FI120652B - Process for the final bleaching of a metal ion-containing pulp with chlorine dioxide - Google Patents
Process for the final bleaching of a metal ion-containing pulp with chlorine dioxide Download PDFInfo
- Publication number
- FI120652B FI120652B FI20031338A FI20031338A FI120652B FI 120652 B FI120652 B FI 120652B FI 20031338 A FI20031338 A FI 20031338A FI 20031338 A FI20031338 A FI 20031338A FI 120652 B FI120652 B FI 120652B
- Authority
- FI
- Finland
- Prior art keywords
- pulp
- chlorine dioxide
- bleaching
- process according
- carried out
- Prior art date
Description
Menetelmä metalli-ioneja sisältävän massan loppuvalkaisemiseksi klooridiok- sidilla - Förfarande för slutblekning av massa innehällande metalljoner med klordioxid S Keksinnön alaFIELD OF THE INVENTION Field of the Invention This invention relates to a process for the final bleaching of a metal ion-containing pulp with chlorine dioxide.
Esillä oleva keksintö koskee menetelmää loppuvalkaisun suorittamiseksi tehokkaasti ja taloudellisesti klooridioksidilla, jossa menetelmä koskee menetelmää metalli-ioneja sisältävän sellun loppuvalkaisemiseksi sellaisen ainoastaan aikalisiä valkai-suvaiheita ja mahdollisesti kompleksia muodostavalla aineella suoritettavan käsitit) telyn sisältävän sekvenssin jälkeen, jossa loppuvalkaisu sisältää kaksi klooridi-oksidivaihetta, joiden välissä suoritetaan pesu ja alkaliuutto, jossa klooridioksidi-vaiheet suoritetaan 8 - 20-prosenttisessa sellukonsentraatiossa ja jossa pH on 2,5 - 4,5, jossa ensimmäisten klooridioksidivaiheiden jälkeen sellu pestään ja siitä poistetaan liuenneiden metalli-ionien poistamiseksi sellainen määrä vettä, että sen kon-15 sentraatioksi tulee 12 - 50 %, ja että selluun lisätään tämän jälkeen uuttotarkoituk-sessa ja pH:n kohottamiseksi nopeasti arvoon 8-14 alkalia, minkä jälkeen selluun lisätään happoa ja klooridioksidia ja tämä johdetaan toiseen klooridioksidivaihee-seen.The present invention relates to a process for efficiently and economically performing final bleaching with chlorine dioxide, comprising a process for final bleaching a metal ion-containing pulp after a treatment comprising only alkali bleaching steps and optionally with a complexing agent, wherein the final bleaching comprises two chlorine oxides. washing and alkali extraction, wherein the chlorine dioxide steps are carried out at a cellulose concentration of 8 to 20% and a pH of 2.5 to 4.5, wherein after the first chlorine dioxide steps the pulp is washed and removed to remove dissolved metal ions -15 centrifugation becomes 12-50% and then pulp is then added to the pulp for the purpose of extraction and to raise the pH rapidly to 8-14 alkali followed by addition of acid and chlorine dioxide and this is led to the second chlorine dioxide step.
Tekniikan tausta 20 Sellun loppuvalkaisu suoritetaan tavallisesti klooridioksidilla, tätä kysymystä on kä- • · « *·*·* sitelty esimerkiksi julkaisussa SE 466 062. Useimmissa tapauksissa tämä tapahtuu : kahdessa vaiheessa käyttämällä uuttovaihetta (E), joka on sellun tekeminen alkali- • · · • V seksi, ja/tai vaiheiden välissä olevaa pesua. Jos erillistä uuttovaihetta ei ole, niin en- *:**: nen sellun pesua voidaan pH:n kohottamiseksi ensimmäisen klooridioksiditomin :*·*: 25 loppupäässä suoritettavan laimentamisen aikana lisätä alkalia. Lyhyen alkaloin- • · ti/neutralointivaiheen (n) tuloksena on seuraavassa klooridioksidivaiheessa suhteel- • · · lisen tehokas valkaistuminen klooridioksidilla (tätä kysymystä on tarkasteltu esi-merkiksi julkaisussa Papermaking Science and Technology, Book 6A, Chemical • · ·BACKGROUND OF THE INVENTION 20 Final bleaching of pulp is usually performed with chlorine dioxide; this issue is discussed, for example, in SE 466 062. In most cases, this is done by: · • Sex, and / or washing between steps. In the absence of a separate extraction step, washing of the pulp prior to *: ** can be done by adding alkali during the final dilution of the first chlorine dioxide atom: * · *: 25. The short alkalization / neutralization step (n) results in a relatively efficient chlorine dioxide bleaching step in the next chlorine dioxide step (this issue has been reviewed, for example, in Papermaking Science and Technology, Book 6A, Chemical).
