ITVI20110276A1 - THERMOPLASTIC COMPOUND FOR SINGLE LAYERED TUBES AND SINGLE LAYER TUBE INCLUDING THIS COMPOUND - Google Patents
THERMOPLASTIC COMPOUND FOR SINGLE LAYERED TUBES AND SINGLE LAYER TUBE INCLUDING THIS COMPOUND Download PDFInfo
- Publication number
- ITVI20110276A1 ITVI20110276A1 IT000276A ITVI20110276A ITVI20110276A1 IT VI20110276 A1 ITVI20110276 A1 IT VI20110276A1 IT 000276 A IT000276 A IT 000276A IT VI20110276 A ITVI20110276 A IT VI20110276A IT VI20110276 A1 ITVI20110276 A1 IT VI20110276A1
- Authority
- IT
- Italy
- Prior art keywords
- compound
- modifying agent
- total weight
- percentage
- compound according
- Prior art date
Description
D E S C R I Z I O N E DESCRIPTION
Campo di applicazione Field of application
La presente invenzione à ̈ generalmente applicabile al settore tecnico dei compound termoplastici ed ha particolarmente per oggetto un compound termoplastico per la realizzazione di tubi monostrato. The present invention is generally applicable to the technical sector of thermoplastic compounds and particularly relates to a thermoplastic compound for the production of single-layer pipes.
L’invenzione ha altresì per oggetto un tubo monostrato comprendente il suddetto compound. The invention also relates to a single-layer pipe comprising the aforementioned compound.
Stato della Tecnica State of the art
Sono note diverse formulazioni di compound termoplastici utilizzabili per la realizzazione di tubi tecnici aventi applicazioni in specifici settori anche molto differenti tra loro. Various formulations of thermoplastic compounds are known which can be used for the production of technical pipes having applications in specific sectors which are also very different from each other.
Ad esempio, neH’ambito di installazioni di impianti elettrici à ̈ comune utilizzare sistemi di canalizzazione di cavi formati da tubi corrugati o spiralati destinati al passaggio dei cavi elettrici. For example, in the field of electrical system installations it is common to use cable ducting systems formed by corrugated or spiral tubes intended for the passage of electrical cables.
Le caratteristiche strutturali, in termini di resistenza meccanica e proprietà ignifughe e termoresistenza, sono opportunamente dimensionate in accordo a precisi standard in funzione dei settori di applicazione. The structural characteristics, in terms of mechanical resistance and fireproof and heat resistance properties, are suitably sized according to precise standards according to the application sectors.
Generalmente, i noti tubi, sia corrugati che spiralati, sono relativamente rigidi e non possono essere curvati, ovvero presentano curvabilità massima estremamente limitata. Generally, the known tubes, both corrugated and spiral, are relatively rigid and cannot be bent, ie they have extremely limited maximum bending.
Inoltre, in caso di eccessiva curvatura sono soggetti al fenomeno del kinking , ovvero si determina una strozzatura in corrispondenza della zona di curvatura con riduzione della sezione utile di passaggio. Furthermore, in the event of excessive curvature they are subject to the phenomenon of kinking, that is, a constriction occurs in correspondence with the curvature area with a reduction of the useful passage section.
Di conseguenza, per la realizzazione del sistema di canalizzazione occorre ricorrere a raccordi o curve atti a collegare i tratti rettilinei, riducendo la flessibilità ed il numero di configurazioni realizzabili. Consequently, for the realization of the ducting system it is necessary to resort to fittings or curves able to connect the straight sections, reducing flexibility and the number of configurations that can be created.
Non da ultimo, la presenza di pareti laterali ad elevato attrito, come nel caso di tubi corrugati, può comportare difficoltà nell'introduzione dei cavi, in particolare per tubi di diametro ridotto. Last but not least, the presence of high friction side walls, as in the case of corrugated pipes, can cause difficulties in the introduction of cables, especially for pipes with a reduced diameter.
La necessità di disporre tubi in materiale polimerico provvisti di elevate resistenza e flessibilità , unitamente ad alta resistenza al kinking à ̈ sentita anche in settori tecnici molto distanti da quello sopra citato. The need to have pipes in polymeric material with high resistance and flexibility, together with high resistance to kinking is also felt in technical sectors very far from the one mentioned above.
