JP2000072970A - Thermoplastic resin composition and hair brush formed thereof - Google Patents
Thermoplastic resin composition and hair brush formed thereofInfo
- Publication number
- JP2000072970A JP2000072970A JP24492798A JP24492798A JP2000072970A JP 2000072970 A JP2000072970 A JP 2000072970A JP 24492798 A JP24492798 A JP 24492798A JP 24492798 A JP24492798 A JP 24492798A JP 2000072970 A JP2000072970 A JP 2000072970A
- Authority
- JP
- Japan
- Prior art keywords
- thermoplastic resin
- resin composition
- polybutylene terephthalate
- hair brush
- copolymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は、トルマリン微粒子
含有熱可塑性樹脂組成物及びその熱可塑性樹脂組成物を
射出成形して得られたヘヤーブラシに関するものであ
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a thermoplastic resin composition containing tourmaline fine particles and a hair brush obtained by injection molding the thermoplastic resin composition.
【0002】[0002]
【従来の技術】近年、活性電子は生体細胞を賦活し、生
体に対して好影響を与えることが注目されている。この
活性電子を、例えば、血行の促進、新陳代謝の促進など
の利用する研究が積極的になされている。2. Description of the Related Art In recent years, it has been noted that active electrons activate living cells and have a favorable effect on living organisms. Research has been actively conducted on utilizing the active electrons, for example, to promote blood circulation and metabolism.
【0003】このような活性電子を放出する物質の1つ
として、天然産のトルマリンが見いだされている。この
トルマリンは、活性電子を放出すると共に、結晶の両端
にプラス極マイナス極が自発的に生じ分極電圧が生じて
構成される電場内に位置する動植物の細胞に微弱電流を
流し、細胞の活性化を促す。[0003] Naturally occurring tourmaline has been found as one of the substances that emit such active electrons. This tourmaline emits active electrons, generates positive and negative poles spontaneously at both ends of the crystal, and generates a polarization voltage. Prompt.
【0004】一方、ヘヤーブラシは、近年、ブラッシン
グ性能以外に種々の機能(例えば帯電防止性能を付与す
ることによりゴミの付着を抑制する)が付与されてい
る。しかし、頭皮、毛髪等身体の一部に作用し健康上の
快適感を与えるものは、未だ市販されていない。On the other hand, in recent years, the hair brush has been provided with various functions other than the brushing performance (for example, by suppressing the adhesion of dust by imparting antistatic performance). However, products that act on a part of the body, such as the scalp and hair, and give a feeling of health comfort have not yet been marketed.
【0005】[0005]
【発明が解決しようとする課題】本発明者らはかかる従
来技術の有する問題点を解決すべく鋭意研究した結果、
本発明を完成したものであって、その目的とするところ
は、従来のヘヤーブラシとは異なり、鉱石であるトルマ
リンを使うことにより、頭皮、毛髪等身体の一部に作用
し健康上の快適感を与えることができる熱可塑性樹脂組
成物およびそれからなるヘヤーブラシを提供することを
目的とする。SUMMARY OF THE INVENTION The present inventors have made intensive studies to solve the problems of the prior art, and as a result,
The purpose of the present invention is to complete the present invention and, unlike conventional hair brushes, use tourmaline, which is an ore, to act on a part of the body such as the scalp and hair to provide a comfortable feeling of health. It is an object of the present invention to provide a thermoplastic resin composition which can be provided and a hair brush comprising the same.
【0006】[0006]
【課題を解決するための手段】すなわち本発明は、熱可
塑性樹脂に対し、粉末状トルマリン鉱石を20重量部以
下含有してなることを特徴とする熱可塑性樹脂組成物及
び射出成形して得られることを特徴とするヘヤーブラシ
である。That is, the present invention is obtained by injection molding a thermoplastic resin composition characterized by containing 20 parts by weight or less of powdered tourmaline ore with respect to the thermoplastic resin. It is a hair brush characterized by the above-mentioned.
