GB2582876A - Hybrid energy storage devices including support filaments

Info

Publication number: GB2582876A
Application number: GB2010385.9A
Authority: GB
Inventors: Rojeski Ronald
Original assignee: Traverse Technologies Corp
Current assignee: Traverse Technologies Corp
Priority date: 2012-07-03
Filing date: 2013-07-03
Publication date: 2020-10-07
Anticipated expiration: 2033-07-03
Also published as: JP6883129B2; GB2579719A; GB2579719B; KR20190112198A; JP2020021739A; GB201916678D0; GB201916680D0; GB2576656B; JP6883130B2; GB2579718B; JP6682693B2; GB2584377A; JP6894031B2; GB2579718A; JP6599485B2; JP2020129538A; GB202005587D0; GB2576655A; GB2581071B; JP6894030B2

Abstract

An electrode comprises a conductive substrate 105 and a material disposed on the substrate, the material comprising (i) carbon nanofibres 110; (ii) an intercalation material 1610 interspersed with the carbon nanofibres; (iii) a plurality of surface effect dominant sites provided by nanoparticles 1430, for catalysing intercalation of charge carriers into the intercalation material; and (iv) a binder 1140. The intercalation material may be coated on the carbon nanofibers (Figs 15, 18), and the nanoparticles may be concentrated on the surface of the intercalation material. The carbon nanofibres may be detached from the substrate and connected thereto via the binder (as shown), or may be directly connected to the substrate, preferably in an array of vertically aligned fibres (Fig 14). The intercalation material is preferably Si. The highly conductive and mechanically stable CNF core supporting a coaxially coated amorphous Si shell is claimed to have a higher theoretical specific capacity by forming a fully lithiated alloy. Addition of the surface effect dominant sites in close proximity to the intercalation medium results in a hybrid device that includes advantages of both batteries and capacitors.

Description

Intellectual Property Office Application No. 6132010385.9 RTM Date:29 July 2020 The following terms are registered trade marks and should be read as such wherever they occur in this document: Super P Intellectual Property Office is an operating name of the Patent Office www.gov.uk /ipo Hybrid Energy Storage Devices Including Support Filaments CROSS-REFERENCE TO RELATED APPLICATIONS 10011 This application is: a continuation-in-part of U.S. non-provisional patent application 13/779,409 tiled February 27, 2013; a continuation-in-pan of U.S. non-provisional patent application Ser. No. 13/725,969 tiled December 21, 2012; and claims benefit and priority to U.S. provisional patent applications: 61/667,876 filed Jul. 3, 2012, 61/677,317 filed Jul. 30, 2012, 61/806,819 filed March 29, 2013, and 61/752,437 filed Jan. 14, 2013.

This application is also related to U.S. non-provisional patent applications 13/779,472, 13/779,522, and 13/779,571 all filed on March 26, 2013.

10021 The disclosures of all the above provisional and non-provisional patent applications are hereby incorporated herein by reference.

BACKGROUND

10031 Field of the Invention

10041 The invention is in the field of energy storage devices, including but not limited to batteries, capacitors and fuel cells, 10051 Related Art [0061 Rechargeable lithium ion batteries are key elect icalenergy storage devices for power supply in portable electronics, power tools, and future electric vehicles. Improving the specific energy capacity, chargingidischar ing speed, and cycling lifetime is critical for their broader applications.

[0071 In current commercial Li-ion batteries,graphite or other carbonaceous materials are used as the anodes which have a theoretical capacity limit at 372 inAhig by forming fully ated LiC6 compound. In contrast, silicon has a much higher theoretical specific capacity of 4,200 mAhig by forming fully lithiated alloy Li4ASi. However, the large volume expansion of lithiated Si by up to -300-400% causes great structural stress that in the past inevitably lead to fractures and mechanical failure, which significantly limited the lifetime of prior art Si anodes.

SUMMARY

1008j In some embodiments, a power storage device includes a hybrid core-shell NW (nano-wire) architecture in a high-performance Li-ion anode by incorporating an array of vertically aligned carbon nanofibers (VACNFs) coaxially coated with a layer of amorphous silicon. The vertically aligned CNFs include multiwallcd carbon nanotubes (MWCNTs), which are optionally grown on a Cu substrate using a DC-biased plasma chemical vapor deposition (PECVD) process. The carbon nanolibers (CNTs) grown by this method can have a unique interior morphology distinguishing them from the hollow structure of common MWCNTs and conventional solid carbon nano fibers. One of the distinguishing characteristics is that these CNFs optionally consist of a series of bamboo-like nodes across the mostly hollow central channel. This microstructure can be attributed to a stack of conical graphitic cups discussed further elsewhere herein. In larger length scale, these PECVDgrown CNFs are typically uniformly aligned normal to the substrate surface and are well separated from each other. They may be without any entanglement or with minimal entanglement,and thus form a brush-like structure referred to as a VACNF array. The diameter of individual CNFs can be selected to provide desired mechanical strength so that the VACNF array is ust and can retain its integrity through Si deposition and wet electrochemical tests.

[0091 Various embodiments of the invention nclude types of support filaments other than VACINIFs. These support filaments can include, for example, nanowires, carbon sheets or other structures described herein. Other embodiments do not include any support filaments and use a binder instead.

[0010] Various embodiments of the invention nclude an energy storage system comprising a conductive substrate; a plurality of vertically aligned carbon nanofibers grown on the substrate, the carbon nanofibers including a plurality multi-walled carbon nanotubes; and an electrolyte including one or more charge carriers.

[00111 Various embodiments of the invention include an energy storage system comprising a conductive substrate; a plurality of vertically aligned carbon nanofibers grown on the substrate; and a layer of intercalation material disposed on the plurality of vertically aligned carbon nanofibers and configured to have a lithium ion storage capacity of between approximately 1,500 and 4,000 mAh per gram of intercalation material.

10012] Various embodiments of the invention include an energy storage system comprising a conductive substrate; a plurality of vertically aligned carbon nanofibers grown on the substrate; and a layer of intercalation material disposed on the plurality of vertically aligned carbon nanofibers and configured such that an ion storage capacity of the intercalation material is approximately the same at charging rates of IC and 3C.

100131 Various embodiments of the invention include a method of producing an energy storage device, the method comprising providing a substrate; growing carbon nano fibers on the substrate, the carbon nonolibers having a stacked-cone structure; and applying intercalation material to the carbon nanofibers, the intercalation material being configured foi intercalation of charge carriers.

100141 Various embodiments of the invention include an energy storage em comprising: an electrolyte including one or more charge ea e s conductive substrate; a plurality of vertically aligned support filaments attached to the substrate; intercalation material disposed on each of the support filaments and configured to reversibly adsorb members of the charge carriers within a bulk of the intercalation material: and a binder disposed on the intercalation material and including a plurality of nanoparticles, each of the nanoparticles being configured to provide surface effect dominant sites configured to adsorb members of the charge carriers via faradaic interactions on surfaces of the nanoparticles.

100151 Various embodiments of the invention include an energy storage system comprising: an electrolyte including one or more charge carriers; a conductive substrate; a plurality of support filaments attached to the substrate; intercalation material disposed on each of the support filaments and configured to reversibly adsorb members of the charge carriers within a hulk of the intercalation material; and a hinder disposed on the intercalation material and including a plurality of surface effect dominant sites configured to catalyze intercalation of the charge carriers into the intercalation material.

[00161 Various embodiments of the invention include an energy storage system comprising: an electrolyte including one or more charge carriers; a conductive substrate; intercalation material configured to reversibly adsorb members of the charge carriers within a bulk of the intercalation material; and a binder disposed on the intercalation material and including a plurality of nanoparticles, each of the nanoparticles being configured to provide surface effect dominant sites configured to donate electrons to members of the charge carriers via faradaic interactions on surfaces of the nanoparticles.

100171 Various embodiments of the invention include an energy storage system comprising: a cathode; and an anode separated from the cathode by an electrolyte including one or more charge carriers, the anode comprising, an intercalation material configured to intercalate the charge carriers and to donate electrons to the charge carriers at a first reaction potential, a plurality of nanoparticles including surface effect dominant sites configured to donate electrons to the charge carriers at a second reaction potential, a absolute difference between the first reaction potential and the second reaction potential being less than 2.4V.

[NM Various embodiments of the invention include a system comprising: means for establishing a potential gradient at an anode of a charge storage device, the anode including an electrolyte, a plurality of surface effect dominant sites, an intercalation material and a substrate; means for receiving a charge carrier of the electrolyte at one of the surface effect dominant sites; means for receiving an electron at the charge carrier from one of the surface effect dominant sites; and means for receiving a charge carrier at the intercalation material. [00191 Various embodiments of the invention include a method of producing an energy storage device, the method comprising: providing a conductive substrate; growing support filaments on the substrate; applying intercalation material to the support nanolibers, the intercalation material being configured for intercalation of charge carriers; and applying a plurality of surface effect dominant sites in close proximity to the intercalation material. 10020] Various embodiments of the invention include a method of producing an anode, the method comprising: providing a conductive substrate; mixing a binding material, surface effect dominant sites and intercalation material, the surface effect dominant sites being configured to accept electrons from charge carriers at a first reaction potential and the intercalation material being configured to accept the charge carriers or electrons from the charge carriers at a second reaction potential; and applying the binding material, surface effect dominant sites and intercalation material to the substrate.

[00211 Various embodiments of the invention include a method of producing an energy storage device, the method comprising: providing a conductive substrate; providing support filaments applying intercalation material to the support filaments, the intercalation material being configured for rcalation of charge carriers; and adding surfacesur ace effect dominant sites to the support filaments.

[00221 Various embodiments of the invention include a method of charging a charge storage device,the method comprising establishing a potential between a cathode and an anode of the charge storage device, the charge storage device including an electrolyte; receiving a first charge carrier of the electrolyte at a surface effect dominant te of the anode; transfe ng an electron of the anode to the first charge carrier; receiving a second charge carrier of the electrolyte at an intercalation material of the anode; and transferring an electron from the intercalation material to the second charge carrier.

[00231 Various embodiments of the invention include a method of charging a charge storage device, the method comprising: establishing a potential gradient at an anode of the charge storage device, the anode including an electrolyte, a plurality of nanoparticles having surface effect dominant sites, an intercalation material and a substrate; receiving a first charge carrier of the electrolyte at one of the surface effect dominant sites; transferring an electron to the first charge carrier from the one of the surface effect dominant sites; receiving a second charge carrier at the intercalation material of the anode; and transferring an electron from the intercalation material to the second charge carrier.

[00241 Various embodiments of the invention include an energy storage system comprising a conductive substrate; a carbon nanofiber, or other support filament, connected to the conductive substrate, the carbon nanofiber including a plurality of exposed nanoscale edges along the length of the carbon nanofiber; and an intercalation material configured to form a shell over at least part of the carbon nanofiber.

100251 Various embodiments of the invention include an energy storage system, such as a battery or electrode, comprising a conductive substrate; a carbon nanofiber, or other support filament, connected to the conductive substrate, the carbon nanofiber including a plurality of cup-like structures along the length of the carbon nanofiber; and an intercalation material configured to form a shell over at least part of the carbon nanofiber.

100261 Various embodiments of the invention include an energy storage system comprising a conductive substrate: a carbon nanofiber, or other support filament, connected to the conductive substrate; and an intercalation material configured to form a shell over at least part of the carbon nanofiber, the intercalation material being disposed in a feather-like structure along a length of the carbon nanofiber.

100271 Various embodiments of the invention include an energy storage system comprising a conductive substrate; a carbon nanofiber connected to the conductive substrate; and an intercalation material configured to form a shell over at least part of the carbon nanofiber, the intercalation material being configured such that expansion of the intercalation material is non-delaminating of the intercalation material from the carbon nanofiber.

