EA038572B1 - Hard surface treatment composition - Google Patents
Hard surface treatment composition Download PDFInfo
- Publication number
- EA038572B1 EA038572B1 EA201990569A EA201990569A EA038572B1 EA 038572 B1 EA038572 B1 EA 038572B1 EA 201990569 A EA201990569 A EA 201990569A EA 201990569 A EA201990569 A EA 201990569A EA 038572 B1 EA038572 B1 EA 038572B1
- Authority
- EA
- Eurasian Patent Office
- Prior art keywords
- composition
- amphoteric
- monomer
- acrylic copolymer
- modified polysaccharide
- Prior art date
Abstract
Description
Область техники, к которой относится изобретениеThe technical field to which the invention relates
Настоящее изобретение относится к композиции для обработки твердых поверхностей. В частности, композиция содержит амфотерный акриловый сополимер и амфотерный модифицированный полисахарид. Как было неожиданно обнаружено, такая композиция оказалась способна обеспечивать получение хороших эксплуатационных характеристик в отношении быстрого высыхания без заметных остатков/пятен на твердой поверхности.The present invention relates to a composition for treating hard surfaces. In particular, the composition contains an amphoteric acrylic copolymer and an amphoteric modified polysaccharide. It was surprisingly found that such a composition was able to provide good fast drying performance without noticeable residues / stains on a hard surface.
Предпосылки создания изобретенияBackground of the invention
Композиции для обработки твердых поверхностей широко используются на протяжении продолжительного времени для сохранения чистоты и блеска предметов хозяйственного обихода. Композиции для обработки твердых поверхностей обычно содержат разнообразные ингредиенты, которые могут обеспечить пользователя композиции оптимальным практическим впечатлением от очистки. Например, в композиции для обработки твердых поверхностей можно добавлять быстровысыхающие полимеры для обеспечения устойчивости к жесткой воде, легкости очистки после первого использования при повторных случаях применения и тому подобного.Compositions for treating hard surfaces have been widely used for a long time to keep household items clean and shiny. Hard surface treatment compositions typically contain a variety of ingredients that can provide the wearer of the composition with an optimal practical cleaning experience. For example, fast drying polymers can be added to hard surface treatment compositions to provide hard water resistance, ease of cleaning after first use on repeated applications, and the like.
Однако может иметь место некоторая сложность при включении в композицию для обработки твердых поверхностей определенного быстровысыхающего полимера, такого как амфотерный акриловый сополимер. На подвергнутой такой обработке твердой поверхности могут возникать нежелательные остатки/пятна, возможно являющиеся результатом добавления быстровысыхающего полимера.However, there may be some difficulty in including a particular fast drying polymer, such as an amphoteric acrylic copolymer, in a hard surface treatment composition. Unwanted residues / stains may occur on a hard surface treated in this way, possibly resulting from the addition of a fast drying polymer.
Поэтому авторы сделали вывод, что существует потребность в способе включения быстровысыхающего полимера в композицию для обработки твердых поверхностей без образования остатков/пятен на подвергаемой обработке твердой поверхности. Как было неожиданно обнаружено, в результате включения амфотерного акрилового сополимера и амфотерного модифицированного полисахарида при массовом соотношении в диапазоне от 0,75:1 до 3:1 композиция для обработки твердых поверхностей способна обеспечить получение хороших эксплуатационных характеристик в отношении быстрого высыхания без образования остатка/пятна на подвергнутой обработке твердой поверхности.Therefore, the authors concluded that there is a need for a method of incorporating a fast drying polymer into a hard surface treatment composition without leaving residues / stains on the hard surface to be treated. Surprisingly, as a result of the inclusion of the amphoteric acrylic copolymer and the amphoteric modified polysaccharide in a weight ratio in the range of 0.75: 1 to 3: 1, the hard surface treatment composition is able to provide good fast drying performance without residue / stain on a treated hard surface.
