IE920998A1 - Polyamide/polyolefin blend release film for the production of a sheet moulding compound and the sheet moulding compound produced with such film - Google Patents
Polyamide/polyolefin blend release film for the production of a sheet moulding compound and the sheet moulding compound produced with such filmInfo
- Publication number
- IE920998A1 IE920998A1 IE099892A IE920998A IE920998A1 IE 920998 A1 IE920998 A1 IE 920998A1 IE 099892 A IE099892 A IE 099892A IE 920998 A IE920998 A IE 920998A IE 920998 A1 IE920998 A1 IE 920998A1
- Authority
- IE
- Ireland
- Prior art keywords
- polyamide
- film according
- film
- alpha
- grafted
- Prior art date
Abstract
Polymer film made from a polyamide/polyolefin alloy for the manufacture of a sheet compounding product, characterised in that it comprises the components A, B, C and D according to the following percentages by weight: 30 </= A + B + C </= 60 0 </= A </= 60 and B + C >/= 1 where 0 </= B </= 60 and A + B + C + D = 100 where 0 </= C </= 60; the said components A, B, C and D having the following compositions: A consists of at least one polyolefin composed of a partially or completely linear alpha-olefin; B represents the alpha-olefin described in A on which one or two functionalised monomers have been grafted; C is a grafted copolymer consisting of at least one monoaminated polyamide oligomer and of an alpha-monoolefin polymer or copolymer grafted by a monomer capable of reacting with the amine function of the said monoaminated oligomer; D consists of at least one aliphatic (co)polyamide. t
Description
POLYAMIDE-POLYOLEFIN RELEASE FILM AND ITS USE IN PRODUCING A SHEET MOLDING COMPOUND BACKGROUND OF THE INVENTION Field of the invention The present invention relates to a polyamide/polyolefin alloy film useful in the preparation of molding compound products, more specifically a sheet molding compound (SMC).
Such a sheet molding compound is employed for manufacturing fabricated parts in areas such as the automobile industry (fenders or bumpers, rear doors, etc), in boatbuilding (hulls of boats) as well as in the electronics industry (housings).
The SMC compound generally consists of a cross-linkable polymer resin, in particular an unsaturated polyester, togeth15 er with reinforcing fillers such as glass fibers, along with various other additives present in smaller amounts.
The SMC compound is normally prepared by laying the fibers on a layer of unsaturated polyester resin, which itself is supported by a removable film generally composed of polyethylene or polyamide.
Following this, a further film of the same nature is layed on top of the resin/filler system in order to form a composite laminate or sandwich structure between the two films. The laminate structure is then passed through a series of kneading and compacting rollers and is generally rolled into large diameter rolls.
After this, it is stored prior to its use in final manufacturing. During the storage period, partially crosslinking of the polyester resin takes place leading to an increase of the SMC compound's viscosity until it reaches a consistency suitable for molding.
Users of the SMC compound who generally are molders, cut off a piece of suitable size from the roll, peel off the support film and insert the SMC compound into a heated mold in order for it to undergo simultaneous transformation and complete hardening. Thus, composite masses in SMC laminate lend themselves readily to use in compression molding operations.
Three properties of the resulting laminate structure film are of capital importance to manufacturers and users of the SMC laminate.
The first of these relates to the styrene permeability of the peelable film. It is essential for the peelable film to have very low styrene permeability in order to avoid loss of styrene monomer, this latter performing the function of cross-linking agent in the SMC laminate. Such loss of styrene monomer is also harmful to the health of operatives during manufacture of the SMC and storage thereof.
The second property concerns the ease of peeling of this film once on the polyester structure, in order to avoid resid5 ual film staying stuck to the structure and to avoid the danger of tearing the film during the SMC manufacturing and transformation operations.
Finally, such peelable films need to have very low humidity take-up and water permeability in order for the quality of the polyester resin, which is highly sensitive to water, not to be changed during the SMC laminate manufacturing operations, during storage of the polyester or during transformation of the SMC.
As has been said above, polyethylene is employed for the peelable film in SMC laminates. Although the characteristics of polyethylene are suitable for the performance of automatic peeling operations, and it exhibits satisfactory inertness towards water for this application, it does however suffer from high permeability to styrene, thus generally requiring such rolls to be wrapped in aluminum foil.
