FR3114576A1 - Lid for closing a container with a heat-sealed peelable flexible film, and thus sealed container. - Google Patents
Lid for closing a container with a heat-sealed peelable flexible film, and thus sealed container. Download PDFInfo
- Publication number
- FR3114576A1 FR3114576A1 FR2009764A FR2009764A FR3114576A1 FR 3114576 A1 FR3114576 A1 FR 3114576A1 FR 2009764 A FR2009764 A FR 2009764A FR 2009764 A FR2009764 A FR 2009764A FR 3114576 A1 FR3114576 A1 FR 3114576A1
- Authority
- FR
- France
- Prior art keywords
- heat
- layer
- container
- flexible film
- sealed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Opercule de fermeture d’un contenant avec un film souple pelable thermoscellé, et dispositif de conditionnement comportant un contenant ainsi operculé. L’invention a trait à un opercule de fermeture d’un contenant (20) rigide ou semi-rigide, comportant un film souple (2) pelable thermoscellé sur le bord (22) d’une ouverture du contenant (20), ce film souple (2) comportant : une couche thermoscellable (8) en matière thermoplastique chargée, thermoscellée sur le contenant (20), ayant une adhésion sur le contenant (20) réduite du fait de la présence d’une charge au sein de cette couche, de façon à rendre le film souple (2) pelable manuellement,au moins une couche métallique (4) recouvrant la couche thermoscellable (8), etau moins un agent d’adhésion (6) à base acrylique entre la couche métallique (4) et la couche thermoscellable (8), cet agent d’adhésion (6) comportant un copolymère comportant au moins 9.5% en poids de motifs carboxyliques par rapport au poids du copolymère. Figure pour l’abrégé : Fig. 1 Lid for closing a container with a heat-sealed peelable flexible film, and packaging device comprising a container thus sealed. The invention relates to a lid for closing a rigid or semi-rigid container (20), comprising a flexible peelable film (2) heat-sealed on the edge (22) of an opening of the container (20), this film flexible (2) comprising: a heat-sealable layer (8) of filled thermoplastic material, heat-sealed onto the container (20), having reduced adhesion to the container (20) due to the presence of a filler within this layer, so as to make the film manually peelable flexible (2),at least one metallic layer (4) covering the heat-sealable layer (8), andat least one acrylic-based adhesion agent (6) between the metallic layer (4) and the heat-sealable layer (8) , this adhesion agent (6) comprising a copolymer comprising at least 9.5% by weight of carboxylic units relative to the weight of the copolymer. Figure for abstract: Fig. 1
Description
La présente invention concerne un opercule de fermeture d’un contenant rigide ou semi-rigide, comportant un film souple pelable thermoscellé sur le bord d’une ouverture du contenant.The present invention relates to a lid for closing a rigid or semi-rigid container, comprising a heat-sealed peelable flexible film on the edge of an opening of the container.
L’invention concerne également un contenant ainsi operculé.The invention also relates to a container sealed in this way.
On connaît des demandes de brevet EP 1 508 530 et US 2018/0170017 des contenants formés d’un film souple en un complexe multicouche comportant une couche métallique entre deux couches en un matériau plastique. Le film souple est thermoscellé sur lui-même pour former un sachet. L’ouverture de ce dernier se fait en déchirant le film souple.Patent applications EP 1 508 530 and US 2018/0170017 are known for containers formed from a flexible film in a multilayer complex comprising a metal layer between two layers of a plastic material. The flexible film is heat sealed on itself to form a sachet. The opening of the latter is done by tearing the flexible film.
Le brevet US 8 672 168 décrit un opercule pelable thermoscellé sur un contenant, comportant un film souple multicouche ayant une couche métallique située entre deux couches en matière plastique dont l’une est destinée à être thermoscellée sur le contenant. Les différentes couches sont assemblées entre elles par un liant.US Pat. No. 8,672,168 describes a peelable lid heat-sealed onto a container, comprising a flexible multilayer film having a metal layer located between two plastic layers, one of which is intended to be heat-sealed onto the container. The different layers are assembled together by a binder.
Les films souples connus, lorsqu’utilisés pour sceller un contenant, sont sujet à un délaminage en présence de certains composés agressifs tels que ceux contenant un agent alcalin ou oxydant. Ce délaminage se traduit par une séparation locale des couches entre elles, ce qui peut entrainer des fuites de la composition cosmétique hors du contenant et/ou une dégradation du produit, en augmentant la perméabilité de l’opercule à l’oxygène de l’air. La durée de conservation des produits et les performances du produit s’en trouve limitées.Known flexible films, when used to seal a container, are subject to delamination in the presence of certain aggressive compounds such as those containing an alkaline or oxidizing agent. This delamination results in a local separation of the layers between them, which can cause the cosmetic composition to leak out of the container and/or degrade the product, by increasing the permeability of the lid to oxygen in the air. . Product shelf life and product performance are limited.
Une solution au problème du délaminage est proposée dans la demande de brevet EP 1 669 305, décrivant un dispositif de conditionnement d’une composition cosmétique comportant un film souple en un complexe multicouche comportant une couche métallique liée par un agent d’adhésion comportant un copolymère ayant au moins 7% en poids de motifs carboxylique et/ou carboxylates à une couche en un matériau plastique. Le film souple peut être refermé sur lui-même pour former un sachet ou se fixer par tout moyen sur un contenant qu’il obture.A solution to the problem of delamination is proposed in patent application EP 1 669 305, describing a device for packaging a cosmetic composition comprising a flexible film in a multilayer complex comprising a metal layer bonded by an adhesion agent comprising a copolymer having at least 7% by weight of carboxylic and/or carboxylate units to a layer of a plastic material. The flexible film can be closed on itself to form a bag or be fixed by any means on a container that it closes.
Cependant, un tel film ne permet pas une ouverture aisée du contenant par pelage.However, such a film does not allow easy opening of the container by peeling.
Il existe donc un besoin pour bénéficier d’un opercule de fermeture d’un contenant rigide ou semi-rigide, permettant à la fois une bonne étanchéité dans le temps du contenant qu’il scelle, une bonne adhérence du film au contenant ainsi qu’une résistance au délaminage en présence de composés agressifs, tout en pouvant être décollé aisément de ce dernier par pelage manuel.There is therefore a need to benefit from a lid for closing a rigid or semi-rigid container, allowing both good sealing over time of the container that it seals, good adhesion of the film to the container as well as resistance to delamination in the presence of aggressive compounds, while being able to be easily detached from the latter by manual peeling.
L’invention vise à répondre à ce besoin et a pour objet un opercule de fermeture d’un contenant rigide ou semi-rigide, comportant un film souple pelable thermoscellé sur le bord d’une ouverture du contenant, ce film comportant :The invention aims to meet this need and has as its subject a lid for closing a rigid or semi-rigid container, comprising a flexible peelable film heat-sealed on the edge of an opening of the container, this film comprising:
- une couche thermoscellable en matière thermoplastique chargée, thermoscellée sur le contenant, ayant une adhésion sur le contenant réduite du fait de la présence d’une charge au sein de cette couche, de façon à rendre le film pelable manuellement,a heat-sealable layer of filled thermoplastic material, heat-sealed on the container, having reduced adhesion to the container due to the presence of a filler within this layer, so as to make the film manually peelable,
- au moins une couche métallique recouvrant la couche thermoscellable, etat least one metallic layer covering the heat-sealable layer, and
- au moins un agent d’adhésion à base acrylique entre la couche métallique et la couche thermoscellable, cet agent d’adhésion comportant un copolymère comportant au moins 9.5% en poids de motifs carboxyliques par rapport au poids du copolymère.at least one acrylic-based adhesion agent between the metal layer and the heat-sealable layer, this adhesion agent comprising a copolymer comprising at least 9.5% by weight of carboxylic units relative to the weight of the copolymer.