Ad esempio, nel settore medicale, e più specificamente in quello dentale, à ̈ noto l'utilizzo di cannule per la suzione di saliva formate da un tubo in materiale polimerico avente diametro relativamente contenuto, generalmente di pochi millimetri. For example, in the medical sector, and more specifically in the dental sector, the use of saliva suction cannulas formed by a tube made of polymeric material having a relatively small diameter, generally of a few millimeters, is known.
Anche per tali applicazioni à ̈ necessario che il tubo presenti adeguata resistenza meccanica unitamente ad elevate flessibilità e resistenza al kinking. Also for these applications it is necessary that the pipe has adequate mechanical resistance together with high flexibility and resistance to kinking.
Ad esempio, da W020091 50073 à ̈ nota una cannula il cui tubo di suzione à ̈ realizzato per estrusione a partire da un compound comprendente PVC plasticizzato ed un materiale espandibile costituito da microsfere termicamente espandibili. For example, from W020091 50073 a cannula is known whose suction tube is made by extrusion starting from a compound comprising plasticised PVC and an expandable material consisting of thermally expandable microspheres.
Tale nota soluzione, oltre ad essere relativamente costosa, Ã ̈ risultata poco affidabile ed economicamente svantaggiosa. This known solution, in addition to being relatively expensive, was not very reliable and economically disadvantageous.
Presentazione dell’invenzione Presentation of the invention
Scopo generale della presente invenzione à ̈ quello di superare gli inconvenienti della tecnica nota sopra riscontrati, realizzando un compound termoplastico per la realizzazione di tubi monostrato ad elevata memoria di forma. The general purpose of the present invention is that of overcoming the drawbacks of the prior art found above, realizing a thermoplastic compound for the production of single-layer pipes with high shape memory.
Uno scopo particolare à ̈ quello di mettere a disposizione un compound termoplastico che consenta di ottenere tubi monostrato che presentino flessibilità relativamente elevata e che allo stesso tempo abbiano basso ritorno elastico per poter essere curvati con semplicità , mantenendo sostanzialmente la forma impartita. A particular purpose is to provide a thermoplastic compound which allows to obtain single-layer pipes which have relatively high flexibility and which at the same time have low elastic recovery in order to be easily bent, while substantially maintaining the given shape.
Un ulteriore scopo del presente trovato à ̈ quello di mettere a disposizione un compound termoplastico che consenta di realizzare tubi monostrato flessibili e che presentino elevata resistenza al fenomeno del kinking. A further object of the present invention is to provide a thermoplastic compound which allows to produce flexible single-layer pipes and which exhibit high resistance to the phenomenon of kinking.
Non ultimo scopo del presente trovato à ̈ quello di mettere a disposizione un compound termoplastico che consenta la realizzazione di tubi monostrato ad elevata finitura superficiale utilizzabili in diversi settori di applicazione, come ad esempio tubi passacavi in impianti elettrici o per la realizzazione di cannule per usi odontoiatrici. Not least object of the present invention is to provide a thermoplastic compound that allows the production of single-layer pipes with a high surface finish that can be used in various sectors of application, such as for example cable glands in electrical systems or for the production of cannulas for uses dentists.
Tali scopi, nonché altri che appariranno più chiaramente in seguito, sono raggiunti da un compound termoplastico, in accordo alla rivendicazione 1, comprendente un materiale polimerico base con modulo di elasticità relativamente elevato miscelato con almeno un additivo come agente modificatore. These purposes, as well as others which will appear more clearly later on, are achieved by a thermoplastic compound, according to claim 1, comprising a basic polymeric material with a relatively high modulus of elasticity mixed with at least one additive as a modifying agent.
II compound si caratterizza per il fatto che detto agente modificatore à ̈ presente in detta miscela in una quantità predeterminata atta ad ottenere un modulo di elasticità complessivo sostanzialmente inferiore a 2GPa misurato secondo la normativa ISO 527 in modo da consentire la realizzazione per estrusione di tubi monostrato aventi elevata flessibilità e basso ritorno elastico. The compound is characterized by the fact that said modifying agent is present in said mixture in a predetermined quantity capable of obtaining an overall modulus of elasticity substantially lower than 2GPa measured according to the ISO 527 standard in order to allow the production of single-layer pipes by extrusion. having high flexibility and low springback.
