GB2411652A - High germanium content wavequide materials also containing titanium - Google Patents

Abstract

The core and/or cladding of the waveguide is made from silica germania titania glass. The glass has molar ratios Ge/ (Si + Ge + Ti) = 0.08-0.17 and Ti/ (Si + Ge + Ti) = greater than naught to 0.08, and preferably a refractive index = 1.48-1.52 at 1550 nm and coefficient of thermal expansion at room temperature = 3 x 10<-6> -4.4 x 10<-6> {C<-1>. The refractive index of the core layer is higher than the refractive index of the cladding layer. The layers are deposited by plasma enhanced chemical vapour deposition. The wave guides are used in liquid crystal based cross-connect optical switching devices.

Description

24 1 1 652 HIGlI GERMANIUM COMMENT WAVEGUIDE MATERIALS CROSS-CE TO

'PLICAON This application claims priority to U.S. Provisional Application No. 60/267,909, entitled HUGE GERMANIUM CONTENT GE-STCON OXIDE AND OXYNrrRIDE WAVEGDES, filed February 9, 2001, and U.S. Patent Application No. 09/917,039, entitled HIGH GEPMANI CONTENT WAVEGUIDE MATERIALS, filed July 27, 2001.

BACEGROLND OF 1; vENiIoN

Field of the Invention

The present invention relates to germaium-silicon oxide, germnTum-silicon oynitride and silica-germ=a-titania materials containing large cation fractions of germanium, processes to deposit and density these materials, and more particularly to such materials that are suitable for use in optical waveguides.

Technical Background

Planar optical devices are comprised of a waveguide core embedded in a waveguide cladding material, wherein the waveguide core has an index of refraction that is higher than the index of refraction of the cladding. The device is generally supported by a substrate. The waveguide core and cladding materials are typically either a silica-based glass or a polymer. Silica glass materials can be deposited by flame hydrolysis deposition (FHD), chemical vapor deposition (CVD), plasma enhanced chemical vapor deposition (PECVD), and physical vapor deposition, including sputtering, electron beam deposition, etc. Flame hydrolysis deposition and plasma enhanced chemical vapor deposition are preferred techmques for depositing silica-based glass waveguide materials (including cladding and core) because these techniques allow higher production rates and the resulting waveguides exruir low propagation losses. Because planer optical devices are typically designed for use with silica optical telecormnunications fiber, the refractive index (n) of He waveguide mars of Ale planar optical device is ty?icaDy matched to that of the fiber (usually n is about t.44 at 1550 am). The dimensions of the waveguide core are typically about 8,um in width, and the refractive index of the core typically exceeds the refractive index of the cladding by between about 0. 2% and about 2%. This refractive index difference between a waveguide core and cladding is generally achieved by doping the core material with nitrogen or a higher refractive index oxide such as germania, phosphorous trioxide, titania, zirconia, etc. in order to raise its refractive index above that of the cladding. Alternatively, dopants such as boron and fluorine may be added to the cladding to depress its refractive index below that of the core.

The fabrication of a planar optical cross-connect signal switching device based on liquid crystal cells may be performed using prismatic liquid crystal cells and a planar waveguide circuit that matches the ordinary refractive index of the liquid crystal. For a typical liquid crystal (e.g. , BL009, described herein) the ordinary refractive index at 1550 nanometers is on the order of 1.501. Thus, a preferred planer waveguide circuit for use in a liquid crystal-based cross-connect dence has a refractive index at 1550 am of about 1.501. Use of a typical planer light wave circuit with a refractive index matched to silica (n= 1.44 at 1550 nm) leads to degradation of the optical performance of the cross-connect (i.e., increased optical cross-talk).

Because liquid crystal based optical cross-connect switching devices requires a ground electrode for applying an electrical field across the liquid crystal-filled trench in order to alter the orientation of the liquid crystal molecules to achieve switching, the use of a silicon substrate upon which the ground electrode may be deposited or a single crystal silicon substrate doped to be conductive is highly preferred when fabricating such devices. In older to prevent large thermal stresses which can cause strain-induced bireDingence and excessive wafer curvature [which complicates photolithography and aliment of input and output optical fibers (pigtails)], it is unportant that the waveguide material, in addition to matching the ordinary refractive index of the liquid crystal 550 - 1.501), also have a coefficient of thermal expansion that matches that of the silicon substrate.

Silicon outride glass materials having a retractive index of about 1.5 at 1550 mn may be made by adjusting the nitrogen content of the glass. However, a Si5Yi TOIL 9,77rn a rechart He index of about 1.S at 1550 mu would have a coefficient of thermal expansion of about 1 x 10-6 C', as compared with a coefficient of thermal expansion of about 3.8 x 10-6 oCi for a silicon substrate. The low coefficient OI thermal expansion (relative to silicon) of the SiON film having a refractive index of 1.5 at 1550 am would consequently result in a large film strain and wafer curvature.

In addition, adding nitrogen to the glass also increases the concentration of N-H bonds. The N-H bond has an overtone at 1510 um which causes strong optical absorption in the 1550 nm communication band.

Thus, in order to fabricate planar optical cross-connect optical signal switching devices based on liquid crystal cells, there is a need for optical waveguide materials having a refractive index of about 1.5 at 1550 am (i.e., matched to the ordinary refractive index of the liquid crystal) and a coefficient of thermal expansion of from about 3 x lo - Ci to about 4.4 x 10 - C' (i.e., matched to a silicon substrate).