【0007】[0007]
【発明の実施の形態】以下、本発明を詳細に説明する。
本発明に用いられる熱可塑性樹脂は、ポリアミド、熱可
塑性ポリエステル、ポリエチレン、ポリプロピレン、A
BS、酢酸ビニル、塩化ビニル、ポリアセタール、ポリ
カーボネート、ポリフェニレンエーテル等があげられる
が、通常ヘヤーブラシの材料として使用されているポリ
アミド、熱可塑性ポリエステル、ポリエチレン、ポリプ
ロピレン、ABS、エチレン−エチルアクリレート共重
合体及びエチレン−酢酸ビニル共重合体が好ましい。BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, the present invention will be described in detail.
The thermoplastic resin used in the present invention includes polyamide, thermoplastic polyester, polyethylene, polypropylene, A
Examples include BS, vinyl acetate, vinyl chloride, polyacetal, polycarbonate, and polyphenylene ether. Polyamide, thermoplastic polyester, polyethylene, polypropylene, ABS, ethylene-ethyl acrylate copolymer, and ethylene which are usually used as a material for a hair brush are used. -Vinyl acetate copolymers are preferred.
【0008】ポリアミドの好ましい具体例としては、市
場に出回っているナイロン6、ナイロン6・6及びナイ
ロン12があげられる。Preferred specific examples of polyamides include nylon 6, nylon 6.6 and nylon 12, which are on the market.
【0009】また、熱可塑性ポリエステルの好ましい例
としては、ポリブチレンテレフタレート及びポリブチレ
ンテレフタレート系共重合体があげられる。Preferred examples of the thermoplastic polyester include polybutylene terephthalate and a polybutylene terephthalate-based copolymer.
【0010】ポリブチレンテレフタレート系共重合体と
は、ダイマー酸、テトラメチレングリコール系重合体ま
たはラクトン系重合体を共重合して得られる重合体であ
る。[0010] The polybutylene terephthalate copolymer is a polymer obtained by copolymerizing dimer acid, tetramethylene glycol polymer or lactone polymer.
【0011】ダイマー酸を共重合したポリブチレンテレ
フタレート系共重合体とは、テレフタル酸又はそのエス
テル形成性誘導体及び水素添加ダイマー酸又はそのエス
テル形成性誘導体を主体とする酸成分と1,4−ブタン
ジオールを主体とするグリコール成分とを重縮合してな
るものである。The polybutylene terephthalate copolymer obtained by copolymerizing dimer acid includes an acid component mainly composed of terephthalic acid or an ester-forming derivative thereof and a hydrogenated dimer acid or an ester-forming derivative thereof, and 1,4-butane. It is obtained by polycondensing a glycol component mainly composed of a diol.
【0012】ダイマー酸を共重合したポリブチレンテレ
フタレート系共重合体の酸成分の1つである水素添加ダ
イマー酸は、不飽和脂肪酸の粘土触媒による低重合体か
ら分離及び水素添加によってトリマー酸、モノマー酸等
の副生成物を除去した後に得られ、純度としては99重
量%以上であることが好ましい。Hydrogenated dimer acid, which is one of the acid components of a polybutylene terephthalate copolymer obtained by copolymerizing dimer acid, is separated from a low polymer of an unsaturated fatty acid by a clay catalyst and is hydrogenated to trimer acid and monomer. It is obtained after removing by-products such as acids, and the purity is preferably 99% by weight or more.
【0013】好ましい具体例としては、ユニケマ社製の
PRIPOL1008(炭素数36で、芳香族タイプ/
脂環族タイプ/直鎖脂肪族タイプ=9/54/37(モ
ル%)のダイマ−酸)、PRIPOL1009(炭素数
36で13/64/23(モル%)のダイマー酸)、さ
らにエステル形成性誘導体としてユニケマ社製のPRI
PLAST3008(PRIPOL1008のジメチル
エステル)があげられる。As a preferred specific example, PRIPOL1008 (36 carbon atoms, aromatic type /
Alicyclic type / linear aliphatic type = 9/54/37 (mol%) dimer acid), PRIPOL 1009 (36/23 / mol (36 mol% dimer acid with 36 carbon atoms)), and further ester-forming properties PRI manufactured by Unichema as a derivative
PLAST3008 (dimethyl ester of PRIPOL1008).