Nel presente testo per modulo di elasticità si intende il modulo di elasticità misurato con prove a trazione secondo la normativa ISO 527. In this text, the modulus of elasticity means the modulus of elasticity measured with tensile tests according to ISO 527.
Secondo un ulteriore aspetto del trovato à ̈ previsto un tubo monostrato, in accordo alla rivendicazione 9, realizzato con il suddetto compound. According to a further aspect of the invention, a single-layer pipe is provided, according to claim 9, made with the aforementioned compound.
Forme vantaggiose di realizzazione del trovato sono ottenute in accordo alle rivendicazioni dipendenti. Advantageous embodiments of the invention are obtained in accordance with the dependent claims.
Breve descrizione dei disegni Brief description of the drawings
Ulteriori caratteristiche e vantaggi del trovato risulteranno maggiormente evidenti alla luce della descrizione dettagliata di forme di realizzazione preferite ma non esclusiva tubi monostrato comprendenti un compound termoplastico secondo il trovato, illustrate a titolo di esempio non limitativo con l'ausilio delle unite tavole di disegno in cui: Further characteristics and advantages of the invention will become more evident in the light of the detailed description of preferred but not exclusive embodiments of single-layer tubes comprising a thermoplastic compound according to the invention, illustrated by way of non-limiting example with the aid of the accompanying drawings in which :
la FIG. 1 Ã ̈ una vista in sezione di un tubo monostrato secondo il trovato in una prima configurazione; FIG. 1 is a sectional view of a single-layer tube according to the invention in a first configuration;
la FIG. 2 Ã ̈ una vista prospettica del tubo di Fig. 1 ; FIG. 2 is a perspective view of the tube of Fig. 1;
le FIG. 3 Ã ̈ una vista laterale di un tubo monostrato secondo il trovato in una seconda configurazione. FIGS. 3 is a side view of a single-layer tube according to the invention in a second configuration.
Descrizione dettagliata di un esempio di realizzazione preferito Con riferimento alle figure citate, sono illustrate due diverse configurazioni di un tubo monostrato ad elevata memoria di forma, indicato globalmente con 1, realizzato mediante un compound termoplastico secondo il trovato. Detailed description of a preferred example of embodiment With reference to the cited figures, two different configurations of a single-layer tube with high shape memory, generally indicated with 1, made by means of a thermoplastic compound according to the invention, are illustrated.
Il compound termoplastico comprende un materiale polimerico base con modulo di elasticità relativamente elevato miscelato con un agente modificatore. The thermoplastic compound comprises a base polymeric material with a relatively high modulus of elasticity mixed with a modifying agent.
Secondo una caratteristica peculiare del trovato l’agente modificatore à ̈ presente nella miscela in una quantità predeterminata atta ad ottenere un modulo di elasticità complessivo sostanzialmente inferiore a 2GPa in modo da consentire la realizzazione per estrusione di tubi monostrato aventi elevata flessibilità e basso ritorno elastico. According to a peculiar characteristic of the invention, the modifying agent is present in the mixture in a predetermined quantity capable of obtaining an overall modulus of elasticity substantially lower than 2GPa so as to allow the production by extrusion of single-layer tubes having high flexibility and low elastic return. .
Opportunamente, il materiale polimerico base potrà presentare modulo di elasticità superiore a 2GPa e preferibilmente superiore a 2,5GPa. Conveniently, the base polymeric material may have a modulus of elasticity higher than 2GPa and preferably higher than 2.5GPa.
Ad esempio, nel caso si utilizzi PVC-U come materiale polimerico base, lo stesso avrà generalmente modulo di elasticità compreso tra 3GPa e 3,5GPa. For example, if PVC-U is used as the base polymeric material, it will generally have a modulus of elasticity between 3GPa and 3.5GPa.
A sua volta, l’agente modificatore presenterà modulo di elasticità inferiore a 1,5GPa e preferibilmente inferiore a 1GPa. In turn, the modifying agent will have a modulus of elasticity lower than 1.5GPa and preferably lower than 1GPa.
