JP2000094558A - Buffer material for soundproof flooring and manufacture thereof - Google Patents
Buffer material for soundproof flooring and manufacture thereofInfo
- Publication number
- JP2000094558A JP2000094558A JP10266670A JP26667098A JP2000094558A JP 2000094558 A JP2000094558 A JP 2000094558A JP 10266670 A JP10266670 A JP 10266670A JP 26667098 A JP26667098 A JP 26667098A JP 2000094558 A JP2000094558 A JP 2000094558A
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- resin layer
- thermoplastic resin
- cushioning material
- thin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、特に比較的防音性
能が低くても使用可能な一般一戸建住宅向きの防音床材
用緩衝材及びその製造方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a cushioning material for a soundproof flooring material for a general detached house which can be used even if the soundproofing performance is relatively low, and a method for manufacturing the same.
【０００２】[0002]
【従来の技術】周知の如く、防音床材用緩衝材には、集
合住宅に使用される高性能なもの（Ｌ−３５〜Ｌ−４５
程度）と、一戸建ての一般住宅に使用される比較的性能
の緩いもの（Ｌ−５０〜Ｌ−６０程度）に大別される。2. Description of the Related Art As is well known, high-performance materials (L-35 to L-45) used for apartment houses are used as cushioning materials for soundproof flooring.
) And those with relatively low performance (about L-50 to L-60) used for single-family ordinary houses.
【０００３】ところで、比較的防音性能が緩くても使用
可能な一般一戸建住宅向きの防音床材用緩衝材として、
略２ｍｍ〜１０ｍｍ程度の多孔質シート（例えば、軟質
ポリウレタンフォームシートや不織布）の平板が使用さ
れている。軟質ポリウレタンフォームシートを例に挙げ
ると、スラブから所定厚さ（例えば４ｍｍ）にスライス
加工された軟質ポリウレタンフォームシートがそのまま
床材の緩衝材として使用されている。By the way, as a cushioning material for soundproof flooring for general detached houses which can be used even if the soundproofing performance is relatively low,
A flat sheet of a porous sheet (for example, a flexible polyurethane foam sheet or a nonwoven fabric) having a thickness of about 2 mm to 10 mm is used. Taking a flexible polyurethane foam sheet as an example, a flexible polyurethane foam sheet obtained by slicing a slab to a predetermined thickness (for example, 4 mm) is used as it is as a cushioning material for flooring.
【０００４】[0004]
【発明が解決しようとする課題】しかし、例えば軟質ポ
リウレタンフォームシートによる緩衝材には、次のよう
な問題点があった。 (1) 床面コンクリートの養生が不十分の時、水が浸み出
してくる。従って、緩衝材が水を吸い込み床板に達する
ので、吸音効果が低下すると共にカビ等が発生し不衛生
となる。 (2) 施工の時、床面に塗布されている接着剤が緩衝材内
に浸み込み、圧縮によりセルが潰れてしまうので、吸音
効果が低下する。However, the cushioning material made of, for example, a flexible polyurethane foam sheet has the following problems. (1) When the curing of the floor concrete is insufficient, water seeps out. Therefore, since the cushioning material absorbs water and reaches the floor plate, the sound absorbing effect is reduced, and mold and the like are generated, which is unsanitary. (2) At the time of construction, the adhesive applied to the floor surface penetrates into the cushioning material and the cells are crushed by compression, so that the sound absorbing effect is reduced.
【０００５】本発明はこうした事情を考慮してなされた
もので、薄いシートと、この薄いシート上に形成され
た、該シートと反対側の主面が接着機能を有した熱可塑
性樹脂層と、この熱可塑性樹脂層上に形成された多孔性
シートとを具備した構成とすることにより、床面から浸
み出してくる水を防止するとともに、床面の接着剤の含
浸を防止しえる防音床用緩衝材を提供することを目的と
する。The present invention has been made in view of such circumstances, and includes a thin sheet, a thermoplastic resin layer formed on the thin sheet and having a main surface opposite to the sheet having an adhesive function. By providing a structure including the porous sheet formed on the thermoplastic resin layer, it is possible to prevent water seeping out from the floor surface and prevent impregnation of the floor surface with the adhesive. It is intended to provide a cushioning material for use.
