ITMI940408A1 - COMPOSITION OF ADHESIVE FOR THE FILLING OF BOXED PARTS OF VEHICLE BODIES - Google Patents

COMPOSITION OF ADHESIVE FOR THE FILLING OF BOXED PARTS OF VEHICLE BODIES Download PDF

Info

Publication number
ITMI940408A1
ITMI940408A1 IT000408A ITMI940408A ITMI940408A1 IT MI940408 A1 ITMI940408 A1 IT MI940408A1 IT 000408 A IT000408 A IT 000408A IT MI940408 A ITMI940408 A IT MI940408A IT MI940408 A1 ITMI940408 A1 IT MI940408A1
Authority
IT
Italy
Prior art keywords
composition
filling
alkane
weight
adhesive
Prior art date
Application number
IT000408A
Other languages
Italian (it)
Inventor
Giancarlo Ferrari
Mario Panfili
Massimo Tomalino
Original Assignee
Ppg Ind Italia S R L
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ppg Ind Italia S R L filed Critical Ppg Ind Italia S R L
Priority to ITMI940408A priority Critical patent/IT1269293B/en
Publication of ITMI940408A0 publication Critical patent/ITMI940408A0/en
Priority to PCT/EP1995/000615 priority patent/WO1995024441A1/en
Priority to PL95316137A priority patent/PL180186B1/en
Priority to BR9507405A priority patent/BR9507405A/en
Priority to MA23797A priority patent/MA23469A1/en
Priority to DZ950025A priority patent/DZ1861A1/en
Publication of ITMI940408A1 publication Critical patent/ITMI940408A1/en
Application granted granted Critical
Publication of IT1269293B publication Critical patent/IT1269293B/en

Description

DESCRIZIONE DESCRIPTION

Nel suo aspetto più generale la presente invenzione si riferisce al riempimento di "parti scatolate" di scocche di veicoli. In its more general aspect, the present invention relates to the filling of "boxed parts" of vehicle bodies.

Con il termine "parti scatolate" si intendono, nel gergo tecnico dei settore, porzioni della scocca di uh veicolo che presentano delle cavità. The term "boxed parts" means, in the technical jargon of the sector, portions of the body of a vehicle which have cavities.

In particolare quest’invenzione concerne una composizione polimerica per il riempimento di dette parti scatolate di scocche di veicoli. In particular, this invention concerns a polymeric composition for filling said boxed parts of vehicle bodies.

E’ noto che nell’ambito della scocca di un veicolo sono presenti un certo numero di parti scatolate. E’ noto altresì che la presenza di dette parti scatolate costituisce un problema per il fatto che esse, essendo cave, propagano ed amplificano le vibrazioni. It is known that within the body of a vehicle there are a certain number of boxed parts. It is also known that the presence of said boxed parts constitutes a problem due to the fact that, being hollow, they propagate and amplify the vibrations.

Inoltre le cavità dì queste parti scatolate tendono a raccogliere umidità e costituiscono pertanto zone in cui la scocca è particolarmente sensibile alla corrosione. Furthermore, the cavities of these boxed parts tend to collect humidity and therefore constitute areas in which the body is particularly sensitive to corrosion.

Si rende pertanto necessario procedere ad un riempimento di tali parti scatolate al fine di conseguire sia un effetto insonorizzante sia una protezione dalla corrosione. Nella tecnica nota li riempimento delle parti scatolate è comunemente effettuato iniettando in esse composizioni, a base rispettivamente di una resina poliolo e di un isocianato, le quali, in seguito alla miscelazione, reagiscono, a temperatura ambiente o a caldo, durante il passaggio della scocca nei forni di lastratura o verniciatura, polimerizzando e dando origine ad una schiuma poliuretanica. Il notevole aumento di volume che si verifica nella formazione della schiuma consente il riempimento totale della parte scatolata. Ciò consente di conseguire l’insonorizzazione acustica e la protezione dalia corrosione. It is therefore necessary to fill these boxed parts in order to achieve both a soundproofing effect and protection from corrosion. In the known art, the filling of the boxed parts is commonly carried out by injecting into them compositions, respectively based on a polyol resin and an isocyanate, which, following mixing, react, at room temperature or hot, during the passage of the body into the paneling or painting ovens, polymerizing and giving rise to a polyurethane foam. The considerable increase in volume that occurs in the formation of the foam allows the total filling of the boxed part. This allows to achieve acoustic soundproofing and corrosion protection.

