IT202100001769A1 - PHONOGRAPH RECORD AND PROCESS FOR THE PRODUCTION OF A PHONOGRAPH RECORD - Google Patents
PHONOGRAPH RECORD AND PROCESS FOR THE PRODUCTION OF A PHONOGRAPH RECORD Download PDFInfo
- Publication number
- IT202100001769A1 IT202100001769A1 IT102021000001769A IT202100001769A IT202100001769A1 IT 202100001769 A1 IT202100001769 A1 IT 202100001769A1 IT 102021000001769 A IT102021000001769 A IT 102021000001769A IT 202100001769 A IT202100001769 A IT 202100001769A IT 202100001769 A1 IT202100001769 A1 IT 202100001769A1
- Authority
- IT
- Italy
- Prior art keywords
- bio
- based material
- polyesters
- phonograph record
- phonograph
- Prior art date
Description
DESCRIZIONE DESCRIPTION
Annessa a domanda di brevetto per INVENZIONE INDUSTRIALE avente per titolo Attached to a patent application for INDUSTRIAL INVENTION having the title
?DISCO FONOGRAFICO E PROCESSO PER LA PRODUZIONE DI UN ?PHONOGRAPH RECORD AND PROCESS FOR THE PRODUCTION OF A
DISCO FONOGRAFICO? PHONOGRAPH RECORD?
Campo tecnico dell?invenzione Technical field of the invention
La presente invenzione ha per oggetto un disco fonografico ed un processo per la produzione dello stesso disco fonografico. The present invention relates to a phonograph record and a process for the production of the same phonograph record.
Tecnica nota Known technique
Con la definizione ?disco fonografico? si fa riferimento, nella presente trattazione, ad un supporto per la riproduzione di tracce acustiche di diversa tipologia. With the definition ?phonographic record? reference is made, in the present discussion, to a support for the reproduction of acoustic tracks of different types.
Sebbene siano attualmente disponibili supporti di riproduzione digitali che consentono di immagazzinare e riprodurre una quantit? di brani musicali sostanzialmente illimitata, la produzione di dischi fonografici ha acquistato nuovo vigore negli ultimi anni grazie alla qualit? del suono, definito dagli appassionati pi? caldo e realistico, ed all?intrinseco fascino vintage che lo rende paragonabile ad un oggetto di design. While digital playback media are currently available that allow you to store and play a large amount of of essentially unlimited pieces of music, the production of phonograph records has gained new vigor in recent years thanks to the quality? of sound, defined by enthusiasts pi? warm and realistic, and with the intrinsic vintage charm that makes it comparable to a design object.
Attualmente, i dischi fonografici sono realizzati mediante lo stampaggio in pressa di una massa tozza, il cosiddetto ?biscotto?, di polivinilcloruro (PVC). Currently, phonograph records are made by pressing a squat mass, the so-called "biscuit", of polyvinyl chloride (PVC).
In particolare, il biscotto viene portato alla temperatura di circa 200?C rendendolo malleabile per permettere il successivo stampaggio in pressa. Durante lo stampaggio, la pressa, mediante due controstampi, applica un?elevata pressione al biscotto deformandolo fino ad ottenere il disco fonografico. In particular, the biscuit is brought to a temperature of about 200°C making it malleable to allow subsequent molding in the press. During moulding, the press, by means of two countermoulds, applies high pressure to the biscuit, deforming it until the phonograph record is obtained.
Successive operazioni di finitura permettono di eliminare le porzioni di materiale in eccesso, dovute, per esempio, alla fuoriuscita del materiale dalla pressa durante lo stampaggio. Subsequent finishing operations make it possible to eliminate the portions of excess material, due, for example, to the leakage of the material from the press during molding.
Svantaggiosamente, lo stampaggio in pressa comporta, quindi, l?inevitabile produzione di sfridi che determinano un incremento dei costi di produzione. Disadvantageously, molding in a press therefore entails the inevitable production of scraps which determine an increase in production costs.
Inoltre, l?impiego del PVC (e pi? in generale di materiali derivanti da materie di origine fossile) affligge molto svantaggiosamente l?ecosistema incrementando l?inquinamento e contribuendo al surriscaldamento globale. Furthermore, the use of PVC (and more generally of materials deriving from materials of fossil origin) affects the ecosystem very disadvantageously, increasing pollution and contributing to global warming.
Breve sommario dell?invenzione Brief summary of the invention
Scopo della presente invenzione ? pertanto quello di ovviare a questi inconvenienti attraverso la realizzazione di un disco fonografico e di un processo per la produzione di un disco fonografico ecocompatibili e che presentino un impatto limitato sull?ambiente. Purpose of the present invention? therefore that of obviating these drawbacks through the creation of a phonograph record and of a process for the production of an eco-compatible phonograph record and which present a limited impact on the environment.
