GB2502257A - On-line control of a manufacturing process for a multicomponent sheet material - Google Patents
On-line control of a manufacturing process for a multicomponent sheet material Download PDFInfo
- Publication number
- GB2502257A GB2502257A GB1207609.7A GB201207609A GB2502257A GB 2502257 A GB2502257 A GB 2502257A GB 201207609 A GB201207609 A GB 201207609A GB 2502257 A GB2502257 A GB 2502257A
- Authority
- GB
- United Kingdom
- Prior art keywords
- signal
- sheet
- sheet material
- parameter
- multicomponent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Controlling a process for the manufacture of a multicomponent sheet material 612. The control method comprises the steps of applying an acoustic or an electromagnetic signal to interact with the sheet material 612 whereby the interaction modifies the applied signal, detecting the modified signal, comparing the modified signal or data derived from it with data relating to the pre-determined parameter and modifying at least one step of the process whereby the data relating to the modified signal are modified towards the data relating to the preÂdetermined parameter. The sheet material 612 may be a laminate or a pre-impregnated fibre reinforced structure. The method may provide continuous in-line feedback control. A further method comprises correlating detected measurement signals with the results of a water pick-up method to calibrate the detected measurement signal results with one or more parameters of the sheet material. A prepreg and/or laminate material 612 may be formed by feeding a reinforcement material 602 through rollers 606 with a curable resin 604. Ultrasound transmitters 610 and receivers 608 may be positioned on opposite sides of the prepreg 612.
Description
A METHOD FOR ON-LINE CONTROL OF A MANUFACTURING PROCESS FOR A
MULTICOMPONENT SHEET MATERIAL
This invention relates to a method for determining on-line a parameter of a multicomponent sheet material and to a method of controlling a process for the manufacture of the multicomponent sheet material, particularly a prepreg material. The invention further relates to a method of producing a roll of a multicomponent sheet material selected from a laminate and a pre-impregnated fibre reinforced structure wherein the sheet material has a desired pre-determined parameter, a quality-verified pre-impregnated fibre reinforced structure and to a process controller for controlling a process for the manufacture of a multicomponent sheet material.
Composite materials have been used to produce both lightly loaded and highly loaded structures, useful in non-load carrying and load carrying applications, respectively. Examples of the former include boat hulls and automobile body panels, while examples of the latter include pressure vessels, frames, fittings and aerospace applications, for instance aircraft fuselages. Because of their wide applicability, composite materials have found use in a wide range of industries including the automotive, marine and aerospace industries. However, due to their ability to be manufactured in forms suitable for bearing heavy loads, composite materials are especially useful in the design of load bearing structural members, particularly where strength, lightness and ease of shaping may be required. Ensuring reliability in the construction of the sheet material and quality control is imperative.
Composite materials typically include a fibrous material, such as carbon, aramid, glass or quartz, bonded together with a resin material for example an epoxy. The load in such composite materials is carried primarily by the fibrous material, and so, the load carrying properties of the composite can be altered by altering the orientation of the fibres in the composite material. For example, composite materials with unidirectional fibres, such as tapes or tows, may generally exhibit the strongest tensile strength along the axis of the fibres. Woven fabrics and bi-directional mats are typically strongest in the plane of the material. Thus, when designing composite materials, fibre orientation and the number of layers, also known as plies, is typically specified in consideration of the anticipated load the composite item will experience.
Fibre composite laminates or parts may typically be manufactured by first impregnating the fibre reinforcement with resin to form a prepreg, and then consolidating two or more layers of prepreg into a laminate in a so-called "layup" process. Formation of a variety of defects, including wrinkles, voids, delaminations, and the like is inherent in the layup process. For example, voids in the prepreg and/or laminate, may result from the inefficient penetration of the resin in to the fibre bundle, tow, or roving, or from outgassing during the consolidation process. Such defects may be formed in greater number when the composite article being formed is relatively large, or incorporates a contour, or otherwise complex shape.
Such defects may not be readily identifiable, detectable or apparent on the surface during the layup process, or, such defects may become visible or exacerbated during the subsequent curing process. The presence of such defects in the finished article may compromise the material strength by as much as a factor of 2, and so, may require that the article be repaired, or, may even require that the part be scrapped, thus contributing to an increase in manufacturing cost due to either the repair cost and/or lead-time required to replace scrapped articles.
A wide range of inspection methods have been applied independently to composite materials. However, the resolution of defects when using some of these composite materials may be limited in some applications. For example, in composite materials wherein the fibres or tows have a random orientation, or in composite materials wherein the fibres desirably comprise carbon, either the structure or the carbon may scatter the measured signal.
Further, in many applications, it may be desirable, or even necessary, to obtain multiple measurements, including both measurements of physical parameters and material properties, of the composite material. Many inspection apparatus' are capable of providing only one measurement, or one type of measurement, or provide data with a standard deviation unacceptable in some applications. In some cases, equipment capable of conducting more sophisticated measurements can be expensive and thus not cost-effective in applications where the profit margin of the article being manufactured does not warrant the expense.
