ES2379421A1 - Anti-slip composition for surfaces (Machine-translation by Google Translate, not legally binding) - Google Patents

Anti-slip composition for surfaces (Machine-translation by Google Translate, not legally binding) Download PDF

Info

Publication number
ES2379421A1
ES2379421A1 ES201230372A ES201230372A ES2379421A1 ES 2379421 A1 ES2379421 A1 ES 2379421A1 ES 201230372 A ES201230372 A ES 201230372A ES 201230372 A ES201230372 A ES 201230372A ES 2379421 A1 ES2379421 A1 ES 2379421A1
Authority
ES
Spain
Prior art keywords
column
lines
slip
application
composition
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
ES201230372A
Other languages
Spanish (es)
Other versions
ES2379421B1 (en
Inventor
Alejandro Irazu Barbero
Miren Igone Irazu Barbero
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to ES201230372A priority Critical patent/ES2379421B1/en
Publication of ES2379421A1 publication Critical patent/ES2379421A1/en
Application granted granted Critical
Publication of ES2379421B1 publication Critical patent/ES2379421B1/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention relates to an anti-slip composition, to its preparation process and to its use as an anti-slip agent, particularly on surfaces of bathtubs and shower trays. (Machine-translation by Google Translate, not legally binding)

Description

Composición antideslizante para superficies Non-slip surface composition

OBJETO DE LA INVENCIÓN OBJECT OF THE INVENTION

La presente invención se refiere a una composición antideslizante para superficies, a su proceso de preparación y a su uso como agente antideslizante, particularmente en superficies de bañeras y platos de duchas. The present invention relates to a non-slip surface composition, its preparation process and its use as a non-slip agent, particularly in bath surfaces and shower trays.

ANTECEDENTES DE LA INVENCIÓN BACKGROUND OF THE INVENTION

Las superficies de cerámica, granito, mármol, porcelana y otras pueden ser resbaladizas sobre todo cuando están mojadas. Las caídas en los platos de ducha o bañeras pueden tener consecuencias graves para la persona que la sufre. Especialmente graves cuando estas se producen en personas mayores. Una rotura de cadera supone un cambio drástico en la vida del accidentado y un importante trastorno en la vida de sus familiares cercanos, así como una dependencia de por vida y un costo de difícil cuantificación. Por ello hay un gran interés en mejorar el coeficiente de fricción de estas superficies para evitar estos problemas. Ceramic, granite, marble, porcelain and other surfaces can be slippery especially when they are wet. Falls in shower trays or bathtubs can have serious consequences for the person suffering from it. Especially serious when they occur in older people. A hip fracture involves a drastic change in the life of the injured party and an important disorder in the lives of their close relatives, as well as a lifetime dependency and a difficult quantification cost. Therefore there is a great interest in improving the coefficient of friction of these surfaces to avoid these problems.

Son conocidas diferentes opciones que tienen como fin aumentar el coeficiente de fricción en las superficies, y hacer estas menos deslizantes, como por ejemplo añadir arena u otros materiales abrasivos, o añadir sobre la superficie bandas adhesivas. Different options are known that aim to increase the coefficient of friction on the surfaces, and make these less sliding, such as adding sand or other abrasive materials, or adding adhesive strips on the surface.

En el modelo de utilidad U200201459 se describe una base antideslizante que se imprime sobre la superficie deseada. Esta base antideslizante tiene relieve en una de sus caras. In the utility model U200201459 a non-slip base is described which is printed on the desired surface. This non-slip base is embossed on one of its faces.

Como hemos visto, aunque varias opciones se han desarrollado para evitar las superficies deslizantes, todavía existe una necesidad de encontrar una composición simple y económica que pueda evitar los deslizamientos y la caída en las superficies. As we have seen, although several options have been developed to avoid sliding surfaces, there is still a need to find a simple and economical composition that can prevent landslides and falling on surfaces.