Ulteriore scopo della presente invenzione ? quello realizzare un processo in grado di ottimizzare il flusso di produzione di un disco fonografico. Another purpose of the present invention ? that of creating a process capable of optimizing the production flow of a phonograph record.
In accordo con la presente invenzione, tale scopo viene raggiunto da un disco fonografico e da un processo per la produzione di un disco fonografico comprendenti le caratteristiche tecniche esposte in una o pi? delle rivendicazioni annesse. In accordance with the present invention, this object is achieved by a phonograph record and by a process for the production of a phonograph record comprising the technical characteristics disclosed in one or more of the attached claims.
Secondo la presente invenzione viene proposto un disco fonografico presentante una prima ed una seconda facciata delle quali almeno una facciata presenta un solco fonografico atto a ricevere una porzione terminale di una puntina di una testina fonografica per riprodurre un suono. According to the present invention, a phonograph record is proposed having a first and a second side of which at least one side has a phonograph groove adapted to receive an end portion of a needle of a phonograph head to reproduce a sound.
Inoltre, il disco fonografico ? realizzato almeno parzialmente in un materiale bio-based derivato almeno parzialmente da fonti rinnovabili. Secondo la presente invenzione viene proposto, inoltre, un processo per la produzione di un disco fonografico comprendente la fase di predisporre una predeterminata quantit? di materiale bio-based derivato almeno parzialmente da fonti rinnovabili e predisporre uno stampo presentante almeno una superficie sagomata atta a riprodurre almeno un solco fonografico sul materiale bio-based. Also, the phonograph record ? made at least partially in a bio-based material derived at least partially from renewable sources. Furthermore, according to the present invention a process is proposed for the production of a phonograph record comprising the step of preparing a predetermined quantity of of bio-based material derived at least partially from renewable sources and preparing a mold having at least one shaped surface suitable for reproducing at least one phonographic groove on the bio-based material.
Inoltre, il processo di produzione comprende la fase di riscaldare il materiale bio-based fino a portarlo ad uno stato almeno parzialmente fluido e la fase di convogliare il materiale bio-based in un condotto di lavorazione facendo assumere al materiale bio-based un determinato profilo di temperature. Furthermore, the production process comprises the step of heating the bio-based material until it reaches an at least partially fluid state and the step of conveying the bio-based material into a processing duct making the bio-based material assume a given profile of temperatures.
Inoltre, il processo di produzione comprende la fase iniettare una determinata quantit? del materiale bio-based nello stampo e la fase di mantenere il materiale bio-based all?interno dello stampo per un intervallo di tempo di raffreddamento. Furthermore, the production process includes the stage of injecting a specific quantity? of the bio-based material in the mold and the step of keeping the bio-based material inside the mold for a cooling time interval.
Breve descrizione dei disegni Brief description of the drawings
Le caratteristiche tecniche dell?invenzione, secondo i suddetti scopi, sono chiaramente riscontrabili dal contenuto delle rivendicazioni sotto riportate, ed i vantaggi dello stesso risulteranno maggiormente evidenti nella descrizione dettagliata che segue, fatta con riferimento ai disegni allegati, che ne rappresentano una forma di realizzazione puramente esemplificativa e non limitativa, in cui: The technical characteristics of the invention, according to the aforesaid purposes, are clearly verifiable from the contents of the claims reported below, and the advantages of the same will become more evident in the detailed description that follows, made with reference to the enclosed drawings, which represent one embodiment thereof purely by way of example and not limiting, in which:
? la Figura 1 ? una vista prospettica di un disco fonografico in accordo con una possibile forma di realizzazione della presente invenzione. ? Figure 1 ? a perspective view of a phonograph record in accordance with a possible embodiment of the present invention.
? la Figura 2 ? una rappresentazione schematica di una possibile forma di realizzazione di un processo per la produzione di un disco fonografico in accordo con un ulteriore aspetto della presente invenzione. ? Figure 2 ? a schematic representation of a possible embodiment of a process for producing a phonograph record in accordance with a further aspect of the present invention.
Descrizione dettagliata dell?invenzione Detailed description of the invention
Con riferimento alle figure annesse ? stato complessivamente indicato con il riferimento numerico 1 un disco fonografico in accordo con la presente invenzione. With reference to the accompanying figures? the reference numeral 1 generally indicates a phonograph record in accordance with the present invention.
Il disco fonografico 1 presenta una prima facciata 2 ed una seconda facciata 3. The phonograph record 1 has a first side 2 and a second side 3.
In particolare, almeno una facciata delle summenzionate prima e seconda facciata 2, 3 presenta un solco fonografico (indicato in inglese con il termine ?groove?) atto a ricevere una porzione terminale di una puntina (indicata in inglese con ?pick-up?) di una testina fonografica per riprodurre un suono. In particular, at least one side of the aforementioned first and second sides 2, 3 has a phonographic groove (indicated in English with the term ?groove?) adapted to receive a terminal portion of a needle (indicated in English with ?pick-up?) of a phonograph cartridge to reproduce a sound.
