ES2276595A1 - Absorbent matrix for disposable absorbent articles, has cationic resin reacting with defibrated cellulose to form polyamides - Google Patents
Absorbent matrix for disposable absorbent articles, has cationic resin reacting with defibrated cellulose to form polyamides Download PDFInfo
- Publication number
- ES2276595A1 ES2276595A1 ES200501465A ES200501465A ES2276595A1 ES 2276595 A1 ES2276595 A1 ES 2276595A1 ES 200501465 A ES200501465 A ES 200501465A ES 200501465 A ES200501465 A ES 200501465A ES 2276595 A1 ES2276595 A1 ES 2276595A1
- Authority
- ES
- Spain
- Prior art keywords
- matrix
- absorbent
- cationic resin
- disposable
- disposable absorbent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Matriz absorbente de integridad mejorada para artículos absorbentes desechables.Enhanced integrity absorbing matrix for disposable absorbent articles.
Los artículos absorbentes desechables, tales como pañales desechables para bebés, pañales desechables para incontinentes, calzones de entrenamiento desechables, toallitas femeninas y panties protectores están constituidos básicamente por una capa superior que permite el paso del fluido, una capa inferior impermeable a los líquidos y una matriz absorbente entre ambas. La matriz absorbente es la encargada de absorber y retener los exudados líquidos o semilíquidos del cuerpo humano que penetran a través de la capa superior del artículo. La matriz además debe ser cómoda y amoldarse al cuerpo del usuario. Otra característica importante de la misma es su integridad o resistencia a la ruptura, ya que una matriz que se hace bolas o se descompone no puede absorber y retener los exudados de la manera adecuada, lo que provoca que se escurra e incomode al usuario.Disposable absorbent articles, such as disposable diapers for babies, disposable diapers for incontinents, disposable training shorts, wipes Feminine and protective panties are basically made up of an upper layer that allows the passage of fluid, a lower layer impervious to liquids and an absorbent matrix between them. The absorbent matrix is responsible for absorbing and retaining liquid or semi-liquid exudates from the human body that penetrate to through the top layer of the article. The matrix must also be comfortable and conform to the user's body. Another feature important of it is its integrity or resistance to rupture, since a matrix that is made balls or decomposes cannot absorb and retain exudates properly, which It causes the user to drain and discomfort.
Con la finalidad de mejorar la resistencia o integridad de la matriz absorbente, la presente invención propone el uso de resinas catiónicas de alta eficiencia dentro de la matriz absorbente de un artículo absorbente desechable, tales resinas, al unirse con la celulosa de la matriz absorbente, forman poliamidas, que son compuestos de cadena larga.In order to improve resistance or integrity of the absorbent matrix, the present invention proposes the use of high efficiency cationic resins within the matrix absorbent of a disposable absorbent article, such resins, at bind with the cellulose of the absorbent matrix, form polyamides, They are long chain compounds.
Existen algunas patentes enfocadas a mejorar la integridad de la matriz en este tipo de artículos. Entre ellas destaca, por ejemplo, la patente US 5,387,208, de Gregory Ashton, donde se describe una matriz absorbente recubierta con una capa de integridad que comprende un tipo de tela no tejida unida a la capa superior; esta capa de integridad puede colocarse también en una parte intermedia de la matriz y/o adyacente a la capa exterior del artículo. Este tipo de capas ayudan en mayor medida a la distribución del líquido y al no retorno del mismo a la superficie del artículo, más que a mejorar la integridad de la matriz, puesto que no fijan ni detienen el movimiento de las fibras dentro de la misma.There are some patents focused on improving the integrity of the matrix in this type of articles. Between them highlights, for example, US Patent 5,387,208, of Gregory Ashton, where an absorbent matrix coated with a layer of integrity comprising a type of nonwoven fabric bonded to the layer higher; this integrity layer can also be placed in a intermediate part of the matrix and / or adjacent to the outer layer of the Article. These types of layers help the distribution of the liquid and its non-return to the surface of the article, rather than improving the integrity of the matrix, since that do not fix or stop the movement of the fibers within the same.
