ES2380032B1 - BIMETAL SHEET AND PROCEDURE FOR OBTAINING THE SAME - Google Patents
BIMETAL SHEET AND PROCEDURE FOR OBTAINING THE SAME Download PDFInfo
- Publication number
- ES2380032B1 ES2380032B1 ES201030094A ES201030094A ES2380032B1 ES 2380032 B1 ES2380032 B1 ES 2380032B1 ES 201030094 A ES201030094 A ES 201030094A ES 201030094 A ES201030094 A ES 201030094A ES 2380032 B1 ES2380032 B1 ES 2380032B1
- Authority
- ES
- Spain
- Prior art keywords
- sheet
- application
- bimetal
- page
- silver
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Lámina bimetal y procedimiento para la obtención de la misma constituida a partir de la unión sólida y uniforme de dos láminas de metales distintos no ferrosos que conforman sus respectivas caras, y obtenida dicha unión mediante la aplicación de calor y presión aplicado con prensa de acero refractario en un entorno controlado de ausencia de oxígeno. Para la obtención de una lámina bimetal (1) compuesta, por ejemplo por una lámina de oro (2) de 750 m/m y una lámina de plata (3) de 925 m/m, la presión aplicada será de 100kg/cm{sup,2} a una temperatura de 850°C. Preferentemente, cuando las láminas (2 y 3) son respectivamente de oro y plata, tienen una proporción en la que la lámina de oro (2) supone un 12,5% del peso total de la misma y la lámina de plata (3) el resto.Bimetal sheet and procedure for obtaining it constituted from the solid and uniform union of two sheets of different non-ferrous metals that make up their respective faces, and obtained said union by applying heat and pressure applied with refractory steel press in a controlled environment of absence of oxygen. To obtain a bimetal sheet (1) composed, for example, of a gold sheet (2) of 750 m / m and a silver sheet (3) of 925 m / m, the applied pressure will be 100kg / cm {sup , 2} at a temperature of 850 ° C. Preferably, when the sheets (2 and 3) are respectively gold and silver, they have a proportion in which the gold sheet (2) represents 12.5% of the total weight thereof and the silver sheet (3) the rest.
Description
LÁMINA BIMETAL Y PROCEDIMIENTO PARA LA OBTENCIÓN DE LA MISMA BIMETAL SHEET AND PROCEDURE FOR OBTAINING THE SAME
Tal como expresa el enunciado la presente memoria descriptiva se refiere a una invención sobre una lámina bimetal y al procedimiento para la obtención de la misma. As stated in the present statement description refers to an invention about a bimetal sheet and the procedure for obtaining Of the same.
Más en particular, el objeto de la invención se centra en una lámina bimetal, es decir, una lámina metálica compuesta por dos metales distintos no ferrosos, de tal forma que por una de sus caras es de un tipo de metal, por ejemplo oro, y por la opuesta de otro metal distinto, por ejemplo plata, estando ambos metales unidos entre sí mediante un determinado proceso que consigue que dicha unión sea totalmente sólida y uniforme, sin que exista ningún tipo de fisura entre las dos capas de metal que lo conforman, permitiendo ventajosamente su manipulación normal como si se tratase de una lámina convencional hecha de un único metal, es decir, sólo de oro o sólo de plata. More in particular, the object of the invention it focuses on a bimetal sheet, that is, a sheet metallic composed of two different metals not ferrous, so that one of its faces is of a type of metal, for example gold, and the opposite of another different metal, for example silver, both being metals joined together by a certain process which makes this union totally solid and uniform, without any type of fissure between the two layers of metal that make it up, allowing advantageously its normal handling as if it is a conventional sheet made of a single metal, that is, only gold or only silver.