SUMMARY OF To {NVENON

This invention provides glass waveguide materials having a refractive index of about 1 5, and a coefficient of thermal expansion of from about 3 x 10 - C3 to about 4.4 x 10 - C' . Because these materials have a refractive index closely matched to the ordinary refractive index of a typical liquid crystal material, and a coefficient of thermal expansion closely matched to that of a silicon substrate, the materials of this invention are extremely useful for the fabrication of waveguides for use in liquid crystal based cross-connect optical switching devices.

accordance with one preferred aspect of this invention, a germaniumsilicon oxide or germanium-silicon oxynitride glass composition having a Ge/(Si + Ge) mole ratio of from about 0.25 to about 0.47 and an N/(N + O) mole ratio of about 0.1 or less is used in a liquid crystal based crossconnect optical switching device. The germaninm-silicon oxide or oxynitride glass compositions of this invention preferably have a eactive mdex of Dom about 1.48 to about 1.52 at 150 mn and a coefficient 0 of thermal expansion at room temperature of from about 3 x 10 - C' to about 4.4 x C ' Acdionaiy this mvenio provides a process to density flints of germamm- silicon oxide glass compositions having a Ge/(Si+Ge) ratio from about 0. 25 to about 0.47, and a process to deposit [ally dense films of germanium silicon oxynitride glass which have a composition having a Ge/(Si Ge) ratio of from about 0.25 to about 0.47 and an N/(N O) ratio of about 0.1 or less.

In accordance with another preferred aspect of this invention, a silicagermania-titania glass composition having a Gel(Si Ge + Ti) mole ratio of from about 0.08 to about 0.17 and a Ti/(Si Ge Ti) mole ratio of from zero to 0.08 is provided for use in a liquid crystal based cross-cormect optical switching device. The silica-germania-titania glass compositions of the invention preferably have a refractive index of from about 1.48 to about 1.52 at 1550 rim, and a coefficient of thermal expansion at room temperature of from about 3 x 10 - C to about 4.4 x 10 - C' . Additional features and advantages of the invention will be set forth in the detailed description which follows and will be apparent to those sldlled in the art from the description or recognized by practicing the invention as described in the description which follows together with the claims and appended drawings.

It is to be understood that the foregoing description is exemplary of the invention only and is intended to provide an overview for the understanding of the nature and character of the invention as it is defined by the claims. The accompanying drawings are included to provide a furler Understanding of the invention and are incorporated and constitute part of this specification. The drawings illustrate various features and embodiments of the invention which, together with their description serve to explain the principals and operation of the invention.

25BRIEF DESCRIPTION OF ME DRAWINGS

Fig. 1 is a graph of estimated refractive index for a germaninin-silicon oxynitride system, Fig. 2 is a graph of estimated coefficients of thermal expansion for a germanium-silicon oxyrutride system; 30Fig. 3 is a graph showing tile compositional range for a germamum- silicon oxyniide material having an index of refrac+;on of from about 1. 48 to about 1.52 at 53 is, Ad ccc o- i elms -rnQn of wom about 3 10 C ' to about 44x 1o-6OC Fig. 4 is a block diagram of an exemplary cross-connect system; Fig. 5 is a detailed schematic diagram of a 2x2 cross-connect system of Pig. 4,

Fig. 6 shows a cross-sectional side view of an exemplary LC prism in a planar waveguide; Figs. 7A and 7B are cross-sectional side views of LC prisms in two different alignment states; Fig. 8 is a perspective view of an LC prism functioning as a polarization splitter; Fig. 9 is a perspective view of an LC prism functioning as a polarization combiner; Figs. lOA and 1OB are perspective views of an LC prism functioning as a TE lS switch and shown in its two different states; Figs. 11A and l1B are perspective views of an LC prism functiorung as a TM switch and shown in its two different states; Fig. 12 is a graph of a typical annealing temperature cycle which win fully densify a germnium-silicon oxide film that contains a large cation fraction of germanium; Fig. 13 is an PTIR spectrum of a germonimn-silicon oxymtride film; Fig. 14 is a graph comparing refractive index at lSSO Tm, (lo*) and elemental composition (right) of the germanium-silicon oxide films deposited by the process of example A in Table 2, and the germanium-silicon oxynitride films deposited by the process of example C in Table 2; Fig. 15 is a graph showing slab waveguide loss as a function of wavelength for germaniurn- siIicon oxynitride planar waveguides deposited by conditions listed in example C in Table 2, with slab waveguide loss being measured with a dual prism coupler; Fig. 16 is an STIR spectrograph of an as-deposited germamum-silicon oxynitride under-clad/core formed under the conditions listed in example C in Table 2;

