FR2514231A1

FR2514231A1 - LEADER FOR FISHING

Info

Publication number: FR2514231A1
Application number: FR8216385A
Authority: FR
Original assignee: Individual
Current assignee: Individual
Priority date: 1981-10-09
Filing date: 1982-09-29
Publication date: 1983-04-15
Also published as: DE3140103A1; FR2514231B1

Abstract

The invention proposes in respect of an angling line, in particular in the form of a steel two-end cheese winding, that a textile core (12) comprising a large number of individual threads consisting of synthetic textile fibre be surrounded by a braid (13) etc. made of stainless steel. The textile core consists of 125 to 1500 individual fibres.

Description

Bas de ligne pour la pêche
L'invention concerne un bas de ligne pour la pêche plus précisément un avançon à base d'acier.Fishing leader
The invention relates to a leader for fishing more precisely a branch line based on steel.

Habituellement, les fils de pêche sont en nylon ou autre polyamide. Il y a certaines espèces de poissons qu'on ne peut pas prendre avec un fil de ce type, parce que ces poissons ont des dents très coupantes et donc peuvent couper le fil. Usually the fishing lines are made of nylon or other polyamide. There are certain species of fish that you cannot catch with a wire of this type, because these fish have very sharp teeth and therefore can cut the wire.

C'est pour cette raison que les pêcheurs utilisent des avan çons en acier câblé. A une extrémité, l'avançon en- acier est relié à la ligne, à l'autre extrémité on monte l'hameçon ou le leurre. Pour faire ces deux montages, les bas de ligne en acier, ou avançons, ont deux boucles, une à chaque extremité. It is for this reason that fishermen use wired steel struts. At one end, the steel leader is connected to the line, at the other end the hook or lure is mounted. To make these two assemblies, the steel leader, or forward, have two loops, one at each end.

La plupart du temps, les boucles sont faites avec des pinces de sertissage, ou soudées, ou ligaturées. On ne peut pas faire de noeuds car ceux-ci se défont facilement. Les avançons sont vendus chez les détaillants d'articles de pêche, en différents longueurs et diamètres, de sorte qu'un magasin bien achalandé a en stock plus de 100 bas de ligne différents.Most of the time, the loops are made with crimping pliers, or welded, or tied. We can not make knots because they are easily untied. The branchlines are sold at fishing tackle retailers in different lengths and diameters, so a well-stocked store has over 100 different hooks in stock.

L'invention a pour but de proposer un bas de ligne, qui ne puisse être coupé par les dents du poisson que l'on a attrapé, extrémement résistant et aussi souple que possible. Un grand avantage serait de pouvoir le nouer. The object of the invention is to provide a leader, which cannot be cut by the teeth of the fish that has been caught, which is extremely resistant and as flexible as possible. A great advantage would be to be able to tie it.

L'invention a pour objet un bas de ligne à base d'acier, caractérisé en ce qu'il comporte une âme textile, constituée de fibres à un seul filament, recouverte par des fils d'acier inoxydable tressés. The subject of the invention is a steel-based leader, characterized in that it comprises a textile core, consisting of fibers with a single filament, covered by braided stainless steel wires.

Le résultat de l'invention est un bas de ligne à base d'acier, extrêmement résistant et très souple. La.résis- tance est environ 35% plus grande que celle d'une ligne en acier de même diamètre et de même souplesse. La résistance à la rupture est supérieure à celle de tout autre avançon en acier, et on peut facilement faire des noeuds. The result of the invention is a steel-based leader, extremely resistant and very flexible. The resistance is about 35% greater than that of a steel line of the same diameter and the same flexibility. The breaking strength is higher than that of any other steel branch line, and knots can easily be made.

Le bas de ligne selon l'invention est fait d'une âme de 125 à 1500 fibres, recouvertes de 8 ou 16 brins d'acier tressés, On peut utiliser aussi des âmes de 10 à 10.000 fibres polyamides et une enveloppe de fils d'acier inoxydables tressés de 4 à 64 brins initiaux. L'âme peut comporter aussi des fils d'acier. The leader according to the invention is made of a core of 125 to 1,500 fibers, covered with 8 or 16 strands of braided steel. It is also possible to use cores of 10 to 10,000 polyamide fibers and an envelope of son of braided stainless steel from 4 to 64 initial strands. The core may also include steel wires.

Le bas de ligne complet peut être enrobé de matière plastique, en particulier de nylon transparent ou coloré. The complete leader can be coated with plastic, in particular transparent or colored nylon.

