ITMI930577A1 - METHOD FOR ASSESSING THE INTERNAL QUALITY OF REFRACTORIES OBTAINED BY MOLTEN CASTING - Google Patents
METHOD FOR ASSESSING THE INTERNAL QUALITY OF REFRACTORIES OBTAINED BY MOLTEN CASTING Download PDFInfo
- Publication number
- ITMI930577A1 ITMI930577A1 IT93MI000577A ITMI930577A ITMI930577A1 IT MI930577 A1 ITMI930577 A1 IT MI930577A1 IT 93MI000577 A IT93MI000577 A IT 93MI000577A IT MI930577 A ITMI930577 A IT MI930577A IT MI930577 A1 ITMI930577 A1 IT MI930577A1
- Authority
- IT
- Italy
- Prior art keywords
- sample
- reflected
- waves
- images
- casting
- Prior art date
Abstract
Metodo per valutare la qualità interna di refrattari ottenuti per getto allo stato fuso comprendente gli stadi di: emissione di impulsi di onde elettromagnetiche da antenne di emissione e ricevimento che si muovono verticalmente nella vicinanza di una faccia laterale di un campione di refrattario ad una porzione interna del campione attraverso la sua faccia laterale in riferimento di posizione a quando il campione è ottenuto per getto; ricevimento di onde elettromagnetiche riflesso dal campione da parte delle antenne di emissione e ricevimento ottenendo così una rappresentazione grossolana di immagini di onde riflesse e valutazione della struttura interna del campione sulla base della rappresentazione delle immagini delle onde riflesse.Method for evaluating the internal quality of refractories obtained by casting in the molten state comprising the stages of: emission of electromagnetic wave impulses from emission and reception antennas that move vertically in the vicinity of a lateral face of a refractory sample to an internal portion of the sample through its lateral face in position reference to when the sample is obtained by casting; reception of electromagnetic waves reflected by the sample by the emission and reception antennas thus obtaining a rough representation of images of reflected waves and evaluation of the internal structure of the sample on the basis of the representation of the images of the reflected waves.
Description
Descrizione di un'invenzione avente per titolo: Description of an invention entitled:
"METODO PER VALUTARE LA QUALIT? INTERNA DI REFRAT-TARI OTTENUTI MEDIANTE GETTO ALLO STATO FUSO" "METHOD FOR ASSESSING THE INTERNAL QUALITY OF REFRAT-TARI OBTAINED BY MOLTEN CASTING"
BASE DELL'INVENZIONE BASIS OF THE INVENTION
CAMPO DELL'INVENZIONE FIELD OF THE INVENTION
Questa invenzione si riferisce ad un metodo per valutare la qualit? interna di refrattari ottenuti mediante getto allo stato fuso, che ? condotto in modo non distruttivo. This invention relates to a method for evaluating the quality? internal of refractories obtained by casting in the molten state, which? conducted in a non-destructive way.
DISCUSSIONE DELLA SITUAZIONE DI BASE DISCUSSION OF THE BASIC SITUATION
Poich? i refrattari ottenuti mediante getto allo stato fuso sono provvisti di eccellente resistenza alla corrosione da parte del vetro fuso, i refrattari ottenuti mediante getto allo stato fuso sono stati utilizzati principalmente in parti di un forno da vetro in contatto con il vetro fuso. In particolare, poich? sono usati refrattari ottenuti per getto allo stato fuso contenenti una grande quantit? di componente e aventi una lunga durata di utilizzo, le durate di utilizzo della maggior parte dei forni da vetro superano 10 anni. Since? the refractories obtained by melt casting have excellent resistance to corrosion by the molten glass, the refractories obtained by casting in the molten state have been mainly used in parts of a glass furnace in contact with the molten glass. In particular, since? are used refractories obtained by casting in the molten state containing a large amount? of component and having a long service life, the service life of most glass furnaces exceed 10 years.
Tuttavia, all' elevarsi dello standard di qualit? richiesto per prodotti di vetro, diventano pi? dure le condizioni operative dei forni da vetro. In particolare, ? richiesta una elevata qualit? per i refrattari ottenuti mediante getto allo stato fuso chiamati "blocco per forno", che sono utilizzati nelle pareti laterali dei forni da vetro. However, as the quality standard rises? required for glass products, they become more? the operating conditions of glass furnaces were harsh. In particular, ? request a high quality? for the refractories obtained by casting in the molten state called "furnace blocks", which are used in the side walls of glass furnaces.
Quando i refrattari ottenuti mediante getto allo stato fuso sono utilizzati in un forno da vetro, i refrattari sono preferibilmente rivestiti in considerazione delle posizioni dei loro difetti interni in modo tale che le loro durate di utilizzo vengano rese eguali e la durata di utilizzo del forno da vetro non sia considerevolmente accorciata per effetto dei difetti interni dei refrattari ottenuti mediante getto allo stato fuso. Tuttavia, quando sono utilizzati in un forno da vetro refrattari ottenuti mediante getto allo stato fuso le cui qualit? interne non sono sufficientemente note, vi sono dei casi inevitabili in cui il vetro fuso fuoriesce dalle pareti laterali del forno da vetro, che si aspettava avesse una sufficiente durata di utilizzo, anche se sono impiegati refrattari densi ottenuti mediante getto allo stato fuso, del tipo chiamato esente da vuoti (VF). (Il refrattario del tipo VF presenta piccoli difetti poich? una grande porzione superiore del refrattario ottenuto mediante getto allo stato fuso che presenta molti difetti ? stata eliminata). When melt-cast refractories are used in a glass furnace, the refractories are preferably coated in consideration of the locations of their internal defects so that their service life is equalized and the service life of the furnace by glass is not considerably shortened due to the internal defects of the refractories obtained by casting in the molten state. However, when melt cast refractories are used in a furnace from glass whose qualities? are not sufficiently known, there are inevitable cases in which the molten glass comes out from the side walls of the glass furnace, which was expected to have a sufficient duration of use, even if dense refractories obtained by casting in the molten state are used, such as called void-free (VF). (The VF type refractory has small defects as a large upper portion of the cast investment which has many defects has been eliminated.)
Esiste una forte richiesta da parte di utilizzatori dei forni da vetro relativa alla precisa valutazione della qualit? interna dei refrattari ottenuti mediante getto allo stato fuso, in modo tale da evitare i problemi precedentemente citati, rendere possibile l'eliminazione di personale di manutenzione necessario per effettuare una riparazione temporanea e poter assicurare una lunga durata di utilizzo del forno dal vetro. Is there a strong demand from users of glass kilns for the precise assessment of quality? of the refractories obtained by casting in the molten state, in such a way as to avoid the aforementioned problems, to make it possible to eliminate the maintenance personnel necessary to carry out a temporary repair and to be able to ensure a long duration of use of the furnace from the glass.
Recentemente, sono comunemente utilizzati come mezzo per investigare le qualit? interne dei prodotti ceramici il metodo di ispezione con i raggi X o il metodo di ispezione con gli ultrasuoni. Tuttavia, nel metodo di ispezione con i raggi X, per l'ispezione di prodotti ceramici di grandi dimensioni contenenti una sostanza a bassa trasmitt?nza dei raggi X, per esempio una sostanza contenente elementi pesanti come Zr02, ? necessario un dispositivo di ispezione a raggi X con una emissione di raggi X di elevata potenza. Inoltre, nel metodo di ispezione con ultrasuoni, ? necessario usare un mezzo di trasmissione, come acqua o grasso, per trasmettere sufficientemente le onde di ultrasuoni da un oscillatore e ricevere le onde di ultrasuoni riflessi dall'interno del campione da ispezionare, e la misura non ? semplice da effettuare. Recently, they are commonly used as a means of investigating qualities. internal ceramic products the X-ray inspection method or the ultrasonic inspection method. However, in the X-ray inspection method, for the inspection of large ceramic products containing a substance with low X-ray transmittance, for example a substance containing heavy elements such as Zr02,? an X-ray inspection device with a high-power X-ray emission is required. Also, in the ultrasonic inspection method,? It is necessary to use a transmission medium, such as water or grease, to sufficiently transmit the ultrasound waves from an oscillator and receive the reflected ultrasound waves from within the sample to be inspected, and the measurement does not? simple to carry out.
Inoltre, i risultati dell'ispezione sono spesso visualizzati semplicemente come immagine, metodo di ispezione che non ? sufficiente per valutare in modo preciso la qualit? interna inclusa la posizione dei difetti o la determinazione della loro natura . In addition, the inspection results are often displayed simply as an image, which inspection method is not? sufficient to accurately assess the quality? internal including the location of the defects or the determination of their nature.
