IT9048252A1 - METALLIC ALLOY ON A SILVER BASE WITH A TITLE OF 800 - 925 WITH HIGH FEATURES OF OXIDATION RESISTANCE - Google Patents
METALLIC ALLOY ON A SILVER BASE WITH A TITLE OF 800 - 925 WITH HIGH FEATURES OF OXIDATION RESISTANCE Download PDFInfo
- Publication number
- IT9048252A1 IT9048252A1 IT048252A IT4825290A IT9048252A1 IT 9048252 A1 IT9048252 A1 IT 9048252A1 IT 048252 A IT048252 A IT 048252A IT 4825290 A IT4825290 A IT 4825290A IT 9048252 A1 IT9048252 A1 IT 9048252A1
- Authority
- IT
- Italy
- Prior art keywords
- silver
- metal alloy
- title
- fact
- percentages
- Prior art date
Description
LEGA METALLICA SU BASE ARGENTO CON TITOLO 800 - 925 AVENTE SPICCATE CARATTERISTICHE DI RESISTENZA ALL'OSSIDAZIONE METALLIC ALLOY ON SILVER BASE WITH TITLE 800 - 925 HAVING STRONG CHARACTERISTICS OF RESISTANCE TO OXIDATION
Il presente trovato riguarda la composizione di una lega metallica su base argento con titolo di argento 800-925 che presenta una notevole resistenza alla sulfurazione ed 'all' ossidazione, ed è esente dalla antiestetica comparsa del colore roseo dovuto al rame, anche dopo un uso prolungato e ripetute puliture della superficie, nonché delle macchie che derivano dal bagno galvanico di argentatura cui si ricorre attualmente, basato sull'impiego di argento al cianuro. The present invention relates to the composition of a metal alloy on a silver base with a silver content of 800-925 which has a remarkable resistance to sulfur and oxidation, and is free from the unsightly appearance of the pink color due to copper, even after use. prolonged and repeated cleaning of the surface, as well as of the stains deriving from the galvanic silver plating bath currently used, based on the use of cyanide silver.
La lega, che costituisce .l'oggetto della presente invenzione, è ottenibile per fusione aggiungendo ad argento coppella un additivo comprendente alcuni metalli che, fusi con l'argento in piccole percentuali variabili a seconda del titolo di argento che si vuole ottenere, conferiscono alla lega d’argento risultante le caratteristiche sopraindicate. The alloy, which is the subject of the present invention, can be obtained by fusion by adding an additive to silver cupel comprising some metals which, fused with the silver in small percentages varying according to the title of silver to be obtained, give the silver alloy resulting in the above characteristics.
Allo stato attuale della tecnica sono note numerose leghe metalliche su base argento volte a evitare o per lo meno a ridurre l'ossidazione superficiale. Tuttavia le leghe citate nella letteratura brevettuale e scientifica hanno il grave inconveniente di presentare una struttura a grana grossolana, un colore non argenteo, irregolarità superficiali e bolle dovute ad inclusioni di gas in fase di fusione: in una parola non sono esteticamente soddisfacenti. Ciò comporta il ricorso ad una successiva argentatura in bagno galvanico di argento al cianuro, che presenta come è noto, numerosi problemi di carattere ecologico. Inoltre l'impiego del cadmio, che pure favorisce la brillantezza, data la sua nota tossicità, condiziona fortemente gli impieghi dei prodotti ottenuti. At the present state of the art, numerous silver-based metal alloys are known aimed at avoiding or at least reducing surface oxidation. However, the alloys mentioned in the patent and scientific literature have the serious drawback of having a coarse-grained structure, a non-silvery color, surface irregularities and bubbles due to gas inclusions in the melting phase: in a word they are not aesthetically satisfactory. This involves the use of a subsequent silver plating in a cyanide silver galvanic bath, which, as is well known, presents numerous ecological problems. Furthermore, the use of cadmium, which also favors brilliance, given its known toxicity, strongly conditions the uses of the products obtained.
Un primo compito del presente trovato è quello di fornire la composizione di una lega metallica su base argento in grado di ovviare agli inconvenienti sopra indicati, che sia dotata cioè oltre che di resistenza all'ossidazione, di ottime caratteristiche estetiche e di un bel colore argento con una tonalità bianca tale che 11 bagno galvanico di argento al cianuro diventa superfluo. A first task of the present invention is to provide the composition of a metal alloy on a silver base capable of obviating the aforementioned drawbacks, that is, which, in addition to resistance to oxidation, has excellent aesthetic characteristics and a beautiful silver color. with such a white hue that the galvanic bath of cyanide silver becomes superfluous.
Un altro scopo dell’invenzione è quello di fornire, per ciascun titolo di argento da realizzare, 800 o 925, un additivo in forma di lingotto, di peso appropriato e con percentuali diverse dei componenti, pronto per essere aggiunto in fase di fusione al peso dell'argento desiderato, per fornire la lega metallica su base argento di cui si è detto. Another object of the invention is to provide, for each title of silver to be made, 800 or 925, an additive in the form of an ingot, of appropriate weight and with different percentages of the components, ready to be added in the melting phase to the weight. of the desired silver, to provide the aforementioned silver-based metal alloy.