In altre parole, almeno una facciata pu? presentare un solco fonografico rilevabile da un fonorivelatore di un giradischi per riprodurre una traccia sonora. In other words, at least one facade can? present a phonograph groove detectable by a phonograph of a turntable to reproduce a soundtrack.
Vantaggiosamente, ciascuna facciata 2, 3 pu? presentare un rispettivo solco fonografico incrementando la durata di riproduzione del disco fonografico 1. Advantageously, each facade 2, 3 can present a respective phonograph groove by increasing the playing time of the phonograph record 1.
In particolare, il disco fonografico 1 pu? essere realizzato nel formato 33 giri, 45 giri o 78 giri. In particular, the phonograph record 1 pu? be made in 33 rpm, 45 rpm or 78 rpm format.
In accordo con ulteriori possibili forme realizzative, il disco fonografico 1 pu? essere realizzato in accordo con differenti formati e/o presentare dimensioni peculiari senza che venga alterato il concetto inventivo alla base della presente invenzione. In accordance with further possible embodiments, the phonograph disc 1 can be made in accordance with different formats and/or have particular dimensions without altering the inventive concept underlying the present invention.
Il disco fonografico 1 ? realizzato almeno parzialmente in un materiale biobased derivato almeno parzialmente da fonti rinnovabili. Phonograph record 1 ? made at least partially in a biobased material derived at least partially from renewable sources.
Nella presente trattazione con la definizione ?materiale bio-based? si intende un materiale interamente o parzialmente ricavato da biomassa vegetale. In this discussion with the definition ?bio-based material? means a material wholly or partially obtained from vegetable biomass.
In altre parole, un materiale ?bio-based? ? un materiale di origine biologica e non include componenti di origine fossile (cio? derivanti da carbone o petrolio). In other words, a ?bio-based? ? a material of biological origin and does not include components of fossil origin (i.e. deriving from coal or oil).
La biomassa utilizzata per fabbricare polimeri bio-based deriva da diverse attivit? come l?agricoltura o l?industria agroalimentare; nelle diverse fasi la biomassa viene fermentata o modificata e, mediante queste procedure, si ottengono i polimeri bio-based o le molecole utilizzate per la loro produzione. The biomass used to manufacture bio-based polymers comes from different activities such as agriculture or the agri-food industry; in the different phases the biomass is fermented or modified and, through these procedures, the bio-based polymers or the molecules used for their production are obtained.
La provenienza della biomassa utilizzata per la produzione suddivide i materiali in tre categorie: i polimeri di prima generazione derivanti dall?industria alimentare, quelli di seconda generazione derivanti dai rifiuti e quelli di terza generazione derivanti dai microorganismi. The origin of the biomass used for production divides the materials into three categories: first generation polymers deriving from the food industry, second generation polymers deriving from waste and third generation polymers deriving from microorganisms.
Ad oggi, le principali risorse rinnovabili utilizzate per la produzione dei materiali bio-based sono cerealicole (amido di mais o grano idrolizzato) o provenienti dall?industria zuccheriera (melassa o canna da zucchero). To date, the main renewable resources used for the production of bio-based materials are cereals (corn starch or hydrolysed wheat) or from the sugar industry (molasses or sugar cane).
Il termine ?bio-based? ? stato definito dal comitato tecnico CEN/TC 411 nella normativa CEN/TR 16721:2014. The term ?bio-based? ? been defined by the CEN/TC 411 technical committee in the CEN/TR 16721:2014 standard.
In questo modo, il disco fonografico 1 riduce l?impatto ambientale che intrinsecamente caratterizza la produzione dei dischi fonografici in accordo con le tecniche note e, in particolare, l?impiego per la produzione di dischi fonografici di materiali come il PoliVinilCloruro (o Cloruro di polivinile o PVC). In this way, the phonograph disc 1 reduces the environmental impact which intrinsically characterizes the production of phonograph discs in accordance with the known techniques and, in particular, the use for the production of phonograph discs of materials such as PolyVinyl Chloride (or polyvinyl or PVC).
Dunque, il disco fonografico 1 contribuisce ad una riduzione delle emissioni dei gas a effetto serra, mettendo a disposizione del mercato un supporto fonografico che supera la necessit? dell?impiego di risorse di origine fossile. Therefore, the phonograph record 1 contributes to a reduction of greenhouse gas emissions, making available to the market a phonographic support that exceeds the need for the phonograph. of the use of resources of fossil origin.
Vantaggiosamente, il disco fonografico 1 pu? essere realizzato interamente in materiale bio-based in modo tale da minimizzare l?impatto ambientale legato alle fasi di produzione. Advantageously, the phonograph disc 1 can be made entirely of bio-based material in order to minimize the environmental impact linked to the production phases.