La présence de l’agent d’adhésion ci-dessus permet d’éviter la délamination des couches, malgré la moindre adhérence de la couche thermoscellable du fait de la présence des charges, ce qui assure une bonne étanchéité de la fermeture, et cela même lorsque le produit est une composition alcaline et/ou oxydante.The presence of the adhesion agent above makes it possible to avoid the delamination of the layers, despite the lower adhesion of the heat-sealable layer due to the presence of the fillers, which ensures good sealing of the closure, and that even when the product is an alkaline and/or oxidizing composition.
La couche thermoscellable permet également d’avoir une bonne adhérence du film sur le contenant tout en permettant un décollement manuel aisé de celui-ci.The heat-sealable layer also makes it possible to have good adhesion of the film to the container while allowing easy manual detachment of it.
Couche thermoscellableheat seal layer
La couche thermoscellable est un matériau polymère dans lequel des charges sont ajoutées.The heat sealable layer is a polymeric material in which fillers are added.
Le matériau polymère peut être choisi parmi les polyoléfines, comme par exemple le polyéthylène ou le polypropylène, les polyalkylène-téréphtalates ou les polyalkylène-isophtalates, comme par exemple le polyéthylène-téréphtalate (PET), le polypropylène téréphtalate, le polybutylène-téréphtalate (polytétraméthylènetéréphtalate), le polydécaméthylène-téréphtalate, le poly-1,4-cyclohexyldiméthylol-téréphtalate ou le polyéthylène-2,6-naphtalènedicarboxylate ou les copolymères de polyalkylène, de polyalkylène-téréphtalate et de polyalkylène-isophtalate, , ainsi que les polymères séquences et les variantes greffées des substances susmentionnées.The polymer material can be chosen from polyolefins, such as for example polyethylene or polypropylene, polyalkylene terephthalates or polyalkylene isophthalates, such as for example polyethylene terephthalate (PET), polypropylene terephthalate, polybutylene terephthalate (polytetramethylene terephthalate ), polydecamethylene terephthalate, poly-1,4-cyclohexyldimethylol terephthalate or polyethylene-2,6-naphthalenedicarboxylate or copolymers of polyalkylene, polyalkylene terephthalate and polyalkylene isophthalate, as well as block polymers and grafted variants of the aforementioned substances.
De préférence, le matériau polymère est du polyéthylène dans lequel des charges ont été ajoutées, notamment connu sous la dénomination PEPeel, i.e. destiné à être pelé.Preferably, the polymer material is polyethylene in which fillers have been added, in particular known under the name PEPeel, i.e. intended to be peeled.
Les charges sont, de préférence, choisies parmi les charges minérales, notamment la silice, de préférence sous forme de bille ou fibre, le carbonate, notamment de type CaCO3 ou sous forme de talc, l’alumine ou le graphite. Comme mentionné plus haut, la présence des charges permet de réduire l’adhérence de la couche thermoscellée sur le contenant, facilitant son pelage.The fillers are preferably chosen from mineral fillers, in particular silica, preferably in the form of beads or fibers, carbonate, in particular of the CaCO3 type or in the form of talc, alumina or graphite. As mentioned above, the presence of fillers reduces the adhesion of the heat-sealed layer to the container, facilitating its peeling.
Le taux de charges dans le matériau polymère peut être inférieur ou égal à 5%, mieux inférieur ou égal à 3% et/ou supérieur ou égal à 1%, mieux supérieur ou égal à 1,5% en poids par rapport au poids total de la couche.The filler content in the polymer material may be less than or equal to 5%, better still less than or equal to 3% and/or greater than or equal to 1%, better still greater than or equal to 1.5% by weight relative to the total weight of the layer.
De préférence, la couche thermoscellable présente une épaisseur supérieure ou égale à 30 µm, mieux supérieure ou égale à 50 µm, encore mieux supérieure ou égale à 90 µm. Une telle épaisseur de la couche thermoscellable permet que cette dernière puisse bien s’écraser sur le bord du contenant lors du thermo-scellage, et ainsi facilite l’opération de soudure sur le contenant.Preferably, the heat-sealable layer has a thickness greater than or equal to 30 μm, better still greater than or equal to 50 μm, even better still greater than or equal to 90 μm. Such a thickness of the heat-sealable layer allows it to be crushed on the edge of the container during heat-sealing, and thus facilitates the welding operation on the container.
Agent d’adhésionMembership Officer
De préférence, le motif carboxylique est l'acide acrylique ou méthacrylique. Preferably, the carboxylic unit is acrylic or methacrylic acid.
De préférence, l'agent d'adhésion est un copolymère d'éthylène et d'acide acrylique.Preferably, the adhesion agent is a copolymer of ethylene and acrylic acid.
Couche métalliqueMetallic layer
De préférence, la couche métallique présente une épaisseur supérieure ou égale à 5 µm, de préférence supérieure ou égale à 8 µm, encore mieux supérieure ou égale à 9 µm et/ou inférieure ou égale à 30 µm, de préférence inférieure ou égale à 15 µm.Preferably, the metallic layer has a thickness greater than or equal to 5 μm, preferably greater than or equal to 8 μm, even better greater than or equal to 9 μm and/or less than or equal to 30 μm, preferably less than or equal to 15 µm.
La couche métallique est de préférence en aluminium ou en alliage d’aluminium, mais d’autres métaux peuvent être utilisés.The metal layer is preferably aluminum or an aluminum alloy, but other metals can be used.
De préférence, la couche métallique est en aluminium ayant un degré de pureté de 99,95 % à 97 % en poids, le reste étant les impuretés inévitables, ou en un d'alliage comportant de l’aluminium, tel que par exemple les alliages AIFe1.5Mn, AIFeSi ou AIFeSiMn, ayant respectivement une pureté supérieure à 97.5%, et de préférence supérieure à 98.5% en poids d'aluminium.Preferably, the metal layer is made of aluminum having a degree of purity of 99.95% to 97% by weight, the remainder being the unavoidable impurities, or of an alloy comprising aluminum, such as for example the alloys AIFe1.5Mn, AIFeSi or AIFeSiMn, respectively having a purity greater than 97.5%, and preferably greater than 98.5% by weight of aluminium.
La couche métallique peut présenter une adhérence améliorée pour l'agent d'adhésion grâce à un prétraitement tendant notamment à augmenter la tension superficielle de ses faces en contact avec l’agent d’adhésion, par exemple brossage, chromage, traitement d'ionisation, à l'ozone, couronne, à la flamme ou au plasma. The metallic layer may have improved adhesion for the adhesion agent thanks to a pretreatment tending in particular to increase the surface tension of its faces in contact with the adhesion agent, for example brushing, chromium plating, ionization treatment, ozone, corona, flame or plasma.
La couche métallique peut avoir été déposée par un procédé de métallisation, par exemple sous vide, sur une face d’une couche en matériau polymère, laquelle est laminée avec les autres couches du film à son contact.The metallic layer may have been deposited by a metallization process, for example under vacuum, on one face of a layer of polymer material, which is laminated with the other layers of the film in contact with it.
