IE910457A1 - Lubricious hydrophilic coating, resistant to wet abrasion - Google Patents

Lubricious hydrophilic coating, resistant to wet abrasion

Info

Publication number
IE910457A1
IE910457A1 IE45791A IE45791A IE910457A1 IE 910457 A1 IE910457 A1 IE 910457A1 IE 45791 A IE45791 A IE 45791A IE 45791 A IE45791 A IE 45791A IE 910457 A1 IE910457 A1 IE 910457A1
Authority
IE
Ireland
Prior art keywords
polymer
coating
hydrophilic
wet
hydrophilic coating
Prior art date
Application number
IE45791A
Inventor
Richard J Whitbourne
Original Assignee
Sterilization Techn Serv
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sterilization Techn Serv filed Critical Sterilization Techn Serv
Priority to IE45791A priority Critical patent/IE910457A1/en
Publication of IE910457A1 publication Critical patent/IE910457A1/en

Abstract

The lubricious hydrophilic coatings of the invention are significantly more lubricious when wet than when dry, are adherent to a variety of substrates, and are resistant to removal by wet abrasion. In one embodiment, the coatings include a hydrophilic polyolefin such as polyvinyl-pyrrolidone and a waterinsoluble stabilizing polymer such as a cellulose ester. The coatings may also include an adherent polymer and a plasticizing agent. The coating may be applied by preparing a solution of the stabilizing polymer and a solution of the hydror/ ilic polyolefin, and coating the substrate first in one then the other. Alternatively, both the stabilizing and hydrophilic polymers may be dissolved in a single solvent system and applied to the substrate in a single step. In another embodiment, only a solution of a hydrophilic polyolefin is applied directly to the substrate. In this embodiment, the solution cf the hydrophilic polyolefin includes a cosolvent which acts as a solvent for both the hydrophilic polyolefin and the substrate. The coatings of the invention nay be applied to biomedical devices and implants such as catheters, condoms, and nasogastric and endotracheal tubes.

Description

This invention relates to hydrophilic, lubricant coatings that make biomedical devices slippery when wet. The method and coating of the invention may be employed to reduce the coefficient of friction of catheters, condoms, contact lenses, peristaltic pump chambers, arteriovenous shunts, gastroenteric feed tubes and endotracheal tubes, or other implants of metal or polymer substrate.
Known lubricious coatings that may be applied to biomedical devices include coatings of polyvinylpyrrolidone (PVP), polyurethane, acrylic polyester, vinyl resin, fluorocarbons, silicone, rubber, or combinations of these substances.' For example, Micklus et al., U.S. 4,100,309 and U.S. 4,119,094 relate to a hydrophilic coating of PVP polyurethane interpolymer formed with polyisocyanate. Ratner et al., U.S. 3,939,049, relates to a method of grafting hydrogels to polymeric substrates using radiation.
Hudgin et al., U.S. 3,975,350, relates to hydrophilic polyurethane polymers. Stoy et al·., U.S. 3,987,497, -2relates to a tendon prothesis with hydrogel coating.
These known hydrogel coatings have disadvantages: They may have an insufficiently low coefficient of friction, they may lack permanence (such as silicone or fluorocarbons), they may be slippery when dry as well as wet, making handling difficult, or (such as the Micklus et al. coatings) they may require the use of hazardous solvents to prepare them and contain unstable, reactive materials, so that separate and new solutions must be prepared daily or more frequently.
Furthermore, in the PVP-polyurethane coatings, little control can be exerted over the degree of lubricity and resistance to wet abrasion of the coatings, and such coatings are often unstable.
In order to solve these problems a hydrophilic lubricant coating was needed which, when wetted, has sufficient lubricity to be useful for biomedical devices such as implants, which adheres to a wide variety of substrates and resists wet abrasion, and which can be prepared from chemically stable and biocompatible solvents .
SUMMARY OF THE INVENTION One embodiment of the present invention relates to a hydrophilic coating which comprises a hydrophilic polymer and a stabilizing polymer in a layer bonded to the surface of the device. The hydrophilic polymer is a polyolefin such as a vinyl polymer having polar pendant groups, a polyacrylate or methacrylate having hydrophilic esterifying groups, a polyether, a polyethylene glycol, or other polyolefin with hydrophilic characteristics. The hydrophilic polymer is -3preferably PVP or PVP vinyl acetate. The stabilizing polymer is a water-insoluble polymer that does not significantly react with the hydrophilic polymer in solution, and is preferably cellulose ester, a copolymer of polymethyl vinyl ether and maleic anhydride, or nylon. The cellulose esters are most preferred. They include ethyl cellulose, hydroxyethyl cellulose, cellulose nitrate, cellulose acetate, cellulose acetate butyrate, and cellulose acetate proprionate.
In one embodiment, the coating has an inner layer where the stabilizing polymer is concentrated and an outer layer where the hydrophilic polymer is concentrated. In another embodiment, the hydrophilic polymer and stabilizing polymer are contained in a single application and comprise a single layer of coating.