Opportunamente, la composizione della miscela sarà tale da avere un compound con modulo di elasticità complessivo compreso tra 1,5GPa e 1,8GPa. Conveniently, the composition of the mixture will be such as to have a compound with an overall modulus of elasticity between 1.5GPa and 1.8GPa.
Inoltre, l’additivo o agente modificatore potrà presentare allungamento a rottura misurato con prove a trazione secondo la normativa ISO 527, sostanzialmente maggiore del 350% e preferibilmente maggiore del 400%. Furthermore, the additive or modifying agent may have elongation at break measured with tensile tests according to ISO 527, substantially greater than 350% and preferably greater than 400%.
A sua volta, invece, il materiale polimerico base potrà essere ottenuto a partire da un polimero amorfo con comportamento a fratture di tipo duttile. In turn, however, the base polymeric material can be obtained starting from an amorphous polymer with ductile fracture behavior.
Grazie a questa particolare combinazione di caratteristiche del materiale polimerico base e dell’agente modificatore, sarà possibile realizzare un tubo monostrato 1 avente flessibilità relativamente elevata per consentire la sua sagomatura manuale, senza il ricorso ad attrezzature specifiche. Thanks to this particular combination of characteristics of the base polymeric material and of the modifying agent, it will be possible to produce a monolayer pipe 1 having relatively high flexibility to allow its manual shaping, without the use of specific equipment.
Allo stesso tempo, l’agente modificatore consentirà di contenere il ritorno elastico permettendo la realizzazione di tubi ad elevata memoria di forma atti a mantenere in maniera stabile la posizione assunta dopo la sagomatura. At the same time, the modifying agent will allow to contain the elastic return allowing the realization of tubes with high shape memory able to maintain in a stable way the position assumed after shaping.
Opportunamente, la miscela potrà essere ridotta in granuli o polvere per consentirne l’utilizzo nei comuni impianti di estrusione di materiali termoplastici. Conveniently, the mixture can be reduced into granules or powder to allow it to be used in common thermoplastic material extrusion plants.
Tuttavia, il tubo monostrato 1 potrà essere realizzato anche mediante comuni procedimenti di stampaggio ad iniezione di materiali termoplastici. However, the single-layer pipe 1 can also be made by means of common injection molding processes of thermoplastic materials.
Opportunamente, il materiale polimerico base potrà essere scelto nel gruppo dei materiali polimerici termoplastici e potrà essere presente nella miscela in una percentuale compresa tra il 10% ed il 90% e preferibilmente tra il 20% ed il 60% rispetto al peso totale della miscela. Conveniently, the base polymeric material can be selected from the group of thermoplastic polymeric materials and can be present in the mixture in a percentage comprised between 10% and 90% and preferably between 20% and 60% with respect to the total weight of the mixture.
Ad esempio, il materiale polimerico base potrà essere PVC-U con valore K compreso tra 50 e 100. For example, the base polymeric material could be PVC-U with a K value between 50 and 100.
L’agente modificatore potrà essere presente nella miscela in una percentuale compresa tra il 10% ed il 90% e preferibilmente tra il 20% ed il 40% rispetto al peso totale della miscela. The modifying agent may be present in the mixture in a percentage between 10% and 90% and preferably between 20% and 40% with respect to the total weight of the mixture.
L’agente modificatore potrà essere scelto nel gruppo dei polietileni ed in particolare potrà essere polietilene clorurato (CPE) avente una percentuale di cloro compresa tra il 25% ed il 40% del peso complessivo dell’agente. The modifying agent can be chosen from the group of polyethylenes and in particular it can be chlorinated polyethylene (CPE) having a percentage of chlorine between 25% and 40% of the total weight of the agent.
L’utilizzo di polietilene clorurato come agente modificatore assicurerà al tubo monostrato 1 una elevata elasticità e facilità di sagomatura e, allo stesso tempo, consentirà di minimizzare il fenomeno del ritorno elastico. The use of chlorinated polyethylene as a modifying agent will ensure high elasticity and ease of shaping to the single-layer pipe 1 and, at the same time, will allow to minimize the phenomenon of springback.