La couche métallique peut encore être une feuille métallique ayant sa propre cohésion lorsqu’elle est amenée au contact des autres couches du film.The metal layer can also be a metal sheet having its own cohesion when it is brought into contact with the other layers of the film.
Film soupleSoft film
De préférence, le film souple présente une extension débordant du contenant et permettant sa préhension pour le décoller manuellement du contenant. Par exemple, cette extension se présente sous la forme d’une languette.Preferably, the flexible film has an extension overflowing from the container and allowing it to be gripped in order to manually detach it from the container. For example, this extension comes in the form of a tab.
De préférence, le film souple est pelé en appliquant une force de traction comprise entre 5N et 30N, mieux entre 8N et 25N. Le film souple peut être pelé avec une force de traction inférieure ou égale à 10 N.Preferably, the flexible film is peeled off by applying a tensile force of between 5N and 30N, better still between 8N and 25N. The flexible film can be peeled off with a pulling force of 10 N or less.
Le film souple peut comporter une couche intermédiaire thermoplastique entre la couche métallique et la couche thermoscellable, l’agent d’adhésion étant au contact de la couche métallique et de cette couche intermédiaire. L’agencement des couches mentionnées ci-dessus peut donc être le suivant : couche métallique/agent d’adhésion/couche intermédiaire/couche thermoscellable.The flexible film may comprise a thermoplastic intermediate layer between the metallic layer and the heat-sealable layer, the adhesion agent being in contact with the metallic layer and this intermediate layer. The arrangement of the layers mentioned above can therefore be the following: metallic layer/bonding agent/intermediate layer/heat-sealable layer.
La couche intermédiaire peut être choisie dans la même liste (détaillée ci-dessus) de matériaux plastiques que la couche thermoscellable, étant dans le même matériau ou non que la couche thermoscellable. De préférence, la couche intermédiaire est dans le même matériau plastique que la couche thermoscellable ou dans un matériau ayant une affinité chimique avec le matériau de la couche thermoscellable. The intermediate layer can be chosen from the same list (detailed above) of plastic materials as the heat-sealable layer, being in the same material or not as the heat-sealable layer. Preferably, the intermediate layer is in the same plastic material as the heat-sealable layer or in a material having a chemical affinity with the material of the heat-sealable layer.
Le film souple peut comporter une couche de recouvrement recouvrant la couche métallique. La couche de recouvrement peut être en un matériau plastique, notamment choisie dans la même liste de matériau plastique que la couche thermoscellable, étant dans le même matériau ou non que la couche thermoscellable. De préférence, la couche de recouvrement est en polyéthylène téréphtalate, et peut contribuer à améliorer la résistance mécanique du film.The flexible film may include a cover layer covering the metal layer. The covering layer may be made of a plastic material, in particular chosen from the same list of plastic material as the heat-sealable layer, being made of the same material or not as the heat-sealable layer. Preferably, the covering layer is made of polyethylene terephthalate, and can contribute to improving the mechanical strength of the film.
De préférence, la couche de recouvrement présente une épaisseur comprise entre 5 µm et 50 µm, mieux entre 10 µm et 20µm.Preferably, the covering layer has a thickness comprised between 5 μm and 50 μm, better still between 10 μm and 20 μm.
Le film souple peut comporter au moins un agent d’adhésion additionnel, de préférence identique à l’agent d’adhésion décrit précédemment, entre la couche métallique et la couche de recouvrement et au contact de celles-ci.The flexible film may comprise at least one additional adhesion agent, preferably identical to the adhesion agent described above, between the metal layer and the covering layer and in contact with the latter.
L’agencement des couches peut donc être le suivant : couche de recouvrement/agent d’adhésion/couche métallique/agent d’adhésion/couche intermédiaire optionnelle/couche thermoscellable.The arrangement of the layers can therefore be the following: cover layer/adhesion agent/metallic layer/adhesion agent/optional intermediate layer/heat-sealable layer.
Dispositif de conditionnementConditioning device
L’invention a également pour objet, selon un autre de ses aspects, un dispositif de conditionnement comportant :The invention also relates, according to another of its aspects, to a packaging device comprising:
- un contenant rigide ou semi-rigide contenant un produit, notamment un produit liquide, une crème ou un gel,a rigid or semi-rigid container containing a product, in particular a liquid product, a cream or a gel,
- un opercule de fermeture tel que décrit ci-dessus, le film souple étant thermoscellé sur un bord du contenant.a closure lid as described above, the flexible film being heat sealed to one edge of the container.
ProduitProduct
De préférence, le produit est un produit cosmétique, notamment un produit de coloration ou décoloration des cheveux.Preferably, the product is a cosmetic product, in particular a hair coloring or bleaching product.
Le produit peut comporter un ou plusieurs colorants directs, des vitamines, un agent oxydant tel qu’un peroxyde et/ou un agent alcalinThe product may contain one or more direct dyes, vitamins, an oxidizing agent such as a peroxide and/or an alkaline agent
De préférence, le produit est une composition alcaline, notamment contenant un agent alcalinisant. En particulier, cet agent alcalinisant est choisi parmi l'ammoniaque et/ou l'éthanolamine et/ou le silicate de sodium et/ou les peroxydes.Preferably, the product is an alkaline composition, in particular containing an alkalizing agent. In particular, this basifying agent is chosen from aqueous ammonia and/or ethanolamine and/or sodium silicate and/or peroxides.
Par ailleurs, ladite composition peut contenir au moins une base d'oxydation.Furthermore, said composition may contain at least one oxidation base.
L'invention sera mieux comprise à la lecture de la description qui suit et à l'examen des figures qui l'accompagnent. Celles-ci ne sont présentées qu'à titre indicatif et nullement limitatif de l'invention.The invention will be better understood on reading the following description and on examining the accompanying figures. These are presented only as an indication and in no way limit the invention.
Description détailléedetailed description
On a illustré à la
- une couche métallique 4,a metal layer 4,
- un agent d'adhésion 6 comportant un copolymère comportant au moins 9.5% en poids de motifs carboxyliques par rapport au poids du copolymère, etan adhesion agent 6 comprising a copolymer comprising at least 9.5% by weight of carboxylic units relative to the weight of the copolymer, and
- une couche thermoscellable 8 en matière thermoplastique chargée, destinée à être scellée thermiquement sur le bord du contenant à fermer.a heat-sealable layer 8 of filled thermoplastic material, intended to be heat-sealed on the edge of the container to be closed.
La couche thermoscellable 8 est apte à être mise au contact du produit.The heat-sealable layer 8 is capable of being brought into contact with the product.
Le film souple 2 peut également comporter, comme cela est illustré, une couche de recouvrement extérieure 10, en matière plastique recouvrant la couche métallique 4. La couche de recouvrement 10 peut être liée à la couche métallique par un agent d’adhésion 6’, de préférence identique à l’agent d’adhésion 6 précédemment décrit.The flexible film 2 may also comprise, as shown, an outer covering layer 10, made of plastic covering the metallic layer 4. The covering layer 10 can be bonded to the metallic layer by an adhesion agent 6', preferably identical to the adhesion agent 6 previously described.
En variante, le deuxième agent d’adhésion 6’est différent du premier. Le deuxième agent d’adhésion peut être tout adhésif de laminage approprié.As a variant, the second adhesion agent 6′ is different from the first. The second adhesion agent can be any suitable laminating adhesive.
