GB1564172A - Transmission belt - Google Patents

Description

(54) TRANSMISSION BELT (71) We, THE ARBEE CORPORA TION, a corporation organized under the Laws of the State of Pennsylvania, United States of America, of 311 West Stiegel Street, Manheim, Pennsylvania 17546 United States of America, do hereby declare the invention, for which we pray that a Patent may be granted us, and the method by which it is to be performed, to be particularly described in and by the follow mg Statement: The present invention relates to transmission belts for use both for power transmission and for conveying and, more particularly, to driving belts of the type comprising a number of superimposed links secured together by interlocking the links without separate fastening means, for example by tab portions of the links which pass through openings formed in the adjacent links.

The present invention has particular application to V-belt for use in environments where the belts are subjected to severe conditions of heat and moisture during their operation, and specifically washing apparatus where the belts are exposed to water, dirt, grease or the like, such as, for example, meat processing apparatus, and seamlesscan-manufacturing apparatus in which freshly-drawn cans are conveyed between opposing runs of transmission belts while flooded with coolant and/or the drawing lubricant.

In meat processing apparatus, the meat may be subjected to baths or sprays at elevated temperature. The transmission means are positioned within the housing of the apparatus so that they are exposed to the harsh conditions within the apparatus housing, including not only the elevated temperature and moisture conditons of the sprays, but also to animal fats of the material being processed at the elevated temperatures.

Interlocking-link type transmission belts are particularly adapted for use in apparatus where it is desirable to avoid the use of fasteners or other metallic parts. Such parts may corrode and fail under harsh operating condition; in food-processing apparatus, metallic shavings or spurs may contaminate the food product; in can manufacturing apparatus, metallic parts may damage or mar the surface of the freshly-drawn cans prior to lithographing and in apparatus operating in an explosive or flammable atmosphere, the metallic parts may generate sparks which might ignite such atmosphere.

Prior link belts of this character have not been entirely satisfactory for use in the hot, moist and/or oily or greasy conditions within food-processing apparatus because of the fact that the links of such belts are normally composed of a multi-ply fabric laminated structure whose integrity is maintained by a suitable bonding agent permeating the laminated structure. Links of this character have been proved highly successful for use in normal operating environments but in the hot, moist and/or oily and greasy environments there is a tendency for the plies of the links to separate and there is a relatively short operating life for such belts. However, they are used because their advantages outweigh such disadvantages.

Furthermore, the conventional fabricreinforced links, when they becom wet, tend to swell and stretch, which affects the tension in the belt. The use of link belts in a wet environment is not normally recommended.

Previous attempts to improve the life span of inter-locking link-type belts operating under extreme conditions have been to provide a secondary locking tab, or to add supplemental reinforcement to retard the escape of the end tab of one link from the receiving apertures of the adjacent links.

Additional effort was directed toward improving the material in the laminated struc tures, such as the fabric component of the structure and the bonding material used to integrate the plies of the structure into a unitary link.

Previous attempts to find a suitable substitute for the multi-ply fabric laminated structures have met with failure.

With the foregoing in mind, the present invention aims to provide a novel interlocking-link-type driving belt which has been discovered to have an extended life in use which is substantially longer than the life of belts using standard material.

According to the invention, a transmission belt comprises a plurality of links arranged in superimposed successive overlapping relation, each of said links having a body portion with at least two longitudinally-aligned apertures, and an integral fastening means comprising a laterally constricted neck portion and a locking tab connected to said body portion by said neck portion, said integral fastening means being longitudinally aligned with said apertures and extending through a forward aperture in the succeeding link and a trailing aperture in the next succeeding link whereby said plurality of links are secured together in overlapping relation to thereby form a belt, said body portion, neck portion and locking tab comprising a homogeneous material consisting of a segmented thermoplastic copolymer containing long chain polyester units derived from a dicarboxylic acid and a long chain glycol and short chain polyester units derived from a dicarboxylic acid and a low molecular weight diol.