Сущность изобретенияThe essence of the invention
В первом варианте осуществления настоящее изобретение направлено на композицию для обработки твердых поверхностей, содержащуюIn a first embodiment, the present invention is directed to a composition for treating hard surfaces comprising
а) от 0,0001 до 3% амфотерного акрилового сополимера в расчете на массу композиции;a) from 0.0001 to 3% of an amphoteric acrylic copolymer based on the weight of the composition;
b) от 0,0001 до 3% амфотерного модифицированного полисахарида в расчете на массу композиции; где (i) массовое соотношение между амфотерным акриловым сополимером и амфотерным модифицированным полисахаридом находится в диапазоне от 0,75:1 до 3:1;b) from 0.0001 to 3% of the amphoteric modified polysaccharide based on the weight of the composition; where (i) the mass ratio between the amphoteric acrylic copolymer and the amphoteric modified polysaccharide is in the range from 0.75: 1 to 3: 1;
(ii) амфотерный акриловый сополимер отличается от амфотерного модифицированного полисахарида;(ii) the amphoteric acrylic copolymer is different from the amphoteric modified polysaccharide;
(iii) амфотерный акриловый сополимер включает в качестве заполимеризованных мономеров, по меньшей мере, мономер (а) и мономер (b), где мономер (а) описывается формулой(iii) the amphoteric acrylic copolymer comprises, as polymerized monomers, at least monomer (a) and monomer (b), wherein monomer (a) is represented by the formula
CH2=CR1-CO-NH-R2-N+R3R4R5X- (1), гдеCH 2 = CR 1 -CO-NH-R 2 -N + R 3 R 4 R 5 X- (1), where
R1 представляет собой метальный радикал или этильный радикал,R 1 represents a methyl radical or an ethyl radical,
R2 представляет собой линейный C2-C6 алкиленовый радикал,R 2 is a linear C2-C6 alkylene radical,
R3, R4 и R5 независимо представляют собой атом водорода, C1-C6 алкильный радикал иR 3 , R 4 and R 5 independently represent a hydrogen atom, a C1-C 6 alkyl radical and
X- представляет собой анион, выбранный из группы галогенов, сульфатов, алкилсульфатов, гидроксида, фосфата, ацетата или формиата;X - represents an anion selected from the group of halogens, sulfates, alkyl sulfates, hydroxide, phosphate, acetate or formate;
мономер (b) представляет собой этиленненасыщенные кислоты и/или их соли; и (iv) амфотерный модифицированный полисахарид содержит элементарные звенья мономера (а).monomer (b) is ethylenically unsaturated acids and / or their salts; and (iv) the amphoteric modified polysaccharide contains monomer units (a).
Во втором варианте осуществления настоящее изобретение направлено на способ обеспечения блеска, быстрого высыхания, легкой повторной очистки или долговременного очищения поверхности или комбинации этих эффектов, включающий стадию введения твердой поверхности в контакт с композицией по настоящему изобретению.In a second embodiment, the present invention is directed to a method of providing shine, fast drying, easy re-cleaning or long-term cleaning of a surface, or a combination of these effects, comprising the step of contacting a hard surface with a composition of the present invention.
В третьем варианте осуществления настоящее изобретение направлено на применение композиции по настоящему изобретению для получения блеска, быстрого высыхания, легкой повторной очистки, или долговременного очищения поверхности, или комбинации этих эффектов.In a third embodiment, the present invention is directed to the use of a composition of the present invention for shine, fast drying, easy re-cleaning, or long-term surface cleaning, or a combination of these effects.
Все другие варианты осуществления настоящего изобретения станут более понятны после ознакомления с подробным описанием изобретения и приведенными далее примерами.All other embodiments of the present invention will become better understood after reading the detailed description of the invention and the following examples.
Подробное описание изобретенияDetailed description of the invention
За исключением примеров или случаев, когда недвусмысленно указано иное, все числа в данном описании изобретения, указывающие на количества материалов или условия проведения реакции, физические свойства материалов и/или применение, необязательно могут пониматься как модифицированные словом приблизительно.Except for examples or cases where otherwise expressly indicated, all numbers in this description of the invention indicating quantities of materials or reaction conditions, physical properties of materials and / or use, may not necessarily be understood as modified by the word about.
Все количества приведены в расчете на массу композиции, если не указано иное.All amounts are based on the weight of the composition, unless otherwise indicated.
- 1 038572- 1 038572
Следует понимать, что при указании любого диапазона значений любое конкретное верхнее значение может быть скомбинировано с любым конкретным нижним значением.It should be understood that when specifying any range of values, any particular high value may be combined with any specific low value.
Во избежание каких бы то ни было сомнений, слово содержащий предназначено для обозначения понятия включающий, но необязательно состоящий из или составленный из. Иными словами, перечисленные стадии или опции необязательно являются исчерпывающими.For the avoidance of any doubt, the word containing is intended to denote a concept including, but not necessarily consisting of, or composed of. In other words, the steps or options listed are not necessarily exhaustive.
Раскрытие изобретения, которое приведено в настоящем документе, следует рассматривать как охватывающее все варианты осуществления, приведенные в пунктах формулы изобретения, как множественным образом зависящие друг от друга, независимо от того, что пункты формулы изобретения могут быть изложены без множественной зависимости или избыточности.The disclosure of the invention, which is given in this document, should be considered as covering all the options for implementation recited in the claims, as plurally dependent on each other, regardless of the fact that the claims may be stated without multiple dependence or redundancy.
