HU220488B1 - Method for renewal of concrete installation - Google Patents
Method for renewal of concrete installation Download PDFInfo
- Publication number
- HU220488B1 HU220488B1 HU9502894A HU9502894A HU220488B1 HU 220488 B1 HU220488 B1 HU 220488B1 HU 9502894 A HU9502894 A HU 9502894A HU 9502894 A HU9502894 A HU 9502894A HU 220488 B1 HU220488 B1 HU 220488B1
- Authority
- HU
- Hungary
- Prior art keywords
- binder
- weight
- composition
- fibers
- additive
- Prior art date
Abstract
A találmány tárgya eljárás beton/vasbeton szerkezetű műtárgyakfelületének bevonására/felújítására. Jellemzője, hogy abevonandó/felújítandó felületet a laza, málló és letört részektől,továbbá a szennyeződésektől mechanikailag és kémiailag megtisztítják,a 2. igénypont szerinti készítmény összetevőiből a leírt receptúraalapján megfelelő konzisztenciájú habarcsot készítenek, majd azt kézivagy gépi módszerrel – az alkalmazott rétegvastagságtól és akompozíció konkrét összetételétől függően egy- vagy többrétegben – azelőkészített alapfelületre felhordják, majd utókezelik. A találmánytárgya továbbá készítmény az 1. igénypont szerinti eljárásfoganatosítására, amely polimerrel módosított, hidraulikus kötésűanyagkompozíció. Jellemzője, hogy – a kötőanyag a teljes keverék3,5–95 tömeg%-a, – az adalék anyag és adalék szer, a kész keverék0,01–25 tömeg%, – a kiegészítőanyag a kész keverék 0,001–1,2 tömeg%-a,– a keverővíz a kötőanyag tömegének 25–120 tömeg%-a, vagy – 1tömegegység kötőanyag, – 2–3,5 tömegegység kemény szemcsekeverék,előnyösen mosott osztályozott tűziszárított kvarchomok 0–0,5 mmszemcseösszetétellel, – 0,01–0,25 tömegegység adalék anyag és adalékszer, – 0,0014–0,07 tömegegység kiegészítőanyag, – 0,35–0,45tömegegység keverővíz. ŕThe subject of the invention is a method for coating/renovating the surface of concrete/reinforced concrete structures. It is characterized by the fact that the surface to be coated/renovated is cleaned mechanically and chemically from loose, worn and broken parts, as well as impurities, a mortar of suitable consistency is prepared from the ingredients of the preparation according to claim 2 based on the described recipe, and then it is applied manually or mechanically - depending on the thickness of the applied layer and the specific composition depending on its composition, in one or more layers - it is applied to the prepared base surface and then treated. The subject of the invention is also a preparation for implementing the process according to claim 1, which is a polymer-modified, hydraulic binder composition. It is characterized by the fact that – the binder is 3.5–95% by weight of the entire mixture, – the additive and additives, the finished mixture 0.01–25% by weight, – the supplementary material is 0.001–1.2% by weight of the finished mixture. a, – the mixing water is 25–120% by weight of the binder mass, or – 1 mass unit of binder, – 2–3.5 mass units of hard grain mixture, preferably washed classified fire-dried quartz sand with a grain composition of 0–0.5 mm, – 0.01–0, 25 mass units of additives and additives, – 0.0014–0.07 mass units of additional material, – 0.35–0.45 mass units of mixing water. ŕ
Description
A találmány tárgya eljárás és készítmény beton/vasbeton szerkezetű műtárgyak felületének bevonására/felújítására.The present invention relates to a method and composition for coating / reconstructing concrete / reinforced concrete structures.
A gyakorlatban előfordulnak olyan, elsősorban beton- és vasbeton szerkezetű műtárgyak például a szennyvízkezelésben, élelmiszeriparban, amelyek felületeit intenziven károsítják a technológiából származó különféle összetételű szennyvizek, illetve ezek bomlástermékéből táplálkozó és a műtárgy felületén megtelepedő baktériumok - kémiai, biológiai korrózió.In practice, there are structures, mainly concrete and reinforced concrete, for example in the wastewater treatment, food industry, whose surfaces are intensively damaged by the wastewater of various composition from the technology, and by bacterial, chemical, nutrient dwelling on the surface of the structure.