Prior art European Patent 27 191 in the name of Allied Chemical Corporation, describes a polyamide release film for use in the manufacture of SMC compounds where the film has low crystall25 inity and consists of a mixture of 70 to 90% by weight of a polyamide (ΡΔ-6 and/or PA-6/6) having a crystallinity less than 35%, and of 10 to 30% of a polyolefin compound or a copolymer thereof, the polyolefin paving a crystallinity of less than 50%. The polyolefin is a high molecular weight alpha-olefin or a copolymer thereof consisting of an alphaolefin and a vinyl acetate monomer or alkyl acrylate monomer.
The film, which has a thickness comprised between 12.7 and 127 urn, has a Graves tear strength of at least 400 g in the longitudinal direction, as determined by ASTM D-1004-66 and a -9 2 styrene permeability less than 200 x 10 g-cm/cm -h.
Commercially available PA films, although they have good characteristics as regards styrene permeability, only have sufficient peelability properties provided that the film is stripped off manually, these properties becoming insufficient when automatic film stripping processes currently under development are applied.
Moreover, with the progressive replacement of PE films by PA films, there is the additional problem of the high sensitivity of polyamides to humidity. Water effectively leads to deterioration of the polyester or epoxy resin, leading to major defects in the parts produced in SMC. In order to overcome this, suppliers of such films have to protect the rolls by applying aluminum films before supply to SMC manufactures and in SMC storage areas prior to final transforma25 tion, thus leading to a not-insignificant increase in costs.
SUMMARY OF THE INVENTION The present invention provides a compatible polyamide/polyolefin film of thickness generally comprised between 10 and 130 μιη, and preferably between 20 and 50 gm, comprising products A, B, C, D, where: A consists of at least one polyolefin comprising a totally or partially linear alpha-olefin the molecular weight of which is comprised between 1000 and 1 000 000; B represents the alpha-olefin specified under A on which 10 one or two functionalized monomers have been grafted, the grafting rate of the functionalized monomer(s) being comprised between 500 ppm and 6% by weight; C is a grafted polymer consisting of at least one polyamide mono-amino oligomer and a polymer or copolymer of alpha mono-olefin grafted with a monomer able to react with the amine function of said mono-amino oligomer; D is constituted by at least one aliphatic (co,polyamide consisting: (i) of a polyamide obtained from aliphatic dicarboxylic acid and an aliphatic diamine, each of which has between 6 and 24 carbon atoms, and/or (ii) a polyamide obtained from an amino-aliphatic acid or lactame having 6 to 24 carbon atoms.
Components A, B, C and D are described in detail below: A consists of at least one polyolefin consisting of a totally or partially linear alpha-olefin of high molecular weight, for example polyethylene, polypropylene or polyisobutylene, copolymers of alpha-olefins with vinyl acetate monomers, such as ethylene/vinyl acetate copolymers, or alkyl acrylate copolymers, such as ethylene/methyl acrylate copolymers or ethylene/ethyl acrylate copolymers or copolymers of ethylene and an alpha-olefin having 3 to 10 carbon atoms. The molecular weight of component A is generally comprised between 1000 and 1 000 000 and preferably between 10 000 and 500 000, which corresponds to a melt index MI comprised between 0.1 and 300 g/min measured at 230°C under 2.16 kg.
B represents the alpha-olefin described under A on which a functionalized monomer has been grafted, said functionalized monomer being selected from the group comprising: acrylic, methacrylic, maleic, fumaric, itaconic, crotonic, 3-dicarboxylic-5-norbornene-2 acids, maleic, dimethylmaleic anhydrides, mono-sodium, di-sodium maleates, acrylamide, itaconic anhydrides, citraconic anhydrides, maleimide, N-phenylmaleimide, diethyl fumarate, vinyl pyridine, the vinyl silanes, 4-vinyl-pyridine, vinyl-thiethoxysilane, allylic alco25 hoi, and in particular maleic acid, maleic anhydride or fumaric acid. Two monomers for grafting can be used simultaneously and can be selected from styrene, 2-methyl-styrene , 4-methyl-styrene, alphamethyl-styrene, beta-methyl-styrene, vinyl-4-anisole, stilbene and indene or mixtures thereof. The other monomer can be selected from the group comprising: maleic, itaconic, citraconic anhydrides, maleimide, and N-phenylmaleimide or mixtures thereof. Generally, the grafting rate of the functionalized monomer or monomers is comprised between 500 ppm and 6% by weight, and is preferably less than 2%.