G

T_;>c, '7 is a plot Of reLac-Yc de- a. me souls -one as a function of mole percent TiO, for silica-titania glasses; Fig. 18 is a plot of die coefficient of thermal expansion verses mole percent TiO2 for silicatitania glasses; Fig. 19 is a plot of the refractive index at 1550 rim verses mole fraction CleO 2 for silica-ye mania glasses calculated using rule of Endures; Fig. 20 is a plot of coefficient of thermal expansion verses mole fraction GeO 2 of siiica-gennaaia glasses calculated using rule of mixtures; Fig. 21 is a graph of estunated refractive index at 1550 am for a silica germania-titania system; Fig. 22 is a graph of estimated coefficients of thermal expansion for a silica gerrnania- titania system; and Fig. 23 is a graph showing the compositional range for a silica-germania tita,a material having an index of refraction of from about 1.48 to about 1.52 at 1550 am and a coefficient of thermal expansion of from about 3 x 10 C' to about 4.4 x - C' DETAILED DESCRIP=ON OF THE PRIED EMBODIMENTS In one aspect, the invention provides compositions of germaniuTn-silicon oxide (GeSiO) and outride (GeSi0N) suitable for the fabrication of liquid crystal based cross-connect optical switching devices based on total internal reflectance using prismatic liquid crystal-filled trenches. The GeSiON composition range of interest for use in liquid crystal based cross-connect optical switching devices may be estimated from the end members of Me GeSiON system using rules of mixtures. As used herein, end members are the pure metal oxides and nitrides Tom which the composition may be derived. The refractive index and coefficient of thermal expansion for the end members of the system (SiO 2, GeO2, Si3N4, and Ge3N4) are shown in Table 1.

able 1 ;e.lactve Eden And -e 1 easvn data for -eSiCN em members.

n63:nm nl550mn a*l07 ( C') Density (g/mL) SiO2 1.4578 1.444 2.63 GeO2 1. 650 1.587 64 4.228 Si3N4 1.95 1.91 30 3.1 Ge3N4 2.23 2.14 48 5.25 Fig. 1 is a graph showing lines of constant refractive index for GeSiON systems estimated from the end member values. The refractive index of GeSiON glasses follows the rule of mixture by mole fraction. Fig. 2 shows lines of constant coefficient of thermal expansion for GeSiON systems estimated from the end member values. The coefficient of thermal expansion of these glasses follows the rule of mixture by volume fraction. From the estimated refractive indices and coefficients of thermal expansion shown in Figs. and 2, it was determined that a refractive index of about 1.5 at 1550 am, and a coefficient of thermal expansion of from about 3 x - C-' to about 4.4 x 10- Ci can be achieved when the Gel(Si + Ge) ratio is from about 0.25 to about 0.47, and the N/tN + O) is 0.1 or less. Fig. 3 shows the composition region 10 of interest, wherein an index of refraction of from about 1.48 to about 1.52 at 1550 run, and a coefficient of thermal expansion of from about 3 tic - C-' to about 4.4 x 10 C1 is achieved. The desired compositions may be represented in terms of parameters x and y by the idealized, hydrogen- free formula Si,_xGe ON I, wherein x and y may range from 0 to 1. The region of primary interest is centered at a Ge/(Ge + Si) ratio of about 0. 35 and an N/(N + O) ratio of about 0.05, with suitable compositions having a Ge/(Si + Ge) ratio of from about 0.25 to about 0.47 and an N/(N + O) ratio of from about 0 to about 0.1.

The germanium silicon oxide or oxynitride films which comprise the core and cladding of the Qp6C waveide me preferably depos ted by clench vapor deposition (CVD). Low pressure CVD (LPCVD), atmospheric pressure CVD (APCVD) and plasma enhanced CVD (PECVD) can be used. However, PECVD is the preferred method. Examples of PECVD deposition are described below.

C-.Q AT US The germanium silicon oxide and oxynitride films of this invention were deposited by PECVD using a STS Multiplex PECYD system. This system comprises a parallel plate reactor where the precursor gases enter through an array of holes in the top electrode (showerhead), and the sample rests on the bottom electrode. The system is pumped with a blower, and a plasma may be formed by either a low frequency (375 kHz) or high frequency (13.56 MHz) RF generator and matching networks. Al+.erna+ nvely, a plasma may also be formed using both generators either by pulsing, or operated simultaneously as described in U.S. Pat. No. 4,464, 223.

Germanium silicon oxide films are formed using silane (SiH4), deuterated silane (SiD4), germane (GeH4), deuterated germane(GeD4), and a suitable carrier gas. Germanium silicon oxyrutode films are formed using silane (SiH 4), deuterated silane (SiD4), germane (GeH4), nitrous oxide (N2 O), n trogen (N2), optionally ammonia (Nob) or deuterated ammonia (Nits), and a suitable carrier gas.

Alternatively, germanium silicon oxide,51ms may be formed from tetraethexysilane, tetramethoxygermane, oxygen, and nitrogen or suitable carrier, and germanium silicon oxynitride films may be formed from tetraethoxysilane, tetramethoxygermane, oxygen, arurnonia or deuterated ammonia, and nitrogen or suitable carrier are used.

A more comprehensive list of possible silicon precursors includes, but is not limited to, silane, disilane, dichlorosilane, silicon tetrachloride, tetraethoxysilane, tetramethoxysilane, diacetoxydi-sec-butoxysilane, diethoxysilane, tetrakisdiethylaminosilane, tetrakisdimethylaunosilane, octarnethylcyclotetrasiloxane, tetramethylcyclotetrasiloxane and bis-tbutylaminosilane. Possible germanium precursors include, but are not limited to, germane, digermane, germanium tetrachloride, tetramethoxygerrnane, tetraethoxygermane, tetramethylgermane, tetraethylgermane, diethyldichlorogerrnane, and octamethylcyclotetragermoxane.

