JP2000169917A - Tourmaline-containing noble metal alloy - Google Patents
Tourmaline-containing noble metal alloyInfo
- Publication number
- JP2000169917A JP2000169917A JP10343695A JP34369598A JP2000169917A JP 2000169917 A JP2000169917 A JP 2000169917A JP 10343695 A JP10343695 A JP 10343695A JP 34369598 A JP34369598 A JP 34369598A JP 2000169917 A JP2000169917 A JP 2000169917A
- Authority
- JP
- Japan
- Prior art keywords
- noble metal
- tourmaline
- silver
- platinum
- gold
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】この発明は、指輪やブロー
チ、ペンダント、ネックレス等の装身具として使用した
ときに、電磁波障害を防止することができる装身具用の
トルマリン含有貴金属合金を提供しようとするものであ
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention aims to provide a tourmaline-containing noble metal alloy for accessories that can prevent electromagnetic interference when used as accessories such as rings, brooches, pendants and necklaces. .
【０００２】[0002]
【従来の技術】従来、金、銀、またはプラチナのいずれ
かを主成分とする貴金属合金は、指輪やブローチ、ペン
ダント、ネックレス等の装身具の用途に貴重な素材とし
て広く使用されてきている。そして、用途やそのデザイ
ン、そこで必要とする色合い等を勘案して、金、銀、ま
たはプラチナのいずれかを主成分とする貴金属合金が適
宜採用されている。2. Description of the Related Art Conventionally, noble metal alloys containing gold, silver, or platinum as a main component have been widely used as valuable materials for accessories such as rings, brooches, pendants, and necklaces. A noble metal alloy containing gold, silver, or platinum as a main component is appropriately used in consideration of the application, its design, and the color required for the application.
【０００３】他方、トルマリンは電気石とも言われ、電
気磁気的作用を備えているとされている。それゆえ近
年、携帯電話やページャ、パソコンのモニタ等から発生
する電磁波による障害を防止するため、それらの機器類
に飾りとして装着することにより使用されている。[0003] On the other hand, tourmaline is also called tourmaline and is said to have an electromagnetic effect. Therefore, in recent years, in order to prevent interference due to electromagnetic waves generated from a mobile phone, a pager, a monitor of a personal computer, and the like, it is used by being attached to such devices as a decoration.
【０００４】[0004]
【発明が解決しようとする課題】ところで従来の金や
銀、プラチナのいずれかを主成分とする貴金属合金を用
いた装身具においては、その適所に磁石を配置あるいは
内蔵させ、その磁気作用によって血行促進や体質改善等
の健康増進を図るようにしたものが知られている。これ
と軌を一にする発想が、携帯電話やページャ、パソコン
のモニタ等から発生する電磁波障害を防止するため、そ
れらの機器類に飾りとしてトルマリンを装着することで
あるといい得る。In a conventional accessory using a noble metal alloy containing gold, silver, or platinum as a main component, a magnet is arranged or incorporated in an appropriate position, and the blood flow is promoted by the magnetic action. And health promotion such as improvement of physical constitution are known. It can be said that the idea to make it the same gauge is to attach tourmaline as a decoration to those devices in order to prevent electromagnetic interference from mobile phones, pagers, personal computer monitors, and the like.
【０００５】しかしながらトルマリン自体は、貴石とし
て認められてはいるが宝石としてはさほどの価値を備え
ているものではない。したがって、貴金属合金を用いた
装身具にトルマリンを配置しても、装身具としての付加
価値が高まることはほとんど考えられない。[0005] Although tourmaline itself is recognized as a precious stone, it is not of great value as a gem. Therefore, even if tourmaline is arranged in a jewelry using a noble metal alloy, it is hardly conceivable that the added value of the jewelry will increase.
【０００６】この発明は、従来例の上記欠点を解消しよ
うとして鋭意研究した結果、金、銀、またはプラチナの
いずれかを主成分とする貴金属素材にトルマリン成分を
含有させることにより、トルマリンの電気磁気的作用が
活用できるとともに、上記貴金属素材自体の価値を減じ
ることなく装身具として利用できるトルマリン含有貴金
属合金を提供しようとするものである。The present invention has been intensively studied to solve the above-mentioned drawbacks of the prior art, and as a result, the tourmaline electromagnetism is obtained by adding a tourmaline component to a noble metal material mainly composed of gold, silver or platinum. It is an object of the present invention to provide a tourmaline-containing noble metal alloy that can be used as an accessory without reducing the value of the above-mentioned noble metal material itself, while utilizing the natural action.