The coating may also contain an adherent polymer such as polyurethane, polyester, styrene polybutadiene, acrylic resin, polyvinvlidene chloride, polycarbonate, and polyvinyl chloride, preferably in the inner layer to promote adhesion to the surface of the device.
A most preferred outer layer composition uses PVP of high molecular weight (e.g. 120,000-360,000).
The inventive coating may be applied to a polymer surface such as polyurethane, polyvinyl chloride, polyacrylate, polycarbonate, polystyrene, polyester resin, polybutadiene- styrene copolymers, nylon, polypropylene, polybutylene, teflon, silicon, and polyvinyl acetal. The coating of the invention can also be applied to glass or metals such as stainless steel. The coating components can be selected to produce a coating with desired properties on these surfaces. -4The method of preparing the coatings of the invention employs stable, non-toxic solutions which may be stored and handled with minimal precautions. The method of applying the coating of the invention comprises preparing a first organic solution of from about 0.01% to about 30% weight to volume of stabilizing polymer, preferably from about 0.2% to about 10%, applying the solution to a substrate surface, and evaporating the solvent, preferably at elevated temperature, then preparing a second solution Of from about 00.01% to about 30% Weight to volume hydrophilic polymer, preferably from about 0.5% to about 20%, applying it to the created surface substrate and evaporating the solvents at room or elevated temperature.
The stabilizing polymer solution may also contain from about 0.01% to about 10% of hydrophilic polymer, preferably from about 0.1% to about 5%. The hydrophilic polymer solution nay also contain from about 0.01% to about 20% of stabilizing polymer, preferably from about 0.1% to about 10%. Alternatively, the stabilizing polymer and hydrophilic polymer can be prepared in a single solution and applied in a single step.
The surface of the device may be pre-treated to promote adhesion of the coating. The solutions may also contain from about 0.1% to about 15% of an adherent polymer, preferably from about 1.0% to about 8.0% weight to volume to promote the bond between substrate and coating.
A plasticizing agent may be included with the stabilizing polymers, in a concentration of from about 0.01% to about 10%, preferably from about 0.1% to about '/ — *’4 * .-. -55.0%, weight to volume. The plasticizing agent may be camphor, castor oil, dioctyl phthalate, acetyl tributyl citrate, dibutyl sebacate, sebacic acid, alkyl resin, dibutylphthalate, polyvinylbutyral or other commonly known plasticizers, singly or in combination. The plasticizing agent is preferably included in the solution of stabilizing polymer. The inventive coating may include a plasticizer to enhance the flexibility of the coating, which may be preferable when the object to be coated is likely to bend during use. Also, the inclusion of a plasticizer is preferred when the stabilizing polymer is nitrocellulose, because the plasticizer reduces the tendency of nitrocellulose to oxidize rapidly or even combust when it is dried in a pure form.
Solvents for the stabilizing and adherent polymer include organic solvents such as ketones, esters, toluene, lactones, dimethylformamide, halogenated solvents, tetrahydrofuran, dioxane, amines, glycol butyl ether, alkyl acetates, acetonitrile, and other commonly known organic solvents. The less roxic solvents are preferred. The inclusion of small amounts of hydroxyl groups such as alcohols and moisture in the solvent does not have a significant detrimental effect on the coating and method of the invention.
Solvents for the hydrophilic polymer include most of the above as well as alcohols, acetic acid, and like solvents. A solvent system may be selected that is capable of dissolving all the constituents of the coating in a uniform solution, can act as a co-solvent in the layer, and is non-toxic.
If desirable, a solvent may be selected that Γ; -6interacts with the particular substrate surface to promote adhesion.
In another embodiment of the present invention, the article to which the coating is to be applied has a polymer surface and an active solvent is used which obviates the need for the inner layer or base coat by permitting a -lubricious hydrophilic layer (or top coat) to be applied directly onto the polymer surface of the article. In this embodiment, the term active solvent is defined as a cosolvent for both the polymer or polymer mixture comprising the polymer surface or at least one or more of the polymers in cases of mixed polymer substrates and for the coating polymer(s).
The solutions may be applied by dipping the object to be coated into a vessel containing the solution, or the solutions may be poured, pumped, brushed or sprayed onto the object.
DETAILED DESCRIPTION OF THE INVENTION The hydrophilic coatings of this invention are highly lubricious when wetted with an aqueous solution such as body fluid, or a lower alcohol such as ethanol or methanol, yet they are substantially less slippery when dry. Thus, an implant coated according to the invention remains non-slippery for ease of handling and preparation, but becomes lubricious when implanted, so as to protect the patient. The lubricity of the coating can be adjusted within a desirable range.
A coating according to the invention may be applied to the surface of a biomedical or other device with sufficient thickness and permanence to retain the coating's desirable qualities throughout the useful life -Ιοί the coated device. The coatings of the invention are non-reactive with living tissue and are non-thrombogenic in blood.
The coating of the invention has beneficial 5 characteristics for use on the surfaces of devices such as biomedical implants. The coating is hydrophilic, absorbing water and swelling in an aqueous environment to become a hydrogel. The coating has lubricant properties, and is significantly more slippery when wet than when dry. The coating is thin, on the order of magnitude of one thousandth of an inch. The coating is coherent and resistant to removal by wet abrasion, and it is adherent to a wide variety of substrates. The coating employs biocompatible substances that are neither toxic nor irritant. The functional characteristics of the coating may be varied as appropriate for many different applications.
