IT201900013800A1 - Compostable film especially for food packaging - Google Patents

Compostable film especially for food packaging Download PDF

Info

Publication number
IT201900013800A1
IT201900013800A1 IT102019000013800A IT201900013800A IT201900013800A1 IT 201900013800 A1 IT201900013800 A1 IT 201900013800A1 IT 102019000013800 A IT102019000013800 A IT 102019000013800A IT 201900013800 A IT201900013800 A IT 201900013800A IT 201900013800 A1 IT201900013800 A1 IT 201900013800A1
Authority
IT
Italy
Prior art keywords
layer
film according
product
multilayer film
packaged
Prior art date
Application number
IT102019000013800A
Other languages
Italian (it)
Inventor
Vincenzo Pogliano
Original Assignee
Pogliano Flexible Packaging Srl
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Pogliano Flexible Packaging Srl filed Critical Pogliano Flexible Packaging Srl
Priority to IT102019000013800A priority Critical patent/IT201900013800A1/en
Publication of IT201900013800A1 publication Critical patent/IT201900013800A1/en

Description

"Film compostabile specialmente per il confezionamento di alimenti" "Compostable film especially for food packaging"

DESCRIZIONE DESCRIPTION

Settore della Tecnica Technical sector

La presente invenzione si riferisce a un film multistrato compostabile, adatto al confezionamento di prodotti farmaceutici e prodotti alimentari, più specialmente per prodotti alimentari. The present invention refers to a compostable multilayer film, suitable for the packaging of pharmaceutical products and food products, more especially for food products.

Arte Nota Note Art

Al giorno d’oggi sono note differenti tipologie di film multistrato per il confezionamento di prodotti farmaceutici, come per esempio nutraceutici, integratori e simili, e di prodotti alimentari, come per esempio salumi, derivati del latte, carni, prodotti da forno e simili. Di grande diffusione sono i fogli del tipo comprendente un primo strato di carta, esterno, accoppiato ad un secondo strato in polietilene e/o polipropilene orientati, interno, come descritto in WO2013/163036. Sullo strato di carta esterno vengono generalmente stampati segni caratteristici, distintivi e ornamentali, mentre lo strato di polimero va a contatto con il prodotto per la migliore conservazione di quest’ultimo. Nowadays, different types of multilayer films are known for the packaging of pharmaceutical products, such as nutraceuticals, supplements and the like, and food products, such as cured meats, dairy products, meats, baked goods and the like. The sheets of the type comprising a first external paper layer coupled to a second internal oriented polyethylene and / or polypropylene layer, as described in WO2013 / 163036, are widely used. Characteristic, distinctive and ornamental signs are generally printed on the outer paper layer, while the polymer layer comes into contact with the product for the best preservation of the latter.

Tali materiali compositi, seppur ampiamente utilizzati, presentano alcuni inconvenienti. These composite materials, although widely used, have some drawbacks.

Numerosi studi effettuati su questi materiali compositi hanno evidenziato che, qualora essi non vengano avviati allo smaltimento separati nei propri componenti, ma avviati integralmente a compostaggio, oppure a procedimenti di produzione di biomassa per altri impieghi (come per esempio biocombustibili o ammendanti del suolo), tali film si degradano in tempi relativamente lunghi, non accettabili alla luce dei requisiti correnti di sostenibilità e riciclabilità. Inoltre, possono insorgere importanti e indesiderate contaminazioni del suolo, nel medio e lungo periodo. Numerous studies carried out on these composite materials have shown that, if they are not sent for separate disposal in their components, but sent entirely to composting, or to biomass production processes for other uses (such as biofuels or soil improvers), these films degrade in a relatively long time, which is not acceptable in light of the current sustainability and recyclability requirements. Furthermore, important and unwanted soil contamination can arise in the medium and long term.

E’ pertanto ancora sentita la necessità di disporre di un film multistrato che permetta di superare gli inconvenienti della tecnica nota. Questo ed altri scopi della presente invenzione sono raggiunti come rivendicato nelle annesse rivendicazioni che costituiscono parte integrante dell’insegnamento tecnico qui fornito. The need is therefore still felt to have a multilayer film that allows to overcome the drawbacks of the known art. This and other purposes of the present invention are achieved as claimed in the attached claims which form an integral part of the technical teaching provided herein.

Descrizione dell’Invenzione Description of the Invention

Scopo principale della presente invenzione è quello di realizzare un film multistrato per il confezionamento di prodotti farmaceutici, come per esempio nutraceutici, integratori e simili, e di prodotti alimentari, come per esempio salumi, derivati del latte, carni, prodotti da forno e simili. The main object of the present invention is to provide a multilayer film for packaging pharmaceutical products, such as nutraceuticals, supplements and the like, and food products, such as cold cuts, milk derivatives, meats, baked goods and the like.

Un altro importante scopo della presente invenzione è quello di realizzare un film multistrato per il confezionamento di prodotti farmaceutici, come per esempio nutraceutici, integratori e simili, e di prodotti alimentari, come per esempio salumi, derivati del latte, carni, prodotti da forno e simili, che sia compostabile e in grado di decomporsi senza rilasciare elementi inquinanti e contaminanti (Riferimento normativo: EN 13432). Another important object of the present invention is to provide a multilayer film for the packaging of pharmaceutical products, such as nutraceuticals, supplements and the like, and of food products, such as cured meats, milk derivatives, meats, baked goods and similar, which is compostable and able to decompose without releasing polluting and contaminating elements (Reference standard: EN 13432).

Ancora uno scopo della presente invenzione è quello di realizzare un film multistrato per il confezionamento di prodotti farmaceutici, come per esempio nutraceutici, integratori e simili, e di prodotti alimentari, come per esempio salumi, derivati del latte, carni, prodotti da forno e simili, che sia in grado di assicurare un maggior mantenimento nel tempo delle caratteristiche chimiche ed organolettiche, nonché della qualità, del prodotto confezionato. Another object of the present invention is to provide a multilayer film for packaging pharmaceutical products, such as nutraceuticals, supplements and the like, and food products, such as cured meats, milk derivatives, meats, baked goods and the like. , which is able to ensure greater maintenance over time of the chemical and organoleptic characteristics, as well as the quality of the packaged product.

Infine, ancora un ulteriore aspetto della presente è quello di fornire un film multistrato che sia producibile a livello industriale, a partire da materie prime commercialmente disponibili e a costi ragionevoli, attraverso metodi e tecnologie consolidate ben note all’Esperto del ramo. Finally, yet another aspect of the present is to provide a multilayer film that is industrially producible, starting from commercially available raw materials and at reasonable costs, through established methods and technologies well known to the expert in the field.