【0014】ダイマー酸を共重合したポリブチレンテレ
フタレート系共重合体の酸成分の1つである水素添加ダ
イマー酸共重合組成は、1〜20モル%であることが好
ましい。The hydrogenated dimer acid copolymer composition, which is one of the acid components of the polybutylene terephthalate copolymer obtained by copolymerizing dimer acid, is preferably 1 to 20 mol%.
【0015】他のポリブチレンテレフタレート系共重合
体としてはテトラメチレングリコール系重合体をジオー
ル成分として共重合したポリエーテルエステル系エラス
トマーがあげられる。Other polybutylene terephthalate copolymers include polyetherester elastomers obtained by copolymerizing a tetramethylene glycol polymer as a diol component.
【0016】さらに、ポリブチレンテレフタレートにカ
プロラクトンを共重合したポリエステルエステル系エラ
ストマーがあげられる。Further, there is a polyester ester elastomer obtained by copolymerizing caprolactone with polybutylene terephthalate.
【0017】本発明で使用する粉末状トルマリン鉱石の
粒径は、ヘヤーブラシの靱性の点で100μm以下が好
ましい。The particle size of the powdered tourmaline ore used in the present invention is preferably 100 μm or less from the viewpoint of the toughness of the hair brush.
【0018】本発明で使用する粉末状トルマリン鉱石の
組成式は、 MX3B3Al3(AlSi2O9)3(O,OH,
F)4(M=NaまたはCa、X=Mg,Fe,Li,
Mn) で表されるものである。The composition of the powdered tourmaline ore used in the present invention is MX3B3Al3 (AlSi2O9) 3 (O, OH,
F) 4 (M = Na or Ca, X = Mg, Fe, Li,
Mn).
【0019】トルマリンは、天然品としては、ブラジ
ル、旧ソ連ウラル、中国の雲南省等で産出されるが、現
在では人工的に結晶を合成することが出来、本発明にお
いては、このような人工的に得られるトルマリンも用い
ることが出来る。Although tourmaline is produced as a natural product in Brazil, the former Soviet Ural, Yunnan Province in China, etc., it is now possible to synthesize crystals artificially. Tourmaline which can be obtained in a special manner can also be used.
【0020】トルマリンは、結晶の単位格子のプラス電
荷の中心と、マイナス電荷の中心が本来位置すべき位置
から大きくずれているため、対称する結晶の両端に電極
を作り電位が永久に保持され、永久電極を保有する。こ
の両極間には、数万エレクトロンボルトにも達する分極
電圧が生じ、これによりその構成される電場内に位置す
る動植物の細胞に神経系統を制御しているのと同一の波
長11μm、0.06mAの微弱電流を流すため細胞の
活性化を促す。また、微粒子状のトルマリンからは活性
電子が放出されることはすでに確認されている。In tourmaline, the center of the positive charge and the center of the negative charge in the unit cell of the crystal are largely displaced from the position where they should be located. Therefore, electrodes are formed at both ends of the symmetrical crystal, and the potential is permanently maintained. Holds permanent electrodes. Between the two poles, a polarization voltage of up to tens of thousands of electron volts is generated, whereby the same wavelength of 11 μm and 0.06 mA as controlling the nervous system is applied to the cells of animals and plants located in the electric field constituted by the electrodes. To activate the cells to pass a weak current. In addition, it has been already confirmed that active electrons are emitted from the fine-particle tourmaline.