Possible oxidizers include, but are not limited to, nitrous oxide, nitric oxide, oxygen, and ozone. Possible nitrogen sources include but are not limited to ammonia, deuterated ammonia, trimethylamine, and hydrazine. Possible carrier gases include but are not limited to nitrogen, argon, helium, xenon, krypton, neon, and hydrogen.

e A so enable, a be, s 1;CAn oxide underclad corker sed of two 8 Am thick layers, each deposited Under the conditions listed as "EX. A lo clad" in Table 2, was formed. On top of this, a 6.25 1lm germanium silicon oxide core with a refractive index contrast of =0.34% was deposited under the conditions listed as "EX. A core" in Table 2. Because these layers were only 98% dense as deposited, each layer was annealed to density the film before subsequent layers were deposited A typical temperature cycle is shown ill Fig. 12. Annealing was performed in an oxidizing atmosphere, with or without steam to suppress the reduction of gerrnim oxide. A cooling rate greater than 200 C/hr from the maximum temperature of 1,100 C to below the strain point of the glass was required to prevent phase separation into germanium rich and germanium poor phases. The core was patterned and etched using conventional photolithography and reactive ion etching techniques.

The patterned core was overcladded with 16-20 Em thick of glass having a refractive index matched to the underclad. The overclad can be deposited using either PECVD is or FUD. Straight waveguides created by this process have wavegruding losses as low as 0.09 dB/cm Doss of 0.59 dB measured for a guide 7.2 cm in length, and a 0.2 dB fiber-to-guide coupling loss was assumed.) In the second example, a 16,um thick germamurn silicon oxynitride underclad layer was deposited umder the conditions listed as "EX. B clads in Table 2. On top of this, a 6.25 thick gerrnamum silicon outride core with a refractive index contrast of An=0.88 was deposited under the conditions listed as "EX. B core" in Table 2. These layers were 100% dense as deposited, and may be deposited in one continuous process, or in discrete process steps.

The core was patterned and etched using conventional photolithography and reactive ion etching techniques. The patterned core is overcladded with a 16-20 Em thick layer of glass having a refractive index matched to the underclad. The overclad can be deposited using either PECVD or PlID. Slab waveguide losses as measured by a prism coupling system were 3.4 dB/cm as deposited. Annealing at 400 - 600 C - ogre o- other mert gas reduced slab wave-de losses to 2.S dB,cm. The FTIR spectrum of a germanium silicon oxynitnde film is shown in Fig. 13. This spectrum shows that the origin of the optical loss is the overtone of the N-H absorption band. lo

n a - file, a ib i-'.: get siv c,.;;,e ',d=ci layer was deposited under the conditions listed as "EX. C clad" in Table 2. On Top of this, a 6.25 Em thick core with a reactive index contrast of An=0 39% was deposited under the conditions listed as "EX. C core" in Table 2. A nitrogen source that is free of hydrogen-nitrogen bonds is preferred. Examples of suitable nitrogen sources include nitrogen gas and nitrous oxide. In this process, high frequency (13.56 MHz) RF power was applied to the top electrode to increase gas disassociation, and low frequency (typically 380 HIz) Rat was applied to the bottom electrode on which the sample rested to provide a negative substrate bias. This process, known as triode mode, provided increased ion bombardment of the sample.

These layers were 100 % dense as deposited, and may be deposited in one continuous process, or in discrete process steps. Fig. 14 shows the filth refractive index and elemental composition as measured by electron microprobe as a function of the gas phase germane mole fraction of hydrides. For an equal germane mole fraction, films deposited with the process described by example C are higher in refractive index than those deposited from the process of example A. The origin of this increase in refractive index is not a higher germanium content, because the microprobe results show that the germane cation mole fraction did not change. The origin of the increase in refractive index can be seen in Fig. 15, which shows the slab waveguide optical loss as a function of input wavelength for the as-deposited underdadlcore Slab waveguide loss at 1550 nm is only 0.3 dBlcm, however a strong loss peak of 1 dB/cm is observed at l51O am. Fig. 16 shows the FfIR spectra of this sample. The tT1x spectrum shows the origin of the 1510 nm absorption peak is an overtone of the N,-H bond seen at 3450 cm' in the FTIR Thus the FTIR and slab waveguide losses indicate that under the conditions of example C, nitrogen is incorporated into the film. Furthermore, the width of the NH bond is narrower than films deposited with ammonia (example B), indicating less variation in the N-H bond angles.

Recipe I1) EX. A Em. A EX. B EX. B EX. C EX. C clad Core Clad core clad core 13.56 MHz RI; (W) on top 70 70 3801dIz RF (W) on top 400 400 400 400 3801dIz RF (W) on bottom 200 200 Pressure (mtorr) 350 350 350 350 300 300 Substrate Temperature ( C) 350 350 350 350 350 350 Showerhead Temperature 250 250 250 250 250 250 C'

J

5% SiH4/Ar (sccm) 165 130 300 248 165 130

_

2o GeH4/Ar (sccm) 250 250 250 1 380 250 250 N20 (scum) 1500 1500 1250 1866 1500 1500 NDs (scam) O O 50 40 O O Deposition Time (mm) 60 52 110 35 120 52

Table 3

Recipe ID EX. A EX. B EX. C Clad Index at 1550 nm 1.4959 1.4924 1.5001 Clad thickness (pm) 16.0 22.36 15.96 Core Index at 1550 mn 1.5021 1. 5056 1.5059

