FR2678294A1 - Process for improving the abrasion resistance of synthetic monofilaments, and monofilaments obtained especially by this process, such as fishing lines - Google Patents
Process for improving the abrasion resistance of synthetic monofilaments, and monofilaments obtained especially by this process, such as fishing lines Download PDFInfo
- Publication number
- FR2678294A1 FR2678294A1 FR9108184A FR9108184A FR2678294A1 FR 2678294 A1 FR2678294 A1 FR 2678294A1 FR 9108184 A FR9108184 A FR 9108184A FR 9108184 A FR9108184 A FR 9108184A FR 2678294 A1 FR2678294 A1 FR 2678294A1
- Authority
- FR
- France
- Prior art keywords
- monofilaments
- abrasion resistance
- silicone oils
- synthetic
- fishing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
La présente demande concerne un procédé pour l'amélioration de la résistance à l'abrasion et de l'aptitude au lancer des fils de pêche ainsi que les fils issus de ce procédé. The present application relates to a process for improving the abrasion resistance and the ability to cast fishing lines as well as the wires resulting from this process.
Dans la pêche au lancer à grande distance, notamment pour la pêche de la carpe en étang et en rivière et pour la pêche en mer du bord de la plage les pêcheurs ont besoin de fils présentant des propriétés particulières :
- résistance à l'abrasion dans les anneaux de la canne, dans les
oeillets métalliques des hameçons, des leurres et des
émerillons,
- résistance à l'échauffement dans les anneaux de la canne,
- faciliter la confection des noeuds de pêche en évitant
l'échauffement du fil au moment du serrage, et assurer un bon
remplissage du moulinet.In long-distance casting fishing, especially for carp fishing in ponds and rivers and for sea fishing at the edge of the beach, fishermen need threads with special properties:
- abrasion resistance in the cane rings, in the
metal eyelets for hooks, lures and
swivels,
- resistance to heating in the rod rings,
- facilitate the making of fishing knots by avoiding
heating of the wire when tightening, and ensuring good
filling the reel.
Dans d'autres techniques de pêche, plus classiques, les pêcheurs recherchent également des fils présentant
- une bonne résistance à l'échauffement lors du déplacement des
plombs sur la ligne,
- une bonne aptitude au lancer dans les pêches au lancer (telles
que pêche au brochet, à la perche ...).In other, more conventional fishing techniques, fishermen also look for threads with
- good resistance to overheating when moving
sinkers on the line,
- a good ability to cast in casting fisheries (such
as pike fishing, perch fishing ...).
Enfin dans toutes les compétitions de lancer sur herbe, en distance et en précision, les sportifs recherchent également les mêmes propriétés. Finally in all competitions to launch on grass, in distance and in precision, the sportsmen also seek the same properties.
Il est connu qu'en ajoutant, à la surface des fils, de l'huile silicone non réactive, on améliore la résistance à l'abrasion, on améliore "la glisse" et on réduit notablement l'échauffement des fils au cours du serrage des noeuds. It is known that by adding non-reactive silicone oil to the surface of the wires, the abrasion resistance is improved, the "sliding" is improved and the heating of the wires is considerably reduced during tightening. some knots.
Malheureusement, cette huile n'est pas fixée sur le fil et elle s'élimine rapidement dans l'eau ou sur les anneaux de la canne par frottement. Unfortunately, this oil is not fixed on the wire and it is quickly eliminated in water or on the cane rings by friction.
Il est donc intéressant de mettre au point un traitement appelé "VS" dans la suite de la demande, qui soit non éliminable dans l'eau et qui apporte les propriétés indiquées ci-dessus de façon permanente. It is therefore interesting to develop a treatment called "VS" in the rest of the application, which is not eliminable in water and which provides the properties indicated above permanently.
La présente invention a pour objet un procédé pour l'amélioration permanente de la résistance à l'abrasion et de l'aptitude au lancer des fils de pêche en monofilaments synthétiques caractérisé en ce que, au cours de la fabrication des monofilaments, on dépose sur les fils des huiles silicones réactives, polymérisées ensuite par traitement thermique au cours de la fabrication du monofilament, cette polymérisation étant accélérée par l'addition d'une émulsion catalysante. The subject of the present invention is a process for the permanent improvement of the abrasion resistance and the ability to cast fishing lines made of synthetic monofilaments, characterized in that, during the manufacture of the monofilaments, the son of reactive silicone oils, then polymerized by heat treatment during the manufacture of the monofilament, this polymerization being accelerated by the addition of a catalyzing emulsion.
La présente demande concerne aussi les fils issus de ce procédé. The present application also relates to the threads resulting from this process.