A procedure known as the water pickup test for determining the degree of waterproofing or impregnation of a unidirectional prepreg material is known. For this purpose, a specimen of unidirectional prepreg material is initially weighed and clamped between two plates in such a way that a strip of specimen, typically about 5 mm wide protrudes. This arrangement is suspended in the direction of the fibres in a water bath for 5 minutes at room temperature (21 °C). After removing the plates, the specimen is again weighed. The difference in weight is used as a measured value for the degree of impregnation. The smaller the amount of water picked up, the higher the degree of waterproofing or impregnation. A disadvantage of the water pickup test is that it does not allow any conclusions to be drawn for example concerning the resin distribution in the prepreg material or the surface finish of the prepreg material. The water pickup test procedure merely provides information of an overall bulk effect, it not being possible to differentiate between the individual influencing variables or characteristic parameters.
Furthermore the water pickup test is typically employed off-line as a quality control measure on samples of a material. This necessarily means that a local failure in quality may not be identified or, if it is, a large quantity of material may be deemed to fail the test and lead to wastage.
A need exists for an improved method of controlling a process for the manufacture of a multi-component sheet material and inspection method which limits or overcomes problems associated with known methods.
In a first aspect! the invention provides a method of controlling a process for the manufacture of a multicomponent sheet material having a desired pre-determined parameter comprising applying an acoustic signal or electromagnetic signal to interact with the sheet material whereby the interaction modifies the applied signal, detecting the modified signal, comparing the modified signal or data derived from it with data relating to the pre-determined parameter and modifying at least one step of the process whereby the data relating to the modified signal is modified towards the data relating to the pre-determined parameter.
In referring to a "parameter" heiein, this term is intended to include any aspect of the multicomponent sheet material including its properties.
The acoustic signal may preferably comprise an ultrasound signal. The electromagnetic signal may comprise a microwave signal (wave length ranging from 0.05 x 102 to lx 102 m), an x-ray signal (wavelength 0.01 nm to 10 nm), a light signal (10 nm to 700 nm), an infrared signal (wavelength 700 nm to 0.1 cm) and/or combinations of the aforesaid signals.
Suitably the method comprises conducting at least one step of a prepreg and/or laminate manufacturing process and measuring at least two properties of the prepreg and/or laminate before, during or after the at least one step.
Advantageously, the in-line method of the invention allows defects to be detected and compensated for during the manufacture of prepregs and composite materials. This reduces or eliminates the amount of rework or scrap produced in conventional manufacturing processes.
Suitably the process is a continuous process.
The multicomponent sheet material is preferably selected from a laminate and a pre-impregnated fibre reinforced structure. Suitably, the laminate or pre-impregnated fibre reinforced structure is produced in a process comprising an impregnation step comprising contacting a resin with a reinforcement material and one or more further steps selected from a compaction step, a lamination step, a consolidation step and a curing step and wherein at least one step of the process is modified during the process in response to the comparison of the detected ultrasound signal with the data relating to the pre-determined parameter.
Suitably, the at least one step of the process is modified continuously during the process thereby to provide in-line feedback control. In the process, any one or more of the process parameters may be modified so as to modify the actual value of the pre-determined parameter towards the desired pre-determined parameter and is suitably selected from the compression of rollers, the gap between resin coater and fibrous material, the temperature of the resin and the flow late of resin. The method of control using continuous ultra-sound measurement allows for ongoing quality control of the product being manufactured.
In a preferred embodiment, the process is a continuous process and comprises contacting a resin dispensed from an applicator with a reinforcement material and passing the material between compression rollers wherein the at least one step of the process which is modified in response to the detected ultrasound signal is selected from the compression of rollers, the distance between the resin applicator and the reinforcement material, the temperature of resin, the flow rate of the resin and the line speed of the process.
Preferably, the ultrasound signal is employed to provide data relating to two or more parameters of the sheet material. In a preferred embodiment, the transmittance of the ultrasound signal through the thickness of the sheet is measured to determine a first parameter of the sheet and optionally a second parameter of the sheet. Preferably the first and second parameters are selected from the level of resin impregnation of the sheet and the thickness of the sheet.
The process is suitably controlled based on data derived from the ultra sound measurement and comparing data relating to the parameter being measured with data relating to a pre-determined value of that parameter. Preferably, the line speed of the process is modified in response to a comparison of the data derived from the detected ultrasound signal and data relating to a pre-determined parameter which correlates with a pre-determined level of level of impregnation of the sheet and/or the thickness of the sheet. By modifying the line speed, the level of resin applied per unit area may be controlled and modified to provide the desired pre-determined level of resin in the prepreg.
The ultrasound signal suitably interacts with the sheet material and one or more parameters selected from the transmittance of the signal through the sheet, the velocity of the detected signal and the time of transmission of the signal through the sheet. The method suitably comprises measuring at least two parameters and/or properties of a prepreg and/or laminate during the manufacture of it. Desirably the method comprises correlating the detected ultrasound signal with two or more desired pre-determined parameters of the sheet.
