IN2012DN03019A - - Google Patents

Download PDF

Info

Publication number
IN2012DN03019A
IN2012DN03019A IN3019DEN2012A IN2012DN03019A IN 2012DN03019 A IN2012DN03019 A IN 2012DN03019A IN 3019DEN2012 A IN3019DEN2012 A IN 3019DEN2012A IN 2012DN03019 A IN2012DN03019 A IN 2012DN03019A
Authority
IN
India
Prior art keywords
steel tube
steel
vtrs100
airbag
mpa
Prior art date
Application number
Inventor
Yuji Arai
Takashi Takano
Takuma Kawamoto
Original Assignee
Sumitomo Metal Ind
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sumitomo Metal Ind filed Critical Sumitomo Metal Ind
Publication of IN2012DN03019A publication Critical patent/IN2012DN03019A/en

Abstract

A steel tube for an airbag which has a low alloy cost and a strength of at least 1000 Mpa and vTrs100 of-80° C or below and a process for its manufacture which can minimize the number of times that softening annealing treatment is performed in a cold drawing step are provided. Stable properties are obtained even when quench hardening is carried out by high frequency induction heating on a large scale. The steel tube has a steel composition which comprises, in mass percent, C: 0.05 - 0.20%, Si: 0.10 - 0.50%, Mn: 0.10 - 1.00%, P: at most 0.025%, S: at most 0.005%, Al: 0.005 - 0.10%, Ca: 0.0005 - 0.0050%, Nb: 0.005 - 0.050%, Ti: 0.005 - 0.050%, Cu: 0.01 - 0.50%, Ni: 0.01 - 0.50%, Cr: 0.01 - 0.50%, B: 0.0005 - 0.0050%, N: 0.002 - 0.010%, and a remainder of Fe and unavoidable impurities.
IN3019DEN2012 2010-06-03 2010-06-03 IN2012DN03019A (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/JP2010/059417 WO2011151908A1 (en) 2010-06-03 2010-06-03 Steel pipe for air bag and process for producing same

Publications (1)

Publication Number Publication Date
IN2012DN03019A true IN2012DN03019A (en) 2015-07-31

Family

ID=45066304

Family Applications (1)

Application Number Title Priority Date Filing Date
IN3019DEN2012 IN2012DN03019A (en) 2010-06-03 2010-06-03

Country Status (10)

Country Link
US (1) US9080223B2 (en)
EP (1) EP2484793B1 (en)
KR (1) KR101425738B1 (en)
CN (1) CN102741438B (en)
CA (1) CA2776984C (en)
ES (1) ES2726767T3 (en)
IN (1) IN2012DN03019A (en)
MX (1) MX2012005710A (en)
PL (1) PL2484793T3 (en)
WO (1) WO2011151908A1 (en)

Families Citing this family (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20140091063A1 (en) * 2012-09-28 2014-04-03 Electro-Motive Diesel, Inc. System for hardening a cylindrical metal component
CN103147017A (en) * 2013-03-21 2013-06-12 宝山钢铁股份有限公司 Steel plate with high strength and excellent low-temperature toughness and manufacturing method thereof
CN104073731B (en) * 2013-03-27 2017-02-22 鞍钢股份有限公司 Method for producing ultrahigh-strength ship plate by adopting direct quenching process
JP6070617B2 (en) * 2014-04-03 2017-02-01 Ｊｆｅスチール株式会社 Seamless steel pipe for fuel injection pipes with excellent internal pressure fatigue resistance
JP6398575B2 (en) * 2014-10-10 2018-10-03 新日鐵住金株式会社 Steel sheet with excellent toughness and method for producing the same
CN108141926A (en) * 2015-09-25 2018-06-08 康讯公司 It is preheated for the large-scale blank electric induction of heat processing technique
CN109563587B (en) * 2016-08-01 2021-03-12 新日铁住金株式会社 Seamless steel pipe and method for producing same
CN107052717A (en) * 2017-04-01 2017-08-18 浙江金固股份有限公司 Spoke manufacture method
DE102018132816A1 (en) * 2018-12-19 2020-06-25 Voestalpine Stahl Gmbh Process for the production of thermo-mechanically produced profiled hot-rolled products
CN112593068A (en) * 2020-12-03 2021-04-02 成都先进金属材料产业技术研究院有限公司 Continuous isothermal annealing method of seamless steel pipe
DE102020133765A1 (en) 2020-12-16 2022-06-23 Benteler Steel/Tube Gmbh High strength steel pipe and method of making high strength steel pipe
AR128805A1 (en) * 2022-03-31 2024-06-12 Nippon Steel Corp SEAMLESS STEEL TUBE
CN115418566B (en) * 2022-08-30 2023-09-08 日照钢铁控股集团有限公司 Manufacturing method of low-cost high-P weather-resistant steel
WO2024185477A1 (en) * 2023-03-09 2024-09-12 日本製鉄株式会社 Seamless steel pipe and inflator bottle for airbags