Opportunamente, la miscela potrà essere presente nel compound in percentuale compresa tra 50% e 80% del peso totale del compound. Conveniently, the mixture may be present in the compound in a percentage between 50% and 80% of the total weight of the compound.
Inoltre, all’interno del compound potranno essere presenti un plastificante monomerico o polimerico in percentuale compresa tra 0% e 30% del peso totale del compound, carbonato di calcio in percentuale compresa tra 0% e 40% del peso totale del compound ed uno stabilizzante termico presente in percentuale compresa tra 1,5% e 5% del peso totale del compound. Furthermore, inside the compound there may be a monomeric or polymeric plasticizer in a percentage between 0% and 30% of the total weight of the compound, calcium carbonate in a percentage between 0% and 40% of the total weight of the compound and a thermal stabilizer present in a percentage between 1.5% and 5% of the total weight of the compound.
In particolare si à ̈ sorprendentemente osservato che l’utilizzo combinato del polietilene clorurato (CPE) e del carbonato di calcio consentirà di contenere notevolmente il ritorno elastico del tubo monostrato 1 anche a temperature ambiente. In particular, it has been surprisingly observed that the combined use of chlorinated polyethylene (CPE) and calcium carbonate will significantly reduce the elastic return of the single-layer pipe 1 even at ambient temperatures.
In particolare, l’utilizzo combinato di polietilene clorurato e carbonato di calcio consentirà al tubo 1 così realizzato di mantenere memoria di almeno l’80% della deformazione impartita. In particular, the combined use of chlorinated polyethylene and calcium carbonate will allow the tube 1 thus made to retain at least 80% of the deformation imparted.
Esempio Example
% rispetto peso Funzione Materiale % of weight Function Material
totale compound Materiale base PVC-U (K=57) 40 Agente modificatore PCE (Cl=36%) 26 Plastificante di-isononil ftalato (DINP) 10 Additivo carbonato di calcio 20 Additivo stabilizzante termico 3,3 Inoltre, il compound potrà comprendere ulteriori additivi quali pigmenti, cariche minerali e lubrificanti al fine di agevolare l’estrusione del compound. total compound Base material PVC-U (K = 57) 40 Modifying agent PCE (Cl = 36%) 26 Plasticizer di-isononyl phthalate (DINP) 10 Calcium carbonate additive 20 Thermal stabilizing additive 3,3 In addition, the compound may include further additives such as pigments, mineral fillers and lubricants in order to facilitate the extrusion of the compound.
La suddetta composizione consentirà altresì di ottenere un tubo monostrato 1 ad elevata finitura superficiale in modo da agevolare l’utilizzo dello stesso in diverse applicazioni tecniche, quali ad esempio l’utilizzo del tubo come passacavi all’interno di impianti elettrici. The above composition will also make it possible to obtain a monolayer pipe 1 with a high surface finish in order to facilitate its use in various technical applications, such as for example the use of the pipe as cable glands in electrical systems.
Nelle Figg. 1 e 2 à ̈ illustrata una prima configurazione di un tubo monostrato 1 ad elevata memoria di forma secondo il trovato utilizzabile in particolare come passacavi o elemento di protezione nell’installazione di cavi conduttori presenti negli impianti elettrici. In Figs. 1 and 2 illustrate a first configuration of a single-layer tube 1 with high shape memory according to the invention which can be used in particular as a cable gland or protection element in the installation of conductive cables present in electrical systems.
Opportunamente, come meglio illustrato in Fig. 1, il tubo monostrato 1 comprenderà una parete periferica 2 sostanzialmente cilindrica avente un rapporto tra diametro esterno d e spessore s sostanzialmente compreso tra 3 e 20 e preferibilmente tra 10 e 15. Conveniently, as better illustrated in Fig. 1, the monolayer tube 1 will comprise a substantially cylindrical peripheral wall 2 having a ratio between external diameter d and thickness s substantially comprised between 3 and 20 and preferably between 10 and 15.