The method of the invention is beneficial because the components can be varied to control lubricity, swelling, flexibility, and resistance to removal by wet abrasion. These characteristics of the coating can thus be adjusted for various substrates and applications.
The method is also beneficial because the solutions of the invention have good shelf stability and remain substantially free of precipitate for periods in the range of months or years, so that various mixtures of the solutions for coatings may be prepared at one time and used to : oat substrates later. Alternatively, the hydrophilic and stabilizing polymers, and if desired, a plasticizing agent and an adherent polymer, may even be prepared in a single solution. Furthermore, since the invention does not require the use of chlorinated -σ &4S7 -8solvents or other acute toxics, fewer precautions are necessary to protect workers from health hazards.
Without intending to limit the invention to its mode of operation, apparently the stabilizing polymers of the invention, particularly modified cellulose polymers, are able to make hydrophilic polymers, such as PVP and PVP-vinyl acetate copolymers, stable and insoluble in water and lower alcohols. The resulting combination, when applied to a substrate, produces a coating that is a stable layer or layers that are bonded to a substrate surface, is not slippery when dry but is desirably lubricious when wet, and is resistant to removal by conditions of wet abrasion. The coating layer bonds to an impervious surface such as stainless steel or glass. It also bonds to polymer surfaces where the surface interacts with the components of the coating.
It is possible to control the degree of stability, wet lubricity, insolubility, flexibility, and adhesion of the coating by varying the weight to volume percentages of the components in the coating solutions. Substantially all of the polymers and plasticizers deposited from solutions onto the surface of the object oeing coated remain in the layer of the coating after the solvents are evaporated. Also, the duration and temperature of the evaporating step may be selected to achieve stability of the coating layer and to achieve a bond between the surface being coated and the coating layer.
Preferably, the outer layer solution contains some amount of an active solvent, i.e., a cosolvent, for the outer layer ingredients as well as the inner layer -9ingredients. As such, the active solvent causes the outer layer solution to penetrate into the inner layer, and is believed to bring about a mixing at the molecular level of the components of both layers.
It is believed that such molecular mixing may lead to chemical reactions such as cross-linking between the components, or may only comprise physical mixing without chemical reaction(s). In any event, in one preferred embodiment, there is a high degree of cross-linking or intermolecular mingling between the hydrophilic polymer and the stabilizing polymer at the interface between the inner and outer layers of the coating relative to the outer surface of the outer layer. Thus, an interpolymer between the two layers may be created as a result of cross-linking or intermolecular mingling between the polymers contained in the separate layers. The slight degree or lack of cross-linking at the outer surface of the coating aids in providing the lubricity of the coating of the present invention.
In practice, the activity of the solvent mixture is adjusted so that the degree of penetration of the outer layer into the inner layer is in a useful range. For example, if the outer layer solvent mixture is too active toward the inner layer, then too much penetration inro the inner layer occurs, and the outer layer will not be sufficiently lubricious when wet. Conversely, if the outer layer solvent is too inactive toward the inner layer, then too little penetration of outer layer into the inner layer occurs, and the coating is too easily removed from the inner layer by wet abrasion.
In another embodiment of the present invention, where the lubricious hydrophilic layer is applied - “ I Ύ/ ) -10directly onto a polymer surface as a top coat, and an active solvent is used which is a cosolvent for both the plastic substrate polymer or polymer mixture or at least one or more of the polymers in cases of mixed polymer substrates, and for the coating polymer(s) in the hydrophilic layer.
After drying, which is typically done at temperatures between 50°C and 100°C, but may be done at higher or lower temperatures, the top coat polymer(s) layer is left partially embedded in the polymer surface. As in the case of the two-layer system, the solvent used during the coating application can be too active such that the top coat penetrates into the polymer surface to such a degree that the coated layer behaves as though it has been highly cross-linked. This causes the top coat to not become sufficiently swollen and lubricious when wet by aqueous fluids. Solvent mixtures can also be too inactive, so that the coating is not resistant enough to abrasion when wet and is too easily removed.
As in the two-layer systems, ether polymers or cross-linking agents may be incorporated with the hydrophilic polymer(s) in the lubricious layer to enhance the adhesion of the layer to the polymer surface, making the lubricious layer more resistant to wet abrasion.
The active solvents which are useful in the present invention may be individual solvents or solvent mixtures containing two or more solvents. In the case of solvent mixtures, one or more of the solvents in the mixture may be active while other solvent(s) in the mixture may be inactive. In any event, the solvent or solvent mixture dissolves or at least disperses the top coat polymer(s). -11In cases where the top coat polymer is dispersed but not dissolved, a point is reached where the top coat polymer(s) go into solution before all of the solvent has left the coating. During the phase of drying where the top coat polymer(s) is in solution, the solvent has also penetrated the substrate polymer(s) of the polymer surface. Thus, intermolecular mingling may take place between the substrate polymer(s) and the top coat polymer(s).