Tuttavia l’impiego deile suddette resine non è privo di inconvenienti, sia da un punto dì vista economico, sia, e soprattutto, da un punto di vista ambientale e tossicologico. However, the use of the aforementioned resins is not without drawbacks, both from an economic point of view and, and above all, from an environmental and toxicological point of view.

Infatti le due composizioni che devono essere miscelate per dar luogo alla schiuma poliuretanica sono contenute in bombolette o grossi contenitori pressurizzati; nel primo caso il contenuto della bomboletta può essere erogato soltanto per il 60% del totale e la bomboletta, contenente ancora una considerevole quantità di prodotto, deve essere poi avviata allo smaltimento, che può essere effettuato soltanto ad opera di ditte specializzate. In fact the two compositions which must be mixed to give rise to the polyurethane foam are contained in cans or large pressurized containers; in the first case the contents of the can can be dispensed only for 60% of the total and the can, still containing a considerable quantity of product, must then be sent for disposal, which can only be carried out by specialized firms.

Nei secondo caso, i contenitori pressurizzati, dopo ogni svuotamento, che anche in questo caso è parziale, devono essere accuratamente puliti prima di essere ririempiti. In the second case, the pressurized containers, after each emptying, which also in this case is partial, must be carefully cleaned before being refilled.

In entrambi i casi risultano evidenti gli inconvenienti economici ed ambientali che l’uso di tali schiume poliuretaniche comporta. In both cases, the economic and environmental drawbacks that the use of such polyurethane foams entails are evident.

Infine, In conseguenza della notevole tossicità dei componenti di dette schiume poliuretaniche si rendono necessarie misure di sicurezza estremamente rigorose per quanto riguarda l’equipaggiamento degli operai addetti alla loro applicazione, che sono costretti ad indossare indumenti di protezione ingombranti e sconfortevoli, se non dei veri e propri scafandri. Finally, as a consequence of the considerable toxicity of the components of said polyurethane foams, extremely strict safety measures are necessary as regards the equipment of the workers assigned to their application, who are forced to wear bulky and uncomfortable protective clothing, if not real and own diving suits.

In conseguenza degli inconvenienti sopra elencati le industrie produttrici di veicoli hanno compiuto molti sforzi di ricerca per l’individuazione di metodi alternativi per risolvere il problema del riempimento delle parti scatolate delle scocche di veicoli. As a result of the drawbacks listed above, the vehicle manufacturing industries have made many research efforts to identify alternative methods to solve the problem of filling the boxed parts of vehicle bodies.

Fra le soluzioni proposte in alternativa all’impiego delle schiume poliuretaniche si può citare l'utilizzo di materiali preformati, a base di gomme o di derivati dell’etilvinilacetato (ÈVA), che, opportunamente fustellati e dimensionati, vengono introdotti nelle parti scatolate prima delle fasi di lastratura o di verniciatura. Durante la cottura in forno che si ha nelle suddette fasi, tali materiali espandono fino a riempire tutta la parte scatolata. Among the solutions proposed as an alternative to the use of polyurethane foams we can mention the use of preformed materials, based on rubber or derivatives of ethyl vinyl acetate (EVA), which, suitably punched and sized, are introduced into the boxed parts before the phases of bodywork or painting. During the cooking in the oven that occurs in the aforementioned phases, these materials expand until they fill the whole boxed part.

Le prestazioni che si ottengono con tali materiali in fatto di insonorizzazione e di protezione contro la corrosione sono del tutto paragonabili a quelle ottenute mediante l’impiego delle schiume poliuretaniche, soprattutto qualora si utilizzino preformati ancorati ad una base metallica, perché in tal caso è possibile un loro inserimento preciso all’interno del vano scatolato tramite saldatura di detta base metallica alla parete di detto vano. The performances obtained with these materials in terms of soundproofing and corrosion protection are completely comparable to those obtained through the use of polyurethane foams, especially if preforms anchored to a metal base are used, because in this case it is possible their precise insertion inside the boxed compartment by welding said metal base to the wall of said compartment.