Les huiles réactives sont déposées au taux d'environ 0,1 à 5 %, de préférence supérieure à 0,15 % et polymérisées par traitement thermique au cours de la production du monofilament, cette polymérisation est accélérée en ajoutant dans l'émulsion aqueuse des huiles réactives, une émulsion catalysante à un taux compris entre 5 et 50 %, de préférence de 10 à 20 % des huiles réactives. The reactive oils are deposited at a rate of approximately 0.1 to 5%, preferably greater than 0.15% and polymerized by heat treatment during the production of the monofilament, this polymerization is accelerated by adding to the aqueous emulsion reactive oils, a catalyzing emulsion at a rate of between 5 and 50%, preferably 10 to 20% of the reactive oils.
Comme huile réactive on utilisera de préférence les huiles silicones sous forme d'émulsion capables de réagir avec le composant synthétique constituant les monofilaments afin de former un gainage permanent, par opposition aux huiles non réactives dont la pellicule formée par dépôt est fugace ainsi qu'expliquée précédemment. L'émulsion catalysante est constituée de préférence de résines époxy condensée sur une amine. As reactive oil, use will preferably be made of silicone oils in the form of an emulsion capable of reacting with the synthetic component constituting the monofilaments in order to form a permanent cladding, in contrast to non-reactive oils whose film formed by deposition is fleeting as explained. previously. The catalyzing emulsion preferably consists of epoxy resins condensed on an amine.
Dans le cas présent, le but du traitement n'est pas de rendre les fils de pêche hydrophobes comme peuvent le permettre certaines huiles silicones réactives. En effet, les fils humides présentent l'avantage d'être beaucoup plus souples et plus élastiques, qualités très appréciées par la majorité des pêcheurs en Europe. In the present case, the aim of the treatment is not to make the fishing lines hydrophobic as some reactive silicone oils may allow. In fact, wet threads have the advantage of being much more flexible and more elastic, qualities highly appreciated by the majority of fishermen in Europe.
Dans certains cas, des fils hydrophobes peuvent présenter un avantage car le pêcheur conserve les mêmes sensations tout au long de la partie de pêche. Pour obtenir un effet hydrophobe, il convient, dans ce cas si on le désire, de déposer un taux d'huile silicone réactive plus élevé que le taux habituellement prévu. In some cases, hydrophobic threads can have an advantage because the fisherman retains the same sensations throughout the fishing trip. To obtain a hydrophobic effect, it is advisable, in this case if desired, to deposit a rate of reactive silicone oil higher than the rate usually provided.
Les fils issus de ce traitement "VS" ont été expérimentés par des pêcheurs de grande valeur technique et capables d'apprécier les différences, en pêchant en mer et en rivière, entre du fil non traité "VS" et du fil traité "VS",. The threads resulting from this "VS" treatment have been experimented by fishermen of great technical value and capable of appreciating the differences, when fishing in the sea and in the river, between untreated thread "VS" and treated thread "VS" ,.
Dans le cas du fil testé traité "VS" on relève les avantages suivants. In the case of the tested yarn treated "VS" the following advantages are noted.
Le premier avantage du traitement "VS" se constate lors du remplissage de la bobine du moulinet. Même si ce dernier n'enroule pas uniformément le nylon sur toute la hauteur de la bobine comme cela se produit fréquemment, le traitement '^VS" compense cette irrrégularité car les spires se positionnent parfaitement les unes à côté des autres. Il en résulte que la bobine peut alors recevoir plus de fil, il n'y a pas de perte de place et cela entraîne obligatoirement des lancers plus longs. The first advantage of the "VS" treatment is seen when filling the reel of the reel. Even if the latter does not evenly wrap the nylon over the entire height of the spool as occurs frequently, the '^ VS "treatment compensates for this irregularity because the turns are positioned perfectly next to each other. As a result the spool can then receive more thread, there is no loss of space and this necessarily results in longer casts.
Ce traitement diminue également l'échauffement sur les anneaux ou le galet du pick up, aussi bien lors du lancer que pendant la lutte contre un poisson. Cette diminution de l'échauffement est encore plus sensible au moment de la réalisation d'un noeud et de son serrage. This treatment also reduces overheating on the rings or the roller of the pick up, both during the launching and during the fight against a fish. This reduction in heating is even more noticeable when a knot is made and when it is tightened.
Les noeuds serrés sur un oeillet métallique (émerillon, anneau brisé ...) s'usent bien plus lentement lors des lancers répétés. Knots tightened on a metal eyelet (swivel, broken ring ...) wear much more slowly during repeated throws.
Le monofilament traité "VS" ne fait pas de bruit en passant dans les anneaux lors du lancer, le frottement se trouve diminué d'où un gain de distance. Le phénomène de résilience est pratiquement éliminé. The monofilament treated "VS" does not make any noise when passing through the rings during the throw, the friction is reduced, hence a gain in distance. The phenomenon of resilience is practically eliminated.