Examples of active solvents useful in the present invention include butyrolactone, alcohols, dimethyl acetamide, and n-methyl-2-pyrrolidone. These solvents and others cause different degrees of swelling of the plastic substrate or inner layer, as the case may be.
The hydrophilic polymers of the coatings are generally PVP of higher molecular weight, 120,000360,000. PVP of lower molecular weight, as low as 15,000, can be used in the underlayer or base coating next to the substrate without deterioration of performance. Some or all of the PVP can be replaced with PVP-vinylacetate copolymer in the one-coat embodiment, or in either layer of the two-coat embodiment.
It has been found that the most preferred stabilizing polymer is a water insoluble cellulose polymer. Alternatives to modified cellulose polymers, such as polymethylvinylether maleic anhydride and nylon may be used instead of or in addition to the modified cellulose polymers, but these are more difficult to work with, and tend to produce coatings with less long-term wet abrasion resistance than coatings prepared without them. When the stabilizing polymer is nitrocellulose, ~ § 5 ί* 4 5 7 J -12it is preferable to include a plasticizing agent.
When tested by subjective methods the coatings of the invention, when wet, are more slippery than wet, greased glass, and, when dry, are no more slippery than dry glass. The coatings of the invention are resistant to removal by wet abrasion as determined by running water over the coatings and rubbing between tightly gripped fingers while wet. The inventive coatings have high adherence when dry, as determined by attaching IQ adhesive tape, pulling the tape off with a vigorous action, and then wetting the coated substrate to determine whether the taped portion retained the lubricant coating. The inventive coatings remain adherent and coherent for extended periods when stored in water, and neither peel off, dissolve, nor dissociate.
The coating systems described herein will produce hydrophilic lubricant coatings, resistant to wet abrasion on surfaces such as polyethylene, polypropylene, silicon, glass, stainless steel, and other substrates generally considered as presenting adherence problems. It may be necessary to treat such surfaces with gas plasma or other ionizing treatment to promote adhesion tc the substrates. The following examples show how the invention can be used.
EXAMPLE 1: Polyurethane tubing was dip coated in a stabilizing polymer solution of .4 gm low viscosity 1/2 second nitrocellulose 2.0 gm dibutylphthalate 1.5 gm campnor -1315 1.9 gm polyvinylbutyral in a solvent mixture of 36.0 ml toluene 13.1 ml butylacetate .9 ml isopropanol .4 ml ethylacetate 18.1 ml ethanol 1.5 ml acetone.
The coated tube was dried for 5 minutes at 65 °C. It was then dip coated with a hydrophilic polymer solution containing 6.6 gm polyvinylpyrrolidone 63.8 ml denatured ethanol 23.6 ml ethyl acetate 12.6 ml dimethylformamide and dried 5 minutes at 65 °C. A hydrophilic coating resulted which was slippery when wet.
EXAMPLE 2: Stvrenebutadiene tubing was dip coated in a stabilizing polymer solution containing 1.9 gm 1/2 second nitrocellulose together with a hydrophilic polymer, 1.5 gm polyvinylpyrrolidone, in ml ethylacetate 34.4 ml denatured ethanol 4.6 ml acetic acid I ml isopropanol and dried 5 minutes at 80 °C. The sample was then dip coated in a hydrophilic polymer solution containing 7.5 gm polyvinylpyrrolidone together with a stabilizing polymer, 0.3 gm nitrocellulose, in ml denatured ethanol -1426.8 ml ethylacetate 0.2 ml isopropanol and dried 5 minutes at 8O’C. A hydrophilic coating resulted that was lubricious when wet.
EXAMPLE 3: Polyurethane tubing was dip coated with a stabilizing and hydrophilic polymer solution containing .9 gm 1/2 sec. cellulose acetate butyrate and 5.9 gm polyvinylpyrrolidone in 33 ml ethyl acetate and 67 ml chloroform and dried 5 minutes at 80 °C. This was then dip coated in a hydrophilic polymer solution containing 5 gm polyvinylpyrrolidone in 95 ml denatured ethanol and dried 5 minutes at SO’C. A hydrophilic coating resulted that was lubricious when wet.
EXAMPLE 4: Samples of polyurethane tubing were coated with a stabilizing and adherent polymer solution containing 1.3 gm nitrocellulose 1.1 gm polyester resin 1.0 gm monobutylester of polymethylvinylether/maleic anhydride copolymer 0.3 ml isopropanol 57.8 ml ethylacetate 22.4 ml denatured ethanol ml dimethylformamide.