Pulping, toim. J. Gullichsen ja H. Paulapuro, sivu A642). Kun klooridioksidilla val- *:*’ 30 kaistuun selluun lisätään alkalia, niin tästä liukenee ligniiniä, joka kuluttaa valkaisu- • · · kemikaaleja ja johtaa lopullisen vaaleuden pienenemiseen mikäli sitä ei klooridi- oksidivaiheen jälkeen pestä pois. Tästä syystä kaksivaiheinen klooridioksidivalkaisu suoritetaan nykyisin käyttämällä vaiheiden välissä olevaa neutralointivaihetta sek- • · · l.l venssin Dn-pesu-D mukaisesti.Pulping, ed. J. Gullichsen and H. Paulapuro, page A642). When alkali is added to the pulp coated with chlorine dioxide, the lignin is dissolved therein, which consumes bleaching chemicals and leads to a reduction in the final brightness if not washed off after the chlorine oxide step. For this reason, biphasic chlorine dioxide bleaching is presently carried out using an intermediate step of neutralization according to Dn wash-D of sequence.
♦ · • · · 35 Lisäksi julkaisussa SE 98 000 797-4 kuvataan valkaisumenetelmää keitetyn ja hap-pidelignifioidun sellun valmistamiseksi, jossa käytetään hyväksi lisättyä happo- 2 valkaisuvaihetta, jonka jälkeen seuraa pesuvaihe vielä matalammassa pH-arvossa kuin mitä siinä valkaisuvaiheessa, josta pesuvaiheesta suodos otetaan. Tässä on tarkoituksena saattaa vaikeasti liuotettavissa olevia yhdisteitä muodostavat metallit liukoiseen muotoon, jotta nämä voidaan pesuvaiheessa poistaa. Tämän mukaisesti voi-5 daan kierron sulkemisastetta valkaisun jälkeen kohottaa.In addition, SE 98 000 797-4 discloses a bleaching process for the production of cooked and oxygen-de-signed pulp, which utilizes an acid-2 bleaching step, followed by a washing step at an even lower pH than the bleaching step from which the filtrate is washed. will be taken. The purpose of this is to dissolve the metals which form difficult to dissolve compounds so that they can be removed during the washing step. Accordingly, the degree of closure of the cycle after bleaching can be increased.
Nykyisen tekniikan ongelmatProblems with current technology
Samanaikaisesti kun valkaisulaitoksilla ollaan suorittamassa järjestelyjä kierron sulkemiseksi yhä tiukemmin vaatimuksin ja esivalkaisu suoritetaan edullisesti aikalisissä vaiheissa (esimerkiksi O, 00, (OP), (PO), (EO), (EOP)) ja kompleksia ήπιοί O dostavan aineen käyttöön perustuvassa vaiheessa (Q), lisääntyy metallien kulkeutuminen sellun mukana loppuvalkaisuun, koska näitä ei ole pesty pois missään happo-vaiheessa. Tämä johtaa saostumien vaaran lisääntymiseen, jos sellu otetaan happo-vaiheesta loppuvalkaisuun, joka tapahtuu klooridioksidivaiheessa, D-vaiheessa. Jos sellun valmistus tapahtuu aikalisissä valkaisuvaiheissa ja kompleksia muodostavaa 15 ainetta sisältävässä vaiheessa ja loppuvalkaisu D-vaiheessa, niin metallit liukenevat ulos ympäröivään nesteeseen happamessa D-vaiheessa. Kun sellu tämän jälkeen tehdään alkaliseksi, niin sellususpensiossa vallitsevat olosuhteet käyvät suotuisiksi saostumille, mikä koskee ennen kaikkea kalsiumyhdisteitä. Esimerkki tällaisesta kalsiumyhdisteestä on kalsiumoksalaatti, joka voi muodostaa posliinimaisen saostu-20 man, jota voi olla vaikeaa poistaa valmistuslaitteistosta. Milloin sellukonsentraatio • · on noin 10 - 15 %, niin tämä saa aikaan sellususpension pH:n asteittaisen muuttu- misen, joka voi johtaa siihen, että pH yltää saostumille otolliselle alueelle (~ 4 - 9).At the same time as bleaching plants are making arrangements to close the cycle with increasingly stringent requirements and pre-bleaching is preferably carried out in the time steps (e.g., O, 00, (OP), (PO), (EO), (EOP)) and