_

Core Thickness (pm) 6.25 7.84 6.13 (%) 0.34 0.88 0.39 Wafer Thickness (pm) 1000 525 525 Stress (MPa) -27.3 - 119.0 38.2 In accordance with another aspect of this invention, compositions of silica germaDia-titania (SiO 2 -GeO 2 -TiO 2) that are appropriate for fabrication of a low index optical cross-cormect optical switching device based on internal reflectance using prismatic liquid crystal cells and the process for depositing optical quality films of these materials are disclosed. The silica-germania-titania composition range of -,e, lair -use if sigma c^,-s^' 'cased c.oss-ccr act ouch 57iTC''g devices May He estimated from the binary systems sillca-ti,ania and silica-germania assure ng no interaction terms. For the silica titania binary system, a linear fi; of refractive index and coefficient of thermal expansion data available the "Handbook of Glass Properties," (13ansal, Narottam P. and Doremus, R. H., Academic Press (1986), Orlando, pp. 138 and 552) was performed. (Figs. 17 and 18). From available literature data and data from PECVD deposited samples, it has been shown Blat the refractive index of siica-gennania glasses follows the rule of mixture by mole fraction (Fig. 19), and that the thermal expansion of bulk glasses follows the rule of mixture by volume fraction (Fig. 20). The refractive index of silica-germania compositions was estimated from a linear fit of the rule of mixture curves, and thermal expansion was estimated from a quadratic fit.

For silica-titanua glasses, the linear coefficients for change of refractive index and thermal expansion with change of composition in mole percent titania is shown in Table 4. It was assumed that the linear coefficient for refractive index at 1550 am is equal to that at sodium line.

Table 4

An/(mol%TiO2),%-l | /(a10')/(mol%TiO2), I% 0.311 -1.195 Linear coefficients for change of refractive index at 1550 nm and coefficients for quadratic fit of thermal expansion with change of composition in mole percent germania for silica-germania glasses are shown In Table 5.

Table 5

\ al /\ (mold GeO2), %-' | 107) | /\ (a.103/ (md%GeO2).C'% I 2 ((a.107)/ by 2 (md%GeO2)o2%-2 0.143 1 7.731 1 99.723 1 -32.035 The estimated refractive index and thermal expansion of silica-gerrnania titania glasses are shown in Figs. 21 and 22 respectively. The region of interest can be defined by a refractive index at 1550 em of from about 1.48 to about 1.52 and a coefficient of Animal en sion of Tom about 3 x 10 - C to about 4.4 x 10-6 C2. The silica-germania-titania glass compositions of interest are - approXaa-,el'- 8-i, mole percent ge,rlia <-TeO 1) and 0-8- mole percent imTua (TiO2). Compositions of interest are shown as region 533 in Fig. 23.

Silica-germaTIia-titania glass Elms can be deposited, for example, by plasma enhanced chemical vapor deposition (PECVD). These films can be deposited from a variety of precursors. Possible silicon precursors include, but are not limited to, silane, disilane, dichlorosiliane, silicon tetrachloride, tetraethoxysilane, tetramethoxysilane, diacetoxydisecbutoxysilane, diethyoxysilane, tetrakisethylammosilane, tetrakisdimethylaminosilane, octamethylcyclotetrasilane, tetramethylcyclotetrasilane and bis--butylaTrunosilane. Possible germanium precursors include, but are not limited to, germane, digerrnane, germanium tetrachloride, tetramethoxygermane, tetraethoxygeTmane, tetramethylgermane, tetraethylgermane, diethyldichlorogermane, arid octamethylcyclotetragermoxane.

Possible titanimn precursors include, but are not limited to titanium tetrachloride, titanium isopropoxide, tetrakisdiethylaminotitanium and tetrakis(trnethylsiloxy)titanium. Possible oxidizers include, but are not limited to, nitrous oxide, nitric oxide, oxygen and ozone.

SiO2eO2-TiO2 EXAMPLES Silica-germania-titania Slims were deposited by PCVD using a STS Multiflex PECVD system. This is a parallel plate reactor where the precursor gases enter through an array of holes in the top electrode (showerhead), and the sample rests on the bottom electrode, a non-rotating heated platen. The system was pumped with a roots blower, and either a low frequency (3751(Hz) or high frequency (13.56 MHz) RF generator and matching network were used to form a plasma. Available process gasses were silane (SiH4), germane (GeH4), deuterated ammonia (ND3), nitrogen (N' ), tetraethoxysilane (TEDS), tetramethoxygermane SMOG), trimethylborate (11) trimethylphosphite (TMPi), and oxygen. Titania sources such as Titanium isopropoxide (TIP) and tetrakis(trimethylsiloxyl)titaniuTn (TTMST) were introduced with a Ash-evaporator liquid delivery system. Other process gasses may be used, such as, for example, deuterated germane and deuterated silane, as would be apparent to the skilled artisan.

Two series o'-wafels were depos,ed USLI18 Be <V yes+ described above in connection with the C-eSiON examples over the composition range of interest using TEOS, TMOG, O I, and either TIP or TTMST. Samples were deposited on 100 mm Si wafers, and 3 inch quartz wafers. Wafer curvature was determined prior to and after deposition, and a film stress was calculated. The refractive index, optical propagation loss, and film thickness were determined with a prism coupling system (Metricon). The concentration of [OE0, [SiO], [GeO] and [TiOj species were examined by infrared spectroscopy, and composition were determined by electron microprobe. Film ther nal expansion coefficients were determined by measuring bending of coated silicon and quartz wafers as a function of temperature. Recipes for core and clad compositions with 'in = 0.75% and 0.34% were determined by fitting experimental data, depositing films, and re-iterating the model.