Tutti questi scopi sono raggiunti, come apparirà più chiaramente in seguito, con le forme di realizzazione e gli insegnamenti qui descritti. All of these objects are achieved, as will become clearer below, with the embodiments and teachings described herein.

Alcuni termini della presente invenzione hanno il significato definito qui di seguito. Il termine “circa” include gli intervalli di condizioni operative e di parametri che possono essere normalmente impiegati nel processo della presente invenzione. Some terms of the present invention have the meaning defined below. The term "about" includes ranges of operating conditions and parameters that can normally be employed in the process of the present invention.

Il termine “compostabilità” si riferisce alla capacità di un materiale organico di trasformarsi in un prodotto finale, che prende il nome di “compost”, frutto della sua degradazione aerobica, cioè in presenza di ossigeno. Il compost maturo è simile ad un terriccio fertile e per le sue caratteristiche può essere impiegato come fertilizzante e/o ammendante del suolo. Le caratteristiche che un materiale di imballaggio deve possedere per il requisito di compostabilità sono regolamentate dalla normativa EN 13432, che completa la precedente Direttiva 94/62/CE. The term “compostability” refers to the ability of an organic material to transform itself into a final product, which takes the name of “compost”, the result of its aerobic degradation, ie in the presence of oxygen. Mature compost is similar to fertile soil and due to its characteristics it can be used as a fertilizer and / or soil improver. The characteristics that a packaging material must possess for the compostability requirement are regulated by the EN 13432 standard, which completes the previous Directive 94/62 / EC.

I termini “rateo di trasmissione di ossigeno” si riferiscono alla capacità del film della presente invenzione di costituire una barriera per la diffusione dell’ossigeno atmosferico verso il prodotto da confezionare. The terms "oxygen transmission rate" refer to the ability of the film of the present invention to constitute a barrier for the diffusion of atmospheric oxygen towards the product to be packaged.

I termini “rateo di trasmissione di vapore d’acqua” si riferiscono alla capacità del film della presente invenzione di costituire una barriera per la diffusione dell’umidità atmosferica verso il prodotto da confezionare. The terms "water vapor transmission rate" refer to the ability of the film of the present invention to constitute a barrier for the diffusion of atmospheric humidity towards the product to be packaged.

Descrizione Sintetica delle Figure Brief Description of the Figures

- la Figura 1 rappresenta una sezione schematica di un film in accordo a una forma di realizzazione dell’invenzione; - Figure 1 represents a schematic section of a film according to an embodiment of the invention;

- la Figura 2 rappresenta una sezione schematica di un film in accordo a una forma di realizzazione dell’invenzione; - Figure 2 represents a schematic section of a film according to an embodiment of the invention;

- la Figura 3 rappresenta una sezione schematica di un film in accordo a una forma di realizzazione dell’invenzione; - Figure 3 represents a schematic section of a film according to an embodiment of the invention;

- la Figura 4 rappresenta una sezione schematica di un film in accordo a una forma di realizzazione dell’invenzione; - Figure 4 represents a schematic section of a film according to an embodiment of the invention;

- la Figura 5 rappresenta una sezione schematica di un film in accordo a una forma di realizzazione dell’invenzione. - Figure 5 represents a schematic section of a film according to an embodiment of the invention.

Descrizione di alcune forme preferite di realizzazione dell’invenzione Description of some preferred embodiments of the invention

Vengono ora descritte diverse forme di realizzazione del film della presente invenzione, con riferimento alle figure annesse. Vantaggiosamente le forme di realizzazione della presente invenzione possono comprendere soluzioni multistrato, più preferibilmente bistrato o tri-strato, che combinano le proprietà di ciascuno strato per raggiungere gli scopi funzionali che la presente invenzione si propone. Various embodiments of the film of the present invention are now described, with reference to the attached figures. Advantageously, the embodiments of the present invention can comprise multilayer solutions, more preferably two-layer or three-layer, which combine the properties of each layer to achieve the functional purposes that the present invention proposes.

Con riferimento alla Figura 1, è descritta una forma di realizzazione del film dell’invenzione, comprendente, dall’alto verso il basso: With reference to Figure 1, an embodiment of the film of the invention is described, comprising, from top to bottom:

- un primo strato 101 realizzato in un primo materiale, da rivolgere verso l’esterno; - una applicazione intermedia 102 di adesivo; - a first layer 101 made of a first material, to be turned outwards; - an intermediate application 102 of adhesive;

- una applicazione intermedia 103 di inchiostro; - an intermediate application 103 of ink;

- un secondo strato 104, in materiale polimerico, a contatto con il prodotto da confezionare. - a second layer 104, made of polymeric material, in contact with the product to be packaged.

La peculiarità del ritrovato risiede nel fatto che il materiale polimerico del secondo strato 104 è dato da un polimero compostabile, adatto al contatto con il prodotto da confezionare, selezionato da un gruppo comprendente acido polilattico (PLA), acido poliglicolico (PGA), poliidrossialcanoato (PHA), o loro miscele, che possono essere lavorati, ad esempio estrusi e/o laminati, come polimeri di origine petrolchimica. Il secondo strato 104 può comprendere anche additivi preposti a modificare colorazione e caratteristiche tecniche, preservandone comunque l’idoneità al contatto con il prodotto da confezionare. The peculiarity of the invention lies in the fact that the polymeric material of the second layer 104 is given by a compostable polymer, suitable for contact with the product to be packaged, selected from a group comprising polylactic acid (PLA), polyglycolic acid (PGA), polyhydroxyalkanoate ( PHA), or their mixtures, which can be processed, for example extruded and / or laminated, as polymers of petrochemical origin. The second layer 104 may also include additives designed to modify color and technical characteristics, while preserving their suitability for contact with the product to be packaged.

In una forma preferita di realizzazione dell’invenzione, il secondo strato 104 è acido polilattico (PLA). Inoltre, detto secondo strato ha una grammatura preferibilmente compresa tra circa 55 g/m<2 >e circa 65 g/m<2>, con uno spessore di circa 50�m. In a preferred embodiment of the invention, the second layer 104 is polylactic acid (PLA). Furthermore, said second layer has a weight preferably comprised between about 55 g / m <2> and about 65 g / m <2>, with a thickness of about 50 m.