The property and/or parameter measured can be any that provide useful information about the prepreg and/or laminate. In some embodiments, the measured property and/or parameter provides information related to the properties of the prepreg and/or laminate, while in others, the measured property and/or parameter provide information related to defects, for example voids, cracks, foreign inclusions, delaminations, porosity, wrinkles, or fibre misalignment within the prepreg and/or laminate. Desirably, at least two measurements are made so that more information is obtained as compared to methods of inline inspection of prepregs and/or laminates that utilize only one measurement.
Where two or more measurements are taken, the measurements may be the same measurement, made at different stages of the manufacturing process, while in others, the measurements may be different, and made at the same, or different, stages of the manufacturing process. One measurement may comprise one made substantially at, or in relation to, the surface of the prepreg and/or laminate, while the other measurement may be made below the surface, for example in relation to the subsurface of the prepreg and/or laminate.
The invention enables a quantity of multicomponent sheet material to be produced wherein the quality of the product meets the desired criteria for quality. The continuous process is typically employed to produce a roll of product. Ensuring the roll of product meets the relevant quality criteria reduces waste and is especially important where the product is to be used in applications involving the material bearing high loads.
In a second aspect, the invention provides a method of producing a roll of a multicomponent sheet material selected from a laminate and a pre-impregnated fibre reinforced structure wherein the sheet material has throughout the roll a desired pre-determined parameter which lies within a tolerance band around the desired pre-determined parameter by controlling the process for the manufacture of the multicomponent sheet material using a method according to the first aspect of the invention.
Suitably, the tolerance band is not more than 10%, preferably not more than 5% and desirably not more than 1% either below or above the desired pre-determined parameter depending on the particular parameter, the intended end-use and the overall desired quality specification. Whilst the tolerance band may be centred on the desired parameter such that the tolerance band extends equally above and below the desired pre-determined parameter, it is also within the scope of the invention to have a lesser or greater tolerance on one side of the desired pre-determined parameter than the other.
Suitably, the desired pre-determined parameter is selected from the level of impregnation of the reinforcement material and the thickness of the sheet. Preferably, the level of impregnation deviates throughout the roll by less than 10% from the desired pre-determined level of impregnation. Suitably, the thickness of the sheet wherein the thickness of the sheet deviates throughout the roll by less than 10% from the desired pre-determined thickness of the sheet.
In a further aspect, the invention provides a pre-impregnated fibre reinforced structure comprising a roll of a multicomponent sheet material selected from a laminate and a pre-impregnated fibre reinforced structure wherein at least one parameter of the multicomponent sheet material has been altered during production of the roll in response to data obtained from ultrasound measurements carried out during the production of the multicomponent sheet material.
Suitably the pre-impregnated fibre reinforced structure comprising a roll of a multicomponent sheet material selected from a laminate and a pre-impregnated fibre reinforced structure has been obtained by a method according to the second aspect of the invention.
Advantageously, the pre-impregnated fibre reinforced structure need not be subjected to off-line quality control analysis. If however, this is desired as a complementary quality control measure, the pre-impregnated fibre reinforced structure may be subjected to a known quality control process in addition to the ultrasound method of the present invention.
In a preferred embodiment, the pre-determined parameter to be measured by ultrasound is a spatial parameter. Preferably the ultrasound signal sweeps across the width of a roll in a continuous production line so as to scan a large part and preferably substantially the entire area of the roll as it is produced. In a preferred embodiment, the ultrasound signal sweeps across the width of the roll and interacts with it so as to provide a modified ultrasound signal providing data relating to the quantity of resin in the sheet material or to the relative quantity of the resin relative to a desired predetermined level of resin in the sheet. Where a tolerance band is applied, detecting the actual level of the resin or monitoring it through the sweep of the ultrasound signal and detection of the modified signal based on variations in the level of the resin allows the operator to determine whether a roll of sheet material passes or fails quality control criteria based on the level of resin falling within the tolerance band.
The invention also provides a method of controlling a process for the manufacture of a multicomponent sheet material having a desired pre-determined parameter comprising applying an ultrasound signal to interact with the sheet material whereby the interaction modifies the ultrasound signal, detecting the modified ultrasound signal, comparing the modified ultrasound signal or data derived from it with data relating to the pre-determined parameter and modifying at least one step of the process whereby the data relating to the modified ultrasound signal is modified towards the data relating to the pre-determined parameter and wherein the multicomponent sheet material is subjected to the water pickup test.
The present invention may be employed in combination with other quality control methods Any additional methods may be selected based upon the parameter or property(ies) being measured. Additional measurement methods include imaging techniques, such as acoustic holography, optical metrology and many varieties of cameras, for example microwave cameras, for dimensional measurements, such as length, width, depth, or measurements made in more than one dimension; thermometers or thermocouples for the measurement of thermal conductivity; magnetometers such as hall-effect sensors, giant magneto-resistive sensors, anisotropic magneto-resistive sensors, atomic magnetometers, superconducting quantum interference devices (SQUIDS) or eddy current coils for the measurement of magnetic permeability; capacitive plates or striplines for the measurement of dielectric constant; ohmmeters and eddy current coils for the measurement of electric conductivity; densitometers or x-ray for the measurement of density or porosity; and magnetometers and coils for the measurement of nuclear quadruple resonance frequency.