The resulting silica-germania-titaria Alms are useful for fabricating low index planar light wave circuits appropriate for a liquid crystal crossconnect switching device based on total internal reflectance of prismatic shaped liquid crystal-filled trenches. The composition achieves the desired refractive index (from about 1.48 to about 1.52) with low wafer wa7;page. Because of the greater surface mobility of me.allorganic precursors, problems associated with the root crack should be avoided.

In addition, this all oxide composition is stable and reflowing is possible.

LC CROSS-CONNECT DEVICE

Fig. 4 shows an exemplary cross-connect system which may incorporate the GeSiON and GeOz-SiO'-TiO: materials of this invention. This system isdescribed fully in commonly owned and copending U.S. Patent Application 091604,039, which is incorporated herein by reference. Lee system comprises an input port 110 coupled to a polarization splitter 120. The splitter 120 is coupled to a TM switch array 130 and a TE switch array 140. Switch arrays 130, 140 are coupled to a polarization combiner 150, in turn coupled to an output port 150. The input port 11 O is a linear array of planar waveguides 'o which an array of fibers can be pigtailed. The spacing between wavegrudes is determined by pigtailing capabilities. Light from the fibers enters Me input port 110 and is transnutted to the polarization splitter 120. i3

bile poiarwaion 3p separates It LONG id HIM " l-E cGmpoe,s. The TM components are then passed to Me TM switch array 130, and the TE components are passed to the TE switch array 140. As described in further detail below, the outputs of the switch arrays 130 and 140 are combined by the polarization combiner 150 and passed to the output port 160. Similar to the input port 110, the output port is a linear array of planar waveguides to which an array of fibers can be pigtailed. TM and TE are defined herein by convention at the LC trench interfaces, and not by waveguide convention.

Fig. 5 is a detailed view of the cross-connect system of Fig. 4 with the exemplary cross-connect being a 2x2 cross-connect. The LC prism elements are prismatic liquid crystal-filled trenches. Light from the input port 110 that enters the polarization splitter 120 which includes a pair of LC prisms 125 that reflect the TE waves to the TE switch array 140 while passing the TM waves to the TM switch array 130 as shown, for example, in Fig. 8 and described below. The switching arrays 130, 140 are preferably between about 50 and 500 Em center to center, and more preferably about 250 gum center to center. Each switch array 130, 140 has a plurality of LC (liquid crystal) prism switching elements 135, 145 in each path 131 132 and 141-142, respectively, as shown, for example, in Figs. lOA, 10B, 11A, and 11, as described below. A single switching element in each paw is set to a reflecting state to pass the light onto the polarization combiner 150. It should be noted that the path length for the TE and TM waves are substantially identical. The polarization combiner 150 includes a pair of LC prisms 155 that each allow the TE wave to pass while reflecting the TM wave to recombine, as shown, for example, in Fig. 9, described below. Thus, the beams are recombined and passed to the appropriate path in the output port 160.

The polarization splitter 120, the switching arrays 130, 140, and polarization combiner 150 are preferably formed with the same fundamental element, which is preferably an LC prism 235 that is formed as a prismshaped LC-filled trench in a planar waveguide, as shown in Fig. 6. The structure fimctions as the desired element depending on an applied voltage, as described below.

The support plate or substrate 210 on which the waveguide is patterned preferably has five deposited layers thereon. The first layer is a first electrode 220, -2 a^ No ret' a,, ee^'-n" Blat ^crs^ a:: " - ae^.e c--=c--e champ sue' as gold, aluminum, or iridium tin oxide. The grounding electrode can be either a single electrode or a senen.ed electrode. A cladding layer 230 is deposited on the first electrode 220, and comprises a cladding layer having a thickness between about 12 and 50 Em thick for the planar waveguide. A core layer 240 is deposited on the cladding layer to a thickness between about 4 and 10 An. A cladding layer 250, similar to the cladding layer 230, is formed above the core layer 240 to a thickness between about 12 and 50 m. The layers 230, 240 and 250 are etched through a photolithographically defined mask or otherwise patterned to form prism-shaped trenches 236 that provide the grid structure of l?ig. 5. As discussed further below, the trench is shaped to define a prism, and is preferably shaped as a triangle.

In accordance with the principles of this invention, core layer 240 and cladding layers 230 and 250 are fabricated, such as with plasma enhanced, chemical vapor deposition, from a GeSiON glass composition having a Gel(Si + Ge) ratio of from about 0.25 to about 0.4 and an N/(N + O) ratio of 0 to about 0.1, whereby the refractive index of the material is from about 1.48 to about 1.52 at 1550 mn, and the coefficient of thermal expansion at room temperature is from about 3 x 10- C-1 to about 4.4 x 10 - C-I. It will be understood by those having ordinary skill in the art that the refractive index of the material comprising core layer 240 will be slightly higher (e.g., typically less Man I % higher) than the refractive index of the cladding layers 230, 250. As can be seen by reference to Fig. 1, this can be most easily achieved by using a slightly higher nitrogen or titania content in the core layer than in the cladding [ayes.

A first alignment layer 255 is disposed above the cladding layer 250 and on the walls of the trench 236 formed by the etching or patterning of layers 230, 240, and 250. The alignment layer 255 comprises a thin copolymer layer or other material, such as an obliquely evaporated SiO, silane coupling agents, or a polymer to assist in homeotropic alignment of LC material in the LC layer 260. The alignment layer 255 is preferably deposited to z thickness of be,-veen one monolaye; and about 100 monolayers (e.g., irorn about 5 nm to about 500 mu). The alignment layer 255 should be thin enough to avoid creating an optical effect due to its refractive index.