Por otra parte, en la industria es conocida la utilización de adhesivos en artículos absorbentes para mejorar la integridad de la matriz absorbente. Así, por ejemplo, la patente US 4,573,986, de James A. Mineola, presenta un artículo absorbente desechable en el cual la matriz absorbente está unida a la capa superior por medio de un patrón de adhesivo, cuyo fin es incrementar la integridad de ésta; el uso de este tipo de adhesivos no asegura una buena integridad, puesto que tienden a adherirse inadecuadamente a las fibras de celulosa, sobre todo cuando el artículo está siendo usado y se adapta a los movimientos del usuario o cuando la matriz se humedece.On the other hand, in the industry the use of adhesives in absorbent articles to improve the integrity of the absorbent matrix. Thus, for example, the US patent 4,573,986, by James A. Mineola, presents an absorbent article disposable in which the absorbent matrix is attached to the layer upper by means of an adhesive pattern, whose purpose is to increase its integrity; the use of this type of adhesives does not ensure good integrity, since they tend to adhere improperly to cellulose fibers, especially when the item is being used and adapts to the movements of the user or when the matrix becomes wet.
La patente US 5,397,317 de Dennis A. Thomas describe una forma de incrementar la integridad de una matriz absorbente mediante el uso de columnas que salen de la capa inferior y/o de la capa superior y se proyectan entre las fibras de la matriz absorbente; estas columnas actúan restringiendo los movimientos de las fibras de la matriz absorbente, lo que mantiene la integridad de la misma. Este método podría resultar efectivo; sin embargo, este tipo de películas con columnas perpendiculares no existe en el mercado, además de que su implementación ocasionaría muchas dificultades durante el proceso de fabricación.US Patent 5,397,317 by Dennis A. Thomas describes a way to increase the integrity of a matrix absorbent by using columns that leave the layer lower and / or upper layer and project between the fibers of the absorbent matrix; these columns act by restricting movements of the fibers of the absorbent matrix, which keeps The integrity of it. This method could be effective; however, these types of films with perpendicular columns do not it exists in the market, in addition to its implementation would cause Many difficulties during the manufacturing process.
La solicitud de patente MX 2002/0000072, del Grupo P.I. Mabe, describe una matriz absorbente que incorpora dentro de la misma una red de integridad que permite que las fibras celulósicas se enreden en ella formando una unión firme entre las fibras y la red, lo cual impide que la matriz se abra o se rompa con los movimientos del usuario.Patent application MX 2002/0000072, of P.I. Mabe, describes an absorbent matrix that incorporates within it an integrity network that allows the fibers cellulosics get tangled in it forming a firm bond between the fibers and the net, which prevents the matrix from opening or breaking with the user's movements.
Ninguno de los antecedentes mencionados describe o contempla el uso de productos químicos, tales como resinas catiónicas, que unan, mediante reacciones químicas, las fibras de celulosa con la resina, formando poliamidas de cadena larga, que permitan el paso del líquido, ayuden a una mejor distribución de los fluidos y mejoren la integridad de la matriz, tal como se logra con la presente invención.None of the mentioned background describes or contemplates the use of chemicals, such as resins cationic, linking, by chemical reactions, the fibers of cellulose with the resin, forming long chain polyamides, which allow the passage of the liquid, help a better distribution of fluids and improve the integrity of the matrix, as achieved with the present invention.
Por otro lado, en algunos artículos se han utilizado resinas catiónicas con el fin de mejorar su resistencia. Por ejemplo, la patente US 5,574,088, de Yassin Elgarthy, trata sobre una composición para incrementar la resistencia de fibras que comprende un organosiloxano modificado con grupos amino, resina formaldehído-melamina; la composición se emplea para mejorar las propiedades de resistencia en el papel. La patente US 5,869,596, de Sharf U. Ahmed, se refiere a una tela no tejida que contiene una poliamida soluble en agua, lo que mejora su resistencia a la ruptura. Ninguno de estos antecedentes, sin embargo, sugiere ni presenta la posibilidad de usar resinas catiónicas a la manera en que se hace en la presente invención, ni para los fines de la misma.On the other hand, some articles have used cationic resins in order to improve its resistance. For example, US Patent 5,574,088, by Yassin Elgarthy, deals with on a composition to increase the resistance of fibers that comprises an organosiloxane modified with amino groups, resin formaldehyde-melamine; the composition is used to improve the resistance properties in the paper. US patent 5,869,596, of Sharf U. Ahmed, refers to a non-woven fabric that It contains a water soluble polyamide, which improves its breaking strength. None of this background, without However, it suggests or presents the possibility of using resins cationic to the way it is done in the present invention, nor for the purposes of it.
La presente invención busca el promover la resistencia en seco o en húmedo de una matriz absorbente, en un artículo absorbente desechable, logrando un mayor aprovechamiento del material hidrófilo, mediante el uso de resinas catiónicas de alta eficiencia que se combinan con la celulosa de la matriz absorbente.The present invention seeks to promote the dry or wet strength of an absorbent matrix, in a disposable absorbent article, achieving greater use of the hydrophilic material, through the use of cationic resins of high efficiency that combine with cellulose matrix absorbent.