In una forma preferita di realizzazione dell’invenzione, il primo strato 101 può essere in carta di cellulosa pura, per alimenti e/o riciclata. Ancora più preferibilmente, il primo strato 101 è carta trasparente, come per esempio pergamina o carta glassine, con una grammatura preferibilmente compresa tra circa 30 g/m<2 >e circa 35 g/m<2>, caratterizzata da ottima resistenza allo strappo e alla trazione, idonea all’imballaggio di alimenti e prodotti deperibili. In a preferred embodiment of the invention, the first layer 101 can be in pure cellulose paper, for food and / or recycled. Even more preferably, the first layer 101 is transparent paper, such as pergamine or glassine paper, with a weight preferably between about 30 g / m <2> and about 35 g / m <2>, characterized by excellent tear resistance. and traction, suitable for the packaging of food and perishable products.

L’Esperto del ramo apprezzerà che, comprendendo detto materiale cartaceo prodotti di origine vegetale, esso è in linea con gli scopi della presente invenzione. The skilled in the art will appreciate that, by including said paper material products of plant origin, it is in line with the purposes of the present invention.

Opzionalmente, in dipendenza della natura del prodotto da confezionare, il primo strato 101 può essere coperto da lacca impermeabilizzante 101’, o può essere usata carta impermeabilizzata. In una forma di realizzazione, il primo strato può essere coperto di lacca impermeabilizzante in ragione di circa 2 g/m<2>, eventualmente preceduto da un’applicazione di primer. Optionally, depending on the nature of the product to be packaged, the first layer 101 can be covered with waterproofing lacquer 101 ', or waterproofed paper can be used. In one embodiment, the first layer can be covered with waterproofing lacquer at a rate of about 2 g / m <2>, possibly preceded by an application of primer.

L’Esperto del ramo apprezzerà che, comprendendo detto materiale cartaceo prodotti di origine vegetale, esso è in linea con gli scopi della presente invenzione. The skilled in the art will appreciate that, by including said paper material products of plant origin, it is in line with the purposes of the present invention.

L’adesivo applicato è preferibilmente a base di materiale atossico, compostabile, come un prodotto selezionato da un gruppo comprendente biopolimeri, come per esempio amidi vegetali, polisaccaridi, e polimeri sintetici compostabili, come per esempio poliisocianati e poliuretani. In una forma preferita di realizzazione dell’invenzione, l’adesivo applicato è un poliisocianato alifatico, addizionato di un opportuno catalizzatore di reticolazione. In accordo con gli scopi della presente invenzione, l’adesivo viene applicato secondo metodologie ben note all’Esperto della tecnica, che non costituiscono una limitazione della presente invenzione, previa dispersione in acqua. The adhesive applied is preferably based on non-toxic, compostable material, such as a product selected from a group comprising biopolymers, such as vegetable starches, polysaccharides, and compostable synthetic polymers, such as polyisocyanates and polyurethanes. In a preferred embodiment of the invention, the adhesive applied is an aliphatic polyisocyanate, added with a suitable crosslinking catalyst. In accordance with the purposes of the present invention, the adhesive is applied according to methods well known to those skilled in the art, which do not constitute a limitation of the present invention, after dispersion in water.

L’inchiostro applicato ha una grammatura preferibilmente compresa tra circa l’1% e circa il 5% della grammatura del film dell’invenzione. Le tipologie e modalità di applicazione dell’inchiostro per fini di etichettura e/o decorativi sono ben note a tutti coloro che sono esperti nella tecnica, e non costituiscono una limitazione della presente invenzione. The ink applied has a weight preferably between about 1% and about 5% of the weight of the film of the invention. The types and methods of ink application for labeling and / or decorative purposes are well known to all those skilled in the art, and do not constitute a limitation of the present invention.

In una forma preferita di realizzazione, il film dell’invenzione può avere una grammatura compresa tra circa 90 g/m2 e circa 105 g/m2, con uno spessore totale di circa 85 μm, un rateo di trasmissione di ossigeno non superiore a circa 430 cm3/m2/24h e un rateo di trasmissione di vapore d’acqua non superiore a circa 170 g/m<2>/24h. In a preferred embodiment, the film of the invention can have a grammage between about 90 g / m2 and about 105 g / m2, with a total thickness of about 85 μm, an oxygen transmission rate not exceeding about 430 cm3 / m2 / 24h and a water vapor transmission rate not exceeding about 170 g / m <2> / 24h.

Con riferimento alla Figura 2, è descritta un’altra forma di realizzazione del film dell’invenzione, comprendente, dall’alto verso il basso: With reference to Figure 2, another embodiment of the film of the invention is described, comprising, from top to bottom:

- un primo strato 111 realizzato in un primo materiale, da rivolgere verso l’esterno; - una applicazione intermedia 112 di inchiostro; - a first layer 111 made of a first material, to be turned outwards; - an intermediate ink application 112;

- una applicazione intermedia 113 di adesivo; - an intermediate application 113 of adhesive;

- un secondo strato 114, in materiale polimerico, a contatto con il prodotto da confezionare. - a second layer 114, made of polymeric material, in contact with the product to be packaged.

La peculiarità del ritrovato risiede nel fatto che il materiale polimerico del secondo strato 114 è dato da un polimero compostabile, adatto al contatto con il prodotto da confezionare, selezionato da un gruppo comprendente acido polilattico (PLA), acido poliglicolico (PGA), poliidrossialcanoato (PHA), o loro miscele, che possono essere lavorati, ad esempio estrusi e/o laminati, come polimeri di origine petrolchimica. Il secondo strato 114 può comprendere anche additivi preposti a modificare colorazione e caratteristiche tecniche, preservandone comunque l’idoneità al contatto con il prodotto da confezionare. The peculiarity of the invention lies in the fact that the polymeric material of the second layer 114 is given by a compostable polymer, suitable for contact with the product to be packaged, selected from a group comprising polylactic acid (PLA), polyglycolic acid (PGA), polyhydroxyalkanoate ( PHA), or their mixtures, which can be processed, for example extruded and / or laminated, as polymers of petrochemical origin. The second layer 114 may also include additives designed to modify color and technical characteristics, while preserving their suitability for contact with the product to be packaged.

In una forma preferita di realizzazione dell’invenzione, il secondo strato 114 è acido polilattico (PLA). In a preferred embodiment of the invention, the second layer 114 is polylactic acid (PLA).