Un rapporto tra diametro esterno e spessore d/s compreso tra 10 e 15 sarà particolarmente efficace nel caso di tubi monostrato 1 costituti dal suddetto compound in quanto conferirà alla parete 2 una elevata resistenza al kinking anche per tubi aventi diametro esterno d corrispondente a quelli dei valori standard presenti nel mercato. A ratio between external diameter and thickness d / s between 10 and 15 will be particularly effective in the case of single-layer pipes 1 consisting of the aforementioned compound as it will give the wall 2 a high resistance to kinking even for pipes having an external diameter d corresponding to those of the standard values on the market.
Secondo una configurazione esemplificativa e non limitativa del trovato, il diametro esterno d del tubo monostrato 1 potrà essere compreso tra 16mm e 32mm e lo spessore s corrispondente potrà essere compreso tra 1mm e 3,2mm. According to an exemplary and non-limiting configuration of the invention, the external diameter d of the single-layer tube 1 may be between 16mm and 32mm and the corresponding thickness s may be between 1mm and 3.2mm.
Come mostrato in Fig. 2, il tubo monostrato 1 risulterà atto ad essere sagomato e piegato con elevati angoli di piegatura a, a’. As shown in Fig. 2, the monolayer tube 1 will be able to be shaped and bent with high bending angles a, aâ € ™.
Una tale composizione del compound permetterà di realizzare tubi monostrato 1 che permettono sagomature senza strozzature o deformazioni della parete 2 con angoli di piegatura a, a’ compresi tra 0° e 120°. Such a composition of the compound will make it possible to produce single-layer pipes 1 which allow shaping without bottlenecks or deformations of the wall 2 with bending angles a, aâ between 0 ° and 120 °.
Secondo una caratteristica particolarmente vantaggiosa, il tubo monostrato 1 potrà presentare caratteristiche elettriche atte a consentirne l’utilizzo nell’impiantistica elettrica di tipo civile e/o industriale. According to a particularly advantageous characteristic, the single-layer pipe 1 may have electrical characteristics suitable for allowing its use in civil and / or industrial electrical systems.
In particolare, il tubo monostrato 1 ottenuto con tale compound potrà risponderà ai requisiti richiesti dalla normativa CEI EN 61386-1 destinata a regolamentare la posa dei conduttori per impianti elettrici o sistemi di telecomunicazione fino a 1000 V in corrente alternata e/o fino a 1500 v in corrente continua. In particular, the single-layer pipe 1 obtained with this compound will be able to meet the requirements of the CEI EN 61386-1 standard intended to regulate the laying of conductors for electrical systems or telecommunication systems up to 1000 V in alternating current and / or up to 1500 v in direct current.
Inoltre, il tubo monostrato 1 potrà essere utilizzato come canalina passacavi consentendo di unire due o più scatole di derivazione senza l'utilizzo di elementi di raccordo nei tratti curvi dello stesso. Furthermore, the single-layer pipe 1 can be used as a cable duct allowing to join two or more junction boxes without using connecting elements in the curved sections of the same.
In questo modo, sarà possibile sagomare il tubo monostrato 1 in modo sostanzialmente uguale a quello della corrispondente scanalatura muraria utilizzando elementi di raccordo solo in corrispondenza delle sue porzioni estremità 4, 5 e non nel tratto curvo intermedio 6. In this way, it will be possible to shape the monolayer pipe 1 in a manner substantially the same as that of the corresponding wall groove using connecting elements only in correspondence with its end portions 4, 5 and not in the intermediate curved section 6.
Pertanto, il tubo 1 secondo il trovato consentirà di realizzare canaline passacavi che non richiedono la predisposizione di percorsi predefiniti. Therefore, the tube 1 according to the invention will make it possible to make cable ducts which do not require the provision of predefined paths.
Opportunamente, il tubo monostrato realizzato con il compound potrà essere utilizzato in diversi ambiti di applicazione in cui sia richiesta una elevata flessibilità ed un basso ritorno elastico. Conveniently, the single-layer pipe made with the compound can be used in different areas of application where high flexibility and low elastic return are required.
Ad esempio, in Fig. 3 Ã ̈ illustrato un tubo monostrato 10 secondo il trovato utilizzato per la costruzione di una cannula di aspirazione 7 ad uso odontoiatrico. For example, Fig. 3 illustrates a monolayer tube 10 according to the invention used for the construction of an aspiration cannula 7 for dental use.
