GB2154573A - Lead-free and cadmium-free glass frit compositions for glazing, enameling and decorating - Google Patents

Abstract

A lead-free, cadmium-free and zinc-free glass frit composition having a fiber softening point of about 535 DEG C to about 609 DEG C consisting essentially of the following components present in the indicated approximate weight percent ranges based on the total composition: <IMAGE> and wherein SIGMA SnO2+CaO is 2-23 SIGMA ZrO+La2O3 is 2-33 SIGMA ZrO2+Al2O3 is 0-26.5 SIGMA CaO+SrO+Bao is 0-19.25

Description

SPECIFICATION Lead-free and cadmium-free glass frit compositions for glazing, enameling and decorating The present invention relates to lead-free and cadmium-free glass frit compositions which possess desirable properties and characteristics which enable them to be used for glazing, enameling and for decorating a variety of food service ware; glassware such as tumblers, chinaware and the like. The compositions of this invention may also find use in selected applications such as microelectronic encapsulation, and for the formation of a light diffusing layer on a glass surface. The decorating glazes and glass compositions of the present invention have the advantage of containing no lead or cadmium components.

Most of today's commercially available food service ware is marketed with varying degrees of external ornamentation and decoration. Manufacturers of such ware have long recognized that decorated glassware has improved customer appeal and will sell better than undercoated ware. As a result, much effort over the years has gone into research and development relating to decorating compositions for all types of dinnerware, tableware, and food service ware in general.

Decorating compositions generally fall into two categories; glazes and enamels. The glazes are usually thought of as clear glasses, while enamels are glazes which contain a coloring material such as a pigment. In actual usage, the glazes and enamels are used in a finely divided form called a "frit", which is selectively applied to the surfaces of the glassware, glass-ceramic ware, chinaware and ceramic ware in accordance with the intended decorative or ornamental pattern. Any of several decorating techniques known in the industry can be used to achieve this result. Typically, the frit is in the form of a paste which consists of the finely divided glaze or enamel composition plus a vehicle.After application to the ware by silk screen or other technique, the ware is heated orfired to fuse the frit, volatilize the vehicle or medium and firmly bond the decoration to the surface of the ware.

According to the present state of the art, there are a variety of decorating compositions available which are used in the decorating of glassware, chinaware and the like, to produce selected patterns and ornamentation. Often times, these available compositions contain lead and/or cadmium oxides. Lead oxide was previously used in these compositions to lower the melting point of the frit so that the frit could be fused onto the surface of the ware at as low a temperature as possible to avoid thermal deformation of the ware.

Cadmium oxide has been used in the past as a colorant in certain frits. Certain States of the Union have now enacted legislation prohibiting the use of cadmium and lead in glazes used for decorating of glassware and chinaware on the ground that these materials are allegedly toxic and that young children would be particularly susceptible to the allegedly toxic affects of these components. The present invention therefore eliminates risks associated with having allegedly toxic materials present in glazing and decorating compositions. Further, the present invention avoids the risk of possible recall of decorated ware in particular states which may in the future enact legislation prohibiting the use of cadmium and/or lead oxides in decorating compositions.

The present invention further eliminates the need for testing the content of decorative glazes and glass compositions to determine if the level of alleged toxic materials has been kept to the required minimum.

Thus, the cost of compliance testing is overcome.

The decorative glaze compositions of the present invention contain no lead and cadmium oxides, thereby enabling the glass manufacturer to recover sales in those states which require or mandate zero lead or cadmium content in glassware sold in those states intended for drinking purposes or in chinaware that comes into contact with food.

The glasses of the present invention can have substantially lower densities than lead containing glasses.

For example, (2.6842 vs. 4.5837). One pound of the new glasses has a higher volume than the previously commercially used decorating materials. The volume of glass available for printing controls the number of decorated glass pieces. For example, 1 pound of lead glass will print approximately 500 glass pieces of a specific design. In contrast, a typical lead-free glass of the invention in the amount of 1 pound will print approximately 850 pieces of the same design.This was arrived at through the following calculation: Volume per pound of material lead glass - Density 4.5837 g/cc lead-free glass - Density 2.6842 g/cc Lead: Volume1 = Wt. = 1 Ib. = 453.6gum~= 98.96 ml Density - 4.5837 - 4.5837 453.6 = No Lead Volume2 = 2.6842 = 168.99 = 170 ml Ratio 500 pieces x 1.7 = 850 pieces The present invention also provides a potential for lower raw material costs because of the avoidance of the need to use the relatively expensive lead and cadmium components. Forthesame reason, the present invention has a potential for lowering the cost of color pigments.

This is illustrated by the following: The glass decorating glazes have minimum of two components: A - Glass (= flux) and B - Color Pigment (= stain) The B part pigment are identical or similar in both lead and lead-free glasses to achieve the selected colors.

The lead-free glass A part raw materials without tin oxide are cheaper than lead glasses. For example, a typical glass of the present invention could be 20% to 30% less expensive, as compared to the cost of one pound of lead containing glass.