In una forma preferita di realizzazione dell’invenzione, il primo strato 111 può essere in carta di cellulosa pura, per alimenti e/o riciclata. Ancora più preferibilmente, il primo strato 111 è carta trasparente, come per esempio pergamina o carta glassine, con una grammatura preferibilmente compresa tra 30 g/m<2 >e circa 35 g/m<2>, caratterizzata da ottima resistenza allo strappo e alla trazione, idonea all’imballaggio di alimenti e prodotti deperibili. L’Esperto del ramo apprezzerà che, comprendendo detto materiale cartaceo prodotti di origine vegetale, esso è in linea con gli scopi della presente invenzione. In a preferred embodiment of the invention, the first layer 111 can be in pure cellulose paper, for food and / or recycled. Even more preferably, the first layer 111 is transparent paper, such as pergamine or glassine paper, with a weight preferably between 30 g / m <2> and about 35 g / m <2>, characterized by excellent tear resistance and traction, suitable for the packaging of food and perishable products. The skilled in the art will appreciate that, by including said paper material products of plant origin, it is in line with the purposes of the present invention.

Opzionalmente, in dipendenza della natura del prodotto da confezionare, il primo strato 111 può essere coperto da lacca impermeabile all’acqua 111’, o può essere usata carta impermeabilizzata. In una forma di realizzazione, il primo strato può essere coperto di lacca impermeabile all’acqua in ragione di circa 2 g/m<2>, eventualmente preceduto da un’applicazione di primer. Optionally, depending on the nature of the product to be packaged, the first layer 111 can be covered with 111 'water-proof lacquer, or waterproofed paper can be used. In one embodiment, the first layer can be covered with water-proof lacquer at a rate of about 2 g / m <2>, possibly preceded by an application of primer.

L’adesivo applicato è preferibilmente a base di materiale atossico, compostabile, come un prodotto selezionato da un gruppo comprendente biopolimeri, come per esempio amidi vegetali, polisaccaridi, e polimeri sintetici compostabili, come per esempio poliisocianati e poliuretani. In una forma preferita di realizzazione dell’invenzione, l’adesivo applicato è un poliisocianato alifatico, addizionato di un opportuno catalizzatore di reticolazione. In accordo con gli scopi della presente invenzione, l’adesivo viene applicato secondo metodologie ben note all’Esperto della tecnica, che non costituiscono una limitazione della presente invenzione, previa dispersione in acqua. The adhesive applied is preferably based on non-toxic, compostable material, such as a product selected from a group comprising biopolymers, such as vegetable starches, polysaccharides, and compostable synthetic polymers, such as polyisocyanates and polyurethanes. In a preferred embodiment of the invention, the adhesive applied is an aliphatic polyisocyanate, added with a suitable crosslinking catalyst. In accordance with the purposes of the present invention, the adhesive is applied according to methods well known to those skilled in the art, which do not constitute a limitation of the present invention, after dispersion in water.

L’inchiostro applicato ha una grammatura preferibilmente compresa tra circa l’1% e circa il 5% della grammatura del film dell’invenzione. Le tipologie e modalità di applicazione dell’inchiostro per fini di etichettura e/o decorativi sono ben note a tutti coloro che sono esperti nella tecnica, e non costituiscono una limitazione della presente invenzione. The ink applied has a weight preferably between about 1% and about 5% of the weight of the film of the invention. The types and methods of ink application for labeling and / or decorative purposes are well known to all those skilled in the art, and do not constitute a limitation of the present invention.

In una forma di realizzazione del film bi-strato della Figura 2, per creare un effetto traspirante in dipendenza della natura del prodotto da confezionare, lo strato 114 può essere perforato. La fase di perforazione dello strato 114 avviene prima dell’assemblaggio per creare il film bi-strato della Figura 2, e avviene tramite tecniche e dispositivi di per sé noti. In aggiunta, l’adesivo 113 può anche essere applicato in modo da formare una pluralità di canali con un caratteristico pattern, per aumentare l’effetto di traspirazione, alcuni di detti canali essendo comunicanti fra loro, ad esempio comunicanti a coppie, ciascuna coppia essendo separata, ossia non comunicante, con le altre coppie. In alternativa, lo strato di adesivo può essere applicato in modo da formare una pluralità di canali con un disegno complementare o in negativo rispetto al pattern sopra citato. Opzionalmente, nel caso di strato 114 perforato e in dipendenza della natura del prodotto da confezionare, allo scopo di proteggere il prodotto dall’ossigeno atmosferico preservandone la qualità, lo strato 111 può essere ricoperto da lacca impermeabile ai gas 111’, detta lacca eventualmente ricoperta a sua volta da vernice protettiva. L’applicazione della lacca 111’ allo strato 111 può essere eventualmente facilitata dall’impiego di un primer. In an embodiment of the bi-layer film of Figure 2, in order to create a transpiring effect depending on the nature of the product to be packaged, the layer 114 can be perforated. The step of perforation of the layer 114 takes place before assembly to create the bi-layer film of Figure 2, and takes place through known techniques and devices. In addition, the adhesive 113 can also be applied so as to form a plurality of channels with a characteristic pattern, to increase the transpiration effect, some of said channels being communicating with each other, for example communicating in pairs, each pair being separate, i.e. not communicating, with the other couples. Alternatively, the adhesive layer can be applied so as to form a plurality of channels with a complementary or negative pattern with respect to the aforementioned pattern. Optionally, in the case of a perforated layer 114 and depending on the nature of the product to be packaged, in order to protect the product from atmospheric oxygen while preserving its quality, the layer 111 can be covered with gas impermeable lacquer 111 ', said lacquer possibly covered in turn from protective varnish. The application of lacquer 111 'to layer 111 can possibly be facilitated by the use of a primer.

Al contrario, in un’altra forma di realizzazione del film della Figura 2 dell’invenzione, per aumentare l’effetto barriera in dipendenza della natura del prodotto da confezionare tra 113 e 114 non perforato, può essere interposta un’applicazione di lacca senza soluzione di continuità secondo tecniche e dispositivi noti all’Esperto del ramo. In alternativa, per aumentare l’effetto barriera nei confronti dell’ossigeno e dell’umidità atmosferica, tra 113 e 114 non perforato, può essere interposto uno strato di acido polilattico (PLA) metallizzato, preferibilmente metallizzato con Alluminio. On the contrary, in another embodiment of the film of Figure 2 of the invention, to increase the barrier effect depending on the nature of the product to be packaged between 113 and 114 non-perforated, an application of lacquer without solution can be interposed. continuity according to techniques and devices known to those skilled in the art. Alternatively, to increase the barrier effect against oxygen and atmospheric humidity, between 113 and 114 not perforated, a layer of metallized polylactic acid (PLA) can be interposed, preferably metallized with aluminum.