Термин твердая поверхность в настоящем изобретении в общем случае относится к любой поверхности в домашнем хозяйстве, включая окна, кухню, ванную комнату, туалет, мебель или пол. Данные поверхности, например, могут быть изготовлены из стекла, глазурованной керамики, металла, камня, пластиков, лака, древесины или их комбинаций.The term hard surface in the present invention generally refers to any surface in a household, including windows, kitchens, bathrooms, toilets, furniture, or floors. These surfaces, for example, can be made of glass, glazed ceramics, metal, stone, plastics, lacquer, wood, or combinations thereof.
Термин сополимер в соответствии с использованием в настоящем документе относится к полимеру, включающему по меньшей мере две различающиеся мономерные композиции.The term copolymer, as used herein, refers to a polymer comprising at least two distinct monomeric compositions.
Термин амфотерный в соответствии с использованием в настоящем документе относится к полимерам, которые содержат как кислотные, так и основные группы и демонстрируют кислотное или основное поведение в зависимости от условий.The term amphoteric, as used herein, refers to polymers that contain both acidic and basic groups and exhibit acidic or basic behavior depending on conditions.
Значения pH в настоящем документе относятся к соответствующим значениям, измеренным при температуре 25°С.The pH values in this document refer to the corresponding values measured at 25 ° C.
Предпочтительно амфотерный акриловый сополимер, подходящий для использования в настоящем изобретении, включает в качестве заполимеризованных мономеров, по меньшей мере, мономер (а) и мономер (b), где мономер (а) описывается формулойPreferably, an amphoteric acrylic copolymer suitable for use in the present invention comprises, as polymerized monomers, at least monomer (a) and monomer (b), wherein monomer (a) is represented by the formula
CH2=CR1-CO-NH-R2-N+R3R4R5X- (1), гдеCH 2 = CR 1 -CO-NH-R 2 -N + R 3 R 4 R 5 X- (1), where
R1 представляет собой атом водорода или С1-С2 алкильный радикал,R 1 represents a hydrogen atom or a C 1 -C 2 alkyl radical,
R2 представляет собой линейный или разветвленный C2-C6 алкиленовый радикал,R 2 represents a linear or branched C 2 -C 6 alkylene radical,
R3, R4 и R5 независимо представляют собой атом водорода, C1-C6 алкильный радикал иR 3 , R 4 and R 5 independently represent a hydrogen atom, a C1-C6 alkyl radical and
X- представляет собой анион, выбираемый из группы галогенов, сульфатов, алкилсульфатов, гидроксида, фосфата, ацетата или формиата; и мономер (b) представляет собой этиленненасыщенные кислоты и/или их соли.X - is an anion selected from the group of halogens, sulfates, alkyl sulfates, hydroxide, phosphate, acetate or formate; and monomer (b) is ethylenically unsaturated acids and / or their salts.
Предпочтительно мономер (а) описывается формулой (1), в которой R1 представляет собой метальный радикал или этильный радикал, R2 представляет собой С2-С6 алкиленовый радикал, R3, R4 и R5 независимо представляют собой атом водорода, Ci-C6 алкильный радикал, а X- представляет собой анион, выбираемый из группы галогенов, сульфатов, алкилсульфатов, гидроксида, фосфата, ацетата или формиата. Более предпочтительно мономер (а) описывается формулой (1), в которой R1 представляет собой метальный радикал, R2 представляет собой группу -CH2-CH2-CH2-, каждый из R3, R4 и R5 представляет собой метальный радикал, а Х- представляет собой анион, выбираемый из группы галогенов, сульфатов, алкилсульфатов, гидроксида, фосфата, ацетата или формиата. Наиболее предпочтительно мономер (а) представляет собой хлорид 3-триметиламмонийпропилметакриламида (сокращенное обозначаемый как МАРТАС).Preferably, monomer (a) is described by formula (1), in which R 1 is a methyl radical or an ethyl radical, R 2 is a C2-C6 alkylene radical, R 3 , R 4 and R 5 are independently a hydrogen atom, Ci-C6 an alkyl radical, and X - is an anion selected from the group of halogens, sulfates, alkyl sulfates, hydroxide, phosphate, acetate or formate. More preferably, monomer (a) is represented by formula (1) in which R 1 is a methyl radical, R 2 is a —CH2 — CH2 — CH2— group, R 3 , R 4 and R 5 are each a methyl radical, and X - is an anion selected from the group of halogens, sulfates, alkyl sulfates, hydroxide, phosphate, acetate or formate. Most preferably, monomer (a) is 3-trimethylammonium propyl methacrylamide chloride (abbreviated as MAPTAC).