In some embodiments, at least one of the measurements suitably provides information related to a property of the prepreg or laminate, or the presence of a defect in the same. For example, at least one measurement may desirably provide information related to the thermal conductivity, magnetic permeability, dielectric constant, electric conductivity, density, nuclear quadruple resonance frequency, etc., of the prepreg and/or laminate. In some embodiments, ultrasound measurements are employed and provide information related to the porosity, fibre volume fraction, voids and/delaminations of the prepreg and/or laminate.
The present invention may be employed in combination with the method described in US2O1O/0065760 for determining at least one characteristic parameter of a CRP specimen, in particular a specimen of prepreg material for aerospace, comprising the following method steps: presenting the specimen, irradiating the specimen with a predetermined spectrum of electromagnetic radiation, recording the interaction between the specimen and the electromagnetic radiation in a data record and determining the characteristic parameter from the recorded data record.
In a further aspect, the invention provides a method of calibrating an ultrasound apparatus for use in a method of controlling a process for the manufacture of a multicomponent sheet material having a desired pre-determined parameter comprising manufacturing a multicomponent sheet material applying an ultrasound signal to interact with the sheet material during its production, detecting the ultrasound signal after interaction with the sheet material, analysing one or more parameters of the sheet material by a water pick-up method and correlating the detected ultrasound signals with the results of the water pick-up method thereby to calibrate the detected ultra-sound results with the one or more parameters of the sheet material.
In another aspect, there is provided an apparatus for the manufacture of a prepreg and/or laminate. The apparatus comprises a controller, a resin infusion apparatus, at least one measurement apparatus, and a processor. The processor is operatively disposed relative to the measurement apparatus and controller so that information may be transmitted therebetween. Suitably the method of the invention is controlled using a process controller.
In a further aspect, the invention provides a process controller for controlling a process for the manufacture of a multicomponent sheet material having a desired pre-determined parameter which comprises contacting a resin dispensed from an applicator with a reinforcement material and passing the material between compression rollers and applying an ultrasound signal to interact with the sheet material whereby the interaction modifies the ultrasound signal, detecting the modified ultrasound signal, comparing the modified ultrasound signal or data derived from it with data relating to the pre-determined parameter and modifying at least one step of the process, the contioller complising: i) a process parameter controller for controlling one or more the parameters in the process selected from the level of force exerted by the compression rollers, the distance between the resin applicator and the reinforcement material, the temperature of the resin, the flow rate of the resin and the line speed of the process; U) a comparator for comparing the detected ultrasound signal or data derived from it with data relating to the desired pre-determined parameter; Ui) a parameter modifier for receiving data from the comparator and providing a signal to the process parameter to modify at least one of the parameters in the piocess whereby the actual value of the pre-determined parameter approaches the desiied value of pre-determined parametel.
In a preferred embodiment, the line speed of the process is controlled in response to measured ultrasound signal.
In embodiments of the invention, the acoustic signal may have a frequency in the ultiasound range. The ultrasound signal may have a frequency of from 100 kHz to 5 MHz, preferably of from 200 kHz to 1 MHz and most preferably of from 300 kHz to 550 kHz.
In a further aspect, the invention provides a production line for producing a roll of a multicomponent sheet material comprising impregnation apparatus for contacting a resin with a reinforcement material and one oi moie furthei appalatus selected from compaction apparatus, lamination apparatus, consolidation apparatus and curing apparatus and ultrasound apparatus adapted to apply ultrasound to the sheet and to detect an ultrasound signal and a process controller according to the invention In a furthei aspect, the invention provides a method of calibrating an ultrasound appalatus for use in a method of controlling a process for the manufacture of a multicomponent sheet material having a desired pre-determined parameter comprising manufacturing a multicomponent sheet material applying an ultrasound signal to interact with the sheet material during its production, detecting the ultrasound signal after interaction with the sheet material, analysing one or more parameters of the sheet material by a water pick-up method and correlating the detected ultrasound signals with the results of the water pick-up method theieby to calibiate the detected ultia-sound results with the one oi more parameters of the sheet material.
In a preferred embodiment, the invention provides a method of quantifying the level of impiegnation of a laminate or stiuctule by a lesin, the method comprising: measuling the tiansmittance and/oi reflection of an ultrasound (UT) signal thiough the thickness of the laminate or structure; and correlating the measured transmittance and/or reflection with a calibration model to determine the level impregnation of the structure or laminate.
Suitably the measured transmittance and/or reflection is correlated with a calibration model derived from measurements obtained using the water pickup method.
Preferably, the method comprises the step of measuring the through thickness velocity of an ultrasound signal, and correlating the velocity with a further calibration model to determine a further parameter or property of the structure or laminate, preferably the further property is the thickness of the laminate or structure.
The invention also provides for articles prepared from prepregs and/or laminates made using the method of the invention.
In some embodiments dimensional information, such as length, width, depth, or measurements made in more than one dimension is suitably obtained. Many imaging techniques are available capable of providing such measurements, either directly, or indirectly via an image that may be further analyzed to provide the desired dimensional information. Examples of such imaging techniques include acoustic holography, eddy current array imaging, optical metrology and many varieties of cameras, for example microwave cameras.