The sample was dried five minutes at 80 °C. The samples were then dip coated in a hydrophilic polymer solution containing 6.6 gm polyvinylpyrrolidone -1563.8 ml denatured ethanol 23.6 ml ethylacetate 12.6 ml dimethylformamide The sample was dried five minutes ar 30 °C, to produce an 3 adherent, lubricious, layered coating. A similar coating was also produced on polyvinylchloride tubing. EXAMPLE 5: This example shows how different adhesive resins 10 can be added to promote adhesion to a substrate. a. The following stabilizing polymer solution was dip coated on polyurethane tubing and dried 5 minutes at 80°C. nitrocellulose 56 gm 15 camphor 15 gm dibutylphthalate 20 gm isopropanol 2 3 ml toluene 225 ml ethyl acetate 330 ml 20 butyl· acetate 96 ml acetone 7 ml This was then dip coated with a hydrophilic polymer solution: polyvinylpyrrolidone (PVP) 3 gm 25 denatured ethanol 27 ml ethyl acetate 10 ml dimethylformamide 12 ml The coating separated from the cubing when immersed in water. b. Example 5(a) was repeated with from 5.0 gm to gm of polyurethane resin added to the nitrocellulose solution to croduce saiwles that showed excellent -16adhesion when immersed in water. c. Example 5(a) was repeated with from 5.0 gm to 17.0 gm polyester resin added to the nitrocellulose solution to produce samples that showed excellent adhesion when immersed in water. d. Example 5(a) was repeated with from 5.0 gm to 17.0 gm of styrene butadiene resin added to the nitrocellulose solution to produce samples that showed excellent adhesion when immersed in water. e. Example 5(a) was repeated with from 5.0 gm to 17.0 gm of urea formaldehyde resin added to the nitrocellulose solution to produce samples that showed excellent adhesion when immersed in water.
EXAMPLE 6 Polyurethane tubing was coated with the following stabilizing polymer solution and dried five (5) minutes at 65 ° C. nitrocellulose 65 gm dibutylphthalate 24 gm campnor 13 gm polyvinylbutyral 23 gm acetone 28 ml ethanol 306 ml butyl acetate 257 ml ethyl acetate 500 ml toluene 550 ml isopropanol 28 ml dimethylformamide 200 ml The sample was then overcoated with the following hydrophilic polymer solution and dried five (5) minutes at 65’C. - έι -j ΰ 4 5 7 J -17polyvinylpyrrolidone 1 gm ethanol 9 ml dimethylformamide 3 ml water 0.5 ml This sample had excellent adhesion when immersed in water.
EXAMPLE 7 An acrylic surface was coated with the following stabilizing polymer solution and dried five (5) minutes at 70“C. cellulose acetate propionate 12.9 gm dibutylphthalate 4.8 gm camphor 3.6 gm acetone 3.2 gm ethyl acetate 55.7 gm toluene 58.6 gm butyl acetate 28.5 gm isopropanol 5.6 gm The sampie was then coated w ith the following hydrophilic polymer solution and dried five (5) minutes at 70”C. acetonitrile 5 ml ethanol 4.5 ml PVP (360,000 mw) 0.5 gm The coating was not soluble in water and was very slippery. EXAMPLE 3 An acrylic surface was coated with the following stabilizing polymer solution and dried five (5) minutes at 7 0 ’ C. -18cellulose acetate dibutylphthalate camphor methylethylketone dimethylformamide 12.9 gm 4.8 gm 3.6 gm 148.3 ml 20.0 ml The sample was then coated with the following hydrophilic polymer solution and dried five minutes at 70’C.
PVP (360,000 row) 0.5 gm cellulose acetate 0.1 gm acetone 6 ml ethanol 4.5 ml acetic acid 1.0 ml methylethylketone 0.9 gm The coating was insoluble in water and was very lubricious.
EXAMPLE 9 An acrylic surface was coated with the following stabilizing and adherent polymer solution and dried five minutes at 70’C. cellulose acetate butyrate 6.5 gm polyester resin 6.0 gm dibutylphthalate 2.4 gm camphor 1.8 gm acetone 2.5 ml ethyl acetate 43.6 ml toluene 43.6 ml butylacetate 22.4 ml The sample was then coated with the following hydrophilic polymer solution and dried five (5) at 70 °C. minutes 910457· -19acetonitrile 5 ml ethanol 4.5 ml PVP (360,000 mw) 0.5 gm This coating was water insoluble and was lubricious when wet.
EXAMPLE 10 Nylon tubing was coated with stabilizing polymer with the following solution and dried ten (10) minutes at 75’C. nylon resin 2 gm trifluoroethanol 18 ml The sample was then overcoated with hydrophilic polymer with the following solution and dried ten (10) minutes at 75’C.
PVP (360,000 mw) 1.0 gm nylon resin 0.3 gm ethanol 9.0 ml dimethylformamide 3.0 ml trifluoroethanol 2.7 ml This coating was not water soluble.