Preferibilmente, il summenzionato materiale bio-based ? scelto dal gruppo comprendente: Preferably, the aforementioned bio-based material ? chosen from the group including:
- acido polilattico (abbreviato PLA= Polylactic Acid), - polylactic acid (abbreviated PLA= Polylactic Acid),
- PLMS (PLA modificato), - PLMS (modified PLA),
- poli-idrossi-alcanoati (PHA), - poly-hydroxy-alkanoates (PHA),
- poli-idrossi-butirrato (PHB), - polyhydroxybutyrate (PHB),
- poli-idrossi-butirrati-co-idrossivalerati (PHBV), - poly-hydroxy-butyrate-co-hydroxyvalerates (PHBV),
- polilattidi, - polylactides,
- polilattide-co-caprolattone, - polylactide-co-caprolactone,
- policaprolattoni (PCL), - polycaprolactones (PCL),
- omo-poliesteri, - homo-polyesters,
- etero-poliesteri, - hetero-polyesters,
- co-poliesteri alifatici, - aliphatic co-polyesters,
- co-poliesteri aromatici, - aromatic co-polyesters,
- Bio-PET, - Bio-PET,
- Bio-PE, - Bio-PE,
- Mater-Bi, - Mater-Bi,
- Bi-Comp, - Bi-Comp,
- Biolice, - Biolice,
- Bioplast, - Bioplast,
- Cereplast Compostables, - Cereplast Compostables,
- Biotecnomais, - Biotechnomais,
- Vegemat, - Vegemat,
- Solanyl, - Solanyl,
-poliidrossialcanoati (PHA), -polyhydroxyalkanoates (PHA),
- poliidrossivaleriato (PHV), - polyhydroxyvaleriate (PHV),
- poiidrossiesanoato (PHH), - polyhydroxyhexanoate (PHH),
- polibutilene succinato (PSB), - polybutylene succinate (PSB),
- Biograde; - Biograde;
- Apinat. - Apinat.
In accordo con una possibile forma di realizzazione della presente invenzione, il disco fonografico 1 pu? essere realizzato almeno parzialmente con un biopolimero in materiale biodegradabile. In accordance with a possible embodiment of the present invention, the phonograph record 1 can be made at least partially with a biopolymer of biodegradable material.
Con il termine ?biopolimero? si intende un polimero che ? stato ottenuto, alternativamente: With the term ?biopolymer? you mean a polymer that ? was obtained, alternatively:
- da microorganismi; - from microorganisms;
- con sintesi convenzionale da monomeri derivati da fonti rinnovabili; - with conventional synthesis from monomers derived from renewable sources;
- da materiale vegetale (come ad esempio materie prime rinnovabili di origine agricola). - from plant material (such as renewable raw materials of agricultural origin).
Con la definizione ?materiale biodegradabile? si intende, nella presente trattazione, che il biopolimero pu? essere decomposto da microrganismi (per esempio batteri o funghi) in sostanze pi? semplici come acqua e gas naturali (come l?anidride carbonica e il metano) o in biomassa. With the definition ?biodegradable material? does it mean, in this discussion, that the biopolymer can? be decomposed by microorganisms (for example bacteria or fungi) into substances more? as simple as water and natural gases (such as carbon dioxide and methane) or in biomass.
L?impiego di un biopolimero biodegradabile per la realizzazione del disco fonografico 1 garantisce una elevata facilit? di smaltimento del disco fonografico 1 in modo tale da ridurne l?impatto ambientale al termine del suo ciclo operativo. The use of a biodegradable biopolymer for making the phonograph record 1 guarantees a high ease of use of disposal of the phonograph record 1 in such a way as to reduce its environmental impact at the end of its operating cycle.
Vantaggiosamente, l?impiego di un materiale bio-based e anche biodegradabile garantisce al disco fonografico 1 un ciclo vita ad impatto ambientale particolarmente limitato grazie ad una riduzione delle emissioni dei gas a effetto serra relativamente alla fase di produzione e ad uno smaltimento nel rispetto dell?ambiente al termine della sua vita operativa. In particolare, il disco fonografico 1 pu? essere realizzato interamente in biopolimero biodegradabile in modo tale da minimizzare l?impatto ambientale indotto dalla produzione e dallo smaltimento del disco fonografico 1 stesso. Advantageously, the use of a bio-based and also biodegradable material guarantees the phonograph disc 1 a life cycle with a particularly limited environmental impact thanks to a reduction in greenhouse gas emissions in relation to the production phase and disposal in compliance with the ?environment at the end of its operational life. In particular, the phonograph record 1 pu? be made entirely of biodegradable biopolymer in such a way as to minimize the environmental impact induced by the production and disposal of the phonographic record 1 itself.
