JP2000154339A - Composition for forming antimicrobial coating film - Google Patents
Composition for forming antimicrobial coating filmInfo
- Publication number
- JP2000154339A JP2000154339A JP10328231A JP32823198A JP2000154339A JP 2000154339 A JP2000154339 A JP 2000154339A JP 10328231 A JP10328231 A JP 10328231A JP 32823198 A JP32823198 A JP 32823198A JP 2000154339 A JP2000154339 A JP 2000154339A
- Authority
- JP
- Japan
- Prior art keywords
- composition
- coating film
- forming
- antibacterial
- organic solvent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は抗菌性塗膜形成用組
成物に関する。具体的には、細菌やヴィールスなどに効
果を発揮する抗菌性を有するラッカーやワニス、エナメ
ル等の各種塗料として用いられる抗菌性塗膜形成用組成
物に関する。TECHNICAL FIELD The present invention relates to a composition for forming an antibacterial coating. Specifically, the present invention relates to a composition for forming an antibacterial coating film used as various paints such as lacquers, varnishes, and enamels having an antibacterial property that exerts an effect on bacteria and viruses.
【０００２】[0002]
【従来の技術】従来から、無機抗菌剤を含有したラッカ
ーやワニスあるいはエナメル等の各種塗料として用いら
れる抗菌性塗膜形成用組成物（以下、「塗料」と称す
る。）が知られている。これらの塗料においては、形成
された塗膜表面に存在する抗菌剤のみが塗膜表面に付着
された細菌等に有効に作用し、塗膜内部に入り込んだ抗
菌剤はその効果を発揮し得なかった。2. Description of the Related Art A composition for forming an antibacterial coating film (hereinafter referred to as "paint") containing an inorganic antibacterial agent and used as various paints such as lacquer, varnish or enamel has been known. In these paints, only the antibacterial agent present on the formed coating film surface effectively acts on bacteria and the like attached to the coating film surface, and the antibacterial agent that has entered the inside of the coating film cannot exert its effect. Was.
【０００３】すなわち、これらの塗料に用いられる無機
抗菌剤の多くは、ごく微量含有されている銀や銅などの
抗菌性金属イオンが細菌等に作用することにより効果を
発揮するものであり、細菌の細胞壁やヴィールスの外殻
を攻撃して死滅させる。従って、抗菌性を有効に発揮さ
せるためには、無機抗菌剤から金属イオンとして溶出す
る必要があり、水の存在が効果を発揮するための前提と
なる。That is, most of the inorganic antibacterial agents used in these paints exhibit an effect by the action of a very small amount of antibacterial metal ions such as silver and copper on bacteria and the like. Attack and kill the cell wall and the outer shell of the virus. Therefore, in order to effectively exhibit antibacterial properties, it is necessary to elute as metal ions from the inorganic antibacterial agent, and the presence of water is a prerequisite for exhibiting the effect.
【０００４】しかしながら、これらの塗料においては、
その多くが合成樹脂を有機溶剤に溶解あるいは分散させ
たものであり、疎水性である。このため、形成された塗
膜表面においては、空気中の水分と接触して無機抗菌剤
から金属イオンが溶出されるが、疎水性のある塗膜の内
部では水分がほとんど存在せず、抗菌性を十分に発揮で
きないという問題があった。However, in these paints,
Many of them are obtained by dissolving or dispersing a synthetic resin in an organic solvent, and are hydrophobic. For this reason, on the surface of the formed coating film, metal ions are eluted from the inorganic antibacterial agent in contact with moisture in the air, but there is almost no moisture inside the hydrophobic coating film, and antibacterial properties There is a problem that cannot fully demonstrate.
【０００５】一方、無機抗菌剤を相当量の水分と長時間
接触させておくと、イオン化されやすい状態で坦持され
ている銀が金属銀や硫化銀として析出し、抗菌性を発揮
しなくなるだけでなく、溶液そのものを茶褐色や黒褐色
に変色させる場合がある。従って、塗料中に水分を多量
に含ませた場合には、抗菌力は向上するものの、塗料そ
のものが変色してしまい、過度に親水性の合成樹脂や溶
剤を使用することも好ましくない。On the other hand, if the inorganic antibacterial agent is kept in contact with a considerable amount of water for a long time, silver carried in a state easily ionized precipitates as metallic silver or silver sulfide, and the antibacterial property is no longer exhibited. Instead, the solution itself may turn brown or dark brown. Therefore, when a large amount of water is contained in the paint, the antibacterial activity is improved, but the paint itself is discolored, and it is not preferable to use an excessively hydrophilic synthetic resin or solvent.