in the ), the migration of metals with the pulp to final bleaching is increased because these have not been washed away at any acid stage. This leads to an increased risk of precipitation if the pulp is taken from the acid stage to the final bleaching, which occurs in the chlorine dioxide stage, D stage. If pulp is produced in the alkaline bleaching steps and in the complexing agent-containing step and in the final bleaching step D, the metals will dissolve out into the surrounding liquid in the acidic D step. Subsequently, by making the pulp alkaline, the conditions in the pulp suspension are favorable for precipitation, especially for calcium compounds. An example of such a calcium compound is calcium oxalate, which may form a porcelain precipitate that may be difficult to remove from the manufacturing equipment. When the cellulose concentration is about 10-15%, this causes a gradual change in the pH of the pulp suspension, which can lead to a pH within the range acceptable for precipitation (~ 4-9).
·*·’; Jos sellu ennen pH:n säätöä ja laimentamista voitaisiin saada kuiva-ainepitoisuudel- • · taan suureksi, kuiva-ainepitoisuus >25 %, niin pH voitaisiin muuttaa nopeasti ja 25 hyppäyksellisesti happamista olosuhteista emäksisiin olosuhteisiin ja näin menetel- • ·· * · '; If the pulp before adjusting and diluting the pH could be • high in dry matter,> 25% in dry matter, the pH could be changed rapidly and by leaps and bounds from acidic to alkaline conditions, and · ·
Ien voitaisiin välttyä saostumille otollisilta kriittisiltä olosuhteilta.Critical conditions favorable for precipitation could be avoided.
• · • · ·• · • · ·
Keksinnön yhteenveto • · · • · · • · [···. Esillä olevassa keksinnössä on yllä olevat ongelmat ratkaistu sen perusteella, että • · siinä on saatu aikaan menetelmä, joka minimoi saostumien muodostumisen vaaran ··· ° v * 30 kaksivaiheisessa klooridioksidivalkaisussa, jossa vaiheiden välissä on lyhyt alkali- • · · uutto, jossa sellususpensio tehdään alkaliseksi sellun pesun sisältävän vedenpoisto-vaiheen jälkeen, jossa pois liuenneet metallit erotetaan pesu-/vedenpoistolaitteis-tossa. Pesu-/vedenpoistotoimenpiteet suoritetaan edullisesti pesu-/vedenpoistopuris- timessa. Toisin sanoen sekvenssi alkalisen esivalkaisun jälkeen on: D-vedenpoisto 35 (mukaan lukien pesu) - nD. Tämän keksinnön lisäetu on se, että siinä kuluu vä- • · 3 hemmän alkalia, koska suuressa sellukonsentraatiossa on alkaliseksi tehtävä aikaisempaa pienempi nestemäärä. Lisäksi voidaan välttyä pH-gradienteilta, koska laimentaminen alkalisella suodoksella suoritetaan sellun sakeuden ollessa olennaisesti kohtalaisen suuri, edullisesti suuri.SUMMARY OF THE INVENTION [···. The present invention solves the above problems by providing a process that minimizes the risk of precipitation ··· ° v * 30 in two-step chlorine dioxide bleaching with a short alkali extraction process, where the pulp suspension is made. alkaline after a pulp washing dewatering step, wherein the dissolved metals are separated in a washing / dewatering apparatus. The washing / dewatering operations are preferably carried out in a washing / dewatering press. In other words, the sequence after alkaline pre-bleaching is: D-dehydration 35 (including washing) - nD. A further advantage of this invention is that it consumes less alkali, • because at high cellulosic concentration, less liquid has to be made alkaline. In addition, pH gradients can be avoided because dilution with an alkaline filtrate is carried out with a substantially moderate pulp consistency, preferably high.