C is a grafted polymer consisting of at least one polyamide mono-amino oligomer and a polymer or copolymer of alpha mono-olefin grafted with a monomer able to react with the amine function of the mono-amino oligomer described in European Patent 342, 066.
D is at least one aliphatic (co)polyamide consisting: (i) of a polyamide obtained from aliphatic dicarboxylic acid and an aliphatic diamine, each of which has between 6 and 24 carbon atoms, and/or (ii) a polyamide obtained from an amino-aliphatic acid or lactame having 6 to 24 carbon atoms, in particular a 6- or 6/6-polyamide or a mixture of the two.
The percentages by weight of the various components are selected such that: < A + B + C < 60 0 < A < 60 and B + C > 1 where 0 < B < 60 and A + B + C + D = 100 where 0 < C < 60; and the viscosities of the various components are such that 5 the polyamide phase constitutes a continuous phase, and can be characterized by the fact that a film about 20 microns thick keeps its shape when plunged into xylene at 130°C for 30 minutes .
Preferred compositions of the films according to the invention are those in which: < A+B+C <45 and B + C > 5 ILLUSTRATIVE EXAMPLES The following examples illustrate the invention without however limiting it.
Example 1 (sheath or tubular film) A mixture comprising, by weight, 33 parts of polypropylene, 57 parts of polyamide-6 and 10 parts of a sequenced copolymer of propylene and 12% by weight of ethylene, of melting point 158°C (copolymer main body), with a maleic grafting rate of 1.16%, grafted with a Mn 2700 monoamine PA-6 oligomer, prepared by the method described in European Patent 342 066, was continuously introduced into a Werner-type extruder. The material temperature was comprised between 255°C and 270°C along the extruder barrel. The screw rotation was 150 rpm and the material throughput 20 kg/h. The *1 granules obtained at the outlet from the extruder were transformed using an extrusion-blowing technique for tubular articles in a Kaufman extruder with a three-groove rotating helical die of diameter 150 mm and a gap of 0.8 mm, in order to produce a 25 |im tubular film. The operating conditions were as follows: cylinder temperature die temperature stretching speed 225-250°C 250-260°C m/min The PA employed was a polyamide-6 of melt index (MI) measured at 235°C under a load of 2.16 kg equal to 20 g/10 min and the polypropylene was a statistical copolymer of propylene and 3% by weight of ethylene with a melt index of 2 g/10 min (sample 1.A).
In order to determine the film's suitability for peeling, surface tension measurements were carried out on the film and, by way of comparison, on a peelable film consisting of a mixture of, by weight, 89% polyamide-6 and 10% of an ethylene/vinyl acetate copolymer containing 9% of vinyl acetate and 1% of titanium dioxide (sample l.B). The surface tension of the two samples was determined by measuring, using a goniometer, the forward contact angle, at equilibrium, of standard drops of liquid on the substrate in conformity with the method described in Fowkes, F.M., Ind.Eng.Chem.,56 (1964) 40 or in Owens, D.K. and Wendt, R.C., J.Appl. Polymer Sci. 13 (1969) 1741. Typical examples of standard liquids are di-iodomethane, glycerol, and benzylic alcohol.
Test no. 1 .A l.B Surface tension (mN.m 1, 32 46 The low surface tension enabled automatic peeling of the film to be carried out on the SMC composite without causing tearing of the film to start, this necessitating shutting down of the production line when manufacturing SMC products.
Water vapor permeability measurements were also carried out under the following conditions: Apparatus: Lyssy vapor permeation tester IL 80 - 40000 Temperature: 38°C Relative humidity: 90% Resistive humidity detector Measurement principle : The membrane to be tested was placed in a saturated atmosphere and in a space provisionally brought to a dry atmosphere. A resistive humidity detector placed in the dry space recorded continuous relative humidity variations as a function of time. The time measurement needed for humidity to go from one limiting value to another was representative of the sample's permeability.