A number of advantages characterize the present invention including the fact that the decorating compositions described herein meet the requirements of good decorating glasses, protective glazes and enamels without using allegedly toxic materials. It is important, particularly for the decoration of glassware and chinaware which is used in a home or restaurant, that the decorating compositions have sufficient alkali resistance and hardness so that they will be able to be exposed for many years to dishwashing cycles without serious degradation which would cause an unattractive deterioration of the decorated ware.

The present invention provides many compositions which can be harder and thereafter more scratch resistant than compositions generally known in the art today. As a result, there are included among the compositions of the present invention those which are especially suited as top coats for chinaware. It has been determined by applicants that the pigmented glasses of the present invention are less sensitive to furnace atmosphere than are compositions known in the art especially those which contain certain cadmium pigments such as cadmium sulfide and cadmium selenide (CdS and CdSe, respectively) which are sensitive to oxidation.Depending on the particular formulations and components, the present invention provides compositions which, in general, have enhanced properties such as lower expansion, high hardness, high chemical resistance, particularly alkali resistance, and a sufficiently longer glassy range in relation to other lead-free glasses such as zinc oxide containing compositions.

In accordance with one feature of the present invention there are provided alumino-borosilicate compositions which may be used for glass and chinaware decorations and hybrid microelectronic applications. In general, the compositions in accordance with this feature of the present invention are based on the A1203 - B203 - SiO2 system, wherein there is also present lithia, Li2O, and at least one other component selected from the group consisting of ZrO2, SnO2, CeO2, La2O3, CaO, SrO, BaO, Na2O, ZrF4, NaF and 3NaF.AIF3.

In another aspect of the invention, there are provided compositions which are free of added aluminium values in the form of A1203 and which are defined as containing substantial amounts of lanthanum oxide expressed as La2O3. These compositions are based on the B203 - SiO2 - ZrO2 - La2O3 system and also contain lithia, Li2O.

Characterized by good chemical resistance, the glasses of the present invention also have good gloss and smoothness. In addition, they have generally hard surfaces without containing allegedly toxic materials.

Among the glasses of the present invention are those which may be fired in the temperature range 580"C to 630"C at the normal rate and holding time, using conventional glassware and chinaware decorating lehrs.

In the industry today, it is important that the compositions used for the decoration of glassware and chinaware have the characteristics described below.

The decorative compositions should be capable of being fired in the firing range of 580"C to 630"C. It is generally desired that the holding time at the peak temperature be in the range of 7 to 11 minutes, with the heating rate of 14"C to 1 50C per minute. The time to reach the peak temperature should range to about 40 minutes t 10 minutes.

The compositions used for decorating should be capable of being fired to a smooth, shiny layer without "running out" of the printed area and at the same time being capable of forming fine lines with no bleeding, that is, the patterns produced on the glassware should be clear and crisp and should not be fuzzy, blurred or indistinct.

It is desirable that the decorated glassware and china ware be capable of withstanding dishwater cycles, preferably in the presence of rather strong detergent, for a range of 5 to 20 years. In addition, the decorated material on the glassware should not be removed or susceptible to attack by the acids normally encountered in fruit juices.

For applications such as art glass, electronic purposes and light diffusing coating the glasses do not need to possess acid and/or alkali resistance.

Finally, the decorated material should not exhibit any cracks after firing or develop any cracks in actual usage.

These properties, features and characteristics can be determined by quantitative test data as well as by observation. Therefore, a specific decorating composition can be evaluated to determine whether it will be satisfactory for commercial purposes. For example, decorated glassware can be subjected to dishwater cycling tests. By subjecting the decorated ware to attack using 5% sodium pyrophosphate at 600C for 8 hours measured at 2-hour intervals, accelerated laboratory tests can be carried out to predict dishwasher resistance.

For the fruit juice test, generally two acids are used to determine the susceptibility of decorated glassware to attack. The first test is a 2% citric acid for 30 minutes at room temperature and the second test is a 4% acetic acid for 24 hours at room temperature.

Smoothness and the characteristics of the fired print definition can be predicted by a test which is called the "flow number" test. The flow number is calculated by the ratio of the measured width to the measured height of a fired sample pellet of the decorating composition. The pellet of the decorating composition is placed on a glass surface and the height of the pellet above the glass surface is measured. The measured width is the width of the pellet surface in contact with the glass surface. Good samples will have a flow number between 1 to 1.2. Numbers lower than 1 suggest lower glass adhesion. Numbers higher than 1.3 suggest a poor definition with run down from printed lines; that is, excessive bleeding of the paste.

Any fracturing or cracking tendencies in the decorated material are related to differences in the thermal contractions of the substrate glass or chinaware (tumbler or dinnerware) and the decorating glass from the peak temperature down to room temperature. These differences can be determined by the residual stress in the tumbler glass caused by the contracting decorating glass. For example, the test can be determined by using a sample cube with 2.5 mm edge which is fired in contact with the base glass with the desired heating rate, holding time and temperature and also cooling rate. The induced stress is measured by polarized light retardation in accordance with procedures known in the art.

The conversion is measured by using a test sample with a thickness of about 100 mils. The thickness of the fired decorating layer is about 1.2 to 2.3 mils. The measured stress values shown in the Table 1 which is set forth below are about 4 to 6 times greater than the expected stress values for fired screen printed decorating layers as determined experimentally. The test specimens were observed for cracking and the observations were recorded in Table 1. It is apparent that the pellet stresses up to approximately 1600 psi did not show cracks in the thin layers which range from 1.2 to 2.3 mils.

