Description

(54) ABSORBENT CROSS-LINKED STARCH MATERIALS (72) We, UNILEVER LIMITED, a company organised under the laws of Great Britain, of Unilever House, Blackfriars, London E.C.4, England, do hereby declare the invention for which we pray that a patent may be granted to us and the method by which it is to be performed, to be particularly described in and by the following statement: This invention relates to absorbent materials, more especially absorbent materials suitable for use in absorbent- disposable products such as, for example, sanitary towels or napkins, tampons and diapers. The invention also relates to processes for producing such materials and to absorbent articles containing such materials.

A number of absorbent materials have been suggested for use in absorbent disposable products, among the first being cellulose in fibre form. Cellulose fibre absorbs by a capillary action and as a result suffers from the serious disadvantage that the absorption is reversible, that is when subjected to pressure the cellulose fibres expel the absorbed liquid.

There has more recently been suggested in US Patent No. 3,070,095 the use of certain gums in articles to improve their absorbency characteristics. These materials are, however, prone to dissolve in an excess of fluid to give a gummy solution. As a result of this tendency to dissolve, gums have not found extensive use as a primary absorbent in disposable absorbent articles.

To overcome the disadvantage of the absorbent materials described in US Patent No.

3,070,095, there have been suggested the use of certain absorbent polymers such as the synthetic polymers of US Patent Specifications Nos. 3,669,103 and 3,670,731 and the modified cellulosic fibre described in US Patent No.3,589,364. These polymers also have the desirable property of irreversible absorption so that absorbed fluid cannot be squeezed out under the pressures normally associated with the use of absorbent disposables.

The present invention concerns a highly absorbent starch derivative, particularly suitable for use in absorbent disposable products such as sanitary towels, tampons and diapers, which is substantially water-insoluble, which is capable of absorbing irreversibly and which is substantially dry and non-sticky to the touch in the swollen state.

According to the invention there is provided a highly absorbent material which is substantially dry and non-sticky to the touch in the swollen state being a substantially water-insoluble cross-lined gelatinised starch, in which the degree of substitution of the cross-linking groups is 0.001 to 0.02, which is substituted by ionic groups which are attached to the starch by ether linkages and which groups are associated with mono- or di-valent counterions, and which has a urine retention value of at least 6 g/g.

Gelatinised starch is starch the granules of which have been disrupted. Gelatinised starch which has not been cross-linked is soluble in cold water.

The urine retention value for an absorbent material is determined in the way already well known for water retention values but using a synthetic urine instead of water. Thus in determining the urine retention value the sample to be tested (0.20 g) is weighed out into a pre-weighed sintered glass Gooch crucible. Synthetic urine (5 ml) is added to the sample ensuring that the sample is completely wetted and it is left to soak for 10 minutes before being placed in a centrifuge tube and spun for 10 minutes at 850 rpm in a centrifuge having a head radius of 9 cm. The crucible with contents is then reweighed. The urine retention value is expressed as the weight of urine retained per gram of dry absorbent. The formula of synthetic urine, derived from the information given in the Handbook of Clinical Laboratory Data, 2nd Edition, 1968, pages 17-20, is a solution in 5 litres of water of the following: grams CaCl2.2H20 3.680 K2SO4 0.175 KC1 44.740 KOH 2.190 NH4Cl 6.020 Citric acid 2.630 Water retention values referred to herein were obtained by the same procedure except that distilled water (10 ml) was used instead of the synthetic urine. Experiments have shown that the same urine retention values are obtained using natural urine in place of the synthetic urine. The absorbent materials of this invention have urine retention values of at least 6 g/g and are desirably in the range 8-20 g/g.

The absorbent starch derivatives of this invention are substantially water-insoluble containing at least 90%, preferably at least 95%, of insoluble carbohydrate. The most preferred materials of the invention are those having a water insolubility of 99% or higher.

A feature of the absorbent materials of the present invention is that although the degree of substitution of the cross-linking groups is relatively low (being smaller, for example, than that of the cross-linked starch products described in Examples 1 to 6 of Canadian patent No.

960,652 or the starch product of Example 2 of British Patent No. 936,039 or the starch product of Example X of United States Patent No. 2,588,463) they are substantially insoluble in water. United States Patent No. 3,622,562 refers to certain cross-linked starch products having a degree of substitution of cross-linking groups of 0.01 but such products are not substantially insoluble in water.

The cross-linking of the starch molecules may be effected by ether bridges of the formula -O-R-O- where R is an aliphatic group, which may be substituted by one or more hydroxy groups, containing 1 to 10 carbon atoms. Preferably R is -CH2CH(OH)CH2-, which is the case when the starch is cross-linked using epichlorhydrin as cross-linking agent.