Segmented thermoplastic copolyester materials suitable for manufacturing the links of a transmission belt in accordance with the invention are described in U.S.

Patents Nos. 3,651.014, 3.763.109 and 3,766,146. A particularly preferred material is that which is commercially available from E.I. duPont de Nemours & Co.. Inc., under the Trade Mark "Hytrel".

Preferably, the segmented thermoplastic copolyester material for use in manufacturing the links of a drive belt in accordance with the invention has a Shore D hardness of from 40 to 72, a particularly preferred Shore D hardness for material being approximately 55.

The links of a transmission belt in accordance with the invention may be fabricated using standard simplified stamping or molding techniques and they may be assembled in the factory or in the field to provide a belt of high durability.

When molded, the links may be formed in a single-step into any one of several configurations, which may be designed to accommodate a specific condition of use.

The invention will now be described, by way of example, with reference to the accompanying drawings, in which: Figure 1 is a plan of a length of transmission belting embodying the present invention, Figure 2 is a side elevational view of the belt shown in Figure 1 with portions broken away to show details of the construction of the belt.

Figure 3 is a transverse sectional view taken on the line 3-3 of Figure 2 showing a sheave in broken lines to illustrate the operation of the belt, Figure 4 is a perspective view of a link of the belt in a flat condition prior to assembly, Figures SA, 5B and 5C are top, end and side elevational views of a shaped link similar to the link of Figure 4 but having pre-formed bevels along the sides and tail, and Figures 6A, 6B and 6C and Figures 7A, 7B and 8C are views similar to Figures SA, SB and SC showing other forms of preformed shaped links in accordance with the invention.

Referring now to the drawings and more particularly to Figures 1 and 2 thereof, the belt 20 comprises a plurality of superimposed links 10 joined together by integral fastening means. Each fastening means comprises a locking tab 11 joined to the body 13 of the link 10 through a constricted neck 14. As illustrated in Figures 2 and 3, the locking tab 11 is spaced a sufficient distance apart from the body 13 to receive therebetween two of the links 10.

The links 10 are provided with registering apertures for receiving the locking tabs 11 and the neck 14 of preceding links 10 as they are assembled in superimposed relation. As shown in Figure 4, the links 10 are provided with forward apertures 26 and trailing apertures 27. When the links are assembled in successive superimposed overlapping relation, the trailing aperture 27 is in registry with the forward aperture 26 of the adjacent link, so that the locking tab 11 of the overlapping link first passes sideways through the forward aperture 26 of the adjacent link and then through the trailing aperture 27 of the innermost link, and then is twisted to bear against the inner surface 18 of the innermost link. For ease of belt assembly, both of the apertures are longer in the axial direction than they are wide so that the locking tab 11 of the link to be assembled in superimposed relation, when twisted so as to align axially with the apertures, will more easily pass through the apertures. When the locking tab 11 is released from its twisted position, it aligns cross-wise with the belt 20 in a position perpendicular to the longitudinal axis of the links 10 and since the width of the apertures is less than the length, the locking tab 11 is unable to pass through the apertures and thus is locked in position against the inner surface of the innermost link as shown in Figure 3.

Figure 3 shows a preferred embodiment of the belt, with locking tab 11 on the inner periphery 18, when in operation in a typical V-belt sheave. As shown in Figure 4, the head portion 21 of the link 10 is wider than the tail portion 22, thus facilitating the natural curvature of the superimposed links 10 by placing the widest portion of the link 10 on the outer periphery 19 of the belt 20.

Thus, by making the head portion wider than the tail portion, the longitudinal centerline of the links automatically assume a convex curvature upon assembly in successive superimposed overlapping relation.

As the locking tabs are passed through successive links and then terminate, their tendency when the belt is tensioned is to dispose themselves parallel to the link by flattening out. In the belt 20, when the tabs lie on the inner periphery 18 of the belt, the outer periphery 19 contains the head portion 21, and since the outer periphery 19 of the belt 20 is wider at any point than that portion of the adjacent or intermediate link, and the intermediate link in turn is wider at that point than the tail portion 22 of the innermost link, the belt assumes a V-shaped cross-section with the tab 11 in the apex of the V-shape, as illustrated in Figure 3.

