KL01 KW45 4J002 CF06X CF061 CH05Y EH036 EH046 EH056 FD17Y GT00

Claims (3)

[Claims] 1. Collected PET bottle crushed product 100-60
Parts by weight and 0 to 40 parts by weight of a polyethylene terephthalate resin, an ester of an aliphatic monohydric alcohol having 4 to 50 carbon atoms and an aliphatic fatty acid having 4 to 50 carbon atoms, a polyhydric alcohol and 4 to 50 carbon atoms A composition comprising 0.001 to 15 parts by weight of a lubricant having an ester bond selected from the group consisting of an ester with an aliphatic fatty acid and a mixture of two or more thereof is supplied to the screw with a [feed zone]: [compression zone]. : The ratio of the number of peaks in the [quantification zone] is [3 to 40]: [1]: [1 to 1]
[5] A method for extruding a pet pipe, characterized by using a single-screw or twin-screw extruder having a screw structure according to [5]. 2. The polyhydric alcohol constituting the lubricant, which is an ester of a polyhydric alcohol and an aliphatic fatty acid having 4 to 50 carbon atoms, comprises ethanediol, propanediol, propanetriol, butanediol, trimethylolpropane, sorbitan, The pet pipe extrusion method according to claim 1, wherein the method is selected from the group consisting of sorbitol, polyglycerol, polyethylene glycol, polypropylene glycol, pentaerythritol, dipentaerythritol and a mixture of two or more thereof. 3. The fatty acid ester of a polyhydric alcohol having an esterification rate of 33 to a hydroxyl group of the polyhydric alcohol.
%. The method for extruding a pet pipe according to claim 1, wherein