The ionic groups preferably have the formula Z-R1-where R' is an alkylene group having 1 to 5 carbon atoms and Z is an anionic group selected from carboxyl, sulphonic or phosphonic groups or a cationic group of the formula

where R2 is hydrogen or C1-4 alkyl, and R3 and R4 are C14 alkyl or are alkylene groups linked together to form a five or six-membered heterocyclic ring. Particularly suitable materials are those wherein Rl is an alkylene group containing 1 or 2 carbon atoms and Z is -COO and preferred details are carboxymethylated cross-linked gelatinised starches. The degree of substitution of the ionic groups will generally be at least 0.1 and is desirably at least 0.2 to obtain the preferred higher urine retention values.

When Z is an anionic group the counterion preferably is an alkali metal, alkaline earth metal ammonium or substituted ammonium ion. The substituted ammonium derivatives may be those in which one or more hydrogen atoms are replaced by C14 alkyl or C2-4 hydroxyalkyl groups or in which the nitrogen atom forms part of a heterocyclic ring. An example of such a substituted ammonium ion is tetramethylammonium. Preferred counterions when Z is an anionic group are the sodium, potassium and ammonium ions. When Z is a cationic group, the counterion may be, for example, chloride, bromide or sulphate.

Particularly preferred absorbent materials of this invention are the sodium and ammonium salts of carboxymethylated epichlorhydrin cross-linked gelatinised starch having a urine retention value of at least 10 g/g and being insoluble in water to the extent of at least 99%by weight.

The invention is also concerned with a process for making the above-described absorbent materials, which process comprises: 1. gelatinising starch; 2. during the gelatinisation or thereafter treating the starch with a cross-linking bifunctional compound to produce a cross-linked gelatinised starch which is substantially insoluble in water and in which the degree of substitution of the cross-linking groups is from 0.001 to 0.02; and 3. during the gelatinisation or thereafter reacting the starch with a monofunctional etherify ing agent to substitute the starch by ionic groups which are attached to the starch by ether linkages and which groups are associated with mono- or di-valent counterions, the degree of substitution of the ionic groups being such that the urine retention value of the substituted cross-linked gelatinised starch is at least 6 g/g.

In a preferred way of conducting this process, steps (1) and (2) are carried out by: (a) forming an aqueous alkaline slurry of starch granules containing the cross-linking bifunctional compound; and (b) rapidly heating the slurry by applying the slurry to a surface heated to 100-1800C to cause gelatinisation of the starch, reaction therewith of the cross-linking bifunctional compound and simultaneous drying, to produce cross-linked gelatinised starch in dry form.

In an alternative process steps (1) and (2) are carried out by: (c) forming an aqueous slurry of starch granules; (d) applying the slurry to a surface heated to 100 - 1800C to cause gelatinisation of the' starch and simultaneous drying; and (e) subsequently reacting the gelatinised starch with the cross-linking bifunctional compound in the presence of water and alkali to produce cross-linked gelatinised starch.

In this procedure, the alkali may be included in the slurry. The gelatinisation is very conveniently effected by feeding the aqueous starch slurry onto the surface of a heated drum upon which it can be pressed out into a thin film. The gelatinisation of starch by applying an aqueous slurry thereof to the surface of a heated drum is in itself a very well known process which has been called the cold-swelling starch process (see for example British Patent No.

787,153).

The reaction of the starch with the monofunctional etherifying agent may be carried out before, during, or after treatment of the starch with the bifunctional cross-linking compound.

To effect the cross-linking of the starch a bifunctional cross-linking agent is used and this may be a compound of the formula Q-R5-Y where R5 is an alkylene group containing 1 to 10, and especially 3 to 10, carbon atoms, which may be substituted by one or more hydroxy groups, and/or which may be interrupted by oxygen atoms, and Q and Y each represent a halogen atom or an epoxy oxygen atom, the latter being linked to carbon atoms of the group R5 with the formation of an oxirane ring. Suitable cross-linking agents are epiclorhydrin, dichlorohydrin, dibromohydrin, 1,2-3 ,4-diepoxybutane, 1,2-7,8-diepoxyoctane, bisepoxypropylether, 1 ,4-butane-diol-bis-epoxypropylether. The amount of cross-linking agent employed is that required to give a degree of substitution of the cross-linking groups within the range 0.001 to 0.02, corresponding to one cross-linking group for each 1,000 anhydroglucose units to one cross-linking group for each 50 anhydroglucose units. Preferably an amount of cross-linking agent is employed to give a degree of substitution of the cross-linking groups of from 0.003 to 0.02. The function of the cross-linking agent is to insolubilise the gelatinised starch. Cross-linking significantly beyond that required to insolubilise the gelatinised starch is not employed since increasing amounts of the cross-linking agent give products having, for a given degree of ionic substitution, lower water and urine retention values.

A preferred method of effecting the cross-linking employs epichlorhydrin and is effected with the gelatinisation of the starch on the surface of a heated drum. In this process the amount of epichlorhydrin (or other volatile cross-linking agent) employed should take account of the loss by vapourisation from the heated surface of part of the cross-linking agent.