EXAMPLE 11 A stainless steel wire guide was coated with stabilizing polymer with the following solution and dried ten minutes at 70“C. nitrocellulose 64.6 gm dibutylphthalate 24.3 gm camphor 17.9 gm polyvinylbutyral 22.5 gm acetone 28.4 ml ethanol 306 . 1 ml butylacetate 257.0 ml ethylacetate 499.2 ml toluene 552.8 ml isopropanol 27.5 ml □ dimethylformamide 200.0 ml The sample was then overcoated with hydrophilic polyme: with the following solution and dried ten (10) minutes at 70’C. PVP 1.0 gm 10 ethanol 9.0 ml dimethylformamide 2.0 ml This coating was insoluble in water and was very lubricious. 15 EXAMPLE 12 The coating method of example 11 was repeated on , acrylic surface and also produced a coating that was insoluble in water and very lubricious. 20 EXAMPLE 13 Nylon tubing was coated with a stabilizing and adherent polymer with the following solution and dried for five (5) minutes at 65’C. nitrocellulose 32.3 gm 25 polyurethane 11.2 gm dibutylphthalate 12.2 gm camphor 9.0 gm polyvinylbutyral 11.2 gm acetone 2 5 ml 30 ethanol 254 ml butylacetate 225.3 ml ethylacetate 439.2 ml -21toluene 467.8 ml isopropanol 13.8 ml dimethylformamide 100 ml The sample was then coated with hydrophilic polymer with the following solution and dried five (5) minutes at 65’C.
PVP 1.0 gm nitrocellulose 0.12 : gm ethanol 9.0 ml dimethylformamide 3.0 ml ethylacetate 0.4 ml coating was insoluble in water and was very lubricious .
EXAMPLE 14 Polyurethane tubing was coated with the following stabilizing polymer solution and dried five (5) minutes at 65C. nitrocellulose 64.6 gm d i b u t y 1 p h t h a i a t e 24.3 gm camphor 17.9 gm polyvinylbutyral 22.5 gm acetone 28.4 ml ethanol 306.1 ml dutylacetate 257.0 ml ethylacetate 449.2 ml toluene 552.8 ml isopropanol· 27.5 ml dimethylformamide 200.0 ml This sample was then overcoated with the following hydrophilic polymer solution and dried five minutes at 65’C. -22PVP 1.Ο gm ethanol 9.0 ml dimethylformamide 2.0 ml This sample coating was insoluble in water and very 5 lubricious when wet.
EXAMPLE 15 Polyvinylchloride tubing was treated in the same way as the nylon tubing in example 13. The resulting coating was insoluble and very lubricious.
EXAMPLE 16 A sample of styrene-butadiene tubing was coated with stabilizing and adherent polymer with the following solution and dried five (5) minutes at 80’C. nitrocellulose 32.3 gm polyurethane 10.0 gm dibutylphthalate 12.2 gm camphor 9.0 gm polyvinylbutyral 11.2 gm acetone 25 ml ethanol 264 ml butylacetate 226.3 ml ethyl acetate 439.2 ml toluene 467.8 ml isopropanol 13.8 ml dimethyformamide 100 ml The sample w-.s then coated with the following hydrophilic polymer solution and dried five minutes at SO’C.
PVP 1.0 gm ethanol 9.0 ml -233.0 ml 0.5 ml dimethylformamide water This sample was insoluble in water and was lubricious when wet.
EXAMPLE 17 This example shows how solvent(s) can be added which improves adhesion by etching or interacting with the layer onto which it is being coated. Several samples of polyurethane tubing were coated with the following stabilizing polymer solution. nitrocellulose 64.6 gm dibutylphthalate 24.3 gm camphor 17.9 gm polyvinylbutyral 22.5 gm acetone 28.4 ml ethanol 306.1 ml butylacetate 257.0 ml ethyl acetate 499.2 ml toluene 552.3 ml isopropanol 27.5 ml dimethylformamide 200.0 ml Samples coated as above were then coated with one of the following solutions containing various amounts of dimethylformamide or acetic acid, . which interact with the surface being coated in order to promote adhesion: (a) Coat with the following hydrophilic polymer solution and dry five (5) minutes at 70C. ?vp 1.0 gm ethanol 9.0 ml dimethylformamide 3.0 ml This hydrophilic coating adhered well, was : insoluble in -24water, and was very lubricious. (b) Coat with hydrophilic polymer, 10% (w/v) PVP in ethanol and dry five (5) minutes at 70’C. This hydrophilic coating dissolved in water and came off. (c) Coat with the following hydrophilic polymer solution and dry five (5) minutes at 70’C.
PVP 1.0 gm ethanol 9.0 ml dimethylformamide 1.0 ml This sample resisted removal when wet, but was not as resistant to wet abrasion as the sample above containing three (3) ml of dimethylformamide. (d) Coat with the following hydrophilic polymer solution and dry five (5) minutes at 70’C.
PVP 1.0 gm ethanol 9.0 ml acetic acid 3.0 ml This hydrophilic coating adhered well, was insoluble in water, and was verv lubricious.
EXAMPLE 18 In this example, the hydrophilic polymer and the stabilizing polymer were combined into a single solution, which was coated on polyurethane tubing and dried five (5) minutes at 80”C: 0.5 gm 0.056 gm 13.7 ml 0.024 gm 1.0 ml coating that was lubricious wet abrasion.
PVP nitrocellulose methy1ethylketone isopropanol acetic acid This produced a single-layer when wet and was resistant to -25EXAMPLE 19 The following solution is coated on polyurethane tubing and dried (5) minutes at SO’C.
PVP 1.5 gm Polyethylene Glycol 2.7 gm Ethanol 68.8 gm Isopropanol 18.0 gm 4-Butyrolactone 3.0 gm In this example, the hydrophilic polymer was 10 combined in a solution which contains at least one solvent which swells the substrate onto which the coating is applied. By swelling the substrate, some of the hydrophilic polymer molecules become entrained in the surface of the substrate after the solvents are evaporated.