En résumé, il apparait que ce traitement "VS" est particulièrement appréciable à chaque fois qu'il s'avère nécessaire de faire des lancers longs (carpe, mer...). Il contribue à nettement améliorer les performances du matériel. A titre d'exemple, avec la même canne, le même moulinet, et le même diamètre de fil, selon le poids propulsé, le traitement "VS" permet un gain de distance de l'ordre de 10 à 20 % tout en diminuant l'usure aux différents points de friction. In summary, it appears that this "VS" treatment is particularly appreciable whenever it is necessary to make long throws (carp, sea ...). It helps to significantly improve the performance of the equipment. For example, with the same rod, the same reel, and the same wire diameter, depending on the propelled weight, the "VS" treatment allows a gain in distance of the order of 10 to 20% while reducing the wear at different friction points.
Le traitement est applicable sur l'ensemble des monofilaments produits pour la pêche et qui sont généralement à base d'homopolyamide tel que le polyamide 6 ou de copolyamides tels que : 66/6 - 66/11 ou encore 6/12. The treatment is applicable to all monofilaments produced for fishing and which are generally based on homopolyamide such as polyamide 6 or on copolyamides such as: 66/6 - 66/11 or 6/12.
Il est également applicable sur les monofilaments polyamide et polyester destinés à des emplois techniques tels que : filtres - feutres de papeterie - tresses tubulaires, etc ... pour lesquels il est souhaitable d'améliorer les coefficients de glissement, la tenue à l'eau et la tenue à l'abrasion. It is also applicable on polyamide and polyester monofilaments intended for technical uses such as: filters - stationery felts - tubular braids, etc. for which it is desirable to improve the sliding coefficients, the water resistance and abrasion resistance.
Ce procédé présente l'intérêt de pouvoir être réalisé directement sur la ligne de production sans altérer la caractéristique des fils obtenus. La comparaison des caractéristiques dynamométriques des fils traités "VS" et non traités présentes sur une même ligne de fabrication permet de constater que les fils traités "VS" et les fils non traités présentent les mêmes caractéristiques dynamométriques de résistance, allongement à la rupture et retrait à l'eau bouillante. This process has the advantage of being able to be carried out directly on the production line without altering the characteristic of the wires obtained. The comparison of the dynamometric characteristics of the treated "VS" and untreated wires present on the same production line shows that the treated "VS" wires and the untreated wires have the same dynamometric characteristics of resistance, elongation at break and shrinkage with boiling water.
L'exemple suivant illustre la présente demande sans la limiter. The following example illustrates the present application without limiting it.
Exemple :
On réalise un monofilament selon la demande en mettant en oeuvre le procédé suivant
- extrusion d'un copolyamide 6/66 dans les proportions 85/15 % et de
viscosité relative VR : 4,3 dans l'acide sulfurique à 98 %,
- passage de la masse fondue dans une tête de filage munie d'une
filière de 14 orifices,
- refroidissement des monofilaments dans un bac dans de l'eau à
25 C,
- étirage partiel au taux de 3,6 dans un bac contenant de l'eau
à 55 C,
- étirage supplémentaire dans un four avec de l'air chaud à
200 C, au taux de 1,6,
- traitement thermique de relaxation fixage au taux de 0,96 dans
un four à air chaud à 200 C,
- passage dans un bain aqueux constitué comme suit
. eau : 7000 g
. émulsion silicone 899 : 1500 g
émulsion silicone 877 : 500 g
émulsion catalytique 6014 : 300 g
l'émulsion silicone 899 ou 20899 est un produit constitué d'agent
tensio-actif non ionique type alkylphénoléthoxylé et d'une huile
silicone 60 % mélange à base d'huile polyorganodiméthylsiloxane,
l'émulsion silicone 879 ou 20879 est un produit constitué d'agent
tensio-actif non ionique type alkylphénoléthoxylé et d'une huile
polyorganosiloxane bloquée, l'émulsion catalytique 6014 est un
catalyseur à base de groupes époxy aminé,
ces trois produits sont commercialisés par Rhône-Poulenc Silicones,
- passage dans un four à air chaud à 1700C et relaxation fixage
au taux de 0,99 en vue de polymériser les huiles silicone
réactives,
- réception des monofilaments sur des supports connus tels que les
bobines à joues d'un bobinoir.Example:
A monofilament is produced according to the request by implementing the following process
- extrusion of a copolyamide 6/66 in the proportions 85/15% and
relative viscosity VR: 4.3 in 98% sulfuric acid,
- passage of the melt in a spinning head provided with a
die with 14 orifices,
- cooling of the monofilaments in a tank in water at
25 C,
- partial stretching at the rate of 3.6 in a tank containing water
at 55 C,
- additional drawing in an oven with hot air at
200 C, at the rate of 1.6,
- thermal relaxation treatment fixing at the rate of 0.96 in
a 200 C hot air oven,
- passage through an aqueous bath constituted as follows
. water: 7000 g
. 899 silicone emulsion: 1500 g
silicone emulsion 877: 500 g
catalytic emulsion 6014: 300 g
the silicone emulsion 899 or 20899 is a product consisting of an agent
non-ionic alkylphenolethoxylated surfactant and an oil
60% silicone blend based on polyorganodimethylsiloxane oil,
the silicone emulsion 879 or 20879 is a product consisting of an agent
non-ionic alkylphenolethoxylated surfactant and an oil
blocked polyorganosiloxane, the catalytic emulsion 6014 is a
catalyst based on amino epoxy groups,
these three products are marketed by Rhône-Poulenc Silicones,
- passage in a hot air oven at 1700C and relaxation fixing
at a rate of 0.99 for the purpose of polymerizing silicone oils
responsive,
- reception of monofilaments on known supports such as
cheek spools of a winder.
