FR2593611A1 - METHOD FOR MANUFACTURING A COLOR FILTER - Google Patents
METHOD FOR MANUFACTURING A COLOR FILTER Download PDFInfo
- Publication number
- FR2593611A1 FR2593611A1 FR8601226A FR8601226A FR2593611A1 FR 2593611 A1 FR2593611 A1 FR 2593611A1 FR 8601226 A FR8601226 A FR 8601226A FR 8601226 A FR8601226 A FR 8601226A FR 2593611 A1 FR2593611 A1 FR 2593611A1
- Authority
- FR
- France
- Prior art keywords
- photopolymer
- colored
- layer
- dye
- dyes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Procédé de fabrication d'un filtre de couleurs caractérisé en ce qu'il comprend par exemple, dans la formation d'un dessin composé de plusieurs zones très fines de nuances différentes à la surface d'un substrat transparent, une opération consistant à transférer sur la surface de ce substrat une couche d'un photopolymère contenant un colorant, qui avait été appliquée sur un support et séchée, et une opération constituant à exposer cette couche à la lumière à travers un masque à dessin fixe, puis à la traiter avec un solvant dans lequel la solubilité des zones exposées et celle des zones non exposées sont différentes pour former le dessin, et on recommence ces opérations dans l'ordre indiqué à des intervalles déterminés pour les couches du photopolymère colorées en d'autres nuances.A method of manufacturing a color filter characterized in that it comprises, for example, in the formation of a pattern composed of several very fine zones of different shades on the surface of a transparent substrate, an operation consisting in transferring onto the surface of this substrate a layer of a photopolymer containing a dye, which had been applied to a support and dried, and an operation consisting in exposing this layer to light through a mask with a fixed pattern, then in treating it with a solvent in which the solubility of the exposed areas and that of the unexposed areas are different to form the design, and these operations are repeated in the order indicated at specified intervals for the layers of the photopolymer colored in other shades.
Description
2593 6112593 611
La présente invention concerne un procédé de fabrication d'un filtre optique de couleurs pour caméras de télévision en couleurs et autres, généralement appelé The present invention relates to a method for manufacturing an optical color filter for color television cameras and the like, generally called
filtre à raies.line filter.
Plus en détail, cette invention concerne un procédé de formation d'un filtre à raies de haute qualité dans lequel les opérations sont relativement simples et qui permet une production à grande échelle sans nécessiter In more detail, this invention relates to a method of forming a high quality line filter in which the operations are relatively simple and which allows large-scale production without requiring
des techniques de pointe ayant des inconvénients. advanced techniques with drawbacks.
La structure de ce filtre à raies comporte, The structure of this line filter comprises,
sur la surface de substrats laissant passer la lumière, com- on the surface of light-passing substrates, such as
me le verre ou autres, des raies très fines avec au moins me glass or other, very fine lines with at least
deux nuances différentes, parallèles ou séquentes. two different shades, parallel or sequential.
La largeur de ces raies est de quelques /um dans le cas de raies fines,et elles sont nécessaires à une The width of these lines is a few / μm in the case of thin lines, and they are necessary for a
bonne disposition des nuances dans un ordre déterminé. good arrangement of shades in a specific order.
C'est la raison pour laquelle, bien que diverses proposi- This is the reason why, although various proposals
tions aient été faites jusqu'ici concernant la fabrication d'un filtre à raies, aucun procédé de formation d'un tel filtre,bon marché et de haute qualité, simple à mettre en oeuvre et permettant une production à grande échelle, n'a tions have been made so far concerning the manufacture of a line filter, no method of forming such a filter, inexpensive and of high quality, simple to implement and allowing large-scale production, has
encore été réalisé.yet been achieved.
On peut par exemple, avec la méthode d'impres- We can for example, with the printing method
sion à l'écran, former un filtre à raies de faible prix, mais il est impossible de faire la pellicule mince, et la screen, form a low-cost line filter, but it is impossible to make the thin film, and the
régularité de celle-ci soulève également des difficultés. regularity of this also raises difficulties.
De plus, la limitation des dimensions du dessin pouvant être réalisé par impression à l'écran rend difficile de In addition, the limitation of the dimensions of the drawing that can be produced by screen printing makes it difficult to
former un dessin fin, de quelques um seulement. form a thin pattern, only a few µm.
Dans la méthode d'interférence avec une pelli- In the interference method with a film-
cule multicouches dans laquelle on évapore un oxyde demétal en plusieurs couches, la pellucule s'épaissit et le coût de fabrication augmente, ce qui enlève à-cette méthode multilayer cule in which a metal oxide is evaporated in several layers, the film thickens and the manufacturing cost increases, which removes this method
tout intérêt pratique.any practical interest.
En outre, dans la méthode dans laquelle on répète la coloration partielle de la pellicule transparente appliquée sur le substrat et séchée pour former le filtre, ou bien dans laquelle on répète la coloration partielle Furthermore, in the method in which the partial coloring of the transparent film applied to the substrate and dried to form the filter is repeated, or in which the partial coloring is repeated
de toute la surface de la pellicule colorée avec un colo- of the entire surface of the colored film with a colo-
rant ayant des caractéristiques spectrales déterminées, il faut répéter la formation et l'élimination de la couche rant having determined spectral characteristics, it is necessary to repeat the formation and the elimination of the layer
colorante de réserve ou de la couche empêchant la décolora- reserve dye or layer preventing discoloration
tion, ce qui complique beaucoup la fabrication du filtre. tion, which greatly complicates the manufacture of the filter.
On ne peut non plus éviter qu'il se forme des taches à par- We also cannot prevent spots from forming
tir des côtés des raies qui ont déjà été colorées, et les shooting from the sides of the lines that have already been colored, and the
conditionsde la coloration, par exemple le choix du colo- coloring conditions, for example the choice of color
rant etc..., ainsi que le maintien de la précision du pro- rant etc ..., as well as maintaining the precision of the pro-
duit, sont rendus difficiles. De même, dans la méthode de fabrication avec traitement décolorant, il y a aussi le risque que la caractéristique spectrale des raies fines à diverses nuances soit- modifiée au cours du temps par l'agent décolorant restant et les produits de décomposition duit, are made difficult. Likewise, in the manufacturing method with bleaching treatment, there is also the risk that the spectral characteristic of fine lines in various shades will be modified over time by the remaining bleaching agent and the decomposition products.
du colorant.dye.
La présente invention a pour objectif de rem6- The present invention aims to rem6-
dier aux imperfections des méthodes connues que l'on vient tell imperfections of known methods that we just
d'indiquer.to indicate.