In some embodiments, optical metrology may be used in addition to ultrasound and is advantageously capable of providing information related to wrinkles or waviness present in the reinforcement material, prepreg and/or laminate. Techniques for conducting optical metrology measurements, as well as analyzing the results thereof, are well known to those of ordinary skill in the art, and are described generally in Yoshizawa, Taoru, Handbook of optical metrology principals and applications, Taylor & Francis, Boca Raton, co. 2008 hereby incorporated by reference herein in its entirety. Further, equipment for conducting such measurements is commercially available from a variety of sources including General Electric Company, FARO and Minolta.
In a preferred embodiment, ultrasound measurements are advantageously taken during infusion, and/or prior to, or during compaction, when they are expected to provide information related to the porosity of the prepreg. Suitably an ultrasound probe(s) is employed and may be placed in close proximity to the resin infusion stage and/or the compression/compaction stage, where it will collect data indicative of the porosity of the prepreg/laminate at a given depth.
The data is then processed by the processor to provide data, for example indicative of the effect of any defects in the green state prepreg and/or laminate on the number and severity of defects the corresponding cured part and/or the impact of any such defects on cured part strength. The processed data provided to the controller, which may then adjust parameters of the process, if desired or required, to reduce the amount, or magnitude, of defects generated in the prepreg and/or laminate by the process.
Process adjustments that may impact the presence, number or impact of defects in the green state prepreg and/or laminate include, but are not limited to, tow tension, temperatures, layup speed, roller pressure, and resin content. And, the processed data may indicate, and so the controller may adjust any of these manually or automatically. Automatic control may be advantageous in some embodiments, as it provides the opportunity for a closed-loop process.
Techniques for conducting ultrasound measurements, as well as analyzing the results thereof, are known to those of ordinary skill in the art, and are described generally in Data, S. K. and Shah, A. H., Elastic waves in composite media and structures with applications to ultrasonic nondestructive evaluation, CRC Press, Boca Raton, co. 2009, hereby incorporated by reference herein in its entirety. Further, equipment for conducting such measurements is commercially available from a variety of sources including General Electric, Olympus, and NOT Systems.
The apparatus employed for putting the invention into effect suitably comprises appropriate sensors, or arrays of sensors, operatively disposed relative to the prepreg and or laminate, or processing equipment at the point of the manufacturing process at which the measurement information is desirably obtained. In some embodiments, the sensor or array(s) of sensors may advantageously be placed proximal to, distal to, or in close proximity to where the resin is desirably infused into the reinforcement material, and/or compaction/compression of the prepreg, layup of one or more prepregs to provide the laminate, or consolidation of the laminate takes place. Stated another way, at least one of the measurements is taken before, during or after infusion of a resin onto a reinforcement material, a compaction step, a lamination/layup step, a consolidation step and/or a curing step.
In a preferred embodiment the ultrasound transmitter and receiver are located above and beneath the sheet. The ultrasound signal may be reflected from the top surface or from the bottom surface or from intermediate layers of the sheet. The signal may also be transmitted or absorbed through the thickness of the sheet or prepreg. Absorption of the signal (as measured by the difference between the energy of the transmitted signal and the received signal following transmission through the prepreg or sheet) provides a measurement of one or more parameters of the sheet or prepreg such as the resin layer thickness or sheet or prepreg thickness or density.
The velocity of the signal through the sheet may also provide an indication of the density or porosity or variations of density or porosity in the prepreg or sheet. The velocity may be measured by the difference between the velocity of the transmitted signal and the received signal following transmission through the prepreg or sheet.
The phase difference between the original transmitted signal and received signal may also be indicative of certain properties of the prepreg or sheet such as porosity or surface defects.
In those embodiments wherein optical metrology is employed to obtain one of the measurements, it may advantageously be employed during layup, when it is expected to provide information related to the laminate surface topography.
Suitably, the data obtained from at least one measurement is advantageously used to monitor and/or modify the manufacturing process. In other words, the data obtained from the measurements may be provided to a processor capable of manipulating the data. For example, the data may be manipulated to provide a historical overview of the measured property of the prepreg and/or laminate, or, the data may be manipulated in order to predict how the properties and/or defects within prepreg and/or laminate may develop during further processing and/or storage.
In some embodiments, the data may be manipulated in order to predict how defects in the uncured, or "green-state", prepreg and/or laminate may present in the cured part. In the same, or other embodiments, the data may be manipulated in order to correlate any defects detected in the measuring steps to cured pad strength. In other words, the data may be manipulated in more than one way, to provide more than one indication. In some embodiments, for example, the data may be manipulated to provide both a prediction of how defects in green-state parts will present in cured parts, and what impact these defects will have in the cured part strength.