【０００６】また、本発明は、薄いシートの片面に熱可
塑性樹脂層を積層する工程と、前記熱可塑性樹脂層上に
多孔性シートを形成する工程と、前記多孔性シート面を
加熱した状態で圧縮し、前記多孔性シート側の熱可塑性
樹脂層は溶融させかつ前記薄いシート側の熱可塑性樹脂
層は溶融させずにそのまま残す工程とを具備した構成と
することにより、床面から浸み出してくる水を防止する
とともに、床面の接着剤の含浸を防止しえる防音床用緩
衝材を製造する方法を提供することを目的とする。[0006] The present invention also provides a step of laminating a thermoplastic resin layer on one side of a thin sheet, a step of forming a porous sheet on the thermoplastic resin layer, and a step of heating the surface of the porous sheet. Compressing the thermoplastic resin layer on the porous sheet side and leaving the thermoplastic resin layer on the thin sheet side as it is without melting, thereby leaching from the floor surface. It is an object of the present invention to provide a method for producing a cushioning material for a soundproof floor that can prevent incoming water and prevent the floor from being impregnated with an adhesive.
【０００７】[0007]
【課題を解決するための手段】本願第１の発明は、薄い
シートと、この薄いシート上に形成された、該シートと
反対側の主面が接着機能を有した熱可塑性樹脂層と、こ
の熱可塑性樹脂層上に形成された多孔性シートとを具備
することを特徴とする防音床材用緩衝材である。According to a first aspect of the present invention, there is provided a thin sheet, a thermoplastic resin layer formed on the thin sheet and having a main surface opposite to the sheet having an adhesive function. And a porous sheet formed on a thermoplastic resin layer.
【０００８】本願第２の発明は、薄いシートの片面に熱
可塑性樹脂層を積層する工程と、前記熱可塑性樹脂層上
に多孔性シートを形成する工程と、前記多孔性シート面
を加熱した状態で圧縮し、前記多孔性シート側の熱可塑
性樹脂層は溶融させかつ前記薄いシート側の熱可塑性樹
脂層は溶融させずにそのまま残す工程とを具備すること
を特徴とする防音床材用緩衝材の製造方法である。[0008] The second invention of the present application comprises a step of laminating a thermoplastic resin layer on one side of a thin sheet, a step of forming a porous sheet on the thermoplastic resin layer, and a step of heating the surface of the porous sheet. Wherein the thermoplastic resin layer on the porous sheet side is melted and the thermoplastic resin layer on the thin sheet side is left as it is without being melted. It is a manufacturing method of.
【０００９】本発明において、薄いシートとしては、防
湿紙、クラフト紙、洋紙等の紙類、あるいは目付量が１
５ｇ／ｍ2 〜７０ｇ／ｍ2 の薄い不織布のいずれかが挙
げられる。In the present invention, as the thin sheet, paper such as moisture-proof paper, kraft paper, and Western paper, or a sheet having a basis weight of 1 is used.
Either thin nonwoven of 5g / m 2 ~70g / m 2 and the like.
【００１０】本発明において、前記熱可塑性樹脂層の材
質としては、例えばポリエチレン樹脂、アクリル樹脂、
熱可塑性ウレタン樹脂が挙げられる。これらの樹脂はコ
ーティング法等により塗布して薄いシート上に形成され
る。熱可塑性樹脂層の厚さは特に限定されないが、風合
い等の点から１６μｍ〜５０μｍ程度が良好である。In the present invention, the material of the thermoplastic resin layer is, for example, polyethylene resin, acrylic resin,
A thermoplastic urethane resin is exemplified. These resins are applied by a coating method or the like and formed on a thin sheet. The thickness of the thermoplastic resin layer is not particularly limited, but is preferably about 16 μm to 50 μm from the viewpoint of hand and the like.
【００１１】本発明において、前記多孔性シートとして
は、軟質ポリウレタンフォームシート、半硬質ポリウレ
タンフォームシート、ポリプロピレン、ポリエステル等
の長繊維不織布、短繊維不織布のいずれかが挙げられ
る。ここで、前記多孔性シートとして軟質ポリウレタン
フォームシートを用いた場合、密度１８ｋｇ／ｍ3 〜６
５ｋｇ／ｍ3 程度、厚さ２〜１０ｍｍ程度の軟質ポリウ
レタンフォームシートが好ましい。また、予め加熱圧縮
することにより、片面又は両面に凹凸模様を形成させた
軟質ポリウレタンフォームシートを使用すると、吸着効
果が向上する。In the present invention, examples of the porous sheet include a flexible polyurethane foam sheet, a semi-rigid polyurethane foam sheet, a long-fiber nonwoven fabric such as polypropylene and polyester, and a short-fiber nonwoven fabric. Here, when a flexible polyurethane foam sheet is used as the porous sheet, the density is 18 kg / m 3 -6.
