JP2000238833A - Paper band for packing - Google Patents
Paper band for packingInfo
- Publication number
- JP2000238833A JP2000238833A JP4127499A JP4127499A JP2000238833A JP 2000238833 A JP2000238833 A JP 2000238833A JP 4127499 A JP4127499 A JP 4127499A JP 4127499 A JP4127499 A JP 4127499A JP 2000238833 A JP2000238833 A JP 2000238833A
- Authority
- JP
- Japan
- Prior art keywords
- paper band
- packing
- strength
- paper
- band
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【0001】[0001]
【産業上の利用分野】本発明は梱包用の紙バンドに関す
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a paper band for packing.
【0002】[0002]
【従来の技術】従来梱包用資材として使われている紙バ
ンドは、表面に部分ケン化のポリ・ビニ−ル・アルコ−
ル水溶液(主として切手の裏側などに使われており、一
般的に水糊と呼ばれている。)を使用しており、その糊
面に水又は水を含んだ液状のものを付けることによりバ
ンドの両端等を合わせる等して接着効果を出している。2. Description of the Related Art A paper band conventionally used as a packing material has a partially-saponified polyvinyl alcohol on the surface.
Water solution (mainly used on the back side of stamps and generally called water glue), and a band is formed by applying water or a liquid containing water to the glue surface. The bonding effect is obtained by, for example, matching the both ends of the device.
【0003】[0003]
【従来技術の欠点】この方法で過去において、自動接着
できる梱包機も出回っていたが、水の塗布が不正確であ
ったり、安定性がなかったり、又季節の変動(湿度や気
温の変化。)によって接着不良を起すなどの虞があり、
そのため現在では紙バンドによる梱包はすべて手作業で
行っており、効率的な作業ができない。Disadvantages of the prior art In the past, packing machines that could be automatically bonded by this method were also available, but the application of water was inaccurate, inconsistent, and seasonal (such as changes in humidity and temperature. ) May cause poor adhesion, etc.
Therefore, at present, all packing with paper bands is performed manually, and efficient work cannot be performed.
【0004】更に部分ケン化のポリ・ビニ−ル・アルコ
−ル水溶液(水糊)を使っているため水分の付着が紙バ
ンド同士のブロッキングを起し易く、作業に支障を来す
虞がある。又高温の状態で保存した場合、カビが発生し
やすくなるという欠点がある。Further, since a partially saponified polyvinyl alcohol aqueous solution (water glue) is used, adhesion of moisture tends to cause blocking between paper bands, which may hinder the operation. . Further, when stored in a high temperature state, there is a disadvantage that mold is easily generated.
【0005】このように従来の紙バンドは様々な問題を
抱えているため、梱包用のバンドはプラスチック製とな
り、熱によって接着する自動梱包機の開発と共に今日に
いたっている。As described above, since the conventional paper band has various problems, the band for packing is made of plastic, and has been developed today with the development of an automatic packing machine that adheres by heat.
【0006】然し乍らこのプラスチック製バンドの使用
後の廃棄処理は、有毒ガスの発生など多くの環境問題を
抱えており、又リサイクルができないなどの欠点があ
る。However, disposal of the plastic band after use has many environmental problems such as generation of toxic gas, and has drawbacks such as the inability to recycle.
【0007】[0007]
【発明が解決しようとする課題】そこで本発明は、リサ
イクルできる紙バンドを熱接着できるように加工し、即
ちプラスチック製バンド用の自動梱包機でも使える紙バ
ンドを提供し、且つリサイクルできるものを提供しよう
とするものである。SUMMARY OF THE INVENTION Accordingly, the present invention provides a paper band which is made of a recyclable paper band so as to be heat-bondable, that is, a paper band which can be used in an automatic packing machine for plastic bands and which can be recycled. What you want to do.
【0008】[0008]
【課題を解決するための手段】本発明は、紙バンド本体
の表面に、ポリ・ビニ−ル・アルコ−ル(以下PVAと
いう。)完全ケン化品(ケン化度90%以上。)5%〜
18%の接着溶液に対し、可塑剤としてのグリセリン又
はジ・グリセリン0.5%〜10%、塩化リチュ−ム
0.1%〜15%、ロ−ト油0.05%〜5%を混合し
た混合液を塗布したものである。According to the present invention, 5% of a completely saponified product (polyvinyl alcohol (hereinafter referred to as PVA)) (having a saponification degree of 90% or more) is provided on the surface of a paper band main body. ~
Glycerin or di-glycerin 0.5% to 10% as a plasticizer, 0.1% to 15% of lithium chloride, and 0.05% to 5% of lotus oil are mixed with an 18% adhesive solution. The mixed solution was applied.