Esempi di lacche impermeabili possono comprendere materiali polimerici selezionati da un gruppo comprendente PVDC (polivinilidene cloruro), EVOH (copolimero etilene-alcol vinilico), PVOH (copolimero propilene-alcol vinilico), o loro miscele. Examples of impermeable lacquers may include polymeric materials selected from a group including PVDC (polyvinylidene chloride), EVOH (ethylene-vinyl alcohol copolymer), PVOH (propylene-vinyl alcohol copolymer), or mixtures thereof.

Ancora in una forma preferita di realizzazione del film della Figura 2 dell’invenzione, il primo strato 111 può essere costituito da un materiale polimerico compostabile, preferibilmente acido polilattico (PLA) trasparente, con interposto tra 113 e 114 una lacca impermeabile ai gas o uno strato di acido polilattico metallizzato, preferibilmente metallizzato con Alluminio. Still in a preferred embodiment of the film of Figure 2 of the invention, the first layer 111 can be constituted by a compostable polymeric material, preferably transparent polylactic acid (PLA), with between 113 and 114 a gas-impermeable lacquer or a metallized polylactic acid layer, preferably metallized with Aluminum.

Con riferimento alla Figura 3, è descritta una forma di realizzazione del film dell’invenzione, comprendente, dall’alto verso il basso: With reference to Figure 3, an embodiment of the film of the invention is described, comprising, from top to bottom:

- una applicazione di inchiostro 121; - an application of ink 121;

- un primo strato 122 realizzato in un primo materiale, da rivolgere verso l’esterno; - una applicazione intermedia 123 di adesivo; - a first layer 122 made of a first material, to be turned outwards; - an intermediate application 123 of adhesive;

- un secondo strato 124, in materiale polimerico, a contatto con il prodotto da confezionare. - a second layer 124, made of polymeric material, in contact with the product to be packaged.

La peculiarità del ritrovato risiede nel fatto che il materiale polimerico del secondo strato 124 è dato da un polimero compostabile, adatto al contatto con il prodotto da confezionare, selezionato da un gruppo comprendente acido polilattico (PLA), acido poliglicolico (PGA), poliidrossialcanoato (PHA), o loro miscele, che possono essere lavorati, ad esempio estrusi e/o laminati, come polimeri di origine petrolchimica. Il secondo strato 124 può comprendere anche additivi preposti a modificare colorazione e caratteristiche tecniche, preservandone comunque l’idoneità al contatto con il prodotto da confezionare. The peculiarity of the invention lies in the fact that the polymeric material of the second layer 124 is given by a compostable polymer, suitable for contact with the product to be packaged, selected from a group comprising polylactic acid (PLA), polyglycolic acid (PGA), polyhydroxyalkanoate ( PHA), or their mixtures, which can be processed, for example extruded and / or laminated, as polymers of petrochemical origin. The second layer 124 may also include additives designed to modify color and technical characteristics, while preserving their suitability for contact with the product to be packaged.

In una forma preferita di realizzazione dell’invenzione, il secondo strato 124 è acido polilattico (PLA). In a preferred embodiment of the invention, the second layer 124 is polylactic acid (PLA).

In una forma preferita di realizzazione dell’invenzione, il primo strato 122 può essere in carta di cellulosa pura, per alimenti e/o riciclata. L’Esperto del ramo apprezzerà che, comprendendo detto materiale cartaceo prodotti di origine vegetale, esso è in linea con gli scopi della presente invenzione. In a preferred embodiment of the invention, the first layer 122 can be in pure cellulose paper, for food and / or recycled. The skilled in the art will appreciate that, by including said paper material products of plant origin, it is in line with the purposes of the present invention.

Opzionalmente, in dipendenza della natura del prodotto da confezionare, il primo strato 121 può essere coperto da lacca impermeabile all’acqua 121’, o può essere usata carta impermeabilizzata. In una forma di realizzazione, il primo strato può essere coperto di lacca impermeabile all’acqua in ragione di circa 2 g/m<2>, eventualmente preceduto da un’applicazione di primer. Optionally, depending on the nature of the product to be packaged, the first layer 121 can be covered with water-proof lacquer 121 ', or waterproofed paper can be used. In one embodiment, the first layer can be covered with water-proof lacquer at a rate of about 2 g / m <2>, possibly preceded by an application of primer.

L’adesivo applicato è preferibilmente a base di materiale atossico, compostabile, come un prodotto selezionato da un gruppo comprendente biopolimeri, come per esempio amidi vegetali, polisaccaridi, e polimeri sintetici compostabili, come per esempio poliisocianati e poliuretani. In una forma preferita di realizzazione dell’invenzione, l’adesivo applicato è un poliisocianato alifatico, addizionato di un opportuno catalizzatore di reticolazione. In accordo con gli scopi della presente invenzione, l’adesivo viene applicato secondo metodologie ben note all’Esperto della tecnica, che non costituiscono una limitazione della presente invenzione, previa dispersione in acqua. The adhesive applied is preferably based on non-toxic, compostable material, such as a product selected from a group comprising biopolymers, such as vegetable starches, polysaccharides, and compostable synthetic polymers, such as polyisocyanates and polyurethanes. In a preferred embodiment of the invention, the adhesive applied is an aliphatic polyisocyanate, added with a suitable crosslinking catalyst. In accordance with the purposes of the present invention, the adhesive is applied according to methods well known to those skilled in the art, which do not constitute a limitation of the present invention, after dispersion in water.

L’inchiostro applicato ha una grammatura preferibilmente compresa tra circa l’1% e il 5% del peso totale della grammatura dell’invenzione. Le tipologie e modalità di applicazione dell’inchiostro per fini di etichettura e/o decorativi sono ben note a tutti coloro che sono esperti nella tecnica, e non costituiscono una limitazione della presente invenzione. The ink applied has a weight preferably between about 1% and 5% of the total weight of the invention. The types and methods of ink application for labeling and / or decorative purposes are well known to all those skilled in the art, and do not constitute a limitation of the present invention.

Con riferimento alla Figura 4, è illustrata un’altra forma di realizzazione dell’invenzione, comprendente, dall’alto verso il basso: With reference to Figure 4, another embodiment of the invention is illustrated, comprising, from top to bottom:

- un primo strato 201 realizzato in un primo materiale, da rivolgere verso l’esterno; - una applicazione intermedia 202 di adesivo; - a first layer 201 made of a first material, to be turned outwards; - an intermediate application 202 of adhesive;

- una applicazione intermedia 203 di inchiostro; - an intermediate application 203 of ink;

- un secondo strato 204, in materiale polimerico, a contatto con il prodotto da confezionare. - a second layer 204, made of polymeric material, in contact with the product to be packaged.