In modo particolare, quando il campione ? un refrattario ottenuto per getto allo stato fuso, una valutazione precisa ? difficile poich? vi sono difetti al suo interno quali soffiature, serie di piccoli pori e cristalli grossolani miscelati con pori. In particular, when the champion? a refractory obtained by casting in the molten state, a precise evaluation? difficult since? there are defects in it such as blowholes, series of small pores and coarse crystals mixed with pores.
E' stato proposto un dispositivo per ricercare oggetti sotterranei, come tecnologia recente, in cui nuclei di ferro esistenti in cemento armato possono essere rilevati mediante onde elettromagnetiche, come nei brevetti giapponesi non esaminati pubblicazioni n. 54191/1990, 52272/1990 e 126176/1990. Secondo questa tecnologia ? possibile rivelare la presenza di nuclei di ferro ad approssimativamente 20 cm di profondit? nel cemento ar? A device has been proposed to search for underground objects, as a recent technology, in which existing iron cores in reinforced concrete can be detected by electromagnetic waves, as in Japanese Patent Unexamined Publications No. 54191/1990, 52272/1990 and 126176/1990. According to this technology? Is it possible to detect the presence of iron nuclei at approximately 20 cm deep? in the concrete ar?
Nel dispositivo per rivelare oggetti sotterranei, antenne di emissione e di ricevimento che si muovono in parallelo con una superficie del campione emettono onde elettromagnetiche e ricevono onde elettromagnetiche riflesse dalla superficie limite (o dall'oggetto) del campione con differenti propriet? elettriche (costante dielettrica) e cos? il dispositivo fornisce la distanza dalla superficie del campione all'oggetto, calcolata in base al tempo tra l'emissione e il ricevimento, e visualizza la posizione dell'oggetto e lo stato in cui si trova in corrispondenza con la posizione assunta in movimento dalle antenne di emissione e ricevimento, come immagine elaborata mediante calcolatore. In the device for detecting underground objects, emitting and receiving antennas that move in parallel with a sample surface emit electromagnetic waves and receive electromagnetic waves reflected from the boundary surface (or object) of the sample with different properties. electrical (dielectric constant) and cos? the device provides the distance from the sample surface to the object, calculated based on the time between emission and receipt, and displays the position of the object and the state in which it is in correspondence with the position assumed in motion by the antennas of emission and reception, as a computer-processed image.
Inoltre, nel' brevetto giapponese non esaminato pubblicazione n. 81679/1992 ? proposta una tecnologia in cui lo spessore restante di refrattario di un forno da vetro ? misurato utilizzando un tale dispositivo e si suggerisce che la tecnologia pu? essere usata per l'ispezione dei materiali refrattari al momento della spedizione. Furthermore, in the Japanese Unexamined Patent Publication No. 81679/1992? proposed a technology in which the remaining thickness of refractory of a glass furnace? measured using such a device and it is suggested that the technology can? be used for inspection of refractory materials at the time of shipment.
SOMMARIO DELL'INVENZIONE SUMMARY OF THE INVENTION
Uno scopo della presente invenzione ? quello di rimediare agli inconvenienti della tecnologia convenzionale nella valutazione della qualit? interna di prodotti ceramici e in particolare di fornire un metodo pratico per valutare in modo preciso e quantitativo la qualit? interna di refrattari ottenuti mediante getto allo stato fuso. Ci? ? effettuato effettuando una ispezione dei refrattari ottenuti mediante getto allo stato fuso, usati principalmente in forni da vetro, utilizzando le caratteristiche peculiari dei refrattari ottenuti per getto allo stato fuso. A purpose of the present invention? to remedy the drawbacks of conventional technology in assessing quality? internal ceramic products and in particular to provide a practical method to evaluate the quality in a precise and quantitative way? internal of refractories obtained by casting in the molten state. There? ? carried out by carrying out an inspection of the refractories obtained by casting in the molten state, mainly used in glass furnaces, using the peculiar characteristics of the refractories obtained by casting in the molten state.
Secondo un aspetto della presente invenzione, viene fornito un metodo per valutare la qualit? interna dei refrattari ottenuti per getto allo stato fuso comprendente gli stadi di: According to one aspect of the present invention, a method is provided for evaluating the quality. of the refractories obtained by casting in the molten state comprising the stages of:
emissione di impulsi di onde elettromagnetiche da antenne di emissione e ricevimento che si muovono verticalmente in vicinanza di una faccia laterale di un campione di refrattario fino ad una porzione interna del campione attraverso la sua faccia laterale in riferimento di posizione a quando il campione ? ottenuto mediante getto; emission of pulses of electromagnetic waves from emitting and receiving antennas moving vertically in the vicinity of a lateral face of a refractory sample to an internal portion of the sample through its lateral face in reference to position when the sample? obtained by casting;
ricevimento di onde elettromagnetiche riflesse dal campione da parte di antenne di emissione e ricevimento ottenendo in questo modo una rappresentazione grossolana di immagini di onde riflesse e valutazione della struttura interna del campione di refrattario sulla base della rappresentazione grossolana di immagini di onde riflesse. reception of electromagnetic waves reflected from the sample by emitting and receiving antennas thus obtaining a coarse representation of images of reflected waves and evaluation of the internal structure of the refractory sample on the basis of the coarse representation of images of reflected waves.
In questa invenzione, la direzione verticale del refrattario ottenuto mediante getto allo stato fuso ? riferita alla posizione che esso aveva quando fu ottenuto mediante getto e questa condizione ? mantenuta nelle descrizioni seguenti. Tuttavia, nella effettuazione effettiva dell'ispezione del campione di refrattario, ? spesso conveniente effettuare l'ispezione in uno stato in cui il refrattario alto, ottenuto mediante getto allo stato fuso, ? ruotato di 90? e si trova in disposto di lato. Il metodo di valutazione della qualit? interna di refrattari ottenuti mediante getto allo stato fuso di questa invenzione include una tale attuazione. Una tale espressione ? adottata per chiarire la relazione di posizione. In this invention, the vertical direction of the refractory obtained by casting in the molten state? referred to the position it had when it was obtained by casting and this condition? maintained in the following descriptions. However, in the actual inspection of the refractory sample,? it is often convenient to carry out the inspection in a state in which the high refractory, obtained by casting in the molten state,? rotated by 90? and is placed sideways. The method of assessing the quality? interior of melt cast refractories of this invention includes such an embodiment. Such an expression? adopted to clarify the position report.
I refrattari ottenuti mediante getto allo stato fuso' sono composti da una struttura densa quasi senza pori ad eccezione delle porzioni che presentano dei difetti. La porzione della struttura densa trasmette bene le onde elettromagnetiche in confronto al cemento. Quindi, anche quando i difetti della struttura densa sono comparativamente piccoli, le onde elettromagnetiche riflesse possono essere ricevute. Quindi, il metodo di ispezione che utilizza un'onda elettromagnetica ? adatto per la valutazione della qualit? interna dei refrattari ottenuti mediante getto allo stato fuso. The refractories obtained by casting in the molten state are composed of a dense structure with almost no pores except for the portions that have defects. The dense portion of the structure transmits electromagnetic waves well compared to concrete. Hence, even when the defects of the dense structure are comparatively small, reflected electromagnetic waves can be received. So, the inspection method that uses an electromagnetic wave? suitable for quality assessment? of the refractories obtained by casting in the molten state.
Quando il refrattario ottenuto per getto allo stato fuso ? delle dimensioni che sono necessarie per poter essere utilizzato nel forno da vetro, il metodo di valutazione della qualit? interna di questa invenzione pu? essere utilizzato quasi senza problemi . When is the refractory obtained by casting in the molten state? of the dimensions that are necessary to be used in the glass furnace, the method of evaluating the quality? internal of this invention can? be used almost without problems.
Le onde elettromagnetiche hanno la propriet? di essere riflesse ad una superficie limite in cui la costante dielettrica varia. La distanza tra la superficie e i difetti in cui le onde elettromagnetiche sono riflesse, pu? essere calcolata dal tempo necessario per il ritorno delle onde elettromagnetiche riflesse. In altre parole, ? possibile rivelare i difetti interni del refrattario ricevendo le onde riflesse dai difetti presenti nel refrattario utilizzando il principio del radar. Electromagnetic waves have the property? to be reflected at a boundary surface where the dielectric constant varies. The distance between the surface and the defects in which the electromagnetic waves are reflected, can? be calculated from the time required for the return of the reflected electromagnetic waves. In other words, ? It is possible to detect the internal defects of the refractory by receiving the waves reflected by the defects present in the refractory using the principle of radar.