La cannula 7 potrà presentare un attacco 8 collegato ad una prima estremità 10’ del tubo 10 ed atta a collegarsi amovibilmente con mezzi di aspirazione, non illustrati, per l’aspirazione della saliva. The cannula 7 may have an attachment 8 connected to a first end 10â € ™ of the tube 10 and adapted to be removably connected to suction means, not shown, for the suction of saliva.
Inoltre, la cannula 7 comprenderà un cappuccio 9 di tipo noto collegato in maniera fissa o amovibile ad una seconda estremità 10†del tubo 10 ed atto ad essere inserito all’interno della cavità orale di un paziente. Furthermore, the cannula 7 will comprise a cap 9 of a known type connected in a fixed or removable manner to a second end 10⠀ of the tube 10 and adapted to be inserted inside the oral cavity of a patient.
Opportunamente, il tubo 10 della cannula 7 potrà presentare diametro esterno dest sostanzialmente compreso tra 5mm e 10mm preferibilmente pari a 6mm. Conveniently, the tube 10 of the cannula 7 may have an outer diameter substantially between 5mm and 10mm, preferably equal to 6mm.
Inoltre, lo spessore s del tubo 10 potrà essere compreso tra 1mm e 5mm e preferibilmente pari a 2mm. Furthermore, the thickness s of the tube 10 may be between 1mm and 5mm and preferably equal to 2mm.
Secondo una configurazione del trovato particolarmente vantaggiosa, 11 tubo 10 della cannula 7 potrà presentare un rapporto tra diametro esterno e spessore d/s sostanzialmente compreso tra 3 e 5. According to a particularly advantageous configuration of the invention, the tube 10 of the cannula 7 may have a ratio between the external diameter and the thickness d / s substantially comprised between 3 and 5.
Un valore del rapporto d/s compreso in tale intervallo consentirà di sagomare agevolmente il tubo 10 ed assicurerà una elevata memoria di forma dello stesso, senza che sia necessario predisporre anime di irrigidimento o similari annegate all’interno del materiale del tubo 10. A value of the ratio d / s included in this interval will allow to easily shape the tube 10 and will ensure a high shape memory of the same, without the need to provide stiffening cores or the like embedded in the material of the tube 10.
In questo modo, l’operatore potrà sagomare il tubo 10 in modo da orientare il cappuccio 9 all’interno della cavità orale secondo una direzione di aspirazione preferita atta a permettere un agevole intervento sul paziente. In this way, the operator will be able to shape the tube 10 so as to orient the cap 9 inside the oral cavity according to a preferred suction direction suitable to allow an easy intervention on the patient.
Da quanto sopra descritto appare evidente che il trovato raggiunge gli scopi prefissati ed in particolare quello di realizzare un compound termoplastico per la realizzazione di tubi monostrato che presentino una elevata flessibilità ed un basso ritorno elastico. From what has been described above it is evident that the invention achieves the intended aim and objects and in particular that of realizing a thermoplastic compound for the production of single-layer pipes which have a high flexibility and a low elastic return.
Il compound ed il tubo secondo il trovato sono suscettibili di numerose modifiche e varianti tutte rientranti nel concetto inventivo espresso nelle rivendicazioni allegate. Tutti i particolari potranno essere sostituiti da altri elementi tecnicamente equivalenti, ed i materiali potranno essere diversi a seconda delle esigenze, senza uscire daN'ambito del trovato. The compound and the tube according to the invention are susceptible of numerous modifications and variations, all of which are within the scope of the inventive concept expressed in the attached claims. All the details can be replaced by other technically equivalent elements, and the materials can be different according to the requirements, without departing from the scope of the invention.
Anche se il compound ed il tubo sono stati descritti con particolare riferimento alle figure allegate, i numeri di riferimento sono utilizzati per migliorare l'intelligenza del trovato e non costituiscono alcuna limitazione all'ambito di tutela rivendicato.' Even if the compound and the tube have been described with particular reference to the attached figures, the reference numbers are used to improve the intelligence of the invention and do not constitute any limitation to the scope of protection claimed.
Claims (10)