DESCRIPCIÓN DE LA INVENCIÓN DESCRIPTION OF THE INVENTION

Los inventores han encontrado una composición antideslizante para superficies, el proceso de preparación de la misma, así como al uso dado a la composición. Dicha composición se aplica a productos terminados. La composición de la invención, una vez que se aplica a por ejemplo una bañera o un plato de ducha confiere a la superficie, una micro rugosidad que hace que la superficie cubierta sea antideslizante, de manera que se aumenta la seguridad y se disminuye las posibilidades de caída cuando una persona se sitúa sobre la superficie. Además, se ha conseguido que la composición sea transparente y no amarillee con el tiempo. The inventors have found a non-slip surface composition, the process of preparing the same, as well as the use given to the composition. This composition applies to finished products. The composition of the invention, once it is applied to, for example, a bathtub or a shower tray gives the surface, a micro roughness that makes the covered surface non-slip, so that it It increases safety and decreases the chances of falling when a person sits on the surface. In addition, it has been achieved that the composition is transparent and does not yellow over time.

Un primer aspecto de la invención se refiere a una composición antideslizante para superficies que comprende: a) un copolímero acrílico poliuretánico; b) un compuesto de fórmula R1-N=C=O donde R1 es un residuo alifático C1-C10; c) un disolvente orgánico y d) sílice. A first aspect of the invention relates to a non-slip surface composition comprising: a) a polyurethane acrylic copolymer; b) a compound of formula R1-N = C = O where R1 is a C1-C10 aliphatic residue; c) an organic solvent and d) silica

El procedimiento de obtención de la composición es sencillo y se lleva a cabo justo antes de aplicar la composición a la superficie que se quiere recubrir. The procedure for obtaining the composition is simple and is carried out just before applying the surface composition to be coated.

Por lo tanto un segundo aspecto de la invención se refiere a un procedimiento de obtención de la composición de la invención que comprende las etapas de: a) Mezclar un copolímero acrílico poliuretánico con un disolvente orgánico; b) Adicionar a la mezcla de la etapa a) un compuesto de fórmula R1-N=C=O donde R1 es un residuo alifático C1- C10 y sílice; c) Homogeinizar la mezcla de la etapa b). Therefore, a second aspect of the invention relates to a process for obtaining the composition of The invention comprising the steps of: a) Mix a polyurethane acrylic copolymer with an organic solvent; b) Add to the mixture of step a) a compound of formula R1-N = C = O where R1 is a C1- aliphatic residue C10 and silica; c) Homogeinize the mixture from stage b).

La composición se utiliza para recubrir superficies, preferentemente bañeras y platos de ducha, de manera que las superficies una vez recubiertas sean antideslizantes. The composition is used to coat surfaces, preferably bathtubs and shower trays, so that once coated surfaces are non-slip.

Por último un tercer aspecto de la invención se refiere a un uso de la composición según la invención como agente antideslizante. Finally, a third aspect of the invention refers to a use of the composition according to the invention as non-slip agent

DESCRIPCIÓN DETALLADA DE LA INVENCIÓN DETAILED DESCRIPTION OF THE INVENTION

Todos los términos como se utilizan en esta solicitud, al menos que se diga otra cosa, se deberán entender con el significado ordinario del estado de la técnica. All terms as used in this application, unless otherwise stated, shall be understood with the ordinary meaning of the prior art.

2 2

El término “copolímero acrílico poliuretánico” como se utiliza aquí se refiere a un copolímero basado en uretano el cual también incluye ácido acrílico. The term "polyurethane acrylic copolymer" as used herein refers to a urethane-based copolymer which also includes acrylic acid.

El término “residuo alifático C1-C10” se refiere a un compuesto de carbono no aromático cíclico o acíclico de cadena ramificada o lineal. The term "C1-C10 aliphatic residue" refers to a cyclic or acyclic non-aromatic carbon compound of branched or linear chain.

Como ya se ha mencionado arriba, un aspecto de la invención se refiere a una composición antideslizante para superficies que comprende: a) un copolímero acrílico poliuretánico; b) un compuesto de fórmula R1-N=C=O donde R1 es un residuo alifático C1-C10; c) un disolvente orgánico y d) sílice. As already mentioned above, one aspect of the invention relates to a non-slip composition for surfaces comprising: a) a polyurethane acrylic copolymer; b) a compound of formula R1-N = C = O where R1 is a C1-C10 aliphatic residue; c) an organic solvent and d) silica

En una materialización preferente de la invención el ratio volumen/volumen entre el copolímero acrílico poliuretánico y el compuesto de fórmula R1-N=C=O está comprendida entre 2.5:1 y 3: 1. Particularmente el ratio entre el copolímero acrílico poliuretánico y el compuesto de fórmula R1-N=C=O es de 3:1 volumen/volumen. In a preferred embodiment of the invention the volume / volume ratio between the acrylic copolymer polyurethane and the compound of formula R1-N = C = O is between 2.5: 1 and 3: 1. Particularly the ratio between the polyurethane acrylic copolymer and the compound of formula R1-N = C = O is 3: 1 volume / volume.