The above-mentioned test techniques and procedures are well known and documented in the field of glass technology.

It should be noted that the compositions of the present invention can be used in conventional screen printing techniques which are well known and understood in the art and do not form a part of this invention.

Any such conventional screen printing methods can be used for purposes of the invention.

In its broadest aspects, the present invention relates to compositions based on a borosilicate glass system represented by the following listed components in the indicated weight percent ranges expressed on an oxide basis.

Component Weight Percent A1203 0-30 B203 16-32 SlO2 11-40 LiO2 4-12 The balance consisting of other compatible glass making components to be described in further detail below.

In addition to these listed ingredients, which form the base glass, the system generally further contains one or more of ZrO2, SnO2, CeO2, La2O3, CaO, SrO, BaO, Na2O, ZrF4, NaF and 3NaF.AIF3.

It will be noted that these compositions are zinc free. Whereas zinc has been used in decorating compositions and has been found useful in achieving low viscosity in glass at specific temperatures, zinc is listed as not desirable in drinking water and should be, limited to no more than about 5 mg/l.

More particularly, the glass compositions of the present invention contain the following components expressed in oxides in weight percent, based on the total composition.

Component Weight Percent Al203 0-30 B203 16-32 SiO2 11-40 Li2O 4-12 ZrO2 0-18 SnO2 0-20 CeO2 0-2 La2O3 0-15 CaO 0-16 SrO 0-13 BaO 0-7 Na2O 0-3.5 F 0-2.6 and wherein 8, SnO2+CaO 2-23 5; zro2+La2o3 2 - 23 E ZrO2+Ai202 0 - 26.5 2 CaO+SrO+BaO 0 - 1925 Table 1 shows representative compositions of the present invention which have been found to materially improve the characteristics of decorated glassware and chinaware.

These compositions include those which have outstanding alkali resistance, and acceptable stress layers.

Some compositions which have relatively high stresses which may cause some cracks can be remedied by including as fillers an appropriate amount of a low expansion ceramic such as beta-eurcryptite. Some color pigments also function to lower the stress as is known in the art. Clays can be used; as well as mullite; quartz and the like.

In a further feature of the present invention, it has been found that the following compositions are especially well suited for the purposes described herein: Component Weight Percent A1203 19-20 B203 28-30 Si02 11-16 LiO2 4-8 ZrO2 4-7.5 SnO2 6-19 La2O3 0-0.5 CaO 0-4 SrO 0-13 BaO 0-7 Na2O 0-0.25 F 0-1.5 Compositions falling within the above stated parameters have good fiber softening point data and develop a compressive stress, or low tensile stress, when tested for stress characteristics.

With the above preferred compositions of the invention, it may be noted that when SnO2 is present in an amount of greater than 10% by weight, the amount of SrO should be less than 10%; conversely when SrO exceeds 10% then the amount of SnO2 should be less than 10%. Also within the parameters stated above, the sum of CaO + SRO should be in the range of 6-21 with a maximum of 7% BaO and 5% CaO, with the added provision that there must always be either BaO or CaO present. Preferred compositions coming within the above ranges are those shown in Table 1, examples 5, 13, 14, 22 and 23.

Some compositions of the invention are colorless and therefore may be used as a barrier or top coating onto conventional decorating compositions which may contain lead and cadmium in order to prevent or retard lead and cadmium release from the decorated surfaces.

The following examples, with the exception of example 15, illustrate the invention without being intended to limit it in any way. Example 15 is intended for purposes of comparison. The comparisons were recalculated to the standard normal oxide percentages. In compositions 1,5-9, 16, cryolite (3NaF.AIF3) was used, in examples 5,7,8, 12-14, and 18, ZrF4 was added; in compositions 3,4 and 15 zircon was added; in compositions 4, 11, 15 and 17 NaF was used. Therefore, in the respective examples, zircon was changed to ZrO2 and SiO2 percentages and cryolite into F, Na2O and Al2O3 percentages. In this table, the symbols "A" and "C" indicate acetic acid and citric acid respectively.