Des exemples d'adhésifs de laminage sont constitués par des adhésifs d'acrylate contenant des solvants, exempts de solvants ou aqueux ou par des systèmes polyuréthane-adhésif. On peut également utiliser des colles qui durcissent sous l'effet de rayonnements électromagnétiques (par exemple sous un rayonnement UV ou un faisceau d'électrons). On peut également réaliser cet adhésif de laminage 6’ à partir de di-isocyanate ou de polyesters aliphatiques, ou encore à partir de laques appropriées comme par exemple des laques à base d'acrylates, des résines époxy, des résines de mélanine, des résines d'urée, polyuréthanes, nitrate de cellulose, polyesters et leurs mélanges. Les laques peuvent être à base de solvant ou à base aqueuse ou être des systèmes à un, deux ou plusieurs composants. Les laques sont par exemple durcissables par séchage, à chaud, chimiquement et/ou par rayonnements (UV ; faisceaux d'électrons ; IR) avec de préférence la présence d’un agent réticulant pour accélérer le durcissement.Examples of laminating adhesives are solvent-containing, solvent-free or aqueous acrylate adhesives or polyurethane-adhesive systems. It is also possible to use adhesives which harden under the effect of electromagnetic radiation (for example under UV radiation or an electron beam). This laminating adhesive 6' can also be made from diisocyanate or aliphatic polyesters, or even from suitable lacquers such as, for example, lacquers based on acrylates, epoxy resins, melanin resins, resins urea, polyurethanes, cellulose nitrate, polyesters and their mixtures. Lacquers can be solvent-based or water-based or be one-, two-, or multi-component systems. Lacquers are, for example, hardenable by drying, hot, chemically and/or by radiation (UV; electron beams; IR) preferably with the presence of a crosslinking agent to accelerate hardening.
La couche de recouvrement 10 peut être réalisée à partir d’une ou plusieurs couches accolées entre elles de matériaux thermoplastiques tels que des matières plastiques vinyliques, par exemple à base de poly(chlorure de vinyle) (PVC), des polyesters, des matières plastiques polyoléfiniques, ou des polyamides. The cover layer 10 can be made from one or more layers joined together of thermoplastic materials such as vinyl plastic materials, for example based on poly(vinyl chloride) (PVC), polyesters, plastic materials polyolefins, or polyamides.
Des exemples de matières plastiques à base de polyesters pouvant convenir sont les polyalkylène-téréphtalates ou les polyalkylène-isophtalates ayant des groupes ou radicaux alkyle contenant de 2 à 10 atomes de carbone ou des groupes alkyle contenant de 2 à 10 atomes de C qui sont interrompus au moins par un -O-, comme par exemple le polyéthylène-téréphtalate (feuilles de PET), le polypropylène téréphtalate, le polybutylène-téréphtalate (polytétraméthylènetéréphtalate), le polydécaméthylène-téréphtalate, le poly-1,4-cyclohexyldiméthylol-téréphtalate ou le polyéthylène-2,6-naphtalènedicarboxylate ou les copolymères de polyalkylène-téréphtalate et polyalkylène-isophtalate, la proportion d'isophtalate étant par exemple de 1 à 10 % en mole, des copolymères et terpolymères, ainsi que des polymères séquences et des variantes greffées des substances susmentionnées. D'autres polyesters appropriés, tels que le polyéthylène naphtalate, sont connus dans le monde technique sous l'abréviation PEN. Examples of plastic materials based on polyesters which may be suitable are polyalkylene terephthalates or polyalkylene isophthalates having alkyl groups or radicals containing from 2 to 10 carbon atoms or alkyl groups containing from 2 to 10 C atoms which are interrupted at least by one -O-, such as for example polyethylene terephthalate (PET sheets), polypropylene terephthalate, polybutylene terephthalate (polytetramethylene terephthalate), polydecamethylene terephthalate, poly-1,4-cyclohexyldimethylol terephthalate or polyethylene-2,6-naphthalenedicarboxylate or copolymers of polyalkylene-terephthalate and polyalkylene-isophthalate, the proportion of isophthalate being for example 1 to 10% by mole, copolymers and terpolymers, as well as block polymers and graft variants of aforementioned substances. Other suitable polyesters, such as polyethylene naphthalate, are known in the technical world under the abbreviation PEN.
D'autres polyesters pouvant convenir sont des copolymères de l'acide téréphtalique et d'un autre acide polycarboxylique avec au moins un glycol. Sont appropriés les copolyesters de l'acide téréphtalique, d'éthylène glycol et d'un glycol supplémentaire. On préfère les polyesters glycol-modifiés qui sont connus du monde technique sous la dénomination PETG ou PETN. Other polyesters which may be suitable are copolymers of terephthalic acid and another polycarboxylic acid with at least one glycol. Suitable are copolyesters of terephthalic acid, ethylene glycol and an additional glycol. Glycol-modified polyesters which are known in the technical world under the name PETG or PETN are preferred.
Des polyesters appropriés sont constitués par les polyalkylène-téréphtalates ayant des groupes ou radicaux alkyle comprenant 2 à 10 atomes de carbone et les polyalkylène-téréphtalates ayant des groupes ou radicaux alkyle contenant 2 à 10 atomes de carbone qui sont interrompus par une ou deux liaisons -0-. Suitable polyesters consist of polyalkylene terephthalates having alkyl groups or radicals containing 2 to 10 carbon atoms and polyalkylene terephthalates having alkyl groups or radicals containing 2 to 10 carbon atoms which are interrupted by one or two bonds - 0-.
D'autres polyesters préférés sont les polyalkylène-téréphtalates ayant des groupes ou radicaux alkyle contenant 2 à 4 atomes de carbone et on préfère tout particulièrement les polyéthylène-téréphtalates. On compte parmi ces polyéthylène-téréphtalates également A-PET, PETP et le PETG cité ou le G-PET. Other preferred polyesters are polyalkylene terephthalates having alkyl groups or radicals containing 2 to 4 carbon atoms and polyethylene terephthalates are most preferred. These polyethylene terephthalates also include A-PET, PETP and the mentioned PETG or G-PET.