L’impiego dei suddetti materiali preformati consente senza dubbio di ovviare agli inconvenienti di tipo ambientale e tossicologico connessi con l’uso delle schiume poliuretaniche, ma comporta costi complessivi elevati sia a causa dell’alto costo dei materiali stessi sia in conseguenza del la laboriosità di applicazione, che incide sui costo della mano d’opera. The use of the aforementioned preformed materials undoubtedly allows to obviate the environmental and toxicological drawbacks associated with the use of polyurethane foams, but involves high overall costs both because of the high cost of the materials themselves and as a consequence of the laboriousness of application, which affects the cost of labor.

Il problema che sta alla base della presente invenzione è quello dì mettere a disposizione una composizione adatta al riempimento delle parti scatolate di scocche di autoveicoli che consenta di superare gli inconvenienti sopra evidenziati con riferimento alla tecnica nota, ovvero che non comporti problemi di tipo tossicologico ed ambientale e sia di facile ed economica applicazione. The problem underlying the present invention is that of providing a composition suitable for filling the boxed parts of vehicle bodies which allows to overcome the drawbacks highlighted above with reference to the known art, or which does not involve toxicological and environmental and is easy and economical to apply.

Questo problema viene risotto secondo l'invenzione da una composizione di adesivo per il riempimento di parti scatolate di scocche di autoveicoli in genere, comprendente, in percentuale in peso sul peso della composizione, da 20 a 35% di resina PVC (PVC/PVA), caratterizzata dal fatto di comprendere da 5 a 15% di un agente rigonfiante a caldo, costituito da un copolimero acrilonitrile/estere acrilico/olefina, incapsulante una quantità appropriata di un alcano. This problem is solved according to the invention by an adhesive composition for filling boxed parts of vehicle bodies in general, comprising, in percentage by weight on the weight of the composition, from 20 to 35% of PVC resin (PVC / PVA) , characterized in that it comprises from 5 to 15% of a hot swelling agent, consisting of an acrylonitrile / acrylic ester / olefin copolymer, encapsulating an appropriate amount of an alkane.

Secondo una modalità di realizzazione preferita il suddetto agente rigonfiante a caldo è utilizzato nella forma di microsfere di detto copolimero, incorporanti un alcano ed aventi un diametro di 8-15 micron. According to a preferred embodiment, the aforementioned hot swelling agent is used in the form of microspheres of said copolymer, incorporating an alkane and having a diameter of 8-15 microns.

Il suddetto alcano è preferibilmente costituito da isobutano. The aforesaid alkane is preferably constituted by isobutane.

Quale agente rigonfiante a caldo viene utilizzato d! preferenza il materiale posto In vendita con il nome di EXPANCEL della EXPANCEL NOBEL INDUSTRIES SWEDEN. Which hot swelling agent is used d! preference the material placed For sale under the name of EXPANCEL of EXPANCEL NOBEL INDUSTRIES SWEDEN.

In maniera vantaggiosa la suddetta composizione di adesivo comprende anche da 0,5 a 1,5% di una carica a basso peso. Advantageously, the above adhesive composition also comprises from 0.5 to 1.5% of a low weight filler.

Preferibilmente la suddetta carica a basso peso è costituita da un copolimero preespanso acrilonitrile/estere acrilico/olefina, incapsulante una quantità appropriata di un alcano. Preferably the aforesaid low weight filler is constituted by an acrylonitrile / acrylic ester / olefin pre-expanded copolymer, encapsulating an appropriate amount of an alkane.

Una composizione preferita di adesivo per il riempimento di parti scatolate di scocche di autoveicoli in genere comprende in percentuale in peso sul peso totale della composizione: A preferred composition of adhesive for filling boxed parts of motor vehicle bodies generally comprises in percentage by weight of the total weight of the composition:

Un plastificante utile per gli scopi della presente invenzione è scelto nel gruppo comprendente ftalati, adipati, benzoati, trimellitati, solfonati e loro miscele. A plasticizer useful for the purposes of the present invention is selected from the group comprising phthalates, adipates, benzoates, trimellitates, sulfonates and their mixtures.