Selon cette invention, le filtre à raies peut être facilement formé de la manière suivante: apres que la couche du photopolymère qui a été appliquée sur le support, séchée et colorée en une nuance déterminée, a été transférée sur le substrat pour former le filtre, on According to this invention, the line filter can be easily formed in the following manner: after the layer of photopolymer which has been applied to the support, dried and colored in a determined shade, has been transferred to the substrate to form the filter, we
expose cette couche colorée à la lumière à travers un mas- expose this colored layer to light through a mask
que à dessin (modèle) puis on la déve- than drawing (model) then we develop it
loppe, ce qui donne le dessin, on trans- loppe, which gives the drawing, we trans-
fère de nouveau par-dessus la couche de photopolymère colo- re-fires over the layer of colored photopolymer
rée en une autre nuance, et on recommence plusieurs fois ces opérations. On peut également former le filtre à raies de la in another shade, and these operations are repeated several times. You can also form the line filter of the
manière suivante: après que la couche du photopolymère con- as follows: after the photopolymer layer has
tenant un colorant d'une nuance a été appliquée sur le sup- holding a shade of a shade has been applied to the substrate
port et séchée, et que cette couche colorée a été exposée à travers un masque à dessin pour former le dessin worn and dried, and that this colored layer was exposed through a drawing mask to form the drawing
sur le support, on transfère le dessin développé sur le sub- on the support, we transfer the drawing developed on the sub-
strat transparent et on sépare la pellicule, puis on recom- transparent layer and we separate the film, then we recommend
mence successivement les mêmes opérations pour les couches successively carry out the same operations for the layers
de photopolymère colorées en d'autres nuances pour trans- of photopolymer colored in other shades for trans-
férer les dessins colorés successivement sur lp substrat transparent. Cette invention permet d'utiliser efficacement le photopolymère, le colorant et autres, jusqu'ici bien connus, et le choix du photopolymère rend possible la formation de dessins très fins, de quelques /um seulement. De plus, comme refer the colored drawings successively to the transparent substrate. This invention allows efficient use of the photopolymer, dye and the like, hitherto well known, and the choice of photopolymer makes it possible to form very fine patterns, of only a few µm. Furthermore, as
la coloration et autres opérations sont inutiles, la pelli- coloring and other operations are unnecessary, the film
cule peut être mince, et par ailleurs le colorant servant à former les images en couleurs peut être également choisi dans une large gamme de pigments, colorants etc..., et le colorant le plus approprié peut ainsi être choisi à la fois pour sa This can be thin, and moreover the dye used to form the color images can also be chosen from a wide range of pigments, dyes, etc., and the most suitable dye can thus be chosen both for its
solidité, sa nuance et autres caractéristiques. solidity, nuance and other characteristics.
Dans le cas d'un filtre à raies pour des caméras In the case of a line filter for cameras
de télévision en couleurs, les raies, d'une épaisseur d'en- color television, the lines, of a thickness of-
viron 1 à 2 /um et d'une largeur d'environ 10 à 30 /um, dans about 1 to 2 / µm and about 10 to 30 / µm wide, in
le rouge, le vert et le bleu qui sont les trois couleurs fonda- red, green and blue which are the three basic colors
mentales de la lumière, sont disposées parallèlement, ces trois couleurs alternant. Mais naturellement l'invention peut aussi être appliquée à d'autres filtres à raies, par exemple à un filtre dont l'ordre de disposition est différent ou à un filtre dans lequel le nombre de couleurs est de deux ou bien de quatre ou plus. L'invention peut s'appliquer en of light, are arranged in parallel, these three colors alternating. But of course the invention can also be applied to other line filters, for example to a filter whose order of arrangement is different or to a filter in which the number of colors is two or else four or more. The invention can be applied in
outre à des filtres dont les couleurs sont plusieurs cou- in addition to filters with multiple colors
leurs pour un mélange soustractif et les raies avec ces nuances se croisent mutuellement,ou encore aux filtres de their for a subtractive mixture and the lines with these shades cross each other, or even to the filters of
couleurs dont les dessins sont autres que des raies. colors whose designs are other than stripes.
Cette invention sera maintenant expliquée plus This invention will now be explained more
en détail.in detail.
Le photopolymère est une matière photosensible dont une irradiation lumineuse produit des modifications The photopolymer is a photosensitive material whose light irradiation produces modifications
telles que polymérisation, réticulation, dimérisation, déré- such as polymerization, crosslinking, dimerization, dere-
ticulation, décomposition, transposition et autres, ce qui ticulation, decomposition, transposition and others, which
entraîne des modifications qui font par exemple que la solu- brings about changes that for example make the solution
bilité dans le solvant augmente ou diminue,par exemple de la caté- solvency increases or decreases, for example,
gorie également appelée matières photosensibles pour la fabri- also called photosensitive materials for the manufacture
cation de plaques, photoréserves, résines photosensibles etc... cation of plates, photoresists, photosensitive resins etc ...
le Ces photopolymères comprennent ceux du type négatif et ceux du type positif, et si l'on emploie un photopolymère négatif dans la première partie de cette These photopolymers include those of the negative type and those of the positive type, and if a negative photopolymer is used in the first part of this
invention, on peut utiliser les deux sortes dans la secon- invention we can use both kinds in the second
des partie, ce qui constitue une caractéristique importante parts, which is an important feature
de l'invention.of the invention.
Comme exemples du photopolymère on connaîit les As examples of the photopolymer we know the
suivants, mais l'invention ne leur est pas limitée. following, but the invention is not limited to them.
Des exemples du photopolymère du type négatif sont les suivants: Examples of the negative type photopolymer are:
(1) Compositions de sels ferriques photosensi- (1) Compositions of photosensitive ferric salts
bles tels que citrate d'ammonium ferrique, tartrate d'ammo- wheat such as ferric ammonium citrate, ammonium tartrate
nium ferrique, oxalate d'ammonium ferrique et oxalate de ferric nium, ferric ammonium oxalate and oxalate
sodium ferrique, qui donnent des ions ferreux par irradia- ferric sodium, which give ferrous ions by irradia-
tion à la lumière,et dematières polymères hydrophiles comme la gélatine, la gélatine modifiée; l'alcool polyvinylique, un acétate de polyvinyle partiellement saponifié, l'acide polyacrylique et des copolymères de l'acide acrylique, ainsi tion in the light, and hydrophilic polymeric materials such as gelatin, modified gelatin; polyvinyl alcohol, partially saponified polyvinyl acetate, polyacrylic acid and copolymers of acrylic acid, as well
que le polyacrylamide et ses homologues. than polyacrylamide and its counterparts.
(2) Compositions de polymères hydrophiles tels (2) Compositions of hydrophilic polymers such
que gélatine, colle de poisson, gomme arabique, alcool poly- than gelatin, fish glue, gum arabic, poly alcohol
vinylique, polyacrylamide, carboxyméthyl-cellulose, copoly- vinyl, polyacrylamide, carboxymethyl cellulose, copoly-
mères d'éther vinylméthylique et d'anhydride maléique etc..., et de sels de tétrezonium de composés diaminés comme la benzidine et la dianidineou de résines diazoiques de condensation de la mothers of vinyl methyl ether and maleic anhydride etc ..., and tetrezonium salts of diamine compounds such as benzidine and dianidine or diazo resins of condensation of
p-diazodiphénylamine avec le paraformaldéhyde. p-diazodiphenylamine with paraformaldehyde.
(3) Résines diazoiques de composés diazoiques condensés, par exemple de la p-diazodiphénylamine avec le paraformaldéhyde. (3) Diazo resins of condensed diazo compounds, for example p-diazodiphenylamine with paraformaldehyde.