La peculiarità del ritrovato risiede nel fatto che il materiale polimerico del secondo strato 204 è dato da una fibra polimerica compostabile, adatta al contatto con il prodotto da confezionare, selezionato da un gruppo comprendente acido polilattico (PLA), acido poliglicolico (PGA), poliidrossialcanoato (PHA), o loro miscele, che possono essere lavorati, ad esempio filati, come polimeri di origine petrolchimica. Il secondo strato 204 può comprendere anche additivi preposti a modificare colorazione e caratteristiche tecniche, preservandone comunque l’idoneità al contatto con il prodotto da confezionare. The peculiarity of the invention lies in the fact that the polymeric material of the second layer 204 is given by a compostable polymeric fiber, suitable for contact with the product to be packaged, selected from a group comprising polylactic acid (PLA), polyglycolic acid (PGA), polyhydroxyalkanoate (PHA), or mixtures thereof, which can be processed, for example yarns, as polymers of petrochemical origin. The second layer 204 may also include additives designed to modify color and technical characteristics, while preserving their suitability for contact with the product to be packaged.

In una forma preferita di realizzazione dell’invenzione, il secondo strato 204 è in fibra di acido polilattico (PLA-F), che conferisce particolare resistenza meccanica al ritrovato. In una forma preferita di realizzazione dell’invenzione, il primo strato 201 può essere in carta di cellulosa pura, per alimenti e/o riciclata. L’Esperto del ramo apprezzerà che, comprendendo detto materiale cartaceo prodotti di origine vegetale, esso è in linea con gli scopi di biodegradabilità e compostabilità della presente invenzione. In a preferred embodiment of the invention, the second layer 204 is in polylactic acid fiber (PLA-F), which gives particular mechanical strength to the invention. In a preferred embodiment of the invention, the first layer 201 can be in pure cellulose paper, for food and / or recycled. The skilled in the art will appreciate that, by including said paper material products of plant origin, it is in line with the purposes of biodegradability and compostability of the present invention.

Opzionalmente, in dipendenza della natura del prodotto da confezionare, il primo strato 111 può essere coperto da lacca impermeabile all’acqua 111’, o può essere usata carta impermeabilizzata. In una forma di realizzazione, il primo strato può essere coperto di lacca impermeabile all’acqua in ragione di circa 2 g/m<2>, eventualmente preceduto da un’applicazione di primer. Optionally, depending on the nature of the product to be packaged, the first layer 111 can be covered with 111 'water-proof lacquer, or waterproofed paper can be used. In one embodiment, the first layer can be covered with water-proof lacquer at a rate of about 2 g / m <2>, possibly preceded by an application of primer.

Esempi di lacche impermeabili possono comprendere materiali polimerici selezionati da un gruppo comprendente PVDC (polivinilidene cloruro), EVOH (copolimero etilene-alcol vinilico), PVOH (copolimero propilene-alcol vinilico), o loro miscele. Examples of impermeable lacquers may include polymeric materials selected from a group including PVDC (polyvinylidene chloride), EVOH (ethylene-vinyl alcohol copolymer), PVOH (propylene-vinyl alcohol copolymer), or mixtures thereof.

L’adesivo applicato è preferibilmente a base di materiale atossico, compostabile, come un prodotto selezionato da un gruppo comprendente biopolimeri, come per esempio amidi vegetali, polisaccaridi, e polimeri sintetici compostabili, come per esempio poliisocianati e poliuretani. Secondo una forma preferita di realizzazione dell’invenzione, l’adesivo applicato è un poliisocianato alifatico, addizionato di un opportuno catalizzatore di reticolazione. In accordo con gli scopi della presente invenzione, l’adesivo viene applicato secondo metodologie ben note all’Esperto della tecnica, che non costituiscono una limitazione della presente invenzione, previa dispersione in acqua. The adhesive applied is preferably based on non-toxic, compostable material, such as a product selected from a group comprising biopolymers, such as vegetable starches, polysaccharides, and compostable synthetic polymers, such as polyisocyanates and polyurethanes. According to a preferred embodiment of the invention, the adhesive applied is an aliphatic polyisocyanate, added with a suitable crosslinking catalyst. In accordance with the purposes of the present invention, the adhesive is applied according to methods well known to those skilled in the art, which do not constitute a limitation of the present invention, after dispersion in water.

L’inchiostro applicato ha una grammatura preferibilmente compresa tra circa l’1% e il 5% del peso totale della grammatura dell’invenzione. Le tipologie e modalità di applicazione dell’inchiostro per fini di etichettura e/o decorativi sono ben note a tutti coloro che sono esperti nella tecnica, e non costituiscono una limitazione della presente invenzione. The ink applied has a weight preferably between about 1% and 5% of the total weight of the invention. The types and methods of ink application for labeling and / or decorative purposes are well known to all those skilled in the art, and do not constitute a limitation of the present invention.

Con riferimento alla Figura 5, è illustrata una forma di realizzazione dell’invenzione, comprendente, dall’alto verso il basso: With reference to Figure 5, an embodiment of the invention is illustrated, comprising, from top to bottom:

- un primo strato 301 realizzato in un primo materiale, da rivolgere verso l’esterno; - una applicazione di inchiostro 302; - a first layer 301 made of a first material, to be turned outwards; - an application of ink 302;

- una applicazione di adesivo 303; - an application of adhesive 303;

- uno strato intermedio 304, in materiale polimerico; - an intermediate layer 304, in polymeric material;

- una applicazione di adesivo 305; - an application of adhesive 305;

- un terzo strato 306, in materiale polimerico, a contatto con il prodotto da confezionare. - a third layer 306, made of polymeric material, in contact with the product to be packaged.

La peculiarità del ritrovato risiede nel fatto che il materiale polimerico dello strato intermedio 304 comprende una fibra polimerica biodegradabile e compostabile, selezionato da un gruppo comprendente acido polilattico (PLA), acido poliglicolico (PGA), poliidrossialcanoato (PHA), o loro miscele, che possono essere lavorati, ad esempio filati, come polimeri di origine petrolchimica. Detto strato intermedio può comprendere anche additivi preposti a modificare colorazione e caratteristiche tecniche, preservandone comunque la compostabilità. In una forma preferita di realizzazione dell’invenzione, detto strato intermedio è in fibra di acido polilattico (PLA-F), che conferisce particolare resistenza meccanica al trovato. The peculiarity of the invention lies in the fact that the polymeric material of the intermediate layer 304 comprises a biodegradable and compostable polymeric fiber, selected from a group comprising polylactic acid (PLA), polyglycolic acid (PGA), polyhydroxyalkanoate (PHA), or their mixtures, which they can be processed, for example yarns, as polymers of petrochemical origin. Said intermediate layer can also include additives designed to modify color and technical characteristics, while preserving their compostability. In a preferred embodiment of the invention, said intermediate layer is made of polylactic acid fiber (PLA-F), which gives particular mechanical strength to the invention.