A technika mai állásánál ezeket a felületeket a szerkezet védelme érdekében különféle műgyanta kötésű szigetelőanyagokkal, műanyag vagy gumiburkolattal látják el.In the state of the art, these surfaces are provided with various resin-bonded insulating materials, plastic or rubber to protect the structure.
Ezen megoldások általában csak körülményesen használhatók, mivel a felhordásnál száraz alapfelület szükséges, több lépcsőben kell az anyagot használni, előírt várakozási idők betartásával. Az alapfelületnek magas mechanikai követelményeket kell kielégíteni. A kivitelezést befolyásolja, adott esetben meghiúsítja a nem megfelelő levegő- és alapfelületi hőmérséklet és nedvességtartalom. Ezeken kívül a hagyományos megoldások költségesek.These solutions are usually only to be used with great difficulty, as the application requires a dry substrate and the material has to be applied in several steps with the required waiting times. The substrate must meet high mechanical requirements. Execution is affected and, where appropriate, frustrated by inadequate air and substrate temperature and humidity. In addition, traditional solutions are expensive.
A HU 183 878 lajstromszámú „Eljárás vasbeton szerkezetek állagának megóvására, helyreállítására” című szabadalmi leírásban ismertetett megoldásnál kéziszerszámmal megtisztítják a műtárgy felületét, melyre ugyancsak kéziszerszámok segítségével meghatározott műgyantakeverékből (Epikote 828 és dietilén-triamin) vagy meghatározott márkájú és összetételű műgyantaréteget vagy meghatározott (Epikote 815 és poliamin) kvarchomokkal töltött epoxigyantát hordanak fel. A műgyanta-homok töltési arány 1:2,84. A védőréteg felhordása előtt a repedéseket kiinjektálják, valamilyen meg nem határozott gyantával.The solution described in patent application HU 183 878, entitled "Method for the preservation and restoration of reinforced concrete structures", cleans the surface of an artwork by hand, which is also made from a resin mixture (Epikote 828 and diethylene triamine) and polyamine) onto a quartz sand-filled epoxy resin. The resin-sand filling ratio is 1: 2.84. Before applying the protective layer, the cracks are grouted with some unspecified resin.
Eljárásunk szerint a felületbevonó réteg kötőanyaga polimerrel javított hidraulikus kötőanyag, ahol a polimer por alakú diszperzió és nem reaktív gyanta, különösen nem a megnevezett gyanta és térhálósító komponensek. A HU 183878 lajstromszámú eljárásban reaktív szintetikus műgyanták szerepelnek.According to our process, the binder for the coating layer is a polymer-enhanced hydraulic binder, wherein the polymer is a powder dispersion and a non-reactive resin, especially not the named resin and crosslinking components. Process HU 183878 discloses reactive synthetic resins.
Eljárásunkban nincs annak szerepe, hogy a felülettisztítást, majd a gyantából képzett réteget kézi vagy gépi módszerekkel hordják fel, szemben a vizsgált és ismertetett szabadalomban kizárólagosan leírt kézi módszer igényével.It does not play a role in the process that the surface cleaning and then the resin layer is applied by hand or machine, as opposed to the manual method exclusively described in the patent studied and described.
Célkitűzésünk egy olyan készítmény kifejlesztése, amely tulajdonságaiban hasonlít az alapszerkezet anyagára - például hidraulikus kötésű az alkalmazáskori hőmérsékleti és nedvességviszonyokra kevésbé érzékeny, biztosítja a gyengébb minőségű szerkezetek védelmét, nem érzékeny az alapszerkezet nedvességtartalmára.Our aim is to develop a composition that resembles the material of the base structure in properties - for example, it is hydraulically bonded less sensitive to application temperature and humidity conditions, provides protection of lower quality structures, and is insensitive to the moisture content of the base structure.
A felhordás technológiája egyszerűbb, kivitelezése olcsóbb legyen. Mindemellett a hagyományos betonnál nagyobb kémiai ellenállóképességgel rendelkezzen, elsősorban az alacsonyabb pH-tartományban. Legyen alkalmas a betonszerkezet védelmére és szigetelésére.Application technology is simpler and cheaper to implement. In addition, it should have greater chemical resistance than conventional concrete, especially in the lower pH range. It should be suitable for protecting and insulating the concrete structure.