Process modelling software and techniques are known in the art, and these may also be applied to the data obtained during practice of the methods to predict, for example defects that may remain, or be exacerbated in a cured part from green state indications, and the impact any such defects may have on the cured part strength. For example, suitable methods for conducting such analysis are described, for example, in Sridhar Ranganathan, Suresh G. Advani, and Mark A. Lamontia, "A Non-Isothermal Process Model for Consolidation and Void Reduction during In-Situ Tow Placement of Thermoplastic Composites," Journal of Composite Materials, 1995 vol. 29, pp. 1040-1062; Yerramalli, C. S., Waas, A. M., "A nondimensional number to classify composite compressive failure," Journal of Applied Mechanics, Transactions ASME, 2004, vol. 71, no. 3, pp. 402-408 and Yerramalli, C. S., Waas, A. M., "A failure criterion for fibre reinforced polymer composites under combined compression-torsion loading", International Journal of Solids and Structures, 2003, vol. 40, no. 5, pp. 1139-1164, hereby incorporated herein by reference for any and all purposes.
Such analysis can be used, in some embodiments, to make changes to the process in order to minimize, or even eliminate, defect formation. Such embodiments thus provide the advantage of a reduction in reworking, or scrap, of defective articles made by the process.
Such process modifications may either be made manually, or via an automated controller operatively disposed relative to the processor in order to receive information therefrom, and relative to the prepreg and/or layup apparatus, in order to provide information thereto.
The present methods are advantageously and readily incorporated into any apparatus for the manufacture of a prepreg and/or laminate, and so, such apparatus are also provided herein. Generally speaking, the apparatus comprises a controller, a resin infusion apparatus, at least one measurement apparatus, and a processor. The processor is operatively disposed relative to the measurement apparatus and controller so that information may be transmitted therebetween. In some embodiments, the apparatus may also comprise a layup apparatus.
The at least one measurement apparatus may be positioned at any location wherein data related to the prepreg and/or laminate can be, and is desirably, collected. In some embodiments, the same type of measurement apparatus may be used at more than one location, while in the same, or in other, embodiments, at least two measurement apparatus are utilized. The measurement apparatus will depend upon the data desirably obtained, and can be chosen based upon the same. In some embodiments, an optical metrology unit is utilized in combination with an ultrasound measurement device.
For example, in those embodiments, wherein at least one measurement provides dimensional data, and the measurement is taken with one or more optical metrology device, the device(s) may be positioned, for example in close proximity to the layup head, and where it will generate 2-D images of the laminate surface topography that, in turn, can be analyzed to detect and characterize any wrinkles in the surface of the laminate.
The present methods and apparatus may be utilized in connection with the manufacture of any prepreg and/or laminate, regardless of the composition thereof. Prepregs typically comprise one or more curable resins, and one or more reinforcing materials, while laminates typically comprise multiple prepregs, layered one upon another.
Generally speaking, suitable curable resins for use in prepregs and laminates include thermoplastic polymeric compositions such as polystyrene, polyethylene terephthalate, polymethylmethacrylate, polyethylene, polypropylene, polyvinylacetate, polyamide, polyvinyl chloride, polyacrylonitrile, polyesters, polyvinyl chloride, polyethylene naphthalate, polyether ketone, polysulfone, polycarbonate, and copolymers thereof.
Prepregs and laminates may also utilize thermoset resins, suitable examples of which include, but are not limited to epoxies, polyesters, vinylesters, phenolic resins, polyurethanes, polyamides, or combinations of two or more of these. Adhesive compositions particularly well suited for use in the present invention include crosslinked thermosetting systems such as polyesters, vinyl-esters epoxies (including acid, base and addition cured epoxies), polyurethanes, silicone resins, acrylate polymers, polysiloxanes, polyorganosiloxanes, and phenolics, as well as blends or hybrids of any of these.
Structural adhesives are often used in prepregs and laminates, and may be used in the prepregs and laminates prepared by the present methods and/or apparatus. Preferred structural adhesives for use in the present composite systems include polyesters, methyl methacrylates, and the like.
Any suitable reinforcing material may be infused using the apparatus, systems and methods described. For example, relatively continuous fibres, or tows, may be arranged to form a unidirectional array of fibres, a cross-plied array of fibres, or bundled in tows that are arranged to form a unidirectional array of tows, or that are woven or cross-plied to form a two-dimensional array, or that are woven or braided to form a three-dimensional fabric. For three-dimensional fabrics, sets of unidirectional tows may, for example, be interwoven transverse to each other.
Useful fibres to be included in such reinforcing materials, such as tapes or fabrics, include without limitation, glass fibres, carbon and graphite fibres, basalt fibres, polymeric fibres, including aramid fibres, boron filaments, ceramic fibres, metal fibres, asbestos fibres, beryllium fibres, silica fibres, silicon carbide fibres, and the like. The fibres may be non-conductive or conductive, depending upon the desired application of the prepreg.
The present methods may be applied in the manufacture of any article comprising a prepreg and/or laminate and are particularly advantageous when applied to large articles due to the cost associated with the manufacture of such articles, and thus, the cost of reworking or scrapping the same. The present methods may also provide particular benefit when applied to prepregs, laminates and/or articles comprising these wherein the reinforcement material comprises carbon filaments or fibres. Carbon has a significantly higher stiffness and lower mass than many other reinforcement materials, for example glass composites. Thus, its use as a reinforcement material can enable the manufacture of prepregs, laminates and articles that may be larger, and yet lighter, with yet acceptable strength for the desired application.
