PROCEDURE AND COMPOSITIONS FOR THE PURIFICATION OF WATER CONTAINING RESIDUAL ACRYLIC AND OPOXY POLYMER POLYMERS Download PDFInfo
- Publication number
- ITTO990418A1 ITTO990418A1 IT1999TO000418A ITTO990418A ITTO990418A1 IT TO990418 A1 ITTO990418 A1 IT TO990418A1 IT 1999TO000418 A IT1999TO000418 A IT 1999TO000418A IT TO990418 A ITTO990418 A IT TO990418A IT TO990418 A1 ITTO990418 A1 IT TO990418A1
- Authority
- IT
- Italy
- Prior art keywords
- solution
- until
- water
- fecl3
- solution containing
- Prior art date
Description
- La presente invenzione ha per oggetto un procedimento, e le composizioni per l'attuazione di tale procedimento, per depurare delle acque contenenti residui di polimeri acrilici od epossiacrilici. Il procedimento si applica specialmente, ma non esclusivamente, per il trattamento di eluati di dry-film o/e di solder resist, quali si formano nella produzione di circuiti elettronici stampati. - The present invention relates to a process, and compositions for carrying out this process, for purifying water containing residues of acrylic or epoxy-acrylic polymers. The process is applied especially, but not exclusively, for the treatment of dry-film or / and solder resist eluates, which are formed in the production of printed electronic circuits.
. Allo stato attuale della tecnica, questi eluati, che presentano un pH compreso-tra 11 e 14, vengono acidificati con acidi minerali, particolarmente con acido cloridrico o con acido solforico, sino a portarli ad un pH prossimo a 3,0, causando cosìja coagulazione dei residui di film polimerico. La sostanza coagulata viene separata dall'acqua di risulta mediante flottazione o precipitazione e viene insaccata, mentre l'acqua di risulta, che ha carattere -fortemente acido (pH prossimo a 3,0), viene ulteriormente trattata, anche per eliminare i residui di polimeri contenuti, assieme ai liquidi concentrati provenienti dalle operazioni galvaniche. Una depurazione definitiva può richiedere anche l'impiego di acqua ossigenata, di solfato ferroso ole di carbone attivo. . In the current state of the art, these eluates, which have a pH between 11 and 14, are acidified with mineral acids, particularly with hydrochloric acid or sulfuric acid, until they are brought to a pH close to 3.0, thus causing coagulation. residues of polymeric film. The coagulated substance is separated from the resulting water by flotation or precipitation and is bagged, while the resulting water, which has a strongly acidic character (pH close to 3.0), is further treated, also to eliminate the residues of polymers contained, together with concentrated liquids from galvanic operations. A definitive purification may also require the use of hydrogen peroxide, ferrous sulphate or activated carbon.
Questo modo di procedere noto presenta vari inconvenienti. Innanzi tutto l'acidificazione degli eluati, che devono essere portati da un pH 11÷14 ad un pH prossimo a 3,0, richiede un grande consumo di acido. Inoltre la sostanza coagulata separata dall'acqua di risulta è una poltiglia che ha un carattere gommoso ed incorfX)ra considerevoli quantità di acido relativamente concentrato, suscettibili di essere successivamente rilasciate, cosicché tale poltiglia deve essere insaccata in appositi sacchi di materiale resistente agli acidi (per esempio meraklon), e deve poi essere smaltita in apposite discariche con costi elevati. Infine l'acqua di risulta, fortemente acida, per poter essere smaltita deve essere portata dal suo pH prossimo a 3,0 ad un pH 7,5÷8,5, ciò che richiede un largo consumo di sostanza alcalina, generalmente soda caustica. Pertanto questo procedimento noto risulta costoso sia per il grande consumo di reagenti che esso richiede, sia per le complicazioni operative che comportano perdite di tempo, sia ancora per le difficoltà di smaltimento del prodotti che ne derivano. This known procedure has various drawbacks. First of all, the acidification of the eluates, which must be brought from a pH 11 ÷ 14 to a pH close to 3.0, requires a large consumption of acid. Furthermore, the coagulated substance separated from the resulting water is a slurry which has a rubbery character and incorporates considerable quantities of relatively concentrated acid, capable of being subsequently released, so that this slurry must be stuffed into special bags of acid-resistant material ( for example meraklon), and must then be disposed of in special landfills with high costs. Finally, the resultant water, strongly acidic, in order to be disposed of must be brought from its pH close to 3.0 to a pH 7.5 ÷ 8.5, which requires a large consumption of alkaline substance, generally caustic soda. Therefore, this known process is expensive both due to the large consumption of reagents that it requires, and due to the operational complications which involve waste of time, and also due to the difficulties in disposing of the resulting products.