La matriz absorbente de la presente invención puede resultar mas económica que una matriz similar debido a que utilizando la resina catiónica de alta eficiencia es posible emplear menos material hidrófilo (celulosa), mejorando la integridad y manteniendo la capacidad de distribución y retención de líquidos dentro de la matriz. De manera adicional, estos ahorros en celulosa, además de su importancia económica, contribuyen a preservar el medio ambiente, particularmente los bosques.The absorbent matrix of the present invention It may be cheaper than a similar matrix because using high efficiency cationic resin is possible use less hydrophilic material (cellulose), improving integrity and maintaining the capacity of distribution and retention of liquids inside the matrix. Additionally, these savings in cellulose, in addition to their economic importance, they contribute to preserve the environment, particularly forests.
Un objetivo de la presente invención es el uso de resinas catiónicas en combinación con fibras de celulosa en la matriz absorbente de un artículo absorbente desechable, de modo que se incremente la integridad o la resistencia a la ruptura de la misma.An objective of the present invention is the use of cationic resins in combination with cellulose fibers in the absorbent matrix of a disposable absorbent article, so that the integrity or resistance to rupture of the same.
Otro objetivo más de la presente invención es el de disminuir el coste de la matriz absorbente utilizando resinas catiónicas en combinación con las fibras de celulosa en la matriz absorbente, pues así se puede disminuir la cantidad de material absorbente (celulosa) dentro de la matriz sin afectar a la funcionalidad de la misma.Another objective of the present invention is the to reduce the cost of the absorbent matrix using resins cationic in combination with cellulose fibers in the matrix absorbent, as this can reduce the amount of material absorbent (cellulose) within the matrix without affecting the functionality of it.
Otro objetivo de la presente invención consiste en obtener un producto más delgado y cómodo para el usuario, ya que se emplea una cantidad menor de material absorbente (celulosa) dentro de la matriz.Another objective of the present invention is to in obtaining a thinner and more comfortable product for the user, since a smaller amount of absorbent material (cellulose) is used within the matrix.
Figura 1: muestra un corte de la matriz absorbente según la presente invención.Figure 1: shows a section of the matrix absorbent according to the present invention.
Figuras 2 y 3: muestran alternativas de configuración de la matriz absorbente de la presente invención.Figures 2 and 3: show alternatives of configuration of the absorbent matrix of the present invention.
Figura 4: (control) muestra una matriz absorbente del estado de la técnica, sin el uso de resina catiónica y después de aplicada una prueba de integridad.Figure 4: (control) shows a matrix absorbent of the state of the art, without the use of cationic resin and after applying an integrity test.
Figura 5: (prueba) muestra una matriz absorbente de acuerdo con la presente invención, con el uso de la resina catiónica y después de aplicada una prueba de integridad.Figure 5: (test) shows an absorbent matrix in accordance with the present invention, with the use of the resin cationic and after applying an integrity test.
Los productos absorbentes desechables, tales como pañales desechables para bebés, para adultos, pañales y protectores para la incontinencia y los calzones de entrenamiento deben proporcionar una adecuada absorción y contención de orina y de exudados corporales. La matriz absorbente de un artículo absorbente desechable es la parte del mismo encargada de absorber y contener los exudados líquidos y semi-líquidos que llegan a la misma. La matriz también debe tener la capacidad de distribuir el o los líquidos, y por ello es importante evitar roturas o separación de las fibras dentro de la matriz para su correcto funcionamiento.Disposable absorbent products, such as disposable diapers for babies, adults, diapers and incontinence protectors and training shorts they must provide adequate absorption and containment of urine and of body exudates. The absorbent matrix of an article disposable absorbent is the part responsible for absorbing and contain liquid and semi-liquid exudates that They arrive at it. The matrix must also have the ability to distribute the liquid (s), and therefore it is important to avoid breakage or separation of the fibers within the matrix for correct operation
En lo sucesivo se describirá la matriz absorbente de un pañal desechable; sin embargo, la presente invención puede ser aplicada a una matriz absorbente para calzones de entrenamiento, para toallitas femeninas o para cualquier otro artículo destinado a absorber exudados corporales y que se desecha después de su uso.The matrix will be described hereinafter absorbent disposable diaper; however, the present invention can be applied to an absorbent matrix for calzones training, for wipes or for any other article intended to absorb body exudates and that is discarded after use.