For effecting the cross-linking some alkaline substance is required to be present in the reaction mixture, save that when formaldehyde is employed acid conditions are required, as is well known. Sodium hydroxide is quite suitable but other alkalis may of course be used. Since the degree of cross-linking effected is small the amount of alkali required to promote the cross-linking reaction is also small. This has the advantage that in forming the aqueous slurry of starch granules to be applied to the heated surface the concentration of the alkali in the slurry can be insufficient to effect any substantial gelatinisation of the starch before the slurry is heated enabling the slurry to be pumped easily through pipes from a holding vessel to the heated surface where gelatinisation, and, if desired, cross-linking and/or substitution by ionic groups, is effected.

This aqueous slurry desirably contains about 1 to 2 parts by weight of water per part of starch although higher amounts of water could be used.

Where cross-linking is effected after gelatinisation and in the presence of aqueous alkali, the amount of water required to be present can be as low as 0.1 to 0.5 parts per part of starch.

A surprising feature of the invention is that although cross-linking of the starch (during or after gelatinisation) can be effected in the presence of the above minor amounts of water, the final cross-linked substantially water-insoluble ionically substituted product nevertheless has high water and urine retention values.

By means of the monofunctional etherifying agent ionic substituent groups are introduced linked to the starch by an ether group. These ionic groups may have the formula Z-R1- where Z and Rl have the above meanings. The monofunctional etherifying agent may have the formula Zl-Rl-X where Rl is an alkylene group of from 1 to 5 carbon atoms, Zl is an anionic or cationic group Z as defined above, or a group capable of being converted into such an ionic group, and X is halogen or an epoxy group. However, activated olefinic compounds carrying an ionic group or a group capable of being converted into an ionic group could be used. The group R is preferably an alkylene group containing 1 or 2 carbon atoms and Z1 is a carboxylic acid group or a salt thereof. Examples of suitable monofunctional etherifying agents are monochloracetic acid, bromopropionic acid, chloroethylene sulphonic acid, chlorohydroxypropane sulphonic acid, epoxypropane sulphonic acid or 2-chlor-N, N-diethyl-ethylamine hydrochloride. Preferred etherifying agents are monochloracetic acid and the sodium salt thereof. When Z is a basic group, this may be quaternised, if desired, prior to etherification of the starch, for example etherification may be conducted with the quaternary ammonium salt formed between epichlorhydrin and triethylamine. Examples of etherifying agents containing an activated olefinic group and a group capable of being converted into an ionic group, eg with alkali, are acrylamide, acrylonitrile and ethyl acrylate. The etherification is carried out in the presence of alkali. Sodium hydroxide is the preferred alkali. The introduction of the ionic groups increases the urine retention value of the starch derivative. The substitution by ionic groups is effected to such degree as to give a salt having a urine retention value of at least 6 g/g.

It will be appreciated from the above that the actual urine retention value of the product obtained after step (3) is dependent both on the cross-linking and on the ionic-substitution stages. These steps are preferably effected in such a manner as to produce an ionically substituted cross-linked gelatinised starch having a urine retention value of at least 8 g/g, more preferably 10-20 g/g. Generally speaking, the substitution by ionic groups should be carried out to result in a degree of substitution of at least 0.1, preferably at least 0.2.

When the substitution stage results in a salt of a carboxylic starch derivative, the process preferably also comprises the additional steps of: 4. treating said starch derivative with an acid to convert the carboxyl groups into their acid form; 5. washing said acid form of the starch derivative with water to remove any soluble salts; and 6. neutralising the acid form of the starch derivative with an alkali to reconvert the starch derivative into an ionic form as an alkali metal, alkaline earth metal, ammonium or substituted ammonium salt.

Conversion of the carboxy group to its acid form and subsequent neutralisation has the advantage that the washing and subsequent drying are facilitated on account of the low water retention of the acid form. Preferably in step (6) the acid form of the starch derivative is neutralised with excess ammonia solution whereafter by heating excess ammonia is removed and the ammonium salt dried.

The starch derivatives of this invention may be obtained from, for example, potato starch, maize starch, wheat starch or tapioca starch.

The invention also relates to liquid absorbent articles containing the absorbent material of the invention, including that prepared by the process of the invention. The liquid absorbent article may comprise a fibrous carrier or support for the absorbent material, such as a woven or unwoven material such as cotton cloth, rayon, wool, surgical gauze or paper as well as cellulosic fluff, on or within which the absorbent material is supported. The absorbent material may be spread on the carrier or it may be mixed with loose fibres to make a composite fluff or wadding which can be enclosed between cover sheets of paper or cloth. The article may also be in the form of a laminate. In a particular form, the carrier comprises two sheets between which the absorbent material is sandwiched.

The absorbent materials of this invention are also useful in other fields, for example as a drying agent; for absorbing perspiration; as a litter material for pets; as a water reservoir agent, eg in horticultural use; and as a carrier for various materials, eg perfumes.

The preparation of absorbent materials in accordance with the invention will now be described with reference to the following Examples 1 to 19 given by way of illustration only.