5 Esillä oleva keksintö koskee menetelmää metalli-ioneja sisältävän sellun loppuval-kaisemiseksi sellaisen pelkästään aikalisiä uuttovaiheita ja mahdollisesti kompleksia muodostavalla aineella suoritetun käsittelyn sisältävän sekvenssin jälkeen, jossa loppuvalkaisu sisältää kaksi klooridioksidivaihetta, joissa sellukonsentraatio on 8 -20 % ja pH 2,5 - 4,5, jossa vaiheiden välillä käytetään pesua ja alkaliuuttoa, jossa 10 sellu ensimmäisen klooridioksidivaiheen jälkeen pestään ja siitä poistetaan pois-liuenneiden metalli-ionien poistamiseksi niin paljon vettä, että tämän konsentraa-tioksi tulee 12 - 50 %, ja että selluun lisätään tämän jälkeen tämän uuttamista varten ja pH:n kohottamiseksi nopeasti alueelle 8-14 alkalia, minkä jälkeen selluun lisätään happoa ja klooridioksidia ja johdetaan toiseen klQoridioksidivaiheeseen.The present invention relates to a process for the final bleaching of a metal ion-containing pulp after a sequence comprising purely alkaline extraction steps and optionally with a complexing agent, wherein the final bleaching comprises two chlorine dioxide steps having a cellulose concentration of 8-20%, pH 2.5-4, 5, wherein washing and alkali extraction are used between the steps, whereupon 10 pulp is washed and removed after the first chlorine dioxide step to remove enough dissolved metal ions to a concentration of 12 to 50%, and thereafter extraction thereof is added to the pulp. and to rapidly raise the pH to the range of 8-14 alkali, then acid and chlorine dioxide are added to the pulp and passed to the second chlorine dioxide stage.
15 Keksinnön yksityiskohtainen selitysDetailed Description of the Invention
Ilmaisun ’’sellu” on tarkoitus sisältää esillä olevassa selityksessä edullisesti sellu, joka voi olla havupuusellua tai lehtipuusellua tai näiden seosta. Sellua saadaan vapauttamalla kuidut kemiallisesti; tämä voi esimerkiksi olla valkaistua sellua, joka on peräisin sekä pehmeästä puusta (havupuusta) että kovasta puusta (lehtipuusta).The term "" pulp "is intended to include, in the present specification, pulp which may be softwood or hardwood pulp or a mixture thereof. Pulp is obtained by chemical release of the fibers; for example, this may be bleached pulp from both softwood (softwood) and hardwood (hardwood).
• · • · · ];1;1 20 Ilmaisun ’’happo” on tarkoitus sisältää esillä olevassa selityksessä happo, joka voi- • · · ' ·1 daan valita ryhmästä, joka koostuu rikkihaposta, suolahaposta, typpihaposta, rikki- : 1.·’ dioksidista, etikkahaposta tai hiilihaposta tai näiden yhdistelmästä.The term "" acid "is intended to include, in the present specification, an acid which may be selected from the group consisting of sulfuric acid, hydrochloric acid, nitric acid, sulfuric acid: 1. · 'Dioxide, acetic or carbonic acid, or a combination thereof.
• ·• ·
Muita kemikaaleja, joita voidaan käyttää klooridioksidivalkaisun yhteydessä, ovat • · ]..It otsoni, vetyperoksidi, hypokloriitti tai alkali. Jos sellun sakeus on suuri, niin otsoni 25 voi olla edullista.Other chemicals that may be used in chlorine dioxide bleaching are · ·] .. It ozone, hydrogen peroxide, hypochlorite or alkali. If the pulp has a high consistency, ozone 25 may be preferred.
• ·• ·
Esillä olevan keksinnön edullisen suoritusmuodon mukaisesti sellusta poistetaan en-simmäisen klooridioksidivaiheen jälkeen sellainen määrä vettä, että tämän konsent- •L raadoksi tulee 25 - 50 %, edullisesti 30 - 40 %.According to a preferred embodiment of the present invention, after the first chlorine dioxide step, the amount of water is removed from the pulp to give a concentration of 25 to 50%, preferably 30 to 40%.
• · · 7 • · · • · ·• · · 7 • · · · · ·
Esillä olevan keksinnön edullisen suoritusmuodon mukaisesti klooridioksidivaihe 30 suoritetaan 8 - 15-prosenttisessa, edullisesti 10 - 12-prosenttisessa sellukonsent-raadossa.According to a preferred embodiment of the present invention, the chlorine dioxide step 30 is carried out in an 8 to 15%, preferably 10 to 12%, cellulose concentrate.