Secondo il trovato ciò è stato ottenuto con una lega metallica comprendente oltre che l’Argento, anche Rame metallico, Antimonio e Germanio. Le percentuali dei componenti nella lega variano a seconda che il titolo dell' argento sia 800 o 925, ma risultano compresi entro i limiti seguenti: According to the invention, this was achieved with a metal alloy comprising not only silver but also metallic copper, antimony and germanium. The percentages of the components in the alloy vary according to whether the title of the silver is 800 or 925, but are included within the following limits:
Ag 82 % - 92,5 % Ag 82% - 92.5%
Cu me 6,59% - 19 % Cu me 6.59% - 19%
Sb 0,06% - 5,95% Sb 0.06% - 5.95%
Ge 0,04% - 0,30% Ge 0.04% - 0.30%
In pratica per ottenere 1000 g. di Argento 800 millesimi di titolo, basta prendere 800 g. di argento coppella e aggiungere un lingotto di 200 g. di una lega metallica in cui i componenti sono presenti nelle seguenti percentuali in peso : In practice to obtain 1000 g. of Silver 800 thousandths of title, just take 800 g. of silver cup and add an ingot of 200 g. of a metal alloy in which the components are present in the following percentages by weight:
Ag da gr. 20 a gr. 60 Ag from gr. 20 to gr. 60
Cu me da gr. 110 ,1 a gr. 190 Cu me from gr. 110, 1 to gr. 190
Sb da mg 60 a mg 6200 Sb from 60 mg to 6200 mg
Ge da mg 40 a mg 300 Ge from 40 mg to 300 mg
Per ottenere 1000 g. di Argento 925 millesimi di titolo, basta prendere 925 g. di argento coppella a aggiungervi un lingotto di 75 g. di una lega metallica in cui i componenti sono presenti nelle seguenti percentuali in peso: To obtain 1000 g. of Silver 925 thousandths of title, just take 925 g. of silver cup to add an ingot of 75 g. of a metal alloy in which the components are present in the following percentages by weight:
Cu me da gr. 65 a gr 73 Cu me from gr. 65 to 73 g
Sb da mg 60 a mg 4889 Sb from 60 mg to 4889 mg
Ge da mg 40 a mg 250 Ge from 40 mg to 250 mg
Le due leghe metalliche a base o non di argento sopraindicate, sono del tutto innocue, e possono essere usate da sole per la realizzazione di strumenti delicatissimi e sofisticati. The two metal alloys with or without silver base indicated above are completely harmless, and can be used alone for the creation of very delicate and sophisticated instruments.
Il rame in bassa percentuale viene aggiunto nella lega di argento per migliorarne le caratteristiche fisico-chimiche e la duttilità, mentre rimane inalterata la resistenza all'ossidazione. A low percentage of copper is added to the silver alloy to improve its physico-chemical characteristics and ductility, while the resistance to oxidation remains unaltered.
L' antimonio viene aggiunto come sbiancante e antiossidante, il germanio e l'indio per le loro qualità di brillantanti. Antimony is added as a whitener and antioxidant, germanium and indium for their brightening qualities.
L'invenzione sarà meglio compresa dagli esempi che seguono che illustrano una preferita composizione percentuale per ciascuno dei due casi. The invention will be better understood from the following examples which illustrate a preferred percentage composition for each of the two cases.
ESEMPIO I EXAMPLE I
Si vogliono ottenere gr. 1000 di Argento 800 millesimi di titolo : a gr.800 argento coppella vengono aggiunti 200 gr. di una lega metallica così costituita : You want to get gr. 1000 of Silver 800 thousandths of title: to gr. 800 silver cup are added 200 gr. of a metal alloy made up of:
Ag gr. 60 Ag gr. 60
Cu me gr. 138 Cu me gr. 138
Sb mg 1800 Sb 1800 mg
Ge mg 200 Ge mg 200
Si porta a fusione ; quando il bagno di argento è pronto si agita bene a lungo prima di colare nella staffa. It leads to fusion; when the silver bath is ready it shakes well for a long time before pouring into the stirrup.
ESEMPIO II EXAMPLE II
Si vogliono ottenere gr. 1000 di Argento 925 millesimi di titolo vengono aggiunti a 925 g di Argento coppella, 75 g di una lega metallica così costituita: You want to get gr. 1000 of Silver 925 thousandths of title are added to 925 g of Silver cup, 75 g of a metal alloy as follows:
Cu me gr. 73,800 Cu me gr. 73,800
Sb mg 1000 Sb 1000 mg
Ge rmg 200 Ge rmg 200
Si porta a fusione. Quando il bagno di argento è pronto si agita bene a lungo e si cola nella staffa. It leads to fusion. When the silver bath is ready, shake well for a long time and pour into the stirrup.
La lega di argento ottenuta con queste due formule ha un bel colore bianco e presenta una fortissima resistenza alla ossidazione quando viene immersa in una soluzione di HC1 K2S in soluzione acquosa per un periodo di circa 5 ore. The silver alloy obtained with these two formulas has a beautiful white color and shows a very strong resistance to oxidation when it is immersed in a solution of HC1 K2S in aqueous solution for a period of about 5 hours.
Vantaggiosamente è stato osservato che anche le saldature presentano il colore dell’argento. Advantageously, it has been observed that even the welds have the color of silver.
Claims (1)