TABLE 1 Glass Compositions (1-12) G/ass No. 1 2 3 4 5 6 7 8 9 10 11 12 % Loss Alk. 0.62 0.49 1.44 1.08 1.28 1.77 1.99 1.94 1.77 1.61 1.77 2.3 % Loss Acids A 7.34 12.78 5.93 16.33 2.87 2.83 4.78 4.06 8.54 7.40 8.07 11.4 % Loss Acids C 4.72 9.18 8.36 11.42 1.74 1.53 1.94 3.82 4.25 5.20 6.60 4.8 Composition Al2O3 19.00 20.0 20.0 20.0 19.7 20.0 20.0 20.0 19.25 20.0 18.0 20.0 B2O3 29.0 28.0 29.0 29.0 28.25 28.2 28.0 28.0 29.0 28.0 28.0 28.0 Li2O 6.0 8.0 6.0 6.0 7.5 7.5 7.5 7.5 6.0 8.0 8.0 8.0 SiO2 18.0 16.0 16.0 16.0 12.75 12.75 12.55 12.75 18.0 16.0 18.0 16.0 ZeO2 5.0 5.0 5.0 5.0 6.10 5.0 6.0 6.11 5.0 5.0 5.0 6.5 SnO2 0 10.0 2.0 0 14.22 12.25 12.22 4.25 0 10.0 5.0 10.0 CeO2 0 0 2.0 2.0 0 0 0 0 2.0 0 0 0 La2O3 2.0 0 0 0 0.5 0.5 0.5 0.5 0 0 0 0 CaO 16.0 0 16.0 16.0 4.0 7.5 6.0 14.0 16.0 13.0 13.0 3.0 SrO 0 13.0 0 0 0 0 0 0 0 0 0 5.0 BaO 0 0 1.0 0 5.25 5.25 5.25 5.25 0 0 0 3.0 Na2O 3.0 0 3.0 3.0 0.8 0.8 0.8 0.5 3.0 0 3.0 0 F 2.0 0 0 3.0 0.93 0.25 1.18 1.14 1.75 0 2 0.5 F.S.P. C DTA 552 567 583 557 538 559 537 556 549 577 556 560 Flow 1.144 1.040 1.031 1.181 1.200 1.155 1.209 1.181 1.125 1.010 1.126 1.101 Stress pai 1700T 1425T 1050T 1700T 450C 1310T 1620T 1700T 1750T 1515T 2060T 1060T Cracks Yes No No Yes No No No Yes Yes No Yes No # SnO2+CaO 16 10 18 16 18.22 19.75 18.22 18.25 16 23 18 13 #ZrO2+La2O3 7 5 5 5 6.6 5.5 6.5 6.61 5 5 5 6.5 #ZrO2+Al2O3 24 25 25 25 25.8 25 26 26.11 24.25 25 23 26.5 #CaO+SrO+BaO 16 13 17 16 9.25 12.75 11.25 19.25 16 13 13 11 TABLE 1 Glass Compositions (13-24) Glass No. 13 14 15 16 17 18 19 20 21 22 23 24 % Loss Alk. 1.99 2.21 3.18 3.07 2.56 4.2 4.46 5.9 2.67 2.05 1.94 0.7 % Loss Acids A 6.80 6.40 15.87 12.3 13.80 13.6 14.97 16.6 16.48 7.54 6.33 8.43 % Loss Acids C 2.30 1.40 10.4 7.7 6.20 3.4 4.58 6.23 6.10 3.42 4.21 3.41 Composition Al2O3 20.0 20.0 20.0 18.70 18.0 20.0 20.0 20.0 20.0 20.0 20.0 0 B2O3 28.0 28.0 29.0 29.0 29.0 28.0 28.0 28.0 28.0 30.0 29.0 30.0 Li2O 8.0 8.0 6.0 6.0 6.0 8.0 8.0 8.0 8.0 4.0 6.0 7.0 SiO2 1.40 11.0 15.80 18.0 18.0 14.0 15.0 10.0 16.0 15.0 16.0 28.0 ZrO2 6.5 6.5 5.0 5.0 5.0 6.5 3.0 6.5 5.0 4.0 5.0 18.0 SnO2 15.0 19.0 0 0 0 15.0 10.0 20.0 7.0 6.0 7.0 0 CeO2 0 0 2.0 2.0 2.0 0 0 0 0 0 0 0 La2O3 0 0 0 0 0 0 0 0 0 0 0 15.0 CaO 3.0 0 14.0 16.0 16.0 0 0 0 2.0 4.0 3.0 2.0 SrO 4.0 0 0 0 0 8.0 16.0 0 11.0 13.0 11.0 0 BaO 0 7.0 0 0 0 0 0 7.0 3.0 4.0 3.0 0 Na2O 0 0 5.60 3.3 3.5 0 0 0 0 0 0 0 F 1.5 0.5 2.60 2.0 2.5 0.5 0 0.5 0 0 0 0 F.S.P. C DTA 567 535 549 558 565 565 557 537 573 565 576 606 Flow 1.081 1.272 1.200 1.082 1.082 1.141 1.103 1.381 1.095 1.0210 0.905 1.020 Stress psi 1080C 805T 1945T 2365T 1800T 1200T 1765T 1265T 1615T 1245T 1435C 630C Cracks No No Yes Yes Yes No Yes No Yes No No No # SnO2+CaO 18 19 14 16 16 15 10 20 9 10 10 2 # ZrO2+La2O3 6.5 6.5 5 5 5 6.5 3 6.5 5 4 5 33 # ZrO2+Al2O3 26.5 26.5 25 23.7 23 26.5 23 26.5 25 24 25 18 # CaO+SrO+BaO 7 7 14 16 16 8 16 7 16 21 17 2.0 TABLE 1 Glass Compositions (25-37) Glass No. 25 26 27 28 29 30 31 32 33 34 35 36 37 % Loss Alk. 0.64 0.85 0.79 0.88 0.42 0.86 1.04 1.45 2.43 3.79 2.77 3.21 2.21 % Loss Acids A 7.72 12.22 8.14 8.55 3.33 6.22 5.42 4.20 6.89 4.80 6.41 6.61 2.58 % Loss Acids C 2.83 4.81 6.20 3.80 3.66 5.74 6.73 3.47 9.09 5.87 5.79 6.12 2.50 Composition Al2O3 0 0 0 0 0 0 0 0 2.0 0 30.0 17.0 15.0 B2O3 30.0 30.0 30.0 32.0 30.0 24.0 24.0 24.0 24.0 24.0 16.0 25.0 32.0 Li2O 7.0 7.0 7.0 7.0 8.0 9.0 9.0 8.0 5.0 8.0 12.0 8.0 8.0 SiO2 30.0 30.0 30.0 30.0 35.0 40.0 40.0 40.0 40.0 40.0 40.0 28.0 29.0 ZRO2 16.0 14.0 12.0 12.0 10.0 5.0 5.0 3.0 4.0 0 0 4.0 4.0 SnO2 0 0 0 0 2.0 1.0 1.0 1.0 0 0 0 0 0 CeO2 0 0 0 0 0 0 0 0 0 0 0 0 0 La2O3 15.0 15.0 15.0 13.0 15.0 15.0 13.0 13.0 13.0 15.0 2.0 6.0 0 CaO 2.0 4.0 6.0 6.0 0 3.0 5.0 8.0 9.0 10.0 0 9.0 9.0 SrO 0 0 0 0 0 0 0 0 0 0 0 9.0 0 BaO 0 0 0 0 0 0 0 0 0 0 0 0 0 Na2O 0 0 0 0 0 3.0 3.0 3.0 3.0 3.0 0 3.0 3.0 F 0 0 0 0 0 0 0 0 0 0 0 0 0 F.S.P. C DTA 595 609 597 596 590 573 574 578 606 574 581 567 573 Flow 1.063 1.010 1.030 1.052 1.030 1.074 1.099 1.021 1.010 1.147 1.117 1.042 1.074 Stress psi 415C 1180T 1390T 1350T 1040T 600T 1200T 850T 1060T 1795T 1180T 380T 310C Cracks No No No No No No No No No Yes No No No # SnO2+CaO 2 4 6 6 2 4 6 7 9 10 0 9 9 # ZrO2+La2O3 31 29 27 25 25 20 18 16 17 15 2 4 4 # ZRO2+Al2O3 16 14 12 12 10 5 5 3 6 0 30 21 19 # Cao+SrO+BaO 2 4 6 6 0 3 5 8 9 10 0 18 9 From the foregoing tables, it will be seen that for those compositions containing aluminium oxide the components included the following in the indicated weight percent ranges based on oxides: Component Weight Percent A1203 15-30 B203 16-32 Li2 4-12 SiO2 8-40 ZrO2 3-6.5 SnO2 0-20 CeO2 0-2 La2O3 0-6 CaO 0-16 SrO 0-13 BaO 0-7 Na2O 0-3.5 F 0-3 wherein from example 1 to 23:: # SnO2+CaO is 9 to 23% # ZrO2+ La2O2 is 3 to 7% # ZrO2+A12O3 is 23 to 26.5% # CaO+SrO+BaO is 7 to 21% Within the above ranges were those compositions which exhibit no cracks in the test. These compositions contain the following ingredients: Component Weight Percent Al2O3 15-30 B203 16-32 Li2O 4-12 SiO2 10-40 ZnO2 4-6.5 SnO2 0-20 CeO2 0-2 La2O3 0-6 CaO 0-16 SrO 0-13 BaO 0-7 Na2O 0-3 F 0-1.5 wherein generally: # SnO2+CaO is 10 to 23% # ZrO2+La2O3 is 4 to 6.5% s, ZrO2+A12O3 is 24 to 26.5% # CaO+SrO+BaO is 7 to 21% Within the broad group alumino-borosilicate compositions are those exemplified by glass numbers 35,36 and 37 in the above table. In this group of glasses ESnO2+CaO is 0-9, #ZrO2+La2O3 is 2-4%, #ZrO2+Al2O3 is 19-30 and #CaO+SrO+BaO is 0-18%.