A flexible polyurethane foam sheet having a thickness of about 5 kg / m 3 and a thickness of about 2 to 10 mm is preferable. In addition, when a flexible polyurethane foam sheet having an uneven pattern formed on one side or both sides by heating and compressing in advance is used, the adsorption effect is improved.
【００１２】本発明において、多孔性シート上にラテッ
クス又は樹脂液による目止め処理層を形成することが好
ましい。これは、目止め処理層の存在により、本体
（板）との接着の際に接着剤が多孔性シート内に浸み込
むのを防止できるからである。前記ラテックスとして
は、合成ゴムラテックスもしくはアクリル樹脂ラテック
スのいずれかが挙げられる。In the present invention, it is preferable to form a filler treatment layer with a latex or a resin solution on the porous sheet. This is because the presence of the filling treatment layer can prevent the adhesive from infiltrating into the porous sheet at the time of bonding to the main body (plate). Examples of the latex include a synthetic rubber latex and an acrylic resin latex.
【００１３】[0013]
【発明の実施の形態】以下、この発明の一実施例に係る
防音床材用緩衝材の製造方法を図１（Ａ），（Ｂ）を参
照して工程順に説明する。なお、下記実施例に述べる各
構成部材の材質、数値等は一例を示すもので、これによ
って本発明の技術的範囲が特定されるものでない。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS A method of manufacturing a cushioning material for a soundproof floor according to an embodiment of the present invention will be described below in the order of steps with reference to FIGS. Note that the materials, numerical values, and the like of the respective constituent members described in the following examples are merely examples, and do not limit the technical scope of the present invention.
【００１４】まず、厚さ０．１５ｍｍの防湿紙（薄いシ
ート）１の片面に、厚さ２５μｍの低融点ポリエチレン
樹脂からなる樹脂層２をコーテイングした。つづいて、
前記樹脂層２上に、密度２７ｋｇ／ｍ3 ，硬さ１８．２
ｋｇ／３１４ｃｍ2 ，厚さ４ｍｍの軟質ポリウレタンフ
ォームシート３を形成した（図１（Ａ）参照）。First, a resin layer 2 made of a low-melting polyethylene resin having a thickness of 25 μm was coated on one surface of a moisture-proof paper (thin sheet) 1 having a thickness of 0.15 mm. Then,
On the resin layer 2, a density of 27 kg / m 3 and a hardness of 18.2
A flexible polyurethane foam sheet 3 having a thickness of 4 kg / 314 cm 2 and a thickness of 4 mm was formed (see FIG. 1A).
【００１５】次に、軟質ポリウレタンフォームシート３
側より１９０℃の加熱装置11を用いて３秒加熱圧縮し、
前記シート３側の樹脂層２表面を溶かして接着剤層４と
するとともに、防湿紙１側の樹脂層２主面はそのまま溶
かさずに残し、防音床材用緩衝材５を製造した（図１
（Ｂ）参照）。Next, the flexible polyurethane foam sheet 3
Heating and compressing for 3 seconds using a heating device 11 at 190 ° C from the side,
The surface of the resin layer 2 on the sheet 3 was melted to form an adhesive layer 4, and the main surface of the resin layer 2 on the moisture-proof paper 1 was left undissolved to produce a cushioning material 5 for soundproof flooring (FIG. 1).
(B)).
【００１６】ここで、前記加熱装置11としては、図２に
示すように、固定ロール12と、この固定ロール12と対向
して配置され前記軟質ポリウレタンフォームシート３を
加熱する加熱ロール13と、複数の支持ロール14等から構
成されている。なお、図中の付番15は防湿紙１片面に樹
脂層２を形成した積層体である。As shown in FIG. 2, the heating device 11 includes a fixed roll 12, a heating roll 13 arranged opposite to the fixed roll 12 and heating the flexible polyurethane foam sheet 3, and a plurality of heating rolls. And the like. Reference numeral 15 in the drawing denotes a laminate in which the resin layer 2 is formed on one surface of the moisture-proof paper 1.