Dans l'exemple choisi, les diamètres des monofilaments produits sont de 0,32 mm avec
- nombre total des monofilaments : 14
- vitesse de bobinage : 91 m/min
- débit en polymère : 6,3 kg/h
- passage de 7 fils dans le bain de silicones, polymérisation dans le
four à 1700C et mise sur bobines directement,
- pour comparaison, 7 fils ne sont pas passés dans le bain de silicones
mais par contre, sont passés dans le four à 1700C et ont été mis sur
bobines après ensimage, avec une émulsion aqueuse habituellement
utilisée pour les fils de pêche.In the example chosen, the diameters of the monofilaments produced are 0.32 mm with
- total number of monofilaments: 14
- winding speed: 91 m / min
- polymer flow: 6.3 kg / h
- passage of 7 wires in the silicone bath, polymerization in the
oven at 1700C and put on coils directly,
- for comparison, 7 wires did not pass through the silicone bath
but by cons, went into the oven at 1700C and were put on
coils after sizing, usually with an aqueous emulsion
used for fishing lines.
Les résultats en laboratoire, confirmés par des tests réels au bord de l'eau, sont les suivants pour ces fils de 32/100 mm
Fils traités "VS" Fils non traités taux de silicone 0,2 % O résistance linéaire à la rupture 7,1 DaN 7,0 DaN perte de résistance après 2 h dans l'eau 5,0 % 5,0 % allongement à la rupture 18,0 % 18,2 % retrait à l'eau bouillante 26,4 % 26,3 % coefficients de friction fil/acier 0,20 0,32 perte de résistance après test abrasion sur toile émerie n0 400 (cycle de 30 tours) 15,0 % 35,0 %
Les tests en laboratoire et l'essai pratique confirment bien
- des caractéristiques que l'on peut considérer comme identiques entre
le fil traité et le fil non traité,
- une réduction importante des coefficients de friction fil/acier pour
le fil traité "VS" comparativement au fil non traité,
- une réduction de la perte de résistance à l'abrasion pour le fil
traité "VS" toujours par rapport au fil non traité.The laboratory results, confirmed by real tests at the water's edge, are as follows for these 32/100 mm wires
"VS" treated yarns Untreated yarns silicone content 0.2% O linear tensile strength 7.1 DaN 7.0 DaN loss of strength after 2 h in water 5.0% 5.0% elongation at rupture 18.0% 18.2% shrinkage with boiling water 26.4% 26.3% coefficients of friction wire / steel 0.20 0.32 loss of resistance after abrasion test on fabric enerie n0 400 (cycle of 30 turns) 15.0% 35.0%
Laboratory tests and practical test confirm well
- characteristics that can be considered identical between
treated wire and untreated wire,
- a significant reduction in the wire / steel friction coefficients for
the treated yarn "VS" compared to the untreated yarn,
- a reduction in the loss of abrasion resistance for the wire
treated "VS" always compared to the untreated wire.
Cet exemple n'est pas limitatif et nous avons également appliqué ce traitement "VS" sur d'autres familles de fils de pêche
- fils répondant aux normes IGFA dans les classes 2 à 130 livres,
- fils pour pêche à la palangre pour
. le corps de ligne : 100 à 200/100 mm en général
. les avançons : 60 à 90/100 mm en général
- fils pour pêche à la mouche dans la gamme des diamètres allant de 7,5
à 50/100 mm,
- fils très souples parfumés ou non parfumés dans la gamme des
diamètres de 5/100 à 50/100 mm. This example is not limiting and we have also applied this "VS" treatment on other families of fishing lines.
- yarns meeting IGFA standards in classes 2 to 130 pounds,
- longline fishing line for
. the main body: 100 to 200/100 mm in general
. the leaders: 60 to 90/100 mm in general
- fly fishing yarn in the range of diameters from 7.5
at 50/100 mm,
- very flexible scented or unscented yarns in the range of
diameters from 5/100 to 50/100 mm.
Claims (6)