In considerazione di questa situazione, uno scopo della presente invenzione è quello di creare un procedimento, e le composizioni per la sua attuazione, che consentano di effettuare la depurazione delle acque contenenti residui di polimeri acrilici od epossiacrilici, quali gli eluati di dry-film, di solder resist ed altri, con un minor consumo di reagenti. Un altro scopo dell'invenzione è quello di rendere possibile tale depurazione con operazioni più semplici, eseguibili in tempi minori. È infine uno scopo dell'invenzione quello di ridurre le difficoltà di smaltimento dei prodotti risultanti da un tale procedimento di depurazione. In consideration of this situation, an object of the present invention is to create a process, and the compositions for its implementation, which allow to carry out the purification of waters containing residues of acrylic or epoxy-acrylic polymers, such as dry-film eluates, of solder resist and others, with a lower consumption of reagents. Another object of the invention is to make this purification possible with simpler operations, which can be carried out in less time. Finally, an object of the invention is to reduce the difficulties in disposing of the products resulting from such a purification process.
Uno o più degli scopi citati si raggiungono, secondo l'invenzione, per mezzo di un procedimento che, in una sua prima forma di realizzazione, comporta le seguenti operazioni: One or more of the aforementioned objects are achieved, according to the invention, by means of a process which, in a first embodiment thereof, involves the following operations:
1 . Aggiungere alle acque da depurare (aventi un pH 11÷14) acido cloridrico sino ad ottenere una prima soluzione intermedia avente un pH compreso tra 8,0 e 9,0, e preferibilmente di circa 8,5; 1. Add hydrochloric acid to the water to be purified (having a pH of 11-14) until a first intermediate solution is obtained having a pH between 8.0 and 9.0, and preferably about 8.5;
provenienti dal procedimento noto. coming from the known process.
* Ancora, l'acqua di risulta presentante un pH prossimo a 6,5 richiede, per essere neutralizzata sino ad un pH prossimo a 7, 5+8, 5 per il suo smaltimento, una quantità di sostanza alcalina, quale la soda caustica, di gran lunga minore di quella occorrente nel procedimento noto, nel quale lo stesso valore finale del pH deve essere raggiunto partendo da un pH prossimo a 3,0. Oltre a ciò, non è neppure sempre necessario procedere ad uno smaltimento di questa acqua di risulta, che può invece essere inviata tale quale in testa all'impianto primario di trattamento. * Furthermore, the waste water having a pH close to 6.5 requires, to be neutralized up to a pH close to 7, 5 + 8, 5 for its disposal, a quantity of alkaline substance, such as caustic soda, far less than that required in the known process, in which the same final pH value must be reached starting from a pH close to 3.0. In addition to this, it is not always necessary to dispose of this waste water, which can instead be sent as it is at the head of the primary treatment plant.
Sono dunque evidenti i vantaggi del procedimento proposto dall'invenzione rispetto al trattamento noto. The advantages of the process proposed by the invention with respect to the known treatment are therefore evident.
Le composizioni caratteristiche utilizzate, secondo l'invenzione, per attuare la prima forma di realizzazione del procedimento descritto (in aggiunta a reagenti abituali come l'acido cloridrico e la soda caustica) sono dunque due: una soluzione contenente da 45 a 55 (e preferibilmente circa 50) g/1 di Al2(S04)3 ed una soluzione contenente dal 36% al 46% (e preferibilmente circa il 41%) in peso di FeCl3. The characteristic compositions used, according to the invention, to carry out the first embodiment of the described process (in addition to usual reagents such as hydrochloric acid and caustic soda) are therefore two: a solution containing from 45 to 55 (and preferably about 50) g / 1 of Al2 (S04) 3 and a solution containing from 36% to 46% (and preferably about 41%) by weight of FeCl3.
Il procedimento secondo l'invenzione è altresì suscettibile di una seconda forma di realizzazione, che permette una semplificazione delle procedure a prezzo di una riduzione molto modesta delle prestazioni. The method according to the invention is also susceptible of a second embodiment, which allows a simplification of the procedures at the price of a very modest reduction in performance.