In these examples the bed volumes of the products obtained at various stages of the processes described are referred to. The bed volume of an absorbent material is determined by allowing 1 gram of the material to stand in excess water in a graduated vessel and reading off the swollen volume.

Urine and water retention values were obtained as described above and are expressed to the nearest quarter of a unit.

The solubility data for the starch derivatives given in the examples were obtained as follows. The absorbent (1 g) was slurried in distilled water (100 ml) at room temperature with stirring for 15 minutes. The slurry was allowed to stand over-night before filtering. The dissolved carbohydrate in the filtrate was measured by the known colorimetric method employing the use of the phenol/sulphuric acid test for soluble carbohydrate. In these determinations to 1 ml of the sample of the test solution were added 1 ml of phenol solution (5% w/v) followed by 5 ml of concentrated sulphuric acid and the liquids mixed by shaking.

After leaving to cool for about an hour the concentration of the soluble carbohydrate was determined using a Unicam SP 800 ultra-violet spectrophotometer from the absorbence at the peak at 483 nm by reference to a glucose standard.

Example 1 Potato starch (1,000 g) was slurried in water (950 ml) containing epiclorhydrin (8.4 ml; 1 .0%epichlorhydrin by weight of starch). Sodium hydroxide (5 g) in water (50 ml) was added with stirring and the mixture was applied to a heated roller via a feeder roller to form a layer on the surface of the roller of about 0.5 mm thickness. The roller itself was heated using steam at 3.77 bars (140"C). The cross-linked starch derivative was removed from the roller as a flake material to yield 914 g of product. The soluble content of the product was found to be 25.0 mg/g and the product was found to have a bed volume of 13.5 ml/g. Since about half of the epichlorhydrin was lost by evaporation from the heated roller the degree of substitution of the cross-linking groups was about 0.01.

Sodium hydroxide (34 g) in water (66 ml) followed by monochloracetic acid (39 g) in water (11 ml) was slowly added with stirring to the cross-linked potato starch (100 g) as prepared above. The mixture was aged overnight in a polythene bag. The theoretical degree of substitution was 0.67.

The moist carboxymethyl derivative was repeatedly dispersed in water and filtered until the filtrate was neutral. The highly water swollen washed cake was dried in a forced air oven (700 C) was milled through a 2 mm screen. The milled product (102.7 g) had a water retention value of 24.75 g/ g, a urine retention value of 13.00 g/ g, a solubility of 0.6 % and a bed volume of 50 ml/g.

Example 2 Example 1 was repeated exactly as far as ageing the carboxymethylated mixture in a polythene bag. The theoretical degree of substitution was again 0.67.

The moist carboxymethyl derivative was dispersed in 10 times its weight of 1N hydrochloric acid and soaked for 15 minutes and then filtered. The gel cake was repeatedly dispersed in water and filtered until the filtrate was substantially free of chloride ions. Ammonium hydroxide, specific gravity 0.910, (70 ml) was mixed with the water swollen washed cake before drying in a forced air oven (70"C) and milling (2 mm screen). The milled product had a water retention value of 20.00 g/g, a urine retention value of 10.25 g/g, a solubility of 0.3% and a bed volume of 51 ml/g.

Example 3 Maize starch (500 g) was slurried in water (475 ml) containing epichlorhydrin (4.2 ml; 1% epichlorhydrin by weight of starch). Sodium hydroxide (2.5 g) in water (25 ml) was added with stirring and the mixture was applied to a heated roller as in Example 1. The cross-linked starch derivative was found to have a bed volume of 8.5 ml/g.

The cross-linked maize starch was carboxymethylated as in Example 1 and the product washed and isolated as the ammonium salt as in Example 2 by treatment first with hydrochloric acid and then ammonium hydroxide. The actual degree of substitution was 0.43. The milled product had a water retention value of 16.25 g/g, a urine retention value of 8.75 g/g, a solubility of 1.5% and a bed volume of 44 ml/g.

Example 4 Potato starch (100 g) was slurried in water (80 ml) containing 1,2-7,8-diepoxyoctane (0.8 ml). Sodium hydroxide (0.5 g) in water (20 ml) was added with stirring and the slurry applied to a heated roller as in Example 1. The soluble content of the product was 11.6 mg/g and the bed volume 15.5 ml/g. The degree of substitution of the cross-linking groups was about 0.009.

The cross-linked potato starch derivative (60 g) milled through a 2 mm screen was carboxymethylated as in Example 1 and the product, after ageing, was washed and isolated as the ammonium salt as in Example 2. The actual degree of substitution was 0.36. The milled product had a water retention valve of 17.25 g/g, a urine retention value of 10.00 g/g, a solubility of 0.5% and a bed volume of 33 ml/g.