100281 Various embodiments of the invention include29. A method of producing an energy storage device, the method comprising providing a conductive substrate; adding carbon nanofibers to the conductive substrate, the carbon nanofibers each including a plurality of exposed nanoscale edges along the length of the carbon nanofiber; and applying intercalation material to the carbon nanofibers, the intercalation material being configured for intercalation of charge carriers.

100291 Various embodiments of the invention include a method of producing an energy storage device, the method comprising providing a conductive substrate; adding carbon nanofibers to the conductive substrate, the carbon nanofibers each including a plurality of cup-like structures along the length of the carbon nanofiber; and applying intercalation material to the carbon nanofibers, the intercalation material ing configured for intercalation of charge carriers.

100301 Various embodiments of the invention include a method of producing an energy storage device, the method comprising providing a conductive substrate; adding carbon nanofibers to the conductive substrate; and applying intercalation material to the carbon nanofibers, the intercalation material being configured for intercalation of charge carriers, and the intercalation material being disposed in a feather-like structure along a length of the carbon nanotiber.

BRIEF DESCRIPTION OF THE DRAWINGS

[0031] FIGs. IA and I B illustrate a CNF array comprising a plurality of CNF grown on a substrate, according to various embodiments of the invention.

[0032] FIGs. 2A-2C illustrate a plurality of vertically aligned CNFs in different states, according to various embodiments of the invention.

[0033] FIGs. 3A-3C illustrate details of a CNF, according to various embodiments of the invention.

100341 FIG. 4 illustrates a schematic of the stacked-cone structure of a CNF, according to various embodiments of the invention.

[0035] FIGS. 5A-5C illustrate an electrochemical characterization of -3 um long CNFs, according to various embodiments of the invention.

[0036] FIGs. 6A-6C illustrates scanning electron microscopy images of 3µm long CNFs, according to various embodiments of the invention.

[0037] FTGs. 7A-7C illustrate results obtained using CNFs including a Si layer as Li-ion battery anodes, according to various embodiments of the invention.

[0038] FIG. 8 illustrates how the capacity of a CNF array varies with charging rate, according to various embodiment of the invention.

[0039] FIG. 9 illustrates Raman spectra of CNF arrays,according to various embodiments of the invention.

100401 FIGs. 10A-10C shows the variation of Li insertion--extraction capacities and the coulombic efficiency over 15 charge-d harge cycles, according to various embodiments of the 'invention.

10041] FIGS. 11A-I IC show scanning electron microscopy images of freshly prepared CNF arrays, according to various embodiments of the invention.

100421 FIG. 11D shows a cross-section of a nanotiber/silicon complex including more than one CNF.

100431 FIG. 12 illustrates a carbon nano-fiber array including fibers of 10 um in length, according to various embodiments of the invention.

[0044] FIG. 13 illustrates methods of producing CNF arrays and/or CNFs, according to various embodiments of the invention.

100451 FIG. 14A illustrates a CNF including a power enhancement material, according to various embodiments of the invention.

10046] FIG. 14B illustrates detail of the power enhancement material illustrated in FIG. 14A, according to various embodiments of the invention.

[00471 FIG. 14C illustrates alternative detail of the power enhancement material illustrated in FIG. 14A, according to various embodiments of the invention.

10048] FIG. 15 illustrates an electrode surface including a power enhancement material and non-aligned CNFs coated by intercalation material, according to various embodiments of the invention.

100491 FIG. 16 illustrates an electrode surface including power enhancement material, nonaligned CNFs and free intercalation material, according to various embodiments of the invention.

10050] FIG. 17 illustrates an electrode surface including intercalation material and power enhancement material, without CNFs, according to various embodiments of the invention. 100511 FIG. 18 illustrates an electrode surface including surface effect dominant sites disposed in close proximity to CNFs, according to various embodiments of the invention.

100521 FIGS. 19 and 20 illustrate electrode surfaces including surface effect dominant sites disposed in close proximity to free intercalation material, according to various embodiments of the invention.

[0(1531 FIG. 21 illustrates methods of assembling an electrode surface, according ous embodiments of the invention.

100541 FIG. 22 illustrates methods of operating a charge storage levice, according to various embodiments of the invention.

DETAILED DESCRIPTION

100551 FIGs. IA and 1B illustrate a CNF Array 100 comprising a plurality of CNF 110 grown on a conductive Substrate 105, according to various embodiments of the invention. In FIG. lA the CNF Array 100 is shown in the Li extracted (discharged) state and in FIG. 1B the CNF Array 100 is shown in the Li inserted (charged) state. The CNF 110 in these and other embodiments discussed herein are optionally vertically aligned. The CM^. 110 are grown on a Substrate 105 of Cu using a DC-biased plasma chemical vapor deposition (PECVD) process. As discussed above, the CNFs I I() grown by this method can have a unique morphology that includes a stack of conical graphitic structures similar to stacked cups or cones or a spiral. This creates a very fine structure that facilitates lithium intercalation. This structure is referred to here as the "stacked-cone" structure elsewhere herein. In larger length scale, these CNFs 110 are typically uniformly aligned normal to the substrate surface and are well separated from each other. The diameter of individual CNFs can be selected to provide desired mechanical strength so that the CINF Array 100 is robust and can retain its integrity through Si deposition and wet electrochemical cycles. A seed layer is optionally employed for growing CNFs 110 on Substrate 105. In use the CNF Array 100 is placed in contact with an Electrolyte 125, which can be a solid, or liquid, or a combination solid and liquid, and also including one or more charge carriers, snch as a lith um ion. The CNFs 110 are configured such that some of Electrolyte 125 is disposed between CNFs 110 and/or can ready Substrate 105 via gaps between CNFs 110.

10056] The diameter of individual CNFs l 10 illustrated in FIGs. lA and 18 are nominally between 100 and 200 nm, although diameters between 75 and 300 TIM, or other ranges are possible. CNFs 1 10 are optionally tapered along their length. The CNFs 110 produced using the techniques discussed herein have excellent electrical conductivity (cs =-2.5x105 Sim) along the axis and do form firm Ohmic contact with Substrate 105. The open space between the CNFs 110 enables a Silicon Layer 115 to be deposited onto each CNFs to form a gradually thinned coaxial shell with a mass at a Tip 120 of the CNF 110. This design enables the whole Silicon Layer 115 to be electrically connected through the CNF 110 and to remain fully active during charge-discharge cycling. The expansion that occurs on alloying of lithium with Silicon Layer 115 can be easily accommodated in the radial direction, e.g. perpendicular to the long dimension of the CNFs 110. The charge and discharge capacity and cycling stability of non-Si-coated CNFs 110 and Si-coated CNFs 110 can be compared. The addition of Silicon Layer 115 provided a remarkable Li' insertion (charge) capacity up to 3938 mAhlgsi at the C/2 rate and retained 1944 mAhlgs; after 110 cylces. This charge/discharge rate and the corresponding capacity are significantly higher than previous architectures using Si nanowires or hybrid Si-C nanostructures. FIGs. I A and 1B are perspective views.

10057] In various embodiments, from 0.01 up to 0.5, 1.0, 1.5, 2.5, 3.0, 4.0, 10, 20, 25 pm (or more) nominal Si thickness can be deposited onto 3 i.un long CNFs 110 to form CNF Arrays 100 such as those illustrated in Has IA and 113. Likewise, in various embodiments, from 0.01 up 0.5, 1.0, 1.5, 2,5, 3.0, 4.0, 10, 20, 25 pm (or more) nominal Si thickness can be deposited onto 10 pm long CNFs 110 to form CNF Arrays 100. In some embodiments he nominal thickness of Sis between 0.01 pin and the mean distance. between CNFs 110.

100581 Using CNF Arrays 100, Li ion storage with up to --4,000 mAh/g mass-specific capacity at C/2 rate is achieved. This capacity is significantly higher than those obtained with Si nanowires alone or other Si-nanostructured carbon hybrids at the same power rate. The improved performance is attributed to the fully activated Si shell due to effective charge collection by CNFs 110 and short Li path length in this hybrid architecture. Good cycling stability has been demonstrated in over 110 cycles. In various embodiments the storage capacity of Li ion storage of CNF Arrays 100 is approximately 750, 1500, 2000, 2500, 3000, 3500 or 4000 mAlt per gram of Si, or within any range between these values. As used herein, the term "nominal thickness" (of e.g., Si) is the amount of Si that would produce a flat layer of Si, of the said thickness, on Substrate 105. For example, a nominal thickness of Si of 1.0 um is an amount of Si that would result in a 1.0 jum thick layer of Si if deposited directly on Substrate 105, Nominal thickness is reported because it can easily he measured by weight using methods know in the art. A nominal thickness of 1.0 pm will result in a smaller thickness of Si Layer 115 on CNFs 110 because the Si is distributed over the greater area of the CNFs 110 surfaces.

100591 FIGs. 2A-2C illustrate CNF Array 100 having an average fiber length of approximately 3 um, according to various embodiments of the invention. FIGs. 2A-2C are scanning electron microscopy (SEM) images. FIG. 2A shows a plurality of vertically aligned CNFs 110 without Silicon Layer 115, FIG. 2B shows a plurality of vertically aligned CNFs 110 including Silicon Layer 115. FIG. 2C shows a plurality of vertically aligned CNFs 110 in the extracted (discharged) state after experiencing 100 lithium charge-discharge cycles. The CNFs 110 are firmly attached to a Cu Substrate 105 with essentially uniform vertical alignment and a random distribution on the surface of the substrate. The samples used in this study have an average areal density of 1.11x109 CNEs/cm2 (counted from top-view SEM images), corresponding o an average nearest -neighbor distance of -330 nm. The average length of the CNEs 110 in Figure -3.0 µm with >90% of CNFs in the range of 2.5 to 3.5 pm in length. The diameter spreads from -80 am to 240 mn with an average of -147 nm. An inverse teardrop shaped Ni catalyst at Tip 120 presents at the tip of each CNF 110 capping the hollow channel at the center of the CNF, which promoted the tip growth of CNF 110 during the PFCVD process, The size of the Ni catalyst nanoparticles defined the diameter of each CNFs 110. Longer CNFs 110, up to 10 am, were also employed in some studies to be discussed in Later sections.

(00601 In various embodiments the average nearest neighbor distance can vary between 200-450nm, 275-385 tun, 300-360nm, or the like. Further, the average length of the CNFs 110 can be between approximately 2-20, 20-40, 40-60, 60-80, 80-100, 100-120, 120-250 (p.m), or more. Standard carbon nanohbers as long as a millimeter long are known in the art. In various embodiments, the average diameter can vary between approximately 50-125, 100200, 125-175 (nm), or other ranges.

[0061] An amorphous Si Layer 115 was deposited onto the CNF Array 100 by magnetron sputtering. The open structure of brush-like CNF Arrays 100 made it possible for Si to reach deep down into the array and produce conformal structures between the CNFs 110. As a result, it formed a thick Si coaling at the CNF tip followed by a gradually thinned coaxial Si shell around the lower portion of the CNF, presenting an interesting tapered core-shell structure similar to a cotton swab. The amount of Si. deposition is characterized by the nominal thickness of Si films on a flat surface using a quartz crystal microbalance (QCM) during sputtering. The Li' insertion/extraction capacities were normalized to the total Si mass derived from the nominal thickness. At 0.50 rtm nominal thickness, the Si-coated CNFs 110 were well-separated from each other, forming an open core-shell CNF array structure (shown in FIG. 2B). This structure allowed electrolyte to freely accessing the entire surface of the Si Layer 115. In the embodiment illustrated the average tip diameter was -457 nm in comparison with the -147 nm average diameter of the CNFs 110 prior to application of the Si Layer 115. The average radial Si thickness at the Tip 120 was estimated to be -155 nm. This was apparently much smaller than the 0.50 tun nominal Si thickness since most Si spread along the full length of CNFs. Other radial Si thicknesses in the range of 10-1000, 20-500, 50-250, 100-200 (nm) or different ranges are found in alternative embodiments. As discussed elsewhere herein, the stacked-cone of CNFs 110 provides additional fine structure to the Si Layer 115. The stacked-cone structure is optionally the result of a spiral growth pattern that produces the stacked-cone structure when viewed in cross-section.