La matriz absorbente (44) de acuerdo con la presente invención tiene una cara superior en contacto con el cuerpo (50), que es la que recibe las descargas corporales, y una cara inferior (40) en contacto con la prenda del usuario. Está constituida generalmente por fibras (22) de un material absorbente, tal como celulosa, y por partículas de material super-absorbente (24), tal como se puede apreciar en la Figura 1, la cual muestra un corte transversal de la matriz absorbente (44) de la presente invención.The absorbent matrix (44) according to the The present invention has an upper face in contact with the body (50), which is the one that receives body discharges, and a lower face (40) in contact with the user's garment. This consisting generally of fibers (22) of an absorbent material, such as cellulose, and by particles of material super absorbent (24), as can be seen in Figure 1, which shows a cross section of the matrix absorbent (44) of the present invention.
Las resinas catiónicas tienen la propiedad de reaccionar con la celulosa formando poliamidas. Para los fines de la presente invención, a la matriz absorbente (44) se le añade una dilución de una resina catiónica en agua, en una concentración tal que la cantidad de resina catiónica adicionada a la matriz sea como máximo de aproximadamente un 1,5% en peso, cantidad autorizada por la FDA (Administración de Alimentos y Fármacos de los Estados Unidos).Cationic resins have the property of react with cellulose forming polyamides. For the purposes of the present invention, an absorbent matrix (44) is added a dilution of a cationic resin in water, in such a concentration that the amount of cationic resin added to the matrix be as maximum of approximately 1.5% by weight, amount authorized by the FDA (State Food and Drug Administration United).
Una resina catiónica está formada por un diácido orgánico, una diamida y un catalizador de cloro; al utilizarse en la producción de una matriz absorbente según lo mostrado en la presente invención, la resina catiónica reacciona con la celulosa formando poliamidas. En las zonas de la matriz donde ocurre la reacción se forma una especie de red que permite el paso del líquido, que favorece una mayor distribución del fluido y que evita las rupturas.A cationic resin is formed by a diacid organic, a diamide and a chlorine catalyst; when used in the production of an absorbent matrix as shown in the present invention, the cationic resin reacts with cellulose forming polyamides. In the areas of the matrix where the reaction forms a kind of network that allows the passage of liquid, which favors a greater distribution of the fluid and prevents the breaks
La reacción de las resinas catiónicas con la celulosa de la matriz absorbente sigue el esquema de reacción siguiente:The reaction of cationic resins with the Cellulose of the absorbent matrix follows the reaction scheme next:
donde R se selecciona de entre el grupo consistente en grupos carboxilo de 5 a 15 átomos de carbono y grupos hidroxilo de 2 a 15 átomos de carbono.where R is selected from the group consisting of carboxyl groups of 5 to 15 carbon atoms and hydroxyl groups of 2 to 15 atoms of carbon.
La molécula de la celulosa tiene una estructura del tipo:The cellulose molecule has a structure of the kind:
\vskip1.000000\baselineskip\ vskip1.000000 \ baselineskip
En general y en los procesos convencionales para la fabricación de una matriz absorbente, la celulosa (22) se desfibra en un molino para después mezclarse con el material super-absorbente (24) y formar la matriz (44). La resina catiónica disuelta en agua se aplica sobre la matriz absorbente (44) de forma que penetre parcialmente la matriz, formando los enlaces entre ésta y la celulosa por la cara superior (50) de la misma, tal y como se muestra en la Figura 2. La resina se aplica, preferentemente, mediante pulverización, aunque puede utilizarse cualquier otro medio adecuado, conocido por los técnicos en la materia.In general and in conventional processes for the manufacture of an absorbent matrix, cellulose (22) is defibrate in a mill and then mix with the material super absorbent (24) and form the matrix (44). The cationic resin dissolved in water is applied on the matrix absorbent (44) so that it partially penetrates the matrix, forming the links between it and cellulose on the upper face (50) thereof, as shown in Figure 2. The resin it is preferably applied by spraying, although it can use any other suitable means known to technicians in the matter.
La resina catiónica puede ser añadida también durante la formación de la matriz (44), de modo que los enlaces entre la celulosa y la resina se formen a todo lo largo y ancho de la matriz (44), tal como se muestra en la Figura 3. La resina puede añadirse igualmente por la cara inferior (40) de la matriz (44), de modo que se formen los enlaces y las cadenas entrecruzadas o reticuladas por esta zona de la misma, o por ambas caras superior (50) e inferior (40), tal y como se muestra en la Figura 5.The cationic resin can also be added. during matrix formation (44), so that the links between the cellulose and the resin are formed throughout the length and width of the matrix (44), as shown in Figure 3. The resin can also be added on the underside (40) of the die (44), of so that links and cross-linked chains are formed or reticulated by this zone of the same, or by both sides superior (50) and lower (40), as shown in Figure 5.