In questa seconda forma di realizzazione, il procedimento secondo l'invenzione comporta le seguenti operazioni: In this second embodiment, the method according to the invention involves the following operations:
1 . Aggiungere alle acque da depurare (aventi un pH 11+14) acido cloridrico sino ad ottenere una soluzione intermedia avente un pH compreso tra 9,0 e 10,5, e preferibilmente di circa 9,5; .1. Add hydrochloric acid to the water to be purified (having a pH of 11 + 14) until an intermediate solution is obtained having a pH between 9.0 and 10.5, and preferably about 9.5; .
2 . Aggiungere a detta soluzione intermedia una soluzione contenente da 75 a 85 (e preferibilmente circa 80) g/1 di Al2(SC>4)3 e da 77 a 87 (e preferibilmente circa 82) g/l di FeCl3, sino ad ottenere una soluzione avente un pH compreso tra 5,0 e 7,0, e preferibilmente di circa 6,0; 2 . Add to said intermediate solution a solution containing from 75 to 85 (and preferably about 80) g / 1 of Al2 (SC> 4) 3 and from 77 to 87 (and preferably about 82) g / l of FeCl3, until a solution having a pH of between 5.0 and 7.0, and preferably about 6.0;
3. Favorire la flocculazione con l'aggiunta di una piccola quantità di polielettrolita; 3. Promote flocculation by adding a small amount of polyelectrolyte;
4 . Attendere la separazione completa o quasi completa della massa flocculata, che forma un fango il quale può essere separato dall'acqua di risulta. 4. Wait for the complete or almost complete separation of the flocculated mass, which forms a sludge which can be separated from the resulting water.
Come si vede, in questa seconda forma di realizzazione del procedimento secondo l'invenzione il numero delle operazioni è ridotto di una unità rispetto alla prima forma di realizzazione, e precisamente si effettua una sola aggiunta dell'unica composizione caratteristica in luogo di due aggiunte successive. La minore prestazione ottenuta consiste nel fatto che una piccola parte del fango flocculato può (anche se non necessariamente) ridisciogliersì, cosicché l'acqua di risulta contiene ancora, in questo caso, piccole quantità di polimero acrilico od epossiacrilico. Queste minori prestazioni sono tuttavìa accettabili in molti casi. As can be seen, in this second embodiment of the method according to the invention the number of operations is reduced by one unit with respect to the first embodiment, and precisely a single addition of the single characteristic composition is made instead of two subsequent additions. . The lower performance obtained consists in the fact that a small part of the flocculated sludge can (although not necessarily) redissolve, so that the resulting water still contains, in this case, small quantities of acrylic or epoxy-acrylic polymer. However, these lower performances are acceptable in many cases.
Il tecnico di produzione potrà dunque scegliere, secondo le esigenze deirimpianto condotto, se applicare la seconda forma di realizzazione del procedimento secondo l'invenzione, in vista delle semplificazioni operative che essa permette, oppure applicare la prima forma di realizzazione del procedimento secondo l'invenzione, in vista dei risultati più perfetti che essa assicura. The production technician will therefore be able to choose, according to the requirements of the conducted plant, whether to apply the second embodiment of the method according to the invention, in view of the operational simplifications that it allows, or to apply the first embodiment of the method according to the invention. , in view of the most perfect results that it ensures.
La composizione unica destinata a consentire l'attuazione della seconda forma di realizzazione del procedimento secondo l'invenzione contiene dunque, in acqua distillata, da 75 a 85 (e preferibilmente circa 80) g/l di Al2(SC>4)3 e da 77 a 87 (e preferibilmente circa 82) g/l di FeC^. Questa composizione può essere vantaggiosamente ottenuta dissolvendo 4 kg di Al2(S04)3 (solfato di alluminio) in 40 ] di acqua distillata ed aggiungendo successivamente 10 l di soluzione 3 M di FeCl3 cloruro ferrico). The unique composition intended to allow the implementation of the second embodiment of the process according to the invention therefore contains, in distilled water, from 75 to 85 (and preferably about 80) g / l of Al2 (SC> 4) 3 and from 77 to 87 (and preferably about 82) g / l of FeC ^. This composition can be advantageously obtained by dissolving 4 kg of Al2 (S04) 3 (aluminum sulphate) in 40] of distilled water and subsequently adding 10 l of 3 M solution of FeCl3 ferric chloride).