Per questo metodo di valutazione della qualit? interna di refrattari ottenuti mediante getto allo stato fuso di questa invenzione, pu? essere utilizzato un rivelatore di oggetti sotterranei o un rivelatore di oggetti esistenti in una massa di cemento. Le antenne di emissione e di ricevimento sono costituite da un'antenna di emissione e da un'antenna di ricevimento che sono sistemate in posizione contigua. La presenza di difetti interni dei refrattari ottenuti mediante getto allo stato fuso pu? essere rivelata mediante esame delle onde riflesse da porzioni diverse dalla superficie esterna del campione di refrattario. Nel metodo di valutazione della qualit? interna di refrattari ottenuti mediante getto allo stato fuso di questa invenzione, lo scopo pu? essere raggiunto analizzando le onde riflesse in posizioni in cui non si abbia praticamente alcuna sovrapposizione con le immagini delle onde riflesse dalla superficie. For this quality assessment method? interior of refractories obtained by casting in the molten state of this invention, can? an underground object detector or an existing object detector in a concrete mass be used. The emitting and receiving antennas consist of an emitting antenna and a receiving antenna which are arranged in contiguous position. The presence of internal defects of the refractories obtained by casting in the molten state can? be detected by examination of the waves reflected from portions other than the outer surface of the refractory sample. In the quality assessment method? internal of refractories obtained by casting in the molten state of this invention, the purpose can? be achieved by analyzing the waves reflected in positions where there is practically no overlap with the images of the waves reflected from the surface.
In questo metodo, l'ispezione pu? essere effettuata senza alcun contatto per effetto delle propriet? delle onde elettromagnetiche, senza usare un mezzo di trasmissione, come acqua o grasso, quale si utilizza nel metodo che sfrutta le onde di ultrasuoni. Non ? necessario fare attenzione alle condizioni della superficie del campione. La riproducibilit? del risultato dell'ispezione ? buona. In this method, the inspection can? be carried out without any contact due to the properties? of electromagnetic waves, without using a transmission medium, such as water or fat, which is used in the method that uses ultrasound waves. Do not ? attention must be paid to the condition of the sample surface. The reproducibility? the inspection result? good.
Inoltre, quando il dispositivo di ispezione ? munito di una funzione di elaborazione dell'immagine, in cui un microcalcolatore ? integrato adottando i recenti progressi dell'elettronica, il dispositivo pu? presentare una buona prestazione operativa e pu? essere utilizzato per ispezionare la qualit? interna dei refrattari ottenuti mediante getto allo stato fuso nel posto di produzione. Also, when the inspection device? equipped with an image processing function, in which a microcomputer? integrated by adopting the recent advances in electronics, the device can? present a good operational performance and can? be used to inspect the quality? of the refractories obtained by casting in the molten state at the production site.
I refrattari ottenuti mediante getto allo stato fuso sono prodotti gettando e solidificando materiale refrattario allo stato fuso in stampi di sabbia o in stampi di grafite. In molti casi, i refrattari ottenuti mediante getto allo stato fuso presentano forme con piani di simmetria o con una coppia di piani paralleli opposti nella direzione verticale. Cio?, il materiale fuso ? gettato in uno stampo avente una coppia di facce interne parallele. In questo caso, il calore sensibile della sostanza fusa e il calore latente generato nella sua solidificazione passano dall'interno del materiale refrattario alle pareti dello stampo che circondano il refrattario. Quindi, la solidificazione inizia dalla superficie del refrattario e procede verso la sua porzione interna. Molten cast refractories are produced by casting and solidifying molten refractory material in sand molds or graphite molds. In many cases, the refractories obtained by casting in the molten state have shapes with planes of symmetry or with a pair of parallel planes opposite in the vertical direction. That is, the molten material? cast in a mold having a pair of parallel internal faces. In this case, the sensible heat of the molten substance and the latent heat generated in its solidification pass from the inside of the refractory material to the walls of the mold that surround the refractory. Then, solidification starts from the surface of the refractory and proceeds towards its internal portion.
Inoltre, poich? il volume della sostanza fusa si riduce durante la solidificazione, la superficie libera della sostanza fusa si muove gradualmente verso il basso e provoca cos? soffiature nella porzione centrale superiore del refrattario. Quindi, nella porzione superiore dello stampo ? prevista una porzione chiamata apertura di alimentazione del fuso, sostanza fusa aggiuntiva ? versata nella porzione e l'apertura di alimentazione di fuso solidificato contenente soffiature ? scartata dopo l'effettuazione del getto. Furthermore, since? the volume of the molten substance is reduced during solidification, the free surface of the molten substance gradually moves downwards and causes cos? blowholes in the upper central portion of the refractory. So, in the upper portion of the mold? provided a portion called melt feed port, additional melt? poured into the portion and the solidified melt feed port containing blowholes? discarded after casting.
Al procedere della solidificazione del materiale refrattario, si registra una differenza? di composizione chimica tra la parte che solidifica per prima e la parte che solidifica successivamente. I cristalli della parte che solidifica rapidamente sono piccoli e i cristalli della parte che solidifica gradualmente sono generalmente grandi. Cristalli prismatici allungati si formano nella direzione di crescita dei cristalli. Quindi, la struttura del refrattario ottenuto mediante getto allo stato fuso normalmente varia a seconda della sua posizione. Is there a difference as the refractory material solidifies? of chemical composition between the part that solidifies first and the part that solidifies later. The crystals of the part that solidifies quickly are small and the crystals of the part that gradually solidifies are usually large. Elongated prismatic crystals are formed in the direction of crystal growth. Therefore, the structure of the refractory obtained by casting in the molten state normally varies according to its position.
Al procedere ulteriore della solidificazione, anche se le condizioni di conduzione termica sono controllate in modo tale che la solidificazione proceda dalla base, la sostanza fusa spesso non pu? muoversi verso il basso. Inoltre la solidificazione procede in uno spazio chiuso. Nel refrattario si formano spazi vuoti (chiamati soffiature) corrispondenti al volume di ritiro della sostanza fusa solidificata . As solidification proceeds further, even if the conditions of thermal conduction are controlled in such a way that solidification proceeds from the base, the molten substance often cannot. move down. Furthermore, solidification proceeds in a closed space. In the refractory, empty spaces (called blowholes) are formed corresponding to the shrinkage volume of the solidified molten substance.
Relativamente alla struttura del refrattario ottenuto mediante getto allo stato fuso, quando la forma del refrattario presenta un piano di simmetria verticale in riferimento di posizione a quando il refrattario ? stato ottenuto per getto, il refrattario ottenuto per getto allo stato fuso presenter? una struttura che ? quasi simmetrica rispetto al piano di simmetria, poich? la distribuzione di temperatura all'interno del refrattario ottenuto mediante getto allo stato fuso durante la solidificazione ? simmetrica rispetto al piano di simmetria. Regarding the structure of the refractory obtained by casting in the molten state, when the shape of the refractory presents a plane of vertical symmetry in reference to position a when the refractory? been obtained by casting, the refractory obtained by casting in the molten state will present? a structure that? almost symmetrical with respect to the plane of symmetry, since? the temperature distribution inside the refractory obtained by casting in the molten state during solidification? symmetrical with respect to the plane of symmetry.
In questo caso, (quando) impulsi di onde elettromagnetiche sono emessi contro il piano di simmetria da una delle facce laterali del refrattario ottenuto per getto allo stato fuso che ? approssimativamente parallela al piano di simmetria. Poich? la struttura presenta una simmetria, non ? necessario analizzare tutte le immagini ottenute dalle onde riflesse. E' possibile valutare l'intera qualit? interna del refrattario ottenuto mediante getto allo stato fuso da una parte delle immagini di onde riflesse. In questo metodo di valutazione della qualit? interna di refrattari ottenuti mediante getto allo stato fuso di questa invenzione, poich? la simmetria della struttura interna del refrattario relativamente al piano di simmetria ? quasi fissa, la valutazione della qualit? interna di tutta la massa dei refrattari ottenuti mediante getto allo stato fuso pu? essere facilitata. In this case, (when) pulses of electromagnetic waves are emitted against the plane of symmetry from one of the lateral faces of the refractory obtained by casting in the molten state which? approximately parallel to the plane of symmetry. Since? the structure has a symmetry, doesn't it? It is necessary to analyze all the images obtained from the reflected waves. Is it possible to evaluate the whole quality? interior of the refractory obtained by casting in the molten state from a part of the images of reflected waves. In this quality assessment method? internal of refractories obtained by casting in the melt state of this invention, since? the symmetry of the internal structure of the refractory relative to the plane of symmetry? almost fixed, the evaluation of the quality? internal of the whole mass of the refractories obtained by casting in the molten state pu? be facilitated.