【0021】このため、前記熱可塑性樹脂に粉末状トル
マリン鉱石が含有されていることによって、本ヘヤーブ
ラシでブラッシングすると、微弱電流や活性電子が頭皮
等の細胞の活性化を促す。For this reason, since powdery tourmaline ore is contained in the thermoplastic resin, when brushing is performed with the present hair brush, a weak current and active electrons promote activation of cells such as the scalp.
【0022】本発明において、粉末状トルマリン鉱石の
配合量は、熱可塑性樹脂100重量部に対し、20重量
部以下であることが肝要である。20重量部を超える場
合、樹脂組成物自体の靱性が低下しヘヤーブラシとして
使用できない。また、トルマリンの前記効果を得るため
には、0.5重量部以上が好ましい。In the present invention, it is important that the amount of the powdered tourmaline ore is not more than 20 parts by weight based on 100 parts by weight of the thermoplastic resin. If the amount exceeds 20 parts by weight, the toughness of the resin composition itself is reduced, and the resin composition cannot be used as a hair brush. In order to obtain the above effects of tourmaline, the amount is preferably 0.5 parts by weight or more.
【0023】本発明の組成物には、本発明の目的を損な
わない範囲で通常の添加剤や少量の強化材、例えば酸化
防止剤及び熱安定剤(例えばヒンダードフェノール、ヒ
ドロキノン、チオエーテル、ホスファイト類及びこれら
の置換体及びその組合せを含む)、紫外線吸収剤(例え
ばレゾルシノール、サリシレート、ベンゾトリアゾー
ル、ベンゾフェノン等)、結晶核剤(例えばカオリン、
タルク等)、滑剤及び離型剤(例えばモンタン酸及びそ
の塩、ステアリン酸及びその塩、ステアリルアルコー
ル、ステアリルアミド、シリコン樹脂等)、染料(例え
ばニトロシン等)及び顔料(例えばカーボンブラック、
硫化カドミウム、フタロシアニン等)を含む着色剤、添
加剤添着液(例えばシリコンオイル等)、強化材(ガラ
ス繊維、炭素繊維、ウィスカー等)等を1種以上添加す
ることが出来る。The composition of the present invention contains conventional additives and small amounts of reinforcing agents such as antioxidants and heat stabilizers (eg, hindered phenols, hydroquinones, thioethers, phosphites) as long as the objects of the present invention are not impaired. , And their substituents and combinations thereof), ultraviolet absorbers (eg, resorcinol, salicylate, benzotriazole, benzophenone, etc.), nucleating agents (eg, kaolin,
Talc, etc.), lubricants and release agents (e.g., montanic acid and its salts, stearic acid and its salts, stearyl alcohol, stearylamide, silicone resins, etc.), dyes (e.g., nitrosine, etc.) and pigments (e.g., carbon black,
One or more kinds of coloring agents containing cadmium sulfide, phthalocyanine, etc., additives impregnating liquids (eg, silicone oil), reinforcing materials (glass fibers, carbon fibers, whiskers, etc.) and the like can be added.
【0024】さらに、帯電防止性を付与する目的で、ケ
ッチェンブラックに代表されるカーボンブラック、導電
性ウィスカー、金属酸化物、ポリエチレングリコールメ
タクリレート共重合体やポリエーテルエステルアミド、
ポリエーテルアミドイミド、ポリエチレンオキシド−エ
ピクロルヒドリン共重合体等の高分子型帯電防止剤、グ
リセリン脂肪酸エステルやアルキルスルホン酸塩、テト
ラアルキルアンモニウム塩、アルキルベタイン等の低分
子系帯電防止剤を1種以上添加することが出来る。Further, for the purpose of imparting antistatic properties, carbon black represented by Ketjen black, conductive whiskers, metal oxides, polyethylene glycol methacrylate copolymers and polyetheresteramides,
Add at least one polymer type antistatic agent such as polyether amide imide, polyethylene oxide-epichlorohydrin copolymer, and low molecular type antistatic agent such as glycerin fatty acid ester, alkyl sulfonate, tetraalkylammonium salt and alkyl betaine. You can do it.