Costituisce inoltre ulteriore peculiarità del ritrovato il fatto che il terzo strato 306 comprende un materiale biodegradabile e compostabile, adatto al contatto con il prodotto da confezionare, selezionato da un gruppo comprendente acido polilattico (PLA), acido poliglicolico (PGA), poliidrossialcanoato (PHA), amido, un poliestere compostabile, o loro miscele, che possono essere lavorati, ad esempio estrusi e/o laminati, come polimeri di origine petrolchimica. In una forma preferita di realizzazione dell’invenzione, il terzo strato 306 è acido polilattico (PLA). A further peculiarity of the invention is also the fact that the third layer 306 comprises a biodegradable and compostable material, suitable for contact with the product to be packaged, selected from a group comprising polylactic acid (PLA), polyglycolic acid (PGA), polyhydroxyalkanoate (PHA) , starch, a compostable polyester, or mixtures thereof, which can be processed, for example extruded and / or laminated, as polymers of petrochemical origin. In a preferred embodiment of the invention, the third layer 306 is polylactic acid (PLA).

Il terzo strato 306 può inoltre comprendere anche additivi preposti a modificare colorazione e caratteristiche tecniche, preservandone comunque l’idoneità al contatto con il prodotto da confezionare. The third layer 306 may also include additives designed to modify color and technical characteristics, while still preserving its suitability for contact with the product to be packaged.

In una forma preferita di realizzazione dell’invenzione, il primo strato 301 può essere in carta di cellulosa pura, per alimenti e/o riciclata. L’Esperto del ramo apprezzerà che, comprendendo detto materiale cartaceo prodotti di origine vegetale, esso è in linea con gli scopi della presente invenzione. In a preferred embodiment of the invention, the first layer 301 can be in pure cellulose paper, for food and / or recycled. The skilled in the art will appreciate that, by including said paper material products of plant origin, it is in line with the purposes of the present invention.

Opzionalmente, in dipendenza della natura del prodotto da confezionare, il primo strato 301 può essere coperto da lacca impermeabile all’acqua 301’, o può essere usata carta impermeabilizzata. In una forma di realizzazione, il primo strato può essere coperto di lacca impermeabile all’acqua in ragione di circa 2 g/m<2>, eventualmente preceduto da un’applicazione di primer. Optionally, depending on the nature of the product to be packaged, the first layer 301 can be covered with waterproof lacquer 301 ', or waterproofed paper can be used. In one embodiment, the first layer can be covered with water-proof lacquer at a rate of about 2 g / m <2>, possibly preceded by an application of primer.

Esempi di lacche impermeabili possono comprendere materiali polimerici selezionati da un gruppo comprendente PVDC (polivinilidene cloruro), EVOH (copolimero etilene-alcol vinilico), PVOH (copolimero propilene-alcol vinilico), o loro miscele. Examples of impermeable lacquers may include polymeric materials selected from a group including PVDC (polyvinylidene chloride), EVOH (ethylene-vinyl alcohol copolymer), PVOH (propylene-vinyl alcohol copolymer), or mixtures thereof.

L’adesivo applicato è preferibilmente a base di materiale atossico, compostabile, come un prodotto selezionato da un gruppo comprendente biopolimeri, come per esempio amidi vegetali, polisaccaridi, e polimeri sintetici compostabili, come per esempio poliisocianati e poliuretani. Secondo una forma preferita di realizzazione dell’invenzione, l’adesivo applicato è un poliisocianato alifatico, addizionato di un opportuno catalizzatore di reticolazione. In accordo con gli scopi della presente invenzione, l’adesivo viene applicato secondo metodologie ben note all’Esperto della tecnica, che non costituiscono una limitazione della presente invenzione, previa dispersione in acqua. The adhesive applied is preferably based on non-toxic, compostable material, such as a product selected from a group comprising biopolymers, such as vegetable starches, polysaccharides, and compostable synthetic polymers, such as polyisocyanates and polyurethanes. According to a preferred embodiment of the invention, the adhesive applied is an aliphatic polyisocyanate, added with a suitable crosslinking catalyst. In accordance with the purposes of the present invention, the adhesive is applied according to methods well known to those skilled in the art, which do not constitute a limitation of the present invention, after dispersion in water.

L’inchiostro applicato ha una grammatura preferibilmente compresa tra circa l’1% e il 5% del peso totale della grammatura dell’invenzione. Le tipologie e modalità di applicazione dell’inchiostro per fini di etichettura e/o decorativi sono ben note a tutti coloro che sono esperti nella tecnica, e non costituiscono una limitazione della presente invenzione. L’Esperto del ramo apprezzerà che nelle forme di realizzazione sopra descritte lo strato di materiale polimerico 104, 114, 124, 204 e 306 ha anche funzione sigillante, ancor più preferibilmente se in forma amorfa, come per esempio acido polilattico (PLA) amorfo. The ink applied has a weight preferably between about 1% and 5% of the total weight of the invention. The types and methods of ink application for labeling and / or decorative purposes are well known to all those skilled in the art, and do not constitute a limitation of the present invention. The skilled in the art will appreciate that in the embodiments described above the layer of polymeric material 104, 114, 124, 204 and 306 also has a sealing function, even more preferably if in amorphous form, such as for example amorphous polylactic acid (PLA).

In aggiunta, l’Esperto del ramo apprezzerà che le caratteristiche costitutive delle forme di realizzazione della presente invenzione le rendono una barriera al contatto del prodotto da confezionare con oli minerali idrocarburici del tipo MOAH e MOSH. Inoltre, vantaggiosamente, dato che la carta non presenta punti di rammollimento si garantisce all’utilizzatore finale del film multistrato della presente invenzione, in fase di confezionamento, un’ottima processabilità, paragonabile a quella di soluzioni della tecnica nota non compostabili. In addition, the skilled in the art will appreciate that the constitutive characteristics of the embodiments of the present invention make them a barrier to the contact of the product to be packaged with hydrocarbon mineral oils of the MOAH and MOSH type. Furthermore, advantageously, since the paper has no softening points, the end user of the multilayer film of the present invention is guaranteed, during the packaging phase, an excellent processability, comparable to that of non-compostable prior art solutions.