(4) Compositions d'azides comme le 4,4'-diazido- (4) Compositions of azides such as 4,4'-diazido-
stilbène-2,2'-disulfonate de sodium et le 4-azido-benzal- sodium stilbene-2,2'-disulfonate and 4-azido-benzal-
acétone-2-sulfonate de sodium, et de polymères tels que polyacrylamide, polyvinylpyrrolidone, gélatine, caséine, acétate de polyvinyle partiellement saponifié et greffé avec sodium acetone-2-sulfonate, and of polymers such as polyacrylamide, polyvinylpyrrolidone, gelatin, casein, polyvinyl acetate partially saponified and grafted with
l'acrylonitrile, nylon N-alcoxyméthylé etc... acrylonitrile, N-alkoxymethylated nylon etc ...
(5) Compositions d'azides tels que 4,4'-azido- (5) Compositions of azides such as 4,4'-azido-
benealacétone et 4,4'-diazidobenzal, méthylcyclohexanone etc...,et de polymères tels que caoutchouc cyclisé, caoutchouc benealacetone and 4,4'-diazidobenzal, methylcyclohexanone etc ..., and of polymers such as cyclized rubber, rubber
synthétique et autres.synthetic and others.
(6) Compositions d'esters de l'acide cinnamique et d'alcool polyvinylique ou d'esters allylacryliques et (6) Compositions of cinnamic acid esters and polyvinyl alcohol or allylacrylic esters and
de sensibilisateurs tels que le 5-nitroacénaphtène, la 1,2- sensitizers such as 5-nitroacenaphthene, 1,2-
benzanthraquinone et autres.benzanthraquinone and others.
(7) Compositions de polymères de monomères viny- (7) Compositions of polymers of viny-
liques ayant un groupe photosensible, par exemple du cinna- liquids having a photosensitive group, for example cinna-
mate de p-vinylphényle ou de ses copolymères-avec d'autres p-vinylphenyl mat or its copolymers-with others
monomères, et d'agents sensibilisateurs comme le 5-nitro- monomers, and sensitizers such as 5-nitro-
acénaphtène. (8) Compositions de monomères vinyliques tels que l'acrylamide, le méthylène-bis-acrylamide, l'acide acenaphthene. (8) Compositions of vinyl monomers such as acrylamide, methylene-bis-acrylamide, acid
acrylique et esters de cet acide, le diacrylate de triéthy- acrylic acid and esters of this acid, triethyl diacrylate
lène-glycol, le dim6thacrylate de polyéthylène-glycol, le lene glycol, polyethylene glycol dim6thacrylate,
triméthacrylate de triméthylol-propane et le tétraméthacry- trimethylol propane trimethacrylate and tetramethacry-
late de pentaérythritol, de dérivés de la cellulose ou d'al- late pentaerythritol, cellulose derivatives or al-
cool polyvinylique et d'inducteurs de photopolymérisation. cool polyvinyl and photopolymerization inducers.
(9) Compositions d'acrylamides tels que le (9) Compositions of acrylamides such as
méthylène-bis-acrylamide et le N,N'-hexaméthylène-bis-mé- methylene-bis-acrylamide and N, N'-hexamethylene-bis-me-
thacrylamide, de nylon soluble dans l'alcool et d'inducteurs thacrylamide, alcohol soluble nylon and inductors
de polymérisation.polymerization.
(10) Compositions de composés éthyléniques comme (10) Compositions of ethylenic compounds such as
l'acrylamide, l'acide acrylique et le N,N'-méthylène-acry- acrylamide, acrylic acid and N, N'-methylene-acry-
lamide, de sels ferriques photosensibles tels que le citrate amide, photosensitive ferric salts such as citrate
d'ammonium ferrique, le tartrate d'ammonium ferrique, l'oxa- of ferric ammonium, ferric ammonium tartrate, oxa-
late d'ammonium ferrique et l'oxalate de sodium ferrique, et de polymères hydrophiles comme la gélatine, une gélatine modifiée, l'alcool polyvinylique, un acétate de polyvinyle partiellement saponifié, le polyacrylamide et copolymères ferric ammonium late and ferric sodium oxalate, and hydrophilic polymers such as gelatin, modified gelatin, polyvinyl alcohol, partially saponified polyvinyl acetate, polyacrylamide and copolymers
d'acrylamide, polyacylamides et leurs homologues. acrylamide, polyacylamides and their counterparts.
(11) Compositions de monomères éthyléniques tels (11) Compositions of ethylenic monomers such
qu'acrylamide et acide acrylique, de colorants photoréduc- than acrylamide and acrylic acid, photoreducent dyes
tibles tels que thionine, riboflavine et bleu de méthylène, targets such as thionine, riboflavin and methylene blue,
de réducteurs comme l'ascorbate de triéthanolamine, la thio- reducing agents such as triethanolamine ascorbate, thio-
urée, l'éthylène diamine -tétracétate de sodium etc..., de urea, ethylene diamine-sodium tetracetate etc ..., from
polymères hydrophiles tels que gélatine, alcool polyviny- hydrophilic polymers such as gelatin, polyvinyl alcohol
lique, polyacrylamide et autres, et si cela est nécessaire d'agents réticulants comme l'acrylate de calcium, l'acrylate lique, polyacrylamide and others, and if necessary crosslinking agents such as calcium acrylate, acrylate
de baryum, le N,N'-méthylène-bis-acrylamide et autres. barium, N, N'-methylene-bis-acrylamide and others.
Des exemples du photopolymère de type positif sont les suivants: (1) Quinone-diazides, par exemple esters de il'acide 0-naphtoquinone-diazidesulfonique, sulfonamides etc..., ou mélanges de ces quinone-diazides et de résines Examples of the positive type photopolymer are the following: (1) Quinone-diazides, for example esters of 0-naphthoquinone-diazidesulfonic acid, sulfonamides, etc., or mixtures of these quinone-diazides and resins
solubles dans les alcalis comme la résine phénolique appe- soluble in alkalis such as phenolic resin
lée Novolaque.Novolak.
(2) Produits de réaction d'anions polynucléaires (2) Polynuclear anion reaction products
d'hétéropolyacides ou d'isopolyacides avec des sels de dia- heteropolyacids or isopolyacids with di-
zonium.zonium.
(3) Composés ayant un groupe 0-nitrobenzaldéhyde comme le phtalate de bis(3-aldéhydo-4-nitrophényle) et (3) Compounds having a 0-nitrobenzaldehyde group such as bis (3-aldehydo-4-nitrophenyl) phthalate and
le carbonate de 3-aldéhydo-4-nitrophényle. 3-aldehydo-4-nitrophenyl carbonate.
(4) Ethylène-dioxy-5,5' résorcinol. (4) Ethylene-dioxy-5,5 'resorcinol.
La couche photosensible d'un photopolymère tel que ci- The photosensitive layer of a photopolymer as below
dessus est appliquée sur le support et elle est séchée de la manière courante après que les agents de coloration tels top is applied to the support and is dried in the usual way after the coloring agents such
que pigments, colorants etc... ont été incorporés à la solu- pigments, dyes etc ... have been incorporated into the solution
tion ou à la dispersion du photopolymère, ou bien, après que la solution du photopolymère seule a été appliquée et séchée, on applique sur le couche photosensible la solution de résine comprenant le colorant et on la sèche. Mais on peut également former la couche photosensible en appliquant et en séchant la solution de résine contenant le colorant tion or dispersion of the photopolymer, or else, after the photopolymer solution alone has been applied and dried, the resin solution comprising the dye is applied to the photosensitive layer and dried. However, the photosensitive layer can also be formed by applying and drying the resin solution containing the dye.
puis en appliquant par-dessus la solution du photopolymère. then applying the photopolymer solution over it.