【０００６】本発明は叙上の従来例の欠点に鑑みてなさ
れたものであり、無機抗菌剤、特に銀系無機抗菌剤によ
る変色が少なく、抗菌作用に優れた塗料を提供すること
にある。The present invention has been made in view of the above-mentioned drawbacks of the prior art, and has as its object to provide a coating material which is less discolored by an inorganic antibacterial agent, particularly a silver-based inorganic antibacterial agent, and which has excellent antibacterial action.
【０００７】そこで、本願発明者らは、鋭意努力の結
果、親水基を有する合成樹脂を用い、これを親水性の有
機溶媒に溶解させることにより上記目的を達成すること
を見出し、本願発明を完成するに至った。The inventors of the present invention have, as a result of diligent efforts, found that the above object can be achieved by using a synthetic resin having a hydrophilic group and dissolving the same in a hydrophilic organic solvent. I came to.
【０００８】[0008]
【課題を解決するための手段】本発明の抗菌性塗膜形成
用組成物は、含水可能な有機溶剤と、この有機溶剤に溶
解し、その分子構造中に少なくとも１以上の親水基を有
する合成樹脂とを含有する塗膜形成性組成物に、銀系無
機抗菌剤を分散若しくは溶解させたことを特徴としてい
る。The composition for forming an antibacterial coating film of the present invention comprises a water-containing organic solvent and a synthetic resin which is dissolved in the organic solvent and has at least one hydrophilic group in its molecular structure. A silver-based inorganic antibacterial agent is dispersed or dissolved in a film-forming composition containing a resin.
【０００９】上述したように、無機抗菌剤を分散若しく
は溶解させるための溶媒としては、抗菌作用の点からは
水を用いるのが好ましい。しかしながら、銀を含有する
銀系無機抗菌剤では、水分と接触するとほとんど１００
％変色を生じる。一方、疎水性の有機溶媒を用いた場合
には変色を防止できるが、合成樹脂に表面を覆われた結
果、銀系無機抗菌剤は水分との接触が遮断され、抗菌作
用を十分に発揮できない。As described above, it is preferable to use water as a solvent for dispersing or dissolving the inorganic antibacterial agent from the viewpoint of antibacterial action. However, silver-based inorganic antibacterial agents containing silver have almost 100
% Discoloration. On the other hand, when a hydrophobic organic solvent is used, discoloration can be prevented, but as a result of covering the surface with a synthetic resin, the silver-based inorganic antibacterial agent is blocked from contact with moisture and cannot exert its antibacterial effect sufficiently. .
【００１０】本発明に用いられる含水可能な有機溶媒と
しては、合成樹脂を溶解若しくは分散させることが可能
であり、含有された銀系無機抗菌剤に含まれた銀イオン
を溶出させるに十分な量の水を含水させることができる
有機溶媒であれば特に限定されるものではないが、合成
樹脂を溶解若しくは分散させた場合に相分離を生じない
程度に、水と相溶性のある有機溶媒が好適に用いられ
る。また、塗膜を短時間に形成させるために適度な揮発
性を有するものが特に好ましい。The water-containing organic solvent used in the present invention can dissolve or disperse a synthetic resin and has an amount sufficient to elute silver ions contained in the contained silver-based inorganic antibacterial agent. The organic solvent is not particularly limited as long as it is an organic solvent capable of containing water, but an organic solvent compatible with water is preferable to the extent that phase separation does not occur when the synthetic resin is dissolved or dispersed. Used for Further, those having an appropriate volatility for forming a coating film in a short time are particularly preferable.