【０００７】[0007]
【課題を解決するための手段】すなわちこの発明のトル
マリン含有貴金属合金は、金、銀、またはプラチナのい
ずれかを主成分とする貴金属素材に、トルマリン粉末を
０．１重量％〜５０重量％添加したことを特徴とするも
のである。That is, the tourmaline-containing noble metal alloy of the present invention comprises 0.1% to 50% by weight of a tourmaline powder added to a noble metal material mainly composed of gold, silver or platinum. It is characterized by having done.
【０００８】またこの発明のトルマリン含有貴金属合金
は、金、銀、またはプラチナのいずれかを主成分とする
貴金属素材に、トルマリン粉末を０．１重量％〜１０重
量％添加したことを特徴とするものである。The tourmaline-containing noble metal alloy according to the present invention is characterized in that tourmaline powder is added in an amount of 0.1% by weight to 10% by weight to a noble metal material mainly containing gold, silver or platinum. Things.
【０００９】さらにこの発明のトルマリン含有貴金属合
金は、金、銀、またはプラチナのいずれかを主成分とす
る貴金属素材に、トルマリン粉末を添加したトルマリン
含有貴金属合金層と、他の貴金属層とを積層したことを
も特徴とするものである。Further, the tourmaline-containing noble metal alloy of the present invention is a laminate of a tourmaline-containing noble metal alloy layer obtained by adding tourmaline powder to a noble metal material mainly containing gold, silver, or platinum, and another noble metal layer. It is also characterized by having done.
【００１０】この発明を以上のように構成する理由は、
トルマリン含有貴金属合金に占めるトルマリンの成分量
を５０重量％以上とすると、鋳造して得た貴金属製装身
具が脆くなって耐久性がなくなってしまうからであり、
０．１重量％〜１０重量％、特に３重量％〜６重量％が
好適であった。The reason for configuring the present invention as described above is as follows.
If the amount of tourmaline contained in the tourmaline-containing noble metal alloy is 50% by weight or more, the noble metal jewelry obtained by casting becomes brittle and loses durability.
0.1% to 10% by weight, especially 3% to 6% by weight, was suitable.
【００１１】もちろん、０．１重量％〜１０重量％、特
に３重量％〜６重量％であっても、トルマリンの上記電
気磁気的作用が損なわれることはなく、得た貴金属装身
具も電気磁気的作用を有するものであった。Of course, even if the amount is 0.1% by weight to 10% by weight, especially 3% by weight to 6% by weight, the above-mentioned electro-magnetic action of tourmaline is not impaired, and the noble metal accessory obtained is also electro-magnetic. It had an effect.
【００１２】この発明はトルマリンの成分量を以上のよ
うに構成したので、長年使用しても電気磁気的作用が損
なわれることはなく、しかも装身具用合金として有用な
トルマリン含有貴金属合金を提供することができるよう
になった。The present invention provides a tourmaline-containing noble metal alloy which does not impair the electromagnetism even when used for many years and which is useful as an alloy for accessories because the tourmaline component is constituted as described above. Is now available.
【００１３】[0013]
【発明の実施の形態】以下この発明のトルマリン含有貴
金属合金の実施の形態を、実施例を用いて詳細に説明す
る。DESCRIPTION OF THE PREFERRED EMBODIMENTS Embodiments of the tourmaline-containing noble metal alloy of the present invention will be described below in detail with reference to examples.
【００１４】[0014]
【実施例１】Ａｕを７５重量％、ＣｕおよびＡｇをそれ
ぞれ１２重量％含み、ＰｄやＺｎを少量添加して溶融撹
拌して溶融金合金を作製した。他方、トルマリンを細か
く粉砕した上ふるいで選別し、得た平均粒子径０．１μ
ｍ〜１００μｍであるトルマリン粉末を溶融金合金９５
重量％に対し、５重量％となるよう投入した。Example 1 A molten gold alloy was prepared by containing 75% by weight of Au, 12% by weight of Cu and Ag, respectively, adding a small amount of Pd or Zn and melting and stirring. On the other hand, tourmaline was finely pulverized and selected with a sieve to obtain an average particle diameter of 0.1 μm.
tourmaline powder having a diameter of 100 to 100 μm and a molten gold alloy 95
It was introduced so as to be 5% by weight with respect to% by weight.