【0025】本発明の熱可塑性樹脂組成物は射出成形品
となるまで、すべての成分が充分に分散されていること
が好ましい。このための方法としては、例えば異方向回
転2軸押出機を用いてペレット状の樹脂を作り、射出成
形工程に供する方法がある。It is preferable that all the components of the thermoplastic resin composition of the present invention are sufficiently dispersed until an injection molded article is obtained. As a method for this, for example, there is a method in which a pellet-shaped resin is produced by using a different-direction rotating twin-screw extruder and is subjected to an injection molding process.
【0026】[0026]
【発明の効果】以上説明したように、本発明の熱可塑性
樹脂組成物およびそれからなるヘヤーブラシは、粉末状
トルマリン鉱石を含有することにより、ブラッシング時
に頭皮等の細胞に刺激を与えることが出来る。As described above, the thermoplastic resin composition of the present invention and the hair brush comprising the same can stimulate cells such as the scalp during brushing by containing powdered tourmaline ore.
【0027】[0027]
【実施例】以下、実施例によって本発明を具体的に説明
する。尚、物性評価は、以下の方法に従って行った。The present invention will be specifically described below with reference to examples. In addition, physical property evaluation was performed according to the following method.
【0028】引張破断伸度:ASTM D638 衝撃強度:ASTM D256 アイゾット、ノッチ付
き、1/4インチTensile elongation at break: ASTM D638 Impact strength: ASTM D256 Izod, notched, 1/4 inch
【0029】(ダイマー酸を共重合したポリブチレンテ
レフタレート系共重合体の製造例)テレフタル酸ジメチ
ル54kg、水素添加ダイマー酸(ユニケマ社製、PR
IPLAST3008)18.4kg、1,4−ブタン
ジオール41kg及びエステル交換及び重合触媒として
テトラ−n−ブチルチタネート0.07kgをエステル
交換槽に仕込み、210℃に加熱して生成するメタノー
ルを系外に溜去し、エステル交換を行った。メタノール
溜去がほぼ完了してから反応生成物を重合槽に移し、1
時間かけて温度250℃、真空度0.5mmHg迄もっ
ていき、その後重縮合を行い、ダイマー酸を共重合した
ポリブチレンテレフタレート系共重合体を得た。(Production Example of Polybutylene Terephthalate Copolymer Copolymerized with Dimer Acid) 54 kg of dimethyl terephthalate, hydrogenated dimer acid (PR, manufactured by Unichema Co., Ltd.)
IPLAST3008) 18.4 kg, 41 kg of 1,4-butanediol and 0.07 kg of tetra-n-butyl titanate as a transesterification and polymerization catalyst were charged into a transesterification tank, and methanol produced by heating to 210 ° C. was collected outside the system. And transesterified. After the methanol distillation is almost completed, the reaction product is transferred to the polymerization tank and
Over a period of time, the temperature was raised to 250 ° C. and the degree of vacuum to 0.5 mmHg, followed by polycondensation to obtain a polybutylene terephthalate copolymer in which dimer acid was copolymerized.