Si deve tuttavia intendere che l'invenzione non è limitata alle due forme di realizzazione descritte ed illustrate come esempi. Alcune modificazioni sono alla portata del tecnico del ramo; per esempio, le quantità dei reagenti ed i valori del pH possono essere diversamente scelti nei campi indicati od in prossimità di essi, ed altri reagenti possono eventualmente essere aggiunti alle composizioni secondo l'invenzione, per ottenere scopi particolari. However, it is to be understood that the invention is not limited to the two embodiments described and illustrated as examples. Some modifications are within the reach of the person skilled in the art; for example, the quantities of the reactants and the pH values can be chosen differently in the indicated ranges or in proximity to them, and other reactants can optionally be added to the compositions according to the invention, to achieve particular purposes.
Queste ed altre modificazioni ed ogni sostituzione con equivalenti tecnici possono essere apportate a quanto descritto, senza per questo dipartirsi dall'ambito dell'invenzione e dalla portata del presente brevetto. These and other modifications and any substitution with technical equivalents can be made to what has been described, without departing from the scope of the invention and the scope of the present patent.
RIVENDICAZIONI
1 . Procedimento per depurare delle acque contenenti residui di polimeri acrilici od epossiacrilici, caratterizzato dal fatto che comporta le seguenti operazioni: 1. Process for purifying water containing residues of acrylic or epoxy-acrylic polymers, characterized in that it involves the following operations:
<• >. Aggiungere alle acque da depurare (aventi un pH 11÷14) acido cloridrico sino ad ottenere una prima soluzione intermedia avente un pH compreso tra 8,0 e 9,0; <•>. Add hydrochloric acid to the water to be purified (having a pH of 11-14) until a first intermediate solution is obtained with a pH between 8.0 and 9.0;
<• >. Aggiungere a detta prima soluzione intermedia una soluzione contenente da 45 a 55 (e preferibilmente circa 50) g/1 di A^SO^, sino ad ottenere una seconda soluzione intermedia avente un pH compreso tra 7,0 ed 8,0; <•>. Add to said first intermediate solution a solution containing from 45 to 55 (and preferably about 50) g / 1 of A ^ SO ^, until a second intermediate solution having a pH comprised between 7.0 and 8.0 is obtained;
• . Aggiungere a detta seconda soluzione intermedia una soluzione contenente dal 36% al 46% (e preferibilmente circa il 41%) in peso di FeCl3, sino ad ottenere una soluzione avente un pH compreso tra 6,0 e 7,0; •. Add to said second intermediate solution a solution containing from 36% to 46% (and preferably about 41%) by weight of FeCl3, until a solution having a pH between 6.0 and 7.0 is obtained;
<• >. Favorire la flocculazione con l'aggiunta di una piccola quantità di polielettrol ita; e <•>. Promote flocculation by adding a small amount of polyelectrol ita; And
<• >. Attendere la separazione completa o quasi completa della massa flocculata, che forma un fango il quale può essere separato dall'acqua di risulta. <•>. Wait for the complete or almost complete separation of the flocculated mass, which forms a sludge which can be separated from the resulting water.
2 . Procedimento secondo la rivendicazione 1, caratterizzato dal fatto che l'acido cloridrico viene aggiunto all'acqua da trattare sino ad ottenere una prima soluzione intermedia avente un pH di circa 8,5. 2 . Process according to claim 1, characterized in that the hydrochloric acid is added to the water to be treated until a first intermediate solution having a pH of about 8.5 is obtained.
3 . Procedimento secondo la rivendicazione 1 , caratterizzato dal fatto che la soluzione contenente Al2(S04)3 viene aggiunta a detta prima soluzione intermedia sino ad ottenere una seconda soluzione intermedia avente un pH di circa 7,5. 3. Process according to claim 1, characterized in that the solution containing Al2 (S04) 3 is added to said first intermediate solution until a second intermediate solution having a pH of about 7.5 is obtained.
4 . Proce<'>dimento secondo la rivendicazione 1, caratterizzato dal fatto che la soluzione contenente FeCl3 viene aggiunta a detta seconda soluzione intermedia sino ad ottenere una soluzione avente un pH di circa 6,5. 4. Process according to claim 1, characterized in that the solution containing FeCl3 is added to said second intermediate solution until a solution having a pH of about 6.5 is obtained.