Le cariche minerali, che possono essere naturali e/o rivestite, sono quelle normalmente utilizzate nelle formulazioni note degli adesivi per scocche e comprendono carbonati e silicati di calcio, talco, mica, caolino, biossido di titanio e simili. The mineral fillers, which can be natural and / or coated, are those normally used in known formulations of body adhesives and include carbonates and silicates of calcium, talc, mica, kaolin, titanium dioxide and the like.

Fra i promotori di adesione utili per gli scopi per la presente Invenzione si possono citare quelli scelti nel gruppo comprendente resine poliammlno-polìammidiche, resine epossidiche, resine melamminiche, resine poliuretaniche e resine ureiche. Among the adhesion promoters useful for the purposes of the present invention, it is possible to mention those selected from the group comprising polyamine-polyamide resins, epoxy resins, melamine resins, polyurethane resins and urea resins.

Quale carica a basso peso viene utilizzato di preferenza un copolimero preespanso commercializzato dalla EXPANCEL NOBEL INDUSTRIES SWEDEN con il nome di EXPANCEL. A pre-expanded copolymer marketed by EXPANCEL NOBEL INDUSTRIES SWEDEN under the name of EXPANCEL is preferably used as a low weight filler.

I catalizzatori e gli acceleranti maggiormente utili sono costituiti da poliammine, perossidi, amidi e simili. The most useful catalysts and accelerators are made up of polyamines, peroxides, starches and the like.

La composizione di quest’invenzione, in tutte le sue formulazioni rientranti nei valori più sopra precisati, è risultata di applicabilità ottimale, utilizzando le tecniche ed apparecchiature attualmente usate per le composizioni di adesivi della tecnica nota. The composition of this invention, in all its formulations falling within the values specified above, was found to be of optimal applicability, using the techniques and equipment currently used for the compositions of adhesives of the known art.

In particolare il materiale dell’Invenzione può essere applicato nelle parti scatolate delle scocche utilizzando pompe airless con rapporto di compressione 45:1 e pistole munite di ugelli denominati "per estrusione”, adatti cioè a consentire la corretta fuoriuscita di materiali a viscosità medio-alta (300.000 - 800.000 cps). In particular, the material of the invention can be applied in the boxed parts of the bodies using airless pumps with a compression ratio of 45: 1 and guns equipped with nozzles called "for extrusion", that is, suitable for allowing the correct release of medium-high viscosity materials. (300,000 - 800,000 cps).

L’applicazione può essere eseguita nella fase di lastratura, distribuendo la composizione dell’invenzione direttamente sulla superficie metallica della scocca, prima della verniciatura cataforetica e della successiva cottura a temperature di 150-180°C. The application can be performed in the paneling phase, distributing the composition of the invention directly on the metal surface of the body, before the cataphoretic painting and subsequent firing at temperatures of 150-180 ° C.

Alternativamente, la composizione secondo l’invenzione può essere applicata sulla vernice cataforetica polimerizzata e successivamente sottoposta a cottura a temperature di 140-1 60°C. Lo spessore dello strato di composizione consigliabile per ottenere un soddisfacente riempimento delle parti scatolate può variare moltissimo a seconda delle caratteristiche geometriche e volumetriche dello scatolato; in generale, il dosaggio ottimale del materiale, e quindi il suo spessore, va regolato tenendo conto del rapporto di espansione del materiale stesso in funzione del ciclo di cottura al quale deve essere sottoposto. Alternatively, the composition according to the invention can be applied on the polymerized cataphoretic paint and subsequently subjected to firing at temperatures of 140-1 60 ° C. The thickness of the layer of composition recommended for obtaining a satisfactory filling of the boxed parts can vary greatly according to the geometric and volumetric characteristics of the boxed part; in general, the optimal dosage of the material, and therefore its thickness, must be adjusted taking into account the expansion ratio of the material itself according to the firing cycle to which it must be subjected.

Per ottenere un'applicazione uniforme è consigliato dì erogare la composizione secondo l'invenzione ad una temperatura compresa fra 20 e 25 °C. To obtain a uniform application it is recommended to dispense the composition according to the invention at a temperature between 20 and 25 ° C.

La trasformazione a caldo ottimale è ottenuta con un ciclo di cottura della composizione durato circa 30 minuti, in un intervallo di temperatura tra 140 e 180°C. The optimal heat transformation is obtained with a cooking cycle of the composition which lasted about 30 minutes, in a temperature range between 140 and 180 ° C.