Despite the fact that the superimposed links are generally V-shaped in crosssection, the edges 17 of the V would be stepped. Therefore, in the final form and after assembly, the edges of the links are trimmed to provide a bevel to ensure proper seating in the associated sheaves. Figure 3 illustrates, as an example, the trimmed sides 23 of the belt 20 and Figure 1 shows the trimmed straight outer edges formed by the sides 23.

The links 10 are fabricated from homogeneous material which is devoid of fabric lamination and comprising a segmented thermoplastic copolyester containing recurring long chain polyester units derived from a dicarboxylic acid and a long chain glycol and short chain polyester units derived from a dicarboxylic acid and a low molelcular weight diol, in particular the material which is commercially available from E.I. duPont de Nemours & Co., Inc..

under the registered Trade mark "Hytrel" and is described in U.S. Patent Nos.

3,651,014; 3,763,109 and 3,766,146. The elimination of the fabric lamina, which have been characteristic of commerciallyavailable belt links of the prior art, is believed to contribute to the durability and operational life of the transmission belts of the present invention. As stated above, the belts of the present invention are designed for use in an environment where conventional commercially-available link belts are not entirely satisfactory. In a particular application, the transmission belt of the present invention is used in meat-processing apparatus in which the belt itself is subjected not only to moisture and heat, for example water 1200F, but also to animal fats. The transmission belts are used with V-pulleys and the operation of the transmission belts subjects them to a wide variety of stresses and strains.Elimination of the fabric lamina from the links 21 is believed to permit the use of a material which is highly resistant to the damage from the severe conditions within the apparatus.

It has been discovered that in fabricating a link of the type shown in the drawings for use in an interlocking-link belt having integral fastener portions passing through successive apertures in succeeding links, a segmented thermoplastic copolyester of the type set forth should have a durometer above 40D (92A) and less than 72D. The preferred durometer has been found to be approximately 55D for use in link belts, as shown in the drawings.

The links formed of the segmented thermoplastic copolyester of the present invention are readily susceptible to being trimmed after assembly into the belt to provide the beveled edges which are aligned to provide the straight edges 23 of the assembled belt, as shown in Figures 1 and 3.

However, the thermoplastic material of the present invention also in susceptible of being pre-formed to produce comparable characteristics in the assembled belt. For example, as shown in Figures 5A, 5B and 5C, a link 30 may be pre-formed by molding or die-cutting to provide a locking tab 31, a body 33 and a neck 34 comparable to the tab 11, body 13 and neck 14. However, in the forming operation, the side edges 37 are pre-formed parallel to each other at the head end, as indicated at 38, and convergent at the tail end, as indicated at 39. This formation provides straight edges 23 in the assembled belt as shown in Figure 1. Furthermore, the edges 37 are also undercut to provide a slight bevel, as indicated at 36.

The angle of the bevel 36 in the respective portions 38 and 39 is selected to ensure proper seating in the associated V-sheaves without trimming. In the formation of the link 30, it may also be preferred to bevel the tail of the link as indicated at 32 to provide a smoother undersurface in the assembled belt. The illustrated configuration is readily accomplished by the use of a suitable die in the process of forming the link.

Figures 6A. 6B and 6C show a further modification of the link shown in Figures 5A. 5B and 5C. The link 40 shown in these Figures includes a locking tab 41 at the head, a neck 44, a body portion 43 and a beveled tail at 42. The side edges of the body portion 43 are formed identically to the side edges 37 of the body portion 33. In this embodiment of the link, the locking tab 41 at the head is formed with a substantially greater thickness than the body portion 43.