The foregoing tables also show compositions that are free of added aluminium oxide, or very low amounts; i.e. on the order of 2% or less. These compositions can be expressed by the following listed ingredients in the indicated weight percent based on oxides.

Components Weight Percent Al203 0-2 B203 24-32 Li2O 5-9 SiO2 16-40 ZrO2 0-18 CaO 0-10 SrO 0-3 Na2O 0-3 wherein; X SnO2+CaO is 2-10% s, ZrO2+La2O2 is 15-33% ="ZrO2+Al2O2 is 0-18% CaO+SrO+BaO is 0-10% Of these compositions some compositions exhibited no cracks and may be expressed by the following listed components in the indicated amounts in weight percent based on oxides.

Component Weight Percent B203 24-30 Li2O 5-9 SiO2 28-40 ZrO2 3-18 SnO2 0-2 La2O3 13-15 CaO 0-9 Na2O 0-3 and wherein: # SnO2+CaO is 2-9% # ZrO2+La2O2 is 17-33% # CaO+SrO+BaO is 0-9% To determine hardness of the glasses of the invention, the Knoop Hardness Numbers (KHN) were measured for the glasses set forth in Table 1 (above). They ranged from 520-594. Commercially used lead glasses ranged from 250-300, in the same Knoop Hardness Numbers. KHN's are values of hardness expressed as the load in kilograms divided by the projected area of a diamond penetration in millimeters corrected for the resolution of the used microscope. E. G.Shand shows KHN's for soda-lime glasses from 445-490, for alumino-silicate glasses 550. (E. B. Shand, "Glass Engineering Handbood", pg. 42, McGraw Hill, 1958).