Family Cites Families (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH10212549A (en) * 1997-01-28 1998-08-11 Sumitomo Metal Ind Ltd High toughness electric resistance welded tube for air bag and its production
JP3678147B2 (en) * 2000-12-27 2005-08-03 住友金属工業株式会社 Steel tube for high strength and toughness airbag and its manufacturing method
EP1375683B1 (en) * 2001-03-29 2012-02-08 Sumitomo Metal Industries, Ltd. High strength steel tube for air bag and method for production thereof
JP2004076034A (en) 2002-08-12 2004-03-11 Jfe Steel Kk Method for producing high strength, high toughness and high workability seamless steel pipe for air bag
US20050000601A1 (en) * 2003-05-21 2005-01-06 Yuji Arai Steel pipe for an airbag system and a method for its manufacture
US20050076975A1 (en) * 2003-10-10 2005-04-14 Tenaris Connections A.G. Low carbon alloy steel tube having ultra high strength and excellent toughness at low temperature and method of manufacturing the same
US20060169368A1 (en) * 2004-10-05 2006-08-03 Tenaris Conncections A.G. (A Liechtenstein Corporation) Low carbon alloy steel tube having ultra high strength and excellent toughness at low temperature and method of manufacturing the same
MX2007005029A (en) * 2004-10-29 2007-06-19 Sumitomo Metal Ind Steel pipe for air bag inflator and method for production thereof.
MXPA05008339A (en) * 2005-08-04 2007-02-05 Tenaris Connections Ag High-strength steel for seamless, weldable steel pipes.
CN101374966B (en) * 2006-02-09 2011-01-19 住友金属工业株式会社 Process for manufacturing an airbag inflator bottle member
EP2078764B1 (en) * 2006-10-27 2012-09-19 Sumitomo Metal Industries Limited Seamless steel tube for airbag accumulators and process for production thereof
JP4770922B2 (en) * 2008-12-08 2011-09-14 住友金属工業株式会社 Steel pipe for airbag and manufacturing method thereof

Also Published As

Publication number Publication date
EP2484793B1 (en) 2019-03-13
US20120205016A1 (en) 2012-08-16
CA2776984A1 (en) 2011-12-08
EP2484793A1 (en) 2012-08-08
EP2484793A4 (en) 2016-01-13
US9080223B2 (en) 2015-07-14
ES2726767T3 (en) 2019-10-09
WO2011151908A1 (en) 2011-12-08
PL2484793T3 (en) 2019-09-30
MX2012005710A (en) 2012-06-12
KR20120056890A (en) 2012-06-04
CA2776984C (en) 2015-11-17
CN102741438B (en) 2014-11-05
KR101425738B1 (en) 2014-07-31
CN102741438A (en) 2012-10-17

Similar Documents

Publication Publication Date Title
IN2012DN03019A (en)
MX371103B (en) Method for producing high-strength steel material having excellent sulfide stress cracking resistance.
UA99127C2 (en) Steel part, chilled by aging thereof in EQUIPMENT, welded PRODUCT with the USe of THIS PART, producing this part with preliminary COATING AND WITHOUT IT, and using the specified steel part
RU2014101779A (en) METHOD FOR PRODUCING HIGH STRENGTH STRUCTURAL STEEL AND PRODUCT FROM HIGH STRENGTH STRUCTURAL STEEL
MX2012007359A (en) Steel, flat steel product, steel component and method for producing a steel component.
MX2011009051A (en) Low alloy steel with a high yield strength and high sulphide stress cracking resistance.
MX2013011154A (en) Abrasion-resistant steel sheet exhibiting excellent resistance to stress corrosion cracking, and method for producing same.
MX2016017400A (en) Method for manufacturing a high strength steel sheet and sheet obtained.
MX336778B (en) Case hardened steel and method for producing same.
MX2013011155A (en) Abrasion-resistant steel sheet exhibiting excellent resistance to stress corrosion cracking, and method for producing same.
RU2016151415A (en) METHOD FOR PRODUCING HIGH-STRENGTH STEEL SHEET POSSESSING IMPROVED STRENGTH, PLASTICITY AND FORMABILITY
RU2015101733A (en) SEAMLESS PIPE FROM HIGH-STRENGTH STAINLESS STEEL WITH HIGH CORROSION RESISTANCE FOR OIL WELL AND METHOD FOR PRODUCING IT
MX2009004425A (en) Seamless steel tube for airbag accumulators and process for production thereof.
UA100056C2 (en) Method for production of cold-rolled and annealed sheet of dual phase steel, sheet produced thereby, method for production of cold-rolled, annealed and galvanized sheet of dual phase (variants) and use of said steel sheet
FI3663416T3 (en) Method for producing a high strength steel sheet having improved strength and formability and obtained sheet
JP2016509130A5 (en)
NZ708752A (en) High-toughness low-alloy wear-resistant steel sheet and method of manufacturing the same
UA101743C2 (en) method for producing seamless pipes (Variants)
MX2016001013A (en) Steel sheet having very high mechanical properties of strength and ductility, manufacturing method and use of such sheets.
MX2016007570A (en) Martensitic steel with delayed fracture resistance and manufacturing method.
RU2012117899A (en) THICK-STEEL STEEL CHARACTERIZING A LOW RATIO BETWEEN THE YIELD TURN AND THE STRENGTH TARGET, HIGH STRENGTH AND HIGH UNIFORM RELATIVE elongation, AND METHOD FOR ITS
UA113628C2 (en) A METHOD OF MAKING A SHEET OR DETAILS OF EMERGENCY MARTENSITE STEEL AND SHEET OR DETAILS OBTAINED IN SUCH A METHOD
RU2016137919A (en) STEEL PIPE FOR HIGH PRESSURE FUEL PIPE AND HIGH PRESSURE USING HER FUEL PIPE
CA2687436A1 (en) Bent pipe and a method for its manufacture
WO2011124851A3 (en) Mechanical part made of steel having high properties and process for manufacturing same