Pour la formation d'images en couleurs du photo- For the formation of color images from photo-
polymère on utilise des pigments et colorants. Comme pigments polymer, pigments and dyes are used. As pigments
on peut prendre des pigments minéraux ou organiques en dis- you can take mineral or organic pigments in dis-
persion aqueuse ou dans un solvant, respectivement, et comme colorants divers colorants solubles dans les huiles, dans aqueous persion or in a solvent, respectively, and as dyes various dyes soluble in oils, in
l'eau, des colorants à l'alcool, des colorants de disper- water, alcohol dyes, disperse dyes
sion et autres.sion and others.
Comme, dans l'exécution de cette invention, on peut prendre des pigments et colorants bien connus suivant le genre du photopolymère employé, la constitution de la couche photosensible et autres facteurs, la choix de l'agent As, in carrying out this invention, well-known pigments and dyes can be taken depending on the kind of photopolymer used, the constitution of the photosensitive layer and other factors, the choice of agent
de coloration est très large, ce qui est une importantecarac- color is very wide, which is an important characteristic
259361 1259361 1
téristique de l'invention, et l'on peut choisir le colorant le plus approprié à la fois pour sa solidité, sa nuance et autres propriétés. Il est cependant nécessaire que le colorant soit compatible avec le photopolymère et la nuance voulue, c'est-à-dire la nuance qui correspond aux trois couleurs complémentaires de la lumière ou au mélange soustractif, et aussi naturellement qu'il soit très pur, téristique of the invention, and one can choose the most suitable dye for its strength, shade and other properties. It is however necessary that the dye is compatible with the photopolymer and the desired shade, that is to say the shade which corresponds to the three complementary colors of light or to the subtractive mixture, and also naturally that it is very pure,
très transparent et très solide solide à la lumière. very transparent and very solid, solid in light.
La formation de l'image par exposition et déve- Image formation by exposure and development
loppement peut se faire par les méthodes bien connues suivant development can be done by the well known methods following
le photopolymère et la constitution de la couche photosensi- the photopolymer and the constitution of the photosensitive layer
ble. Comme support on peut indiquer le polychlorure de vinyle, corn. Polyvinyl chloride can be used as support,
le polyéthylène, le polypropylène, le polystyrène, des poly- polyethylene, polypropylene, polystyrene, poly-
amides et polycarbonates, l'acétylcellulose, des polyesters, le téréphtalate de polyéthylène etc..., que l'on choisit en tenant compte de l'adhérence de la couche photosensible au support, de la constance des dimensions de celui-ci et autres facteurs. Ensuite, pour améliorer l'aptitude au transfert, l'adhérence ou autres, du photopolymère coloré au substrat en vue de'former le filtre à raies, il est plus efficace amides and polycarbonates, acetylcellulose, polyesters, polyethylene terephthalate etc ..., which is chosen taking into account the adhesion of the photosensitive layer to the support, the constancy of the dimensions of the latter and others factors. Then, to improve the transferability, adhesion or the like, of the colored photopolymer to the substrate in order to deform the line filter, it is more effective
d'appliquer sur le support du photopolymère coloré des sous- to apply to the support of the colored photopolymer
couches préalables, par exemple une couche de séparation ou autres. On peut aussi former sur la couche du photopolymère coloré une couche thermosensible ou sensible à la pression en une mince pellicule, et si cette couche adhésive sensible à la pression ou thermosensible est appliquée sur le substrat pour former le filtre à raies, on peut obtenir une adhérence plus solide. Il faut choisir la couche de séparation ou la couche adhésive en tenant compte de la nature du support utilisé, du photopolymère, de la solution de développement preliminary layers, for example a separation layer or the like. One can also form on the layer of the colored photopolymer a heat-sensitive or pressure-sensitive layer in a thin film, and if this pressure-sensitive or heat-sensitive adhesive layer is applied to the substrate to form the line filter, one can obtain a stronger adhesion. You must choose the separation layer or the adhesive layer taking into account the nature of the support used, the photopolymer, the development solution.
et autres facteurs.and other factors.
De même, également quand le dessin ou modèle Likewise, also when the design
formé sur le support est transféré sur le substrat trans- formed on the support is transferred to the trans-
parent, comme dans la seconde partie de l'invention,l'appli- parent, as in the second part of the invention, the appli-
cation préalable sur le support de sous-couches, par exemple d'une couche de séparation ou autres, est plus efficace pour améliorer l'aptitude au transfert. De même, pour améliorer l'adhérence du dessin après son transfert sur le substrat transparent, on peut appliquer sur le support une couche Pre-cation on the support of sublayers, for example a separating layer or the like, is more effective in improving the transferability. Similarly, to improve the adhesion of the design after it has been transferred to the transparent substrate, a layer can be applied to the support.
adhésive sensible à la pression ou thermosensible qui adhè- pressure sensitive or heat sensitive adhesive
re très bien à la couche photosensible et qui peut être fa- cilement séparée du support. De même, l'application sur le substrat transparent de la couche adhésive sensible à la re very well to the photosensitive layer and which can be easily separated from the support. Similarly, the application to the transparent substrate of the adhesive layer sensitive to the
pression ouà la chaleur améliore l'efficacité. pressure or heat improves efficiency.
Comme agents de séparation on peut prendre des matières polymères, prépolymères et autres,aptes à jouer ce rôle, qui sont employés de manière connue pour des papiers de séparation, par exemple une résine de silicone,une résine As separating agents, it is possible to take polymeric materials, prepolymers and the like, capable of playing this role, which are used in known manner for separation papers, for example a silicone resin, a resin
alkyde, une résine de polyuréthanne ou de polyester, une ré- alkyd, a polyurethane or polyester resin, a
sine aminée ou une résine phénolique, ou un mélange de deux ou plusieurs de ces résines, et l'on peut fixer des groupes fonctionnels sur les chaînes latérales ou aux extrémités de ces polymères ou prépolymères pour qu'ils se réticulent ou amino sine or a phenolic resin, or a mixture of two or more of these resins, and functional groups can be attached to the side chains or to the ends of these polymers or prepolymers so that they crosslink or
se polymérisent sous l'action de la lumière. polymerize under the action of light.
Comme adhésifsthermosensibles qui adhèrent très As heat sensitive adhesives that adhere very
bien à la couche photosensible et qui peuvent être facile- good at photosensitive layer and which can be easy-
ment séparés du support, on peut indiquer un copolymère d'éthylène et d'acétate de vinyle ou de chlorure de vinyle et de propionate de vinyle, une résine de polyoléfine, un ment separated from the support, one can indicate a copolymer of ethylene and vinyl acetate or vinyl chloride and vinyl propionate, a polyolefin resin, a
polymère à base de chlorure de vinyle, un copolymère d'éthy- vinyl chloride-based polymer, an ethylene-
lène avec un ester d'acide carboxylique, une résine de poly- lene with a carboxylic acid ester, a poly-
vinylacétal hydrosoluble,une résine de butyral, de formai ou à base de chlorure de vinylidène, une polyolëfine chlorée, un copolymère éthylèneacétate de vinyle chloré, une résine acrylique ou à base de caoutchouc etc..., que l'on choisit water-soluble vinyl acetal, a butyral, formaldehyde or vinylidene chloride-based resin, a chlorinated polyolefin, an ethylene-chlorinated vinyl acetate copolymer, an acrylic or rubber-based resin, etc., which one chooses
d'une manière appropriée en fonction de la couche photosen- appropriately depending on the photosensitive layer
sible ou de la nature du support.sible or the nature of the support.
