FR2651175A1 - Composite pipe (tube) with selective permeability, and its method of manufacture - Google Patents

Composite pipe (tube) with selective permeability, and its method of manufacture Download PDF

Info

Publication number
FR2651175A1
FR2651175A1 FR8911293A FR8911293A FR2651175A1 FR 2651175 A1 FR2651175 A1 FR 2651175A1 FR 8911293 A FR8911293 A FR 8911293A FR 8911293 A FR8911293 A FR 8911293A FR 2651175 A1 FR2651175 A1 FR 2651175A1
Authority
FR
France
Prior art keywords
tube
foam
hydrophobic agent
tube according
foaming
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
FR8911293A
Other languages
French (fr)
Other versions
FR2651175B1 (en
Inventor
Verstraete Gilles
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GLOANEC
Original Assignee
GLOANEC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GLOANEC filed Critical GLOANEC
Priority to FR8911293A priority Critical patent/FR2651175B1/en
Publication of FR2651175A1 publication Critical patent/FR2651175A1/en
Application granted granted Critical
Publication of FR2651175B1 publication Critical patent/FR2651175B1/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

The tube, especially for the air intake of an internal-combustion engine for vehicles, is characterised in that it is constituted by an inner support tube (1) forming a reinforcing member permeable to air and to liquids, and by a tubular outer layer 2 which is applied to the inner layer 1 in order to completely surround it and which is constituted by an air-permeable and liquid-impermeable foam containing a hydrophobic agent. In order to produce such a tube, a foaming agent is applied to the outer surface of the support tube 1 and the hydrophobic agent is added to it.

Description

La présente invention est relative à un tube composite à perméabilité sélective, ainsi qu à un procédé pour fabriquer un tel tube. The present invention relates to a composite tube with selective permeability, as well as to a process for manufacturing such a tube.

L'invention s'applique en particulier, mais non exclusivement, à un tel tube qui est utilisé pour la prise d'air de moteurs à combustion interne. The invention applies in particular, but not exclusively, to such a tube which is used for the intake of air from internal combustion engines.

Elle a pour but de fournir un tube de ce genre qui présente une bonne propriété d'isolation acoustique et qui, tout en étant imperméable à l'eau , et plus généralement aux liquides, est perméable à l'air
A cet effet, le tube selon l'invention est caractérisé par le fait qu'il est constitué par un tube intérieur de support formant armature et perméable à l'air et aux liquides, et par une couche extérieure tubulaire qui est appliquée sur le tube intérieur pour l'entourer complètement et qui est constituée par une mousse perméable à l'air et imperméable à 1' eau contenant un agent hydrophobe
Le tube intérieur de support est par exemple constitué par un tube tissé, un tube tressé, un tube tricoté, un tube en#non-tissé, un tube en grillage, un tube en treillis ou un tube métallique ajouré .Ce tube intérieur peut, sulvant sa nature, être renforcé, par exemple par des fils métalliques ou des fibres de verre, de carbone ou d'aramide.It aims to provide a tube of this kind which has a good sound insulation property and which, while being impermeable to water, and more generally to liquids, is permeable to air.
To this end, the tube according to the invention is characterized by the fact that it is constituted by an inner support tube forming an armature and permeable to air and liquids, and by an outer tubular layer which is applied to the tube. interior to completely surround it and which consists of an air permeable and waterproof foam containing a hydrophobic agent
The inner support tube is for example constituted by a woven tube, a braided tube, a knitted tube, a non-woven # tube, a mesh tube, a trellis tube or an openwork metal tube. depending on its nature, be reinforced, for example with metal wires or glass, carbon or aramid fibers.

Quant à la mousse, elle peut appartenir au groupe des polymères polyacryliques, l'acétate d'éthyle-vinyle, le caoutchouc naturel ou synthétique et leurs combinaisons. La mousse peut contenir au moins un adjuvant qui a pour fonction notamment d'agir comme épaississant, comme catalyseur et/ou sur la porosité, la raideur et/ou la stabilité de la mousse. As for the foam, it can belong to the group of polyacrylic polymers, ethyl vinyl acetate, natural or synthetic rubber and their combinations. The foam may contain at least one adjuvant which has the function in particular of acting as a thickener, as a catalyst and / or on the porosity, stiffness and / or stability of the foam.

De préférence, cette mousse contient un agent de dilution.Preferably, this foam contains a diluting agent.