En caso de que la resina catiónica se aplique por las caras superior (50) y/o inferior (40) de la matriz, tal aplicación puede abarcar desde aproximadamente un 50 a un 100% de la superficie superior o inferior de la misma, y puede aplicarse formando líneas, en zig-zag, o con cualquier patrón deseado.In case the cationic resin is applied on the upper (50) and / or lower (40) faces of the matrix, such application can cover from about 50 to 100% of the upper or lower surface thereof, and can be applied forming lines, zigzag, or with any pattern wanted.
La matriz absorbente (44) de la presente invención puede ser recta, tal y como se muestra en la Figura 1, o puede tener cualquier otra forma que se desee, y puede contener otros elementos, tales como una o más capas de transferencia.The absorbent matrix (44) of the present invention may be straight, as shown in Figure 1, or It can have any other shape you want, and it can contain other elements, such as one or more transfer layers.
A manera de ejemplo, se aplicaron por pulverización 0,8 g de una dilución al 1% de resina catiónica en agua, tal resina catiónica contenía 1,3-dicloro-2-propanol, ácido adípico, dietilentriamina, polímero de epiclorhidrina y sulfato clorhídrico sobre la cara superior (50) de una matriz absorbente de un pañal desechable. La parte central de la matriz absorbente fue sometida a una prueba de resistencia longitudinal, obteniéndose un incremento de alrededor del 100% en la resistencia longitudinal de la matriz que contiene la resina catiónica en comparación con una matriz de las mismas características y sin resina catiónica.As an example, they were applied by spraying 0.8 g of a 1% dilution of cationic resin in water, such cationic resin contained 1,3-dichloro-2-propanol, adipic acid, diethylenetriamine, epichlorohydrin polymer and hydrochloric sulfate on the upper face (50) of a matrix absorbent disposable diaper. The central part of the matrix absorbent was subjected to a longitudinal resistance test, obtaining an increase of about 100% in resistance longitudinal of the matrix containing the cationic resin in comparison with a matrix of the same characteristics and without cationic resin
Comparativo de resistencia del núcleo en secoComparison of resistance of core in dry
\vskip1.000000\baselineskip\ vskip1.000000 \ baselineskip
Por otro lado, el pañal de prueba con la matriz que contiene la resina catiónica y un pañal control sin resina en la matriz se sometieron a una prueba de integridad; los resultados se muestran en las Figuras 4 y 5, en las cuales se puede apreciar claramente el efecto positivo del uso de la resina catiónica sobre la integridad de la matriz absorbente.On the other hand, the test diaper with the matrix which contains the cationic resin and a control diaper without resin in the matrix underwent an integrity test; the results They are shown in Figures 4 and 5, in which you can see clearly the positive effect of the use of cationic resin on the integrity of the absorbent matrix.
En la prueba de integridad utilizada al pañal desechable se adicionaron aproximadamente 250 ml de orina sintética y se colocaron por separado en bolsas de polietileno selladas, las cuales tenían pequeñas perforaciones por toda su superficie, las bolsas con los pañales en su interior se colocaron dentro de una mezcladora, consistente en un recipiente que gira en el sentido de las manecillas del reloj, durante aproximadamente dos minutos; posteriormente, se cambió el sentido de rotación, girando en sentido contrario al de las manecillas del reloj durante aproximadamente dos minutos y así sucesivamente. Además, dentro del recipiente se introdujeron dos pelotas de tenis. Se puso en funcionamiento la mezcladora y se la dejó trabajando durante cinco minutos aproximadamente, se sacaron los pañales de las bolsas y se miraron a través de una pantalla luminosa de forma que se puedo identificar perfectamente si había o no rupturas o fracturas en la matriz absorbente.In the integrity test used to the diaper disposable approximately 250 ml of synthetic urine were added and placed separately in sealed polyethylene bags, the which had small perforations all over their surface, the diaper bags inside were placed inside a mixer, consisting of a container that rotates in the direction of the hands of the clock, for approximately two minutes; subsequently, the direction of rotation was changed, turning in counterclockwise during approximately two minutes and so on. In addition, within bowl two tennis balls were introduced. Got in operation of the mixer and let it work for five minutes, diapers were removed from the bags and they looked through a luminous screen so that I can perfectly identify whether or not there were ruptures or fractures in the absorbent matrix
Por otra parte, se realizaron pruebas de uso a los pañales tratados con la resina catiónica, obteniéndose como resultado que alrededor del 70% de las madres de los usuarios hicieron observaciones sobre la mejor integridad de los mismos.On the other hand, use tests were performed on diapers treated with cationic resin, obtained as result that about 70% of the mothers of the users They commented on their best integrity.