【0009】[0009]
【実施例】本発明を実施例により詳記すると、紙縒状に
撚った紙の撚り紐を多数並設し接着剤により固定した紙
バンド本体の表面に、PVA完全ケン化品(ケン化度9
0%以上。)5%〜18%の接着溶液に対し、可塑剤・
グリセリン又はジ・グリセリン0.5%〜10%、塩化
リチュ−ム0.1%〜15%、ロ−ト油0.05%〜5
%を混合した混合液を塗布し、乾燥したものである。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described in more detail with reference to the following Examples. A number of twisted paper strands are arranged side by side and fixed on the surface of a paper band body with an adhesive. Degree 9
0% or more. ) 5% to 18% adhesive solution, plasticizer
Glycerin or diglycerin 0.5% to 10%, lithium chloride 0.1% to 15%, lotus oil 0.05% to 5
% Is applied and dried.
【0010】PVAのケン化度が90%より低い場合は
耐水性が低下し、梱包資材としては適しなく、ポリ・ビ
ニ−ル・アルコ−ル完全ケン化品(ケン化度90%以
上。)の添加量も5%未満では接着強度が落ち、又18
%を超えると生産性が悪くなり、又高粘度になるため塗
布作業に支障を来す虞がある。好ましくは8%乃至13
%である。範囲外の接着溶液の場合、可塑剤、塩化リチ
ュウム、ロ−ト油の添加量を調整しても接着不良となっ
たり、接着強度にバラツキが生じ、梱包資材として利用
することは困難性が生じる。When the degree of saponification of PVA is lower than 90%, the water resistance is lowered and it is not suitable as a packing material, and it is completely saponified with polyvinyl alcohol (90% or more saponification degree). If the addition amount is less than 5%, the adhesive strength is lowered, and
%, Productivity may deteriorate, and the viscosity may become high, which may hinder the coating operation. Preferably 8% to 13
%. In the case of an adhesive solution out of the range, even if the added amount of the plasticizer, lithium chloride, and roto oil is adjusted, poor adhesion or variation in adhesive strength occurs, making it difficult to use as a packing material. .
【0011】紙バンド本体の形状としては、紙の撚り紐
を多数並設し接着したもののほか、長尺紙を折り畳み接
着したものとか、紙芯を紙で包んで接着したものなど何
れでも良い。As the shape of the paper band main body, any of a number of twisted paper strings arranged side by side and bonded, a type obtained by folding and bonding long paper, or a type obtained by bonding a paper core wrapped with paper may be used.
【0012】可塑剤、例えばグリセリン又はジ・グリセ
リン0.5%〜10%の混合目的は、紙バンドが製品と
なった後も保湿効果を持たせ、ヒ−トシ−ルの際の接着
強度を高めるものである。0.5%未満では接着強度は
弱くなり、又15%を超えると強度的に弱くなり、同時
に紙バンドに張りがなくなる為機械適正が悪くなる。好
ましくは1%〜7%である。The purpose of mixing a plasticizer, for example, glycerin or diglycerin 0.5% to 10%, is to provide a moisturizing effect even after the paper band becomes a product, and to improve the adhesive strength in heat sealing. To enhance. If it is less than 0.5%, the adhesive strength will be weak, and if it exceeds 15%, the strength will be weak. Preferably it is 1% to 7%.
【0013】可塑剤は、高沸点、水溶性の、水酸基、ア
ミノ基、アミド基を有する化合物、例えばグリセリン、
エチレングリコ−ル、トリエチレングリコ−ル、エタノ
−ルアミン、エタノ−ルアセトアミド、尿素等が有効で
ある。これら可塑剤の添加量も0.5%〜10%の範囲
内である。The plasticizer is a compound having a high boiling point and water solubility, having a hydroxyl group, an amino group or an amide group, for example, glycerin,
Ethylene glycol, triethylene glycol, ethanolamine, ethanolacetamide, urea and the like are effective. The addition amount of these plasticizers is also in the range of 0.5% to 10%.
【0014】塩化リチュ−ム0.1%〜15%の混合目
的は、接着強度であるが、0.1%未満の添加量では強
度増大の変化を認められず、又15%を超えると好まし
い結果は得られない。好ましい分量は0.5%から5%
である。The purpose of mixing 0.1% to 15% of chlorinated lithium is adhesive strength. However, if the amount is less than 0.1%, no change in strength is observed, and if it exceeds 15%, it is preferable. No result is obtained. The preferred amount is 0.5% to 5%
It is.