【００１１】当該有機溶媒としては、例えば、メタノー
ル、エタノール、ｎ−プロピルアルコール、イソプロピ
ルアルコール、ｎ−ブチルアルコール、イソブチルアル
コール、イソアミルアルコール、エチレングリコールな
どの低級アルコール類、アセトンやメチルエチルケトン
などの低級ケトン類、酢酸メチル、酢酸エチルなどの酢
酸エチルエステル類などが挙げられ、これら１種若しく
は２種以上を混合して用いることが可能である。特に、
以下に述べる合成樹脂の溶解性や塗布後の乾燥等の観点
から、イソプロピルアルコールやイソアミルアルコール
が好適に用いられる。Examples of the organic solvent include lower alcohols such as methanol, ethanol, n-propyl alcohol, isopropyl alcohol, n-butyl alcohol, isobutyl alcohol, isoamyl alcohol, ethylene glycol, and lower ketones such as acetone and methyl ethyl ketone. And ethyl acetate such as methyl acetate and ethyl acetate, and the like, and these can be used alone or in combination of two or more. In particular,
Isopropyl alcohol and isoamyl alcohol are preferably used from the viewpoint of solubility of the synthetic resin described below, drying after coating, and the like.
【００１２】また、当該有機溶媒には、合成樹脂の溶解
性を高めるために、ベンゼンやトルエン、シクロヘキサ
ンなど疎水性有機溶媒を、相分離を生じない程度に混合
して用いることもできる。In order to increase the solubility of the synthetic resin, a hydrophobic organic solvent such as benzene, toluene, or cyclohexane may be mixed with the organic solvent so as not to cause phase separation.
【００１３】さらに、必要に応じて、銀系無機抗菌剤の
効果をより発揮するために、水を混合することも可能で
ある。このとき、抗菌性塗膜形成用組成物中の含水率
（カールフィッシャー法による）は、１０重量％以下で
あることが好ましい。１０重量％を越えて水を混合した
場合には、銀系無機抗菌剤から溶出された銀イオンが析
出し、抗菌性塗膜形成用組成物を変色させる恐れがあ
る。また、溶解された合成樹脂が不溶化され、相分離を
引き起こす恐れも生じる。Further, if necessary, water can be mixed in order to further exert the effect of the silver-based inorganic antibacterial agent. At this time, the water content (by Karl Fischer method) in the composition for forming an antibacterial coating film is preferably 10% by weight or less. When water is mixed in an amount exceeding 10% by weight, silver ions eluted from the silver-based inorganic antibacterial agent may precipitate and discolor the composition for forming an antibacterial coating. Further, the dissolved synthetic resin may be insolubilized and cause a phase separation.
【００１４】次に、本発明において用いられる合成樹脂
としても、その分子構造中に少なくとも１以上の親水基
を有し、上記含水可能な有機溶媒に溶解若しくは分散可
能なものであって、塗布乾燥後に塗膜を形成可能なもの
であれば特に限定されるものではない。当該合成樹脂
は、アルコール基やカルボキシル基などの親水基を含有
すればよく、例えば、単量体成分として、ポリビニルア
ルコールやこれらのエステルを含む各種誘導体のポリマ
ー（ビニルアルコール系ポリマー）、あるいはアクリル
酸やメタクリル酸並びにこれらのエステルを含む各種誘
導体のポリマー（アクリル酸系ポリマー）、あるいはこ
れらの各種単量体と他の単量体とのコポリマーなどを挙
げることができる。また、上記有機溶媒に溶解若しくは
分散され、相分離を生じない限り、ニトロセルロールを
用いることもできる。Next, the synthetic resin used in the present invention also has at least one hydrophilic group in its molecular structure and can be dissolved or dispersed in the water-containing organic solvent. There is no particular limitation as long as a coating film can be formed later. The synthetic resin only needs to contain a hydrophilic group such as an alcohol group or a carboxyl group. For example, as a monomer component, a polymer of various derivatives including polyvinyl alcohol or an ester thereof (vinyl alcohol-based polymer), or acrylic acid And polymers of various derivatives including methacrylic acid and esters thereof (acrylic acid polymers), or copolymers of these various monomers with other monomers. Also, nitrocellulose can be used as long as it is dissolved or dispersed in the above organic solvent and does not cause phase separation.
【００１５】より具体的には、ビニルアルコール系ポリ
マーとして、ポリビニルブチラールやポリ酢酸ビニルな
どを、アクリル酸系ポリマーとしては、ブチルメタクリ
ル酸ポリマーやアクリル酸メチル、メタクリル酸メチル
などを挙げることができ、これらの１種若しくは２種以
上を用いることができる。More specifically, examples of the vinyl alcohol-based polymer include polyvinyl butyral and polyvinyl acetate, and examples of the acrylic acid-based polymer include butyl methacrylate polymer, methyl acrylate, and methyl methacrylate. One or more of these can be used.