【0030】実施例1〜12 上記製造例で得られたダイマー酸を共重合したポリブチ
レンテレフタレート系共重合体、テトラメチレングリコ
ールを共重合したポリブチレンテレフタレート系共重合
体(ペルプレンP−150B、東洋紡社製)、カプロラ
クトンを共重合したポリブチレンテレフタレート系共重
合体(ペルプレンS−2001、東洋紡社製)、ポリブ
チレンテレフタレート(PBT724、カネボウ合繊社
製)、ナイロン6(MC120、カネボウ合繊社製)、
ナイロン6・6(レオナ1300、旭化成社製)、ナイ
ロン12(ダイアミドL1801、ダイセル・ヒュルス
社製)、ポリエチレン(ウルトゼックス2010J、三
井化学社製)、ポリプロピレン(J101、グランドポ
リマー社製)、ABS(GA−501、住友ダウ社
製)、エチレン−エチルアクリレート共重合体(EVA
FLEX−EEA A−704 三井・デュポンポリケ
ミカル社製))及びエチレン−酢酸ビニル共重合体(E
VAFLEX EV460)100重量部に対し、粉末
状トルマリン鉱石(新素材開発社製)を2重量部配合
し、スクリュー径30mmの同方向2軸混練押出機(日
本製鋼社製 TEX−30α)で溶融混練し、ペレット
を得た。Examples 1 to 12 A polybutylene terephthalate copolymer obtained by copolymerizing the dimer acids obtained in the above production examples and a polybutylene terephthalate copolymer obtained by copolymerizing tetramethylene glycol (Perprene P-150B, Toyobo Co., Ltd.) ), A polybutylene terephthalate copolymer obtained by copolymerizing caprolactone (Perprene S-2001, manufactured by Toyobo Co., Ltd.), polybutylene terephthalate (PBT724, manufactured by Kanebo Synthetic), nylon 6 (MC120, manufactured by Kanebo Synthetic),
Nylon 6.6 (Leona 1300, manufactured by Asahi Kasei Corporation), Nylon 12 (Diamid L1801, manufactured by Daicel Huls), polyethylene (Ultzex 2010J, manufactured by Mitsui Chemicals), polypropylene (J101, manufactured by Grand Polymer), ABS ( GA-501, manufactured by Sumitomo Dow), ethylene-ethyl acrylate copolymer (EVA
FLEX-EEA A-704 (manufactured by DuPont-Mitsui Polychemicals)) and ethylene-vinyl acetate copolymer (E
2 parts by weight of powdered tourmaline ore (manufactured by New Material Development Co., Ltd.) is blended with 100 parts by weight of VAFLEX EV460) and melt-kneaded with a biaxial kneading extruder having a screw diameter of 30 mm (TEX-30α manufactured by Nippon Steel Corporation). Then, a pellet was obtained.
【0031】得られたペレットを減圧乾燥後、射出成形
に供し試験片を得、物性試験に供した。また、図1に示
す形状のヘヤーブラシを成形し、頭髪のブラッシングテ
ストを実施した。結果を表1に示した。After the obtained pellets were dried under reduced pressure, they were subjected to injection molding to obtain test specimens, which were subjected to physical property tests. Further, a hair brush having the shape shown in FIG. 1 was molded, and a hair brushing test was performed. The results are shown in Table 1.
【0032】[0032]
【表1】 [Table 1]
【0033】実施例13、14 比較例1 実施例1で使用したダイマー酸を共重合したポリブチレ
ンテレフタレート系共重合体95重量部、帯電防止剤と
してカーボンブラック(ケッチェンブラックEC600
JD ライオンアクゾ社製)5重量部に対し、実施例1
で使用した粉末状トルマリン鉱石を表2に示す組成で配
合し、実施例1と同様の方法でペレットを得、評価し
た。結果も表2に示した。Examples 13 and 14 Comparative Example 1 95 parts by weight of a polybutylene terephthalate copolymer obtained by copolymerizing dimer acid used in Example 1 and carbon black (Ketjen Black EC600) as an antistatic agent
Example 1 for 5 parts by weight (JD Lion Akzo)
The powdered tourmaline ore used in the above was blended with the composition shown in Table 2, and pellets were obtained and evaluated in the same manner as in Example 1. The results are also shown in Table 2.
【0034】[0034]
【表2】 [Table 2]
【0035】[0035]
【発明の効果】実施例1〜14より、本発明の熱可塑性
樹脂組成物トルマリン微粒子を含有しており、頭髪ブラ
ッシング時に上述したトルマリンの効果を与える。From the results of Examples 1 to 14, the thermoplastic resin composition of the present invention contains the fine particles of tourmaline, and gives the above-mentioned effects of tourmaline during hair brushing.
【図1】本発明の実施例で使用したヘヤーブラシであ
る。FIG. 1 shows a hair brush used in an embodiment of the present invention.