Le antenne di emissione e di ricevimento sono disposte nelle vicinanze del campione di refrattario in modo tale che i rumori prodotti dalle onde riflesse da parte degli oggetti circostanti possono essere trascurati. Il campione ? sottoposto a scansione da parte degli impulsi di onde elettromagnetiche emessi dalle antenne di emissione e ricevimento che si muovono verticalmente. La scansione ? preferibilmente effettuata muovendo in parallelo le antenne di emissione e ricevimento lungo una faccia laterale del campione. Gli impulsi di onde elettromagnetiche emessi normalmente hanno un considerevole angolo di osservazione (per esempio 90?) e sono riflessi dalla faccia laterale di incidenza del campione dai difetti interni, dalla faccia laterale posteriore opposta alla faccia laterale di incidenza e dalle altre facce laterali e limite per essere ricevuta dalle antenne di emissione e ricevimento. Le onde riflesse includono onde di rumori che sono riflessi dalle facce laterali di incidenza e posteriore in tempi diversi e sono chiamate onde molteplicemente riflesse. The emitting and receiving antennas are arranged in the vicinity of the refractory sample in such a way that the noises produced by the waves reflected by the surrounding objects can be neglected. The sample ? scanned by the pulses of electromagnetic waves emitted by the emitting and receiving antennas which move vertically. Scan ? preferably carried out by moving the emitting and receiving antennas in parallel along a lateral face of the sample. The pulses of electromagnetic waves emitted normally have a considerable viewing angle (for example 90 °) and are reflected from the lateral incidence face of the sample by the internal defects, from the posterior lateral face opposite to the lateral incidence face and from the other lateral and limit faces to be received by the emitting and receiving antennas. Reflected waves include noise waves that are reflected from the incident side and back faces at different times and are called multiply reflected waves.
E' possibile rilevare la posizione in cui l'onda elettromagnetica ? riflessa rispetto alla posizione verticale del refrattario ottenuto mediante getto allo stato fuso ricevendo le onde elettromagnetiche riflesse con le antenne di ricevimento e di emissione. E' possibile ottenere una rappresentazione di immagini di onde riflesse del refrattario, incluse le immagini di onde riflesse dalle superfici, che corrisponda alla sezione verticale del refrattario ottenuto per getto allo stato fuso, mediante scansione con gli impulsi di onde elettromagnetiche. E' possibile visualizzare immediatamente la rappresentazione di immagini delle onde riflesse su di un visualizzatore del dispositivo di ispezione integrato con un microcalcolatore . Is it possible to detect the position where the electromagnetic wave? reflected with respect to the vertical position of the refractory obtained by casting in the molten state, receiving the electromagnetic waves reflected with the receiving and emitting antennas. It is possible to obtain a representation of images of reflected waves of the refractory, including images of waves reflected from the surfaces, which corresponds to the vertical section of the refractory obtained by casting in the molten state, by scanning with the pulses of electromagnetic waves. It is possible to immediately visualize the representation of images of the reflected waves on a viewer of the inspection device integrated with a microcomputer.
In una attuazione preferibile del metodo di valutazione della qualit? interna di refrattari ottenuti mediante getto allo stato fuso di questa invenzione, una rappresentazione elaborata di onde riflesse ? ottenuta rimuovendo immagini di umori di onde riflesse provocati dalla superficie o dalle superfici del campione dalla rappresentazione grossolana di immagini di onde riflesse o rimuovendo le onde riflesse di rumori provocati dalla superficie o dalle superfici del campione dalle onde riflesse ricevute del campione. In questo modo la valutazione della qualit? interna del campione utilizzando la rappresentazione elaborata di immagini di onde riflesse risulta facilitata. In a preferable implementation of the quality assessment method? interior of melt-cast refractories of this invention, an elaborate representation of reflected waves? obtained by removing images of reflected wave humours caused by the sample surface (s) from the coarse representation of reflected wave images or by removing reflected noise waves caused by the sample surface (s) from received sample reflected waves. In this way the evaluation of the quality? internal sample using the elaborate representation of reflected wave images is facilitated.
Un metodo semplice per rimuovere le immagini provocate dalle onde riflesse dalle superfici ? quello di ottenere separatamente una rappresentazione di immagini di onde riflesse di refrattari ottenuti mediante getto allo stato fuso senza difetti (sono presenti solo immagini di onde riflesse dalle superfici), sottrarre questa rappresentazione di immagini di onde riflesse dalle superfici dalla rappresentazione di immagini di onde riflesse del campione e ottenere una rappresentazione elaborata di immagini di onde riflesse provocate soltanto dai difetti interni. In questa sottrazione non ? sempre necessario rimuovere le immagini riflesse in modo molteplice dalle superfici, che sono presenti nella rappresentazione vicine alla singola immagine di onde riflesse dalla superficie posteriore del campione. A simple method to remove images caused by waves reflected from surfaces? to separately obtain a representation of images of reflected waves of refractories obtained by casting in the melt state without defects (there are only images of waves reflected from the surfaces), subtract this representation of images of waves reflected by surfaces from the representation of images of reflected waves sample and obtain an elaborate representation of reflected wave images caused only by internal defects. In this subtraction not? It is always necessary to remove the multiply reflected images from the surfaces, which are present in the representation close to the single image of waves reflected from the back surface of the sample.
Nella specifica formazione di una immagine di onde riflesse del campione refrattario senza immagine di onde riflesse dalle superfici, la rappresentazione di immagini delle onde riflesse dalle superfici ? memorizzata nella memoria di un microcalcolatore del dispositivo di ispezione e la sottrazione delle onde riflesse dalle superfici o delle immagini di onde riflesse dalle superfici ? effettuata in modo automatico. In questo modo, pu? essere ottenuta una rappresentazione elaborata delle immagini delle onde riflesse, senza le onde riflesse dalle superfici prodotte dalle superfici del campione. Inoltre, quando la forma della sezione del campione di refrattario non varia nella posizione verticale, ? possibile ottenere la rappresentazione elaborata delle immagini delle onde riflesse senza le immagini delle onde riflesse dalle superfici semplicemente sottraendo le immagini delle onde riflesse dalle superfici ottenute dalla porzione senza difetti interni. Quando gli impulsi di onde elettromagnetiche emessi sono accompagnati da un rumore (onda secondaria), l'interpretazione dell'immagine delle onde riflettenti ? ulteriormente facilitata effettuando la rimozione delle onde riflesse dei rumori (sottrazione) contemporaneamente con la rimozione delle onde molteplicemente riflesse. In the specific formation of a reflected wave image of the refractory sample without an image of waves reflected from the surfaces, the representation of images of the waves reflected from the surfaces? stored in the memory of a microcomputer of the inspection device and the subtraction of waves reflected by surfaces or images of waves reflected by surfaces? carried out automatically. In this way, it can? an elaborate representation of the reflected wave images be obtained, without the reflected waves from the surfaces produced by the sample surfaces. Also, when the section shape of the refractory sample does not vary in the vertical position,? It is possible to obtain the elaborate representation of the images of the reflected waves without the images of the waves reflected by the surfaces simply by subtracting the images of the waves reflected by the surfaces obtained from the portion without internal defects. When the emitted electromagnetic wave pulses are accompanied by a noise (secondary wave), the image interpretation of the reflective waves? further facilitated by carrying out the removal of the reflected noise waves (subtraction) simultaneously with the removal of the multiply reflected waves.
In un'altra attuazione preferibile di un metodo di valutazione della qualit? interna di refrattari ottenuti mediante getto allo stato fuso di questa invenzione, la valutazione del campione di refrattario ? effettuata sulla base delle immagini delle onde riflesse rispetto ad una met? della rappresentazione delle immagini delle onde riflesse tra una faccia laterale di incidenza e il piano centrale (il piano di simmetria verticale) a met? della distanza tra la faccia laterale d'incidenza e la faccia laterale posteriore. In another preferable implementation of a quality assessment method? internal of melt cast refractories of this invention, the refractory sample evaluation? carried out on the basis of the images of the waves reflected with respect to a half? of the representation of the images of the waves reflected between a lateral incidence face and the central plane (the plane of vertical symmetry) in the middle? of the distance between the lateral incidence face and the posterior lateral face.