It therefore appears that the glasses of this invention are exceptionally harder than lead containing decorating glasses (520 vs. 250), they are somewhat harder than soda-lime glasses (520 vs. 490) and similar to alumin-silicate glasses.

As previously mentioned, clear coatings may be prepared from compositions of the present invention and then employed as glazes or overcoats for other ware. To illustrate this embodiment of the invention, lead and cadmium containing glasses were overprinted with glass No. 1 of Table 1 and cofired. When tested for alkali resistance, the coated samples were superior. They also showed high gloss and more intense color.

The following Table A lists the results obtained with the three most critical colors: red, orange and yellow comparing coated and uncoated samples. The samples did not have any cracks eventhough glass No. 1 has a relatively high stress.

TABLE A Coated and uncoated lead and cadmium containing glass samples Red ~ . Orange Yellow Uncoated Coated Uncoated Coated Uncoated Coated %Alkali Loss 2.19 1.03 1.14 0.70 1.58 1.15 Gloss Lost Retained Low High Low Medium Color Dull Intense Good Slightly Good Good Better Cracks No No No No No No The compositions of the present invention can be used to produce a wide range of pigment colors. The desirable colors are obtained by adding color pigments to a base glass (in single component) such as shown in Table 1 orto a mixture of two or more glasses orto a mixture of glass plus filler. The range of color pigments addition is from 0.5% to 15% by weight.The low limit 0.5% of white titania oxide is used to achieve white translucent color effects commonly used in so-called "etched glassware". The upper limit of 15% is used in complex color requiring several pigments including opacifier agents. The most useful range is from 4% to 12% of pigments used for all basic and relatively simple color tones like black, white, yellow, orange, browns and tans.

Table 2 lists several important colors: yellow, orange, brown and maroon with their characteristics. These results illustrated the stress reductions achieved by additions of the low expansion filler ss-eucryptite from 1700T to 320C. The pigment chemistry is shown on line 2 of Table 2. From 1 to 15% pigment is generally used. Line 3 lists the percentage of the color pigment used. ss-eucryptite percentage is shown on line 4. The loss in weight is accelerated alkali test is listed on line 6. Line 7 shows the induced stress as explained above.

Sample No. 6 had stress of 945 psi tension and it did not show any cracks. The thin printed and fired layer had a stress of 160 psi tension. This approach to decreasing the induced stresses has a disadvantage of less smoothness and gloss due to relatively coarse (20-44 microns) ss-eucryptite particles used for better results.

Low expansion ss-eucryptite is described in pending U.S. patent application Serial No. 286,105 filed July 22, 1981 of Perry Pirooz, the entire disclosure of which is relied on and incorporated herein by reference. From about 5 to 15% of low expansion fillers may be used to prepare colored enamel in accordance with this aspect of the invention.

TABLE 2. Colors 7 2 3 4 5 6 7 Color Maroon Yellow Brown Buff Deep Orange Tan Pigment Fe2O3 CrNbTi FeZr FeZnTi FeZn CrWti % Pigment 2 5 5 5 5 10 9/0 Filler 13 13 13 13 13 13 Beta Eucryptite % Loss Alk. 1.85 1.69 1.76 1.11 1.62 0.89 Flow 1.071 1.020 1.060 1.050 1.062 1.031 Stress 200C 315C 320C 800T 610T 945T Pellet about 100 mils Cracks No No No No No No BaseGlass 1 1 1 1 1 1 It was found that the present compositions such as illustrated in Table 1 having high tension stresses and cracks can be enhanced by incorporating low thermal expansion fillers which effectively reduce the apparent stress of this composite mixture. Additions from 1% to 15% of e.g., (3-eucryptite were effective reducers of high tensions. The amount of these fillers depends on the original stress of the base glass used. For example, glass No. 21 requires only 1% of ss-eucryptite to eliminate visible cracks. Composition No. 16 needs maximum of 15% of ss-eucryptite to pass the no crack criteria.

Although many glasses of Table 1 can be used as single base glass components, they are some with high tension stresses. This stress can be decreased to the good level by addition of another glass from in Table 1 with compression stress or very low tension stress. This second component glass is selected from listed glasses like No. 5, 13, 22 and 23. It was found experimentaly that small amounts of 2% additions of the above glasses will decrease the tension stress below the cracking limit. These glasses can be added up to 95% to form useful combinations. Consequently, range of selected glasses is from 1% to 99%. The proper selection is made the specific requirements of the flow numbers for the specific color pigments.Some pigments decrease the flow substantially and others have very little or no effect on flow number.

For example, the glasses No. 4 and No. 13 have good flows as single components (1.200,1.081,1.020) On the other hand, glass No. 23 is less flowing and requires addition of No. 1 glass.