【0015】ロ−ト油(ひまし油スルホン酸ナトリウ
ム、通常47%溶液となっている。)はコ−ティング又
は潤滑性、平滑性を向上させ、また熱効率を高める効果
があり、0.05%未満の添加量では潤滑性等の効果は
認められず、又5%を超えると逆に接着強度が衰えるよ
うになり好ましくない。好ましくは0.5%から3%で
ある。Lot oil (castor oil sodium sulfonate, usually in a 47% solution) has the effect of improving coating or lubricity, smoothness and heat efficiency, and is less than 0.05%. No effect such as lubricity is recognized with the addition amount of, and when it exceeds 5%, the adhesive strength is undesirably deteriorated. Preferably it is 0.5% to 3%.
【0016】又必要に応じ消泡剤(ポリオキシアルキレ
ングリコ−ル誘導体を主成分とした。)を、前記の接着
溶液に対し、0.01%から5%の範囲内で混ぜる。こ
れにより工程中に発生しやすい泡を防ぎ、紙バンド本体
に斑のない塗布作業ができ、接着強度にもバラ付きがな
くなる。0.01%未満では消泡効果が得られず、又5
%を超えると消泡効果は得られるが製品に支障を来す虞
がある。好ましくは0.3%から3%である。If necessary, an antifoaming agent (containing a polyoxyalkylene glycol derivative as a main component) is mixed with the above-mentioned adhesive solution in a range of 0.01% to 5%. This prevents bubbles that are likely to be generated during the process, makes it possible to perform a coating operation without unevenness on the paper band main body, and eliminates a variation in adhesive strength. If it is less than 0.01%, no defoaming effect can be obtained, and
%, The defoaming effect can be obtained, but there is a possibility that the product will be hindered. Preferably it is 0.3% to 3%.
【0017】以上の実施例に基づいた接着強度検査の結
果は表1〜3のとおりである。接着機械はプラスチック
製バンドを接着する自動梱包機を使用する。Tables 1 to 3 show the results of the adhesive strength test based on the above examples. The bonding machine uses an automatic packing machine that bonds plastic bands.
【0018】[0018]
【表1】 その結果、臨海値の(2)(5)の試験例の強度検査は
梱包有効接着強度の限界値(60kg±3)であり、
(3)(4)では強度も増し、梱包に耐えうる強度であ
った。因に母材(紙バンド本体)自体の破断強度は80
kg(12m巾)以上である。(2)(5)の試験例の
混合液成分量の範囲内の試験例では何れも梱包有効接着
強度以上(70kg以上)であった。[Table 1] As a result, the strength test of the test examples of the critical values (2) and (5) is the limit value (60 kg ± 3) of the effective bonding strength of the packing,
In (3) and (4), the strength was increased, and the strength was high enough to withstand packing. The breaking strength of the base material (paper band body) itself is 80
kg (12 m width) or more. (2) In each of the test examples within the range of the mixed liquid component amount in the test example of (5), the packing adhesive strength was not less than 70 kg (70 kg or more).
【0019】[0019]
【表2】 その結果(1)では充分な接着強度は得られず、臨海値
の(2)(5)の試験例の強度検査は梱包有効接着強度
の限界値(60kg±3)であり、(3)(4)では更
に強度も増し、梱包に耐えうる強度であった。因に母材
(紙バンド本体)自体の破断強度は80kg以上であ
る。(2)(5)の試験例の混合液成分量の中間の範囲
内の試験例では何れも梱包有効接着強度以上(71kg
以上)であった。[Table 2] As a result, sufficient adhesive strength was not obtained with (1), and the strength test of the test examples of the critical values (2) and (5) was the limit value (60 kg ± 3) of the effective adhesive strength for packaging, and (3) ( In 4), the strength was further increased, and the strength was high enough to withstand packing. Incidentally, the breaking strength of the base material (paper band body) itself is 80 kg or more. (2) In the test examples in the middle range of the mixed liquid component amount of the test examples in (5), all of the test pieces are equal to or more than the packaging effective adhesive strength (71 kg).
Above).
【0020】[0020]
【表3】 その結果(1)では充分な接着強度は得られず、臨海値
の(2)(5)の試験例の強度検査は梱包有効接着強度
の限界値(60kg±3)であり、(3)(4)では強
度も増し、梱包に耐えうる強度であった。因に母材(紙
バンド本体)自体の破断強度は80kg以上である。
(2)(5)の試験例の混合液成分量の中間の範囲内の
試験例では何れも梱包有効接着強度の範囲内(60±3
kg以上)であった。[Table 3] As a result, sufficient adhesive strength was not obtained with (1), and the strength test of the test examples of the critical values (2) and (5) was the limit value (60 kg ± 3) of the effective adhesive strength for packaging, and (3) ( In 4), the strength was increased, and the strength was high enough to withstand packing. Incidentally, the breaking strength of the base material (paper band body) itself is 80 kg or more.