En outre, comme adhésifs à appliquer sur le substrat transparent, on utilise des adhésifs bien connus, thermosensiblesou sensiblesà la pression, auxquels ne sont In addition, as adhesives to be applied to the transparent substrate, well-known adhesives, which are heat-sensitive or pressure-sensitive, are used, which are not
pas imposées de limitations spéciales. no special limitations imposed.
Comme méthode de transfert de la couche du photo- As a method of transferring the photo layer
polymèresur le substrat de verre,suivant la première partie de cette invention, on peut utiliser la machine à stratifier bien connue, et appliquer la méthode d'adhérence par pression ou par fusion à chaud ou autres, *suivant la nature polymers on the glass substrate, according to the first part of this invention, one can use the well-known laminating machine, and apply the method of adhesion by pressure or by hot melting or others, * depending on the nature
de l'adhésif ou de la couche du photopolymère. adhesive or photopolymer layer.
Si le dessin (modèle) formé sur le support est trans- féré sur le substrat transparent, suivant la seconde partie de l'invention, il est préférable que l'épaisseur de la pellicule du filtre à raies soit faible si le dessin est transféré seul, mais suivant le type employé on peut If the drawing (model) formed on the support is transferred to the transparent substrate, according to the second part of the invention, it is preferable that the thickness of the film of the line filter is small if the drawing is transferred alone , but depending on the type used we can
également transférer le dessin avec la couche adhésive in- also transfer the design with the adhesive layer
diquée qui adhère très bien à la couche photosensible et qui peut être facilement séparée du support, et il va sans dire que dans ce cas l'épaisseur de la couche adhésive given which adheres very well to the photosensitive layer and which can be easily separated from the support, and it goes without saying that in this case the thickness of the adhesive layer
doit être aussi faible que possible. On effectue ordinaire- should be as low as possible. We perform ordinary-
ment le transfert avec la machine à stratifier, en choisissant la méthode d'adhérence par pression ou par la chaleur suivant le type de couche photosensible ou de couche adhésive qui transfer with the laminating machine, choosing the method of adhesion by pressure or by heat depending on the type of photosensitive layer or adhesive layer which
est employé dans la première partie de l'invention. is used in the first part of the invention.
Ainsi qu'il a été dit plus haut, on peut utiliser efficacement selon la présente invention des photopolymères, colorants, agents de séparation, adhésifs etc..., qui sont As mentioned above, photopolymers, dyes, release agents, adhesives, etc., which can be used effectively according to the present invention.
tous bien connus, et par les techniques de transfert égale- all well known, and by transfer techniques equally
ment connues on peut fabriquer des filtres à raies de grande we can make large line filters
qualité suivant un procédé relativement simple, ce qui sup- quality in a relatively simple process, which
prime les défauts des diverses méthodes connues jusqu'à pre- premium the faults of the various methods known until pre-
sent. C'est ainsi que l'emploi du photopolymère permet la formation de dessins très fins, de quelques /um seulement, et comme la coloration et autres opérations deviennent smells. This is how the use of the photopolymer allows the formation of very fine patterns, of only a few μm, and as the coloring and other operations become
inutiles, la pellicule peut également être mince. unnecessary, the film may also be thin.
De plus, non seulement le choix des conditions de coloration et la conduite de la coloration n'exigent pas une exactitude rigoureuse ni le plus grand soin, mais en outre se trouve résolu le plus grave problème, qui est qu'au moment de la seconde coloration et de la coloration ultérieure, le colorant migre vers la zone qui a déjà été préalablement colorée en la tachant ou en s'y mélangeant, produisant ainsi In addition, not only the choice of coloring conditions and the conduct of coloring do not require rigorous accuracy or care, but also the most serious problem is solved, which is that at the time of the second coloring and subsequent coloring, the dye migrates to the area that has already been previously colored by staining or mixing therewith, thereby producing
259361 1259361 1
un effet néfaste sur sa caractéristique spectrale. En plus a harmful effect on its spectral characteristic. More
de cela, dans les méthodes connues de conduite d'une décolo- of this, in the known methods of conducting a decolo-
ration partielle, un problème semblable est posé par ce qui reste de l'agent décolorant qui est un oxydant, un réducteur ou autres, problème que cette invention permet également de résoudre. Comme il a été dit, la présente invention permet partial ration, a similar problem is posed by what remains of the bleaching agent which is an oxidant, a reducing agent or the like, a problem which this invention also makes it possible to solve. As has been said, the present invention allows
de fabriquer facilement des filtres à raies d'une grande qua- easily fabricate a large number of line filters
lité constante sans nécessiter des techniques de pointe et compliquées. Par ailleurs, le choix du dessin,quand on expose la couche du photopolymère coloré, permet de faire des filtres de couleurs avec des dessins variés, par exemple en constant quality without requiring advanced and complicated techniques. Furthermore, the choice of design, when the layer of colored photopolymer is exposed, makes it possible to make color filters with various designs, for example in
mosaique ou autres, ainsi qu'à raies diverses. mosaic or other, as well as various lines.
Les exemples qui sont donnés ci-après décrivent plus en détail la présente invention sans en limiter la The examples which are given below describe the present invention in more detail without limiting its
portée, exemples dans lesquels les parties de matièresindi- scope, examples in which parts of materials
quées sont données en poids dans tous les cas. are given by weight in all cases.
EXEMPLE 1:EXAMPLE 1:
A des solutionsaqueused'un photopolymère à 5 % To solutions that have a 5% photopolymer
de matière solide, comprenant 10 parties de gélatine (pro- solid matter, comprising 10 parts of gelatin (pro-
duit S-778 de Nippi Co.) et 1 partie de bichromate de potas- duit S-778 from Nippi Co.) and 1 part of bichromate of potash-
sium, on ajoute respectivement des colorants ayant diverses nuances pour sium, we add respectively dyes having various shades to
préparer trois sortes de compositions colorées. prepare three kinds of colored compositions.