Al termine della fase di cottura, l’adesivo della composizione della presente invenzione costituisce un riempimento che si adatta perfettamente alle pareti delle parti scatolate, aderendovi coesivamente e sigillandole completamente, pur mantenendo una struttura compatta microcellulare e quindi a bassa densità. Come conseguenza di tali proprietà si ottengono prestazioni ottimali In fatto di Isolamento acustico e di protezione dalla corrosione. At the end of the firing phase, the adhesive of the composition of the present invention constitutes a filling that adapts perfectly to the walls of the boxed parts, adhering cohesively and sealing them completely, while maintaining a compact microcellular structure and therefore low density. As a consequence of these properties, optimal performances are obtained in terms of acoustic insulation and corrosion protection.

Vale la pena di sottolineare che la composizione di adesivo secondo l’invenzione costituisce un materiale tossicologicamente ed ecologicamente sicuro, in quanto, a differenza delle schiume poliuretaniche, non contiene né sviluppa sostanze tossiche o nocive in alcuna delle fasi della sua utilizzazione (applicazione o cottura) e non presenta alcun problema di smaltimento. It is worth underlining that the adhesive composition according to the invention constitutes a toxicologically and ecologically safe material, since, unlike polyurethane foams, it does not contain or develop toxic or harmful substances in any of the phases of its use (application or cooking ) and does not present any disposal problems.

Inoltre, la composizione dell’Invenzione presenta una notevole facilità di applicazione, che può effettuarsi con le normali attrezzature di linea impiegate da tutti i costruttori di autoveicoli per l’estrusione di adesivi e sigillanti. Tale facilità di applicazione consente vantaggiosamente un considerevole risparmio di mano d’opera in confronto al metodi che comportano l’applicazione di materiali preformati. Furthermore, the composition of the invention has a considerable ease of application, which can be carried out with the normal line equipment used by all vehicle manufacturers for the extrusion of adhesives and sealants. This ease of application advantageously allows a considerable saving of manpower compared to the methods that involve the application of preformed materials.

La facilità di applicazione della composizione dell’Invenzione è tale che se ne può realisticamente prevedere una robotizzazione, con conseguenti ulteriori vantaggi dal punto di vista del risparmio di mano d’opera e dei tempi di produzione. The ease of application of the composition of the invention is such that it can realistically be robotized, with consequent further advantages from the point of view of labor savings and production times.

Ulteriori caratteristiche e vantaggi dell’Invenzione risulteranno maggiormente da alcuni esempi di composizione di adesivi per il riempimento di parti scatolate di scocche e relativi risultati delle prove su di essi effettuate, dati qui di seguito a titolo indicativo e non limitativo e nel quali tutte le parti e percentuali sono fornite in peso sul peso totale della composizione, se non altrimenti Indicato. Further characteristics and advantages of the invention will become clearer from some examples of compositions of adhesives for filling boxed parts of bodies and relative results of the tests carried out on them, given below by way of non-limiting indication and in which all the parts and percentages are given by weight of the total weight of the composition, unless otherwise indicated.

ESEMPIO 1 EXAMPLE 1

In un miscelatore orizzontale, munito di agitatore di acciaio inox posto in rotazione a 17-25 giri/minuto, vennero successivamente dosati i seguenti componenti: In a horizontal mixer, equipped with a stainless steel stirrer set in rotation at 17-25 rpm, the following components were subsequently dosed:

Plastificanti 37 Promotori di adesione Plasticizers 37 Adhesion promoters

Additivi e pigmenti 5,5 Additives and pigments 5.5

Dopo agitazione protratta per 10 minuti per ottenere una miscelazione omogenea, alla miscela vennero ulteriormente addizionati e dosati i seguenti componenti: After prolonged stirring for 10 minutes to obtain a homogeneous mixing, the following components were further added and dosed to the mixture:

Espandente microsfere (EXPANCEL) 5 Expanding microspheres (EXPANCEL) 5

Resine viniliche 24 Vinyl resins 24

Carica a basso peso (EXPANCEL preespanso) 1,5 Low weight charge (pre-expanded EXPANCEL) 1.5

Cariche naturali e rivestite 26 Natural and coated fillers 26

Dopo ulteriore agitazione per circa 10 minuti, la miscela risultò perfettamente omogenea. After further stirring for about 10 minutes, the mixture was perfectly homogeneous.