El campo de aplicación de la presente invención se enmarca dentro del sector técnico de la industria del metal, preferentemente centrado en el ámbito de la joyería y orfebrería en el que mayoritariamente se trabajan metales preciosos como el oro y la plata y cuya diferencia de valor permite un The scope of this invention is part of the technical sector of the metal industry, preferably focused on the field of jewelry and goldsmithing in which mostly precious metals such as gold and silver and whose difference in value allows a
importante ahorro. significant savings
En la actualidad, y como referencia al estado de la técnica, por parte del solicitante, se desconoce la existencia de ninguna otra invención que presente unas características técnicas, estructurales y constitutivas semejantes a las que presenta la que aquí se preconiza. At present, and as a reference to the state of the technique, by the applicant, it is unknown the existence of any other invention that presents technical, structural and constitutive similar to those presented here It is recommended.
En este sentido cabe señalar que son ampliamente conocidas, desde antiguo, la utilización y manipulación tanto del oro como de la plata para la realización de múltiples tipos de objetos, especialmente de carácter ornamental, decorativo y, especialmente, joyas y similares. In this sense it should be noted that they are widely known, since ancient times, the use and manipulation of both gold and silver for realization of multiple types of objects, especially ornamental, decorative and, Especially jewelry and the like.
En dicho uso, es igualmente corriente la combinación de ambos metales en una misma pieza, sin embargo, hasta ahora, no se conoce ningún procedimiento que permita su unión de forma sólida para conseguir una lámina que, conjugando las características típicas de cada uno de dichos metales por cada una de sus caras, a la hora de manipularlo, se comporte como una lámina monopieza, siendo este el objetivo de la presente invención. In such use, the combination of both metals in one piece, without However, until now, no procedure is known that allows its union in a solid way to achieve a sheet that, combining the typical characteristics of each of said metals for each of its faces, to when handling it, behave like a sheet monopieza, this being the objective of the present invention.
Así, la lámina bimetal y el procedimiento para la obtención de la misma que la presente invención propone se configura como una destacable novedad dentro de su campo de aplicación, ya que, a tenor de su Thus, the bimetal sheet and the procedure for obtaining the same as the present invention proposed is configured as a remarkable novelty within of its field of application, since, according to its
implementación y de forma taxativa, se alcanzan satisfactoriamente los objetivos anteriormente señalados, estando los detalles caracterizadores que lo hacen posible adecuadamente recogidos en las reivindicaciones finales que acompañan a la presente memoria descriptiva. implementation and in a taxable way, they are achieved satisfactorily the objectives above indicated, being the characterizing details that make it possible properly collected in the Final claims accompanying this descriptive memory.
De manera concreta lo que la invención preconiza es una lámina bimetal constituida a partir de dos láminas independientes de metales distintos no ferrosos, por ejemplo una de oro y otra de plata, las cuales, mediante un proceso de unión que comprende la aplicación de calor y presión mediante una prensa de acero refractario en un entorno controlado de ausencia de oxígeno, que evita cualquier tipo de oxidación y permite una soldadura uniforme y sin ningún tipo de fisura entre ambas láminas, éstas quedan sólidamente unidas entre sí convirtiéndose en las caras superior e inferior de una lámina monopieza bimetal apta para ser manipulada de la misma forma que si fuera sólo de un único metal, es decir sólo de oro o sólo de plata. Specifically what the invention preconiza is a bimetal sheet constituted from two independent sheets of different metals no ferrous, for example one of gold and another of silver, the which, through a union process that includes the application of heat and pressure by means of a press refractory steel in a controlled absence environment of oxygen, which prevents any type of oxidation and allows a uniform welding without any type of fissure between both sheets, these remain solidly joined together becoming the upper faces and bottom of a bimetal single piece sheet suitable for being manipulated in the same way as if it were only in one only metal, that is to say only gold or only silver.
Así, la lámina bimetal obtenida, que presenta por una de sus caras la apariencia brillo color y características particulares y propias del oro y por la opuesta las de la plata, pudiéndose trabajar y manipular de manera convencional como si se tratara de una lámina de oro o de una lámina de plata. Es decir, se puede estirar, estampar, troquelar, laminar acuñar, etc., sin que pierda su apariencia de oro por un lado y de plata por el otro, guardando siempre las mismas proporciones de oro y plata. Thus, the bimetal sheet obtained, which presents on one of its faces the appearance shine color and particular characteristics of gold and the opposite those of silver, being able to work and manipulate in a conventional manner as if it were a gold foil or a silver foil. That is to say, can be stretched, stamped, stamped, laminated, minted, etc., without losing its golden appearance on the one hand and of silver on the other, always keeping the same proportions of gold and silver.