Colorant rouge de la composition colorée R: Suminol Milling Red RS (de Sumitomo Chemical) Colorant vert de la composition colorée G: Mélange en quantités égales du colorant Acid Fast Yellow MR (de Chugai Chemicals) et du colorant Sumitomo Brilliant Blue 5G (de Sumitomo Chemical) Colorant bleu de la composition colorée B: Supranol Cyanine 6B (de Bayer) On ajoute les colorants respectifs de manière Red dye of colored composition R: Suminol Milling Red RS (from Sumitomo Chemical) Green dye of colored composition G: Mix in equal amounts of Acid Fast Yellow MR dye (from Chugai Chemicals) and Sumitomo Brilliant Blue 5G dye (from Sumitomo Chemical) Blue dye of color composition B: Supranol Cyanine 6B (from Bayer) The respective dyes are added in a manner
que les absorbances spectrales de raies d'environ 1/um d'épais- that the spectral absorbances of lines of about 1 / µm thick-
seur soient supérieures à 1,5 aux longueurs d'ondes respectives auxquelles l'absorbance devient maximale dans sors are greater than 1.5 at the respective wavelengths at which the absorbance becomes maximum in
le filtre.the filter.
il On applique respectivement ces trois sortes de compositions colorées surdes pellicules en téréphtalate de polyéthylène orientées suivantleurs deux axes, de 75/u.., de manière que leur épaisseur après séchage soit d'envird 1/um, et on les sèche. Par ailleurs, sur l'une des faces d'une plaque de verre transparente d'une épaisseur de 2 mm, on applique l'adhésif polyoléfinique thermosensible AC 1000 (de Mitsubishi Yuka Fine) de manière que son épaisseur après These three kinds of colored compositions are respectively applied to polyethylene terephthalate films oriented along their two axes, of 75 μm, so that their thickness after drying is around 1 μm, and they are dried. Furthermore, on one side of a transparent glass plate with a thickness of 2 mm, the thermosensitive polyolefinic adhesive AC 1000 (from Mitsubishi Yuka Fine) is applied so that its thickness after
séchage soit de 2/um, et on le sèche. drying is 2 µm, and dried.
On place ensuite la couche adhésive du verre transparent sur la composition colorée R de la The adhesive layer of the transparent glass is then placed on the colored composition R of the
pellicule et on les fait adhérer avec un rouleau à 100 C. film and they are adhered with a roller at 100 C.
Quand on sépare la pellicule, la couche R de la composition colorée est transférée sur le substrat de verre. En plaçant un masque qui comporte des zones de transmission de lumière de 100/um de large à des intervalles de 200/um, on irradie à l'ultraviolet la couche R de la composition colorée sur le substrat de verre pour la durcir dans ses parties qui correspondent aux zones de transmission de la lumière, puis on dissout les zones non exposées avec de l'eau tiède pour When the film is separated, the R layer of the colored composition is transferred to the glass substrate. By placing a mask which has light transmission zones of 100 μm wide at intervals of 200 μm, the R layer of the colored composition is irradiated on the glass substrate to harden its parts. which correspond to the areas of light transmission, then dissolve the unexposed areas with lukewarm water to
les éliminer, ce qui laisse des raies rouges. remove them, leaving red lines.
On superpose la pellicule sur laquélle a été appliquée la composition colorée G, composition que l'on transfère d'une manière semblable sur les raies rouges sur le substrat de verre, puis, en déplaçant la position du masque ci-dessus par un cadre, on irradie à l'ultraviolet The film is superimposed on which the colored composition G has been applied, a composition which is transferred in a similar manner to the red lines on the glass substrate, then, by moving the position of the mask above by a frame, we irradiate with ultraviolet
et on élimine ensuite les zones non exposées de la même ma- and then remove unexposed areas in the same way
nière que ci-dessus, ce qui forme une image avec des raies nier than above, which forms an image with lines
rouges et des raies vertes qui alternent. red and green stripes that alternate.
On recommence ensuite les opérations précédentes We then repeat the previous operations
avec la pellicule sur laquelle a été appliquée la compo- with the film on which the compound has been applied
sition colorée B, ce qui donne finalement le filtre avec des raies rouges, vertes et bleues, contiguës entre elles colored section B, which finally gives the filter with red, green and blue lines, contiguous between them
dans la direction de la largeur.in the direction of the width.
EXEMPLE 2:EXAMPLE 2:
A des solutiors aqueuses à 5 % de matière solide Has aqueous solutiors with 5% solid matter
d'un photopolymère,comprenant 10 parties d'alcool polyviny- a photopolymer, comprising 10 parts of polyvinyl alcohol
lique (degré de polymérisation moyen 1700 - 2400, degré de saponification 98,5 + 0,5 %) et 0,6 partie d'un produit de sulfonation d'un condensat de p-diazodiphénylamine avec lique (average degree of polymerization 1700 - 2400, degree of saponification 98.5 + 0.5%) and 0.6 part of a sulfonation product of a p-diazodiphenylamine condensate with
le formaldéhyde comme agent réticulant, on ajoute respec- formaldehyde as crosslinking agent, respectively add
tivement comme colorants les pigments suivants dispersés dans de l'eau pour préparer trois sortes de compositions as dyes the following pigments dispersed in water to prepare three kinds of compositions
colorées dont les nuances diffèrent. colored with different shades.
Pigment jaune de la composition colorée Y: Aquafine AF Yellow E-2 (de Dainichi Seika Co.) Pigment magenta de la composition colorée M: Aquafine AF Red E-3 (de Dainichi Seika Co.) Pigment cyan de la composition colorée C: Yellow pigment of colored composition Y: Aquafine AF Yellow E-2 (from Dainichi Seika Co.) Magenta pigment of colored composition M: Aquafine AF Red E-3 (of Dainichi Seika Co.) Cyan pigment of colored composition C:
Aquafine AF Blue E-1 (de Dainichi Seika Co.). Aquafine AF Blue E-1 (from Dainichi Seika Co.).
On ajoute ces pigments dans des proportions telles que la caractéristique spectrale soit la même que These pigments are added in proportions such that the spectral characteristic is the same as
dans l'exemple 1 précédent.in Example 1 above.
On suit ensuite le même procédé que dans l'exem- We then follow the same process as in example-
ple 1, sauf qu'après l'irradiation à l'ultraviolet on dissout ple 1, except that after ultraviolet irradiation it dissolves
* dans de l'eau pour les éliminer les zones non réticulées.* in water to remove uncrosslinked areas.
La composition colorée Y est transférée sur la plaque de verre transparente dont une face a été recouverte d'une couche de 2/um de l'adhésif AC 1000, et après exposition à travers un masque on la développe, ce qui donne des raies jaunes sur la plaque de verre. Avec les compositions colorées M et C on recommence ensuite les mêmes opérations, ce qui forme le filtre à raies en couleurs jaune, magenta The colored composition Y is transferred to the transparent glass plate, one face of which has been covered with a layer of 2 μm of the adhesive AC 1000, and after exposure through a mask, it is developed, which gives yellow stripes. on the glass plate. With the colored compositions M and C the same operations are then repeated, which forms the line filter in yellow, magenta colors
et cyan.and cyan.
EXEMPLE 3:EXAMPLE 3:
A des solutionsmaqueuses à 5 % de matière solide To 5% solid matter makeup solutions
d'un photopolymère,comprenant 10 parties de gélatine (pro- of a photopolymer, comprising 10 parts of gelatin (pro-
duit S-778 de Nippi Co.) et 0,4 partie d'oxalate d'ammo- duit S-778 from Nippi Co.) and 0.4 parts of ammonium oxalate
nium ferrique,on ajoute respectivement des pigments disper- ferric nium, disper-
sés dans de l'eau comme colorants pour préparer les composi- dyed in water as colorants to prepare the compounds
tions colorées R, G et B,dont les nuances diffèrent. colored R, G and B, with different shades.