La composizione così ottenuta venne applicata in verniciatura sulla superficie metallica già rivestita di vernice elettroforetica della parte scatolata della scocca corrispondente al puntone anteriore di un autoveicolo (modello Lancia Thema), impiegando una quantità di prodotto pari a circa 500 grammi. The composition thus obtained was applied in paint on the metal surface already coated with electrophoretic paint of the boxed part of the body corresponding to the front strut of a car (Lancia Thema model), using a quantity of product equal to about 500 grams.

L’applicazione veniva effettuata ad una temperatura ambiente di 22 °C. The application was carried out at an ambient temperature of 22 ° C.

Per cottura In forno a 145°C per 25 minuti il prodotto subì un’espansione tale da riempire completamente la suddetta parte scatolata. By cooking In the oven at 145 ° C for 25 minutes, the product underwent such an expansion as to completely fill the aforementioned boxed part.

ESEMPIO 2 EXAMPLE 2

Venne seguita la stessa procedura dell’Esempio 1, utilizzando gli stessi componenti, per ottenere una composizione in cui l’agente espandente a caldo (EXPANCEL) era compreso per il 10, 0% e la carica a basso peso (EXPANCEL preespanso) per l' 1,0%. The same procedure as in Example 1 was followed, using the same components, to obtain a composition in which the hot blowing agent (EXPANCEL) was included for 10.0% and the low weight filler (EXPANCEL pre-expanded) for the 1.0%.

La composizione venne agevolmente applicata con le apparecchiature ed I dispositivi della tecnica usuale, seguendo gli stessi lay-out. The composition was easily applied with the apparatuses and devices of the usual technique, following the same lay-out.

ESEMPIO 3 EXAMPLE 3

La procedura dell’Esempio 1 venne ripetuta con gli stessi componenti e con l’eccezione che venne usato un 15,0% di agente rigonfiente (EXPANCEL) ed uno 0,5% di carica a basso peso (EXPANCEL preespanso). The procedure of Example 1 was repeated with the same components and with the exception that a 15.0% swelling agent (EXPANCEL) and a 0.5% low weight filler (EXPANCEL pre-expanded) were used.

L’applicazione venne realizzata nella maniera descritta nell’Esempio 1. The application was carried out in the manner described in Example 1.

Sulle composizioni di adesivo ottenute secondo gli esempi precedenti vennero effettuate le prove standard normalmente previste dalle Case Automobilistiche per la valutazione dei materiali insonorizzanti utilizzati per riempire le parti scatolate delle scocche degli autoveicoli. On the adhesive compositions obtained according to the previous examples, the standard tests normally provided for by the car manufacturers for the evaluation of the soundproofing materials used to fill the boxed parts of the vehicle bodies were carried out.

Nella Tabella che segue vengono riportati i risultati di tali prove. The results of these tests are reported in the following table.

TABELLA TABLE

Fra i dati sopra riportati sono da evidenziare soprattutto quelli relativi all’assorbimento d’acqua ed alla resistenza alla corrosione, in quanto cruciali per il raggiungimento di uno degli scopi più importanti della presente invenzione, e cioè la protezione delle parti scatolate dalla corrosione. Among the data reported above, those relating to water absorption and corrosion resistance should be highlighted, as they are crucial for achieving one of the most important purposes of the present invention, namely the protection of the boxed parts from corrosion.

Tali dati sono risultati assolutamente soddisfacenti e si ritiene possano essere attribuiti alla caratteristica struttura espansa presentata dall’adesivo al termine della sua applicazione e cottura. Infatti la struttura espansa dell’adesivo comprende una pluralità di celle sferoidali, di diametro molto regolare e molto uniformemente distribuite in tutto lo spessore del riempimento costituito dail’adesivo. These data were absolutely satisfactory and it is believed that they can be attributed to the characteristic expanded structure presented by the adhesive at the end of its application and firing. In fact, the expanded structure of the adhesive includes a plurality of spheroidal cells, with a very regular diameter and very evenly distributed throughout the thickness of the filling made up of the adhesive.