Le forme di realizzazione della presente invenzione sono suscettibili di numerose modifiche e varianti, tutte in accordo con il concetto inventivo della presente invenzione, per garantire le caratteristiche del materiale composito qui descritto. Preferibilmente, materiali impiegati e dimensioni possono variare a seconda delle esigenze e degli scopi desiderati. Applicabilità industriale The embodiments of the present invention are susceptible of numerous modifications and variations, all in accordance with the inventive concept of the present invention, to ensure the characteristics of the composite material described here. Preferably, the materials used and the dimensions can vary according to the needs and the desired purposes. Industrial applicability

Con la presente invenzione si è messo a punto un film multistrato per il confezionamento di prodotti farmaceutici e di alimenti, compostabile e la cui decomposizione avviene in tempi vantaggiosamente inferiori ai film della tecnica precedente, nel rispetto della normativa EN13432 sugli imballaggi. Vantaggiosamente, la presente invenzione può essere infine realizzata, a partire da materie prime commercialmente disponibili e a costi ragionevoli, attraverso metodi e tecnologie consolidate ben note all’Esperto del ramo. With the present invention a multilayer film for the packaging of pharmaceutical and food products has been developed, compostable and whose decomposition takes place in advantageously shorter times than the films of the previous art, in compliance with the EN13432 regulation on packaging. Advantageously, the present invention can finally be realized, starting from commercially available raw materials and at reasonable costs, through established methods and technologies well known to those skilled in the art.

Claims (10)

RIVENDICAZIONI 1. Film multistrato compostabile adatto al confezionamento di prodotti farmaceutici e prodotti alimentari, più specialmente per prodotti alimentari, comprendente: - almeno un primo strato (101, 111, 122, 201, 301) realizzato in un primo materiale; - almeno un’applicazione intermedia (102, 113, 123, 202, 303) di adesivo; - almeno un’applicazione intermedia (103, 112, 121, 203, 302) di inchiostro; - almeno un altro strato (104, 114, 124, 204, 306) in materiale polimerico, a contatto con il prodotto da confezionare. CLAIMS 1. Compostable multilayer film suitable for the packaging of pharmaceutical products and food products, more especially for food products, comprising: - at least a first layer (101, 111, 122, 201, 301) made of a first material; - at least one intermediate application (102, 113, 123, 202, 303) of adhesive; - at least one intermediate application (103, 112, 121, 203, 302) of ink; - at least one other layer (104, 114, 124, 204, 306) of polymeric material, in contact with the product to be packaged. 2. Film multistrato secondo la rivendicazione 1, in cui detto altro strato (104, 114, 124, 204, 306) è selezionato da un gruppo comprendente acido polilattico (PLA), acido poliglicolico (PGA), poliidrossialcanoato (PHA), amido, un poliestere compostabile, o loro miscele. Multilayer film according to claim 1, wherein said other layer (104, 114, 124, 204, 306) is selected from a group comprising polylactic acid (PLA), polyglycolic acid (PGA), polyhydroxyalkanoate (PHA), starch, a compostable polyester, or mixtures thereof. 3. Film multistrato secondo le rivendicazioni 1 e 2, in cui detto altro strato (104, 114, 124, 204, 306) è preferibilmente costituito di acido polilattico (PLA), ancora più preferibilmente in forma amorfa. 3. Multilayer film according to claims 1 and 2, wherein said other layer (104, 114, 124, 204, 306) is preferably made of polylactic acid (PLA), even more preferably in amorphous form. 4. Film multistrato secondo la rivendicazione 1, caratterizzato dal fatto che l’adesivo applicato è selezionato da un gruppo comprendente biopolimeri, come per esempio amidi vegetali, polisaccaridi, e polimeri sintetici biodegradabili, come per esempio poliisocianati, poliuretani, addizionati di un opportuno catalizzatore di reticolazione. 4. Multilayer film according to claim 1, characterized in that the adhesive applied is selected from a group comprising biopolymers, such as for example vegetable starches, polysaccharides, and biodegradable synthetic polymers, such as for example polyisocyanates, polyurethanes, added with a suitable catalyst of crosslinking. 5. Film multistrato secondo la rivendicazione 4, in cui l’adesivo applicato è preferibilmente un poliisocianato, più preferibilmente un poliisocianato alifatico. 5. Multilayer film according to claim 4, in which the adhesive applied is preferably a polyisocyanate, more preferably an aliphatic polyisocyanate. 6. Film multistrato secondo la rivendicazione 1, in cui il primo strato (101, 111, 121, 201, 301) comprende carta di cellulosa pura, per alimenti e/o riciclata. 6. Multilayer film according to claim 1, wherein the first layer (101, 111, 121, 201, 301) comprises pure cellulose, food grade and / or recycled paper. 7. Film bi-strato secondo una qualsiasi delle rivendicazioni precedenti, comprendente: - un primo strato 101; - un’applicazione intermedia 102 di adesivo; - un’applicazione intermedia 103 di inchiostro; - un secondo strato 104 in materiale polimerico, a contatto con il prodotto da confezionare. 7. Double layer film according to any one of the preceding claims, comprising: - a first layer 101; - an intermediate application 102 of adhesive; - an intermediate application 103 of ink; - a second layer 104 of polymeric material, in contact with the product to be packaged. 8. Film bi-strato secondo la rivendicazione 7, in cui il primo strato 101 è preferibilmente carta trasparente, come per esempio pergamina o carta glassine. 8. Double layer film according to claim 7, wherein the first layer 101 is preferably transparent paper, such as for example glassine or glassine paper. 9. Film bi-strato secondo la rivendicazione 7, in cui il secondo strato 104 è acido polilattico (PLA). 9. Double layer film according to claim 7, wherein the second layer 104 is polylactic acid (PLA). 10. Film bi-strato secondo la rivendicazione 7, in cui il primo strato 101 è ricoperto da un’applicazione di lacca impermeabilizzante 101’, detta lacca impermeabilizzante preceduta da un’applicazione di primer. 10. Double-layer film according to claim 7, in which the first layer 101 is covered with an application of waterproofing lacquer 101 ', called waterproofing lacquer preceded by an application of primer.
IT102019000013800A 2019-08-02 2019-08-02 Compostable film especially for food packaging IT201900013800A1 (en)