The liquid crystal layer 260 is then deposited over the first alignment layer 255 bow in me trench 26 and over one ciaacing layer you. Me nicmess or one liquid crystal material above the first alignment layer 255 is preferably less than about 25 m. Any liquid crystal material can be used, including those from the nematic class (preferred) and the ferroelectric class. One liquid crystal material that can be used is BL009 (EM Industries, Inc.), having a birefringence of about 0.28. It should be noted that the larger the birefrgence for the LC material, the more preferable the material is for use with the system of the present invention. The geometry of the prism trenches depends on the LC bireIringence, with larger bireIringences giving a smaller trench and more efficient switching.

A second alignment layer 265 is disposed on the LC layer 260. The second alignment layer 265 is preferably substantially similar in composition and thickness to the alignment layer 255, although this does not have to be the case.

A top plate preferably has two layers. The first top plate layer is a second electrode, such as an address electrode layer 270 that comprises a patterned conductive coating such as gold, aluminum, or indium tin oxide. The second top plate layer, which covers the first top plate layer, is a cover glass 280. The thickness of the layers 270 and 280 is not critical, as would be known by those skilled in the art, and each can have a thickness between about 0.3 and 300,um or every greater It should be noted that the fast and second electrodes can act as the grounding and address electrodes, respectively, or the first and second electrodes can act as the address and grounding electrodes, respectively.

Figs. 7A and 7B illustrate the orientation of the LC molecules of LC layer 260 in trench 236 without and with a voltage applied to the second electrode 270, respectively. With substantially no voltage applied, as shown in Fig. 7A, the LC molecules tend to align substantially perpendicular to any interface coated with a properly chosen first alignment layer. Therefore, the director axis inside the trench 235 lies in the plane of the waveguide fabric and perpendicular to the trench interface. When a sufficient voltage is applied to the address electrode, as shown in Fig. 7B the LC molecules rotate to align with the electric field. In this case, the director axis lies s'abSftially perpendicular to the substrate. A typical voltage Mat is sufficient to turn on the address electrode is between about 3 and volts. I he threshold voltage depends on the LC material bemg Bused and Me distance between the chic" OiGS " ',-"Ui] be rioted -age me namer me am lien yo fate nn'!e me TnTO5nni voltage, the faster the switch action.

Because the hirefringence of an LC material is typically on Me order or about 0.1 to 0.3, the optical properties for the TE and TM guided modes are substantially different and can be significantly changed with an applied field. As described below, the LC prisms can be used for polarization splitting, TE and TM switching, polarization combining, signal splitting, and variable optical attenuating.

An LC prism 235 utilized as a polarization splitting element 125 is shown in Fig. 8. The LC prism used as splitter 125 is shown with an electric field applied across the volume of the LC material so as to align the LC molecules perpendicular to the triangular facets in a similar orientation as illustrated in Fig. 7B. Since TE light is polarized parallel to the LC director, it experiences the extraordinary refractive index, He= 1.7, and is totally internally reflected at the back surface (i.e., the long side) of the LC prism triangle. TM light sees only the ordinary refractive index, no= 1.5, and passes through LC prism 235 without refracting or reflecting.

Fig. 9 shows an LC prism used as a polarization combiner 155. The LC prism is shown with an electric field applied across the volume of the LC material to align the LC molecules perpendicular to the triangular facets in a similar orientation as illustrated in Figs. 7B and 8. As shown, the TM light passes through combiner 155 without refracting or resecting while TE light is reflected at the back surface of the LC prism triangle. Both the TE and TM light thus exit the same side of the triangular prism.

Figs. 1OA and lOB show an LC prism used as a TE switch 145. In Fig. lOA, the LC prism is shown with no electric field applied across the volume of the LC prism. When no electric field is applied, the LC molecules are homeotropically aligned parallel to the triangular facets in a similar orientation as illustrated in Fig. 7A. The TE polarized light sees only the ordinary refractive index no in this case, and passes through the LC prism. When switching is desired, a voltage is applied across the first and second electrodes and hence across the volume of the prism thereby rotating and aligning the LC molecules vertically in the same orientation as in Figs. 7B, 8, and 3. Similar to the polarization splitter, the TE light reflects off the t,pQ ( se c7race or r e Em n7cm fr!nge Cal7n the T1;: light ^o erit the LC prism through a different face than is shown in Fig. lOA.

Figs. 11A and llB illustrate an LC prism used as a TM switch 13. Pig. llA shows the TM switch 135 with an electric field applied across the volume of the LC prism in which case the LC molecules are aligned vertically in the same manner as shown in Figs. 7B, 8, 9, and lOB. When in this state, TM light passes through switch 135 without refraction or reflection. Fig. llB shows the TM switch 135 when no electric field is applied to the LC prism. In this state, the LC molecules are aligned perpendicular to the thangle surfaces and are thus aligned in the same manner as in Figs. 7A and lOA. When in this state, TM light is reflected from the hypotenuse of the triangle and exit a different face of the triangle as shown in Fig. llB.

As will be apparent to those skilled in the art, the polarization splitting elements 125 and polarization combining elements 155 are bidirectional. Similarly, TM and TE switches 135 and 145, respectively, are also bi-directional. Thus, light signals may be input through output ports 160 and exit from input ports 110.