【００１６】当該合成樹脂は、用いられる合成樹脂の種
類や有機溶媒の種類によっても異なるが、合成樹脂の溶
液（分散液）、つまり塗膜形成用組成物中、概ね１〜３
０重量％配合され、特に、１０〜２０重量％配合するの
が好ましい。The synthetic resin varies depending on the type of the synthetic resin used and the type of the organic solvent.
0% by weight, particularly preferably 10 to 20% by weight.
【００１７】本発明に含有される銀系無機抗菌剤として
も特に限定されるものではなく、例えば、特開平３−２
８７５０８号公報に開示されたアルミナの表面に銀イオ
ンを含むアルミノ珪酸塩の被膜を有する抗菌性組成物
や、特開平３−２５２３０８号公報に開示されたシリカ
ゲルの表面に銀イオンを含むアルミノ珪酸塩の被膜を有
する抗菌性組成物を挙げることができる。The silver-based inorganic antibacterial agent contained in the present invention is not particularly limited.
87508 discloses an antibacterial composition having a coating of aluminosilicate containing silver ions on the surface of alumina, and an aluminosilicate containing silver ions on the surface of silica gel disclosed in JP-A-3-252308. An antimicrobial composition having a coating of
【００１８】これらの抗菌性組成物の粒径としては、例
えば３０〜１００メッシュのものを用いることができる
が、抗菌性塗膜形成用組成物中への均質な分散性を考慮
すれば、さらに粒径の細かい、例えば２００〜３００メ
ッシュの粒子またはより微細な数ミクロン〜数十ミクロ
ンの粒子のものが好適である。The particle size of these antibacterial compositions may be, for example, 30 to 100 mesh, but if uniform dispersion in the composition for forming an antibacterial coating film is taken into consideration, furthermore, Particles having a small particle size, for example, 200 to 300 mesh particles or finer particles having a size of several microns to several tens of microns are preferable.
【００１９】また、当該銀系無機抗菌剤は、抗菌性塗膜
形成用組成物中に合成樹脂（固形分）に対して、約０．
１〜１０重量％（多くの場合は１〜５重量％）の割合で
配合されるが、銀系無機抗菌剤の種類や抗菌性塗膜形成
用組成物の使用目的に応じて適宜調整される。もちろ
ん、上記銀系無機抗菌剤に限定されるものではなく、種
々の銀系無機抗菌剤を用いることもできる。The silver-based inorganic antibacterial agent is added to the composition for forming an antibacterial coating film in an amount of about 0.
It is blended at a ratio of 1 to 10% by weight (often 1 to 5% by weight), but is appropriately adjusted depending on the type of the silver-based inorganic antibacterial agent and the intended use of the composition for forming an antibacterial coating. . Of course, the present invention is not limited to the silver-based inorganic antibacterial agents, and various silver-based inorganic antibacterial agents can be used.
【００２０】本発明に係る抗菌性塗膜形成用組成物は、
種々な用途に応用できるものであり、当該塗膜形成用組
成物に顔料を添加することにより、エナメルやラッカー
として用いることができる。当該顔料としては、通常の
塗料に用いられるものであれば、特に限定されるもので
はない。また、顔料を用いることなく、透明な状態で用
いることによってワニスとして用いることもできる。The composition for forming an antibacterial coating film according to the present invention comprises:
It can be applied to various uses, and can be used as an enamel or a lacquer by adding a pigment to the coating film forming composition. The pigment is not particularly limited as long as it is used for ordinary paints. In addition, it can be used as a varnish by using it in a transparent state without using a pigment.
【００２１】もちろん、当該抗菌性塗膜形成用組成物に
は、通常塗料に用いられる各種の添加剤、例えば、可塑
剤や乾燥促進剤、界面活性剤、シリコーン化合物などの
消泡剤などを含有させることができるのは言うまでもな
い。Of course, the composition for forming an antibacterial coating film contains various additives usually used in paints, for example, a plasticizer, a drying accelerator, a surfactant, and an antifoaming agent such as a silicone compound. Needless to say, it can be done.