100621 The transmission electron microscopy (TEM) images in FIGs. 3A -3C further illustrate the structural details of Si-coated CNFs 110. A Si Layer 115 of -390 um Si was produced directly above the Tip 120 of a -210 nm diameter CNF 110. The largest portion of the cotton-swab-shaped Si Layer I t5 was -430 nm in diameter which appeared near the very end of the Tip 120. The coaxial Si Layer 115 around the CNF 110 showed a feather-like texture with modulated contrast, clearly different from the uniform Si deposits above the tip (see FIG. 3A). This is likely a result of the stacked-cone microstructure of the PECVD-grown Chi-Fs 110. It is known from the literature that such CNFs 110 include unevenly stacked cuplike graphitic structures along the CNF 110 center axis. The use of such variations in the diameter of CNFs 110 was previously disclosed in commonly owned U.S. Patent Application Ser. No. 12/904,113 filed Oct. 13, 2010.

[0063] The stacked-cone structure along the length of each CNF consists of one to five, five to fifteen, or more than ten cup-like graphitic layers that can be clearly seen in FIG. 313 as indicated by the dashed lines. At the edge of each stacked-cone the side edges of some of the graphitic layers are exposed. At these exposed edges lithium may be able to penetrate between the graphitic layers. At a molecular scale, the cup-like structures comprise cones of grapheme and/or graphitic sheets with which lithium can interact. The cup edges are nanoscale edges and can have the properties of graphene edges while between the graphitic layers may be found properties as between graphene sheets. The cup edges provide seems in the vertically aligned carbon nano-fibers through which lithium ions can migrate. The novel microstructure of the VACNFs generates stacks of exposed graphitic edges along the length of the CNF sidewall, e.g. the cup edges. These nanoscale edges are similar to the edges typically found on grapheme/graphitic sheets and ribbons. These exposed cup edges result in varied silicon nucleation rates and thus a modulated silicon shell texture is produced. These exposed edges also form a good interface between the VACNF core and the Si shell to facilitate fast electron transfer in this hybrid structure. The two different structures of the Si shell can be controlled by varying the growth process of the VACNFs. Areas of the VACNF that include the cup structure results in the feather like Si shell, while areas of the VACNF that do not include the cup structure have a Si structure similar to that observed at the tip of the VACNF. The VACNF is optionally configured to have one or more areas without the cup stacking structure along the length of the VACNFs as well as at the tip. In alternative embodiments, the carbon nano-fibers still include the cup stacking structure having exposed graphitic/grapheme or graphite edges but are not vertically aligned and/or even directly attached to the substrate. While the use of a "cup-stacking" graphitic microstructure is discussed elsewhere herein, other methods of producing exposed nanoscale edges of graphite sheets include unzipping carbon nanotubes using an acid. Exposed nanoscale edges produced expected to also provide advantages in terms of controlling and/or securing a Sishell and may be included in some embodiments. For example, the edges of graphite nanoscale ribbons can be used to influence the growth of a Si shell around these ribbons. f0064] As used herein, the term "nanofiber" is meant to include structure having at least two dimensions on the nanoscale (less than one micrometer). These include, for example, wires, tubes and ribbons in which a thickness and width are nanoscale but a length may or may not be nanoscale. The term nanofiber is meant to exclude graphene sheets which a thickness may be nanoscale but a length and width are both nanoscale. in various embodiments the support filaments discussed herein are nanofibers.

100651 The resolution and contrast of FIGs. 3B and 3C are limited since the electron beam needs to penetrate through hundreds of nanometer thick CNF or Si-CNF hybrid, but the structural characteristics are consistent with the high-resolution TEM studies using smaller CNFs in literature. This unique structure generated clusters of broken graphitic edges along the CNF sidewall which cause varied nucleation rates during Si deposition and thus modulate the density of the Si Layer 115 on the CNF 110 sidewall. The modulated density results in the ultra-high surface area Si structures indicated by a (100 run square) Box 310 in FIG 3A. The feather like Sistructures of Si Layer 115 provide an excellent Li ion interface that results in very high Li capacity and also fast electron transfer to CNF 110. In FIG. 3A the dark area at Tip 120 is Nickel catalyst for growth of the CNFs. Other catalysts can also be used. [00661 FIGS. 3B and 3C are images recorded before (3B) and after (3C) lithium intercalatiom'extraction cycles. The sample in 3C was in the delithiated (discharged) state when it was taken out of an electrochemical cell. The dashed lines in FIG. 3B are visual guidance of the stacked-cone graphic layers inside the CNFs 110. The long dashed lines in FIG. 3C represent the sidewall surface of the CNF 110.

100671 As discussed elsewhere herein, the stacked-cone structure of CNFs 110 is drastically different from commonly used carbon nanotubes (CNTs) or graphite. The stacked-cone structure results in improved Li' insertion, even 'ithout the addition of Si Layer 115, relative to standard carbon nanotubes or nanowires. For example, the stacked-cone graphitic structure of CNFs 110 allows Li-intercalation into the graphitic layers through the sidewall of CNFs 110 (rather than merely at the ends). The Li--transport path across the wall of each of GNPs 110 is very short (with D -290 rim in some e odin. )quite different from the long path from the open ends in conunonly used seamless carbon nanotubes (CNTs). FIG. 4 illustrates a schematic of the stacked-cone structure of CNFs 110. In this particular embodiment the average values of the parameters are: CNF radius rc r= 74 nm, CNF wall thickness ts = -50 mn, graphitic cone angle 0 = 100, and the graphitic cone length D isin0 = 290 urn.

[00681 FIGs. 5A-5C illustrate an electrochemical characterization of -3 pm long CNFs 110. This characterization illustrates the phenomenon described in relation to FIG 4. FIG. 5A shows cyclic voltammograms (CV) from 1.5 V to 0.001 V versus a Li/Li reference electrode at 0.1, 0.5 and 1.0 mV/s scan rates. A lithium disk was used as the counter electrode. Data were taken from the second cycle and normalized to the exposed geometric surface area. FIG. 5B shows the galvanostatic charge-discharge profiles at C/0.5, Cl and C/2 power rates, corresponding to current densities of 647, 323 and 162 mA/g (normalized to estimated carbon mass) or 71.0, 35.5 and 17.8 itAlcm2 (normalized to the geometric surface area), respectively. FIG. 5C shows intercalation and extraction capacities (to left vertical axis) and Coulombic efficiency (to right vertical axis) versus the cycle number at C/I charge-discharge rate. (The CR discharge rate = I hour, C/2 discharge rate = 120 min, 2C = C/0.5 -30 min, etc.) [00691 A freshly assembled half-cell typically showed the open circuit potential (OCP) of the uncoated CNFs 110 anode was -2.50 to 3.00 V vs. Li/Li reference electrode. The CVs measured between 0.001 V and 1.50 V show that Li' intercalation starts as the electropotential is below 1.20 V. The first cycle from OCP to 0.001 V involved the formation of a necessary protective layer, i.e. the solid electrolyte interphase (5E1), by the decomposition of solvent, salts, and impurities and thus presented a large cathodic current. Subsequent CVs showed smaller but more stable currents. The cathodic current associated with Li' intercalation rose slowly as the electrode potential was swept to negative until a sharp cathodic peak appeared at 0.18 V. As the electrode potential eversed to positive after reaching the low limit at 0,001 V, lithium extraction observed in the whole range up to 1.50 V, indicated by the continuous anodic current and a broad peak at 1.06 V. 1007111 The CV features of CNF arrays 100 were somewhat different from those of staged intercalation into graphite and slow Li.' diffusion into the hollow channel of CNTs. Li-ion insertion into CNFs 110 is likely through intercalation between graphitic layers from the sidewall due to its unique structure. The TENS image in FIG. 3C indicates that the graphitic stacks in the stacked-cones inside the CNF ll 0 are somewhat disrupted during Li' intercalation-extraction cycles, likely due to the large volume change that occurs on Li intercalation. Some debris and nanoparticles are observed as white objects inside CNFs 110 as well as at the exterior surface. These show penetration into the interior of the CNFs through the sidcwall.

[00711 The galvanostatic charge-discharge profiles in FIG. 5B showed that the Lid-storage capacity decreased as the power rate was increased from C/2 to C/0.5 (C/0.5 is also referred to as "2C"). To make it easier to compare the rates (particularly for those higher than C/1), we use the fractional notation C/0.5 herein instead of "2C" that is more popularly used in the literature. The Li intercalation and extraction capacities were normalized to the estimated mass of the CNFs 110 (L1 x 104 glcm2) that was calculated based on a hollow vertically aligned CNF structure with the following average parameters: length (3.0 um), density (1.1 x 109 CNFs per cm2), outer diameter (147 mu), and hollow inner diameter (49 nm, -1/3 of the outer diameter). The density of the solid graphitic wall of the CNFs 110 was assumed to be the same as graphite (2.2 glcm2). At the normal C/2 rate, the intercalation capacity was 430 mA h g71 and the extraction capacity is 390 tnA h both of which are slightly higher than the theoretical value of 372 mA h g for graphite, which may he attributed to SE1 forntation and the irreversible Li insertion into the hollow compartments inside the CNFs 110. The extraction capacities were found to be more than 90% of the intercalation values at all power rates and both the intercalation and extraction capacities decreased by -9% as the power rate increased from C/2 to C/1 and by -20% from C/1 to C/0.5, comparable to graphite anodes. [00721 Upon charge-discharge cycling, the intercalation capacity was found to slightly drop from 410 mA It g-1 to 370 inA. h g-1 after 20 cycles at the C/1 rate, while the extraction capacity was maintained between 375 and 355 mA1. The overall coulombic efficiency (i.e. the ratio of extraction capacity to intercalation capacity) was -94%, except in the first two cycles due to SEI formation on the CM', 110 surface. The SEI film is known to form readily on carbonaceous anodes during the initial cycles which allows lithium ion diffusion but is electrically insulating, leading to an increase in series resistance. The TEM image (FIG. 3C) and SEM image (FIG. 6A) show that a non-uniform thin film was deposited on the CNF 110 surface during charge-discharge cycles. In some embodiments, the SET serves as a sheath to increase the mechanical strength of the CNFs 110, preventing them from collapsing into mierobundles by the cohesive capillary force of a solvent as observed in the study with other polymer coatings.

[0073] FIGs. 6A-6C illustrates scanning electron microscopy images of 3 inn long CNFs 110, according to various embodiments of the invention. FIG. 6A shows CNFs 110 in delithiated (discharged) state after intercalation/extraction cycles. FIG. 6B shows CNFs 110 including Si Layer 115 after 100 cycles in the delithiated state. FIG. 6C shows CNFs 110 including Si Layer 115 after 100 cycles in the lithiated state. These images are 45 degree perspective views.

[00741 FIGS. 7A-7C illustrate results obtained using CNFs 110 including a SiLayer 115 as Li-ion battery anodes. These results were obtained using a nominal Si thickness of 0.50 um. FIG. 7A shows cyclic voltammograms between 1.5 V and 0.05 V versus Li/Li at 0.10, 0.50 and 1.0 mV s scan rates. The measurements were made after the sample going through 150 charge-discharge cycles and the data of the second cycle at each scan rate are shown. FIG. 7B shows galvanostatic charge-discharge profiles at C10.5, Cil and CC power rates with the sample at 120 cycles. All profiles were taken from the second cycle at each rate. FIG. 7C shows insertion and extraction capacities (to the left vertical axis) and coulombic efficiency (to the right vertical axis) of two CNF Arrays 100 (used as electrodes) versus the charge-discharge cycle number. The first CNF Array 100 was first conditioned with one cycle at the C110 rate, one cycle at the C15 rate, and two cycles at the C/2 rate. It was then tested at the C/2 insertion rate and C/5 extraction rate for the rest of the 96 cycles. The filled and open squares represent the insertion and extraction capacities, respectively. The second electrode was first conditioned with two cycles each at C/10, C/5, Ci2, C/1, C/0.5 and C/0.2 rates. It was subsequently tested at the C/1 rate for the next 88 cycles. The columbic efficiencies of both electrodes are represented by filled ( 1st electrode) and open (2nd electrode) diamonds, which mostly overlap at 99%.