【００１７】上記実施例によれば、防湿紙１の片面に低
融点ポリエチレン樹脂からなる樹脂層２をコーテイング
し、更に前記樹脂層２上に所定の密度，硬さを有する軟
質ポリウレタンフォームシート３を形成した後、加熱ロ
ール13により３秒加熱圧縮することにより、前記シート
３側の樹脂層２表面を溶かして接着剤層４とするととも
に、防湿紙１側の樹脂層２主面はそのまま溶かさずに残
すことができる。従って、従来の防音床材用緩衝材と比
べ、接着剤層４の存在により樹脂層２と軟質ポリウレタ
ンフォ−ムの接着を強固にするとともに、溶融せず残っ
た樹脂層２により防湿効果を期待することができる。According to the above embodiment, a resin layer 2 made of a low-melting polyethylene resin is coated on one side of the moisture-proof paper 1, and a flexible polyurethane foam sheet 3 having a predetermined density and hardness is formed on the resin layer 2. After formation, the surface of the resin layer 2 on the sheet 3 is melted into an adhesive layer 4 by heating and compressing for 3 seconds by a heating roll 13, and the main surface of the resin layer 2 on the moisture-proof paper 1 is not melted as it is. Can be left. Therefore, compared with the conventional cushioning material for soundproof flooring, the presence of the adhesive layer 4 strengthens the adhesion between the resin layer 2 and the soft polyurethane foam, and the moisture-proof effect is expected by the resin layer 2 remaining without melting. can do.
【００１８】なお、上記実施例では、加熱ロールを備え
た加熱装置により軟質ポリウレタンフォームシートを加
熱する場合について述べたが、これに限らず、図３に示
すように下型21と加熱機能を有した上型22から構成され
たプレス装置23により軟質ポリウレタンフォームシート
を加熱してもよい。但し、この場合、軟質ポリウレタン
フォームシートは上型22側に位置し薄いシートは下型に
位置するように配置する。In the above embodiment, the case where the flexible polyurethane foam sheet is heated by the heating device provided with the heating roll is described. However, the present invention is not limited to this, and as shown in FIG. The flexible polyurethane foam sheet may be heated by a press device 23 composed of the upper die 22 thus formed. However, in this case, the flexible polyurethane foam sheet is arranged on the upper mold 22 side, and the thin sheet is arranged on the lower mold.
【００１９】また、本発明に係る防音床材用緩衝材は、
図１（Ｂ）に示す構成のものに限らず、図４に示すよう
に、軟質ポリウレタンフォームシート３の表面に目止め
処理層31を形成したものでもよい。こうした構成によれ
ば、本体（板）との接着の際に接着剤が軟質ポリウレタ
ンフォームシート３に浸み込むのを防止することができ
る。Further, the cushioning material for soundproof flooring according to the present invention comprises:
The structure shown in FIG. 1 (B) is not limited to the structure shown in FIG. 4, and a soft polyurethane foam sheet 3 having a surface provided with a filler treatment layer 31 may be used. According to such a configuration, it is possible to prevent the adhesive from penetrating into the flexible polyurethane foam sheet 3 at the time of bonding to the main body (plate).
【００２０】[0020]
【発明の効果】以上詳述したように本発明によれば、薄
いシートと、この薄いシート上に形成された、該シート
と反対側の主面が接着機能を有した熱可塑性樹脂層と、
この熱可塑性樹脂層上に形成された多孔性シートとを具
備した構成とすることにより、床面から浸み出してくる
水を防止するとともに、床面の接着剤の含浸を防止しえ
る防音床材用緩衝材及びその製造方法を提供できる。As described above in detail, according to the present invention, a thin sheet, a thermoplastic resin layer formed on the thin sheet and having a main surface opposite to the sheet having an adhesive function,
By providing a structure including the porous sheet formed on the thermoplastic resin layer, it is possible to prevent water seeping out from the floor surface and prevent impregnation of the floor surface with the adhesive. A cushioning material for materials and a method for producing the same can be provided.
【図１】本発明の一実施例に係る防音床材用緩衝材の製
造方法を工程順に示す断面図。FIG. 1 is a sectional view showing a method of manufacturing a cushioning material for a soundproof flooring according to an embodiment of the present invention in the order of steps.
【図２】本発明に係る防音床材用緩衝材の加熱工程に使
用される加熱装置の説明図。FIG. 2 is an explanatory view of a heating device used in a heating step of a cushioning material for soundproof flooring according to the present invention.
【図３】本発明に係る防音床材用緩衝材の加熱工程に使
用されるプレス装置の説明図。FIG. 3 is an explanatory view of a press device used in a heating step of the cushioning material for soundproof flooring according to the present invention.
【図４】本発明の他の実施例に係る防音床材用緩衝材の
断面図。FIG. 4 is a cross-sectional view of a cushioning material for soundproof flooring according to another embodiment of the present invention.