Találmányunk szerinti készítmény azon a felismerésen alapul, hogy ha:The composition of the present invention is based on the recognition that:
- Kötőanyagból:- Of binder:
- hidraulikus kötőanyag - például spec. cement -, amely a következő fontosabb összetételijellemzőkkel rendelkezik:hydraulic binder - for example spec. cement - which has the following principal compositional characteristics:
- HM (hidraulikus modulus,- HM (hydraulic module,
Michelis szerint): 0,50-0,80Michelis): 0.50-0.80
- SM (szilikát modulus,- SM (silicate module,
Kühl szerint): 0,08-0,35Kuhl): 0.08-0.35
- AM (alumínium modulus): 2,00-9,00- AM (Aluminum Module): 2.00-9.00
- Adalék anyagból:- Of an additive:
- előnyösen por- és szennyeződésmentes kémiailag stabil és ellenálló, 50 mm alatti szemcseméretű szemcsés anyagkeverék, például kvarchomok, kavics, égetett kerámia, alkálimentes vulkáni kőzetőrlemény vagy az előzőek keverékei.preferably a dust-and-dirt-free chemically stable and resilient mixture of particulate matter having a particle size of less than 50 mm, such as quartz sand, gravel, burnt ceramic, alkali-free volcanic rock or mixtures of the foregoing.
- Adalék szerből:- Of an additive:
- a kötőanyag tulajdonságainak célszerű előnyös módosítására alkalmas anyagok - például kötésszabályozó, tapadásfokozó, vízháztartást befolyásoló szerek -, mint például: vízben diszpergált vagy rediszpergálható polimerek - például vinil-acetát, vinil-verzát, akril, akril-kopolimerek, természetes és mesterséges latexek, etilének, továbbá cellulózok, melamingyanta, nátrium-glukonát, nátrium-trifoszfát, lítium-karbonát stb.agents suitable for advantageously modifying the properties of the binder, such as binder regulators, tackifiers, water retention agents, such as: water-dispersible or redispersible polymers, such as vinyl acetate, vinyl pervate, acrylic, acrylic copolymers, natural and artificial latexes, , celluloses, melamine resin, sodium gluconate, sodium triphosphate, lithium carbonate and the like.
- Kiegészítőanyagból:- Of auxiliary materials:
- kémiailag ellenálló, szervetlen vagy szerves anyagú rostok, szálak, mint például üvegszál, szénszál, etilén-, poliészter-, polipropilénszálak vagy rostok.- chemically resistant, inorganic or organic fibers, fibers, such as glass fibers, carbon fibers, ethylene, polyester, polypropylene or fibers.
- Keverővízből, megfelelő konzisztenciájú habarcsot készítünk, úgy célkitűzésünk megvalósult.- We make mortar of appropriate consistency from mixing water, so our goal has been achieved.
Találmányunk tehát eljárás beton/vasbeton szerkezetű műtárgyak felületének bevonására/felújítására.Thus, the present invention is a process for coating / reconditioning concrete / reinforced concrete structures.
Jellemzője, hogy a bevonandó/felújítandó felületet a laza, málló és letört részektől, továbbá a szennyeződésektől mechanikailag és kémiailag megtisztítjuk, a találmány szerinti készítmény összetevőiből a leírt recepttára alapján megfelelő konzisztenciájú habarcsot készítünk, majd azt kézi vagy gépi módszerrel - az alkalmazott rétegvastagságtól és a kompozíció konkrét összetételétől függően egy- vagy többrétegben - az előkészített alapfelületre felhordjuk, majd utókezeljük.Typically, the surface to be coated / reconditioned is mechanically and chemically cleaned of loose, crumbling and broken parts, as well as contaminants, and the composition of the present invention is prepared according to the recipe described above and then manually or mechanically applied to the applied layer. Depending on the particular composition of the composition, it is applied in one or more layers to the prepared substrate and then cured.