Because some of the hydrophilic polymer is tightly bound into the substrate surface, it is made resistant to wet brasicn and produces a single-layer coating that is lubricious when wet.
EXAMPLES 20-24 The following solutions are prepared, dip-coated onto an S french polyurethane tube, ar.d thereafter dried for 10 minutes at SO’C.
INGREDIENT_Ex. 29_Ex. 21 Ex. 22 Ex. 23_Ex. 24 % PV Pin oenzyl Alcohol N,N, Dimechyl 30 Acetamide Glacial Acetic - C 5 - o s 16.0 g 15.0 g 7.5 g 4.0 g 16.0 g Acid 910457’ -26INGREDIENT_Ex. 20 Ex. 21 Ex. 22 Ex. 23_Ex, 24 N-Methyl-2- — — — --- 7.5 g Pyrrolidone Denatured Ethanol 25.3 g --- 1.8 g 1.8 g 1,8 g To evaluate the performance of coated lubricious layers with regard to wet lubricity and wet abrasion resistance the following test method was used. After the coating was dried to remove the organic solvents, a solution of Gentian Violet (such as Cat. No. 3240 from Ricca Chemical Company) is applied to the coated surface using a brush or cotton swab. This dye is strongly absorbed into the lubricious layer, but not into the plastic substrate. Next, the dyed sample is held under cold gently running water. After rinsing the samples with water, they are rubbed briskly between the thumb and forefinger of one hand using a firm grip. In cases where adhesion to the plastic substrate is very poor, the coated layer may wash off completely from the surface as evidenced by washing off of substantially all of the dye. In cases where the coated layer has penetrated too far into and/or become to hardened as by incorporation of too much polymeric or cross-linking agent into the coating, the dye srain can be very strong after rinsing. During the finger rubbing test, most or all of such coated layers will stay on the plastic substrate, as evidenced by retention of most of the dye, but they will nor feel very lubricious. Intermediate between these extremes are coatings that have a more desirable balance of lubricious feel and resistance to -27removal by wet rubbing. An ability to make such qualitative assessments is quickly developed by persons skilled in evaluating physical properties of various plastic or other materials.
The coating of Example 20 washed off completely when held under cold running water, indicating that there was little or no penetration into the polyurethane and hardening of the coating. This is expected since ethanol shows very low solvent activity toward this polyurethane surface.
The outermost portion of the coatings of Examples 21 and 23 rubbed off when wet, but a thin layer remained that was very lubricious. The retained dye intensity was intermediate. These samples were judged co have very good balance between resistance to wet abrasion and lubricity.
The coatings of Examples 22 and 24 were not very lubricious when wet rubbed and the coating did not feel swollen ny water in comparison to Examples 21 and 23. Samples were extremely resistant to rubbing off when wet as evidenced by a much more intense residual dye stain after wet rubbing when compared to Examples 21 and 23. These are examples where the solvent is too active so that little lubricity results.
These samples show how the performance of the lubricious layer can be adjusted to balance the resistance to wet rub off and the lubricity by selecting and using solvents alone or in combination that provide a sufficient degree of activity.
EXAMPLE 25 A solution was made as follows: -28Polyvinylpyrrolidone 0.4 g Denatured Ethanol 19.6 g Benzyl Alcohol 10.0 g This solution was dip coated on polyurethane 5 tubing and then drying for 22 minutes at 80’C. A solution of Gentian Violet is applied to the coated surface as detailed in Examples 20-24. When tested, this coating was fairly resistant to wet ruff-off and was very lubricious. Comparing it to the coating of Example 21, it was a little more lubricious, but it was somewhat less resistant to wet rub-off.
EXAMPLE 26 The following solution was dip coated over 15 polyurethane tubing and dried 12 minutes at 80’C. A solution of Gentian Violet is applied to the coated surface as detailed in Examples 20-24.
Polyvinylpyrrolidone Benzyl Alcohol 0.4 10.5 20 Denatured Ethanol 3.6 N,N, Dimethylacetamide 5.0 g g g g This coating was very lubricious and a lubricious layer remained on the surface after vigorous wet rubbing which would not be removed.
EXAMPLE 27 The following solution was dip coated on polyvinyl chloride tubing and dried 12 minutes at 80’C.
Polyvinyl Pyrrolidone 0.9 gm Methyline Chloride 5.0 gm N-Methy1- 2-Pyrrolidone 10.0 gm -29Α solution of Gentian Violet is applied to the coated surface as detailed in Examples 20-24. After cooling, the coating was tested for wet lubricity and wet rub resistance by using the aforementioned Gentian Violet test regimen.
This coating was very lubricious and a lubricious layer remained on the surface after vigorous wet rubbing which could not be removed.
The examples provided above are not meant to 10 be exclusive. Many other variations of the present invention, including the use of other cosolvents and polymer mixtures, would be obvious ro those skilled in the art, and are contemplated to be within the scope of the appended claims.