Quant à l'agent hydrophobe que contient la mousse, il peut être constitué par un composé à base de fluor ou de silicone, de préférence sous la forme d'une résine
Dans l'application particulière considérée , la couche extérieure de mousse est appliquée par exemple à raison de 200 à 400 g/m2 , de préférence 350 g/m2, et elle peut présenter une densité de 0,3 à 0,5. As for the hydrophobic agent that the foam contains, it can be constituted by a compound based on fluorine or silicone, preferably in the form of a resin.
In the particular application considered, the outer layer of foam is applied for example at a rate of 200 to 400 g / m2, preferably 350 g / m2, and it can have a density of 0.3 to 0.5.

Pour réaliser le tube ci-dessus, le procédé selon l'invention consiste à appliquer sur la surface extérieure du tube de support un produit de moussage et à ajouter au produit de moussage l'agent hydrophobe#
Par exemple,l'agent hydrophobe est ajouté avant le mous- sage par simple adjonction au produit de moussage, ou pendant le moussage par pulvérisation, ou même après séchage ou traitement ultérieur de polymérisation ou de réticulation. To make the above tube, the method according to the invention consists in applying a foaming product to the external surface of the support tube and in adding the hydrophobic agent # to the foaming product.
For example, the hydrophobic agent is added before foaming by simple addition to the foaming product, or during spraying foaming, or even after drying or subsequent polymerization or crosslinking treatment.

Le produit de moussage peut être appliqué sur le tube intérieur de support soit par enduction, soit par pulvérisation. The foaming product can be applied to the inner support tube either by coating or by spraying.

De préférence, on fait subir à la mousse un traitement de polymérisation, par exemple par traitement thermique ou par utilisation d'un rayonnement ionisant, notamment ultraviolet, infra- rouge, par micro-ondes ou par rayons gamma. Preferably, the foam is subjected to a polymerization treatment, for example by heat treatment or by the use of ionizing radiation, in particular ultraviolet, infrared, by microwave or by gamma rays.

On comprendra bien l'invention à la lecture du complément de description qui va suivre et en référence à la figure unique annexée qui représente une coupe axiale d'une partie d'un tube réalisé conformément à l'invention. The invention will be clearly understood on reading the additional description which follows and with reference to the single appended figure which represents an axial section of a part of a tube produced in accordance with the invention.

Le tube représente# sur la figure qui, dans l'application préférée de l'invention, est destiné à être utilisé pour la prise d'air d'un moteur à combustion interne pour véhicules, est constitué de deux éléments , à savoir un tube intérieur de support 1 constituant une armature mécanique et perméable à l'air et aux liquides, et par une couche extérieure tubulaire 2 qui est appliquée sur le tube 1 pour l'entouret complètement et qui est constituée par une mousse perméable à l'air et imperméable aux liquides, notamment à 1' eau, cette mousse contenant un agent hydrophobe. The tube represents # in the figure which, in the preferred application of the invention, is intended to be used for the air intake of an internal combustion engine for vehicles, consists of two elements, namely a tube support interior 1 constituting a mechanical reinforcement and permeable to air and liquids, and by a tubular external layer 2 which is applied to the tube 1 for the surround completely and which is constituted by a foam permeable to air and impermeable to liquids, in particular to water, this foam containing a hydrophobic agent.

Le tube intérieur de support 1 peut etre constitué de toute manière appropriée, par exemple par un tube tissé, tressé, tricoté, non-tissé, en grillage, en treillis ou en métal ajouré . Si le tube composite doit présenter une résistance mécanique importante , ou encore si le tube intérieur 1 n'est lui-même pas assez résistant , ce dernier peut être renforcé par exemple par des fils métalliques ou des fibres de verre, de carbone ou d'aramide. The inner support tube 1 can be constituted in any suitable manner, for example by a woven, braided, knitted, non-woven, mesh, mesh or openwork metal tube. If the composite tube must have a high mechanical resistance, or if the inner tube 1 is not itself sufficiently resistant, the latter can be reinforced for example by metallic wires or fibers of glass, carbon or aramid.

Quant à la mousse de la couche extérieure 2, elle peut être constituée par un polymère polyacrylique , l'acétate d'éthyle-vinyie ,le caoutchouc naturel ou synthétique, ou encore une combinaison de ces produits . De préférence,cette mousse contient au moins un adjuvant qui a pour fonction notamment d'agir comme épaississant, comme catalyseur et/ou sur la porosité, la raideur et/ou la stabilité de la mousse. As for the foam of the outer layer 2, it can consist of a polyacrylic polymer, ethyl acetate-vinyie, natural or synthetic rubber, or a combination of these products. Preferably, this foam contains at least one adjuvant which has the function in particular of acting as a thickener, as a catalyst and / or on the porosity, stiffness and / or stability of the foam.

De préférence, cette mousse contient un agent de dilution.Preferably, this foam contains a diluting agent.