【００２２】また、当該抗菌性塗膜形成用組成物を用い
て塗膜を形成する場合には、数μｍ〜１０μｍ程度に塗
膜を形成するのが望ましく、この厚さに塗膜を形成可能
なように適宜合成樹脂や有機溶媒を選択するのが望まし
い。この程度の厚さの塗膜にした場合に、最も抗菌作用
を発揮できる。When a coating film is formed using the composition for forming an antibacterial coating film, the coating film is preferably formed to a thickness of about several μm to 10 μm. It is desirable to appropriately select a synthetic resin or an organic solvent. When a coating film having such a thickness is formed, the antibacterial effect can be exhibited most.
【００２３】[0023]
【実施例】次に本発明の実施例に係る抗菌性塗膜形成用
組成物を作成し、本発明による効果を確認した。EXAMPLES Next, compositions for forming an antibacterial coating film according to examples of the present invention were prepared, and the effects of the present invention were confirmed.
【００２４】合成樹脂として、ブチルメタクリル酸ポリ
マー（重量平均分子量、約７０００）を、イソプロピル
アルコールに溶解し、ポリマー３重量％を含む溶液（塗
膜形成用組成物）を得た。この溶液に、当該溶液中のポ
リマー（固形分）に対して５重量％となるように、アル
ミナの表面に銀イオンを含むアルミノ珪酸塩の被膜を有
する抗菌性組成物（商品名「バクテノン」 平均粒径１
μｍ）を含有して、実施例に係る抗菌性塗膜形成用組成
物（ワニス）を得た。As a synthetic resin, a butyl methacrylic acid polymer (weight average molecular weight, about 7,000) was dissolved in isopropyl alcohol to obtain a solution (composition for forming a coating film) containing 3% by weight of the polymer. In this solution, an antibacterial composition (trade name “Bactenone” having a coating of aluminosilicate containing silver ions on the surface of alumina) was adjusted to 5% by weight based on the polymer (solid content) in the solution. Particle size 1
μm) to obtain a composition (varnish) for forming an antibacterial coating film according to the example.
【００２５】〔抗菌力試験〕このものを、５ｃｍ角のＰ
ＶＣ樹脂板にスプレーにて、膜厚１０μｍ程度に塗布し
て、塗膜を形成した。その後、この塗膜を用い、２５℃
において大腸菌を用いた塗膜密着法（２４時間評価）に
て抗菌力を評価した。なお、比較例として、塗膜を形成
させていないＰＶＣ樹脂板を用いた。[Antibacterial activity test]
It was applied to a VC resin plate by spraying to a film thickness of about 10 μm to form a coating film. Then, using this coating film, 25 ℃
The antibacterial activity was evaluated by the coating film adhesion method using Escherichia coli (evaluated for 24 hours). As a comparative example, a PVC resin plate on which no coating film was formed was used.
【００２６】 〔評価結果〕 ──────────────────────────────── 菌数変化（ＣＦＵ／ｍｌ） 検 体 名 ───────────────── ０ ｈｒ ２４ｈｒ ──────────────────────────────── 実 施 例 ６．１×１０ ＜１０ 比 較 例 ６．１×１０ ６．４×１０ ────────────────────────────────[Evaluation Results] 変 化 Change in bacterial count (CFU / ml) ０ 0 hr 24 hr ────────────────────────────── << Example 6.1 * 10 <10 Comparative Example 6.1 * 10 6.4 * 10} ───────
【００２７】上記結果からも分かるように、本発明に係
る抗菌性塗膜形成用組成物を用いた場合には、良好に抗
菌力を発揮することができた。また、当該抗菌性塗膜形
成用組成物は、長期間保存しても変色することがなかっ
た。As can be seen from the above results, when the composition for forming an antibacterial coating film according to the present invention was used, the antibacterial activity was successfully exhibited. In addition, the composition for forming an antibacterial coating film did not discolor even when stored for a long period of time.
【発明の効果】本発明の抗菌性塗膜形成用組成物は、含
水可能な有機溶剤と、この有機溶剤に溶解し、その分子
構造中に少なくとも１以上の親水基を有する合成樹脂と
を含有する塗膜形成性組成物に、銀系無機抗菌剤を分散
若しくは溶解させたことを特徴としているので、溶出さ
れた銀イオンによる変色を抑えるとともに、配合された
銀系無機抗菌剤の抗菌作用を十分に発揮させることがで
きる。The composition for forming an antibacterial coating film of the present invention comprises a water-containing organic solvent and a synthetic resin dissolved in the organic solvent and having at least one hydrophilic group in its molecular structure. The film-forming composition is characterized by dispersing or dissolving a silver-based inorganic antibacterial agent, so that discoloration due to eluted silver ions is suppressed and the antibacterial action of the compounded silver-based inorganic antibacterial agent is reduced. It can be fully demonstrated.