5 . Procedimento per depurare delle acque contenenti residui di polimeri acrilici od epossiacrilici, caratterizzato dal fatto che comporta le seguenti operazioni: 5. Process for purifying water containing residues of acrylic or epoxy-acrylic polymers, characterized in that it involves the following operations:
<• >. Aggiungere alle acque da depurare (aventi un pH 11÷14) acido cloridrico sino ad ottenere una soluzione intermedia avente un pH compreso tra 9,0 ed 11 ,0; <•>. Add hydrochloric acid to the water to be purified (having a pH of 11-14) until an intermediate solution is obtained with a pH between 9.0 and 11.0;
<• >. Aggiungere a detta soluzione intermedia una soluzione contenente da 75 a 85 (e preferibilmente circa 80) g/1 di Al2(SC>4)3 e da 77 a 87 (e preferibilmente circa 82) g/l di FeCl3, sino ad ottenere una soluzione avente un pH compreso tra 5,0 e 7,0; <•>. Add to said intermediate solution a solution containing from 75 to 85 (and preferably about 80) g / 1 of Al2 (SC> 4) 3 and from 77 to 87 (and preferably about 82) g / l of FeCl3, until a solution having a pH between 5.0 and 7.0;
·. Favorire la flocculazione con l'aggiunta di una piccola quantità di polielettrolita; e ·. Promote flocculation by adding a small amount of polyelectrolyte; And
<• >. Attendere la separazione completa o quasi completa della massa floccuiata, che forma un fango il quale può essere separato dall'acqua di risulta. <•>. Wait for the complete or almost complete separation of the flocked mass, which forms a sludge which can be separated from the resulting water.
6 . Procedimento secondo la rivendicazione 5, caratterizzato dal fatto che l'acido cloridrico viene aggiunto alle acque da depurare sino ad ottenere una soluzione intermedia avente un pH di circa 9,5. 6. Process according to claim 5, characterized in that hydrochloric acid is added to the water to be purified until an intermediate solution having a pH of about 9.5 is obtained.
7 . Procedimento secondo la rivendicazione 5, caratterizzato dal fatto che la soluzione unica contenente Al2(S04)3 e FeCl3 viene aggiunta a detta soluzione intermedia sino ad ottenere una soluzione avente un pH di circa 6,0. 7. Process according to claim 5, characterized in that the single solution containing Al2 (S04) 3 and FeCl3 is added to said intermediate solution until a solution having a pH of about 6.0 is obtained.
8 . Procedimento secondo la rivendicazione 1 oppure 5, caratterizzato dai fatto che viene applicato alla depurazione di eluati di dry-film o/e di solder resisi. 8. Process according to claim 1 or 5, characterized in that it is applied to the purification of dry-film eluates or / and resized solder.
9 . Composizioni da impiegare, in aggiunta a reagenti abituali, per l'attuazione del procedimento secondo la rivendicazione 1 , caratterizzate dal fatto che includono: 9. Compositions to be used, in addition to usual reagents, for carrying out the process according to claim 1, characterized in that they include:
<• >. una soluzione contenente da 45 a 55 g/l di Al2(S04)3, e <•>. a solution containing 45 to 55 g / l of Al2 (S04) 3, e
• . una soluzione contenente dal 36% al 46% in peso di FeCl3- •. a solution containing from 36% to 46% by weight of FeCl3-
10 . Composizioni secondo la rivendicazione 9, caratterizzate dai fatto che includono: 10. Compositions according to claim 9, characterized in that they include:
<• >. una soluzione contenente circa 50 g/l di A^CSO^, e <•>. a solution containing about 50 g / l of A ^ CSO ^, e
<• >. una soluzione contenente circa il 41% in peso di FeCl3· <•>. a solution containing about 41% by weight of FeCl3
11 . Composizione unica da impiegare, in aggiunta a reagenti abituali, per l'attuazione del procedimento secondo la rivendicazione 5, caratterizzata dal fatto che contiene da 75 a 85 g/l di Al2(S04)3 e da 77 a 87 g/l di FeC^. 11. Unique composition to be used, in addition to usual reagents, for carrying out the process according to claim 5, characterized in that it contains from 75 to 85 g / l of Al2 (S04) 3 and from 77 to 87 g / l of FeC ^.
12 . Composizione secondo la rivendicazione 11 , caratterizzata dal fatto che comprende circa 80 g/l di Al2(S04)3 e circa 82 g/l di FeCl3. 12. Composition according to claim 11, characterized in that it comprises about 80 g / l of Al2 (S04) 3 and about 82 g / l of FeCl3.