L'agent hydrophobe que contient la mousse est de toute nature appropriée; par exemple, il peut être constitué par un composé å base de fluor ou de silicone, et se présente de préférence sous la forme d'une résine
Dans l'application préférée à un tube de prise d' air pour un moteur à combustion interne, la couche extérieure 2 est appliquée à raison de 200 à 400 g/m2, de préférence 350 g/m2, la mousse présentant une densité de l'ordre de 0,3 à 0, 5.The hydrophobic agent contained in the foam is of any suitable nature; for example, it may consist of a compound based on fluorine or silicone, and is preferably in the form of a resin
In the preferred application to an air intake tube for an internal combustion engine, the outer layer 2 is applied at a rate of 200 to 400 g / m2, preferably 350 g / m2, the foam having a density of l '' from 0.3 to 0.5.

Pour réaliser le tube ci-dessus, selon l'invention, on applique sur la surface extérieure du tube intérieur 1 un produit de moussage tel que défini ci-dessus, et on ajoute à ce produit de moussage l'agent hydrophobe avant la fin du moussage. To make the above tube, according to the invention, a foaming product as defined above is applied to the outside surface of the inner tube 1, and the hydrophobic agent is added to this foaming product before the end of the foaming.

Cet agent hydrophobe est ajouté soit avant le moussage lui 6me par adjonction préalable au produit de moussage,soit #pendant le moussage,par exemple par pulvérîsation,ou même après séchage ou traitement ultérieur de polymérisation ou de réticulation. This hydrophobic agent is added either before foaming itself by prior addition to the foaming product, or # during foaming, for example by spraying, or even after drying or subsequent treatment of polymerization or crosslinking.

Quant au produit de moussage lui-même , il est appliqué de toute manière appropriée, par exemple par enduction ou par pulvérisation. As for the foaming product itself, it is applied in any suitable manner, for example by coating or spraying.

De préférence, on fait subir à la mousse un traitement de polymérisation , par exemple un traitement thermique ou en utilisant un rayonnement ionisant , notamment ultraviolet, infra-rouge,par micro-ondes ou aux rayons gamma
On réalise ainsi un tube composite qui, grfice aux propriétés indiquées ci-dessus du tube intérieur 1 et de la couche extérieure 2 en mousse, est imperméable aux liquides, notamment aux projections d'eau dans l'application à un tube de prise d'air pour moteur à combustion interne, et perméable aux gaz, notamment à l'air . En outre, grace à la présence de la couche extérieure 2 en mousse, ce tube présente de bonnes propriétés d'isolation acoustique
Bien entendu, l'invention n'est pas limitée au mode, de réalisation, non plus qu'au mode d'application, qui ont été décrits; on pourrait au contraire concevoir diverses variantes sans-sortir pour autant de son cadre Preferably, the foam is subjected to a polymerization treatment, for example a heat treatment or by using ionizing radiation, in particular ultraviolet, infrared, by microwave or gamma rays.
A composite tube is thus produced which, thanks to the properties indicated above of the inner tube 1 and the outer layer 2 of foam, is impermeable to liquids, in particular to water projections in the application to a pick-up tube. air for internal combustion engine, and permeable to gases, in particular to air. In addition, thanks to the presence of the outer foam layer 2, this tube has good sound insulation properties.
Of course, the invention is not limited to the embodiment, nor to the mode of application, which have been described; on the contrary, we could conceive of various variants without departing from its framework

Claims (13)