Preferibilmente, il summenzionato biopolimero biodegradabile ? un biopoliestere scelto dal gruppo comprendente: Preferably, the aforementioned biodegradable biopolymer is a biopolyester selected from the group comprising:
- acido polilattico (PLA); - polylactic acid (PLA);
- PLMS; - PLMS;
- poli-idrossi-alcanoati (PHA), il quale deriva dalla fermentazione batterica a partire da zuccheri e lipidi; - poly-hydroxy-alkanoates (PHA), which derives from bacterial fermentation starting from sugars and lipids;
- poli-idrossi-butirrato (PHB); - polyhydroxybutyrate (PHB);
- poli-idrossi-butirrati-co-idrossivalerati (PHBV); - poly-hydroxy-butyrate-co-hydroxyvalerates (PHBV);
- polilattidi; - polylactides;
- polilattide-co-caprolattone; - polylactide-co-caprolactone;
- policaprolattoni (PCL); - polycaprolactones (PCL);
- omo-poliesteri; - homo-polyesters;
- etero-poliesteri; - hetero-polyesters;
- co-poliesteri alifatici; - aliphatic co-polyesters;
- co-poliesteri aromatici. - aromatic co-polyesters.
Il PLA (abbreviazione di Polylactic Acid= acido polilattico) ? un polimero biodegradabile, ottenuto dalla fermentazione di mais o destrosio. The PLA (abbreviation of Polylactic Acid = polylactic acid)? a biodegradable polymer, obtained from the fermentation of corn or dextrose.
Il PLA ha propriet? meccaniche e termiche simili alla plastica tradizionale basata sul petrolchimico (come polietilene), pertanto il PLA pu? essere stampato e fabbricato utilizzando gli stessi apparati utilizzati per le materie plastiche. Does PLA have properties mechanical and thermal properties similar to traditional petrochemical-based plastics (such as polyethylene), therefore PLA can be molded and manufactured using the same equipment used for plastics.
PLMS ? PLA composito rinforzato con fibre di legno, basato su una matrice di PLA biodegradabile al 100%. PLMS ? Wood fiber reinforced PLA composite, based on a 100% biodegradable PLA matrix.
In particolare, il PLMS ? stato sviluppato da Kareline Oy (Finlandia) ed ? indicato con il nome commerciale Kareline. In particular, the PLMS ? was developed by Kareline Oy (Finland) and ? referred to under the trade name Kareline.
Vantaggiosamente, la presenza di fibre di rinforzo migliora le caratteristiche meccaniche e la capacit? di stampaggio ad iniezione, riducendo il tempo di ciclo dello stampaggio ad iniezione. Inoltre, il PLMS presenta una biodegradabilit? pi? veloce rispetto a PLA. Advantageously, the presence of reinforcing fibers improves the mechanical characteristics and the capacity? of injection molding, reducing the cycle time of injection molding. Furthermore, PLMS has a biodegradability? more faster than PLA.
In accordo con una possibile forma di realizzazione della presente invenzione, il disco fonografico 1 ? realizzato in acido polilattico (PLA) che unisce le vantaggiose caratteristiche dei materiali bio-based e biodegradabili e, inoltre, presentando una rigidezza comparabile a quella del PVC garantisce una elevata qualit? della riproduzione sonora. In accordance with a possible embodiment of the present invention, the phonograph record 1 ? made of polylactic acid (PLA) which combines the advantageous characteristics of bio-based and biodegradable materials and, furthermore, presenting a stiffness comparable to that of PVC, guarantees a high quality? of sound reproduction.
Si sottolinea che l?acido polilattico (PLA) ? un materiale anche compostabileche, per mezzo di un processo di compostaggio della durata di qualche mese (tipicamente 3-6 mesi), si trasforma in un compost, cio? un concime naturale di grande utilit? per l?arricchimento dei terreni, per aiutare le coltivazioni e mitigare la desertificazione ed il rischio idrogeologico. It should be emphasized that polylactic acid (PLA) ? a material that is also compostable which, by means of a composting process lasting a few months (typically 3-6 months), is transformed into a compost, ie? a natural fertilizer of great utility for the enrichment of the land, to help crops and mitigate desertification and hydrogeological risk.
Vantaggiosamente, il disco fonografico 1 viene realizzato mediante un processo di stampaggio ad iniezione presentando, dunque, bassi costi di realizzazione grazie all?elevata produttivit? che caratterizza tale tecnologia di stampaggio. Advantageously, the phonograph disc 1 is made by means of an injection molding process, therefore having low production costs thanks to the high productivity that characterizes this molding technology.
In accordo con un ulteriore aspetto, la presente invenzione fa riferimento ad un processo 100 per la produzione di un disco fonografico. In accordance with a further aspect, the present invention relates to a process 100 for producing a phonograph record.