Adottando il metodo di emettere gli impulsi di onde elettromagnetiche contro il piano di simmetria verticale del refrattario ottenuto mediante getto allo stato fuso, quando l'analisi ? effettuata su una met? della rappresentazione ottenuta di immagini delle onde riflesse, pu? essere effettuata la valutazione completa del refrattario ottenuto mediante getto allo stato fuso. By adopting the method of emitting pulses of electromagnetic waves against the plane of vertical symmetry of the refractory obtained by casting in the molten state, when the analysis? carried out on a half? of the representation obtained of images of the reflected waves, pu? the complete evaluation of the refractory obtained by casting in the molten state be carried out.
Inoltre, relativamente alle immagini ottenute, ci sono porzioni leggere e profonde. Si effettua un esame delle immagini delle onde riflesse della rappresentazione di immagini relativamente alla met? della distanza tra la faccia laterale di incidenza e la faccia laterale posteriore. Si conferma che la porzione profonda dell'immagine corrisponde a un grande difetto, come una soffiatura o un aggregato di cristalli grossolani, mentre la porzione leggera dell'immagine corrisponde a difetti, per esempio piccoli pori o cristalli grossolani, tagliando il campione di refrattario e confrontando il campione tagliato con le immagini ottenute mediante la prova di ispezione. Inoltre, si ? trovato che l'area integrata delle immagini profonde e l'area integrata delle immagini leggere indicano le dimensioni o i gradi dei rispettivi difetti. Furthermore, in relation to the images obtained, there are light and deep portions. Is an examination of the reflected wave images of the image representation relative to the half? of the distance between the lateral incidence face and the posterior lateral face. It is confirmed that the deep portion of the image corresponds to a large defect, such as a blow or an aggregate of coarse crystals, while the light portion of the image corresponds to defects, for example small pores or coarse crystals, by cutting the refractory sample and comparing the cut sample with the images obtained by the inspection test. Also, yes? found that the integrated area of the deep images and the integrated area of the light images indicate the sizes or degrees of the respective defects.
In un'altra attuazione preferibile di un metodo di valutazione della qualit? interna di refrattari ottenuti mediante getto allo stato fuso di questa invenzione, la valutazione del campione di refrattario ? effettuata emettendo gli impulsi di onde elettromagnetiche contro il piano di simmetria verticale del campione da una direzione approssimativamente ortogonale rispetto al piano di simmetria verticale del campione. Nell'ottenimento di immagini di onde riflesse ? possibile minimizzare le immagini di onde riflesse che sono difficili da interpretare, adottando una tale relazione di posizione con il piano di simmetria del campione ed ? quindi possibile effettuare la valutazione della qualit? interna facilmente e con buona affidabilit?. In another preferable implementation of a quality assessment method? internal of melt cast refractories of this invention, the refractory sample evaluation? carried out by emitting pulses of electromagnetic waves against the vertical symmetry plane of the sample from a direction approximately orthogonal to the vertical symmetry plane of the sample. In obtaining images of reflected waves? possible to minimize reflected wave images that are difficult to interpret by adopting such a position relationship with the sample symmetry plane and d? therefore it is possible to carry out the evaluation of the quality? internal easily and with good reliability.
In un'altra attuazione preferibile di un metodo per valutare la qualit? interna di refrattari ottenuti mediante getto allo stato fuso di questa invenzione, il campione di refrattario ? ripartito in 1, 2, ..., n parti ipotizzando (n-1) piani orizzontali, la rappresentazione delle immagini delle onde riflesse ? divisa in 1, 2, ..., n porzioni corrispondenti rispettivamente alle parti in cui ? stato suddiviso il campione e le rispettive parti del campione sono valutate sulla base delle porzioni rispettive della rappresentazione suddivisa delle immagini delle onde riflesse. In another preferable implementation of a method for assessing the quality? interior of melt cast refractories of this invention, the refractory sample? divided into 1, 2, ..., n parts assuming (n-1) horizontal planes, the representation of the images of the reflected waves? divided into 1, 2, ..., n portions corresponding respectively to the parts in which? The sample has been split and the respective parts of the sample are evaluated on the basis of the respective portions of the split representation of the reflected wave images.
Per esempio, il campione ? suddiviso in 4 parti con 3 piani orizzontali e la rappresentazione ottenuta delle immagini delle onde riflesse ? suddivisa in 4 porzioni corrispondenti alle rispettive parti. Quando il refrattario ottenuto mediante getto allo stato fuso ? ripartito in l, 2, 3 e 4 parti a partire dalla porzione superiore (1 ? sul lato dell'apertura di getto in cui ? eliminata l'apertura di alimentazione del fuso), la rappresentazione di immagini di onde riflesse ? suddivisa in porzioni corrispondenti 1,2,3 e 4 e la valutazione pu? essere effettuata relativamente a ciascuna parte. For example, the champion? divided into 4 parts with 3 horizontal planes and the representation obtained of the images of the reflected waves? divided into 4 portions corresponding to the respective parts. When is the refractory obtained by casting in the molten state? divided into 1, 2, 3 and 4 parts starting from the upper portion (1? on the side of the casting opening where the melt supply opening is eliminated), the representation of images of reflected waves? divided into corresponding portions 1,2,3 and 4 and the evaluation can? be carried out in relation to each party.
La valutazione della qualit? interna relativamente a ciascuna parte pu?, per esempio, essere effettuata nel seguente modo. Rispetto ad una met? della rappresentazione di immagini delle onde riflesse fino a met? profondit? a partire dalla faccia laterale di incidenza, ciascuna area sommata di immagini profonde e ciascuna area sommata di immagini leggere nelle porzioni 1, 2, 3 e 4 ? misurata relativamente a ciascuna parte e le qualit? delle rispettive parti sono indicate con A, B, C e D o con valori di valutazione (Ti) sulla base di uno standard mostrato in Tabella 1. The evaluation of the quality? internal for each part can, for example, be done in the following way. Compared to a half? of the representation of images of the waves reflected up to half? depth starting from the lateral face of incidence, each summed area of deep images and each summed area of light images in portions 1, 2, 3 and 4? measured relative to each part and the qualities? of the respective parts are indicated with A, B, C and D or with evaluation values (Ti) based on a standard shown in Table 1.
TABELLA 1 TABLE 1
Effettuando la valutazione della qualit? interna relativamente alle parti rispettive, le qualit? delle parti rispettive possono essere indicate per le rispettive parti di refrattari ottenuti mediante getto allo stato fuso. Quando i refrattari ottenuti mediante getto allo stato fuso sono usati in un forno da vetro, ? possibile promuovere la durata di utilizzo del forno da vetro mediante il rivestimento con i refrattari ottenuti mediante getto allo stato fuso in considerazione delle qualit? interne delle parti rispettive. Inoltre, il metodo dell'invenzione ? utile come mezzo di ispezione per determinare le preferibili condizioni di getto, variando le condizioni di getto dei refrattari ottenuti per getto allo stato fuso, e non ? necessario ispezionare il loro interno tagliando i campioni ottenuti mediante getto. Carrying out the quality assessment? internal relative to the respective parts, the qualities? respective parts may be indicated for the respective parts of refractories obtained by casting in the molten state. When melt cast refractories are used in a glass furnace,? Is it possible to promote the duration of use of the glass furnace by coating with refractories obtained by casting in the molten state in consideration of the qualities? internal parts of the respective parts. Furthermore, the method of the invention? useful as a means of inspection to determine the preferable casting conditions, by varying the casting conditions of the refractories obtained by casting in the molten state, and not? It is necessary to inspect their interior by cutting the samples obtained by casting.
In un'altra attuazione preferibile di un metodo di valutazione della qualit? interna di refrattari ottenuti mediante getto allo stato fuso di questa invenzione, in aggiunta alla valutazione su ciascuna parte del campione di refrattario, si effettua una valutazione globale in cui la valutazione globale del campione ? effettuata ponderando i valori di valutazione delle parti e sommando i valori ponderati. In questo modo, pu? essere effettuata la valutazione globale della qualit? interna corrispondente alla prestazione pratica dei refrattari ottenuti mediante getto allo stato fuso. In another preferable implementation of a quality assessment method? internal of melt cast refractories of this invention, in addition to the evaluation on each part of the refractory sample, a global evaluation is made in which the global evaluation of the sample? carried out by weighting the valuation values of the parts and adding the weighted values. In this way, it can? be carried out the global assessment of the quality? internal corresponding to the practical performance of the refractories obtained by casting in the molten state.