Találmányunk továbbá készítmény beton/vasbeton szerkezetű műtárgyak felületének bevonására/felújítására, amely polimerrel módosított, hidraulikus kötésű anyagkompozíció.The present invention also provides a composition for coating / reconstructing concrete / reinforced concrete structures which is a polymer modified hydraulic bonded material composition.
Jellemzője, hogy:It is characterized by:
- a kötőanyag a teljes keverék 3,5-95 tömeg%-a,- the binder is from 3.5% to 95% by weight of the total mixture,
- az adalék anyag és adalék szer, a kész keverék 0,01-25 tömeg%,- additive and additive, 0.01-25% by weight of the final mixture,
- a kiegészítőanyag a kész keverék 0,001-1,2 tömeg%-a,- from 0.001 to 1.2% by weight of the final mixture,
- a keverővíz a kötőanyag tömegének 25-120 tömeg%-a, vagy25% to 120% by weight of the binder, or
- 1 tömegegység kötőanyag,- 1 mass of binder,
HU 220 488 BlHU 220 488 Bl
- 2-3,5 tömegegység adalék anyag- 2-3.5 parts by weight of additive
- 0,0,1 - 0,25 tömegegység adalék szer,- 0.0.1 to 0.25% by weight of additive,
- 0,0014-0,07 tömegegység kiegészítőanyag,- 0,0014-0,07 mass units of supplement,
- 0,35-0,45 tömegegység keverővíz.- 0.35-0.45 mass units of mixing water.
Előnyös megvalósítás, ha a:A preferred embodiment is:
Kötőanyaga:Cementing Material:
- hidraulikus kötőanyag - például spec. cement -, amely a következő fontosabb összetételi jellemzőkkel rendelkezik:hydraulic binder - for example spec. cement - which has the following principal compositional characteristics:
- HM (hidraulikus modulus,- HM (hydraulic module,
Michelis szerint): 0,50-0,80Michelis): 0.50-0.80
- SM (szilikát modulus,- SM (silicate module,
Kühl szerint): 0,08-0,35Kuhl): 0.08-0.35
- AM (alumínium modulus): 2,00-9,00- AM (Aluminum Module): 2.00-9.00
Adalékanyaga:Additive material:
- por- és szennyeződésmentes kémiailag stabil és ellenálló, 50 mm alatti szemcseméretű szemcsés anyagkeverék, például kvarchomok, kavics, égetett kerámia, alkálimentes vulkáni kőzetőrlemény (kemény szemcsekeverék), előnyösen mosott osztályozott tűziszáritott kvarchomok 0-0,5 mm szemcseösszetétellel, vagy az előzőek keverékei.- Dust and dirt-free chemically stable and resistant granular material with a particle size of less than 50 mm, such as quartz sand, gravel, calcined ceramic, alkali-free volcanic rock (hard granular mixture), preferably washed graded fire-dried quartz sand 0-0.5 mm granules, .
Adalékszere:Admixtures:
- a kötőanyag tulajdonságainak célszerű előnyös módosítására alkalmas anyagok - például kötésszabályozó, tapadásfokozó, vízháztartást befolyásoló szerek -, mint például: vízben diszpergált vagy rediszpergálható polimerek - például vinilacetát, vinil-verzát, akril, akril-kopolimerek, természetes és mesterséges latexek, etilének, továbbá cellulózok, melamingyanta, nátrium-glukonát, nátrium-trifoszfát, lítium-karbonát stb.agents suitable for advantageously modifying the properties of the binder, such as binder regulators, tackifiers, water-modifying agents, such as: water-dispersible or redispersible polymers, such as vinyl acetate, vinyl pervate, acrylic, acrylic copolymers, natural and artificial latexes, celluloses, melamine resin, sodium gluconate, sodium triphosphate, lithium carbonate and the like.
Kiegészítőanyaga:Additional material:
- kémiailag ellenálló, szervetlen vagy szerves anyagú rostok, szálak, mint például üvegszál, szénszál, etilén-, poliétersz-, polipropilénszálak vagy rostok.- chemically resistant, inorganic or organic fibers, fibers, such as glass fibers, carbon fibers, ethylene fibers, polyether fibers, polypropylene fibers or fibers.