Les exemples de matières polyoléfiniques pouvant convenir sont les polyéthylènes (PE), par exemple polyéthylène haute densité (HDPE, densité supérieure à 0,944 g/cm3), polyéthylène de densité moyenne (MDPE, densité de 0,926 à 0,940 g/cm3), polyéthylène linéaire de densité moyenne (LMDPE, densité de 0,926 à 0,940 g/cm3), polyéthylène basse densité (LDPE, densité de 0,910 à 0,925 g/cm3) et polyéthylène linéaire basse densité (LLDPE, densité de 0,916 à 0,925 g/cm3), par exemple sous forme de feuilles non orientées (feuille de PE) ou orientées monoaxialement ou biaxialement (feuille de oPE), des polypropylènes (PP), tels que polypropylène orienté axialement ou biaxialement (feuille de oPP) ou polypropylène coulé (feuille de cPP), polypropylène amorphe ou cristallin ou leurs mélanges ou polypropylène atactique ou isotactique ou leurs mélanges, poly-1-butène, poly-3-méthybutène, poly-4-méthylpentène et leurs copolymères, puis polyéthylène avec acétate de vinyle, alcool vinylique, acide acrylique, tels que par exemple, des résines ionomères, comme des copolymères d'éthylène d'acide acrylique, d'acide méthacrylique, d'esters acryliques, tétrafluoroéthylène ou polypropylène, en outre copolymères statistiques, copolymères séquences ou mélanges polymère d'oléfine-élastomère. Les matériaux polyoléfiniques peuvent également comporter des cyclo-oléfines en tant que monomère d'un homopolymère ou de copolymères. Examples of polyolefinic materials which may be suitable are polyethylenes (PE), for example high density polyethylene (HDPE, density greater than 0.944 g/cm3), medium density polyethylene (MDPE, density of 0.926 to 0.940 g/cm3), linear polyethylene medium density (LMDPE, density 0.926 to 0.940 g/cm3), low density polyethylene (LDPE, density 0.910 to 0.925 g/cm3) and linear low density polyethylene (LLDPE, density 0.916 to 0.925 g/cm3), for example in the form of non-oriented sheets (PE sheet) or monoaxially or biaxially oriented (oPE sheet), polypropylenes (PP), such as axially or biaxially oriented polypropylene (oPP sheet) or cast polypropylene (cPP sheet), amorphous or crystalline polypropylene or their mixtures or atactic or isotactic polypropylene or their mixtures, poly-1-butene, poly-3-methylbutene, poly-4-methylpentene and their copolymers, then polyethylene with vinyl acetate, vinyl alcohol, acryl acid ic, such as for example ionomer resins, such as ethylene copolymers of acrylic acid, methacrylic acid, acrylic esters, tetrafluoroethylene or polypropylene, furthermore random copolymers, block copolymers or polymer mixtures of olefin- elastomer. Polyolefin materials can also include cyclo-olefins as a monomer of homopolymer or copolymers.
On préfère l’éthylène acide acétique.Ethylene acetic acid is preferred.
Les exemples de polyamides (PA) pouvant convenir sont le polyamide 6, homopolymère de ε-caprolactame (polycaprolactame) ; le polyamide 11, le polyamide 12, homopolymère de w-laurine-lactame (polylaurinelactame) ; le polyamide 6,6, homopolycondensat d'hexaméthylènediamine et d'acide adipique (polyhexaméthylèneadipamide) ; le polyamide 6,10, homopolycondensat d'hexaméthylènediamide et d'acide sébacique (polyhexaméthylènesébacamide) ; le polyamide 6,12, homopolycondensat d'hexaméthylènediamide et de diacide dodécanoïque (polyhexaméthylènedodécanamide) ou le polyamide 6-3-T, homopolycondensat de triméthylhexaméthylènediamide et d'acide téréphtalique (polytriméthylhexaméthylènetéréphtalamide), ainsi que leurs mélanges. Les couches en polyamide peuvent être étirées monoaxialement ou biaxialement (oPA). Examples of suitable polyamides (PA) are polyamide 6, homopolymer of ε-caprolactam (polycaprolactam); polyamide 11, polyamide 12, homopolymer of w-laurine-lactam (polylaurinelactam); polyamide 6,6, homopolycondensate of hexamethylenediamine and adipic acid (polyhexamethyleneadipamide); polyamide 6.10, homopolycondensate of hexamethylenediamide and sebacic acid (polyhexamethylenesebacamide); polyamide 6,12, homopolycondensate of hexamethylenediamide and dodecanoic diacid (polyhexamethylenedodecanamide) or polyamide 6-3-T, homopolycondensate of trimethylhexamethylenediamide and terephthalic acid (polytrimethylhexamethyleneterephthalamide), as well as mixtures thereof. Polyamide layers can be stretched monoaxially or biaxially (oPA).
La couche de recouvrement 10 est de préférence constituée de polyalkylène téréphtalate par exemple du polyéthylène téréphtalate de manière à améliorer la résistance aux chocs du film 1, notamment améliorer la résistance aux chocs. The cover layer 10 is preferably made of polyalkylene terephthalate, for example polyethylene terephthalate, so as to improve the impact resistance of the film 1, in particular to improve the impact resistance.
La couche de recouvrement 10 peut présenter une épaisseuracomprise entre 8 µm et 25 µm, de préférence entre 10 µm et 15 µm.Cover layer 10 may have a thickness a of between 8 μm and 25 μm, preferably between 10 μm and 15 μm.
Le film souple peut également comporter entre la couche métallique 4 et la couche thermoscellable 8, une couche intermédiaire thermoplastique 7. Cette dernière peut être reliée à la couche métallique par l’agent d’adhésion 6. Elle peut présenter une épaisseurecomprise entre 5 et 25 µm, par exemple sensiblement égale à 12 µm. The flexible film may also comprise, between the metallic layer 4 and the heat-sealable layer 8, a thermoplastic intermediate layer 7. The latter may be connected to the metallic layer by the adhesion agent 6. It may have a thickness e of between 5 and 25 μm, for example substantially equal to 12 μm.
Dans l’exemple illustré, le film souple se présente avec la structure suivante : couche de recouvrement 10/agent d’adhésion 6’/couche métallique 4/agent d’adhésion 6/couche intermédiaire 7/couche thermoscellable 8.In the example illustrated, the flexible film has the following structure: cover layer 10/adhesive agent 6'/metallic layer 4/adhesive agent 6/intermediate layer 7/heat-sealable layer 8.