En otra materialización preferente el volumen del disolvente respecto al volumen del copolímero acrílico poliuretánico está comprendido entre un 5% y un 25%. Particularmente el volumen del disolvente respecto al volumen el copolímero acrílico poliuretánico es el 10%. In another preferred embodiment the volume of the solvent with respect to the volume of the acrylic copolymer Polyurethane is between 5% and 25%. Particularly the volume of the solvent with respect to the Volume the polyurethane acrylic copolymer is 10%.

EJEMPLOS EXAMPLES

Ejemplo 1. Procedimiento de obtención de la composición de la invención. Example 1. Procedure for obtaining the composition of the invention.

Se mezcló 90 ml de un copolímero acrílico poliuretánico comercial AKS58, con 12 ml del disolvente comercial CS/154, después se añadió 30 ml de un isocianato alifático comercial, producto 820/C y por último se añadió 20 g de sílice. Todos los productos de la casa comercial Sestriere. 90 ml of an AKS58 commercial polyurethane acrylic copolymer was mixed with 12 ml of the commercial solvent CS / 154, then 30 ml of a commercial aliphatic isocyanate, product 820 / C was added and finally 20 g of silica was added. All products of the Sestriere commercial house.

La mezcla se realizó en una bandeja y posteriormente se aplicó con un rodillo en una superficie de una bañera con un rodillo de pintor. The mixing was carried out on a tray and subsequently applied with a roller on a surface of a bathtub with a painter roller.

La mezcla se realiza justo antes de la aplicación. No es posible realizarla y envasarla con anterioridad. Mixing is done just before application. It is not possible to carry it out and package it beforehand.

La mezcla se probó en una superficie de loza y en una superficie acrílica. Se añadió, jabones, champú, y acondicionadores, de todas las manera la superficie fue antideslizante, evitando en todo momento la sensación de inseguridad que transmiten las superficies resbaladizas The mixture was tested on a crockery surface and on an acrylic surface. Soaps, shampoo, and conditioners were added, in all ways the surface was non-slip, avoiding at all times the feeling of insecurity transmitted by slippery surfaces

3 3

Claims (9)