To illustrate this aspect of the invention, curved 6 ounce orange juice tumblers (Bolero) were printed by Hot Melt (hot wax) inks with "wheat" design, with several colors ranging from yellow to orange, by a technique known as "blend". Two basic colors are blended together at the middle of the screen to achieve a variety of color shades. In Table 3, the six samples used glass No. 13 and glass No. 1 with the ratio No. 13 to No,. 1 from 1 to 3. Tumbler No. 6 had ratio 1 and tumbler No. 5 had ratio 3 as seen below. Small amounts of low expansion fillers were added to this mixture (e.g. 2% ss-eucryptite + 1% Cer-VitQ C-1 01). Table No. 3 lists the obtained results.The best results are listed under tumblers No. 1 to 3. The glass in these color mixtures was finely ground to less than 12 microns. Tumblers No. 4 and 6 were printed by exactly the same mixture as tumblers No. 1-3, but with particles sizes less than 44 microns (-325 mesh). The alkali losses in percentages were calculated from total loss in weight by substracting the weight losses due to the unprinted tumbler.

TABLE 3. Tumblers - Wheat design Tumbler 1 2 3 3 5 6 % Loss Alk. 0.5 1.0 0.8 1.32 1.38 3.11 % Loss Acids 2.93 2.57 1.64 5.74 7.45 4.38 Flow 1.060 1.020 1.043 1.040 1.020 1.051 Stress 250C 315C 260C 715C 825C 815T Glass 13 Ratio 2 2.2 2 2.6 3 1 Glass 1 The stress numbers in Table 1 can be converted to the standard coefficients of thermal expansion a x 10-7 per degree Centigrade (0-300") by a experimentally determined conversion factor 154 - per unit of expansion.

The listed stress numbers divided by the factor of 154 yields units of thermal expansion differences between the base glass (the tumbler glass) with a coefficient (a) of 83 x 10-7 per C and the glasses of this invention.

The compression stresses indicate thermal expansions lower than the tumbler glass and the tensions indicate thermal expansions higher than the base glass. Consequently, when tension is observed, the calculated units are added to the 83 x 109 per "C. On the other hand, when compression stresses are observed, the calculated units are subtracted from the 83 x 10-7 per"C.

For example, in sample No. 1, the observed stress is 1700. The calculation is then carried out as follows: 1700 tension divided by 154 = 11.04 units 83 + 11.04 = 94.04 x 107per'C This compares favorably to a measured value of 94.1 x 10-7 per "C.

In an@@@ @llustration, for sample No. 13, a compression stress of 1080 was measured.

1080C divided by 154 = 7.01 83 - 7.01 = 75.99 compared to the measured value of 76.1 For sample No. 5, the compression stress was measured as 460.

460C divided 154 = 2.99 83 - 2.99 = 80.01 compared to measured value of 80.00 In making the glasses as shown in Table 1, various ingredients were melted; generally, in quantities ranging from 10 to 50 pounds. Glass No. 1 was made in a quantity of 3,000 pounds using the following batch compositions which are typical raw materials which can be used for forming the glasses of the invention.

The following composition is based on a 100 pounds of batch material or approximately 85 pounds of the resulting glass: Batch ingredients Amounts Glass Sand 7.7 Alumina (A-10) 12.7 Anhydrous Boric Acid 23.6 Lithium Carbonate 12.0 Lathanum Carbonate 2.5 Nepheline-Syenite 7.8 Cryolite 4.0 Milled Zircon 6.1 High Calcite Limestone 23.6 100 pounds The above-identified batch materials were melted at a temperature of 2200"F for 2 hours. The melt was stirred eight times and thereafter cooled. The glass was then formed into chips by using a water-cooled rolling mill in accordance with conventional procedures. Because of the high volatilization rate, it is desirable to minimize the loss of boric oxide. The chips formed should be clear and transparent without any opaque inclusions which may evidence the presence of undissolved alumina.Stirring is necessary in order to minimize separation of the top layer which contains boric acid and silica and a bottom layer which contains alumina and zircon.

Two additional batch compositions are shown below to illustrate the type of materials used for purposes of the invention.

Batch Raw Materials Grams Ottawa 290 (sand) 27.8566 Anhydrous boric acid 36.8717 Calcined Kyanite 59.6637 Milled Zircon 11.9792 Anhydrous borax 19.9661 Lithium carbonate 39.3631 Stontium carbonate 25.4686 Lanthanum oxide 11.9393 Total Batch 233.1082 gas. Total glass weight 200.000 grams. Fusion loss 33.1082 grams.

Batch Raw Materials Grams Ottawa 290 (sand) 32.4947 Anhydrous boric acid 51.0280 Calcined Kyanite 52.5354 Milled Zircon 11.9665 Anhydrous Borax 19.9441 Lithium carbonate 39.3203 High Calcite Limestone 32.6886 Total batch 239.9777 grams. Total glass weight 200.000 grams. Fusion loss 39.777 grams.

The fiber softening point range for these compositions is 535"C to 609C.

Further variations and modifications will become apparent to those skilled in the art from the foregoing and are intended to be encompassed by the claims which follow.