100751 The CVs in FIG. 7A present very similar features to those of Si nano-wires. Compared to uncoated CNF Array 1E0, both the cathodic wave for Li insertion and the anodic wave for LF extraction shift to lower values (below -0.5 and 0.7 V, respectively). The peak current density increases by 10 to 30 times after application of Si Layer 115 and is directly proportional to the scan rate. Clearly, alloy-forming Li insertion into Si is much faster than intercalation into uncoated CNFs, which was limited by the slow diffusion of Li between graphitic layers. The cathodic peak at ---0.28 V was not observed in previous studies on pure Si nanowires. The three anodic peaks representing the transformation of die Li-Si alloy into amorphous Si are similar to those with Siianowires despite shifting to lower potentials by 100 to 200 mV.

100761 The galvanostatic charge-discharge profiles of a CNF Array including Si Layer 115, shown. in FIG. 7B included two remarkable features: (1) a high Li insertion (charge) and extraction (discharge) capacity of -3000 mA h (ged4 was obtained at the C/2 rate even after 120 cycles; and (2) the Lim capacity was nearly the same at the C/2, CIL and C/0.5 power rates. In other words, the capacity of CNF Army 100 to operate as an electrode did not decline when charging rates were increased from C/2 to C/1 and C/0.5. Over these charging rates the capacity was nearly independent of charging rate, in various embodiments. The total Li storage capacity of CNF Arrays 100 including Si Layer 115 was about 10 times greater than CNF Arrays 100 that lacked Si Layer 115. This occurred even though the low potential limit for the charging cycle was increased from 0.001 V to 0.050 V. As a result, the amount of Li intercalation into the CNF core appears to have been negligible. The specific capacity was calculated by dividing only the mass of Si that was calculated from the measured nominal thickness and a bulk density of 2.33 g cm-3. This method was chosen as an appropriate metric to compare the specific capacity of the Si Layer 115 to the theoretical value of bulk Si. For the 3.0 um long CNFs 110 deposited with a Si Layer 115 of 0.456 um nominal thickness, the real mass density of Si Layer 115 was -1.06 x 104 g aril', comparable to that of CNFs 110 (-1.1 x g crif2). The corresponding coulombic efficiency in FIG. 78 is greater than 99% at all three power rates, much higher than that of the CNFs 110 without Si Layer 115.

100771 FIG. 8 illustrates how the capacity of CNF Array 100 varies with charging rate, according to various embodiments of the invention. Data is shown for several numbers of cycles. FIG. 8 shows average specific discharge capacity for a group of cycles with identical current rates versus the charge rate (C-rate) required to itchieve full capacity in set hours (C/h e.g., full Capacity/hours). Vertical Lines are focused on C/4, IC, 3C and 8C. The CNF Array 100 was first conditioned with two cycles each at C/8, C/4, C/2, C/1, C/0.8, C/0.4, and C/0.16 rates srantnetrically, and subsequently tested at a Cl symmetric rate for the next 88 cycles. This a repeated from cycle 10 I to cycle 200. Starting at cycle 201, the electrode was cycled for five cycles at each of 7/4, C/3, Li72, C/1, C/0.75, C/0.66, (70.50, C/0.33, C/0.25, C/0.20 and C/0.1.5 rates symmetrically and subsequently tested at a C/1 symmetric rate for the next 45 cycles. This was repeated from cycle 301 to cycle 400 and from cycle 401 to cycle 500. The change in capacity is small (<16%) while the C-rate is varied by 32 fold. The electrode after 100 cycles showed increased capacity when the C-rate is changed from 3C to 8C. Thus, faster charge rates resulted in improved capacity. High capacity (>2,700 itnAhig) was obtained at both high. and lower rates (C/4 and 8C). Capacity at rates above 3C increase as C-rate increased. The drop in specific capacity with the number of cycles is due to known, correctable, factors.

[0078] Both the CVs and charge-discharge measurements indicated that the Li insertion into Si Layer 115 was fast and highly reversible, which are features desired for high-performance Li-ion battery anodes. This was further demonstrated (See FIG. 7C) with two long cycling tests on two identical samples at different testing conditions: (1) slow asymmetric tests with the C/2 rate for insertion and the C/5 rate for extraction; and (2) the fast symmetric test at the Cll rate for both insertion and extraction. Both sets of data showed >98% coulombic efficiency over the long cycling except for the initial conditioning cycles (4 cycles in the former and 12 cycles in the latter at varied low rates). In the slow asymmetric tests, the insertion capacity only dropped by 8.3% from 3643 mA h &Si at the 5th cycle to 3341 mA h at the 100th cycle. Even at the 01 charge-discharge rate, the insertion capacity only drops by 11% from 3096 mA h g i at the 13'h cycle to 2752 inA h g J at the 100th cycle. The difference in the Li apacity between these two sets of data was mostly attributable to the initial conditioning parameters and small sample-to-sample variations. This was indicated by the similar values of insertion-extraction capacity during the first few conditioning cycles in FIG. 7C at C/10 and C/5 rates. The faster rates (C/0.5 for 9th and 10th cycles and C/0.2 for Ilth and 121 cycles in sample 1 were found to be harmful and caused an irreversible drop in the capacity. However, the electrode became stabilized after longer cycling. As shown in FIG. 7B, the charge-discharge profiles are almost identical at C/2, and C/0.5 rates, which were measured with sample #1 after going through 120 cycles. This is over a charging rate variation of four times.

100791 The specific capacity of the Si Layer 115 in the range of 3000 to 3650 mA h 2[1 is consistent with the highest values of amorphous Si anodes summarized in literature. It is remarkable that the entire Si shell in the CNF Array 110 was active for Li+ insertion and remained nearly 90% of the capacity over 120 cycles, which to our knowledge has not been achieved before except with flat ultrathin (<50 am) Si films. The specific capacity disclosed herein is significantly higher than those reported using other nanostructured Si materials at similar power rates, including -2500 mA h g11 at the 02 rate and -2200 mA h g-1 at the Cil rate with Si NWs, and -800 mA h gr at the Cil rate with randomly oriented carbon nanofiber -Si core-shell NWs. Clearly, the coaxial core-shell NW structure on well-separated CNFs 110, such as included in various embodiments of the invention, provides an enhanced charge-discharge rate, nearly full LE storage capacity of Si, and a long cycle life, relative to the prior art.

100801 As shown in FIG. 7C, an anomalously high insertion capacity (4500 tit& h g') was always observed in the initial cycles, which was 20--30% higher than the latter cycles. In contrast, the extraction values were relatively stable over all cycles. The extra insertion capacity can be attributed to the combination of three irreversible reactions: (I) the formation of a thin SEH (surface electrolyte interphase) layer (of tens of nanometcrs); (2) reactions of Li with SiO" presented on the Si surface (SiO, -r 2xli -> Si + xLi1O); and (3) the conversion of the starting crystalline Si coating with a higher theoretical capacity (-4200 mA h g11) into amorphous Si with lower capacity (<3800 mA h g 1). The TEM. image (FIG. 3C) and SEW( image (FIG. 6B) showed that a non-uniform SEI can be deposited on the surface of Si Layer after the charge-discharge cycles. This elastic SET film can help secure Si Layer 115 on the CNF 110 surfaces as CNF Array 110 goes through the large volume expansion-contraction cycles that occur during the charge-discharge cycles. The dramatic difference between the SEN4 images in FIGs. 6B and 6C indicates the large expansion of Si Layer 115 in the lithiated (charged) state relative to the non-lithiated state. (Although some of the expansion may be due to oxidation of Li by air as the electrochemical cell was dissembled for imaging.) Note that the production of SEI during initial charge-discharge cycles causes the differences seen in Si Layer 115 between FIGs. 3A and 3B. In FIG. 3B the Si has interacted with electrolyte to produce SEI that fills the gaps between the feather-like structures. The interaction can include mixing, chemical reactions, charge coupling, encapsulation, and/or the like. The Si Layer 115, therefore, looks more uniform in FIG. 3B, However, the Si Layer 115 now comprises interleaved layers of Si (the feather-like strictures) and SEI. Each of these interleaved layers can be on the order of a few lOs of nanometers. The SEI layer can be an ion permeable material that is a product of interaction between the electrolyte and Si Layer 115 (or other electrode material).

100811 The crystalline and amorphous structure of the Si shell was revealed by Raman spectroscopy, As shown in FIG. 9, the pristine CNF Array 100 including Si Layer 115 showed multiple broad bands overlapped in the range of 350 to 550 eni] corresponding to amorphous Si, and a much higher sharp band at 480 cult corresponding to nanocrystalline Si. After charge-discharge tests, the sharp peak disappeared while the broad hands merged into a single peak at 470 cult. The bare CNFs 110 did not show any feature in this range. The crystalline Si peak downshifted by,-40 cm -1 from that measured with a single-crystalline Si(100) wafer and by -20 to 30 cu-t from other micro-crystalline Si materials. This shift was likely due to the much smaller crystal size and large disorders. The original Si Layer 115 likely consisted of nanocrystals embedded in an amorphous matrix associated with the feather-like TEM image in FIG. 3A. After initial cycles, the Sianocry, s als were converted into amorphous Si consistent with the TEM images after the cycling test (see FIGs. 3B and 3C). However, the Si Layer 115 apparently did not slide along the length of the CNF, in contrast to the large longitudinal expansion (by up to 100%) in pure Si NAVs. This indicates that, in some embodiments, expansion of the silicon is primarily radial rather than longitudinal with respect to the carbon nano-fiber. In some embodiments, expansion occurs between the feather-like structures of the Si. For example, the expansion of one feather may be in the direction of the nearest neighbor feathers above and below, thus filling the gap between the feathers. In either case, the expansion occurs in a manner such that delamination of the silicon is dramatically reduced relative to the prior art. Si Layer 115 was, thus, securely attached to CNFs 110 for over 120 cycles. The volume change of the Si shell during Li' insertion was dominated by radial expansion, while the CNF--Si interface remained intact. 100821 Various embodiments of the invention include CNFs 110 having different lengths and silicon shell thickness. One factor that can be controlled when CNFs 110 are generated is the open space between each CNF 110, e.g., the mean distance between CNFs 110 within CNF Array 100. This space allows Si Layer 115 to expand radially when charging and, thus in some embodiments provides stability. Because an optimum electrode structure depends on both the length of CNFs 110 and the thickness of Si Layer 115, it is sometimes desirable to use longer CNFs 110 and thicker Si Layers 115 in order to obtain higher total Li storage capacity. Longer CNFs 110 do correlate with greater storage capacity. FIGs 10A-10C shows the variation of Li' insertion extraction capacities and the coulombic efficiency over 15 charge-discharge cycles with three 10 tun long CNF 110 samples deposited with Si Layer 115 at a nominal thickness of 0.50, 1.5 and 4.0 um, respectively. After conditioning at the CIO rate for the first cycle and the C5 rate for the second cycle, asymmetric rates (C/2 for nsertion and C/5 for extraction) were used in subsequent cycles similar to the measurements of sample #1 ur FIG. 7C. This protocol provided nearly 100% eoul mbic efficiency and minimum degradation over the cycles. The nominal thickness was measured in situ with a quartz crystal microbalance during sputtering.