La combinaison d'acier et de fibres textiles offre de nombreux avantages
- le bas de ligne selon l'invention est d'environ 35% plus résistant que les lignes en acier usuelles ;
- il est aussi souple et doux qu1une ligne de pêche normale
- il ne peut pas être coupé par les dents des poissons ;
- il peut être noué comme une ligne normale
on peut renforcer les noeuds avec des colles à
deux composants, ou des colles cyano-acryliques;
- avec ce bas de ligne, il n'est pas nécessaire d'acheter des avançons en acier tout faits, parce qu'il est facile à monter
- monté par le pêcheur, ce bas de ligne est environ 70% moins cher que des bas de ligne en acier déjà montes
- il est presque indestructible.Les pliures et les vrilles peuvent être redressées, en le tirant entre deux doigts ou en utilisant un redresseur de fil d'acier ;
- il est tressé et ne vrille pas
- il est vert clair et est presque invisible pour le poisson
- il a une surface rugueuse-et coupe les plantes au fond de l'eau. The combination of steel and textile fibers offers many advantages
- the leader according to the invention is about 35% more resistant than the usual steel lines;
- it is as flexible and soft as a normal fishing line
- it cannot be cut by the teeth of the fish;
- it can be knotted like a normal line
we can reinforce the knots with glues
two components, or cyano-acrylic adhesives;
- with this leader it is not necessary to buy ready-made steel branchlines, because it is easy to assemble
- assembled by the fisherman, this leader is about 70% cheaper than already assembled steel leaders
- it is almost indestructible. The folds and tendrils can be straightened, by pulling it between two fingers or using a steel wire straightener;
- it is braided and does not twist
- it is light green and is almost invisible to fish
- it has a rough surface - and cuts the plants at the bottom of the water.

- il retient les odeurs des amorces liquides
- il réduit le besoin d'avoir un gros stock d'avan çons en acier différents. Avec seulement quelques rouleaux, le revendeur a -toutes les possibilités. Cela économise de l'argent et de la place dans le magasin du détaillant.- it retains the odors of liquid primers
- it reduces the need to have a large stock of different steel struts. With just a few rolls, the dealer has it all. This saves money and space in the retailer's store.

A titre d'exemple, on a représenté au dessin annexé
Figure 1 - une canne à lancer normalement équipée d'une ligne et d'un avançon à base d'acier
Figure 2 - une section verticale du bas de ligne selon l'invention ;
Figure 3 - une section verticale d'un bas de ligne selon l'invention, enrobé
Figure 4 - un bas de ligne selon l'invention, vu en perspective
Figure 5 - un avançon avec une cuillère ondulante une cuillère tournante ou un hameçon.By way of example, there is shown in the accompanying drawing
Figure 1 - a spinning rod normally fitted with a steel base line and branch line
Figure 2 - a vertical section of the leader according to the invention;
Figure 3 - a vertical section of a leader according to the invention, coated
Figure 4 - a leader according to the invention, seen in perspective
Figure 5 - a branch line with an undulating spoon, a rotating spoon or a hook.

La canne à pêche 10 est équipée avec une ligne 11, et le bas de ligne à base d'acier 11a, au bout. L'avançon à base d'acier 11a est constitué d'une âme textile de 10 à 10.000 fibres aramides (polyamide aromatique), telles que celle fabriquée par DU PONT DE NEMOURS sous le nom de "KEVLAR". The fishing rod 10 is equipped with a line 11, and the steel base line 11a, at the end. The steel-based branchline 11a consists of a textile core of 10 to 10,000 aramid fibers (aromatic polyamide), such as that manufactured by DU PONT DE NEMOURS under the name of "KEVLAR".

L'âme 12 consiste en une grande quantité de fibres textiles et est recouverte de fils d'acier tressés 13, 13a, et 13b. The core 12 consists of a large amount of textile fibers and is covered with braided steel wires 13, 13a, and 13b.

L'enveloppe en acier tressé (Figure 4) est la protection de l'âme contre la coupe. The braided steel casing (Figure 4) is the protection of the core against cutting.

Le bas de ligne selon l'invention peut être gaminé de nylon transparent ou coloré ou d'un produit similaire (figure 3). The leader according to the invention can be coated with transparent or colored nylon or a similar product (FIG. 3).

La figure 5 montre que l'avançon à base d'acier ila a une boucle 14 et un noeud 15 à une extrémité, et à- l'autre extrémité une boucle 16 et un noeud 17, avec une cuillère ondulante 18 et un hameçon 19. Les noeuds 15 et 17 sont renforcés avec de la colle. FIG. 5 shows that the steel-based branch line ila has a loop 14 and a knot 15 at one end, and at the other end a loop 16 and a knot 17, with an undulating spoon 18 and a hook 19 The nodes 15 and 17 are reinforced with glue.

Claims

R E V E N D I C A T I-O N S

1. - Baside steel-based line, for the pole, characterized in that it comprises a textile core (12) consisting of fibers with a single filament, covered by braided stainless steel wires (13).

2. - Leader according to claim 1, characterized in that the textile reprimand is made up of 10 to 10,000 fibers.

3. - Bottom line according to claim 2, charac terized in that the textile core consists of 125 to 1,500 fibers.

4. - Leader according to one of claims 2 and 3, characterized in that the textile core consists of aramid fibers.

5. - Bottom line according to one of claims 1 to 4, characterized in that the textile core (12) is colored by a yellow, brown or green coloring, for mimicry.

6. - Leader according to one of claims 1 to 5, characterized in that the textile fibers of the core (12) are mixed with steel wires.

7. - Leader according to one of claims 1 to 6, characterized by the fact that the steel envelope is braided with a number of strands multiple of 4.

8. - Leader according to one from claims 1 to 7, characterized in that the braided steel casing is covered with plastic.

9. - Leader according to one of claims 1 to 8, characterized in that its diameter is between 0.1 and 4 mm.

10. - Leader according to one of claims 1 to 9, characterized by a diameter between 0.2 and 2mm.