However, the final strength of components made of prepregs and/or laminates comprising carbon can depend greatly on the manufacturing process. Defects such as wrinkles, delaminations, porosity and voids can greatly reduce the final strength of the composite by introducing stress concentrators into the material structure that may cause localized premature failure or redirect stresses from applied loads in ways that are not accounted for in the design of the component.
Examples of industries wherein large scale articles are routinely manufactured from prepregs and/or laminates, and/or prepregs and/or laminates comprising a carbon containing reinforcement material include the energy industry, where large segments of, for example pipeline or other plant apparatus, may find benefit from application of the principles discussed herein. Examples of particular applications further include wind turbine components, such as, turbine blades or subcomponents of such, for example spars, spar caps, airfoil skins, or the cylindrical root section or tower sections of wind turbines.
Laminates prepared from prepregs prepared using the methods and apparatus described may also be used in aviation applications, such as wing skins, fuselage skins, spars, or flat laminates such as ribs.
The invention is illustrated with reference to the accompanying drawings in which: Figure 1 is a flow chart representing steps in an inline inspection method in accordance with some embodiments of the invention; Figure 2 is a flow chart representing steps in an exemplary inline inspection method in accordance with some embodiments of the invention; and Figure 3 is a diagram presenting an implementation of the method of the invention according to another embodiment of the invention.
Figure 1 is a flow chart illustrating one embodiment of the method. As shown, method 100 involves manufacturing a prepreg and/or laminate at step 102, and measuring a parameter or property of the prepreg and/or laminate using an ultrasound method during the manufacture thereof at step 104. The measurements may generally be taken at any point in the manufacturing process of a prepreg or laminate including, resin infusion, compression/compaction, lamination/layup, consolidation and curing.
In Figure 2, method 400 comprises conducting a step of a prepreg/laminate manufacturing process at step 404, measuring at least two properties of the prepreg/laminate at step 406, and analyzing the data obtained at step 408. The analysis of the data may then be utilized to adjust the manufacturing process, if necessary or desired, as shown at step 402.
Figure 3 is a diagram presenting an implementation of the method of the invention 614 according to another embodiment. A prepreg and/or laminate material 612 is formed by feeding a reinforcement material 602 through rollers 606 with a film of curable resin 604.
Four ultrasound transmitters 610 are positioned after the rollers and aligned parallel to the width of the prepreg at spaced intervals to one side of the prepreg, facing the prepreg sheet.
Four ultrasound receivers 608 are positioned on the opposite side of the prepreg to the transmitters in positions opposite to the transmitters. An ultrasound signal is produced by each of the ultrasound transmitters 610 which is transmitted through the prepreg and received by the receivers 608. The output of the ultrasound receivers 608 is converted to a digital signal with an analogue to digital converter 620 and received by a data acquisition system 622. A signal processing unit 624 then compares the received signal to a reference signal which corresponds to the original transmitted signal. The change of the transmitted signal is correlated to the impregnation level of the prepreg to provide the resin impregnation of the reinforcement material, which can be displayed in real-time. The data is compared to predetermined values and used to adjust a parameter of the manufacturing process (e.g. roller force) with closed loop control, to ensure uniform impregnation of resin into the reinforcement material. The resin thickness data is also recorded to associate this with a corresponding batch of prepreg. This system can also be used to detect errors and fluctuations of resin that occur, for example, following a change of film roll or fibre creel.
There is thus provided a method of controlling a resin impregnation process and resin impregnated materials as controlled by such a method. The method may also be used to determine the level of resin impregnation in resin impregnated materials, and in particular in composite materials which comprise a fibrous reinforcement material and a resin material. In this way, the quality of the resin impregnated materials can be measured.
Claims (25)
- CLAIMS1. A method of controlling a process for the manufacture of a multicomponent sheet material having a desired pre-determined parameter comprising applying an acoustic or an electromagnetic signal to interact with the sheet material whereby the interaction modifies the applied signal, detecting the modified signal, comparing the modified signal or data derived from it with data relating to the pre-determined parameter and modifying at least one step of the process whereby the data relating to the modified signal is modified towards the data relating to the pre-determined pa ra meter.
- 2. A method according to claim 1, wherein the applied signal comprises an acoustic signal in the form of an ultrasound signal.
- 3. A method according to any of the preceding claims wherein the process is a continuous process.
- 4. A method according to any of the preceding claims wherein the multicomponent sheet material is selected from a laminate and a pre-impregnated fibre reinforced structure.
- 5. A method according to claim 4 wherein the laminate or pre-impregnated fibre reinforced structure is produced in a process comprising an impregnation step comprising contacting a resin with a reinforcement material and one or more further steps selected from a compaction step, a lamination step, a consolidation step and a curing step and wherein at least one step of the process is modified during the process in response to the comparison of the detected signal with the data relating to the pre-determined parameter.
- 6. A method according to any one of the preceding claims wherein the at least one step of the process is modified continuously during the process thereby to provide in-line feedback control.