10083] The specific capacities as high as 3597 mA h g t and 3416 mA h g' were obtained with 0.50 and 1.5 itm thick Si Layer 115, respectively, very similar to that with 0.50 inn thick Si Layer 115 on 3.0 jun long CNFs 110 (see FIG. 7C). The capacity remained nearly constant over 15 cycles. However, the electrode with 4.0 pm nominal Si thickness showed a significantly lower specific capacity at only 2221 mA h This indicates that, with expansion, the Si Layers 115 from adjacent CNFs 110 began to contact into each other, limiting them from further expansion and limiting diffusion of Li between CNFs 110. As a result, only a fraction of the silicon coating was active in lithium insertion. The cycle stability was correspondingly worse than the samples with thinner Si Layers 115.

10084] The same amount of Si (500 nm nominal thickness) on CNF Arrays 110 comprising 10 pm long CNFs 110 gave nearly the same amount of Li' storage capacity (3597 mA h see Fig, 6a) as that of 3 pm long CNFs 110 (3643 mA h sec FIG. 7C), even though the carbon mass is more than 3 times higher. This is very strong evidence that the contribution of CNFs 110 is negligible in calculating Lit storage. it is likely that very little Li' ions were intercalated into CNFs 110 in the Si-coated sample, this contributes to the stability of the structure during multiple charge-discharge cycles.

(0085] The variation of the specific Li' storage capacity in the three samples correlated well with their structurca revealed by the SEM images illustrated in FIGS. 11A-1 IC. FIGS. 11 A-11C show scanning electron microscopy images of freshly prepared CNF Arrays 100 (on -10 pm long CNFs 110). The Si Layer 115 was generated using a nominal Si thickness of (a) 0.50 pm, (b) 1.5 jun, and c) 4.0 pm, which were measured in-situ using a quartz crystal microbalance during deposition. All images are 450 perspectivi, views. At 0.50 p.m nominal Si thickness, the average tip diameter was found to he -388 nm on the 10 um long CNFs, mach smaller than the -457 nm average diameter on the 3.0 pm long CNFs 110. The Si Layer 115 was thinner but more uniformly spread along the 10 pm long CNFs 110.

[00861 It is noted that growing 10 urn CNFs 110 took 120 min, about six times as long as growing the 3 pm CNFs 110. Some nickel catalysts were slowly etched by NH7 during the long PECVD process, resulting in continuous reduction in the Ni nanoparticle size and leading to the tapered Tip 120 (as shown in FIG. 12). The CNF 110 length variation also increased with long CNFs 110. These factors collectively reduced the shadow effects of the Tip 120. As a result, even at 1.5 urn nominal Si thickness, the CNFs 110 coated with Si Layer 115 are well separated from each other. The SEM image of 1.5 pm Si on 10 pm CNF Arrays 100 (FIG. 11B) is very similar that of 0.50 pm Si on 3.0 pin CNF Arrays 110 (FIG. 2B). But as the nominal Si thickness was increased to 4.0 pm, the Si Layers 115 clearly merged with each other and filled up most of the space between the CNFs 110 (see FIG. 10C). This reduced the free space needed to accommodate the volumetric expansion of the Si Layer 1151. As a result, the specific Li' storage capacity significantly dropped.

100871 FIGs. 11A and LIB each include roughly the same number of CNFs 110, however, FIG. 11B has substantially fewer visible Tips 120. This is because Si Layer 115 can form a nano-fiber/silicon complex that includes a single CNF 110 (a cross-section of which is shown in FIG. 1 A). Or, Si Layer 115 can form a naaofiber/silicon complex that includes two, three or more CNF 110 under a single cover of silicon. This occurs when two or more CNFs 110 come together during the Si Layer 115 deposition process. A nanofiher/silicon complex is a structure that includes a continuous Si Layer 115 that envelops one or more CNF 110. A cross-section of a nanofiber'silicon complex that includes two CNF 110 is illustrated iu FIG. 111/ In various embodiments at least 1%, 5% or 10% of nanofiber'silicon complexes include more than one CNF 110.

100881 In various embodiments, instances of CNF Arrays 100 having 0.50 and 1.5 pm nominal Si thicknesses have comparable mass-specific capacities of 3208 343 and 3212 it--234 mA h g 1, respectively. The samples with a 4.0 pm nominal Si thickness give much lower capacity at 2072 ± 298 mA h g-1. The thinner Si coatings are fully activated and provide the maximum Li insertion capacity that amorphous Si could afford. On the other hand, the area-specific capacity increases proportionally with the Si thickness from 0.373 ± 0.040 mA h enf at 0.50 pm Si to 1.12 ± 0.08 mA h c -at 1.5 prn Si thickness, but drops off from the linear curve to give 1.93 (e, 0.28 mA h cm -at 4.0 pin nominal Si thickness. At the 4.0 micrometer nominal silicon thickness, only a fraction of the extra silicon in the thick Si coating is actively involved in Li storage. The thickness of 4.0 pm is greater than the mean distance between CNFs 110. The electrochemical results are consistent with the structure shown in SEM image in FIG. 11C, which shows that space between CNFs 110 is essentially filled.

[00891 In various embodiments of the invention, the structure of CNF Array 100 includes an Si Layer of approximately 200 to 300 nm radial thickness on CNFs 110 having a length of approximately 30-40, 40-75, 75-125 microns (or more or combinations thereof) and diameters on the order of -50 mu In some embodiments, these CNF Array 100 are grown on conductive foils having a thickness within the ranges of-10 microns, -10-20 microns, -1050 microns, or more. In various embodiments, Si (equivalent to 1.5 um nominal thickness on a flat surface) is deposited onto 10 pm long CNFs 100 to form CNF Arrays 100. This is accomplished while maintain the open vertical core-shell nanowire ucture with individual CNFs 110 well separated from each other such that Li ions can penetrate the CNF Arrays 100 between the CNFs 110. This unique hybrid architecture allowed the Si Layers 115 to freely expandicontract in the radial direction during Li+ insertion and extraction. High-performance Li storage with a mass-specific capacity of 3000 to 3650 mA h tiT1 was obtained even at the Cl rate. The capacity matched the maximum value that would be expected froth a similar mass of amorphous Si, ndicating that the Si Layer [15 was fully active. This 3D nanostructured architecture enables effective electrical connection with bulk quantities of Si material while maintaining a short Li+ insertion-extraction path. As a result, high capacity near the theoretical limit is possible for over 120 charge-discharge cycle. There was little change in capacity as the rate was increased 20 times from C/10 to C/0.5 (or 2C). The high capacity at significantly improved charging and power rates and the extraordinary cycle stability make this novel structure a choice anode material for high-performance Li-ion batteries. The same core-shell concept may be applied to cathode materials by replacing the Si shell with Tith, LiCo02, LiNi02, LiNrIns04, LiFePO4, LTA), Li202, or the like.

[00901 FIG. 13 illustrates methods of producing the CNF Arrays 100 and/or CNFs 110 disclosed herein. In a Provide Substrate Step 1310 a Substrate 105 is provided. Substrate 105 is optionally suitable for growth of CNFs 110. Substrate 105 may include a variety of materials, for example Cu. Substrate 105 is optionally a conductive foil having a thickness described elsewhere herein. In an optional Provide Nucleation Sites Step 1320 nucleation cites for the growth of CNFs 110 are provided on Substrate 105. A variety of nucleation materials, such as Ni particles, are known in the art. The nucleation cites are optionally provided at a density so as to produce mean distances between CNFs 110, such as those taught elsewhere herein. Provide Nucleation Sites Step 1320 is optional in embodiments in which nucleation is not required for growth of CNFs 110, or similar structures, or in which CNFs 110 are attached to Substrate 105 using a binder alter being grown elsewhere. 1009Ij In a Grow CNFs Step 1330 CNI2s 110 are grown on Substrate 105 or, in some embodiments separate from Substrate 105. The CNFs 110 are optionally grown to produce the stacked-cone structure taught elsewhere herein, to produce structures having exposed graphitic edges along their length, or to produce ni tarty variable structure. The CNFs 110 can be grown to any of the lengths taught elsewhere herein. Growth is ptionally accomplished using PECVD processes such as those taught or cited in "A high-performance lithium-ion battery anode based on the core-shell heterostructure of silicon-coated vertically aligned carbon nandfibers" Klankowski et al. .T. Mater. Chem. A, 2013, I, 1055.

[0092] In an Apply Si Layer Step 1340 an intercalation material such as Si Layer 115 is applied to the grown CNFs 110. In some embodiments, Apply Si Layer Step 1340 occurs before CNFs 110 are attached to Substrate 105, The applied material may have any of the nominal thicknesses taught elsewhere herein so as to produce a Si Layer 115 thickness of tens or hundreds of nanometers. In some embodiments, Apply Si Layer Step 1340 includes growing intercalation material in structures that are dependent on exposed edges along the lengths of CNFs 110. For example, when CNFs 110 include the cup-like structure discussed herein, Apply Si Layer Step 1340 includes growing the feather-like structures illustrated in the figures, e.g. FIG 3A..

[0093] In an optional Apply PEM Step 1345 a power enhancement material (PEM) is added to the CNF Array100 or CNFs 110. In some embodiments, Apply PEM Step 1345 occurs before CNFs 110 are attached to Substrate 105. The PEM typically includes a binder and surface effect dominant sites, as discussed in further detail elsewhere herein. In an optional Condition Step 1350 the CNF Array 100 produced using Steps 1310-1340 is conditioned using one or more lithium intercalation cycles.

100941 FIG. 14A illustrates a CNF 110 including a Power Enhancement Material 1320, according to various embodiments of the invention. The Power Enhancement Material 1320 is applied as a layer over the intercalation material, e.g. over Silicon Layer 115. FIG. 14B illustrates detail of the Power Enhancement Material 1320 illustrated in FIG. 14B, according to various embodiments of the invention. Power Enhancement Material 1320 includes Surface Effect Dominant Sites 1430 and an optional Binder 1440. Silicon Layer 115 is but one example of intercalation material. Where Silicon Layer 115 is used as an example herein, it should be understood that other types of intercalation material can be substituted or combined with silicon. Such alternative or additional intercalation materials include Ag, Al, Bi, C, Se, Sb, Sn and Zn. The CNF 110 illustrated in FIG. 14 is typically one of a large number of CNF 110 within a CNF Array 100.

[0095] In some embodiments, Surface Effect Dominant Sites 1430 include surfaces of a nanoparticle configured to adsorb charge carriers in a faradaic interaction, e.g., to undergo redox reactions with charge carriers. They arc referred to as "surface effect dominant" because typically, for these nanoparticles, the faradaic interaction between the charge carriers and the nanoparticle surfaces dominate bulk faradaic interactions. Thus, the charge carriers arc much more likely to react at the surface relative to the bulk of the nanoparticles. For example, a lithium ion would more likely adsorb onto the surface of the nanoparticle rather than being absorbed into the bulk of the nanoparticle. These nanoparticle are sometimes referred to as surface redox particles. The faradaic interaction results in a pseudo capacitor that can store a significant amount of loosely bound charge and thus provide a significant power density. In pseudo capacitance an electron is exchanged (e.g., donated). In this case between the charge carrier to the nanoparticle. While some potentials would result in some intercalation of charge carrier into the nanoparticle, this does not constitute the bulk of the interaction at Surface Effect Dominant Sites 1430 and can degrade some types of nanoparticles. A laradaie interaction is an interaction in which a charge is transferred (e.g., donated) as a result of an electrochemical interaction.