A felhasználói igényeknek megfelelően a találmány szerinti készítményt az előzőekben leírt összetételnek megfelelően a következő példakénti receptek szerint javasoljuk összeállítani:According to the needs of the users, the composition according to the invention according to the composition described above is recommended to be prepared according to the following exemplary formulas:
1. példaExample 1
- 1 tömegegység kötőanyag: SECAR 51,- 1 mass of binder: SECAR 51,
- 2 tömegegység adalék anyag: 0-0,5 mm kvarchomok,- 2 parts by weight of additive: 0-0.5 mm quartz sand,
- 0,10 tömegegység adalék szer-keverék: (Dimetil-propandial, Tylose II20 P, Agitan P800, Vinnapas RE 545 Z),- 0.10 parts by weight of additive mixture: (Dimethylpropandial, Tylose II20 P, Agitan P800, Vinnapas RE 545 Z),
- 0,007 tömegegység kiegészítőanyag: MAVIFLOCKPH014,- 0,007 parts by weight of supplement: MAVIFLOCKPH014,
- 0,35 tömegegység keverővíz.- 0.35 mass units mixing water.
2. példaExample 2
- 1 tömegegység kötőanyag: CLF,- 1 weight unit binder: CLF,
- 2,5 tömegegység adalék anyag: 0-0,3 mm kvarchomok,- 2,5 parts by weight of additive: 0-0,3 mm quartz sand,
- 0,089 tömegegység adalék szer-keverék: (Dimetil-propandial, Tylose II 20 P, Agitan P800, Vinnapas RE 545 Z),- 0.089 parts by weight of additive mixture: (Dimethylpropandial, Tylose II 20 P, Agitan P800, Vinnapas RE 545 Z),
- 0,01 tömegegység kiegészítőanyag: Technocell 200,- 0,01 parts by weight supplement: Technocell 200,
- 0,4 tömegegység keverővíz.- 0.4 mass units mixing water.
3. példaExample 3
- 1 tömegegység kötőanyag: SECAR 51,- 1 mass of binder: SECAR 51,
- 2 tömegegység adalék anyag: 0-0,3 mm kvarchomok,- 2 parts by weight of additive: 0-0,3 mm quartz sand,
- 0,25 tömegegység adalék szer-keverék: (Dimetil-propandial, Tylose II20 P, Agitan P800, MowilithLDM 200 P Microsil),- 0.25 parts by weight of additive mixture: (Dimethylpropandial, Tylose II20 P, Agitan P800, MowilithLDM 200 P Microsil),
- 0,0014 tömegegység kiegészítőanyag: MAVIFLOCKPHO 14,- 0,0014 parts by weight of supplement: MAVIFLOCKPHO 14,
- 0,45 tömegegység keverővíz.- 0.45 weight units of mixing water.
A találmány szerinti eljárás során a bevonásra vagy a felújításra kijelölt felületet a laza, málló és letört részektől, továbbá a szennyeződésektől mechanikailag és kémiailag megtisztítjuk.In the process of the invention, the surface designated for coating or reconditioning is mechanically and chemically cleaned of loose, friable and broken parts, as well as dirt.
A találmány szerinti készítmény összetevőiből a leírt receptora alapján megfelelő konzisztenciájú habarcsot készítünk, majd azt kézi vagy gépi módszerrel az előkészített alapfelületre felhordjuk.The ingredients of the composition of the present invention are prepared according to the described receptor using a mortar of suitable consistency and then applied by hand or machine to the prepared substrate.
A felhordás az alkalmazott rétegvastagságtól és a kompozíció konkrét összetételétől függően egy- vagy többrétegű lehet.The application may be one or more layers depending on the layer thickness employed and the particular composition of the composition.
A frissen felhordott anyagot a környezeti körülményektől függően a szükséges ideig, előnyösen 1-7 napig nedvesítéssel vagy utókezelő szerrel óvni kell a gyors kiszáradástól.The freshly applied material, depending on the environmental conditions, should be protected from rapid drying for a sufficient period of time, preferably 1-7 days, by moistening or curing agent.
Az eljárás alkalmas profil és felületi hiányok pótlására is.The method is also suitable for correcting profile and surface imperfections.
Claims (5)