Successivamente sar? data una spiegazione di un esempio del metodo di valutazione globale quantitativa del campione di refrattario. Questo metodo di valutazione ? effettuato determinando preventivamente una formula di calcolo, considerando il grado di ponderazione per esempio relativamente all'importanza di ciascuna parte. Later it will be? given an explanation of an example of the method of quantitative global evaluation of the refractory sample. This method of evaluation? carried out by determining in advance a calculation formula, considering the degree of weighting for example in relation to the importance of each part.
Per esempio, quando il campione ? suddiviso in quattro parti 1, 2, 3 e 4 i valori valutati delle rispettive parti sono (si assume che la parte 4 sia disposta nel lato interno del forno da vetro e usata in contatto con il vetro fuso, il che richiede la massima resistenza alla corrosione) . Per esempio, il grado di ponderazione, considerando l'importanza di ciascuna parte, ? rispettivamente 1, 2, 3 o 4. La valutazione totale del campione di refrattario ? effettuata effettuando il calcolo con la formula For example, when the champion? divided into four parts 1, 2, 3 and 4 the estimated values of the respective parts are (it is assumed that part 4 is arranged in the inner side of the glass furnace and used in contact with the molten glass, which requires maximum resistance to corrosion). For example, the degree of weighting, considering the importance of each part,? 1, 2, 3 or 4 respectively. The total evaluation of the refractory sample? performed by performing the calculation with the formula
In questo metodo di valutazione globale, In this global valuation method,
pi? piccolo ? il valore numerico che si ottiene migliore ? la qualit? del refrattario ottenuto mediante getto allo stato fuso. pi? small ? which numerical value gets better? the quality? of the refractory obtained by casting in the molten state.
BREVE DESCRIZIONE DEI DISEGNI BRIEF DESCRIPTION OF THE DRAWINGS
La Fig. 1 ? un diagramma di flusso per spiegare un tipico esempio di un metodo per valutare la qualit? interna di refrattari ottenuti mediante getto allo stato fuso di questa invenzione; Fig. 1? a flowchart to explain a typical example of a method for assessing quality? interior of melt cast refractories of this invention;
la Fig. 2 ? un esempio di una rappresentazione di immagini di onde riflesse prima di aver rimosso le immagini di onde riflesse dalle superfici ottenuta con il metodo di valutazione della qualit? interna di questa invenzione; Fig. 2? an example of an image representation of reflected waves before removing the reflected wave images from surfaces obtained with the quality assessment method? internal of this invention;
la Fig. 3 ? la rappresentazione di immagini di onde riflesse dopo che porzioni delle immagini di onde riflesse dalle superfici sono state rimosse dalla rappresentazione di Fig. 2 e Fig. 3? the representation of images of reflected waves after portions of the images of waves reflected from the surfaces have been removed from the representation of Fig. 2 and
la Fig. 4 ? un esempio della sezione verticale di un materiale refrattario ottenuto mediante getto allo stato fuso a cui ? applicato il metodo di valutazione della qualit? interna di questa invenzione. Fig. 4? an example of the vertical section of a refractory material obtained by casting in the molten state at which? applied the quality assessment method? internal of this invention.
DESCRIZIONE DETTAGLIATA DELLE ATTUAZIONI PREFERITE Sar? data una spiegazione specifica della presente invenzione in riferimento ad attuazioni. Tuttavia, questa invenzione non ? ristretta a questi esempi. La Fig. 1 ? un diagramma di flusso che mostra un esempio di un metodo per valutare la qualit? interna di refrattari ottenuti mediante getto allo stato fuso secondo la presente invenzione e le seguenti attuazioni furono effettuate in accordo con la procedura del diagramma di flusso. DETAILED DESCRIPTION OF THE PREFERRED ACTUATIONS Sar? given a specific explanation of the present invention with reference to embodiments. However, this invention is not? restricted to these examples. Fig. 1? a flowchart showing an example of a method for assessing quality? of melt cast refractories according to the present invention and the following embodiments were carried out in accordance with the flow chart procedure.
Il campione esaminato era un materiale refrattario ottenuto mediante getto allo stato fuso per forni da vetro chiamato ZB1691 prodotto da Asahi Glass Company Ltd., contenente almeno 35% in peso di Le dimensioni del campione erano 250 mm x 450 mm per 1200 mm e il peso del campione era approssimativamente 513 kg. Il campione di refrattario fu posto a terra, dove il campione fu ruotato di 90? in modo che la faccia del lato superiore (la faccia superiore del campione di refrattario in cui l'apertura di alimentazione del fuso era stata eliminata) dei refrattari ottenuti mediante getto allo stato fuso fosse sul lato destro. The sample examined was a refractory material obtained by melt casting for glass furnaces called ZB1691 manufactured by Asahi Glass Company Ltd., containing at least 35% by weight of The sample dimensions were 250 mm x 450 mm by 1200 mm and the weight of the sample was approximately 513 kg. The refractory sample was placed on the ground, where the sample was rotated 90? so that the top side face (the top face of the refractory sample in which the melt supply opening had been eliminated) of the melt cast refractories was on the right side.
Fu utilizzato come dispositivo di ispezione utilizzante onde elettromagnetiche un rivelatore di oggetti interni per cemento. Il dispositivo di ispezione era integrato con un microcalcolatore munito di una funzione per elaborare immagini e di un visualizzatore di immagini e fu collegata ad esso una stampatrice per rappresentare l'immagine visualizzata . An interior object detector for concrete was used as an inspection device using electromagnetic waves. The inspection device was integrated with a microcomputer equipped with an image processing function and an image viewer and a printer was connected to it to represent the displayed image.
Le onde elettromagnetiche utilizzate sono impulsi di onde elettromagnetiche aventi una ampiezza di un nanosecondo (l'impulso di onde elettromagnetica emesso da un oscillatore era una singola onda di forma triangolare e l'onda elettromagnetiche emessa da un'antenna era un aggregato di una pluralit? di onde elettromagnetiche triangolari). Le antenne di emissione e di ricevimento sono poste di fronte alla faccia da 450 mm x 1200 mm, che ? la faccia superiore ruotata. Nell'ispezione interna del materiale refrattario, la scansione fu effettuata emettendo gli impulsi di onde elettromagnetiche mentre si muovevano le antenne di emissione e di ricevimento lungo la faccia nella direzione orizzontale (nella direzione verticale quando la relazione di posizione) era riferita al (senso del getto) . The electromagnetic waves used are pulses of electromagnetic waves having an amplitude of one nanosecond (the pulse of electromagnetic waves emitted by an oscillator was a single wave of triangular shape and the electromagnetic wave emitted by an antenna was an aggregate of a plurality of waves). of triangular electromagnetic waves). The emitting and receiving antennas are placed in front of the 450 mm x 1200 mm face, which? the top face rotated. In the internal inspection of the refractory material, the scan was carried out by emitting the pulses of electromagnetic waves while moving the emitting and receiving antennas along the face in the horizontal direction (in the vertical direction when the position relationship) was referred to (direction of the cast).
Le onde elettromagnetiche riflesse durante la scansione del campione di refrattario con gli impulsi di onde elettromagnetiche venivano ricevute dalle antenne di emissione e di ricevimento La Fig. 2 mostra un esempio di rappresentazione di immagini di onde riflesse visualizzate sul visualizzatore del dispositivo di ispezione. In Fig. 2, la faccia F indica una faccia laterale a cui sono inviati gli impulsi di onde elettromagnetiche e la faccia R un'altra faccia laterale, opposta alla faccia laterale a cui sono inviate le onde elettromagnetiche. Il lato destro del diagramma corrisponde alla faccia in cui fu tagliata via nel getto l'apertura di alimentazione del fuso (il lato superiore del getto). Nella rappresentazione delle immagini delle onde riflesse, le immagini delle onde riflesse dalla superfici FA, FB, FC, RA, RB, RC e RD sono visualizzate in bande. The electromagnetic waves reflected during the scanning of the refractory sample with the pulses of electromagnetic waves were received by the emitting and receiving antennas. Fig. 2 shows an example of representation of reflected wave images displayed on the display of the inspection device. In Fig. 2, face F indicates a side face to which the pulses of electromagnetic waves are sent and face R another side face, opposite to the side face to which the electromagnetic waves are sent. The right side of the diagram corresponds to the face where the melt supply opening (the top side of the jet) was cut off in the casting. In the image representation of reflected waves, images of the waves reflected by the surfaces FA, FB, FC, RA, RB, RC and RD are displayed in bands.