La couche intermédiaire 7 est de préférence en matière thermoplastique choisie parmi les polyoléfines, comme par exemple le polyéthylène ou le polypropylène, les polyalkylène-téréphtalates ou les polyalkylène-isophtalates ayant des groupes ou radicaux alkyle contenant de 2 à 10 atomes de carbone ou des groupes alkyle contenant de 2 à 10 atomes de C qui sont interrompus au moins par un -O-, comme par exemple le polyéthylène-téréphtalate (feuilles de PET), le polypropylène téréphtalate, le polybutylène-téréphtalate (polytétraméthylènetéréphtalate), le polydécaméthylène-téréphtalate, le poly-1,4-cyclohexyldiméthylol-téréphtalate ou le polyéthylène-2,6-naphtalènedicarboxylate ou les copolymères de polyalkylène-téréphtalate et polyalkylène-isophtalate, la proportion d'isophtalate étant par exemple de 1 à 10 % en mole, des copolymères et terpolymères, ainsi que des polymères séquences et des variantes greffées des substances susmentionnées. Des matières thermoplastiques appropriées sont constituées par les polyalkylène-téréphtalates ayant des groupes ou radicaux alkyle comprenant 2 à 10 atomes de carbone tel que les polyéthylène-téréphtalates. On compte parmi ces polyéthylène-téréphtalates également A-PET, PETP et le PETG cité ou le G-PET. Les exemples de matières polyoléfiniques pouvant convenir sont les polyéthylènes haute densité (HDPE, densité supérieure à 0,944 g/cm3), polyéthylène de densité moyenne (MDPE, densité de 0,926 à 0,940 g/cm3), polyéthylène linéaire de densité moyenne (LMDPE, densité de 0,926 à 0,940 g/cm3), polyéthylène basse densité (LDPE, densité de 0,910 à 0,925 g/cm3) et polyéthylène linéaire basse densité (LLDPE, densité de 0,916 à 0,925 g/cm3), par exemple sous forme de feuilles non orientées (feuille de PE) ou orientées monoaxialement ou biaxialement (feuille de oPE), des polypropylènes (PP), tels que polypropylène orienté axialement ou biaxialement (feuille de oPP) ou polypropylène coulé (feuille de cPP), polypropylène amorphe ou cristallin ou leurs mélanges ou polypropylène atactique ou isotactique ou leurs mélanges, poly-1-butène, poly-3-méthybutène, poly-4-méthylpentène et leurs copolymères, puis polyéthylène avec acétate de vinyle, alcool vinylique, acide acrylique, tels que par exemple, des résines ionomères, comme des copolymères d'éthylène d'acide acrylique, d'acide méthacrylique, d'esters acryliques, tétrafluoroéthylène ou polypropylène, en outre copolymères statistiques, copolymères séquences ou mélanges polymère d'oléfine-élastomère. Les matériaux polyoléfiniques peuvent également comporter des cyclo-oléfines en tant que monomère d'un homopolymère ou de copolymères. The intermediate layer 7 is preferably made of thermoplastic material chosen from polyolefins, such as for example polyethylene or polypropylene, polyalkylene-terephthalates or polyalkylene-isophthalates having groups or alkyl radicals containing from 2 to 10 carbon atoms or groups alkyl containing from 2 to 10 C atoms which are interrupted by at least one -O-, such as for example polyethylene terephthalate (PET sheets), polypropylene terephthalate, polybutylene terephthalate (polytetramethylene terephthalate), polydecamethylene terephthalate, poly-1,4-cyclohexyldimethylol-terephthalate or polyethylene-2,6-naphthalenedicarboxylate or copolymers of polyalkylene-terephthalate and polyalkylene-isophthalate, the proportion of isophthalate being for example from 1 to 10% by mole, copolymers and terpolymers, as well as block polymers and graft variants of the aforementioned substances. Appropriate thermoplastic materials consist of polyalkylene terephthalates having alkyl groups or radicals comprising 2 to 10 carbon atoms, such as polyethylene terephthalates. These polyethylene terephthalates also include A-PET, PETP and the mentioned PETG or G-PET. Examples of polyolefinic materials which may be suitable are high density polyethylene (HDPE, density greater than 0.944 g/cm3), medium density polyethylene (MDPE, density of 0.926 to 0.940 g/cm3), linear medium density polyethylene (LMDPE, density from 0.926 to 0.940 g/cm3), low density polyethylene (LDPE, density from 0.910 to 0.925 g/cm3) and linear low density polyethylene (LLDPE, density from 0.916 to 0.925 g/cm3), for example in the form of non-oriented sheets (PE sheet) or monoaxially or biaxially oriented (oPE sheet), polypropylenes (PP), such as axially or biaxially oriented polypropylene (oPP sheet) or cast polypropylene (cPP sheet), amorphous or crystalline polypropylene or mixtures thereof or atactic or isotactic polypropylene or mixtures thereof, poly-1-butene, poly-3-methylbutene, poly-4-methylpentene and their copolymers, then polyethylene with vinyl acetate, vinyl alcohol, acrylic acid, such as, for example, ionomeric resins, such as ethylene copolymers of acrylic acid, methacrylic acid, acrylic esters, tetrafluoroethylene or polypropylene, further random copolymers, block copolymers or olefin polymer-elastomer blends. Polyolefin materials can also include cyclo-olefins as a monomer of homopolymer or copolymers.
La couche métallique 4 selon l'invention peut être une feuille métallique en fer, acier, nickel, cuivre, étain, bronze, laiton, aluminium ou leurs alliages. Avantageusement, la feuille métallique 4 est en aluminium ayant un degré de pureté de 99,95 % à 97 % en poids, le reste étant les impuretés inévitables ou des éléments d'alliage. Des exemples d'alliages sont ceux ayant comme composant principal l'aluminium et comme éléments d'alliage Fe ; Si ; Mg ; Mn ; Ti et/ou Cu, comme par exemple les alliages AIFe1.5Mn, AIFeSi ou AIFeSiMn, ayant respectivement une pureté supérieure à 97.5%, et de préférence supérieure à 98.5% en poids d'aluminium.The metal layer 4 according to the invention can be a metal sheet made of iron, steel, nickel, copper, tin, bronze, brass, aluminum or their alloys. Advantageously, the metal sheet 4 is made of aluminum having a degree of purity of 99.95% to 97% by weight, the remainder being the unavoidable impurities or alloying elements. Examples of alloys are those having as main component aluminum and as alloying elements Fe; Whether ; mg; Mn; Ti and/or Cu, such as for example the AlFe1.5Mn, AlFeSi or AlFeSiMn alloys, having respectively a purity greater than 97.5%, and preferably greater than 98.5% by weight of aluminium.
De préférence, la couche métallique 4 est réalisée à partir d'aluminium, et présente une épaisseurbcomprise entre 5 et 30 µm, de préférence de l'ordre de 12 µm.Preferably, the metal layer 4 is made from aluminum, and has a thicknessbbetween 5 and 30 μm, preferably of the order of 12 μm.
Les faces 12 et 14 de la couche métallique 4 peuvent présenter une adhérence améliorée pour l'agent d'adhésion grâce à un prétraitement tendant notamment à augmenter la tension superficielle de ces faces 12 et 14, par exemple brossage, chromage, traitement d'ionisation, à l'ozone, couronne, à la flamme ou au plasma. The faces 12 and 14 of the metal layer 4 can have improved adhesion for the adhesion agent thanks to a pretreatment tending in particular to increase the surface tension of these faces 12 and 14, for example brushing, chrome plating, ionization treatment , ozone, corona, flame or plasma.
L’agent d’adhésion 6 est un copolymère qui comprend au moins un premier monomère carboxylique selon le motif suivant
(-CH2-CR3COOR2-)m
R3= H ou CH3,
R2= H ou groupe alkyle non substitué, linéaire ou ramifié, tel qu'un groupe méthyle, éthyle, propyle ou isobutyle ou R2représente un groupe cycloalkyle C4à C1,
et m étant choisi de telle sorte que ce premier monomère représente entre plus de 9,5% en poids du copolymère. The adhesion agent 6 is a copolymer which comprises at least a first carboxylic monomer according to the following pattern
(-CH 2 -CR 3 COOR 2 -) m
R 3 = H or CH 3 ,
R 2 = H or an unsubstituted, linear or branched alkyl group, such as a methyl, ethyl, propyl or isobutyl group or R 2 represents a C 4 to C 1 cycloalkyl group,
and m being chosen such that this first monomer represents more than 9.5% by weight of the copolymer.
En particulier ce copolymère comprend au moins un second monomère de motif alkylénique contenant de 1 à 10 atomes de carbone, et en particulier présentant un motif éthylénique selon la formule suivante :
(-CH2 -CH2 -)n
n étant choisi de telle sorte que ce second monomère représente entre 71 et 92% en poids du copolymère. In particular, this copolymer comprises at least one second monomer with an alkylene unit containing from 1 to 10 carbon atoms, and in particular having an ethylenic unit according to the following formula:
(-CH2 -CH2 -) n
n being chosen such that this second monomer represents between 71 and 92% by weight of the copolymer.
De préférence, le copolymère formant l’agent adhésif 6 est un copolymère d'éthylène et d’acide acrylique comportant 9,5% en poids d'acide acrylique.Preferably, the copolymer forming the adhesive agent 6 is a copolymer of ethylene and acrylic acid comprising 9.5% by weight of acrylic acid.