[0961 The nanoparticles that include Surface Effect Dominant Sites 1430 can be comprised of transition 1 oxides, such as TiO2, Va205, MnO, Mn02, NiO, tantalum oxide, ruthenium oxide, rubidium oxide, tin oxide, cobalt oxide, nickel oxide, copper oxide, iron oxide, and/or the like, They may also be comprised of metal nitrides, carbon, activated carbon. graphen phite, titanate (L14Ti501)), crystalline silicon,germanium, melt hydrides, iron phosphates, polyaniline, mesophase carbon, and/or the like. It is appreciated that mixtures of the above and/or other materials having desired faradaic properties may he included in the Surface Effect Dominant Sites 1430. In various embodiments, these nanoparticles can be less than 1, 2, 3, 5, 8, 13, 21 or 34 nanometers in diameter. The lower limit of the nanoparticle size is a function of the size of the molecules of constituent materials. A nanoparticle includes at least a few molecules. A smaller size provides for a greater surface to bulk ratio of possible adsorption sites. However, a particle comprising only a couple of molecules has reduced stability. The nanoparticles are optionally multi-layered. For example, they can comprise a TiO2 layer (or any of the other nanoparticle materials discussed herein) on a transition metal, Co, Ni, Mn, Ta, Ru, Rb, Ti, Sn, V2.02, FeO, Cu or Fe core or a graphene/graphite layer on a core of some other material. In some embodiments, different core materials affect the reaction potentials of the surface material. The amount of Surface Effect Dominant Sites 1430 is optionally selected depending on desired power and energy densities. For example, a greater power density may be achieved by have a larger number of Surface Effect Dominant Sites 1430 per quantity of intercalation material, or a greater amount of energy density may be achieved by having a larger amount of intercalation material per number of Surface Effect Dominant Sites 1430. It is an advantage of some embodiments of the invention that both historically high energy and power density can be achieved simultaneously.

10097] By adsorbing charge carriers on the surface of the nanoparticle the charge carriers can provide a power density such as previously only achieved with capacitors. This is because the release of the harge is not dependent on diffusion of charge carriers though. an intercalation material. Further, by placing the Surface Effect Dominant Sites 1430 in close proximity to the intercalation material, charge carriers can move from the intercalation I to the Surface Effect Dominant Sites 1430 (or directly to the electrolyte). This results in energy densities that are equal to or greater than conventional batteries. Both the energy densities f batteries and the power densities of capacitors are achieved in the same device. Note that during discharge charge carriers within the intercalation material can migrate to the Surface Effect Dominate Sites 1430 and thus recharge these sites.

[00981 In some embodiments, Surface Effect Dominant Sites 1430 are disposed on larger particles. For example, the particle size may be greater than 1. 10, 25, 100 or 250 microns, (hut generally less than 1 millimeter). Activated carbon, graphite and graphcne are materials that can he included in particles of these sizes. For example, activated carbon can he included in Power Enhancement Material 1320 while having a pore size of Surface Effect Dominant Sites 1430 similar to the nanoparticic diameters taught above. For the purposes of this disclosure, a nanoparticle is a particle with an average diameter of less than 1 1.1m. 100991 Optional Binder 1440 is configured to keep the Surface Effect Dominant Sites 1430 in proximity to the intercalation material. In some embodiments, the distribution of Surface Effect Dominant Sites 1430 is uniform throughout Binder 1440, For example, nanoparticles including the Surface Effect Dominant Sites 1430 may be mixed with Binder 1440 before Binder1440 is applied to the intercalation material to produce a relatively uniform distribution. Alternatively, the nanoparticles may be applied to the surface of the intercalation material prior to application of Binder 1440. This can result in a greater concentration of Surface Effect Dominant Sites 1430 (within Binder 1440) proximate to the intercalation material as compared to areas of Binder 1440 that are distal to the intercalation material. Binder 1440 is optional in embodiments in which Surface Effect Dominant Sites 1430 or the associated nanoparticles are directly attached to the intercalation material, e.g., attached to Silicon Layer 115.

1001001 Binder 1440 is permeable (e.g,, porous) to charge carriers of the electrolyte. Examples of suitable materials for Binder 1440 include poiyvinyTidene fluoride (PVDF), styrene butadiene rubber, poly (acrylic acid) (PAA), carbo-xymethyl-cellulose (CMC), and/or the like. Other binders may be used that meet the permeability requirements.

Binder 1440 optionally includes materials that ase its conductivity. For example, Binder 1440 may include conductive polymer, graphite, graphene, metal nanoparticles, carbon nano-tubes, carbon nano fibers, metal nano-wires, Super-P (conductive carbon black), and/or the like. The materials are preferably at concentrations high enough to make Binder 1440 conductive, e.g., a percolation threshold.

1001011 The addition of Surface Effect Dominant Sites 1430 in close proximity to the intercalation material (e.g., Silicon Layer 115) does not necessarily require the use of vertically aligned CNF 110, or any support filaments. For example, FIG. 15 illustrates an electrode surface including Power Enhancement Material 1320 and non-aligned CNTs 110 coated by intercalation material, according to various embodiments of the invention. In these embodiments, the GM's 110 are not directly attached to Substrate 110, but are held in close proximity to Substrate 110 by Binder 1440. In some embodiments, CNFs 110 including the cup like structure illustrated in for example, FIG. 3B, arc used in the non-attached configurations, such as illustrated in FIG. 15. In these embodiments, the cuplike structure still helps to prevent delamination of the silicon from the underlying CNF 110. While CNF 110 are used herein as an example of support filaments, it should be understood that other types of support filaments discussed herein can be used to supplement or replace the carbon nanofibers of CNF 110 in any of the examples.

100102] The embodiments illustrated by FIG. 15 can be produced, for example, by first growing unattached CNFs 110. These are then coated with Silicon Layer 115 (or some other intercalation material) such that the intercalation material is generally in contact with the CNFs 110 as a coating layer. The coated CNFs 110 are then mixed with Surface Effect Dominant Sites 1430 and Binder 1440. Finally, the resulting mixture is deposited on Substrate 105.

[001031 FIG. 16 illustrates an electrode surface including Power Enhancement Material 1320, non-aligned CNFs 110 and free Intercalation Material 1610, according to various embodiments of the invention. In these embodiments, the Intercalation Material 1610 is not necessarily disposed around the CNF 110 as a coating. The Intercalation Material 1610 is free in the sense that it is not restricted to the surface of CNFs 110, however it is still held in proximity to Substrate 105 by Binder 1440.

[001041 The embodiments illustrated in FIG. 16 can be produced, for example, by mixing Binder 1440, Surface Effect Dominant Sites 1430, Intercalation Material 1610 and CNF 110 together (in any order). The mixture is then applied to Substrate 105. In these embodiments, CNFs 110 may or may not be attached to Substrate 105 by means other than Binder 1440. Intercalation Material 1610 may and/or may not be in contact with CNF 110 or Substrate 105. Likewise, Surface Effect Dominant Sites 1430 are optionally in contact with Substrate 105, CNF 110, and/or Intercalation Material 1610. Intercalation Material 1610 optionally includes particles, suspensions, clusters, and/or droplets of intercalation material with sizes of at least 0.1, 0.6, 1, 1.5, 2, 3,5, 7, 9, 10, 13, 15, 18, 21 or 29 tim or any range there between. Other sizes are possible in alternative embodiments.

[00105] FIG. 17 illustrates an electrode surface including Binder 1440, Surface Effect Dominant Sites 1430 and Intercalation Material 1610, without support i laments, according to various nbodiments of the invention_ In these embodiments Surface Effect Dominant Sites 1430 and Intercalation Material 1610 are held in proximity to Substrate 11005 by Binder 1440.

[001061 FIG. 18 illustrates an electrode surface similar to that illustrated in FIG 15. However, ut the embodiments illustrated by FIG. 18 Surface Effect Dominant Sites 1430 are concentrated in close proximity to Intercalation Material 1610 For example, in some embodiments at least 2%. 0% 25%, 50%, 75% or 85% of Surface Effect Dominant Sites 1430 are on particles in contact with Intercalation Material 1610. Increased concentration of Surface Effect Dominant Sites 1430 proximate to Intercalation Material 1610 can be achieved using methods described elsewhere herein, This results in a greater concentration of Surface Effect Dominant Sites 1430 at the surface of Intercalation Material 1610 relative to other volumes within Binder 1440.

1001071 FIGs. 14C, 19 and 20 illustrate an electrode surface similar to that illustrated in FIGs. 14B, 16 and 17 respectively. However, in the embodiments illustrated by these figures, Surface Effect Dominant Sites 1430 are disposed in close proximity to free intercalation material, according to various embodiments of the invention. As in the embodiments illustrated by FIG. 18, in some embodiments at least 2%. 10%, 25%, 50%, 75% or 85% of Surface Effect Dominant Sites 1430 are in contact with Intercalation Material 1610. In some embodiments a higher concentration of nanoparticles including Surface Effect Dominant Sites 1430 are disposed within 5 nanometers of Intercalation Material 1610 surfaces than between 10 and 15 nanometers of these surfaces. Increased concentration of Surface Effect Dominant Sites 1430 proximate to Intercalation Material 1610 can he achieved by selecting appropriate Zeta potentials of the nanoparticles and Intercalation Material 1610 in solution so that the nanoparticles form an electrostatic double layer at the surface of Intercalation Material 1610. The Zeta potential is the electric potential in the nerfacial double layer at the location of the surface versus a point in the bulk liquid away from the surface. The Zeta potential is optionally greater than 25 mV (absolute). In other embodiments, the nanoparticles are applied to the surfaces of Intercalation Material 1610 prior to the application of Binder L440.

10011181 Intercalation Material 1610, as illustrated in FIGS. 16-20, can include any single one or combination of the materials discussed herein with respect to Silicon Layer 115 (including or excluding silicon). Likewise, CNFs 110, as illustrated in FIGS. 16-20, can include any single one or combination of the various types fibers discussed here (including or excluding carbon anofibers). For example, these CNEs 110 may include branched fibers, multi-walled fibers, wires, aerogel, graphite, carbon, graphene, boron-nitride nanotubes. etc. The number of Surface Effect Dominant Sites 1430 and CNF 110 shown in these figures and other figures herein is for illustrative purposes only. For example, in practice the number of Surface Effect Dominant Sites 1430 can be much greater. Likewise, the amount and size of Intercalation Material 1610 and Silicon Layer 115 shown is for illustrative purposes. Alternative embodiments may include greater or lesser amounts and greater or lesser sizes. Likewise, the depth of EEM 1420 and the length of CNF 1 10 can vary from that shown in the figures.

[00109] In various embodiments, the amount of nanoparticles including Surface Effect Dominant Sites 1430 may be selected to so as to result in at least 0.1, 0.5, 0.7, 0.9, 1.1, 1.3, 1.5, 2, 3, 5, 10, 25, 50 or 100 (or any range there between) times a monolayer of the nanoparticles on the surface of Intercalation Material 1610 or Silicon Layer 115 (as measured in a discharged state). As used herein, a 0.1 monolayer indicates 10% and a 10x monolayer is 10 monolayers. In various embodiments, the amount of nanoparticles including Surface Effect Dominant Sites 1430 may he selected to result in at least 1, 5, 10, 20, 50, 100, 250 or 500 manometer layer (or any combination there between) of nanoparticles on the surface of Intercalation Material 1610 (as measured in a discharged state). Other coverage densities as measured in onolayers or depth are possible. As the coverage of the nanoparticles (that include Surface Effect Dominant Sites 1430) approaches 1.0 monolayer the nanoparticles can form a layer between the Intercalation Material 1610 and charge carriers le electrolyte that migrate through Binder 1440. For example in some embodiments the electrolyte includes lithium as a charge carrier. The lithium can migrate through Binder 1440 and undergo a faradaie reaction with Surface Effect Dominant Sites 1430 in which an electron is donated to the lithium from one of Surface Effect Dominant Sites 1430. This electron has been transferred (e.g., donated) from Substrate 105 to the nanopartiele via Intercalation Material 1610. Because the nanoparticles iftirm a barrier, at this stage in a charging process, only a limited amount of charge carrier reaches Intercalation Material 1610. Charging is dominated by reactions at the Surface Effect Dominant Sites 1430. In some embodiments, charging can be rapid because intercalation of the charge carrier into Intercalation Material 1610 is not necessary before the faradaic reaction with the charge carrier occurs. The presence of Surface Effect Dominant Sites 1430 greatly increases the surface area where the initial faradaic reaction can occur prior to intercalation. Surface Effect Dominant Sites 1430 catalyze the intercalation of charge carrier into Intercalation Material 1610. The charge carrier can be intercalated in the form as received at Surface Effect Dominant Sites 1430 or intercalated in an alternate form such as a metal oxide. If intercalated as a metal oxide, the oxygen of the oxide may be recycled back to the Surface Effect Dominant Site 1430 following the intercalation.