Il summenzionato processo di produzione 100 comprendente la fase 101 di predisporre una predeterminata quantit? di materiale biobased scelto dal gruppo comprendente: The aforementioned production process 100 comprising the step 101 of preparing a predetermined amount of of biobased material chosen from the group including:
- acido polilattico (PLA), - polylactic acid (PLA),
- PLMS, - PLMS,
- poli-idrossi-alcanoati (PHA), - poly-hydroxy-alkanoates (PHA),
- poli-idrossi-butirrato (PHB), - polyhydroxybutyrate (PHB),
- poli-idrossi-butirrati-co-idrossivalerati (PHBV), - poly-hydroxy-butyrate-co-hydroxyvalerates (PHBV),
- polilattidi, - polylactides,
- polilattide-co-caprolattone, - polylactide-co-caprolactone,
- policaprolattoni (PCL), - polycaprolactones (PCL),
- omo-poliesteri, - homo-polyesters,
- etero-poliesteri, - hetero-polyesters,
- co-poliesteri alifatici, - aliphatic co-polyesters,
- co-poliesteri aromatici, - aromatic co-polyesters,
- Bio-PET, - Bio-PET,
- Bio-PE, - Bio-PE,
- Mater-Bi, - Mater-Bi,
- Bi-Comp, - Bi-Comp,
- Biolice, - Biolice,
- Bioplast, - Bioplast,
- Cereplast Compostables, - Cereplast Compostables,
- Biotecnomais, - Biotechnomais,
- Vegemat, - Vegemat,
- Solanyl, - Solanyl,
- poliidrossialcanoati (PHA), - polyhydroxyalkanoates (PHA),
- poliidrossivaleriato (PHV), - polyhydroxyvaleriate (PHV),
- poliidrossiesanoato (PHH), - polyhydroxyhexanoate (PHH),
- polibutilene succinato (PSB), - polybutylene succinate (PSB),
- Biograde; - Biograde;
- Apinat. - Apinat.
In questo modo il processo 100 permette la produzione di dischi fonografici presentanti un ciclo vita ad impatto ambientale particolarmente limitato grazie all?impiego di materiali di origine biologica (ed, in particolare, non presentanti componenti di origine fossile, cio? derivanti da carbone o petrolio). In this way the process 100 allows the production of phonograph records having a life cycle with a particularly limited environmental impact thanks to the use of materials of biological origin (and, in particular, not having components of fossil origin, i.e. deriving from coal or oil ).
Vantaggiosamente, il summenzionato materiale bio-based pu? essere, inoltre, un biopolimero biodegradabile. Advantageously, the aforementioned bio-based material can also be a biodegradable biopolymer.
In particolare, il biopolimero biodegradabile ? selezionato tra: acido polilattico (PLA), PLMS, poli-idrossi-alcanoati (PHA), poli-idrossi-butirrato (PHB), poli-idrossi-butirrati-co-idrossivalerati (PHBV), polilattidi, polilattideco-caprolattone, policaprolattoni (PCL), omo-poliesteri, etero-poliesteri, copoliesteri alifatici e co-poliesteri aromatici. In particular, the biodegradable biopolymer ? selected from: polylactic acid (PLA), PLMS, polyhydroxyalkanoates (PHA), polyhydroxybutyrate (PHB), polyhydroxybutyratecohydroxyvalerates (PHBV), polylactides, polylactidecocaprolactone, polycaprolactones ( PCL), homo-polyesters, hetero-polyesters, aliphatic co-polyesters and aromatic co-polyesters.
In questo modo, il processo di produzione 100 permette la produzione di un disco fonografico 1 il cui smaltimento impatta limitatamente sull?ambiente. In this way, the production process 100 allows the production of a phonograph record 1 whose disposal has a limited impact on the environment.
Ancora pi? vantaggiosamente, il materiale bio-based pu? essere un materiale compostabile, per esempio l?acido polilattico (PLA), garantendo un rapido smaltimento in condizioni di compostaggio ed un impatto positivo sull?ambiente legato alla produzione di compost a seguito dello smaltimento del disco fonografico 1. even more advantageously, the bio-based material can? be a compostable material, for example polylactic acid (PLA), ensuring rapid disposal in composting conditions and a positive impact on the environment linked to the production of compost following the disposal of the phonograph record 1.
Il processo di produzione 100 comprende inoltre la fase 102 di predisporre uno stampo presentante almeno una superficie sagomata atta a riprodurre almeno un solco fonografico sul summenzionato materiale bio-based. The production process 100 further comprises the step 102 of preparing a mold having at least one shaped surface suitable for reproducing at least one phonographic groove on the aforementioned bio-based material.
Preferibilmente, il summenzionato stampo ? uno stampo a raffreddamento condizionato, per esempio a liquido, che permette un raffreddamento del materiale processato in accordo con determinate tempistiche e/o range di temperature. Preferably, the aforementioned mold ? a mold with conditioned cooling, for example liquid, which allows a cooling of the processed material in accordance with certain times and/or temperature ranges.