4 Käytettävä klooridioksidi on edullisesti vesiliuoksen muodossa. Lisäksi valkaisu suoritetaan edullisesti happamessa ympäristössä pH-arvosta 2,5 pH-arvoon 4,5.The chlorine dioxide used is preferably in the form of an aqueous solution. Further, the bleaching is preferably carried out in an acidic environment from pH 2.5 to pH 4.5.
Esillä olevan keksinnön edullisessa suoritusmuodossa menetelmässä käytettävä pH:n nopea kohottaminen alkaliuuton aikana tehdään siten, että pH nousee arvoihin 5 8-14, edullisesti 9 - 12, ja se nousee edullisimmin pH-arvoihin 9-11.In a preferred embodiment of the present invention, the rapid increase in pH used in the process during alkali extraction is done so that the pH rises to 5-8-14, preferably 9-12, and most preferably rises to 9-11.
Esillä olevan keksinnön edullisen suoritusmuodon mukaisesti sisäänmenevä sellu on sakeudeltaan keskitasoa (sellukonsentraatio on tavallisesti 8 - 20 %; niin kutsuttu MC-sellu) ja sellu, josta vesi on klooridioksidia käyttäen suoritettavan ensimmäisen loppuvalkaisuvaiheen jälkeen poistettu, on sakeudeltaan vahvaa (sellukon-10 sentraatio on tavallisesti 25 - 50-prosenttinen; niin kutsuttu HC-sellu).According to a preferred embodiment of the present invention, the incoming pulp has a medium consistency (generally a pulp concentration of 8-20%; so-called MC pulp) and the pulp which has been dewatered after the first final bleaching step using chlorine has a high consistency (cellulose concentration of 10 25-50%; so-called HC pulp).
Esillä olevan keksinnön edullisen suoritusmuodon mukaisesti sellu ensimmäisen klooridioksidivaiheen jälkeen laimennetaan ja sille suoritetaan vedenpoisto, johon sisältyy sellun pesu, jolloin sellusta saadaan pois metalleja runsaasti sisältävää happoa, minkä jälkeen sellu laimennetaan alkaloidulla suodoksella niin, että pH ennen 15 klooridioksidin ja hapon lisäämistä selluun toista klooridioksidivaihetta varten nousee arvoon > 8, edullisesti pH-arvosta 8 pH-arvoon 14.According to a preferred embodiment of the present invention, the pulp, after the first chlorine dioxide step, is diluted and subjected to a dewatering process comprising washing the pulp to remove acid-rich metals from the pulp, followed by diluting the pulp with alkaline filtrate so that the pH is increased rises to> 8, preferably from pH 8 to pH 14.
Esillä olevan keksinnön edullisen suoritusmuodon mukaisesti hapon ja klooridioksidin lisäys ennen toista klooridioksidivaihetta suoritetaan 15 sekunnista 5 mi- . . nuuttiin, edullisesti 30 sekunnista 2 minuuttiin, alkalin lisäyksen jälkeen.According to a preferred embodiment of the present invention, the addition of acid and chlorine dioxide before the second chlorine dioxide step is carried out for 15 seconds to 5 minutes. . noodles, preferably from 30 seconds to 2 minutes, after the addition of alkali.
• · · ♦ · · • · :1·*: 20 Esillä olevan keksinnön edullisen suoritusmuodon mukaisesti käsittely kompleksia :1♦*: muodostavalla aineella ennen loppuvalkaisua on suoritettu pH-alueella 4,5 - 10, • · edullisesti pH-alueella 4,5 - 7.According to a preferred embodiment of the present invention, the treatment with the complexing agent: 1 ♦ *: prior to final bleaching has been carried out in a pH range of 4.5 to 10, preferably in a pH range of 4, 5-7.
·· » ♦ · ♦ : ·1 Esillä olevan keksinnön edullisen suoritusmuodon mukaisesti sellun konsentrointi ·♦* suoritetaan tässä menetelmässä pesuun ja vedenpoistoon tarkoitetussa laitteessa 25 esimerkiksi käyttämällä pesupuristinta tai puristinta, edullisesti pesupuristinta tai ♦ ♦ φ : vedenpoistopuristinta. Sellun kuljettamiseen (siirtämiseen) reaktorista toiseen käy- :***: tetään edullisesti vielä yhtä pumppua tai vastaavaa laitetta.According to a preferred embodiment of the present invention, the concentration of pulp · ♦ * in this process is carried out in a washing and dewatering apparatus 25, for example by using a washing press or a press, preferably a washing press or a ♦ ♦ veden: dewatering press. Preferably, another pump or similar device is used to convey (transfer) the pulp from one reactor to another.