【００２８】このとき、前記抗菌性塗膜形成用組成物中
の含水率は、１０％以下に設定するのが好ましく、配合
された合成樹脂が相分離を引き起こすなく、安定な抗菌
性塗膜形成用組成物を提供できる。At this time, the water content in the composition for forming an antibacterial coating is preferably set to 10% or less, and the compounded synthetic resin does not cause phase separation, so that a stable antibacterial coating can be formed. Compositions can be provided.
【００２９】特に、前記合成樹脂として、ブチルメタク
リル酸ポリマーやポリビニルブチラールを用いることに
より、好適に本発明に係る抗菌性塗膜形成用組成物を提
供でき、前記塗膜形成用組成物中、概ね１〜３０重量
％、特に、１０〜２０重量％を含有させることにより、
良好に塗膜を形成できる。In particular, by using a butyl methacrylate polymer or polyvinyl butyral as the synthetic resin, the composition for forming an antibacterial coating film according to the present invention can be suitably provided. By containing 1 to 30% by weight, particularly 10 to 20% by weight,
A good coating film can be formed.
【００３０】また、塗膜厚さ１０μｍ以下に形成可能
に、合成樹脂や有機溶媒を選択するのが望ましく、この
ときに最も効果的に抗菌作用を発揮できる。It is desirable to select a synthetic resin or an organic solvent so that the coating film can be formed to a thickness of 10 μm or less. At this time, the antibacterial effect can be exhibited most effectively.
─────────────────────────────────────────────────────
────────────────────────────────────────────────── ───
【手続補正書】[Procedure amendment]
【提出日】平成１２年１月１７日（２０００．１．１
７）[Submission date] January 17, 2000 (2000.1.1)
7)
【手続補正１】[Procedure amendment 1]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】特許請求の範囲[Correction target item name] Claims
【補正方法】変更[Correction method] Change
【補正内容】[Correction contents]
【特許請求の範囲】[Claims]
【手続補正２】[Procedure amendment 2]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】０００８[Correction target item name] 0008
【補正方法】変更[Correction method] Change
【補正内容】[Correction contents]
【０００８】[0008]
【課題を解決するための手段】本発明の抗菌性塗膜形成
用組成物は、含水可能な有機溶媒と、この有機溶媒に溶
解若しくは分散可能で、ビニルアルコール系ポリマー、
アクリル酸系ポリマー、ニトロセルロースからなる群か
ら選ばれたいずれか１種のポリマーと、銀系無機抗菌剤
とを分散若しくは溶解させた抗菌性塗膜形成用組成物で
あって、該抗菌性塗膜形成用組成物中の含水率が１０重
量％以下となるように水分を含有させたことを特徴とし
ている。 Means for Solving the Problems Formation of antibacterial coating film of the present invention
The composition for use is composed of an organic solvent that can
Dissolvable or dispersible, vinyl alcohol polymer,
A group consisting of acrylic acid polymer and nitrocellulose
Any one polymer selected from the group consisting of a silver-based inorganic antibacterial agent
With an antimicrobial coating film forming composition in which
The moisture content in the composition for forming an antibacterial coating film is 10 times
Characterized by containing water so as to be less than
ing.
【手続補正３】[Procedure amendment 3]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００２７[Correction target item name] 0027
【補正方法】変更[Correction method] Change
【補正内容】[Correction contents]
【００２７】上記結果からも分かるように、本発明に係
る抗菌性塗膜形成用組成物を用いた場合には、良好に抗
菌力を発揮することができた。また、当該抗菌性塗膜形
成組成物は、長期間保存しても変色することがなかっ
た。 As can be seen from the above results, the present invention
Good antimicrobial coating composition,
Bacterial power could be demonstrated. In addition, the antibacterial coating
The composition does not discolor even after long-term storage
Was.