Example 5 1% Cross-linked potato starch (100 g) as prepared in Example 1 was carboxymethylated as in that example, aged overnight in a polythene bag and treated with 1N HC1 and washed by being repeatedly dispersed in water as in Example 2. To the water swollen washed cake (964 g) was added with stirring a solution of sodium carbonate (16.2 g) in water (100 ml) before drying in a forced air oven (70"C). The milled product (102.1 g) had a water retention value of 19.25 g/g, a urine retention value of 11.50 g/g, a solubility of 0.8% and a bed volume of 42 ml/g.

Example 6 To a cake (878.5 g) of acid washed carboxymethylated cross-linked starch, obtained as in the preceding Example, was added with stirring a solution of magnesium carbonate (16.8 g) in water (100 ml) before drying in a forced air oven (70"C). The milled product (113.5 g) had a water retention value of 9.25 g/g, a urine retention value of 8.75 g/g, a solubility of 0.6% and a bed volume of 23 ml/g.

Example 7 The sodium salt of carboxymethylated cross-linked starch prepared as in Example 1 (20 g) was soaked in 1M magnesium chloride solution (1,000 ml) with occasional stirring for 24 hours then repeatedly washed and filtered until the filtrate was substantially free of chloride ions and dried in a forced air oven (700 C). The milled product (16.8 g) had a water retention value of 12.50 g/g, a urine retention value of 10.50 g/g and a bed volume of 29 ml/g.

Example 8 Alkali potato starch was prepared exactly as the cross-linked starch in Example 1 except that no epichlorhydrin was added to the slurry before roller drying. Water (20 ml) was sprayed onto the alkali starch (100 g) which was then transferred to a sealable jar where epichlorhydrin (0.17 ml; 0.20% by weight of starch) was added and the jar tightly sealed and placed in an oven at 50"C for 1 hour. The cross-linked starch product (bed volume 13 ml/g, soluble carbohydrate content 7.0 mg/g, degree of substitution of cross-linking groups of about 0.004) was immediately carboxymethlated as in Example 1, aged overnight, treated with acid and washed as in Example 2 until the filtrate was substantially free of chloride ions and the water swollen cake (1,339 g) ammoniated (70 ml of ammonium hydroxide solution sg 0.910) and dried in a forced air oven (70"C).

The milled product (108.6 g) had a water retention value of 12.25 g/g, a urine retention value of 9.00 g/g, a solubility of 0.6%, and a bed volume of 28 ml/g.

Examples 9 to 11 Alkali potato starch was prepared exactly as the cross-linked starch in Example 1 except that no epichlorhydrin was added to the slurry before roller drying. Water (20 ml) was sprayed onto alkali starch (100 g) which was then transferred to a jar where epichlorhydrin was added as indicated in Table 1 below and the jar tightly sealed and shaken for 0.5 hour then left at room temperature for 22.5 hours. The cross-linked starch products were then immediately carboxymethylated as in Example 1, aged overnight, treated with hydrochloric acid and washed as in Example 2 until the filtrates were substantially chloride free and the water swollen cakes ammoniated (70 ml of ammonium hydroxide solution sg 0.910) and dried in a forced air oven (70"C).

The milled products were tested for water retention value, urine retention value, solubility and bed volume. The data are given in Table 1.

Table 1 Epichlorhydrin Water Urine Bed Degree of Retention Retention Solubility Volume Example ml Substitution Value Value (%) (ml/g) 9 0.1275 0.003 17.75 12.00 0.8 41 10 0.1700 0.004 15.25 10.25 0.7 32 11 0.2550 0.006 13.25 10.00 0.5 27 Examples 12 to 16 1% Cross-linked potato starch (100 g) was carboxymethylated as in Example 1 to a degree of substitution shown in Table 2. The aged moist carboxymethyl derivative was then repeatedly dispersed in distilled water ( 8 1) and filtered until the filtrate was neutral. The highly water swollen cakes were dried in a forced air oven (70"C). Urine retention values are given in Table 2.

Table 2 Sodium Monochlor- Urine Hydroxide acetic acid Degree of Retention Example (g) (g) Substitution Value 12 19.8 23.3 0.25 10.50 13 29.6 35.0 0.42 12.25 14 39.5 46.6 0.56 13.75 15 49.4 58.3 0.66 13.25 16 74.1 87.4 0.71 14.50 Example 17 Sodium hydroxide (12.5 g) in water (30 ml) followed by acrylamide (8.8 gin water (30 ml) was slowly added with stirring to 1% cross-linked potato starch (20 g); the theoretical degree of substitution was 1.0. The mixture was aged overnight in a polythene bag then repeatedly dispersed in water (2 1) and filtered until the filtrate was neutral. The highly water swollen cake (704 g) was dried in a forced air oven (70"C). The carboxyethylated starch product (23 g) had a water retention value of 21.25 g/g, a urine retention value of 11.75 g/g, a solubility of 1.3% and a bed volume of 46 ml/g.