100110) In some embodiments, because the nanoparticles form an imperfect barrier some charge carriers still reach Intercalation Material 1610 at this stage of charging (e.g., an initial stage of charging a power storage device including the electrodes discussed herein). Because the Intercalation Material 1610 of some embodiments, such as silicon, expands when charge carrier intercalation occurs the surface area Intercalation Material 1610 also increases. This reduces the surface coverage of nanoparticles on the surface of Intercalation Material 1610 and reduces the effectiveness of the nanoparticles in forming a barrier to charge lets.car Thus, as charging es, greater numbers of charge carriers per unit time can reach Intercalation Material 1610. This is optionally continued until charging is dominated by reactions within the Intercalation Material 1610. The reduction in surface coverage may also increase the average fraction of Surface Effect Dominant Sites 1430 on each nanopartiele that are exposed to the electrolyte. As used herein the phrase "surface coverage" is used to represent a density of a species on a surface and may be measured as a number of monolayers (or fraction thereof), as a thickness, or as a concentration, etc. (001111 In some embodiments, the power storage at Surface Effect Dominant Sites 1430 occurs at potentials at which faradaic surface reactions occur but intercalation of charge carriers into the nanoparticles that include the Surface Effect Dominant Sites 1430 does not occur. This prevents degradation of the nanoparticles by repeated intercalation and de-intercalation of charge carrier and allows for a longer cycle lifetime. At the same electrode it is desirable to store power within Intercalation Material 1610 via faradaic reactions that occur at a higher potentials, optionally including potentials that would cause intercalation of charge carriers into the nanoparticles having Surface Effect Dominant Sites 1430. This can occur in sonic embodiments of the invention because there is a potential drop between Substrate 105 and the Electrolyte 125.

1001121 In one specific example, in which lithium is the charge carrier, the Surface Effect Dominant Sites 1430 are on TiO2 nanoparticles and Intercalation Material 1610 is predominantly silicon. The particular voltages in other embodiments will be understood to be dependent on the chemical species included in Surface Effect Dominant Sites 1430 and Intercalation ial 1610, and the reactions occurring during charging, etc. In various embodiments the potential difference between Surface Effect Dominant Sites 1430 and Substrate 105 is at least 0.001, 0.2, 0.3, 0.4, 0.5, 0.6, 0.8, 1.0, 1.3, 1.7, 2.0, 2.2, or 2.4V, or any range there between. As used herein the term "potential" is used to refer to an absolute clue le.g., 1 81) of an electrostatic potential.

1001131 FIG. 21 illustrates methods of assembling an electrode surface, according t various embodiments of the invention. The assembled electrode surface may be used, for example, as an anode in a battery, capacitor or hybrid device. The methods illustrated in FIG. 21 are optionally used to produce the various electrodes discussed elsewhere herein.

100114( In a Provide Substrate Step 2110 a conductive substrate is provided. Provide Substrate Step 21 10 is similar to Provide Substrate Step 1310. In Provide Substrate Step 2110, Substrate 105 optionally suitable for growth of CNFs 110 or other support filaments is provided. As discussed herein. Substrate 105 may include a variety of materials, for example Cu, Au, Sn, etc. Substrate 105 optionally includes nucleation sites as described elsewhere herein.

[00115] In an optional Provide CNF Step 2120, CNF 110 (or any of the other support filaments described herein) are provided. Provide CNF Step 2120 is optional in embodiments in which electrodes that lack support filaments, such as those illustrated by FIGs. 17 and 20, are produced. In some embodiments the CNF 110 are provided by growing CNF 110 on Substrate 105. In some embodiments, CNF 110 are provided by adding CNF 110 to a mixture, that is later applied to Substrate 105. In some embodiments CNF 110 are produced separate from Substrate 105 and later attached to Substrate 105.

(00116] In a Provide Intercalation Material Step 2130, Intercalation Material 1610 is provided. In some embodiments, Intercalation Material 1610 is first applied to CNF 110. In various embodiments, Intercalation Material 1610 is applied as a colloidal suspension, using vapor deposition, in a solvent; as a paste, or the like.

[00117] In a Provide Surface Effect Dominant Sites (SEDS) Step 2140, Surface Effect Dominant Sites 1430 are provided. As discussed elsewhere herein, the Surface Effect Dominant Sites 1430 may be disposed on nanoparticles or larger structures such as graphite, graphene or activated carbon. Surface Effect Dominant Sites 1430 can be provided as a suspension in Binder 1140, or in a solvent, using tter deposition, using electro deposition, using evaporation, as a spray or the like. In some embodiments a Zeta potential of Intercalation Material 1610 is selected such that Surface Effect Dominant Sites 1430 are concentrated at surfaces of Intercalation Material 1610.

[001181 In an Apply Step 2150 Intercalation Material 1610, Surface Effect Dominant Sites 1430 and optionally CNFs 110 are applied to Substrate 105. These materials can be applied in a wide variety of orders and combinations. For example, Intercalation Material 1610 can be applied to CNFs 110 (perhaps already attached to Substrate 105) and then Surface Effect Dominant Sites 1430 can he then applied on top of the Intercalation Material 1610. Alternatively, free CNF 110, Intercalation Material 1610 may be first mixed, then Surface Effect Dominant Sites 1430 and Binder 1140 either alone or in combination are added. Based on the teachings herein, one of ordinary skill in the art will understand that in different embodiments, these components can be mixed or added in any order or combination. Further, the components can be mixed prior to or after being applied to Substrate 105. The Steps 2110-2150 can be performed in any order. Apply Step 2150 is optionally followed by Condition Step 1350.

1001191 In some embodiments the method illustrated in FIG. 21 includes mixing Intercalation Material 1610 and Surface Effect Dominant Sites 1430 in a suspension in a solvent with a sufficient amount of dispersion. The dispersion is optionally applied to CNFs 110. The solvent of the dispersion is then evaporated from the mixture resulting in a powder or coating on the CND's 110. Binder 1440 can be added to the suspension before or after application to the CNFs 110. In some embodiments, the application of Surface Effect Dominant Sites 1430 occurs at the final stage of Intercalation Material 1610 deposition by changing the materials being putt d onto Substrate 105. In these embodiments, for example, TiO2 can be added to the sputtering mix after almost all the Intercalation Material 1610 is deposited. This produces a sputtered layer of TiO, as Surface Effect Dominant Sims 1430 on top of intercalation Material 1610.

[001201 FIG. 22 illustrates nethods of operating a charge storage device, according to various embodiments of the invention. This method may be used, for example, when charging the charge storage device. In some embodiments the method includes attaching a charging device to both an anode and cathode of the charge storage device via wires. This charging storage device places potentials at the anode and cathode resulting in a potential gradient there between. The potential gradient drives electrons into the anode. The steps illustrated in FIG. 22 optionally occur contemporaneously, e.g., they can occur at the same or at overlapping times with respect to each other.

1001211 In an Establish Potential Step 2210 a potential is established at the charge storage device. This potential may be between an anode and a cathode of the charge device. Such a potential will result in a potential gradient between Substrate 105 and Electrolyte 125 within the charge storage device. The potential gradient can produce a potential difference between locations of Surface Effect Dominant Sites 1430 and Intercalation Material 1610. In various embodiments this potential difference is at least 0.001, 0.1, 03, 0.4, 0.5, 0.8, 1.0, 1.3, 1.7, 2.0, or 2.4 V, or any range there between.

1001221 In a Receive Lithium Step 2220 a charge carrier, of which Lithium is but one possible example, is received at one of Surface Effect Dominant Sites 1430. This charge carrier is optionally received through Binder 1440.

1001231 In a Transfer Electron Step 2230 an electron is transferred (e.g., donated) from Surface Effect Dominant Site 1430 to the charge cane eceived in Receive Lithium Step 2220. This transfer may comprise sharing of the electron between the Surface Effect Dominant Site 1430 and the charge carrier. The electron is transferred in a faradaic reaction and is typically conducted from Substrate 105. The transfer c- while the charge caner is at the surface f the Surface Effect Dominant Site 1430 and occurs at c potential of that location. A reaction potential of the electron transfer is, for example, dependent on the reaction potential of the charge carrier and the reaction potential of the Stuface Effect Dominant Site 1430. The reaction potential can be dependent on both the Surface Effect Dominant Site 1430 and the nearby Intercalation Material 1610. As used herein, the term "reaction potential" is used to refer to the potential at which a reaction occurs at an appreciable rate. The reaction potential of a reaction can be illustrated by, for example, peaks in a cyclic voltammogram. In another example, the potentials required for the reactions Li + --* Li or 2Lif + MC) + 2e- Li20 T M (where M is any of the transition metals discussed herein) to occur in an electrochemical cell are the reaction potentials of these reactions. The reaction potential can be highly dependent or the environment in which the reaction occurs. For example, the second reaction above may have a lower reaction potential in the presence of a TiO2 nanoparticle having a diameter in the range of 2-10 mu. Likewise, the reaction potential can be influenced by the energy required for intercalation or by the close proximity of Surface Effect Dominant Sites 1430 and Intercalation Material 1610.

(00124] In an Intercalate Lithium Step 2240 a. charge carrier, of which Lithium is but one possible example, is intercalated within Intercalation Material 1610. This step may include migration of the charge carrier into the hulk interior f Intercalation Material 1610. The charge carrier can he received at Intercalation Material 1610 as the same chemical species as received at the Surface Effect Dominant Sites 1430 in Receive Lithium Step 2220, or alternatively in as a chemical species produced at the Surface Effect Dominant Sites 1430. For example, the charge carrier can he received at the Intercalation Material. 1610 as an oxide (e.g., LTO, etc.) of the chemical species received at Surface Effect Dominant Sites 1430.

[00125] In a Transfer Electron Step 2250 an electron is transferred from Intercalation Material 1610 to the charge carrier of Intercalate Lithium Step 2240. The electron is transferred in a faradaic reaction and is typically conducted from Substrate 105. The transfer occurs while the charge carrier is within Intercalation Material 1610 and occurs at the potential of that location. A reaction potential of the electron transfer may be dependent on the reaction potential of the charge carrier and the reaction potential of the Into calation Material 1610_ The potential of this conduction hand can be influenced by both the Intercalation Material 1610 and nearby Surface Effect Dominant Sites 1430. Surface Dominant Sites 1430 can catalyze transfer of lithium from Electrolyte 125 to Intercalation Material 1610. As discussed elsewhere herein, this transfer can occur via an intermediate oxide such as LkO. The ork function of this electron transfer can be different than the work function of the electron transfer in Transfer Electron Step 2230. For example, in various embodiments the work function is at least 0.001, 0.1, 0.3, 0.4, 0.5, 0.8, 1.0, 1.3, 1.7, 2.0 or 2.4V, or any combination there between. In some embodiments it is thermodynamically more favorable for lithium to be intercalated into Intercalation Material 1610 than into the bulk of nanoparticles that include the Surface Effect Dominant Sites 1430. However, the presence of the Surface Effect Dominant Sites 1430 can catalyze intercalation of a charge carrier into Intercalation Material 1610.

100126] if the charge carrier is converted to an oxide in Transfer Electron Step 2230 then, in some embodiments, Transfer Electron Step 2250 include transfer of an oxygen back from Intercalation Material 1610 hack to Surface Effect Dominant Sites 1430. This oxygen received at Intercalation Material 1610 as the oxide of the charge carrier, and is released from the charge carrier during calatio After being transferred back to Surface Effect Dominant Sites 1430, this oxygen can then be used in further occurrences of Transfer Electron Step 2230, i.e., the oxygen is recycled.