REIVINDICACIONES
1.one.
Composición antideslizante para superficies que comprende: a) un copolímero acrílico poliuretánico; b) un compuesto de fórmula R1-N=C=O donde R1 es un residuo alifático C1-C10; c) un disolvente orgánico y d) sílice.  Non-slip surface composition comprising: a) a polyurethane acrylic copolymer; b) a compound of formula R1-N = C = O where R1 is a C1-C10 aliphatic residue; c) an organic solvent and d) silica
2.2.
Composición antideslizante según reivindicación 1 caracterizada porque el ratio volumen/volumen entre el copolímero acrílico poliuretánico y el compuesto de fórmula R1-N=C=O está comprendida entre 2.5:1 y 3: 1.  Non-slip composition according to claim 1 characterized in that the volume / volume ratio between the Polyurethane acrylic copolymer and the compound of formula R1-N = C = O is between 2.5: 1 and 3: 1.
3.3.
Composición antideslizante según reivindicación 2 caracterizada porque el ratio entre el copolímero acrílico poliuretánico y el compuesto de fórmula R1-N=C=O es de 3:1 volumen/volumen.  Non-slip composition according to claim 2 characterized in that the ratio between the acrylic copolymer Polyurethane and the compound of formula R1-N = C = O is 3: 1 volume / volume.
4.Four.
Composición antideslizante según cualquiera de las reivindicaciones 2-3 caracterizada porque el volumen del disolvente respecto al volumen del copolímero acrílico poliuretánico está comprendido entre un 5% y un 25%.  Non-slip composition according to any of claims 2-3 characterized in that the volume of the Solvent with respect to the volume of the polyurethane acrylic copolymer is between 5% and 25%.
5.5.
Composición antideslizante según reivindicación 4 caracterizada porque el volumen del disolvente respecto al volumen el copolímero acrílico poliuretánico es el 10%.  Non-slip composition according to claim 4 characterized in that the volume of the solvent with respect to the Volume the polyurethane acrylic copolymer is 10%.
6.6.
Procedimiento de obtención de la composición según las reivindicaciones 1-5 caracterizado porque comprende las etapas de: a) Mezclar un copolímero acrílico poliuretánico con un disolvente orgánico; b) Adicionar a la mezcla de la etapa a) un compuesto de fórmula R1-N=C=O donde R1 es un residuo alifático C1- C10 y sílice; c) Homogeinizar la mezcla de la etapa b)  Method of obtaining the composition according to claims 1-5 characterized in that it comprises the stages of: a) Mix a polyurethane acrylic copolymer with an organic solvent; b) Add to the mixture of step a) a compound of formula R1-N = C = O where R1 is a C1- aliphatic residue C10 and silica; c) Homogeinize the mixture of stage b)
7. 7.
Uso de la composición según las reivindicaciones 1-5 como agente antideslizante.  Use of the composition according to claims 1-5 as a non-slip agent.
4 4 OFICINA ESPAÑOLA DE PATENTES Y MARCAS SPANISH OFFICE OF THE PATENTS AND BRAND N.º solicitud: 201230372 Application no .: 201230372 ESPAÑA SPAIN Fecha de presentación de la solicitud: 13.03.2012 Date of submission of the application: 13.03.2012 Fecha de prioridad: Priority Date: INFORME SOBRE EL ESTADO DE LA TECNICA REPORT ON THE STATE OF THE TECHNIQUE 51 Int. Cl. : Ver Hoja Adicional 51 Int. Cl.: See Additional Sheet DOCUMENTOS RELEVANTES RELEVANT DOCUMENTS
Categoría Category
56 Documentos citados Reivindicaciones afectadas 56 Documents cited Claims Affected
A TO
US 5433979 A (NORTON COMPANY) 18.07.1995, columna 1, líneas 9-13; columna 2, líneas 66-68; columna 3, líneas 1-2; columna 4, líneas 11-46. 1-7 US 5433979 A (NORTON COMPANY) 18.07.1995, column 1, lines 9-13; column 2, lines 66-68; column 3, lines 1-2; column 4, lines 11-46. 1-7
A TO
US 5401560 A (NORTON COMPANY) 28.03.1995, columna 6, líneas 23-48; columna 8, líneas 48-58. 1-7 US 5401560 A (NORTON COMPANY) 28.03.1995, column 6, lines 23-48; column 8, lines 48-58. 1-7
A TO
US 5783303 A (MINNESOTA MINING AND MANUFACTURING COMPANY) 21.07.1998, columna 1, líneas 9-13; columna 23, ejemplos 31 y 32. 1-7 US 5783303 A (MINNESOTA MINING AND MANUFACTURING COMPANY) 21.07.1998, column 1, lines 9-13; column 23, examples 31 and 32. 1-7
A TO
JP 2005016151 A (OHBAYASHI DORO KK) 20.01.2005, Resumen de la base de datos WPI. Recuperado de EPOQUE. Ver Resumen. 1-7 JP 2005016151 A (OHBAYASHI DORO KK) 20.01.2005, Summary of the WPI database. Recovered from EPOQUE. See Summary. 1-7