【００１５】得た金合金は、色調と明るさ、変色度合い
ともトルマリン粉末を添加しなかったものとほとんど遜
色ないものであった。なお、変色度合いの判定試験は、
表面研磨した試料を０．１重量％のＮａ2Ｓおよび５重
量％のＮａＣｌ水溶液に１０時間浸漬して行なった。The obtained gold alloy was almost inferior in color tone, brightness, and degree of discoloration to that in which no tourmaline powder was added. The test for determining the degree of discoloration is as follows.
The surface-polished sample was immersed in an aqueous solution of 0.1% by weight of Na 2 S and 5% by weight of NaCl for 10 hours.
【００１６】[0016]
【実施例２】Ａｇを８５重量％、ＡｕおよびＰｄをそれ
ぞれ５重量％含み、ＣｕやＩｎ、Ｚｎを少量添加して溶
融撹拌して溶融銀合金を作製した。他方、トルマリンを
細かく粉砕した上ふるいで選別し、得た平均粒子径０．
１μｍ〜１００μｍであるトルマリン粉末を溶融銀合金
９２重量％に対し、８重量％となるよう投入した。Example 2 A molten silver alloy was prepared by containing 85% by weight of Ag and 5% by weight of each of Au and Pd, adding a small amount of Cu, In, or Zn and melting and stirring. On the other hand, tourmaline was finely pulverized and screened with a sieve to obtain an average particle diameter of 0.1.
Tourmaline powder having a size of 1 μm to 100 μm was added so as to be 8% by weight based on 92% by weight of the molten silver alloy.
【００１７】得た銀合金は、色調と明るさ、変色度合い
ともトルマリン粉末を添加しなかったものとほとんど遜
色ないものであった。The obtained silver alloy was almost inferior in color tone, brightness, and degree of discoloration to that in which no tourmaline powder was added.
【００１８】[0018]
【実施例３】Ｐｔを９０重量％、ＣｕおよびＧａをそれ
ぞれ５重量％含み、Ｐｄを少量添加して溶融撹拌して溶
融プラチナ合金を作製した。他方、トルマリンを細かく
粉砕した上ふるいで選別し、得た平均粒子径０．１μｍ
〜１００μｍであるトルマリン粉末を溶融銀合金９７重
量％に対し、３重量％となるよう投入した。Example 3 A molten platinum alloy was produced by adding 90% by weight of Pt and 5% by weight of Cu and Ga, adding a small amount of Pd, and melting and stirring. On the other hand, tourmaline was finely pulverized and screened with a sieve to obtain an average particle diameter of 0.1 μm.
Tourmaline powder having a size of １００100 μm was introduced so as to be 3% by weight with respect to 97% by weight of the molten silver alloy.
【００１９】得たプラチナ合金は、色調と明るさ、変色
度合いともトルマリン粉末を添加しなかったものとほと
んど遜色ないものであった。The obtained platinum alloy had almost the same color tone, brightness and degree of discoloration as those without the addition of tourmaline powder.
【００２０】[0020]
【発明の効果】この発明によれば、トルマリンの成分量
を以上のように構成したので、長年使用しても電気磁気
的作用が損なわれることはなく、しかも装身具用合金と
して有用なトルマリン含有貴金属合金を提供することが
できるようになった。According to the present invention, since the amount of tourmaline is constituted as described above, the electromagnetism is not impaired even when used for many years, and the tourmaline-containing noble metal is useful as an alloy for accessories. Alloys can now be provided.
Claims (3)
成分とする貴金属素材に、トルマリン粉末を０．１重量
％〜５０重量％添加したことを特徴とするトルマリン含
有貴金属合金。1. A tourmaline-containing noble metal alloy comprising 0.1 to 50% by weight of a tourmaline powder added to a noble metal material containing any one of gold, silver and platinum as a main component.
成分とする貴金属素材に、トルマリン粉末を０．１重量
％〜１０重量％添加したことを特徴とするトルマリン含
有貴金属合金。2. A tourmaline-containing noble metal alloy comprising 0.1% to 10% by weight of tourmaline powder added to a noble metal material mainly containing gold, silver or platinum.
成分とする貴金属素材に、トルマリン粉末を添加した貴
金属合金層と、他の貴金属層とを積層してなる請求項１
または２に記載のトルマリン含有貴金属合金。3. A precious metal material containing one of gold, silver, and platinum as a main component, a precious metal alloy layer to which tourmaline powder is added, and another noble metal layer laminated.
Or the tourmaline-containing noble metal alloy according to 2.