Example 18 Triethylamine (85.5 ml), epichlorhydrin (48.4 ml) and water (200 ml) were stirred together for 16 hours to form the quaternary ammonium salt. Potato starch (25 g), epichlorhydrin (0.25 ml) and the quaternary adduct (35 ml) were mixed together for 1 minute and then the suspension dried to a flake on a roller drum drier (heated at 1400C) upon which gelatinisation, cross-linking and substitution of the starch all took place. The dried flake was milled through a 1 mm screen. The product had a urine retention value of 11.25 g/gm. The starch was substituted by quaternised groups of the formula -CH2CH(OH)CH2 N+(C2H5)3 Cl Example 19 0.5% Cross-linked potato starch was prepared exactly as in Example 1 but using half the stated amount of epichlorhydrin. 6 kg of this product were dispersed in aqueous isopropanol (42 1 of 91 %isopropanol) and heated to 40-50"C in a 1001 jacketed reaction vessel. S

The heating chamber 11 is an enclosure consisting essentially of an open feedthrough system of rollers 14, radiant heaters 15, and forced extraction exhaust duct 16.

The sanitary towel shown in Figure 2 consists of a non-woven longitudinal layer rayon fabric outer wrapper A, which may be water soluble. This wrapper is transversely sealed at its ends B.

Immediately below the wrapper is a stain reducing layer C. This is desirably a siliconetreated perforated non-woven layer.

Below the stain-reducing layer is a penetration layer D consisting of 16 layers of multi-ply crepe of 26 grammes per square metre weight. Then below the penetration layer are three layers of absorbent coated sandwich material E made as described above with reference to Figure 1.

Around the three layers E is a lower absorbent sheet F, which also consists of a tissue carrier layer carrying a continuous deposit of the absorbent material.

Then finally below the absorbent sheet is an impervious polyethylene layer G, and on the outside a gripstrip keeper H which is a conventional silicone-treated adhesive tape for keeping the towel in position in use.

Figure 3 and 4 show a tampon formed from a rolled sheet 20 of the absorbent coated sandwich material made as described above with reference to Figure 1 interspersed with a layer 21 of a long staple fibrous material of cotton, rayon or a cotton/rayon mix. A withdrawal cord 22 is provided.

In Specification No. 1,508,570 there is described and claimed a process for the preparation of a water absorbing, cross-linked starch derivative comprising applying a mixture of starch granules, water and a cross-linking agent as a thin film to a heated surface to effect granule rupture and cross-linking to produce a substantially water-insoluble cross-linked gelatinised starch having a water swelling volume (as therein defined) of at least 5 ml/g.

In Specification No. 1508,123 there is described and claimed a process for making a starch derivative useful for absorbing relatively large quantities of water and urine which comprises applying a mixture of starch granules, water and cross-linking agent as a thin film to a heated surface to effect granule rupture and cross-linking to produce a substantially water-insoluble cross-linked gelatinised starch having a water swelling volume (as therein defined) of from 5 to 25 ml/g, and carboxyalkylating the cross-linked gelatinised starch to an actual degree of substitution of from 0.1 to 0.8 to provide a carboxyalkylated cross-linked gelatinised starch having a water regain (as therein defined) greater than 10 ml/g.

In Specification No. 1,519,949 there is described and claimed a process for obtaining in a purified form a substantially water-soluble absorbent which is a carboxyalkylated starch derivative in salt form which process comprises converting a salt form of the absorbent by treatment with acid into an acid form, washing said acid form of the absorbent with water, and subsequently reconverting the absorbent into a salt form by treatment with an alkali.

WHAT WE CLAIM IS: 1. An absorbent material which is substantially dry and non-sticky to the touch in the swollen state being a substantially water-insoluble cross-linked gelatinised starch, in which the degree of substitution of the cross-linking groups is 0.001 to 0.02, which is substituted by ionic groups which are attached to the starch by ether linkages and which groups are associated with mono- or di-valent counterions, and which has a urine retention value of at least 6 g/g.

2. An absorbent material as claimed in claim 1, wherein the degree of substitution of the cross-linking groups is from 0.003 to 0.02.

3. An absorbent material as claimed in claim 1 or claim 2 wherein the cross-linking is effected by ether bridges of the formula -O-R-O where R is an aliphatic group containing 1 to 10 carbon atoms.

4. An absorbent material as claimed in claim 3, wherein R is -CH2CH(OH)CH2-.

5. An absorbent material as claimed in any of the preceding claims, wherein the ionic groups have the formula Z-R'- where R1is an alkylene group having 1 to 5 carbon atoms and Z is an anionic carboxyl, sulphonic or phosphonic group or a cationic group of the formula

where R2 is hydrogen or C14 alkyl, and R3 and R4 are C1-4 alkyl or are alkylene groups linked together to form a five or six-membered heterocyclic ring.