A TO
NL 9300665 A (BOOGAARD, W. W. R.) 16.11.1994, Resumen de la base de datos WPI. Recuperado de EPOQUE. Ver Resumen. 1-7 NL 9300665 A (BOOGAARD, W. W. R.) 16.11.1994, Summary of the WPI database. Recovered from EPOQUE. See Summary. 1-7
Categoría de los documentos citados X: de particular relevancia Y: de particular relevancia combinado con otro/s de la misma categoría A: refleja el estado de la técnica O: referido a divulgación no escrita P: publicado entre la fecha de prioridad y la de presentación de la solicitud E: documento anterior, pero publicado después de la fecha de presentación de la solicitud Category of the documents cited X: of particular relevance Y: of particular relevance combined with other / s of the same category A: reflects the state of the art O: refers to unwritten disclosure P: published between the priority date and the date of priority submission of the application E: previous document, but published after the date of submission of the application
El presente informe ha sido realizado • para todas las reivindicaciones • para las reivindicaciones nº: This report has been prepared • for all claims • for claims no:
Fecha de realización del informe 12.04.2012 Date of realization of the report 12.04.2012
Examinador N. Martín Laso Página 1/4 Examiner N. Martín Laso Page 1/4
INFORME DEL ESTADO DE LA TÉCNICA REPORT OF THE STATE OF THE TECHNIQUE Nº de solicitud: 201230372 Application number: 201230372 CLASIFICACIÓN OBJETO DE LA SOLICITUD C09K3/14 (2006.01) CLASSIFICATION OBJECT OF THE APPLICATION C09K3 / 14 (2006.01) C09D175/04 (2006.01) C08K3/36 (2006.01) Documentación mínima buscada (sistema de clasificación seguido de los símbolos de clasificación) C09D175 / 04 (2006.01) C08K3 / 36 (2006.01) Minimum documentation sought (classification system followed by classification symbols) C09K, C09D, C08K C09K, C09D, C08K Bases de datos electrónicas consultadas durante la búsqueda (nombre de la base de datos y, si es posible, términos de búsqueda utilizados) INVENES, EPODOC, WPI, TXT, NPL, XPESP, CAS. Electronic databases consulted during the search (name of the database and, if possible, terms of search used) INVENES, EPODOC, WPI, TXT, NPL, XPESP, CAS. Informe del Estado de la Técnica Página 2/4 State of the Art Report Page 2/4 OPINIÓN ESCRITA  WRITTEN OPINION Nº de solicitud: 201230372 Application number: 201230372 Fecha de Realización de la Opinión Escrita: 12.04.2012 Date of Written Opinion: 12.04.2012 Declaración Statement
Novedad (Art. 6.1 LP 11/1986) Novelty (Art. 6.1 LP 11/1986)
Reivindicaciones Reivindicaciones 1-7 SI NO Claims Claims 1-7 IF NOT
Actividad inventiva (Art. 8.1 LP11/1986) Inventive activity (Art. 8.1 LP11 / 1986)
Reivindicaciones Reivindicaciones 1-7 SI NO Claims Claims 1-7 IF NOT
Se considera que la solicitud cumple con el requisito de aplicación industrial. Este requisito fue evaluado durante la fase de examen formal y técnico de la solicitud (Artículo 31.2 Ley 11/1986). The application is considered to comply with the industrial application requirement. This requirement was evaluated during the formal and technical examination phase of the application (Article 31.2 Law 11/1986). Base de la Opinión.-  Opinion Base.- La presente opinión se ha realizado sobre la base de la solicitud de patente tal y como se publica. This opinion has been made on the basis of the patent application as published. Informe del Estado de la Técnica Página 3/4 State of the Art Report Page 3/4 OPINIÓN ESCRITA  WRITTEN OPINION Nº de solicitud: 201230372 Application Number: 201230372 1. Documentos considerados.-  1. Documents considered.- A continuación se relacionan los documentos pertenecientes al estado de la técnica tomados en consideración para la realización de esta opinión. The documents belonging to the state of the art taken into consideration for the realization of this opinion are listed below.
Documento Document
Número Publicación o Identificación Fecha Publicación Publication or Identification Number publication date
D01 D01
US 5433979 A (NORTON COMPANY) 18.07.1995 US 5433979 A (NORTON COMPANY) 07/18/1995
D02 D02
US 5401560 A (NORTON COMPANY) 28.03.1995 US 5401560 A (NORTON COMPANY) 03/28/1995
D03 D03
US 5783303 A (MINNESOTA MINING AND MANUFACTURING COMPANY) 21.07.1998 US 5783303 A (MINNESOTA MINING AND MANUFACTURING COMPANY) 21.07.1998