Sar? data una illustrazione di un metodo per rimuovere le immagini riflesse dalle superfici dalla rappresentazione grezza di immagini di onde riflesse. L'immagine di onde riflesse, per esempio, in vicinanza di una linea P a tratto e punto, in cui difetti interni non sono sostanzialmente presenti, fu adottata come immagine di onde riflesse dalle superfici da sottrarre. L'immagine di onde FA riflesse dalla superficie e le sue immagini di onde FB ed FC riflesse in modo molteplice erano generate a causa della faccia F quando le antenne di emissione e ricevimento erano dirette nella direzione di P e l'immagine di onde FA riflesse dalla superficie e le sue immagini di onde riflettentesi in modo molteplice RB, RC e RD erano causate dalla faccia R (le immagini RC e RD sono poste al di sotto della posizione corrispondente alla faccia R nella rappresentazione di immagini di onde riflesse) . Quando la rappresentazione di immagini delle onde riflesse del campione totale doveva essere ulteriormente investigata, queste immagini di onde riflesse erano conservate nella memoria del microcalcolatore come segnali di riferimento che venivano sottratti dalla rappresentazione grezza delle immagini delle onde riflesse cancellando in questo modo (elaborando) le immagini riflesse dalle superf ici. Sar? given an illustration of a method for removing reflected images from surfaces from the raw representation of reflected wave images. The image of reflected waves, for example, in the vicinity of a dotted line P, in which internal defects are not substantially present, was adopted as an image of waves reflected by the surfaces to be subtracted. The image of FA waves reflected from the surface and its images of multiply reflected FB and FC waves were generated due to the F face when the emitting and receiving antennas were directed in the direction of P and the image of reflected FA waves from the surface and its images of multiply reflecting waves RB, RC and RD were caused by the R face (the RC and RD images are placed below the position corresponding to the R face in the representation of reflected wave images). When the reflected wave image representation of the total sample had to be further investigated, these reflected wave images were stored in the memory of the microcomputer as reference signals which were subtracted from the raw representation of the reflected wave images thereby erasing (processing) the images reflected from the surfaces.
La Fig. 3 mostra la rappresentazione elaborata delle immagini delle onde riflesse in cui i rumori delle immagini riflesse dalla superficie FA, FB e FC, erano rimossi. La ragione del fatto che le immagini riflesse dalla superficie RA, RB, RC ed RD rimangono in Fig. 3 ? che i materiali refrattari ottenuti mediante getto allo stato fuso erano provvisti di un piano di simmetria, quindi l'ispezione del campione globale pu? essere effettuata in modo sufficiente analizzando le immagini delle onde riflesse di met? porzione tra la superficie di incidenza delle onde elettromagnetiche e il piano di simmetria e quindi queste immagini di onde riflesse dalla superficie non furono rimosse. Fig. 3 shows the elaborated representation of the reflected wave images in which the noises of the reflected images from the surface FA, FB and FC, were removed. The reason why the images reflected from the surface RA, RB, RC and RD remain in Fig. 3? that the refractory materials obtained by casting in the molten state were provided with a plane of symmetry, therefore the inspection of the global sample can? be carried out sufficiently by analyzing the images of the reflected waves of met? portion between the surface of incidence of electromagnetic waves and the plane of symmetry and therefore these images of waves reflected from the surface were not removed.
Nelle Fig. 2 e 3, le immagini profonde G indicano immagini di onde riflesse provocate da soffiature o da un aggregato di cristalli grossolani e le immagini leggere H immagini di onde deboli riflesse provocate da cristalli grossolani o fini pori. Ci? fu confermato tagliando un certo numero di refrattari ottenuti mediante getto allo stato fuso che erano stati ispezionati e osservando le loro sezioni e confrontando le immagini. Come mostrato in Fig. 3, il campione di refrattario ? suddiviso in per esempio 4 parti nella direzione dell'altezza. Cio?, l'altezza del refrattario ottenuto per getto allo stato fuso, 1200 m, ? divisa in 4 parti di 300 mm e le parti 1, 2, 3 e 4 sono valutate per effettuare la valutazione globale del refrattario ottenuto per getto allo stato fuso. In Figs. 2 and 3, the deep images G indicate images of reflected waves caused by blowholes or an aggregate of coarse crystals and the light images H images of reflected weak waves caused by coarse crystals or fine pores. There? it was confirmed by cutting a number of molten cast refractories that had been inspected and looking at their sections and comparing the images. As shown in Fig. 3, the refractory sample? divided into for example 4 parts in the direction of the height. That is, the height of the refractory obtained by casting in the molten state, 1200 m,? divided into 4 parts of 300 mm and parts 1, 2, 3 and 4 are evaluated to carry out the global evaluation of the refractory obtained by casting in the molten state.
Come ? mostrato in Fig. 3, l'altezza del campione di refrattario dalla base alla superficie di taglio S, in cui l'apertura del getto solidificato (apertura di alimentazi ne del fuso) dei refrattari ottenuti per getto allo stato fuso ? tagliata via in senso orizzontale, ? suddivisa da piani orizzontali SI, S2, S3 e la rappresentazione di immagini di onde riflesse ? suddivisa nelle rispettive porzioni 1, 2, 3 e 4 corrispondenti alle rispettive parti mostrate in Fig. 3. Il numero di divisioni n pu? essere aumentato in accordo con le necessit? e pu? essere effettuata una fine valutazione delle parti. How ? shown in Fig. 3, the height of the refractory sample from the base to the cutting surface S, in which the opening of the solidified casting (melt supply opening) of the refractories obtained by casting in the molten state? cut off horizontally,? divided by horizontal planes SI, S2, S3 and the representation of images of reflected waves? divided into the respective portions 1, 2, 3 and 4 corresponding to the respective parts shown in Fig. 3. The number of divisions n can? be increased in accordance with the needs? and can? a fine evaluation of the parts be carried out.
Nel caso del refrattario ottenuto per getto allo stato fuso era possibile arrivare alla qualit? totale del refrattario mediante ispezione fino ad una profondit? corrispondente a met? dello spessore, come precedentemente detto, ci? fu effettuato nel seguente modo. La spiegazione sar? data in riferimento nella Fig. 3. Si tira una linea retta L nella posizione (125 mm dalla faccia F) corrispondente alla met? dello spessore (250 mm) del refrattario nella rappresentazione di immagini di onde riflesse. La valutazione ? effettuata sulle immagini fino a met? profondit? sul lato adiacente alla faccia di incidenza o sopra la linea retta L (si rimuovono le immagini del rumore fino a met? spessore) . In the case of the refractory obtained by casting in the molten state was it possible to reach the quality? total of the refractory by inspection up to a depth? corresponding to half? of the thickness, as previously said, there? was carried out in the following way. The explanation will be? given in reference in Fig. 3. Is a straight line L drawn in the position (125 mm from face F) corresponding to the middle? of the thickness (250 mm) of the refractory in the representation of images of reflected waves. The evaluation ? carried out on the images up to half? depth on the side adjacent to the incidence face or above the straight line L (noise images up to half thickness are removed).
Nel caso del refrattario ottenuto per getto allo stato fuso, quasi nessuna immagine di onde riflesse dalla faccia R appare sul lato della faccia F della linea retta L (oppure, ? facile controllare la rappresentazione di immagini di onde riflesse in modo tale che l'immagine delle onde riflesse dalla faccia R non appaia sul lato della linea retta L dalla parte della faccia F). Quindi, ? possibile effettuare in modo sufficiente la valutazione anche quando l'immagine delle onde riflesse dalla superficie della faccia R non ? rimossa. In the case of the cast refractory, almost no image of reflected waves from face R appears on the side of face F of straight line L (or, it is easy to control the image representation of reflected waves so that the image waves reflected by the R face does not appear on the side of the straight line L from the side of the face F). Therefore, ? possible to carry out the evaluation sufficiently even when the image of the waves reflected from the surface of the face R is not? removed.