REVENDICATIONS 1. Tube composite à perméabilité sélective, notamment tube de prise d'air pour moteur à combustion interne pour véhicule , caractérisé par le fait qu'il est constitué par un tube intérieur de support (1) formant armature et perméable à l'air et aux liquides, et par une couche extérieure tubulaire (2) appliquée sur le tube intérieur pour l'entourer complètement et constituée par une mousse perméable à l'air et imperméable aux liquides contenant un agent hydrophobe. 1. Composite tube with selective permeability, in particular air intake tube for internal combustion engine for vehicle, characterized in that it is constituted by an inner support tube (1) forming a frame and permeable to air and to liquids, and by a tubular outer layer (2) applied to the inner tube to completely surround it and constituted by a foam permeable to air and impermeable to liquids containing a hydrophobic agent. 2. Tube selon la revendication 1, caractérisé par le fait que le tube intérieur de support (1) appartient au groupe constitué par un tube tissé, un tube tressé, un tube tricoté, un tube en non-tissé, un tube en grillage, un tube en treillis et un tube métallique ajouré. 2. Tube according to claim 1, characterized in that the inner support tube (1) belongs to the group consisting of a woven tube, a braided tube, a knitted tube, a non-woven tube, a mesh tube, a trellis tube and an openwork metal tube. 3. Tube suivant l'une des revendications 1 et 2, caractérisé par le fait que le tube intérieur de support (1)est renforcé, par exemple par des fils métalliques ou des fibres de verre, de carbone ou d'aramide. 3. Tube according to one of claims 1 and 2, characterized in that the inner support tube (1) is reinforced, for example by metal son or glass, carbon or aramid fibers. 4. Tube selon l'une des revendications 1 à 3, caractérisé par le fait que la mousse appartient au groupe constitué par les polymères polyacryliques, l'acétate d'éthylevinyle, le caoutchouc naturel ou synthétique et leurs combinaisons. 4. Tube according to one of claims 1 to 3, characterized in that the foam belongs to the group consisting of polyacrylic polymers, ethyl vinyl acetate, natural or synthetic rubber and their combinations. 5. Tube selon l'une des revendications 1 à 4, caractérisé par le fait que la mousse contient au moins un adjuvant ayant pour fonction notamment d'agir comme épaississant, comme catalyseur et/ou sur la porosité, la raideur et/ou la stabilité de la mousse 5. Tube according to one of claims 1 to 4, characterized in that the foam contains at least one adjuvant having the function in particular of acting as a thickener, as a catalyst and / or on the porosity, the stiffness and / or the foam stability 6. Tube selon l'une des revendications 1 à 5, caractérisé par le fait que la mousse contient un agent de dilution. 6. Tube according to one of claims 1 to 5, characterized in that the foam contains a diluting agent. 7. Tube selon l'une des revendications 1 à 6, caractérisé par le fait que l'agent hydrophobe est unCcomposé à base de fluor ou de silicone, de préférence sous forme de résine. 7. Tube according to one of claims 1 to 6, characterized in that the hydrophobic agent is unCcomposer based on fluorine or silicone, preferably in the form of resin. 8. Tube selon l'une des revendications 1 à 7, caractérisé par le fait que la couche extérieure (2) de mousse est 2 à raison de 200 à 400 g/m de préférence 350 g/m. 2 appliquée à raison de 200 à 400 g/m , de préférence 350 g/m  8. Tube according to one of claims 1 to 7, characterized in that the outer layer (2) of foam is 2 at a rate of 200 to 400 g / m, preferably 350 g / m. 2 applied at a rate of 200 to 400 g / m, preferably 350 g / m 9. Tube selon l'une des revendications 1 à 8, carac térisé par le fait que la couche extérieure (2) de mousse présente une densité de 0,3 à 0,5. 9. Tube according to one of claims 1 to 8, charac terized in that the outer layer (2) of foam has a density of 0.3 to 0.5. 10. Procédé de fabrication du tube selon l'une des revendications 1 à 9, caractérisé par le fait qu'il consiste à appliquer sur la surface extérieure du tube de support (1) un produit de moussage et à ajouter au produit de moussage l'agent hydrophobe. 10. A method of manufacturing the tube according to one of claims 1 to 9, characterized in that it consists in applying to the outer surface of the support tube (1) a foaming product and adding to the foaming product l hydrophobic agent. 11. Procédé selon la revendication 10, caractérisé par le fait que l'agent hydrophobe est ajouté avant le moussage par adjonction, pendant le moussage, par exemple par pulvérisation, ou après séchage ou traitement ultérieur de polymérisation ou de réticulation. 11. Method according to claim 10, characterized in that the hydrophobic agent is added before foaming by addition, during foaming, for example by spraying, or after drying or subsequent treatment of polymerization or crosslinking. 12. Procédé selon l'une des revendications 10 et 11, caractérisé par le fait que le produit de moussage est appliqué par enduction ou par pulvérisation. 12. Method according to one of claims 10 and 11, characterized in that the foaming product is applied by coating or by spraying. 13. Procédé selon l'une des revendications 10 à 12, caractérisé par le fait qu'on fait subir à la mousse un traitement de polymérisation, par exemple par traitement thermique ou par utilisation d'un rayonnement ionisant, notamment ultraviolet, infra-rouge, par micro-ondes ou aux rayons gamma.  13. Method according to one of claims 10 to 12, characterized in that the foam is subjected to a polymerization treatment, for example by heat treatment or by the use of ionizing radiation, in particular ultraviolet, infrared , by microwave or gamma rays.
FR8911293A 1989-08-28 1989-08-28 COMPOSITE TUBE WITH SELECTIVE PERMEABILITY, AND MANUFACTURING METHOD THEREOF. Expired - Fee Related FR2651175B1 (en)