As shown in Figure 6C, the locking tab 41 is substantially thicker than the body portion 43 and the neck 44 tapers in thickness from the thickness of the tab 41 to the thickness of the body portion 43. The tab thickness is less than the width of the apertures to faciliate assembly. This configuration of link is particularly adapted for use in belt assemblies in which there is a substantial tendency for the locking tab to flex and pull through the receiving apertures of the adjacent links. The enlarged thickness of the tab 41 resists such flexing and assists in maintaining the integrity of the belt assembly.

Such a link is conveniently fabricated by the proper selection of a suitable die configuration in an injection molding operation.

Figures 7A, 7B and 7C illustrate a link 50 which is pre-formed with a curvature conforming closely to the curvature assumed by the link when assembled in a belt and tensioned. as shown in Figures 1 and 2. As shown in these Figures, the link 5() includes a locking tab 51. a neck 54. a body portion 53 and a beveled tail at 52. In this embodiment, the portions are of substantially uniform thickness throughout. However. the body portion 53 is pre-formed or permanentlv set with a shallow dished curvature centrallv thereof as indicated bv the radius at 55. and the neck 54 and locking tab 51 are curved downwardly with a curvature, as indicated bv the radius 56.It should be noted that the radius 56 is substantially smaller than the radius of the curvature 55.

so as to conform the link closelv to the curvatures naturallv assumed bv the link when it is assembled into a belt and tensioned. The side edges of the link St) are shaped similarly to the side edges 37. as is evident in the drawing. The link may be formed and set in a single operation. as discussed above. or may also be formed and set in sequence.

The embodiment of Figures 7A. 7B and 7C is particularly suitable where the tension of the belt is critical. With the belt of this embodiment. when the arcuate links are assembled, the tendency of the belt to elongate in use is minimized. With the flat links. the stiffness of the link tends to foreshorten the belt when the belt is new and it requires considerable additional tension to straighten the belt to the condition shown in Figure 1. With the links preformed as shown in Figures 7A, 7B and 7C.

the curvature set into the links assists in the assembled belt assuming the flat configuni- tion shown in Figure 1. Thus. as the belt is used, the length and tension of the assembled belt remain substantially constant throughout the life of the belt.

The links of the present invention are susceptible of being injection-molded in any particular configuration desired. Alternatively, the sheet may be die-stamped to provide the desired configuration, the thermoplastic character of the material affording wide latitude in the selection of appropriate manufacturing techniques. It should be noted that inasmuch as the links may be molded to their ultimate shape prior to assembly in the belt, all of the links of the belt are identical in configuration. Thus, when it becomes necessary to repair the belt. as by replacing a link in the field, the link inserted in the belt (having been formed to the exact configuration of the link which it replaces) will align with the side edges of the remaining links and will seat properly in the sheaves without the need for trimming or other forming operations.These links therefore avoid the problems of nonuniform trimming of the belts which is inherent in the conventional two-step process of the prior art. Furthermore. the use of molding techniques to form the bevels generates a molded-surface condition on the bevels which is characteristically distinct from the trimmed-surface condition generated by a separate trimming operation.

Transmission belts made in accordance with the invention are particularly suited for use in wet processing apparatus where the belt is exposed to hot water, coolants andlor drawing lubricants. The links of the present invention resist retention of the liquid and thereby retain their dimensional stability whether wet or drv. The belt is particularly adapted for use in can manufacturing apparatus wherein the freshlv-drawn cans are conveyed between V-belts running around V-sheaves. Such belts are highly sensitive to variations in tension, and slack in the belt tends to permit disengagement from the sheave. The present invention provides a belt resistant to stretching and thereby tends to preserve the proper tension in the V-belts so as to reduce the tendency of the belts to disengage from their pulleys.