D04 D04
JP 2005016151 A (OHBAYASHI DORO KK) 20.01.2005 JP 2005016151 A (OHBAYASHI DORO KK) 01/20/2005
D05 D05
NL 9300665 A (BOOGAARD, W. W. R.) 16.11.1994 NL 9300665 A (BOOGAARD, W. W. R.) 16.11.1994
2. Declaración motivada según los artículos 29.6 y 29.7 del Reglamento de ejecución de la Ley 11/1986, de 20 de marzo, de Patentes sobre la novedad y la actividad inventiva; citas y explicaciones en apoyo de esta declaración  2. Statement motivated according to articles 29.6 and 29.7 of the Regulations for the execution of Law 11/1986, of March 20, on Patents on novelty and inventive activity; quotes and explanations in support of this statement La solicitud se refiere a una composición antideslizante para superficies que comprende un copolímero acrílico poliuretánico, un isocianato con un residuo alifático de 1 a 10 C, sílice y un disolvente orgánico, al procedimiento de preparación de dicha composición y a su uso como agente antideslizante. The application refers to a non-slip surface composition comprising a polyurethane acrylic copolymer, an isocyanate with an aliphatic residue of 1 to 10 C, silica and an organic solvent, to the method of preparing said composition and to its use as a non-slip agent. Los documentos D01-D03 divulgan composiciones antideslizantes para ser aplicados sobre distintas superficies que incorporan entre otros un copolímero acrílico poliuretánico y sílice (ver D01: columna 1, líneas 9-13; columna 2, líneas 6668; columna 3, líneas 1-2; columna 4, líneas 11-46. D02: columna 6, líneas 23-48; columna 8, líneas 48-58. D03: columna 1, líneas 9-13; columna 23, ejemplos 31 y 32). Documents D01-D03 disclose non-slip compositions to be applied on different surfaces that incorporate among others a polyurethane acrylic copolymer and silica (see D01: column 1, lines 9-13; column 2, lines 6668; column 3, lines 1-2; column 4, lines 11-46. D02: column 6, lines 23-48; column 8, lines 48-58. D03: column 1, lines 9-13; column 23, examples 31 and 32). El documento D04 divulga una composición para el recubrimiento de superficies formada por una resina tipo uretano como componente mayoritario, junto a una resina de isocianato como endurecedor y sílice como agregado antideslizante. Dicha composición puede ser aplicada sobre las superficies de carreteras evitando el deslizamiento de vehículos por la lluvia (resumen). Document D04 discloses a surface coating composition formed by a urethane type resin as a major component, together with an isocyanate resin as a hardener and silica as a non-slip aggregate. This composition can be applied on road surfaces avoiding the sliding of vehicles through rain (summary). El documento D05 divulga una composición antideslizante para ser aplicada sobre el suelo de bañeras formada por poliuretano como adhesivo, isocianato como endurecedor y pasta de propiltex como antideslizante, encontrándose dichos componentes en la composición en una proporción de 100:34,2:7 (resumen). Document D05 discloses a non-slip composition to be applied on the bathtub floor formed by polyurethane as adhesive, isocyanate as a hardener and propyltex paste as non-slip, said components being found in the composition in a ratio of 100: 34.2: 7 (summary ). Se considera que ninguno de dichos documentos, tomados solos ni en combinación, divulgan ni dirigen al experto en la materia hacia una composición antideslizante que comprenda de forma conjunta un copolímero acrílico poliuretánico, un isocianato y sílice, lo que le confiere una microrugosidad determinada. It is considered that none of these documents, taken alone or in combination, disclose or direct the person skilled in the art towards a non-slip composition that together comprises a polyurethane acrylic copolymer, an isocyanate and silica, which gives it a certain micro-purity. Por lo tanto, la invención definida en las reivindicaciones 1-7 de la solicitud es nueva y posee actividad inventiva (Art. 6.1 y Therefore, the invention defined in claims 1-7 of the application is new and has inventive activity (Art. 6.1 and 8.1 LP 11/1986). 8.1 LP 11/1986). Informe del Estado de la Técnica Página 4/4 State of the Art Report Page 4/4
ES201230372A 2012-03-13 2012-03-13 Non-slip surface composition Expired - Fee Related ES2379421B1 (en)