1001271 While the description of FIG. 22 above assumes that the charge carrier received in Receive Lithium Step 2220 and the charge carrier Intercalate Lithium Step 2240 are two different individual charge carriers (that could be of the same type), in various embodiments steps 2220, 2230 and 2240 can be performed in by the same individual charge carriers. For example, in sonicembodiments, Receive Lithium Step 2220 includes receiving a charge carrier at one of Surface Effect Dominant Sites 1430. Transfer Electron Step 2230 then includes a reaction in which the charge carrier reacts with the Surface Effect Dominant Site 1430 to produce an intermediate compound. In some embodiment this reaction includes 21a- --s 2e- Li20 + M (Where M is any of the transition metals discussed herein and Li2O is the resulting intermediate compound). In Intercalate Lithium Step 2240 the intermediate compound (e.g., Lis0) is intercalated into intercalation Material 1610, or one (or both) of the Li in the intermediate compound arc transferred from the 0 of Li:0 to an atom of the Intercalation material (e.g., LLSi). This transfer may result in regeneration of the MO that was split in Transfer Electron Step 2230. Note that in this example the same individual Li atom was involved in each of the Steps 2220-2230 and 2240. Transfer Electron Step 2250 is not required in these embodiments of the methods illustrated by FIG. 22. It is possible that in some embodiments both reaction sequences that include an intermediate such as Li20 and reaction sequences that do not include an intermediate occur during a single charging cycle.

1001281 Several embodiments are specifically illustrated and/or described herein.

However, it will he appreciated that modifications and variations are covered by the above teachings and within the scope of the appended claims without departing from the spirit and intended scope thereof. For example, while the examples discussed herein have been focused on CNFs having a stacked-cone structure the teachings may be adapted to other materials having similar or alternative structures, Likewise, while a Cu substrate and Li charge carriers are discussed herein other substrates and charge carriers will be apparent to one of ordinary skill in the art. Silicon Layer 115 is optionally formed of intercalation materials in addition to or as an alternative to silicon. For example, tin, germanium, carbon, graphite, graphene, silicon, other materials discussed herein or combinations thereof could be used as intercalation material. Additionally, aerogels,nano-wires, Tit"), (titanium oxide), metal wires, carbon wires, or boron nitride nano-fibers can be used in place of the carbon nano-fibers discussed herein. The relative concentrations of Binder 1440, Surface Effect Dominant Sites 1430, Intercalation Material 1610 and CM; 110 and other elements in the figures can vary significantly from that illustrated.

1001291 The electrodes taught herein may be included in a wide variety of energy storage devices including capacitors, batteries and hybrids thereof These energy storage devices can be used in, for example, lighting systems, portable electronics. load balancing devices, communication devices, backup power supplies, vehicles and computing devices. The concepts taught herein can be, in many cases, applied to cathodes as well as anodes.

[00130j Details of VACNF Growth and Silicon Deposition, Microscopy and Spectroscopy Characterization, and Electrochemical Cell Assembly and Charge-Discharge Tests can be found in US provisional application 61/667,876 filed Jul. 3, 2012.

10111311 The embodiments discussed herein are illustrative of the present invention. As these embodiments of the present invention are described with reference to illustrations, various modifications or adaptations of the methods and or specific structures described may become apparent to those skilled in the art. All such modifications, adaptations, or variations that rely upon the teachings of the present invention, and through which these teachings have advanced the art, are considered to be within the spirit and scope of the present invention. Hence, these descr pti s and awings should not he considered in a limiting sense, as it is understood that the present invention is in no way limited to only the embodiments i llustrated.

Aspects of the invention will now be described with reference to the following numbered clauses: 1. An energy storage system comprising: a conductive substrate; a carbon nanoliber connected to the conductive substrate, the carbon nanoliber including a plurality of exposed nanoscale edges along the length of the carbon nanofiber; and an intercalation material configured to form a shell over at least part of the carbon nanofiber.

2. The system or method of clause 1, 29, 30 or 31, wherein each of the exposed nanoscale edges include edges of multiple graphitic sheets.

3. The system or method of clause 29, 30, 31, 1 or 2, wherein each of the exposed nanoscale edges is configured to control growth of the intercalation material.

4. The system or method of clause 29, 30, 31, 1-2 or 3, wherein each of the exposed nanoscale edges is configured to provide a migration path for charge carriers to an interior of the carbon nanoliber.

5. The system or method of clause 29, 30, 31, 1-3 or 4, wherein each of the exposed nanoscale edges include multiple graphene edges.

6. An energy storage system comprising: a conductive substrate; a carbon nanofiber connected to the conductive substrate, the carbon nanofiber including a plurality of cup-like structures along the length of the carbon nanofiber; and an intercalation material configured to form a shell over at least part of the carbon nanofiber.

7. The system or method of clause 29, 30, 31, 1-5 or 6, wherein each of the cup-like structures include walls having multiple graphitic sheets.

8. The system or method of clause 29, 30, 31, 1-6 or 7, wherein each of the cup-like structures are configured to control growth of the intercalation material.

9. An energy storage system comprising: a conductive substrate; a carbon nanofiber connected to the conductive substrate; and an intercalation material configured to form a shell over at least part of the carbon nanofiber, the intercalation material being disposed in a feather-like structure along a length of the carbon nanofiber.

10. An energy storage system comprising: a conductive substrate; a carbon nanofiber connected to the conductive substrate; and an intercalation material configured to form a shell over at least part of the carbon nanofiber, the intercalation material being configured such that expansion of the intercalation material is non-delaminating of the intercalation material from the carbon nanofiber.

11. The system or method of clause 29, 30, 31, 1-9 or 10, wherein the expansion is radial to the carbon nanofiber.

12. The system or method of clause 29, 30, 31, 1-10 or 11, wherein the expansion is between parts of the intercalation material disposed on the carbon nanofiber.

13. The system or method of clause 1-11 or 12, further comprising an electrolyte in contact with the intercalation material and including a charge carrier.

14. The system or method of clause 29, 30, 31, 13, wherein the electrolyte is a solid electrolyte.

15. The system or method of clause 29, 30, 31, 13 or 14, wherein the charge carrier includes lithium.

16. The system or method of clause 29, 30, 31, 1 -14 or 15, wherein the carbon nanofiber is one of a plurality of vertically aligned carbon nanotibers attached to the substrate.

17. The system or method of clause 29, 30, 31, 1-15 or 16, wherein the conductive substrate, carbon nanofiber and intercalation material are configured to function as an anode.

18. The system or method of clause 17, further comprising a cathode in contact with the electrolyte.

19. The system or method of clause 1-17 or 18, wherein the carbon nanofiber is directly attached to the conductive substrate.

20. The system or method of clause 28, 29, 30, 1-18 or 19, wherein the intercalation layer includes silicon.

21. The system or method of clause 29, 30, 31, 1-19 or 20, wherein the carbon nanofiber is configured to grow an intercalation material structure at the exposed edges of the carbon nanofiber.

22. The system or method of clause 29, 30, 31, 1-19 or 20, wherein the carbon nanofiber is indirectly attached to the conductive substrate using a binder.

23. The system or method of clause 29, 30, 31, 1-21 or 22, wherein the cup-like structures include spiral with cup-like cross-section.

24. The system or method of clause 1-22 or 23, wherein carbon nanofiber and the intercalation material result in an insertion capacity for Li+ of between 2752 and 3650 mAhg-I, and at least a 85% retention of the insertion capacity for 100 charge discharge cycles.

25. The system or method of clause 29, 30, 31, 1-23 or 24, wherein the intercalation material is disposed in a layer having a nominal thickness of between 0.1 and 4.0 gm.

26. The system or method of clause 29, 30, 31, 1-24 or 25, wherein the carbon nanofiber is between 3 and 200 gm in length.

27. The system or method of clause 1-25 or 26, further comprising a plurality of nanoparticles attached to the intercalation material, each of the nanoparticles being configured to provide surface effect dominant sites configured to adsorb charge carriers via faradaic interactions on surfaces of the nanoparticles.

28. The system or method of clause 29, 30, 31, 1-26 or 27, wherein the conductive substrate, carbon nanofiber and intercalation material are configured such that an insertion capacity for Li+ increases as a charge rate is increased from 2C to 8C.

29. A method of producing an energy storage device, the method comprising: providing a conductive substrate; adding carbon nanofibers to the conductive substrate, the carbon nanofibers each including a plurality of exposed nanoscale edges along the length of the carbon nanofiber; and applying intercalation material to the carbon nanofibers, the intercalation material being configured for intercalation of charge carriers.

30. A method of producing an energy storage device, the method comprising: providing a conductive substrate; adding carbon nanofibers to the conductive substrate, the carbon nanofibers each including a plurality of cup-like structures along the length of the carbon nanofiber; and applying intercalation material to the carbon nanofibers, the intercalation material being configured for intercalation of charge carriers.

31. A method of producing an energy storage device, the method comprising: providing a conductive substrate; adding carbon nanofibcrs to the conductive substrate; and applying intercalation material to the carbon nanofibers, the intercalation material being configured for intercalation of charge carriers, and the intercalation material being disposed in a feather-like structure along a length of the carbon nanofiber.

32. The method of clause 29, 30 or 31, further comprising adding an electrolyte in contact with the intercalation material and including a charge carrier.

33. The method of clause 29-31 or 32, wherein the carbon nanofibers are vertically aligned carbon nanofibers attached to the substrate.

34. The method of clause 29-32 or 33, wherein the conductive substrate, carbon nanofibers and intercalation material are configured to function as an anode.

35. The method of clause 29-33 or 34, further comprising a cathode in contact with the electrolyte.

36. The method of clause 29-34 or 35, wherein the carbon nanofibers arc attached directly to the conductive substrate.

37. The method of clause 29-35 or 36, further comprising attaching a plurality of nanoparticles to the intercalation material, each of the nanoparticles being configured to provide surface effect dominant sites configured to adsorb charge carriers via faradaic interactions on surfaces of the nanoparticles.

38. The system or method of clause 1-27 or 28, wherein the intercalation material includes first silicon structure at a time of the carbon nanofiber and a second silicon structure along a length of the carbon nanofiber.

Claims

Claims 1.
An electrode comprising: a conductive substrate; and a material disposed on the substrate, wherein the material comprises: carbon nanofibers; an intercalation material interspersed with the carbon nanofibers that reversibly adsorbs charge carriers within a bulk of the intercalation material; a plurality of surface effect dominant sites that catalyze intercalation of the charge carriers into the intercalation material; and a binder, wherein the surface effect dominant sites comprise nanoparticles, wherein the nanoparticles comprise transition metal oxides, metal nitrides, activated carbon, graphene, graphite, titanate, crystalline silicon, tin, germanium, metal hydrides, iron, phosphates, polyaniline, mesophase carbon or a mixture of two or more thereof 2.
The electrode of claim 1, wherein the intercalation material comprises silicon, silver, aluminum, bismuth, selenium, antimony, tin, zinc, or combinations thereof The electrode of claim 1, wherein the intercalation material comprises silicon
4. The electrode of claim 3, wherein the intercalation material is in the form of particles, suspensions, clusters, droplets, or combinations thereof
5. The electrode of claim 3, wherein the intercalation material comprises particles having sizes in a range of 0.1 pm to 29 pm
6. The electrode of claim 3, wherein the intercalation material comprises particles having sizes in a range of 5 um to 15 pm.
7. The electrode of claim 1, wherein the binder comprises polyvinylidene fluoride (PVDF), styrene butadiene rubber, poly(acrylic acid) (PAA), or carbo-xymethyl-cellulose (CMC)
8. The electrode of claim 7, wherein the binder further comprises conductive polymer, graphite, graphene, metal nanoparticles, carbon nano-tubes, carbon nano fibers, metal nano-wires, or conductive carbon black.
9. An energy storage system comprising: a cathode; an electrolyte including one or more charge carriers; and the electrode of any preceding claim as an anode, wherein the anode is separated from the cathode by the electrolyte.