(2) In the test examples in the middle range of the mixed liquid component amount in the test example of (5), all of the test examples fall within the range of the packaging effective adhesive strength (60 ± 3
kg or more).
【0021】[0021]
【効果】以上の結果、ポリ・ビニ−ル・アルコ−ル完全
ケン化品(ケン化度90%以上。)5%〜18%の接着
溶液単独では目的とする接着強度又は安定した接着強度
を得るのは困難であるが、可塑剤0.5%〜10%、塩
化リチュ−ム0.1%〜15%、ロ−ト油0.05%〜
5%を混合した混合液を紙バンド本体に塗布することに
より、これら成分の相乗効果により梱包有効接着強度以
上の強度が安定して得られる。[Effects] As a result, a completely saponified product of polyvinyl alcohol (a saponification degree of 90% or more) with 5% to 18% of an adhesive solution alone can achieve the intended adhesive strength or stable adhesive strength. It is difficult to obtain, but 0.5% to 10% of plasticizer, 0.1% to 15% of lithium chloride, 0.05% of lotus oil
By applying a mixed solution containing 5% to the paper band body, a strength equal to or higher than the packaging effective adhesive strength can be stably obtained due to a synergistic effect of these components.
【0022】また5%〜18%接着溶液に対し、消泡剤
を0.01%から5%の範囲内で混合した混合液を塗布
することにより、工程中に発生しやすい泡を防ぎ、紙バ
ンド本体に混合液の斑のない塗布作業ができ、接着強度
にもよりバラ付きのなくなることが認められた。Further, by applying a mixed solution in which an antifoaming agent is mixed in a range of 0.01% to 5% with respect to a 5% to 18% adhesive solution, bubbles which are easily generated during the process can be prevented, and It was confirmed that the coating operation could be performed without unevenness of the mixed solution on the band main body, and that the adhesive strength became more uniform.
【0023】又吸湿性が少なく紙バンド同士のブロッキ
ングなくなって紙バンドの品質を高めるばかりか、安定
した強度のまま保存等ができる。In addition, since the paper bands have low hygroscopicity and do not block each other, the quality of the paper bands can be improved, and the paper bands can be stored with stable strength.
【0024】紙バンド表面はコ−ティングされるため耐
水効果が得られ、又紙バンド自体の「腰」が強くなり、
自動梱包機によって梱包する際のレ−ルへの挿通がスム
−ズになり、円滑な作業ができる。Since the surface of the paper band is coated, a water-resistant effect is obtained, and the "stiffness" of the paper band itself becomes strong.
Insertion into the rail when packing by an automatic packing machine is smooth, and smooth work can be performed.
【0025】更に最大の特徴としては使用後の紙バンド
はリサイクルができ、環境問題を考えた場合に有効的な
梱包材料といえる。The most significant feature is that the used paper band can be recycled and is an effective packing material in consideration of environmental problems.
Claims (2)
・アルコ−ル完全ケン化品(ケン化度90%以上。)5
%〜18%の接着溶液に対し、可塑剤0.5%〜10
%、塩化リチュ−ム0.1%〜15%、ロ−ト油0.0
5%〜5%を混合した混合液を塗布し、乾燥させた梱包
用紙バンド。1. A completely saponified product of polyvinyl alcohol (a saponification degree of 90% or more) on the surface of a paper band main body.
% To 18% adhesive solution, plasticizer 0.5% to 10%
%, 0.1% to 15% chloride chloride, 0.0
A packing paper band coated with a mixed solution of 5% to 5% and dried.
・アルコ−ル完全ケン化品(ケン化度90%以上。)5
%〜18%の接着溶液に対し、可塑剤0.5%〜10
%、塩化リチュ−ム0.1%〜15%、ロ−ト油0.0
5%〜5%、消泡剤防0.01%〜5%を混合した混合
液を塗布し、乾燥させた梱包用紙バンド。2. A completely saponified product of polyvinyl alcohol (a saponification degree of 90% or more) on the surface of the paper band main body.
% To 18% adhesive solution, plasticizer 0.5% to 10%
%, 0.1% to 15% chloride chloride, 0.0
A packing paper band coated with a mixed solution of 5% to 5% and 0.01% to 5% of antifoaming agent and dried.