Ciascuna cella è costituita da un involucro di copolimero di acrilonitrile/estere acrilico/olefina incapsulante un alcano. Each cell consists of an acrylonitrile / acrylic ester / olefin copolymer shell encapsulating an alkane.

La struttura espansa del riempimento costituito dall’adesivo The expanded structure of the filling consisting of the adhesive

non è comunque porosa, perché non è generata da sostanze che per trattamento a caldo liberano un gas, dando luogo a pori di dimensioni molto differenti fra loro e molto irregolarmente distribuiti, che costituiscono delle cavità in cui può essere raccolta umidità. however, it is not porous, because it is not generated by substances which, by heat treatment, release a gas, giving rise to pores of very different sizes and very irregularly distributed, which constitute cavities in which humidity can be collected.

Claims (7)

RIVENDICAZIONI 1. Composizione di adesivo per il riempimento di parti scatolate di scocche di autoveicoli comprendente, in percentuale in peso sul peso della composizione, da 20 a 35% di resina PVC (PVC/PVA), caratterizzata dal fatto dì comprendere da 5 a 15% di un agente rigonfiante a caldo, costituito da un copolimero acrilonitrile/estere acrilico/olefina, incapsulante una quantità appropriata di un alcano. CLAIMS 1. Composition of adhesive for filling boxed parts of vehicle bodies comprising, in percentage by weight on the weight of the composition, from 20 to 35% of PVC resin (PVC / PVA), characterized in that it comprises from 5 to 15% a hot swelling agent, consisting of an acrylonitrile / acrylic ester / olefin copolymer, encapsulating an appropriate amount of an alkane. 2. Composizione secondo la rivendicazione 1, caratterizzata dal fatto che detto copolimero incorporante un alcano è utilizzato nella forma di microsfere aventi un diametro di 8-15 micron. 2. Composition according to claim 1, characterized in that said copolymer incorporating an alkane is used in the form of microspheres having a diameter of 8-15 microns. 3. Composizione secondo la rivendicazione 2, caratterizzata dal fatto che detto alcano è isobutano. 3. Composition according to claim 2, characterized in that said alkane is isobutane. 4. Composizione secondo la rivendicazione 3, caratterizzata dal fatto di comprendere, in percentuale in peso sul peso della composizione, da 0,5% a 1,5% di carica a basso peso. 4. Composition according to claim 3, characterized in that it comprises, in percentage by weight on the weight of the composition, from 0.5% to 1.5% of low weight filler. 5. Composizione secondo la rivendicazione 4, caratterizzata dal fatto che detta carica a basso peso è costituita da un copolimero preespanso acrilonitrile/estere acrilico/oleflna incapsulante una quantità appropriata di un alcano. 5. Composition according to claim 4, characterized in that said low weight filler is constituted by a pre-expanded acrylonitrile / acrylic ester / olefin copolymer encapsulating an appropriate amount of an alkane. 6. Composizione di adesivo per il riempimento di parti scatolate di scocche di autoveicoli caratterizzata dal fatto di comprendere In percentuale in peso sul peso totale della composizione: 6. Composition of adhesive for filling boxed parts of vehicle bodies characterized by the fact that it comprises, in percentage by weight of the total weight of the composition: 7. Composizione secondo ia rivendicazione 6, caratterizzata dal fatto che detto agente rigonfiante a caldo è costituito da un copolimero acrilonltrile/estere acrilico/olefina, incapsulante una quantità appropriata di un alcano e detta carica a basso peso è costituita da un copolimero preespanso acrilonitrile/estere acrilico/olefina incapsulante una quantità appropriata di un alcano. 7. Composition according to claim 6, characterized in that said hot swelling agent is constituted by an acrylonitrile / acrylic ester / olefin copolymer, encapsulating an appropriate amount of an alkane and said low weight filler is constituted by an acrylonitrile / pre-expanded copolymer acrylic ester / olefin encapsulating an appropriate amount of a alkane.
ITMI940408A 1994-03-07 1994-03-07 COMPOSITION OF ADHESIVE FOR FILLING BOXED PARTS OF VEHICLE BODIES IT1269293B (en)