Il processo di produzione 100 comprende inoltre una fase 103 di riscaldare il materiale bio-based fino a portarlo ad uno stato almeno parzialmente fluido. The production process 100 further comprises a step 103 of heating the bio-based material until it is at least partially fluid.
Vantaggiosamente, il processo di produzione 100 comprende inoltre una fase 104 di essiccare il materiale bio-based precedente alla fase di riscaldare il materiale bio-based in modo da conferire al materiale biobased propriet? fisiche e meccaniche ottimali per lo stampaggio. Advantageously, the production process 100 further comprises a step 104 of drying the bio-based material prior to the step of heating the bio-based material so as to give the bio-based material properties optimal physical and mechanical properties for moulding.
L?essiccazione permette di controllare con elevata precisione una pluralit? di differenti parametri del processo di produzione del disco fonografico. Per esempio, un?efficace essiccazione del materiale bio-based limita, preferibilmente impedisce, la formazione di gas durante la fase di iniettare una determinata quantit? di materiale bio-based nello stampo (che verr? nel seguito approfonditamente descritta), garantendo una elevata qualit? del disco fonografico, in particolare limitando la formazione di imperfezioni superficiali durante il processo di realizzazione del disco fonografico. Secondo una possibile forma realizzativa del processo, il polimero biobased impiegato ? acido polilattico (PLA) e la fase di essiccare il materiale bio-based comprende disporre il materiale bio-based ad una temperatura di essiccazione compresa tra 30? C e 50? C, per un periodo di essiccazione compreso tra un?ora e cinque ore. Drying allows you to control with high precision a plurality of of different parameters of the phonograph record production process. For example, an effective drying of the bio-based material limits, preferably prevents, the formation of gas during the phase of injecting a certain quantity? of bio-based material in the mold (which will be described in detail below), guaranteeing a high quality? of the phonograph record, in particular by limiting the formation of surface imperfections during the phonograph record making process. According to a possible embodiment of the process, the biobased polymer used? polylactic acid (PLA) and the step of drying the bio-based material comprises arranging the bio-based material at a drying temperature of between 30? C and 50? C, for a drying period of between one and five hours.
Si sottolinea che la temperatura ed il periodo di essiccazione dipendono dal materiale impiegato nel processo, dunque, possono essere differenti da quelli precedentemente indicati senza che venga alterato il concetto inventivo alla base della presente invenzione. It is emphasized that the temperature and the drying period depend on the material used in the process, therefore, they can be different from those previously indicated without altering the inventive concept underlying the present invention.
Il processo di produzione 100 comprende inoltre una fase 105 di convogliare il materiale bio-based in un condotto di lavorazione facendo assumere al materiale bio-based un determinato profilo di temperature. Preferibilmente, il summenzionato profilo di temperature comprende uno o pi? valori di temperatura compresi in un intervallo di temperature tra 140? C e 200? C. The production process 100 further comprises a step 105 of conveying the bio-based material into a processing conduit causing the bio-based material to assume a given temperature profile. Preferably, the aforementioned temperature profile comprises one or more? temperature values included in a temperature range between 140? C and 200? c.
Il processo di produzione 100 comprende inoltre una fase 106 di iniettare una determinata quantit? di materiale bio-based nello stampo. The production process 100 further comprises a step 106 of injecting a certain quantity? of bio-based material in the mold.
In questo modo, il processo di produzione 100 permette di minimizzare la generazione di sfridi di produzione iniettando sostanzialmente l?esatta quantit? di materiale bio-based di cui sar? composto il disco fonografico. Preferibilmente, la fase di iniezione comprende applicare al materiale biobased una pressione compresa tra 1500 bar e 3000 bar per promuovere un ingresso del materiale bio-based nello stampo. In this way, the production process 100 allows to minimize the generation of production scraps by substantially injecting the exact quantity? of bio-based material of which sar? composed the phonograph record. Preferably, the injection step comprises applying to the biobased material a pressure of between 1500 bar and 3000 bar to promote entry of the biobased material into the mould.
In accordo con una possibile forma di realizzazione della presente invenzione, il processo di produzione 100 prevede l?impiego di acido polilattico (PLA) sottoposto ad una fase di essiccazione eseguita ad una temperatura compresa tra i 30? C ed i 50? C per un periodo compreso tra le due e le sei ore. In accordance with a possible embodiment of the present invention, the production process 100 provides for the use of polylactic acid (PLA) subjected to a drying step carried out at a temperature between 30? C and 50? C for between two and six hours.