Temperature measurement was converted into permeability values by comparison with values measured previously using a known permeability standard test.
The results are expressed in g/m /24h and are summarized in the table below: Test no. Water vapor permeability l.A *56 1 .B 380 Humidity take-up measurements were also carried out using a weighing method (measurement of take-up in weight at 100% relative humidity at 23°C starting from a time T ).
The styrene permeability of film l.A was also measured 20 using the method described in American Institute of Chemical Engineers, 53rd National Meeting, Preprint no. 32d, 1964, by Bixler and Michaels. According to this method, the sample had -9 2 a styrene permeability of about 8 x 10 g-cm/cm -h. A styrene -9 2 permeability that is less than 200 x 10 g-cm/cm -h is con25 sidered as good.
Time Take-up weight (in %) l.A " l.B To 0 0 To + 4 h 2 3 To + 8 h 2 3 To + 24 h 2.1 3 To + 96 h 2.1 3.6 To + 120 h 2.1 3.6 Example 2 (flat film) A mixture comprising, by weight, 29.7 parts of polypropylene homopolymer of MI (230°C/2.16 kg) equal to 5.10 parts of maleic-grafted ethylene/propylene copolymer (EPRm) containing 70% by weight of ethylene and 500 ppm of maleic anhydride of melt index 9 g/10 min (230°C/10 kg), 51.3 parts of polyamide-6 of MI 20 g/lOmin (235°C/2.16 kg), 9 parts of the grafted and maleic grafted copolymer main body of example 1 was continuously introduced into a Werner extruder. Along the extruder shaft, the material temperature was comprised between 250°C and 270°C, .the screw rotation speed was 150 rpm and the material throughput was 20 kg/h. The granules obtained at the outlet from the extruder were transformed using a cast extrusion technique employing a Thoret extruder into the form of a flat film or cast film of 25 um thickness (sample 2.A). Operating conditions were as follows: Temperature profile : 22<0-250°C Cylinder temperature : 80°C Screw speed : 28 rpm By way of comparison, a flat film of the same composition and thickness as sample l.B was employed (sample 2.B).
Surface tension measurements as defined for example 1 were carried out and are summarized in the table below: Test no. 2.A 2.B Surface tension 32 46 (mN.m 1) Water vapor permeability measurements as well as humidi ty take-up measurements were carried out and gave the follow- ing results: Test no. Water vapor permeability (in g/m2/24 h) 2.A 50 2.B 380 Time Take-up weight (in %) 2.A , 2.B 5 To 0 0 T = To + 4 h 1.5 3 T = To + 8 h 1.5 3 T = To + 24 h 1.7 3 T = To + 96 h 1.7 3.6 10 T = To + 120 h 1.7 3.6 The present invention also relates to a method of producing a sheet molding compound in which: a) a layer of thermosetting resin suitable for thermal processing is poured, in fluid form, onto a polymer film according to the invention which is advancing continuously, b) a reinforcing material is introduced onto the advancing fluid layer, c) a polymer film according to the invention is placed in contact with the upper surface of the reinforced fluid layer thus forming a composite mass of sandwich-structure, d) the sandwich-structure composite mass is caused to advance through a series of kneading and compacting rollers, and e) the sandwich-structure composite mass is rolled into a roll for partial heat treatment.
The present invention also relates to a sandwich-structure comprising: (i) a central layer of a reinforced unhardened thermosetting sheet molding product, (ii) two outer layers of polymer film according to the invention .
Claims (17)
1.- A polymer film formed of a polyamide/polyolefin alloy for the production of a sheet molding compound, comprising components A, B, C and D in the following 5 percentages by weight: 30 < A + B + C < 60 0 < A < 60 and B + C > 1 where 0 < B < 60 and A + B + C + D = 100 where 0 < C < 60; said components A, B, C and D having the following composi 10 tions: A consists of at least one polyolefin comprising a totally or partially linear alpha-olefin the molecular weight of which is comprised between 1000 and 1 000 000; B represents the alpha-olefin specified under A on which 15 one or two functionalized monomers have been grafted, the grafting rate of the functionalized monomer or monomers being comprised between 500 ppm and 6% by weight; C is a grafted polymer consisting of at least one 20 polyamide mono-amino oligomer and a polymer or copolymer of alpha mono-olefin grafted with a monomer able to react with the amine function of said mono-amino oligomer; D is constituted by at least one aliphatic (co)polyamide 25 consisting: (i) of a polyamide obtained from aliphatic dicarboxylic acid and an aliphatic diamine, each of which has between 6 and 24 carbon atoms, and/or (ii) a polyamide obtained from an amino-aliphatic acid 5 or lactame having 6 to 24 carbon atoms.