Claims (12)

1. A lubricious hydrophilic coating for an article which is substantially more slippery when wet than when dry, resistant to removal by wet abrasion and essentially insoluble in aqueous solution comprising a hydrophilic polymer selected from the group consisting of polyvinylpyrrolidone and polyvinylpyrrolidonepolyvinyl acetate copolymer, and a mixture of the above, and a water-insoluble stabilizing polymer consisting essentially of a cellulose ester, a copolymer of polymethyl vinyl ether and maleic anhydride, an ester of the copolymer, nylon, and a mixture of any of the foregoing.
2. The coating of claim 1 which is applied to the surface of a polymer selected from the group consisting of glass, metal, polyurethane, polyvinylchloride, polyacrylate, polycarbonate, polystyrene, polyester resins, polybutadiene-styrene copolymers, nylon, polypropylene, and polybutylene.
3. An article having the lubricious hydrophilic coating of claim 1.
4. The coating of claim 1 in which the stabilizing polymer is concentrated in the inside portion of the coating adjacent the surface of the article and the hydrophilic polymer is concentrated in the outer portion of the coating.
5. An article having a lubricious hydrophilic coating, comprising an article having a polymer surface, and a lubricious hydrophilic coating on said 910457’ -31substrate, said hydrophilic coating including a hydrophilic polymer selected from the group consisting of polyvinylpyrrolidone, polyvinylpyrrolidone polyvinyl acetate copolymer, and a mixture of the above, said hydrophilic coating having an exposed outer surface and an interfacing surface with said polymer surface, said hydrophilic coating having a high degree of crosslinking or intermolecular mingling between said hydrophilic polymer and said polymer surface at said interfacing surface relative to said outer surface, said hydrophilic coating being substantially more slippery when wet than when dry, resistant to removal by wet abrasion, and essentially insoluble in aqueous solution.
6. The article of claim 5, wherein said polymer surface comprises polyvinylchloride, polyacrylate, polycarbonate, polystyrene, polyester resins, polybutadiene-styrene copolymers, nylon, polypropylene, polybutvlene, teflon, silicon, and polyvinyl acetal.
7. An article having a lubricious hydrophilic coating, comprising an article having a polymer surface selected from the group consisting of polyurethane, polyvinylchloride, polyacrylate, polycarbonate, polystyrene, polyester resins, polybutadiene-styrene copolymers, nylon, polypropylene, polybutylene, teflon, silicon, and polyvinyl acetal, and a lubricious hydrophilic coating on said substrate, surface with said polymer surface, said hydrophilic coating having an exposed outer surface and an interfacing said hydrophilic coating including a -32hydrophilic polymer selected from the group consisting of polyvinylpyrrolidone, polyvinylpyrrolidone polyvinyl acetate copolymers, and a mixture of the above, said hydrophilic coating penetrating said polymer surface of said polymer surface via the use of a cosolvent for both said hydrophilic polymer and said polymer surface during application of said hydrophilic coating, said hydrophilic coating having a high degree of cross-linking or intermolecular mingling between said hydrophilic polymer and said polymer surface at said interfacing surface relative to said outer surface, said coating being substantially more slippery when wet than when dry and resistant to removal 17 wet abrasion.
8. An article having a lubricious hydrophilic coating, comprising an article having a polymer surface comprising polyurethane, and a lubricious hydrophilic coating comprising polyvinylpyrrolidone, said hydrophilic coating penetrating said polymer surface of said substrate via use of a cosolvent for both polyvinylpyrrolidone and polyurethane, said hydrophilic coating having an exposed outer surface and an interfacing surface with said polymer surface, said hydrophilic coating having a high degree of cross-linking or intermolecular mingling between the polyvinylpyrrolidone and polyurethane at said interfacing surface relative to said outer surface, said hydrophilic coating being substantially more slippery when wet than when dry, resistant to removal by wet abrasion, and essentially insoluble in aqueous solution, the degree of lubricity and resistance -33to wet removal being controlled in part by the particular cosolvent or cosolvent mixture used and the amount of cosolvent used.
9. A lubricious composite, comprising an outer layer having an exposed outer surface, said outer layer comprising a hydrophilic polymer selected from the group consisting of polyvinylpyrrolidone and polyvinylpyrrolidone-polyvinyl acetate copolymer, and a mixture of the above, an inner layer comprising a water-insoluble stabilizing polymer selected from the group consisting of a cellulose ester, a copolymer of polymethyl vinyl ether and maleic anhydride, an ester of the copolymer, nylon, and a mixture of any of the foregoing, said composite being substantially more slippery when wet than whey dry, resistant to removal by wet abrasion, and essentially insoluble in aqueous solution, the ratio of said hydrophilic polymer to said stabilizing polymer altering the degree of wet lubricity, resistance to removal and insolubility of said composite.
10. An article having the lubricious composite coating of claim 9. -3411. A coating substantially as hereinbefore described with reference to the Examples.
11.
12. An article substantially as hereinbefore described with reference to the Examples.
IE45791A 1991-02-12 1991-02-12 Lubricious hydrophilic coating, resistant to wet abrasion IE910457A1 (en)