Inoltre, il processo di produzione 100 prevede di riscaldare l?acido polilattico (PLA) fino ad uno stato almeno parzialmente fluido e la successiva applicazione di una pressione compresa tra 1500 bar e 3000 bar per promuoverne l?ingresso all?interno dello stampo convogliando il materiale attraverso il summenzionato condotto di lavorazione in modo tale che assuma un profilo di temperature decrescente nella direzione di emissione del materiale bio-based e comprese in un intervallo di temperature tra i 200? C ed i 150? C. Furthermore, the production process 100 provides for heating the polylactic acid (PLA) up to an at least partially fluid state and the subsequent application of a pressure between 1500 bar and 3000 bar to promote its entry into the mold by conveying the material through the aforementioned processing duct in such a way that it assumes a temperature profile decreasing in the emission direction of the bio-based material and included in a temperature range between 200? C and the 150? c.
Vantaggiosamente, pu? essere applicato un profilo di temperature selezionato dall?intervallo sopra indicato e decrescente a partire da una temperatura massima in corrispondenza dell?ugello di iniezione del materiale all?interno del condotto di lavorazione ad una temperatura minima in corrispondenza della tramoggia che permette il passaggio del materiale dal condotto allo stampo. Advantageously, can? be applied a temperature profile selected from the range indicated above and decreasing starting from a maximum temperature at the injection nozzle of the material inside the processing duct to a minimum temperature at the hopper which allows the passage of the material from the duct to the mould.
In questo modo, il processo di produzione 100 permette di facilitare lo stampaggio dell?acido polilattico (PLA) conferendogli propriet? fisiche e meccaniche che lo rendono maggiormente processabile. In this way, the production process 100 makes it possible to facilitate the molding of polylactic acid (PLA) by giving it properties physical and mechanical properties that make it more processable.
In accordo con alcune possibili forme realizzative puramente esemplificative e non limitative della presente invenzione, la fase di iniezione 106 pu? essere realizzata secondo una tecnologia di iniezione sottomarina o iniezione a canale caldo. In accordance with some possible embodiments which are purely exemplary and non-limiting of the present invention, the injection step 106 can be made according to a submarine injection or hot runner injection technology.
Vantaggiosamente, la fase di iniezione comprende iniettare il materiale bio-based in corrispondenza di una pluralit? di differenti aperture del summenzionato stampo rendendo maggiormente omogenea la distribuzione del fluido all?interno dello stampo. Advantageously, the injection step comprises injecting the bio-based material at a plurality of? of different openings of the aforementioned mould, making the distribution of the fluid inside the mold more homogeneous.
Il processo di produzione 100 comprende inoltre una fase 107 di mantenere il materiale bio-based all?interno dello stampo per un intervallo di tempo di raffreddamento definito. The production process 100 further comprises a step 107 of keeping the bio-based material inside the mold for a defined cooling time interval.
Vantaggiosamente, la fase di mantenimento 107 pu? essere realizzata applicando tonnellaggio allo stampo. Advantageously, the maintenance phase 107 can? be accomplished by applying tonnage to the mold.
In questo modo, la fase 107 di mantenimento consente di evitare variazioni nella geometria del pezzo durante il raffreddamento, garantendo al processo un?elevata precisione dimensionale nella realizzazione del disco fonografico. In this way, the holding step 107 allows to avoid variations in the geometry of the piece during cooling, guaranteeing the process a high dimensional precision in the making of the phonographic record.
Preferibilmente, il valore dell?intervallo di tempo di raffreddamento definito ? maggiore di 30 secondi, in particolare compreso tra 30 secondi e 60 secondi. Preferably, the value of the defined cooling time interval? greater than 30 seconds, especially between 30 seconds and 60 seconds.
Si osserva quindi che la presente invenzione raggiunge gli scopi proposti realizzando un disco fonografico ed un processo per la produzione di un disco fonografico ecocompatibili e presentanti un impatto limitato sull?ambiente grazie all?impiego di un materiale bio-based derivato almeno parzialmente da fonti rinnovabili e vantaggiosamente anche biodegradabile. It can therefore be observed that the present invention achieves the proposed aims by realizing an environmentally friendly phonograph record and a process for the production of a phonograph record which have a limited impact on the environment thanks to the use of a bio-based material derived at least partially from renewable sources and advantageously also biodegradable.
Vantaggiosamente, la presente invenzione che supera la necessit? dell?impiego di risorse di origine fossile intrinsecamente inquinanti per la realizzazione di supporti fonografici, garantendo l?ecosostenibilit? delle fasi di produzione e di smaltimento. Advantageously, the present invention which overcomes the necessity of the use of intrinsically polluting resources of fossil origin for the production of phonographic supports, guaranteeing eco-sustainability? of the production and disposal stages.
Vantaggiosamente, inoltre, la presente invenzione ottimizza il processo produttivo di dischi fonografici grazie all?impiego della stampa ad iniezione che permette elevati ratei produttivi e ridotti costi di gestione. Furthermore, the present invention advantageously optimizes the production process of phonograph records thanks to the use of injection molding which allows high production rates and reduced management costs.
Claims (16)