2. - A film according to claim 1, wherein the polyolefin of component A is selected from the group comprising: polyethylene, polypropylene or polyisobutylene, copolymers of alpha-olefins with vinyl acetate monomers, notably ethylene/10 vinyl acetate copolymers, alkyl acrylate copolymers, notably ethylene/methyl acrylate copolymers or ethylene/ethyl acrylate copolymers or copolymers of ethylene and an alpha-olefin having 3 to 10 carbon atoms.
3. - A film according to claim 1, wherein the molecular 15 weight of the polyolefin of component A is comprised between 10 000 and 500 000.
4. - A film according to claim 1, wherein the functionalized monomer of component B is selected from the group comprising: acrylic, methacrylic, maleic, fumaric, 20 itaconic, crotonic, 3-dicarboxylic-5-norbornene-2 acids, maleic, dimethylmaleic anhydrides, mono-sodium, di-sodium maleates, acrylamide, itaconic anhydrides, citraconic anhydrides, maleimide, N-phenylmaleimide, diethyl fumarate, vinylpyridine, the vinylsilanes, 4-vinylpyridine, 25 vinylthiethoxysilane, allylic alcohol, or a mixture thereof.
5. - A film according to claim 4, wherein said functionalized monomer is selected from the group comprising: maleic acid, maleic anhydride or fumaric acid.
6. - A film according to claim 1 wherein the 5 functionalized monomers of component B are selected one from the group comprising styrene, 2-methylstyrene, 4-methylstyrene, alpha-methylstyrene, beta-methylstyrene, vinyl-4-anisole, stilbene and indene or mixtures thereof, and the other is selected from the group comprising: maleic, 10 itaconic, citraconic anhydrides, maleimide, and N-phenylmaleimide or mixtures thereof.
7. - A film according to claim 1, wherein the grafting rate of compound B is less than 2% by weight.
8. - A film according to claim 1, wherein compound D con15 sists of a 6 polyamide, 6/6 polyamide or a mixture thereof.
9. - A film according to claim 1, wherein the following holds: 30 < A+B+C <45 and B + C > 5
10. - A film according to claim 1, comprising the following components A, B, C and D: 20 - A is polypropylene; - B, if present, is a copolymer of ethylene and maleic-grafted propylene; - C is a grafted copolymer consisting of at least one mono-amino oligoamide and a (co)polymer of alpha-olefin 25 grafted by a monomer able to react with the amine function of said oligoamide; - D is 6-polyamide and/or 6/6-polyamide.
11. - A film according to claim, 1, wherein the thickness of said film is comprised in the range of from 10 to 130 um, 5 and preferably from 20 to 50 μπι.
12. - A sandwich-structure comprising: (i) a central layer of a reinforced unhardened thermosetting sheet molding product, (ii) two outer layers of polymer film according to any one of 10 claims 1 to 11.
13. - A method for producing a sheet molding compound in which: a) a layer of thermosetting resin suitable for thermal processing is poured, in fluid form, onto a polymer film 15 as defined in any one of claims 1 to 11, advancing continuously, b) a reinforcing material is introduced onto the advancing fluid layer, c) a polymer film as defined in any one of claims 1 to 11 20 is placed in contact with the upper surface of the reinforced fluid layer thus forming a composite mass of a sandwich-structure, d) the sandwich-structure composite mass is caused to advance through a series of kneading and compacting 25 rollers, and e) the sandwich-structure composite mass is rolled into a roll for partial heat treatment.
14. - A polymer film according to claim 1, substantially as hereinbefore described and exemplified.
15. - A sandwich-structure according to claim 12, substantially as hereinbefore described and exemplified.
16. - A method according to claim 13 for producing a sheet molding compound, substantially as hereinbefore described and exemplified.
17. - A sheet molding compound, whenever produced by a method claimed in a preceding claim.