- Objetivo: Objective:
- evaluar la funcionalidad de la aplicación de poliamidas en el pañal buscando una mejor integridad.evaluate the application functionality of diaper polyamides looking for better integrity.
Metodología: Se contactó con 68 consumidores de pañales económicos T4, a quienes se les dejó la primera muestra para que la utilizaran durante dos días; en la segunda visita se preguntó sobre la funcionalidad de la primera muestra y se entregó la segunda, durante la tercera visita se preguntó nuevamente sobre el funcionamiento de la segunda y se entregó una tercera muestra, de la cual se pregunto sobre su funcionalidad en la cuarta visita y se preguntó sobre la preferencia. Las muestras fueron identificadas como:Methodology: 68 was contacted consumers of economic diapers T4, who were left the first sample to be used for two days; in the second visit was asked about the functionality of the first Sample and the second one was delivered, during the third visit asked again about how the second one works and delivered a third sample, of which he wondered about his functionality on the fourth visit and wondered about the preference. The samples were identified how:
- Muestra A: Sample A:
- Classic T4 con un 1% de resina catiónica, 4 g de celulosa + 1 g de SAP (polímero super-absorbente)Classic T4 with 1% cationic resin, 4 g of cellulose + 1 g SAP (polymer super absorbent)
- Muestra B: Sample B:
- Classic T4 controlClassic T4 control
- Muestra C:Sample C:
- Classic T4 con un 2% de resinas catiónicasClassic T4 with 2% resins cationic
\newpage\ newpage
Comentarios de los usuarios de la muestra:Comments from sample users:
Cabe mencionar que se aplicó la misma resina catiónica diluida al 2% sobre la cara superior (50) de un pañal desechable disminuyendo al mismo tiempo la cantidad de material absorbente (celulosa) en 1 g. Los resultados de la prueba de integridad mostraron una mayor integridad en el pañal con la resina que en un pañal control; y en las pruebas de uso no se apreciaron diferencias en cuanto a funcionalidad (absorción, retención y distribución) entre la muestra que contenía la resina y menor cantidad de celulosa y el control. Por otra parte, alrededor del 65% de las mamás notaron una mayor integridad en el pañal con la resina.It is worth mentioning that the same resin was applied 2% diluted cationic on the upper face (50) of a diaper disposable while reducing the amount of material absorbent (cellulose) in 1 g. The test results of integrity showed greater integrity in the diaper with the resin that in a diaper control; and in the tests of use they were not appreciated differences in functionality (absorption, retention and distribution) between the sample containing the resin and lower amount of cellulose and control. Moreover, around the 65% of moms noticed greater diaper integrity with the resin.
De lo anterior se puede concluir que es factible disminuir la cantidad de material absorbente dentro de una matriz absorbente que contiene resinas catiónicas, sin afectar la funcionalidad en cuanto a la absorción, retención y distribución de fluidos dentro de la misma, de tal forma que logran ahorros significativos, sin afectar a la funcionalidad y mejorando la integridad de la matriz.From the above it can be concluded that it is feasible decrease the amount of absorbent material within a matrix absorbent containing cationic resins, without affecting the functionality regarding the absorption, retention and distribution of fluids within it, so that they achieve savings significant, without affecting functionality and improving the matrix integrity.
Por último, las pruebas de laboratorio en cuanto a la capacidad de absorción, retorno de líquidos a la superficie del pañal, tiempos de absorción y distribución confirmaron los resultados obtenidos en las pruebas de uso.Finally, laboratory tests in terms of to absorption capacity, return of liquids to the surface diaper, absorption and distribution times confirmed the Results obtained in the use tests.
Si bien la invención ha sido descrita en función de sus modalidades preferentes, los alcances de la misma comprenden cualquier tipo de cambio o modificación a la misma que pueda ser evidente para un técnico en la materia.While the invention has been described in function of its preferred modalities, its scope includes any type of change or modification to it that may be Obvious to a technician in the field.
Claims (11)