GB706251A - Improvements in the manufacture of lamellar pigments of ductile materials - Google Patents
Improvements in the manufacture of lamellar pigments of ductile materialsInfo
- Publication number
- GB706251A GB706251A GB1107/51A GB110751A GB706251A GB 706251 A GB706251 A GB 706251A GB 1107/51 A GB1107/51 A GB 1107/51A GB 110751 A GB110751 A GB 110751A GB 706251 A GB706251 A GB 706251A
- Authority
- GB
- United Kingdom
- Prior art keywords
- polythene
- roller mill
- aluminium
- fragments
- slurry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
Lamellar pigments of ductile material are made by dispersing fragments of the material in a liquid vehicle and introducing the resultant slurry into a roller mill (see Group II) in which it flows repeatedly between surfaces resiliently pressed together in rolling and non-rubbing contact. Suitable materials are aluminium, copper alloys, ferrous metals, stainless steel, lead, precious metals and thermoplastic resins such as polythene. The vehicle for metallic fragments may be benzene, toluene, white spirit or kerosene mixed with colza or castor oil or tallow, lanolin or beeswax. Wetting agents such as triethanolamine or arylethylsulphonates or stearic acid may be added. Polythene may be dispersed in aqueous emulsions of fats. The slurry may be recycled through the roller mill or may be fed through a series of mills in which the rollers have progressively smaller diameters. In an aluminium pigment made by the process in which the average diameter of the flakes is D and the thickness e , the ratio D 2/e exceeds 500 and the covering power is greater than 18,000 sq. cm. per gram.
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
FR706251X | 1950-01-17 |
Publications (1)
Publication Number | Publication Date |
---|---|
GB706251A true GB706251A (en) | 1954-03-24 |
Family
ID=9067654
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB1107/51A Expired GB706251A (en) | 1950-01-17 | 1951-01-15 | Improvements in the manufacture of lamellar pigments of ductile materials |
Country Status (1)
Country | Link |
---|---|
GB (1) | GB706251A (en) |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0305158A1 (en) * | 1987-08-25 | 1989-03-01 | Toyo Aluminium Kabushiki Kaisha | Aluminium flake pigment |
EP0451785A1 (en) * | 1990-04-11 | 1991-10-16 | Asahi Kasei Metals Limited | Aluminum pigment and process for production thereof |
EP1080810A1 (en) * | 1998-04-20 | 2001-03-07 | Asahi Kasei Metals Limited | Aluminum pigment |
-
1951
- 1951-01-15 GB GB1107/51A patent/GB706251A/en not_active Expired
Cited By (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0305158A1 (en) * | 1987-08-25 | 1989-03-01 | Toyo Aluminium Kabushiki Kaisha | Aluminium flake pigment |
JPS6454070A (en) * | 1987-08-25 | 1989-03-01 | Toyo Aluminium Kk | Aluminum flake pigment |
US4936913A (en) * | 1987-08-25 | 1990-06-26 | Toyo Aluminium Kabushiki Kaisha | Aluminum flake pigment |
USRE36911E (en) * | 1987-08-25 | 2000-10-17 | Toyo Aluminium Kabushiki Kaisha | Aluminum flake pigment |
EP0451785A1 (en) * | 1990-04-11 | 1991-10-16 | Asahi Kasei Metals Limited | Aluminum pigment and process for production thereof |
EP1080810A1 (en) * | 1998-04-20 | 2001-03-07 | Asahi Kasei Metals Limited | Aluminum pigment |
EP1080810A4 (en) * | 1998-04-20 | 2005-01-19 | Asahi Chemical Metals | Aluminum pigment |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US2002891A (en) | Bronze, bronze powders, and method of making the same | |
GB706251A (en) | Improvements in the manufacture of lamellar pigments of ductile materials | |
CN105036575A (en) | Steel slag powder grinding technology of two-section ball milling | |
US2080346A (en) | Metallic paint | |
US3099080A (en) | Method of converting metal powder into flake | |
GB1255172A (en) | Dispersion | |
US1920234A (en) | Method of producing aluminum bronze powder and lubricants therefor | |
CN115025875B (en) | Flotation separation method for copper-molybdenum bulk concentrate | |
US2528034A (en) | Mica-coated metallic paint pigments | |
DE942998C (en) | Process for the production of metals | |
EP0021465A1 (en) | Process for briquetting a material containing sponge iron | |
AT150970B (en) | Bronze paint and method of making it. | |
AT212286B (en) | Method and device for transferring solid, irregularly shaped ferro-silicon particles into spherical or spherical form | |
US53563A (en) | Improvement in the manufacture of bronze-powder | |
DE654147C (en) | Device for the production of fine flakes and red lead | |
CN105709910A (en) | Ore grinding optimization characterization method for cassiterite and polymetallic sulfide ore | |
RU1791001C (en) | Roller press | |
AT233271B (en) | Process for the production of aluminum powder | |
US585098A (en) | C omposition of matter for treating sheet metal | |
DE2146357A1 (en) | Removing cobalt and nickel from iron oxide ores - - by rouling the ore with liquid reducer | |
DE933883C (en) | Process for wet grinding of metal bronzes | |
US1240599A (en) | Flotation of minerals. | |
DE1190894B (en) | Process for spherizing irregularly shaped particles, especially heavy materials | |
Traveria et al. | The Characterisation of Red Spots on the Surface of Hot Rolled Steel Plate by XPS, XRD, SEM and EXDA | |
DE816628C (en) | Traction sheave chuck |