L’agent adhésif 6 peut avoir une épaisseurcinférieure ou égale à 10 µm, mieux inférieure ou égale à 5 µm.The adhesive agent 6 may have a thickness c less than or equal to 10 μm, better still less than or equal to 5 μm.
La couche thermoscellable 8 est de préférence en une matière thermoplastique chargée.The heat-sealable layer 8 is preferably made of a filled thermoplastic material.
Ladite matière thermoplastique peut être choisie parmi les polyoléfines, comme par exemple le polyéthylène ou le polypropylène, les polyalkylène-téréphtalates ou les polyalkylène-isophtalates ayant des groupes ou radicaux alkyle contenant de 2 à 10 atomes de carbone ou des groupes alkyle contenant de 2 à 10 atomes de C qui sont interrompus au moins par un -O-, comme par exemple le polyéthylène-téréphtalate (feuilles de PET), le polypropylène téréphtalate, le polybutylène-téréphtalate (polytétraméthylènetéréphtalate), le polydécaméthylène-téréphtalate, le poly-1,4-cyclohexyldiméthylol-téréphtalate ou le polyéthylène-2,6-naphtalènedicarboxylate ou les copolymères de polyalkylène-téréphtalate et polyalkylène-isophtalate, la proportion d'isophtalate étant par exemple de 1 à 10 % en mole, des copolymères et terpolymères, ainsi que des polymères séquences et des variantes greffées des substances susmentionnées. Des matières thermoplastiques appropriés sont constitués par les polyalkylène-téréphtalates ayant des groupes ou radicaux alkyle comprenant 2 à 10 atomes de carbone tel que les polyéthylène-téréphtalates. On compte parmi ces polyéthylène-téréphtalates également A-PET, PETP et le PETG cité ou le G-PET. Les exemples de matières polyoléfiniques sont les polyéthylènes haute densité (HDPE, densité supérieure à 0,944 g/cm3), polyéthylène de densité moyenne (MDPE, densité de 0,926 à 0,940 g/cm3), polyéthylène linéaire de densité moyenne (LMDPE, densité de 0,926 à 0,940 g/cm3), polyéthylène basse densité (LDPE, densité de 0,910 à 0,925 g/cm3) et polyéthylène linéaire basse densité (LLDPE, densité de 0,916 à 0,925 g/cm3), par exemple sous forme de feuilles non orientées (feuille de PE) ou orientées monoaxialement ou biaxialement (feuille de oPE), des polypropylènes (PP), tels que polypropylène orienté axialement ou biaxialement (feuille de oPP) ou polypropylène coulé (feuille de cPP), polypropylène amorphe ou cristallin ou leurs mélanges ou polypropylène atactique ou isotactique ou leurs mélanges, poly-1-butène, poly-3-méthybutène, poly-4-méthylpentène et leurs copolymères, puis polyéthylène avec acétate de vinyle, alcool vinylique, acide acrylique, tels que par exemple, des résines ionomères, comme des copolymères d'éthylène d'acide acrylique, d'acide méthacrylique, d'esters acryliques, tétrafluoroéthylène ou polypropylène, en outre copolymères statistiques, copolymères séquences ou mélanges polymère d'oléfine-élastomère. Les matériaux polyoléfiniques peuvent également comporter des cyclo-oléfines en tant que monomère d'un homopolymère ou de copolymères. Said thermoplastic material can be chosen from polyolefins, such as for example polyethylene or polypropylene, polyalkylene terephthalates or polyalkylene isophthalates having alkyl groups or radicals containing from 2 to 10 carbon atoms or alkyl groups containing from 2 to 10 C atoms which are interrupted by at least one -O-, such as polyethylene terephthalate (PET sheets), polypropylene terephthalate, polybutylene terephthalate (polytetramethylene terephthalate), polydecamethylene terephthalate, poly-1, 4-cyclohexyldimethylol-terephthalate or polyethylene-2,6-naphthalenedicarboxylate or polyalkylene-terephthalate and polyalkylene-isophthalate copolymers, the proportion of isophthalate being for example 1 to 10 mol%, copolymers and terpolymers, as well as block polymers and grafted variants of the aforementioned substances. Appropriate thermoplastic materials consist of polyalkylene terephthalates having alkyl groups or radicals comprising 2 to 10 carbon atoms, such as polyethylene terephthalates. These polyethylene terephthalates also include A-PET, PETP and the mentioned PETG or G-PET. Examples of polyolefin materials are high density polyethylene (HDPE, density greater than 0.944 g/cm3), medium density polyethylene (MDPE, density 0.926 to 0.940 g/cm3), linear medium density polyethylene (LMDPE, density 0.926 to 0.940 g/cm3), low density polyethylene (LDPE, density of 0.910 to 0.925 g/cm3) and linear low density polyethylene (LLDPE, density of 0.916 to 0.925 g/cm3), for example in the form of non-oriented sheets (sheet of PE) or monoaxially or biaxially oriented (oPE sheet), polypropylenes (PP), such as axially or biaxially oriented polypropylene (oPP sheet) or cast polypropylene (cPP sheet), amorphous or crystalline polypropylene or mixtures thereof or polypropylene atactic or isotactic or their mixtures, poly-1-butene, poly-3-methylbutene, poly-4-methylpentene and their copolymers, then polyethylene with vinyl acetate, vinyl alcohol, acrylic acid, such as for example ionomer resins s, such as ethylene copolymers of acrylic acid, methacrylic acid, acrylic esters, tetrafluoroethylene or polypropylene, further random copolymers, block copolymers or olefin polymer-elastomer blends. Polyolefin materials can also include cyclo-olefins as a monomer of homopolymer or copolymers.
De préférence, la couche thermoscellable est une couche de polyéthylène chargé, connu sous la dénomination PEPeel.Preferably, the heat-sealable layer is a layer of filled polyethylene, known under the name PEPeel.
La matière thermoplastique de la couche thermoscellable 8 comporte en tant que charges, de préférence, des charges minérales.The thermoplastic material of the heat-sealable layer 8 comprises, as fillers, preferably mineral fillers.
Les charges minérales peuvent être de la silice, de préférence sous forme de bille ou fibre, le carbonate, notamment de type CaCO3 ou sous forme de talc, l’alumine ou le graphite, ou un mélange des charges ci-dessus.The mineral fillers can be silica, preferably in the form of beads or fibers, carbonate, in particular of the CaCO3 type or in the form of talc, alumina or graphite, or a mixture of the above fillers.
De préférence, le pourcentage en poids de charges minérales dans la couche thermoscellable 8 est inférieur ou égal à 5%, mieux inférieur ou égal à 3% et/ou supérieur ou égal à 1%, mieux supérieur ou égal à 1,5% en poids par rapport au poids total de la couche Preferably, the percentage by weight of mineral fillers in the heat-sealable layer 8 is less than or equal to 5%, better still less than or equal to 3% and/or greater than or equal to 1%, better still greater than or equal to 1.5% by weight relative to the total weight of the layer
De préférence, la couche thermoscellable 8 est une couche de polyéthylène chargé en silice. Elle présente, de préférence une épaisseurdsupérieure ou égale à 30 µm, mieux supérieure ou égale à 50 µm, encore mieux supérieure ou égale à 90 µm.. Preferably, the heat-sealable layer 8 is a layer of silica-filled polyethylene. It preferably has a thickness d greater than or equal to 30 μm, better still greater than or equal to 50 μm, even better still greater than or equal to 90 μm.