───────────────────────────────────────────────────── フロントページの続き (72)発明者 山本 正樹 山口県防府市鐘紡町4番1号カネボウ合繊 株式会社内 Fターム(参考) 3B202 AA11 AB00 EA01 EA05 EB10 4J002 AA011 BB031 BB061 BB071 BB121 BD041 BF021 BN151 CB001 CF001 CF071 CF101 CF191 CG001 CH071 CL001 CL011 CL031 DJ006 DK006 FD010 FD050 FD060 FD070 FD090 FD100 FD160 FD170 GC00 ──────────────────────────────────────────────────続 き Continuing from the front page (72) Inventor Masaki Yamamoto 4-1 Kanebo-cho, Hofu-shi, Yamaguchi Pref. CF001 CF071 CF101 CF191 CG001 CH071 CL001 CL011 CL031 DJ006 DK006 FD010 FD050 FD060 FD070 FD090 FD100 FD160 FD170 GC00
Claims (8)
状トルマリン鉱石を20重量部以下含有してなることを
特徴とする熱可塑性樹脂組成物。1. A thermoplastic resin composition comprising 20 parts by weight or less of powdered tourmaline ore with respect to 100 parts by weight of a thermoplastic resin.
可塑性ポリエステル、ポリエチレン、ポリプロピレン、
ABS、エチレン−エチルアクリレート共重合体及びエ
チレン−酢酸ビニル共重合体である請求項第1記載の熱
可塑性樹脂組成物。2. A thermoplastic resin composition comprising: polyamide, thermoplastic polyester, polyethylene, polypropylene,
The thermoplastic resin composition according to claim 1, wherein the thermoplastic resin composition is ABS, an ethylene-ethyl acrylate copolymer, and an ethylene-vinyl acetate copolymer.
・6及びナイロン12である請求項2記載の熱可塑性樹
脂組成物。3. The polyamide is nylon 6, nylon 6.
The thermoplastic resin composition according to claim 2, which is 6 and nylon 12.
テレフタレート及びポリブチレンテレフタレート系共重
合体である請求項第3項記載の熱可塑性樹脂組成物。4. The thermoplastic resin composition according to claim 3, wherein the thermoplastic polyester is a polybutylene terephthalate or a polybutylene terephthalate copolymer.
が、ダイマー酸、テトラメチレングリコール系重合体及
びラクトン系重合体を共重合して得られる重合体である
請求項第4項記載の組成物。5. The composition according to claim 4, wherein the polybutylene terephthalate-based copolymer is a polymer obtained by copolymerizing a dimer acid, a tetramethylene glycol-based polymer and a lactone-based polymer.
チレンテレフタレート系共重合体が、テレフタル酸又は
そのエステル形成性誘導体及び水素添加ダイマー酸又は
そのエステル形成性誘導体を酸成分と1,4−ブタンジ
オールをグリコール成分とから得られるポリブチレンテ
レフタレート系共重合体である請求項第5記載の組成
物。6. A polybutylene terephthalate-based copolymer obtained by copolymerizing dimer acid, comprising terephthalic acid or its ester-forming derivative and hydrogenated dimer acid or its ester-forming derivative as an acid component and 1,4- The composition according to claim 5, which is a polybutylene terephthalate copolymer obtained from butanediol and a glycol component.
状トルマリン鉱石を0.5〜20重量部含有した熱可塑
性樹脂組成物である請求項第1項記載の熱可塑性樹脂組
成物。7. The thermoplastic resin composition according to claim 1, which is a thermoplastic resin composition containing 0.5 to 20 parts by weight of powdered tourmaline ore based on 100 parts by weight of the thermoplastic resin.
鉱石を含有してなる熱可塑性樹脂組成物によって射出成
形して得られることを特徴とするヘヤーブラシ。8. A hair brush obtained by injection molding a thermoplastic resin composition with a thermoplastic resin composition containing powdered tourmaline ore.