WHAT WE CLAIM IS: 1. A transmission belt comprising a plu reality of links arranged in superimposed successive overlapping relation, each of said links having a body portion with at least two longitudinallv-aligned apertures. and an integral fastening means comprising a laterally constricted neck portion and a locking tab connected to said body portion by said neck portion, said integral fastening means being longitudinally aligned with said apertures and extending through a forward aperture in the succeeding link and a trailing aperture in the next succeeding link whereby said plu

**WARNING** end of DESC field may overlap start of CLMS **.

Claims (13)

**WARNING** start of CLMS field may overlap end of DESC **. beveled tail at 42. The side edges of the body portion 43 are formed identically to the side edges 37 of the body portion 33. In this embodiment of the link, the locking tab 41 at the head is formed with a substantially greater thickness than the body portion 43. As shown in Figure 6C, the locking tab 41 is substantially thicker than the body portion 43 and the neck 44 tapers in thickness from the thickness of the tab 41 to the thickness of the body portion 43. The tab thickness is less than the width of the apertures to faciliate assembly. This configuration of link is particularly adapted for use in belt assemblies in which there is a substantial tendency for the locking tab to flex and pull through the receiving apertures of the adjacent links. The enlarged thickness of the tab 41 resists such flexing and assists in maintaining the integrity of the belt assembly. Such a link is conveniently fabricated by the proper selection of a suitable die configuration in an injection molding operation. Figures 7A, 7B and 7C illustrate a link 50 which is pre-formed with a curvature conforming closely to the curvature assumed by the link when assembled in a belt and tensioned. as shown in Figures 1 and 2. As shown in these Figures, the link 5() includes a locking tab 51. a neck 54. a body portion 53 and a beveled tail at 52. In this embodiment, the portions are of substantially uniform thickness throughout. However. the body portion 53 is pre-formed or permanentlv set with a shallow dished curvature centrallv thereof as indicated bv the radius at 55. and the neck 54 and locking tab 51 are curved downwardly with a curvature, as indicated bv the radius 56.It should be noted that the radius 56 is substantially smaller than the radius of the curvature 55. so as to conform the link closelv to the curvatures naturallv assumed bv the link when it is assembled into a belt and tensioned. The side edges of the link St) are shaped similarly to the side edges 37. as is evident in the drawing. The link may be formed and set in a single operation. as discussed above. or may also be formed and set in sequence. The embodiment of Figures 7A. 7B and 7C is particularly suitable where the tension of the belt is critical. With the belt of this embodiment. when the arcuate links are assembled, the tendency of the belt to elongate in use is minimized. With the flat links. the stiffness of the link tends to foreshorten the belt when the belt is new and it requires considerable additional tension to straighten the belt to the condition shown in Figure 1. With the links preformed as shown in Figures 7A, 7B and 7C. the curvature set into the links assists in the assembled belt assuming the flat configuni- tion shown in Figure 1. Thus. as the belt is used, the length and tension of the assembled belt remain substantially constant throughout the life of the belt. The links of the present invention are susceptible of being injection-molded in any particular configuration desired. Alternatively, the sheet may be die-stamped to provide the desired configuration, the thermoplastic character of the material affording wide latitude in the selection of appropriate manufacturing techniques. It should be noted that inasmuch as the links may be molded to their ultimate shape prior to assembly in the belt, all of the links of the belt are identical in configuration. Thus, when it becomes necessary to repair the belt. as by replacing a link in the field, the link inserted in the belt (having been formed to the exact configuration of the link which it replaces) will align with the side edges of the remaining links and will seat properly in the sheaves without the need for trimming or other forming operations.These links therefore avoid the problems of nonuniform trimming of the belts which is inherent in the conventional two-step process of the prior art. Furthermore. the use of molding techniques to form the bevels generates a molded-surface condition on the bevels which is characteristically distinct from the trimmed-surface condition generated by a separate trimming operation. Transmission belts made in accordance with the invention are particularly suited for use in wet processing apparatus where the belt is exposed to hot water, coolants andlor drawing lubricants. The links of the present invention resist retention of the liquid and thereby retain their dimensional stability whether wet or drv. The belt is particularly adapted for use in can manufacturing apparatus wherein the freshlv-drawn cans are conveyed between V-belts running around V-sheaves. Such belts are highly sensitive to variations in tension, and slack in the belt tends to permit disengagement from the sheave. The present invention provides a belt resistant to stretching and thereby tends to preserve the proper tension in the V-belts so as to reduce the tendency of the belts to disengage from their pulleys. WHAT WE CLAIM IS:

1. A transmission belt comprising a plu reality of links arranged in superimposed successive overlapping relation, each of said links having a body portion with at least two longitudinallv-aligned apertures. and an integral fastening means comprising a laterally constricted neck portion and a locking tab connected to said body portion by said neck portion, said integral fastening means being longitudinally aligned with said apertures and extending through a forward aperture in the succeeding link and a trailing aperture in the next succeeding link whereby said plu

rality of links are secured together in overlapping relation to thereby form a belt, said body portion, neck portion and locking tab comprising a homogeneous material consisting of a segmented thermoplastic copolyester containing long chain polyester units derived from a dicarboxylic acid and a long chain glycol and short chain polyester units derived from a dicarboxylic acid and a low molecular weight diol.

2. A drive belt according to claim 1 wherein said homogeneous material has a Shore D hardness of from 40 to 72.

3. A drive belt according to claim 2 wherein said homogeneous material has a Shore D hardness of 55.

4. A transmission belt according to any of the preceding claims wherein said body portion is of substantially uniform thickness throughout, and said locking tab is substantially thicker than said uniform thickness, and wherein further the length of said constricted neck portion exceeds the combined thicknesses of the body portions of said plurality of overlapped links.

5. A transmission belt according to claim 4 wherein said constricted neck portion tapers in thickness from the thickness of said locking tab to the thickness of said body portion.

6. A transmission belt according to any of the preceding claims wherein the transverse width of said apertures is less than the width of said locking tab, greater than the width of said constricted neck portion and greater than the thickness of said locking tab and the length of said apertures is greater than their transverse width to afford passage of said locking tab sideways through said apertures during assembly of said belt.

7. A transmission belt according to any of claims 1 to 3 wherein said integral fastening means of each link has a permanent set curving downwardly away from the upper surface of said body portion intermediate said forward aperture and said neck portion.

8. A transmission belt according to any of the preceding claims wherein all of said links are identical in configuration, each link having a body portion with downwardly directed bevels along the side walls and an upward facing bevel across the tail end remote from said constricted neck portion.

9. A transmission belt according to claim 8 wherein said side walls of said body portion adjacent said constricted neck portion extend parallel to the longitudinal center line of said link, and adjacent said tail end converge towards one another in the direction of said tail.

10. A transmission belt according to claim 8 or 9 wherein said beveled surfaces have a molded surface condition throughout.

11. A method of making an interlocking-link type transmission belt comprising the steps of molding a plurality of individual links from a homogeneous material consisting of a segmented thermoplastic copolyester containing long chain polyester units derived from a dicarboxylic acid and a long chain glycol and short chain polyester units derived from a dicarboxylic acid and a low molecular weight diol, all of said links being identical and having a body portion with at least two longitudinally-aligned apertures, and an integral fastening means comprising a laterally constricted neck portion and a locking tab aligned with said apertures, said apertures having a width less than the width of said locking tab, greater than the width of said neck and greater than the thickness of said locking tab, and assembling said links into a belt by disposing said links in superimposed successive overlapping relation and interlocking said links by passing the locking tab of each link sideways through the forward aperture in the succeeding link and a trailing aperture in the next succeeding link and twisting the tab to bear against the surface of the link surrounding said trailing aperture to thereby interlock said links to form a transmission belt.

12. A method according to claim 11 in which the segmented thermoplastic copolyester employed has a Shore D hardness of from 40 to 72, preferably approximately 55.

13. A transmission belt constructed and arranged substantially as herein described with reference to, and as illustrated in, Figures 1 to 4, Figures 1 to 4 as modified by Figures 5A - 5C, Figures 1 to 4 as modified by Figures 6A - 6C or Figures 1 to 4 as modified by Figures 7A - 7C, of the accompanying drawings.