The foregoing description of the invention has been presented for purposes of illustration and description. It is not intended to be exhaustive or to limit the invention to Me precise fond disclosed, and modifications and variations are possible in light of the above teachings or may be acquired from practice of the invention.

The drawings and description were chosen in order to explain the principles of the invention and its practical application. It is intended that the scope of the invention be defined by the claims appended hereto, and their equivalents.

Claims (11)

1. CLAIMS: 1. A glass composition comprising a silica-gerrnania-titania

   having a Ge/(Si + Ge + Ti) mole ratio of from 0.08 to 0.17 and a Ti/(Si + Ge + Ti) mole ratio of from greater then Oto O.8.
2. 2. The glass composition of claim 1 exhibiting a refractive index of from 1.48 to 1.52 at 1550 nm, and having a coefficient of thermal expansion at room temperature of from3xlO6 C3 to4.4 x10-6 C-.
3. 3. A silica-germanian-titania glass composition according to claim 1 substantially as hereinbefore described.
4. 4. A planar optical device comprising: a waveguide core and waveguide cladding, wherein at least one of the waveguide core and the waveguide cladding is a silica-germania-titania glass having a Ge/(Si + Ge + Ti) mole ratio of from 0.08 to 0.17 and a Ti/(Si + Ge + Ti) mole ratio of from greater than O to 0.08.
5. 5. The planar optical device of claim 4, wherein the planar optical device is an optical switch having liquid crystal switches located at intersecting waveguides.

   6. The planar optical device of claim 5, wherein the planar optical device is a cross-connect optical switching device.

   7. The planar optical device of any one of claims 4 to 6, wherein the silica- germania-titania glass has a refractive index of from 1.48 to 1.52 at 1550 rim and a coefficient of thermal expansion at room temperature OI from 3 x 1 o-6 C to 4.4 x 1 o-6 C 8. The planar optical device of any one of claims 4 to 7 further comprising a liquid-crystal element coupled to the waveguide.

   9. A planar optical device in which at least one of the waveguide core and the wave('uide clad1ing is of a silica-germania-titania g!acs according to claim 1 substantially as hereinbefore described. s

   10. A method of forming a planar optical device on a silicon substrate, comprising: depositing on a silicon substrate by plasma enhanced chemical vapor deposition a silica-germania-titania cladding layer having a Ge/(Si + Ge + Ti) mole ratio of from 0.08 to 0.17 and a Ti/(Si + Ge + Ti) mole ratio of from greater than O to 0.8; and depositing on the cladding layer by plasma enhanced chemical vapor deposition a silica-germania-titania core layer having a Ge/(Si + Ge + Ti) mole ratio of from 0.08 to 0.17 and a Ti/(Si + Ge + Ti) mole ratio of from greater than O to 0.08, wherein the refractive index of the core layer is higher than the refractive index of the cladding layer.

   1 1. A method of making a silica-gerrnar,ia-titania planar optical device substantially as hereinbefore described with reference to one or more of the examples.

   Amendments to the claims have been filed as follows 1. A glass composition comprising a silica-germania-titania having a Ge/(Si + Ge + Ti) mole ratio of from 0.08 to 0.17 and a Ti/(Si + Ge + Ti) mole ratio of from greater than O to 0.08.

   2. The glass composition of claim 1 exhibiting a refractive index of from 1.48 to 1.52 at 1550 nm, and having a coefficient ofthermal expansion at room temperature of from 3 x 10-6 C-' to 4.4 x 10-6 C-I.

   3. A silica-germanian-titania glass composition according to claim 1 substantially as hereinbefore described. ( '

   4. A planar optical device comprising: a waveguide core and waveguide cladding, wherein at least one of the waveguide core and the waveguide cladding is a silica-germania-titania glass having a Ge/(Si + Ge + Ti) mole ratio of from 0.08 to 0.17 and a Ti/(Si + Ge + Ti) mole ratio of ' from greater than O to 0.08.

   it, ( . . 5. The planar optical device of claim 4, wherein the planar optical device is an optical switch having liquid crystal switches located at intersecting waveguides.
6. 6. The planar optical device of claim 5, wherein the planar optical device is a cross-connect optical switching device.
7. 7. The planar optical device of any one of claims 4 to 6, wherein the silica- germania-titania glass has a refractive index of from 1.48 to 1.52 at 1550 nm and a coefficient ofthermal expansion et room temperature offrom 3 x 10-6 C to 4.4 x 10-6 Ci
8. 8. The planar optical device of any one of claims 4 to 7 further comprising a liquid-crystal element coupled to the waveguide.
9. 9 A planar optical device in which at least one of the wave.ide core and the waveguide cladding is of a silica-germania-titania glass according to claim I substantially as hereinbefore described.
10. 10. A method of forming a planar optical device on a silicon substrate, comprising: depositing on a silicon substrate by plasma enhanced chemical vapor deposition a silica-germania-titania cladding layer having a Ge/(Si + Ge + Ti) mole ratio of from 0.08 to 0.17 and a Ti/(Si + Ge + Ti) mole ratio of from greater than O to 0.08; and l O depositing on the cladding layer by plasma enhanced chemical vapor deposition a silica-germania-titania core layer having a Ge/(Si + Ge + Ti) mole ratio of from 0.08 to 0.17 and a Ti/(Si + Ge + Ti) mole ratio of from greater than O to 0.08, wherein the refractive index of the core layer is higher than the refractive index of the cladding layer.
11. 11. A method of making a silica-germania-titania planar optical device substantially as hereinbefore described with reference to one or more of the examples.