6. An absorbent material as claimed in claim 5, wherein Rl is an alkylene group contain

**WARNING** end of DESC field may overlap start of CLMS **.

Claims

**WARNING** start of CLMS field may overlap end of DESC **. The heating chamber 11 is an enclosure consisting essentially of an open feedthrough system of rollers 14, radiant heaters 15, and forced extraction exhaust duct 16. The sanitary towel shown in Figure 2 consists of a non-woven longitudinal layer rayon fabric outer wrapper A, which may be water soluble. This wrapper is transversely sealed at its ends B. Immediately below the wrapper is a stain reducing layer C. This is desirably a siliconetreated perforated non-woven layer. Below the stain-reducing layer is a penetration layer D consisting of 16 layers of multi-ply crepe of 26 grammes per square metre weight. Then below the penetration layer are three layers of absorbent coated sandwich material E made as described above with reference to Figure 1. Around the three layers E is a lower absorbent sheet F, which also consists of a tissue carrier layer carrying a continuous deposit of the absorbent material. Then finally below the absorbent sheet is an impervious polyethylene layer G, and on the outside a gripstrip keeper H which is a conventional silicone-treated adhesive tape for keeping the towel in position in use. Figure 3 and 4 show a tampon formed from a rolled sheet 20 of the absorbent coated sandwich material made as described above with reference to Figure 1 interspersed with a layer 21 of a long staple fibrous material of cotton, rayon or a cotton/rayon mix. A withdrawal cord 22 is provided. In Specification No. 1,508,570 there is described and claimed a process for the preparation of a water absorbing, cross-linked starch derivative comprising applying a mixture of starch granules, water and a cross-linking agent as a thin film to a heated surface to effect granule rupture and cross-linking to produce a substantially water-insoluble cross-linked gelatinised starch having a water swelling volume (as therein defined) of at least 5 ml/g. In Specification No. 1508,123 there is described and claimed a process for making a starch derivative useful for absorbing relatively large quantities of water and urine which comprises applying a mixture of starch granules, water and cross-linking agent as a thin film to a heated surface to effect granule rupture and cross-linking to produce a substantially water-insoluble cross-linked gelatinised starch having a water swelling volume (as therein defined) of from 5 to 25 ml/g, and carboxyalkylating the cross-linked gelatinised starch to an actual degree of substitution of from 0.1 to 0.8 to provide a carboxyalkylated cross-linked gelatinised starch having a water regain (as therein defined) greater than 10 ml/g. In Specification No. 1,519,949 there is described and claimed a process for obtaining in a purified form a substantially water-soluble absorbent which is a carboxyalkylated starch derivative in salt form which process comprises converting a salt form of the absorbent by treatment with acid into an acid form, washing said acid form of the absorbent with water, and subsequently reconverting the absorbent into a salt form by treatment with an alkali. WHAT WE CLAIM IS:

1. An absorbent material which is substantially dry and non-sticky to the touch in the swollen state being a substantially water-insoluble cross-linked gelatinised starch, in which the degree of substitution of the cross-linking groups is 0.001 to 0.02, which is substituted by ionic groups which are attached to the starch by ether linkages and which groups are associated with mono- or di-valent counterions, and which has a urine retention value of at least 6 g/g.

4. An absorbent material as claimed in claim 3, wherein R is -CH2CH(OH)CH2-.

ing 1 or 2 carbon atoms and Z is -COO-.

7. An absorbent material as claimed in any of the preceding claims which is a carboxymethylated cross-linked gelatinised starch.

8. An absorbent material as claimed in any of the preceding claims, wherein the degree of substitution by the ionic groups is at least 0.1.

9. An absorbent material as claimed in any of the preceding claims, wherein the ionic groups are anionic groups and the counterions are alkali metal, alkaline earth metal, ammonium or substituted ammonium ions.

10. An absorbent material as claimed in claim 9, wherein the counterion is the sodium ion.

11. An absorbent material as claimed in claim 9, wherein the counterion is the potassium ion.

12. An absorbent material as claimed in claim 9, wherein the counterion is the ammonium ion.

13. An absorbent material as claimed in any of the preceding claims which is at least 95 % insoluble in water.

14. An absorbent material as claimed in any of the preceding claims which as a urine retention value of from 8 to 20 g/g.

15. An absorbent material as claimed in claim 1 being a sodium or ammonium salt of carboxymethylated epichlorhydrin-cross-linked gelatinised starch having a urine retention value of at least 10 g/ g and being insoluble in water to the extent of at least 99%by weight.

16. Process for making an absorbent material as claimed in claim 1 comprising: 1. gelatinising starch; 2. during the gelatinisation or thereafter treating the starch with a cross-linking bifunctional compound to produce a cross-linked gelatinised starch which is substantially insoluble in water and in which the degree of substitution of the cross-linking groups is from 0.001 to 0.02; and 3. during the gelatinisation or thereafter reacting the starch with a monofunctional etherifying agent to substitute the starch by ionic groups which are attached to the starch by ether linkages and which groups are associated with mono- or di-valent counterions, the degree of substitution of the ionic groups being such that the urine retention value of the substituted cross-linked gelatinised starch is at least 6 g/g.