Dicha particularidad permite la ventaja, en cuanto a la utilidad de la lámina bimetal obtenida, de que, por ejemplo en el ámbito de la orfebrería y This particularity allows the advantage, in as to the usefulness of the bimetal sheet obtained, of that, for example in the field of goldsmithing and
joyería en que se suele trabajar con metales preciosos de elevado valor económico, permite realizar piezas con la apariencia de un determinado metal, por ejemplo el oro y con las propiedades de un metal precioso pero mucho más económica, sin que dichas piezas pierdan con el tiempo o el desgaste su apariencia, tal como ocurre con las piezas bañadas o chapadas. jewelry that usually works with precious metals of high economic value, it allows to realize pieces with the appearance of a certain metal, for example the gold and with the properties of a precious metal but much cheaper, without these pieces losing with time or wear your appearance, as it happens with the parts bathed or plated.
Cabe señalar además que, preferentemente, las proporciones en peso de las láminas de metal de que se parte para la obtención de la lámina bimetal preconizada en el caso concreto de estar hecho con oro y plata, son de un 87,5% de plata y un 12,5% de de oro, si bien admite cualquier otra proporción que se desee en función del tipo de metal utilizado y el ahorro o no que se pretenda conseguir. It should also be noted that, preferably, the proportions by weight of the metal sheets of which part for obtaining the bimetal sheet recommended in the specific case of being made with gold and silver, are 87.5% silver and 12.5% gold, although it admits any other proportion that is desired depending on the type of metal used and saving or not That is intended to achieve.
Por otra parte, ahondado en los detalles del descrito procedimiento de obtención de la lámina bimetal preconizada, debe destacarse que, por ejemplo, para una lámina de oro de 750 m/m de aleación (18 kilates) y una lámina de plata de 925 m/m, la presión aplicada será de 100Kg/cm2 a una temperatura de 850ºC. On the other hand, delved into the details of described procedure for obtaining the sheet Bimetal advocated, it should be noted that, for example, for a 750 m / m gold alloy sheet (18 carats) and a silver foil of 925 m / m, the pressure applied will be 100Kg / cm2 at a temperature of 850ºC.
La descrita lámina bimetal y el procedimiento para la obtención de la misma representan, pues, una innovación de características técnicas desconocidas hasta ahora, razones que unidas a su utilidad práctica, la dotan de fundamento suficiente para obtener el privilegio de exclusividad que se solicita. The described bimetal sheet and the procedure to obtain it, therefore, they represent a innovation of unknown technical characteristics So far, reasons that together with its practical utility, they provide it with sufficient foundation to obtain the exclusivity privilege requested.
Para complementar la descripción que se está realizando y con objeto de ayudar a una mejor To complement the description that is being performing and in order to help a better
comprensión de las características de la invención, se acompaña a la presente memoria descriptiva, como parte integrante de la misma, de un juego de planos, en los que con carácter ilustrativo y no limitativo se ha representado lo siguiente: understanding of the features of the invention, it accompanies the present specification, as part member of it, of a set of planes, in the that with an illustrative and non-limiting nature represented the following:
La figura número 1.-Muestra una vista esquematizada de las láminas de metal distinto de que se parte para la obtención de la lámina bimetal objeto de la invención. Figure number 1.-Shows a view schematized from metal sheets other than that it is split to obtain the bimetal sheet object of the invention.
La figura número 2.-Muestra una vista esquematizada de la lámina bimetal obtenida mediante el proceso preconizado. Figure number 2.-Shows a view schematized of the bimetal sheet obtained by recommended process.