Claims (15)

1. A lead-free, cadmium-free and zinc-free glass frit composition having a fiber softening point of about 535 C to about 609 C consisting essentially of the following components present in the indicated approximate weight percent ranges based on the total composition: Component Weight Percent A1203 0-30 B203 16-32 SiO2 11-40 Li2O 4-12 ZrO2 0-18 SnO2 0-20 CeO2 0-

2 La203 0-15 CaO 0-16 SrO 0-13 BaO 0-7 Na2O 0-

3.5 F 0-2.6 and wherein # SnO2+CaO is 2-23 # ZrO2+La2O3 is 2-33 # ZrO2+Al2O3 is 0-26.5 # CaO+SrO+BaO is 0-19.25 2.The glass frit composition according to claim 1 and consisting essentially of the following components present in the indicated weight percent ranges based on the total composition: Component Weight Percent Al203 19-20 B203 28-30 SiO2 11-16 LiO2 4-8 ZrO2 4-7.5 SnO2 6-19 La2O3 0-0.5 CaO 0-

4 SrO 0-13 BaO 0-7 Na2O 0-0.25 F 0-1.

5 3.The glass frit composition according to claim 1 and consisting essentially of the following components present in the indicated weight percent ranges based on the total composition: Component Weight Percent Al2O3 15-30 B203 16-32 Li2O 4-12 SiO2 11-40 ZrO2 3-

6.5 SnO2 0-20 CeO2 0-2 La2O3 0-6 CaO 0-16 SrO 0-13 BaO 0-7 Na2O 0-3.5 F 0-3 wherein X SnO2+CaO is 9 to 23% # ZrO2+La2O3 is 3 to 7% # ZrO2+Al2O3 is 23 to 26.5% # CaO+SrO+BaO is 7 to 19.25% 4.The glass frit composition according to claim 1 and consisting essentially of the following components present in the indicated weight percent ranges based on the total composition: Composition Weight Percent Al2O3 15-30 B203 16-32 Li2O 4-12 SiO2 11-40 ZrO2 4-6.5 SnO2 0-20 CeO2 0-2 La2O3 0-6 CaO 0-16 SrO 0-13 BaO 0-7 Na2O 0-3 F 0-1.5 wherein generally: # SnO2+CaO is 10 to 23% # ZrO2+La2O3 is 4to 6.5% # zrO2+AI203 is 24 to 26.5% # CaO+SrO+BaO is 7 to 19.25% 5.The glass frit composition according to claim 1 and consisting essentially of the following components present in the indicated weight percent ranges based on the total composition: Component Weight Percent A1203 0-2 B203 24-32 Li2O 5-9 SiO2 16-40 ZrO2 0-18 SnO2 0-10 La2O3 13-15 CaO 0-10 SrO 0-3 Na2O 0-3 wherein # SnO2+CaO is 2-10% # ZrO2+La2O3 is 15-33% # ZrO2+Al2O3 is 0-18% # CaO+SrO+BaO is 0-10% 6.The glass frit composition according to claim 1 and consisting essentially of the following components present in the indicated weight ranges based on the total composition: Component Weight Percent 8203 24-30 Li2O 5-9 SiO2 28-40 ZrO2 3-18 SnO2 0-2 La2O3 13-15 CaO 0-9 Na2O 0-3 and wherein: ~ SnO2+CaO is 2-9% 8 Zro2+La2o3 is 17-33% # CaO+SrO+BaO is 0-9%

7. The glass frit composition according to claim 1 consisting essentially of the following components present in the indicated weight percent ranges based on the total composition: Component Weight Percent A1203 19.7 B203 28.25 Li2O 7.50 SiO2 12.75 ZrO2 6.10 SnO2 14.22 La2O3 0.5 CaO 4 BaO 5.25 Na2O 0.

8 F 0.93 8.The glass frit composition according to claim 1 consisting essentially of the following components present in the indicated weight percent ranges based on the total composition: Component Weight Percent A1203 20 B203 28 Li2O 8 SiO2 14 ZrO2 6.5 SnO2 15 CaO 3 SrO 4 F 1.5

9. The glass frit composition according to claim 1 consisting essentially of the following components present in the indicated weight percent ranges based on the total composition: Composition Weight Percent Al203 20 8203 28 Li2O 8 SiO2 11 ZrO2 6.5 SnO2 19 BaO 7 F 0.5

10.The glass frit composition according to claim 1 consisting essentially of the following components present in the indicated weight percent ranges based on the total composition: Component Weight Percent A1203 20 B203 30 Li2O 4 SiO2 15 ZrO2 4 SnO2 6 CaO 4 SrO 13 BaO 4

11. The glass frit composition according to claim 1 consisting essentially of the following components present in the indicated weight percent ranges based on the total composition: Component Weight Percent A1203 20 B203 29 Li2O 6 SiO2 16 ZrO2 5 SnO2 7 CaO 3 SrO 11 BaO 3

12. A colored enamel for decorating glass, glass-ceramic and ceramic ware comprising frit as defined in claim 1 and from 4% to 15% of a low expansion filler or pigment, based on the weight of the glass frit.

13. The colored enamel of claim 12 wherein the filler is low expansion -eurcryptite.

14. A method of reducing stress in decorating compositions for application to glass, glass-ceramic and ceramic ware comprising incorporating from 5 to 15% of a low expansion filler into a glass frit as defined in claim 1.

15. A lead-free, cadmium-free and zinc-free glass frit composition, substantially as hereinbefore described.