【手続補正４】[Procedure amendment 4]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００２８[Correction target item name] 0028
【補正方法】変更[Correction method] Change
【補正内容】[Correction contents]
【００２８】[0028]
【発明の効果】本発明の抗菌性塗膜形成用組成物は、含
水可能な有機溶媒と、この有機溶媒に溶解若しくは分散
可能で、ビニルアルコール系ポリマー、アクリル酸系ポ
リマー、ニトロセルロースからなる群から選ばれたいず
れか１種のポリマーと、銀系無機抗菌剤とを分散若しく
は溶解させた抗菌性塗膜形成用組成物であって、該抗菌
性塗膜形成用組成物中の含水率が１０重量％以下となる
ように水分を含有させたことを特徴としているので、溶
出された銀イオンによる変色を抑えるとともに、配合さ
れた銀系無機抗菌剤の抗菌作用を十分に発揮させること
ができる。特に、配合された合成樹脂が相分離を引き起
こすことなく、安定な抗菌性塗膜形成用組成物を提供で
きる。 The composition for forming an antibacterial coating film of the present invention contains
Water-soluble organic solvent and dissolved or dispersed in this organic solvent
Possible, vinyl alcohol polymer, acrylic acid polymer
Rim, selected from the group consisting of nitrocellulose
Disperse one kind of polymer and silver-based inorganic antibacterial agent
Is a dissolved antimicrobial coating film-forming composition,
Water content in the composition for forming a functional coating film is 10% by weight or less
It is characterized by containing moisture as described above.
In addition to suppressing discoloration due to the released silver ions,
To fully demonstrate the antibacterial action of the selected silver-based inorganic antibacterial agent
Can be. In particular, compounded synthetic resin causes phase separation
Provides stable antibacterial coating composition without rubbing
Wear.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ｃ０９Ｄ 7/12 Ｃ０９Ｄ 7/12 Ｚ 129/14 129/14 133/10 133/10 (72)発明者 岩田 浩 兵庫県尼崎市西長洲町２丁目５番13号 日 本電子材料株式会社内 Ｆターム(参考） 4J002 AB021 BE021 BE061 BG051 DA076 DE146 DJ006 FB076 FD186 GH01 HA05 4J038 CE021 CE071 CG031 CG131 CH031 HA216 JA19 JA20 JA33 JA56 KA06 KA15 NA05──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛ (Reference) C09D 7/12 C09D 7/12 Z 129/14 129/14 133/10 133/10 (72) Inventor Iwata Hiroshi 2-5-13 Nishi-Nagasu-cho, Amagasaki-shi, Hyogo Japan Electronic Materials Co., Ltd. F-term (reference) 4J002 AB021 BE021 BE061 BG051 DA076 DE146 DJ006 FB076 FD186 GH01 HA05 4J038 CE021 CE071 CG031 CG131 CH031 HA216 JA19 JA20 KA15 NA05
Claims (5)
溶解若しくは分散し、その分子構造中に少なくとも１以
上の親水基を有する合成樹脂とを含有する塗膜形成性組
成物に、銀系無機抗菌剤を分散若しくは溶解させたこと
を特徴とする抗菌性塗膜形成用組成物。1. A film-forming composition comprising a water-containing organic solvent and a synthetic resin dissolved or dispersed in the organic solvent and having at least one or more hydrophilic groups in its molecular structure, a silver-based composition. A composition for forming an antibacterial coating film, wherein an inorganic antibacterial agent is dispersed or dissolved.
は、１０重量％以下であることを特徴とする請求項１記
載の抗菌性塗膜形成用組成物。2. The composition for forming an antibacterial coating according to claim 1, wherein the water content in the composition for forming an antibacterial coating is 10% by weight or less.
リマーであることを特徴とする請求項１又は２記載の抗
菌性塗膜形成用組成物。3. The composition for forming an antibacterial coating film according to claim 1, wherein the synthetic resin is a butyl methacrylic acid polymer.
であることを特徴とする請求項１又は２記載の抗菌性塗
膜形成用組成物。4. The composition for forming an antimicrobial coating film according to claim 1, wherein the synthetic resin is polyvinyl butyral.
とを特徴とする請求項１、２、３又は４に記載の抗菌性
塗膜形成用組成物。5. The composition for forming an antibacterial coating film according to claim 1, wherein a coating film can be formed to a thickness of 10 μm or less.