Les couches 4, 6, 6’, 8 et 10 peuvent être transparentes, translucides ou opaques et peuvent être colorées partiellement ou totalement.Layers 4, 6, 6', 8 and 10 can be transparent, translucent or opaque and can be partially or totally colored.
La face extérieure 15 du film souple 2, peut être recouverte par un motif imprimé, lui-même éventuellement recouvert par une laque. On peut également doter la face extérieure 15 d'une laque, cette laque pouvant être selon le cas également imprimée et/ou susceptible d'être imprimée sur les installations d'emballage, par exemple au moyen de rayons UV, de solvants ou de faisceaux lasers ou d'électrons. The outer face 15 of the flexible film 2 can be covered with a printed pattern, itself optionally covered with a lacquer. It is also possible to provide the outer face 15 with a lacquer, this lacquer possibly also being printed and/or capable of being printed on the packaging installations, for example by means of UV rays, solvents or lasers or electrons.
De préférence, le film souple 2 est obtenu par laminage des couches les unes sur les autres.Preferably, the flexible film 2 is obtained by laminating the layers on top of each other.
De préférence, le film souple 2 est utilisé pour participer au conditionnement de produits cosmétiques tels que des compositions de coloration des fibres kératiniques, notamment les compositions pour la coloration d'oxydation contenant un agent alcalin.Preferably, the flexible film 2 is used to take part in the packaging of cosmetic products such as compositions for dyeing keratin fibres, in particular compositions for dyeing oxidation containing an alkaline agent.
Le contenant 20 peut être réalisé dans un matériau rigide ou semi-rigide thermoformé ou injecté ou mis en forme autrement. De préférence, le film souple 2 est scellé à un rebord 22 du contenant 20, délimitant une ouverture dudit logement obturée par ledit film souple 2.The container 20 can be made of a rigid or semi-rigid material that is thermoformed or injected or otherwise shaped. Preferably, the flexible film 2 is sealed to a rim 22 of the container 20, delimiting an opening of said housing closed by said flexible film 2.
L'ouverture de l’opercule s’effectue par décollement du film souple 2. A cet effet, le film souple 2 peut comporter une extension préhensible 24 tel qu’une languette par exemple. L’utilisateur peut alors saisir cette extension 24 pour décoller le film souple du contenant en exerçant une force de traction perpendiculairement au plan d’extension du film souple 2 et ainsi ouvrir le contenant. The lid is opened by peeling off the flexible film 2. For this purpose, the flexible film 2 may include a grippable extension 24 such as a tab for example. The user can then grasp this extension 24 to detach the flexible film from the container by exerting a traction force perpendicular to the plane of extension of the flexible film 2 and thus open the container.
Le dispositif peut servir de recharge à un boîtier ou de contenant unidose. The device can be used as a refill for a box or as a single-dose container.
ExemplesExamples
Les films souples comportant les couches successives suivantes ont été scellés sur un même contenant comportant une composition de coloration liquide :The flexible films comprising the following successive layers were sealed on the same container comprising a liquid coloring composition:
- (Exemple comparatif) Laque (1 µm)/feuille d’aluminium (38 µm)/Colle (3µm)/Polyéthylène (12 µm)/Laque thermocollante (4.5 µm),(Comparative example) Lacquer (1 µm)/aluminum foil (38 µm)/Glue (3µm)/Polyethylene (12 µm)/Hot-melt lacquer (4.5 µm),
- (Exemple selon l’invention) Polyéthylène téréphtalate (12 µm)/Copolymère d'éthylène et d'acide acrylique à 9,5% en poids d’acide acrylique dans le copolymère (5 µm)/feuille d’aluminium (12 µm)/Polyéthylène (12 µm)/PEPeel comportant 2% de charges en poids (50 µm). (Example according to the invention) Polyethylene terephthalate (12 μm)/Copolymer of ethylene and acrylic acid with 9.5% by weight of acrylic acid in the copolymer (5 μm)/aluminum foil (12 μm) /Polyethylene (12 µm)/PEPeel with 2% fillers by weight (50 µm).
Les contenants scellés ont subi un test de vieillissement accéléré par chauffage à 45°C.Sealed containers have undergone an accelerated aging test by heating to 45°C.
Après vieillissement, la composition de coloration contenue dans le contenant scellé avec le film souple A présente une odeur, une couleur et un aspect inchangés. Néanmoins, le film souple s’est partiellement détaché et s’est délaminé et le taux en alcalin de la composition par rapport à celui de la composition initiale est très faible. La composition s’est donc détériorée durant le vieillissement prématuré, démontrant une mauvaise conservation de la composition cosmétique dans ce contenant au cours du temps. After ageing, the coloring composition contained in the container sealed with the flexible film A has an unchanged smell, color and appearance. Nevertheless, the flexible film has partially detached and delaminated and the alkaline content of the composition compared to that of the initial composition is very low. The composition therefore deteriorated during premature aging, demonstrating poor conservation of the cosmetic composition in this container over time.
Après vieillissement, la composition de coloration contenue dans le contenant scellé avec le film souple B présente une odeur, une couleur, un aspect et un taux d’alcalins inchangés. Le film souple ne présente pas de délamination, ni de décollement. La composition cosmétique est donc conservée efficacement au cours du temps dans ce contenant. After aging, the coloring composition contained in the container sealed with the flexible film B has an unchanged odor, color, appearance and alkali content. The flexible film shows no delamination or detachment. The cosmetic composition is therefore effectively preserved over time in this container.
L’invention n’est pas limitée aux exemples décrit ci-dessus.The invention is not limited to the examples described above.
Par exemple, le film plastique peut être dépourvu de couche de recouvrement ou de couche intermédiaire.For example, the plastic film may have no covering layer or intermediate layer.
Claims (10)
- une couche thermoscellable (8) en matière thermoplastique chargée, thermoscellée sur le contenant (20), ayant une adhésion sur le contenant (20) réduite du fait de la présence d’une charge au sein de cette couche, de façon à rendre le film souple (2) pelable manuellement,
- au moins une couche métallique (4) recouvrant la couche thermoscellable (8), et
- au moins un agent d’adhésion (6) à base acrylique entre la couche métallique (4) et la couche thermoscellable (8), cet agent d’adhésion (6) comportant un copolymère comportant au moins 9.5% en poids de motifs carboxyliques par rapport au poids du copolymère.
- a heat-sealable layer (8) of filled thermoplastic material, heat-sealed onto the container (20), having reduced adhesion to the container (20) due to the presence of a filler within this layer, so as to make the film flexible (2) manually peelable,
- at least one metallic layer (4) covering the heat-sealable layer (8), and
- at least one acrylic-based adhesion agent (6) between the metallic layer (4) and the heat-sealable layer (8), this adhesion agent (6) comprising a copolymer comprising at least 9.5% by weight of carboxylic units per relative to the weight of the copolymer.
- un contenant (20) rigide ou semi-rigide contenant un produit, notamment un produit liquide, une crème ou un gel.
- un opercule de fermeture tel que défini dans l’une quelconque des revendications précédentes, le film souple (2) étant thermoscellé sur un bord (22) du contenant (20).
- a rigid or semi-rigid container (20) containing a product, in particular a liquid product, a cream or a gel.
- a closure lid as defined in any one of the preceding claims, the flexible film (2) being heat sealed to an edge (22) of the container (20).