Pigment rouge de la composition colorée R: Mélange en proportions égales des pigments Red pigment of colored composition R: Mixing of pigments in equal proportions
Aquafine AF Yellow E-2 et Aquafine AF Red E-3. Aquafine AF Yellow E-2 and Aquafine AF Red E-3.
Pigment vert de la composition colorée G: Mélange en proportions égales des pigments Green pigment of colored composition G: Mixing of pigments in equal proportions
Aquafine Yellow E-2 et Aquafine AF Blue E-1. Aquafine Yellow E-2 and Aquafine AF Blue E-1.
Pigment bleu de la composition colorée B: Mélange en proportions égales des pigments Blue pigment of colored composition B: Mixing of pigments in equal proportions
Aquafine AF Blue E-1 et Aquafine AF Red E-3. Aquafine AF Blue E-1 and Aquafine AF Red E-3.
Tous ces pigments sont fabriqués par Dainichi Seika Co. On suit le même procédé que dans l'exemple 1 All these pigments are manufactured by Dainichi Seika Co. We follow the same process as in Example 1
sauf que dans le développement après irradiation à l'ultra- except that in development after irradiation with ultra-
violet, on plonge pendant 1 minute le substrat de transfert dans une solution aqueuse à 1 % de H202 à la température de 18 C pour insolubiliser suffisamment les zones exposées puis on le plonge dans de l'eau à 37 C pour dissoudre et purple, the transfer substrate is immersed for 1 minute in an aqueous solution of 1% H 2 O 2 at a temperature of 18 C to sufficiently insolubilize the exposed areas and then it is immersed in water at 37 C to dissolve and
éliminer les zones non réticulées. eliminate uncrosslinked areas.
EXEMPLE 4:EXAMPLE 4:
A des solutions aqueuses à 5 % de matière solide d'un photopolymèrecomprenant 10 parties de gélatine (S-778, de Nippi Co.) et 1 partie de bichromate de potassium,on ajoute respectivement des colorants de nuances différentes Dyes of different shades are added to 5% solid aqueous solutions of a photopolymer comprising 10 parts of gelatin (S-778, from Nippi Co.) and 1 part of potassium dichromate.
pour préparer trois sortes de compositions colorées. to prepare three kinds of colored compositions.
Colorant rouge de la composition colorée R: Suminol Milling Red RS (de Sumito Chemical) Colorant vert de la composition colorée G: Mélange en proportions égales des colorants Acid Fast Yellow MR (Chugai Chemical) et Sumitomo Brilliant Blue 5G (Sumitomo Chemical) Colorant bleu de la composition colorée B: Red dye of colored composition R: Suminol Milling Red RS (from Sumito Chemical) Green dye of colored composition G: Mix in equal proportions of dyes Acid Fast Yellow MR (Chugai Chemical) and Sumitomo Brilliant Blue 5G (Sumitomo Chemical) Blue dye of the colored composition B:
Supranol Cyanine 6B (Bayer).Supranol Cyanine 6B (Bayer).
On ajoute ces colorants respectifs dans des proportions telles que les absorbances spectrales de raies These respective dyes are added in proportions such as the spectral absorbances of the lines.
d'environ lpm d'épaisseursoientsupérieures à 1,5 aux lon- about lpm thicker than 1.5 times longer
gueurs d'ondes dominantes respectives dans le filtre à raies. respective dominant wave generators in the line filter.
On applique respectivement ces trois sortes de compositions colorées surdes pelliculesen téréphtalate de polyéthylène de 75 Pm étiréesbiaxialement, en une épaisseur These three kinds of colored compositions are respectively applied to 75 μm biaxially stretched polyethylene terephthalate films in a thickness
après séchage d'environ lpm, et on les sèche. after drying about lpm, and they are dried.
Par ailleurs, sur l'une des faces d'une plaque In addition, on one side of a plate
de verre transparente de 2 mm d'épaisseur on applique l'adhé- 2 mm thick transparent glass, apply the adhesive
sif thermosensible polyoléfinique AC 1000 de Mitsubishi Yuka Fine en polyolefinic heat sensitive AC 1000 from Mitsubishi Yuka Fine in
une épaisseur après séchage de 2pm, et on le sèche. a thickness after drying of 2pm, and it is dried.
Après avoir placé un masque avec des zones de transmission de lumière de 100 1pm de large à des intervalles de 200pm, on irradie à l'ultravioletles trois compositions colorées respectives pour réticuler les zones exposées, puis on dissout les zones non exposées dans de l'eau tiède pour les éliminer, ce qui donne des pellicules After placing a mask with light transmission zones 100 1pm wide at 200pm intervals, the three respective colored compositions are ultraviolet irradiated to crosslink the exposed areas, then the unexposed areas are dissolved in lukewarm water to remove them, which gives dandruff
à raies rouges, vertes et bleues,respectivement. with red, green and blue stripes, respectively.
On met alors la pellicule à raies rouges en contact étroit avec la couche d'adhésif de la plaque de verre transparente et on fait passer l'ensemble entre deux cylindres chauffés à 100 C pour bien faire adhérer les deux éléments, puis on sépare la pellicule support, les raies The red stripe film is then placed in close contact with the adhesive layer of the transparent glass plate and the assembly is passed between two cylinders heated to 100 ° C. to make the two elements adhere well, then the film is separated. support, rays
rouges se formant ainsi sur la plaque de verre. On lui-super- red forming on the glass plate. We super-him
pose ensuite la pellicule à raies vertes en déplaçant la then apply the green stripe film by moving the
position des raies au moyen d'un cadre et on lamine l'ensem- position of the lines by means of a frame and the whole is laminated
ble de la même manière entre les cylindres, et après avoir séparé la pellicule on a une image avec des raies rouges et vertes qui alternent. En recommençant une troisième fois cette opération de transfert avec la pellicule à raies ble in the same way between the cylinders, and after separating the film we have an image with alternating red and green lines. By repeating this transfer operation a third time with stripe film
bleues on obtient finalement le filtre à raies rouges, ver- blue we finally get the red line filter, ver-
tes et bleues,contiguês entre elles dans la direction de your and blue, contiguous between them in the direction of
la largeur.the width.
EXEMPLE 5:EXAMPLE 5:
Sur des pellicules de polypropylène de lO10m on applique respectivement trois sortes de couches colorées avec trois sortes de colorants de nuances différentes, d'une résine de formal (Denka Vinylek N 30, de Denki Kagaku Co.), pour avoir des épaisseurs après séchage de 1/um, et on les sèche, les colorants étant les colorants rouge, vert et bleu de l'exemple 4 dans des proportions déterminées comme On polypropylene films of 10 m, three kinds of colored layers are applied respectively with three kinds of dyes of different shades, of a formal resin (Denka Vinylek N 30, from Denki Kagaku Co.), to have thicknesses after drying. 1 / μm, and they are dried, the dyes being the red, green and blue dyes of Example 4 in proportions determined as
dans cet exemple.in this example.