１…防湿紙（薄いシート）、 ２…樹脂層、 ３…軟質ポリウレタンフォームシート、 ４…接着剤層、 11…加熱装置、 12…固定ロール、 13…加熱ロール、 14…支持ロール、 21…下型、 22…上型、 23…プレス装置、 31…目止め処理層。 DESCRIPTION OF SYMBOLS 1 ... Moistureproof paper (thin sheet), 2 ... Resin layer, 3 ... Soft polyurethane foam sheet, 4 ... Adhesive layer, 11 ... Heating device, 12 ... Fixed roll, 13 ... Heating roll, 14 ... Support roll, 21 ... Bottom Mold, 22 ... Upper mold, 23 ... Press machine, 31 ... Filler treatment layer.
───────────────────────────────────────────────────── フロントページの続き Ｆターム(参考） 4F100 AK01B AK07C AK253 AK41C AK51C AN023 AR00C AT00A BA02 BA07 BA10A BA103 DD08C DG10A DG15A DG15C DJ00C DJ01C EC052 EJ192 EJ422 EJ81C GB07 HB21C JB16B JD04A JD05 JK13C JL11B JM01C YY00A ────────────────────────────────────────────────── ─── front page of continued F-term (reference) 4F100 AK01B AK07C AK253 AK41C AK51C AN023 AR00C AT00A BA02 BA07 BA10A BA103 DD08C DG10A DG15A DG15C DJ00C DJ01C EC052 EJ192 EJ422 EJ81C GB07 HB21C JB16B JD04A JD05 JK13C JL11B JM01C YY00A
Claims (7)
された、該シートと反対側の主面が接着機能を有した熱
可塑性樹脂層と、この熱可塑性樹脂層上に形成された多
孔性シートとを具備することを特徴とする防音床材用緩
衝材。1. A thin sheet, a thermoplastic resin layer formed on the thin sheet and having a main surface opposite to the sheet having an adhesive function, and a porous layer formed on the thermoplastic resin layer. A cushioning material for soundproof flooring, comprising a sheet.
紙、洋紙等の紙類、あるいは目付量が１５ｇ／ｍ2 〜７
０ｇ／ｍ2 の薄い不織布のいずれかであることを特徴と
する請求項１記載の防音床材用緩衝材。2. The thin sheet is made of paper such as moisture-proof paper, kraft paper, or Western paper, or has a basis weight of 15 g / m 2 to 7 g / m 2.
Insulating floor members for cushioning material according to claim 1, wherein a is any one of a thin nonwoven of 0 g / m 2.
フォームシート、半硬質ポリウレタンフォームシート、
ポリプロピレン、ポリエステル等の長繊維不織布、短繊
維不織布のいずれかであることを特徴とする請求項１記
載の防音床材用緩衝材。3. The porous sheet is a flexible polyurethane foam sheet, a semi-rigid polyurethane foam sheet,
2. The cushioning material for soundproof flooring according to claim 1, wherein the cushioning material is one of a long fiber nonwoven fabric and a short fiber nonwoven fabric such as polypropylene and polyester.
片面に凹凸模様が形成されていることを特徴とする請求
項１記載の防音床材用緩衝材。4. The cushioning material for soundproof flooring according to claim 1, wherein the porous sheet has a flat plate or an uneven pattern formed on at least one surface.
脂液による目止め処理層を有することを特徴とする請求
項１記載の防音床材用緩衝材。5. The cushioning material for a soundproof flooring according to claim 1, further comprising a filler treatment layer made of a latex or a resin liquid on the porous sheet.
もしくはアクリル樹脂ラテックスのいずれかであること
を特徴とする請求項４記載の防音床材用緩衝材。6. The cushioning material according to claim 4, wherein the latex is one of a synthetic rubber latex and an acrylic resin latex.
層する工程と、前記熱可塑性樹脂層上に多孔性シートを
形成する工程と、前記多孔性シート面を加熱した状態で
圧縮し、前記多孔性シート側の熱可塑性樹脂層は溶融さ
せかつ前記薄いシート側の熱可塑性樹脂層は溶融させず
にそのまま残す工程とを具備することを特徴とする防音
床材用緩衝材の製造方法。7. A step of laminating a thermoplastic resin layer on one side of a thin sheet, a step of forming a porous sheet on the thermoplastic resin layer, and compressing the porous sheet surface in a heated state, Melting the thermoplastic resin layer on the porous sheet side and leaving the thin thermoplastic resin layer on the thin sheet side without melting.