A la vista de las mencionadas figuras, y de acuerdo con la numeración adoptada, se puede apreciar como la invención preconiza una lámina bimetal (1) constituida a partir de la unión de dos láminas metálicas independientes de distinto metal no ferroso, una primera lámina (2), por ejemplo de oro, y una segunda lámina (3), por ejemplo de plata, las cuales, preferentemente, especialmente en el caso de tratarse concretamente de oro y plata, se presentan en una proporción tal que la primera lámina (2) de oro supone un 12,5% del peso total de la lámina bimetal (1), mientras que la segunda lámina (3) de plata supone el 87,5% restante, pero si bien ello no supone una limitación, ya que admite cualquier otra proporción. In view of the aforementioned figures, and of according to the numbering adopted, it can be appreciated as the invention advocates a bimetal sheet (1) constituted from the union of two sheets independent metal of different non-ferrous metal, a first sheet (2), for example of gold, and a second sheet (3), for example of silver, which, preferably, especially in the case of treatment specifically of gold and silver, they are presented in a proportion such that the first sheet (2) of gold assumes 12.5% of the total weight of the bimetal sheet (1), while the second sheet (3) of silver represents the 87.5% remaining, but while that does not mean limitation, since it admits any other proportion.
Por su parte, la citada unión entre dichas láminas (2) y (3) se produce a partir de un procedimiento que consiste en la aplicación de calor y For its part, the aforementioned union between said sheets (2) and (3) are produced from a procedure consisting of the application of heat and
presión, aplicado mediante una prensa de acero refractario en un entorno controlado de ausencia de oxígeno, que evita cualquier tipo de oxidación y permite una soldadura uniforme y sin ningún tipo de fisura entre ambas láminas (2 y 3), y a partir del cual éstas quedan sólidamente unidas entre sí convirtiéndose en las caras superior e inferior de la lámina bimetal pressure, applied by a steel press refractory in a controlled environment of absence of oxygen, which prevents any type of oxidation and allows a uniform welding without any type of fissure between both sheets (2 and 3), and from which these are solidly linked together becoming on the upper and lower sides of the bimetal sheet
(1) con la ventaja de que ser manipulada de la misma forma que si fuera solo de oro o solo de plata. (1) with the advantage of being manipulated from it so that if it were only gold or only silver.
Así, en un ejemplo concreto de realización, para una primera lámina (2) de oro de 750 m/m y una segunda lámina (3) de plata de 925 m/m, la presión aplicada será de 100Kg/cm2 a una temperatura de 850ºC. Thus, in a specific embodiment, for a first sheet (2) of 750 m / m gold and a second sheet (3) of 925 m / m silver, the pressure applied will be 100Kg / cm2 at a temperature of 850ºC.
En resumen, pues, la lámina bimetal (1) preconizada está constituida a partir de la unión sólida y uniforme de dos láminas de metales distintos no ferrosos que conforman sus respectivas caras, en la que cuando dichas láminas son una primera lámina (2) de oro (2), y una segunda lámina de plata (3), preferentemente, se presentan en una proporción en la que la lámina de oro (2) supone un 12,5% del peso total de la misma y la lámina de plata (3) el resto, habiendo sido obtenida dicha unión, en cualquier caso, mediante la aplicación de calor y presión aplicado con prensa de acero refractario en un entorno controlado de ausencia de oxígeno. In summary, then, the bimetal sheet (1) advocated is constituted from the union solid and uniform of two different metal sheets non-ferrous that make up their respective faces, in the that when said sheets are a first sheet (2) of gold (2), and a second sheet of silver (3), preferably, they are presented in a proportion in the that the gold foil (2) represents 12.5% of the total weight of it and the silver foil (3) the rest, having this union was obtained, in any case, by the application of heat and pressure applied with press refractory steel in a controlled absence environment of oxygen
Descrita suficientemente la naturaleza de la presente invención, así como la manera de ponerla en práctica, no se considera necesario hacer más extensa su explicación para que cualquier experto en la materia comprenda su alcance y las ventajas que de ella se derivan, haciendo constar que, dentro de su esencialidad, podrá ser llevada a la práctica en otras Describe sufficiently the nature of the present invention, as well as how to put it in practice, it is not considered necessary to make more extensive your explanation so that any subject matter expert understand its scope and the advantages of it derive, stating that, within their essentiality, may be implemented in other
formas de realización que difieran en detalle de la indicada a título de ejemplo, y a las cuales alcanzará igualmente la protección que se recaba siempre que no se altere, cambie o modifique su principio fundamental. embodiments that differ in detail from the indicated by way of example, and which will reach also the protection that is collected whenever alter, change or modify its fundamental principle.