Per esempio, la valutazione su ciascuna parte fu effettuata come segue. Le immagini di onde riflesse sul lato dalla parte della faccia F della linea retta L sono classificate in immagini profonde e in immagini leggere, relativamente ad ogni parte individuata dalle linee rette SI, S2 ed S3, e si calcolano le aree totali delle rispettive immagini classificate. Entrambe le aree delle immagini si confrontano con la tabella di valutazione standard delle immagini mostrata in Tabella 1 e la valutazione di struttura A, B, C e D o il valore di valutazione in punti ? determinato per ciascuna parte. La Tabella 2 mostra un esempio del risultato della valutazione. Inoltre, quando ? necessaria una valutazione pi? dettagliata, pu? essere fatta un'altra valutazione della qualit? interna emettendo onde elettromagnetiche ad una faccia laterale contigua del refrattario ottenuto mediante getto allo stato fuso avente una forma di un parallelepipedo rettangolo o emettendo onde elettromagnetiche ad una faccia laterale opposta. For example, the evaluation on each part was made as follows. The images of waves reflected on the side from the side of the face F of the straight line L are classified into deep images and into light images, relative to each part identified by the straight lines SI, S2 and S3, and the total areas of the respective classified images are calculated . Do both image areas compare with the standard image rating table shown in Table 1 and structure rating A, B, C and D or rating value in points? determined for each part. Table 2 shows an example of the evaluation result. Also, when? need an evaluation more? detailed, can? be made another assessment of the quality? internal by emitting electromagnetic waves to a contiguous side face of the refractory obtained by means of a molten jet having the shape of a rectangular parallelepiped or by emitting electromagnetic waves to an opposite side face.
Tabella 2 Table 2
Inoltre, la valutazione totale fu effettuata per esempio come segue. In questo esempio, fu assegnato alla parte 4 un grado di ponderazione elevato (assumendo che la parte 4 fosse disposta al lato interno del forno da vetro) e il valore di valutazione della parte 4 in Tabella 2 fu moltiplicato per 4 e i prodotti furono sommati. Furthermore, the total evaluation was carried out for example as follows. In this example, part 4 was given a high degree of weighting (assuming part 4 was placed on the inside of the glass kiln) and the rating value of part 4 in Table 2 was multiplied by 4 and the products were added together.
La Fig. 4 ? una illustrazione schematica che mostra un esempio di una sezione di un refrattario ottenuto per gett? allo stato fuso del tipo esente da vuoti (in cui l?apertura di alimentazione di fuso solidificato con molte soffiature era stata eliminata) , tagliato nella direzione verticale dopo che era stata effettuata la valutazione della qualit? interna secondo il metodo dell'invenzione. La porzione scura in Fig. 4 mostra una soffiatura o un poro. Come risultato della valutazione della qualit? interna di numerosi refrattari ottenuti mediante getto allo stato fuso con il metodo dell'invenzione e del confronto dei risultati della prova con i difetti interni trovati tagliando effettivamente i refrattari, fu confermato che il metodo di valutazione della qualit? interna di questa invenzione ? un metodo capace di valutare in modo preciso la qualit? interna del refrattario ottenuto mediante getto allo stato fuso. Fig. 4? a schematic illustration showing an example of a section of a refractory obtained by casting? in the void-free melt state (where the solidified melt supply port with many blowholes had been eliminated), cut in the vertical direction after the quality assessment had been made. internal according to the method of the invention. The dark portion in Fig. 4 shows a blow or pore. As a result of the quality assessment? of numerous refractories obtained by casting in the molten state with the method of the invention and by comparing the test results with the internal defects found by actually cutting the refractories, it was confirmed that the method of evaluating the quality? internal of this invention? a method capable of accurately evaluating the quality? internal part of the refractory obtained by casting in the molten state.
Il metodo di valutazione della qualit? interna inventato per refrattari ottenuti per getto allo stato fuso ? applicabile alla valutazione della qualit? interna di mattoni ottenuti per pressatura o per-getto. In questo caso, sono selezionate facce laterali approssimativamente ortogonali alla direzione di uno spessore pi? sottile (normalmente ci sono due facce laterali sul lato anteriore e sul lato posteriore) in modo che le onde elettromagnetiche trasmesse abbiano facilit? a raggiungere difetti e le onde riflesse siano facili da ricevere. Le antenne di emissione e di ricevimento sono disposte in vicinanza di una delle facce laterali. Gli impulsi di onde elettromagnetiche sono emessi contro la porzione interna del mattone muovendo le antenne di emissione e di ricevimento lungo la faccia laterale del mattone e si ricevono le onde riflesse che tornano indietro. The quality assessment method? internal invented for refractories obtained by casting in the molten state? applicable to quality assessment interior of bricks obtained by pressing or casting. In this case, side faces are selected approximately orthogonal to the direction of a thickness pi? thin (normally there are two side faces on the front side and on the back side) so that the electromagnetic waves transmitted have ease? to reach defects and reflected waves are easy to receive. The emitting and receiving antennas are arranged in the vicinity of one of the side faces. The pulses of electromagnetic waves are emitted against the inner portion of the brick by moving the emitting and receiving antennas along the side face of the brick and the reflected waves are received and returned back.
Quando il campione ? un mattone formato per pressatura o a getto, si sceglie una faccia laterale adiacente ad una porzione con elevata possibilit? di contenere difetti tra entrambe le facce laterali del campione di mattone in una direzione di uno spessore pi? sottile. Gli impulsi di onde elettromagnetiche sono emessi dalla faccia laterale del campione verso il suo interno mentre si muovono le antenne di emissione e di ricevimento in vicinanza della faccia laterale. La rappresentazione di immagini delle onde riflesse dal campione ? ottenuta ricevendo le onde elettromagnetiche riflesse dal campione di mattone da parte delle antenne di emissione e ricevimento. La struttura all'interno del campione ? valutata sulla base delle immagini delle onde riflesse. When the champion? a brick formed by pressing or casting, you choose a side face adjacent to a portion with high possibility? to contain defects between both side faces of the brick sample in a direction of a thickness more? subtle. The pulses of electromagnetic waves are emitted from the lateral face of the sample towards the inside while the emitting and receiving antennas move in the vicinity of the lateral face. The representation of images of the waves reflected by the sample? obtained by receiving the electromagnetic waves reflected from the brick sample by the emitting and receiving antennas. The structure within the sample? evaluated on the basis of images of reflected waves.
Questo metodo utilizza il fatto che i difetti sono suscettibili di essere provocati in posizione adiacente ad una faccia laterale del mattone formato (per esempio, nel caso di mattone formato mediante pressatura ? probabile che una "laminazione" sia provocata dalla vicinanza della faccia laterale in contatto con un pistone dello stampo) . Quando i difetti interni sono presenti solo vicino al lato in cui sono disposte le antenne di emissione e di ricevimento, ? possibile valutare facilmente la qualit? interna del mattone effettuando gli stessi stadi del caso del refrattario ottenuto per getto allo stato fuso. This method utilizes the fact that defects are likely to be caused adjacent a side face of the formed brick (for example, in the case of a pressed brick it is likely that a "lamination" is caused by the proximity of the side face in contact. with a mold piston). When the internal defects are present only near the side where the emitting and receiving antennas are arranged,? can you easily evaluate the quality? inside the brick by carrying out the same steps as in the case of the refractory obtained by casting in the molten state.
Secondo il metodo di valutazione della qualit? interna di refrattari ottenuti per getto allo stato fuso secondo l'invenzione, la valutazione pu? essere effettuata in modo non distruttivo con buona prestazione operativa sul posto di produzione senza utilizzare una apparecchiatura su larga scala. Anche quando sono presenti all'interno piccoli difetti, la posizione e il grado possono essere determinati in modo preciso e facile utilizzando la struttura simmetrica del refrattario ottenuto per getto allo stat? fuso relativamente al piano di simmetria verticale che ? formato durante l'operazione di getto. Quindi, il metodo dell'invenzione ? adatto per il controllo di qualit? e per la valutazione dei refrattari ottenuti per getto allo stato fuso. According to the quality assessment method? internal of refractories obtained by casting in the molten state according to the invention, the evaluation can? be done non-destructively with good operational performance at the production site without using large-scale equipment. Even when small defects are present inside, the position and grade can be determined precisely and easily using the symmetrical structure of the cast refractory to the stat? fused relative to the plane of vertical symmetry that? formed during the casting operation. So, the method of the invention? suitable for quality control? and for the evaluation of the refractories obtained by casting in the molten state.
Pu? essere ottenuto un effetto significativo nell'allungamento della durata di utilizzo e nell 'assicurare la affidabilit? del forno da vetro per effetto del rivestimento del forno da vetro con i refrattari ottenuti per getto allo stato fuso in considerazione dei dati da valutazione, incluse le posizioni e dimensioni dei difetti all'interno dei refrattari ottenuti per getto allo stato fuso. Pu? be obtained a significant effect in extending the duration of use and in ensuring reliability? of the glass furnace due to the coating of the glass furnace with the cast refractories in the molten state in consideration of the evaluation data, including the positions and dimensions of the defects within the refractories obtained by casting in the molten state.
Claims (7)