17. A process as claimed in claim 16, wherein steps (1) and (2) are carried out by: (a) forming an aqueous alkaline slurry of starch granules containing the cross-linking bifunctional compound; and (b) rapidly heating the slurry by applying the slurry to a surface heated to 100-1800C to cause gelatinisation of the starch, reaction therewith of the cross-linking bifunctional compound and simultaneous drying, to produce cross-linked gelatinised starch in dry form.

18. A process as claimed in claim 16, wherein steps (1) and (2) are carried out by: (c) forming an aqueous slurry of starch granules; (d) applying the slurry to a surface heated to 100-1800Cto causegelatinisation of the starch and simultaneous drying; and (e) subsequently reacting the gelatinised starch with the cross-linking bifunctional compound in the presence of water and alkali to produce cross-linked gelatinised starch.

19. A process as claimed in claim 18, wherein the alkali is included in the slurry.

20. A process as claimed in claim 17 or 19 in which the concentration of the alkali in the aqueous starch slurry is insufficient to effect any substantial gelatinisation of the starch prior to heating.

21. A process as claimed in any of claims 16 to 20, wherein the gelatinisation and cross-linking of the starch are effected on the surface of a heated drum.

22. A process as claimed in any of claims 16 to 21, wherein the cross-linking bifunctional compound has the formula Q-R5-Y where R5 is an alkylene group containing from 1 to 10 carbon atoms and Q and Y represent a halogen or an epoxy oxygen atom, the latter being linked to carbon atoms of the group R5 with the formation of an oxirane ring.

23. A process as claimed in claim 22, wherein the cross-linking bifunctional compound is epichlorhydrin.

24. A process as claimed in any of claims 16 to 23, wherein the degree of substitution of the cross-linking groups is from 0.003 to 0.02.

25. A process as claimed in any of claims 16 to 24, wherein the ionic groups have the formula Z-R'- where Z and Rl have the meanings defined in claim 5.

26. A process as claimed in claim 25, wherein the monofunctional etherifyine agent has the formula Z '-R l-X where R1 is an alkylene group of from 1 to 5 carbon atoms, Z is an ionic group as defined in claim 5 or a group capable of being converted into such an ionic group, and X is halogen or an epoxy group.

27. A process as claimed in claim 26, wherein Rl is an alkylene group containing 1 or 2 carbon atoms and Z1 is a carboxylic acid group or a salt thereof.

28. A process as claimed in claim 27, wherein the etherifying agent is monochloracetic acid or the sodium salt thereof.

29. A process as claimed in any of claims 16 to 28, wherein the degree of substitution of the ionic groups is at least 0.1.

30. A process as claimed in any of claims 16 to 29 in which the ionic groups are carboxyl, comprising the additional steps of: 4. treating said starch derivative with an acid to convert the carboxyl groups into their acid form; 5. washing said acid form of the starch derivative with water to remove any soluble salts; and 6. neutralising the acid form of the starch derivative with an alkali to reconvert the starch derivative into an ionic form as an alkali metal, alkaline earth metal, ammonium or substituted ammonium salt.

31. A process as claimed in claim 30, wherein in step (6) the acid form of the starch derivative is neutralised with excess ammonia solution whereafter by heating excess ammonia is removed and the ammonium salt dried.

32. A process as claimed in any of claims 17 to 19, wherein the aqueous slurry of starch granules contains about 1 to 2 parts by weight of water per part of starch.

33. A process as claimed in claim 18, wherein in step (e) the amount of water is from 0.1 to 0.5 parts per part of starch.

34. A process as claimed in any of claims 16 to 33, wherein said counterions in step (3) are sodium ions.

35. A process as claimed in any of claims 16 to 34, wherein the cross-linking and etherification are effected in such manner as to produce an absorbent material having a urine retention value of at least 8 g/g.

36. A process as claimed in any of claims 16 to 35, wherein the cross-linking is effected in such manner as to produce an absorbent material which is at least 95% insoluble in water.

37. A process as claimed in any of claims 16 to 36, wherein the starch derivative produced is the sodium or ammonium salt of carboxymethylated epichlorhydrin-cross-linked gelatinised starch having a urine retention value of at least 10 g/g and being insoluble in water to the extent of at least 99% by weight.

38. A process of making an absorbent material substantially as herein described with reference to any of Examples 1 to 19.

39. An absorbent material made by the process claimed in any of claims 16 to 38.

40. A liquid absorbent article containing an absorbent material as claimed in any of claims 1 to 15 or 39.

41. A liquid absorbent article as claimed in claim 40, wherein the absorbent material is supported on or within a fibrous carrier sheet.

42. A liquid absorbent article as claimed in claim 41, wherein the absorbent material is sandwiched between two sheets.

43. A liquid absorbent article as claimed in claim 41 or 42, wherein the carrier is made of paper.

44. A sanitary towel or tampon containing an absorbent material as claimed in any of claims 1 to 15 or 39.

45. A sanitary towel as claimed in claim 44 substantially as herein described with reference to Figure 2.

46. A tampon as claimed in claim 44 substantially as herein described with reference to Figures 3 and 4.