Claims (5)
- Categoría Category
- 56 Documentos citados Reivindicaciones afectadas 56 Documents cited Claims Affected
- A TO
- WO 2008105749 A1 (GUNER KUYUMCULUK KALIP MAKINA ET AL.) 04.09.2008, página 5, 1-4 WO 2008105749 A1 (GUNER KUYUMCULUK KALIP MAKINA ET AL.) 04.09.2008, page 5, 1-4
- línea 12 – página 7, línea 13; figura 1. line 12 - page 7, line 13; Figure 1.
- A TO
- EP 1767116 A1 (SILMAR SPA) 28.03.2007, párrafos [37 - 44]; figura 1. 1-4 EP 1767116 A1 (SILMAR SPA) 28.03.2007, paragraphs [37-44]; Figure 1. 1-4
- A TO
- ES 290539 U (VICENTA ISABEL BRIZ TORRES) 01.04.1986, páginas 3 - 4; reivindicación 1. 1-4 EN 290539 U (VICENTA ISABEL BRIZ TORRES) 01.04.1986, pages 3-4; claim 1. 1-4
- A TO
- US 2003096135 A1 (STERN LEACH COMPANY) 22.05.2003, párrafos [13 - 14], [25 - 40]. 1-4 US 2003096135 A1 (STERN LEACH COMPANY) 22.05.2003, paragraphs [13-14], [25-40]. 1-4
- A TO
- US 1904241 A (ERWIN KAMMERER) 18.04.1933, página 1, línea 65 - página 2, línea 122. 1-4 US 1904241 A (ERWIN KAMMERER) 18.04.1933, page 1, line 65 - page 2, line 122. 1-4
- Categoría de los documentos citados X: de particular relevancia Y: de particular relevancia combinado con otro/s de la misma categoría A: refleja el estado de la técnica O: referido a divulgación no escrita P: publicado entre la fecha de prioridad y la de presentación de la solicitud E: documento anterior, pero publicado después de la fecha de presentación de la solicitud Category of the documents cited X: of particular relevance Y: of particular relevance combined with other / s of the same category A: reflects the state of the art O: refers to unwritten disclosure P: published between the priority date and the date of priority submission of the application E: previous document, but published after the date of submission of the application
- El presente informe ha sido realizado • para todas las reivindicaciones • para las reivindicaciones nº: This report has been prepared • for all claims • for claims no:
- Fecha de realización del informe 23.04.2012 Date of realization of the report 23.04.2012
- Examinador M. García González Página 1/4 Examiner M. García González Page 1/4
- Novedad (Art. 6.1 LP 11/1986) Novelty (Art. 6.1 LP 11/1986)
- Reivindicaciones 1-4 Reivindicaciones SI NO Claims 1-4 Claims IF NOT
- Actividad inventiva (Art. 8.1 LP11/1986) Inventive activity (Art. 8.1 LP11 / 1986)
- Reivindicaciones 1-4 Reivindicaciones SI NO Claims 1-4 Claims IF NOT
- Documento Document
- Número Publicación o Identificación Fecha Publicación Publication or Identification Number publication date
- D01 D01
- WO 2008105749 A1 (GUNER KUYUMCULUK KALIP MAKINA ET AL.) 04.09.2008 WO 2008105749 A1 (GUNER KUYUMCULUK KALIP MAKINA ET AL.) 04.09.2008
- D02 D02
- EP 1767116 A1 (SILMAR SPA) 28.03.2007 EP 1767116 A1 (SILMAR SPA) 03/28/2007