Sur ces couches colorées respectives on applique On these respective colored layers we apply
ensuite un photopolymère constitué par une résine phénoli- then a photopolymer consisting of a phenolic resin
que Novolaque soluble dans les alcalis et un produit de condensation du chlorure de 1,2-naphtoquinone-diazido(2)-5 sulfonyle avec une résine Novolaque soluble dans les alcalis, dans le rapport pondérai 2, pour avoir des épaisseurs après séchage de 0,5/m, et on sèche, ce qui donne trois sortes de pellicules photosensibles dans les couleurs rouge, verte that alkali-soluble Novolac and a condensation product of 1,2-naphthoquinone-diazido (2) -5 sulfonyl chloride with an alkali-soluble Novolac, in the weight ratio 2, to have thicknesses after drying of 0 , 5 / m, and dried, which gives three kinds of photosensitive films in the colors red, green
et bleue.and blue.
Sur une face de la plaque de verre transparente de 2 mm d'épaisseur on applique un adhésif de polyester (produit Bostic 7040, de Bostic Japan Co. ) pour avoir une On one side of the 2 mm thick transparent glass plate, a polyester adhesive is applied (product Bostic 7040, from Bostic Japan Co.) to have a
épaisseur après séchage de 2/um, et on le sèche. thickness after drying of 2 µm, and dried.
On procède alors comme dans l'exemple 4 à la formation des raies et au transfert sur la plaque de verre, sauf que l'on développe les pellicules photosensibles avec une solution aqueuse alcaline à 0,4 % d'hydroxyde de sodium et 30 % de salicylate de sodium, ce qui forme le filtre à Then, as in Example 4, the lines are formed and transferred to the glass plate, except that the photosensitive films are developed with an aqueous alkaline solution containing 0.4% of sodium hydroxide and 30%. sodium salicylate, which forms the
raies rouges, vertes et bleues.red, green and blue stripes.
R E V E N DI C A T I 0 NSR E V E N DI C A T I 0 NS
1.- Un procédé de fabrication d'un filtre de 1.- A process for manufacturing a filter
couleurs caractérisé en ce qu'il comprend, dans la forma- colors characterized in that it includes, in the forma-
tion d'un dessin (modèle) composé de plusieurs zones très fines de nuances différentes à la surface d'un substrat transparent, une opération consistant à transférer sur la tion of a drawing (model) composed of several very fine areas of different shades on the surface of a transparent substrate, an operation consisting in transferring onto the
surface de ce substrat une couche d'un photopolymère con- surface of this substrate a layer of a photopolymer
tenant un colorant, qui avait été appliquée sur un support et séchée, et une opération consistant à exposer la couche du photopolymère colorée à la lumière à travers un masque holding a dye, which had been applied to a support and dried, and an operation of exposing the layer of the colored photopolymer to light through a mask
à dessin fixé, puis à la traiter avec un solvant dans le- fixed drawing, then treat it with a solvent in the-
quel la solubilité des zones exposées et celle des zones non exposées sont différentes pour former le dessin, et on the solubility of the exposed areas and that of the unexposed areas are different to form the design, and we
recommence ces opérations dans l'ordre indiqué à des inter- repeat these operations in the order indicated at intervals
valles déterminés pour les couches du photopolymère colorées determined values for colored photopolymer layers
en d'autres nuances, ou bien une opération consistant à appli- in other shades, or an operation consisting in applying
quer sur le support une couche du photopolymère contenant put a layer of photopolymer on the support
un colorant d'une nuance et à la sécher, une opération con- a dye of a shade and to dry it, an operation con-
sistant à exposer cette couche colorée à la lumière à tra- being able to expose this colored layer to light through
vers un masque à dessin fixé pour ensuite former par dévelop- towards a fixed drawing mask to then form by development
pement le dessin sur le support, et une troisième opération consistant à transférer ce dessin à la surface du substrat transparent, puis on recommence ces trois opérations dans the drawing on the support, and a third operation consisting in transferring this drawing to the surface of the transparent substrate, then these three operations are repeated in
l'ordre indiqué à des intervalles déterminés pour les cou- the order indicated at specified intervals for the
ches du photopolymère contenant des colorants d'autres nuances. 2.-Le procédé selon la revendication 1 dans lequel les couches de photopolymère colorées sont de trois nuances of the photopolymer containing dyes of other shades. 2. The process according to claim 1, in which the colored photopolymer layers are of three shades.
correspondant aux trois couleurs complémentaires de la lu- corresponding to the three complementary colors of the
mière.mother.
3.- Le procédé selon la revendication 1 dans 3.- The method according to claim 1 in
lequel les couches du photopolymère colorées sont de plu- which the colored photopolymer layers are more
sieurs couleurs complémentaires pour un mélange soustrac- several complementary colors for a subtractive mixture
tif.tif.
4.- Un procédé selon les revendications 1 à 3 4.- A method according to claims 1 to 3
dans lequel le photopolymère de type négatif est choisi in which the negative type photopolymer is chosen
parmi des compositions comprenant des sels ferriquesphoto- from compositions comprising ferric salts
sensibles et des polymères hydrophiles, des polymères hydrophiles et des sels de tétrazonium de composés diaminés ou de résines diazoiques, une résine diazoique sensitive and hydrophilic polymers, hydrophilic polymers and tetrazonium salts of diamine compounds or diazo resins, a diazo resin
seulement, des azides et des polymères, un ester cinna- only azides and polymers, a cinna-
mique d'alcool polyvinylique ou des esters allylacryliques et des sensibilisateurs, des polymères ou copolymères de monomères vinyliques avec un groupe photosensible et des sensibilisateurs, des monomères vinyliques, des dérivés de la cellulose ou d'alcool polyvinylique et des inducteurs de photopolymérisation, des acrylamides, un nylon soluble dans polyvinyl alcohol or allylacrylic esters and sensitizers, polymers or copolymers of vinyl monomers with a photosensitive group and sensitizers, vinyl monomers, cellulose or polyvinyl alcohol derivatives and photopolymerization inducers, acrylamides , a nylon soluble in
l'alcool et des inducteurs de photopolymérisation, des com- alcohol and light-curing inducers,
posés éthyléniques, des sels ferriques photosensibles et des polymères hydrophiles, ou des monomères éthyléniques, des colorants photoréductibles, des agents réducteurs, des ethylenic coatings, photosensitive ferric salts and hydrophilic polymers, or ethylenic monomers, photoreducible dyes, reducing agents,
polymères hydrophiles et si nécessaire des agents de réticu- hydrophilic polymers and, if necessary, cross-linking agents
lation.lation.
5.- Un procédé selon les revendications 1 à 3, 5. A process according to claims 1 to 3,
dans lequel le photopolymère du type positif est choisi par- in which the positive type photopolymer is chosen by-
mi des compositions comprenant des quinone-diazides ou leurs mélanges avec des résines solubles dans les alcalis, des mi compositions comprising quinone-diazides or their mixtures with alkali-soluble resins,
produits de réaction d'anions polynucléaires d'hétéropoly- Polynuclear anion reaction products of heteropoly-
acides ou d'isopolyacidesavec des sels de diazonium, des acids or isopolyacids with diazonium salts,
composés ayant un groupe 0-nitro-benzaldéhyde, et l'éthy- compounds having a 0-nitro-benzaldehyde group, and ethyl-
lène dioxy-5,5'-résorcinol.lene dioxy-5,5'-resorcinol.