♦ ♦♦ v : Esillä olevaa keksintöä kuvataan yksityiskohtaisemmin käyttämällä hyväksi kuvioi- ··· ta ja esimerkkiä ja näiden on katsottava ainoastaan kuvaavan eikä millään tavoin ra-30 joittavan keksintöä, sellaisena kuin tämä esitetään oheen liitetyissä patenttivaa- « · timuksissa.♦ ♦♦ v: The present invention will be described in more detail by reference to the drawings and example, and should be considered as merely illustrating and not in any way limiting the invention as set forth in the appended claims.
55
Kuvion selityksetExplanations of the figure
Kuvio 1 esittää periaateluonnosta, jossa tämän keksinnön mukaista menetelmää kuvataan sellaisen järjestelmän muodossa, joka on tarkoitettu klooridioksidia käyttäen suoritettavaan loppuvalkaisuun, jossa mainittua menetelmää voidaan käyttää.Figure 1 illustrates a draft principle illustrating the process of the present invention in the form of a system for final bleaching using chlorine dioxide in which said process can be used.
5 Esimerkki5 Example
Kuten kuviosta 1 voidaan havaita, voidaan esillä olevan keksinnön mukaista loppu-valkaisumenetelmää käyttää menetellen seuraavasti:As can be seen in Figure 1, the final bleaching process of the present invention can be used as follows:
Sellu, joka on valkaistu aikalisissä valkaisuvaiheissa ja jota on käsitelty kompleksia muodostavalla aineella, kuljetetaan ensimmäiseen klooridioksidi (C102) -reaktoriin, 10 minkä jälkeen sellu laimennetaan ja pestään. (Sellun lähtö-pH voi olla 8 - 12). Tämä pesu voidaan suorittaa käyttäen edellä olevassa selityksessä olevan kuvauksen mukaista väkevöintilaitetta käyttäen edullisesti pesupuristinta tai vedenpoistopuris-tinta. Sellun pesun aikana poistetaan sellusta tullut metalleja runsaasti sisältävä liuos. Tässä vaiheessa sellun sakeus on olennaisesti kohtalaisen suuri, edullisesti suuri.The pulp, bleached in the alkaline bleaching steps and treated with the complexing agent, is transported to the first chlorine dioxide (C102) reactor, after which the pulp is diluted and washed. (The pulp may have an initial pH of 8-12). This washing can be carried out using a concentrator as described in the above description, preferably using a washing press or a dewatering press. During pulp washing, the metal-rich solution from the pulp is removed. At this stage, the consistency of the pulp is substantially moderate, preferably high.
15 Tämän jälkeen sellu laimennetaan nopeasti aikaisempaan sakeuteen laimentamalla natriumhydroksidia (NaOH) sisältävällä nesteellä, jolloin saadaan aikaan nopea al-kaliuutto. pH:n säätöön käytettävä happo ja C102 lisätään samalla kun sellu siirretään sellun loppuvalkaisuvaiheeseen sisältyvään toiseen reaktoriin.The pulp is then rapidly diluted to its former consistency by dilution with sodium hydroxide (NaOH) containing liquid to provide rapid alkaline extraction. The pH adjustment acid and C102 are added as the pulp is transferred to a second reactor included in the pulp final bleaching step.
• 9 v.: Keksintö ei luonnollisesti rajoitu esitettyyn suoritusmuotoon, vaan sitä voidaan 20 muunnella keksinnön hengen puitteissa.9 years: The invention is, of course, not limited to the embodiment shown, but may be modified within the spirit of the invention.
·· · • · · • · • · • · ·· · • · · • · • · »»· • · • · »· · • · · • · • · ··· • · • · »·« ·♦· ♦ · · * · · • · ♦ · • · · 1 • · · • · · • · · • ♦····················································· · · · · · · · · · · · · · · · · · · · ♦ · * * * 1 ♦ ♦ ♦ 1 1 1
Claims (6)