- 7. A method according to any one of the preceding claims wherein the process is a continuous process and comprises contacting a resin dispensed from an applicator with a reinforcement material and passing the material between compression rollers wherein the at least one step of the process which is modified in response to the detected signal is selected from the compression of rollers, the distance between the resin applicator and the reinforcement material, the temperature of resin, the flow rate of the resin and the line speed of the process.
- 8. A method according to any one of the preceding claims wherein the signal is transmitted through the thickness of the sheet and is measured to determine a first parameter of the sheet.
- 9. A method according to claim 7 wherein the transmittance of the signal through the thickness of the sheet is measured to determine a first and a second parameter of the sheet.
- 10. A method according to claim 8 wherein the first parameter and second parameter are selected from the level of impregnation of the sheet and the thickness of the sheet.
- 11. A method according to any one of the preceding claims wherein the line speed of the process is modified in response to a comparison of the data derived from the detected signal and data relating to a pre-deterniined parameter which correlates with a pre-determined level of impregnation of the sheet and/or the thickness of the sheet.
- 12. A method according to any one of the preceding claims wherein the signal interacts with the sheet material and one or more parameters selected from the transmittance of the signal through the sheet, the velocity of the detected signal and the time of transmission of the signal through the sheet is detected.
- 13. A method according to any one of the preceding claims which comprises correlating the detected signal with two or more desired pre-determined parameters of the sheet.
- 14. A method of producing a multicomponent sheet material selected from a laminate and a pre-impregnated fibre reinforced structure wherein the sheet material has a desired pre-determined parameter which deviates throughout the multicomponent sheet material by less than 10% from the desired pre-determined parameter by controlling the process for the manufacture of the multicomponent sheet material using a method according to any one of claims 1 to 13.
- 15.A method according to claim 14 wherein the desired pre-determined parameter is selected from the level of impregnation of the reinforcement material and the thickness of the sheet.
- 16. A method according to claim 15 wherein wherein the level of impregnation deviates throughout the sheet material by less than 10% from the desired pie-determined level of impregnation.
- 17. A method according to claim 15 wherein the thickness of the sheet deviates throughout the sheet material by less than 10% from the desired pie-determined thickness of the sheet.
- 18. A quality-verified pre-impregnated fibre reinforced structure comprising a roll of a multicomponent sheet matenal selected from a laminate and a pie-impregnated fibre reinforced structure obtained by a process controlled by method according to any one of claims ito 13 which has not been subjected to off-line quality control analysis.
- 19.A structure according to claim 18 which has not been subjected to a water pick-up test.
- 20. A method of calibrating a measurement signal apparatus for use in a method of controlling a process for the manufacture of a multicomponent sheet matenal having a desired pie-determined parameter comprising manufacturing a multicomponent sheet material applying an ultrasound signal to interact with the sheet material during its production, detecting the measurement signal after interaction with the sheet matenal, analysing one or more parameters of the sheet matenal by a water pick-up method and correlating the detected measurement signals with the results of the water pick-up method thereby to calibrate the detected measurement signal results with the one or more parameters of the sheet material.
- 21. A process controller for controlling a process for the manufacture of a multicomponent sheet material having a desired pre-determined parameter which comprises contacting a resin dispensed from an applicator with a reinforcement material and passing the material between compression rollers and applying an ultrasound signal to interact with the sheet material whereby the interaction modifies the ultrasound signal, detecting the modified ultrasound signal, comparing the modified ultrasound signal or data derived from it with data relating to the pie-determined parameter and modifying at least one step of the process, the controller comprising: i) a process parameter controller for controlling one or more the parameters in the process selected from the level of force exerted by the compression rollers, the distance between the resin applicator and the reinforcement material, the temperature of the resin, the flow rate of the resin and the line speed of the process; U) a comparator for comparing the detected ultrasound signal or data derived from it with data relating to the desired pre-determined parameter; Ui) a parameter modifier for receiving data from the comparator and providing a signal to the process parameter to modify at least one of the parameters in the process whereby the actual value of the pre-determined parameter approaches the desired value of pre-determined parameter.
- 22. A controller according to claim 21 wherein line speed of the process is controlled in response to measured ultrasound signal.
- 23. A production line for producing a roll of a multicomponent sheet material comprising impregnation apparatus for contacting a resin with a reinforcement material and one or more further apparatus selected from compaction apparatus, lamination apparatus, consolidation apparatus and curing apparatus and ultrasound apparatus adapted to apply ultrasound to the sheet and to detect an ultrasound signal and a process controller according to any one of claims 21 and 22.
- 24. A pre-impregnated fibre reinforced structure comprising a roll of a multicomponent sheet material selected from a laminate and a pre-impregnated fibre reinforced structure wherein at least one parameter of the multicomponent sheet material has been altered during production of the roll in response to data obtained from ultrasound measurements carried out during the production of the multicomponent sheet material.
- 25. A pre-impregnated fibre reinforced structure according to claim 24 wherein the at least one parameter of the multicomponent sheet material has been altered in a process as claimed in in any one of claims 14 to 17.