13 . Composizione secondo la rivendicazione 12, caratterizzata dal fatto che viene ottenuta dissolvendo 4 kg di Al2(S04)3 (solfato di alluminio) in 40 l di acqua distillata ed aggiungendo successivamente 10 l di soluzione 3 IVI di FeCl3 (cloruro ferrico). 13. Composition according to claim 12, characterized in that it is obtained by dissolving 4 kg of Al2 (S04) 3 (aluminum sulphate) in 40 l of distilled water and subsequently adding 10 l of 3 IVI solution of FeCl3 (ferric chloride).
14 . Procedimento e composizioni per depurare delle acque contenenti residui di polimeri acrilici od epossiacrilici, e specialmente per il trattamento di eluati di dry-film o/e di solder resist, quali si formano nella produzione di circuiti elettronici stampati, caratterizzati dalle particolarità, disposizioni, modi di operare e contenuti, quali appaiono dalla descrizione sopraestesa o sostituiti da loro equivalenti tecnici, presi nel loro insieme, nelle loro varie combinazioni o separatamente. 14. Process and compositions for purifying water containing residues of acrylic or epoxy-acrylic polymers, and especially for the treatment of dry-film or / and solder resist eluates, which are formed in the production of printed electronic circuits, characterized by the particularities, arrangements, methods to operate and contents, as appear from the above description or replaced by their technical equivalents, taken as a whole, in their various combinations or separately.
2 . Aggiungere a detta prima soluzione intermedia una soluzione contenente da 45 a 55 (e preferibilmente circa 50) g/1 di Al2(S04)3, sino ad ottenere una seconda soluzione intermedia avente un pH compreso tra 7,0 ed 8,0, e preferibilmente di circa 7,5; 2 . Add to said first intermediate solution a solution containing from 45 to 55 (and preferably about 50) g / 1 of Al2 (S04) 3, until a second intermediate solution having a pH between 7.0 and 8.0 is obtained, and preferably about 7.5;
3 . Aggiungere a detta seconda soluzione intermedia una soluzione contenente dal 36% al 46% (e preferibilmente circa il 41%) in peso di FeCl3> sino ad ottenere una terza soluzione intermedia avente un pH compreso tra 6,0 e 7,0, e preferibilmente di circa 6,5; 3. Add to said second intermediate solution a solution containing from 36% to 46% (and preferably about 41%) by weight of FeCl3> until obtaining a third intermediate solution having a pH between 6.0 and 7.0, and preferably of about 6.5;
4 . Favorire la flocculazione con l'aggiunta di una piccola quantità di polielettrolita; e 4. Promote flocculation by adding a small amount of polyelectrolyte; And
5 . Attendere la separazione completa o quasi completa della massa flocculata, che forma un fango il quale può essere separato dall'acqua di risulta. 5. Wait for the complete or almost complete separation of the flocculated mass, which forms a sludge which can be separated from the resulting water.
Questo fango non ha carattere gommoso e contiene solo quantità assai piccole di liquido, il quale presenta un pH prossimo a 6,5. This mud has no rubbery character and contains only very small quantities of liquid, which has a pH close to 6.5.
Si nota innanzitutto che con questo procedimento si consuma, nella fase 1 , una quantità di acido nettamente minore di quella occorrente nel procedimento noto, per il fatto che la soluzione viene portata dal suo pH iniziale ad un pH prossimo a 8,5 anziché prossimo a 3,0. First of all, it is noted that with this process, in phase 1, a significantly lower quantity of acid is consumed than that required in the known process, due to the fact that the solution is brought from its initial pH to a pH close to 8.5 rather than close to 3.0.
Inoltre, i fanghi che risultano dalla fase 5, non essendo di carattere gommoso e contenendo poco liquido di ridotta acidità, non richiedono di essere insaccati in contenitori speciali e smaltiti in apposite discariche; essi possono invece essere mescolati con altri fanghi provenienti da un impianto di trattamento primario ed essere pressati per lo smaltimento. Un simile procedimento presenta costi dell'ordine di 320 ITL/kg, da confrontare con i costi dell'ordine di 700÷1000 ITL/kg che si incontrano nello smaltimento delle sostanze coagulate, aventi carattere gommoso, Furthermore, the sludge resulting from phase 5, not being of a rubbery character and containing little liquid of reduced acidity, does not need to be stuffed into special containers and disposed of in suitable landfills; instead they can be mixed with other sludges coming from a primary treatment plant and pressed for disposal. Such a procedure has costs of the order of 320 ITL / kg, to be compared with the costs of the order of 700 ÷ 1000 ITL / kg that are encountered in the disposal of coagulated substances, having a rubbery character,
Claims (14)