Мономер (b) предпочтительно представляет собой С3-С8 этиленненасыщенные кислоты и/или их соли. Более предпочтительно мономер (b) выбирают из акриловой кислоты, метакриловой кислоты или их соли. Еще более предпочтительно мономер (b) выбирают из акриловой кислоты, солей щелочных металлов или аммония и акриловой кислоты.Monomer (b) is preferably C 3 -C 8 ethylenically unsaturated acids and / or their salts. More preferably, monomer (b) is selected from acrylic acid, methacrylic acid, or a salt thereof. Even more preferably monomer (b) is selected from acrylic acid, alkali metal or ammonium salts and acrylic acid.
Молярное соотношение между мономером (а) и мономером (b) предпочтительно находится в диапазоне от 1:10 до 10:1, более предпочтительно от 1:6 до 4:1, а еще более предпочтительно от 1:3 до 2:1.The molar ratio between monomer (a) and monomer (b) is preferably in the range from 1:10 to 10: 1, more preferably from 1: 6 to 4: 1, and even more preferably from 1: 3 to 2: 1.
Еще более предпочтительно амфотерный акриловый сополимер включает в качестве сополимеризованных мономеров, по меньшей мере, мономер (а) и мономер (b), где мономер (а) представляет собой хлорид 3-триметиламмонийпропилметакриламида, а мономер (b) представляет собой акриловую кислоту или соли щелочных металлов для акриловой кислоты.Even more preferably, the amphoteric acrylic copolymer comprises, as copolymerized monomers, at least monomer (a) and monomer (b), where monomer (a) is 3-trimethylammonium propylmethacrylamide chloride and monomer (b) is acrylic acid or alkali salts metals for acrylic acid.
Предпочтительно амфотерный акриловый сополимер включает в качестве заполимеризованных мономеров мономеры аддитивной полимеризации в виде этилакрилата, 2-акриламидо-2метилпропансульфоновой кислоты и/или N-изопропиламида.Preferably, the amphoteric acrylic copolymer comprises, as polymerized monomers, addition polymerization monomers in the form of ethyl acrylate, 2-acrylamido-2methylpropanesulfonic acid and / or N-isopropylamide.
В особенности предпочтительным амфотерным акриловым сополимером являются сополимер хлорида акриламидопропилтриметиламмония/акрилата натрия/этилакрилата, сополимер хлорида акриламидопропилтриметиламмония/акрилата натрия/N-изопропиламида/2-акриламидо-2-метилпропансульфоновой кислоты или их смесь.A particularly preferred amphoteric acrylic copolymer is acrylamidopropyltrimethylammonium chloride / sodium acrylate / ethyl acrylate copolymer, acrylamidopropyltrimethylammonium chloride / sodium acrylate / N-isopropylamide / 2-acrylamido-2-methylpropane sulfonic acid copolymer, or a mixture thereof.
Например, сополимер хлорида акриламидопропилтриметиламмония/акрилата натрия/этилакрилата, подходящий для использования в настоящем изобретении, доступен на коммерческих условиях в компа- 2 038572 нии BASF под наименованием Polyquart® Ampho 149, сополимер хлорида акриламидопропилтриметиламмония/акрилата натрия/N-изопропиламида/2-акриламидо-2-метилпропансульфоновой кислоты доступен на коммерческих условиях в компании BASF под наименованием Polyquart® Pro A.For example, a copolymer of acrylamidopropyltrimethylammonium chloride / sodium acrylate / ethyl acrylate suitable for use in the present invention is commercially available from BASF under the name Polyquart® Ampho 149, a copolymer of acrylamidopropyltrimethylammonium chloride / acrylate sodium / acrylate / sodium acrylate / acrylate / sodium acrylate / acrylate copolymer. -2-methylpropane sulfonic acid is commercially available from BASF under the name Polyquart® Pro A.
Амфотерный акриловый сополимер предпочтительно характеризуется среднемассовой молекулярной массой (Mw) согласно измерению с использованием водной гельпроникающей хроматографии (ГПХ) с детектированием светорассеяния (SEC-MALLS) в диапазоне от 10000 до 500000 Да, более предпочтительно от 50000 до 350000 Да, а еще более предпочтительно от 100000 до 200000 Да.The amphoteric acrylic copolymer preferably has a weight average molecular weight (M w ) as measured by water gel permeation chromatography (GPC) with light scattering (SEC-MALLS) in the range of 10,000 to 500,000 Da, more preferably 50,000 to 350,000 Da, and even more preferably from 100,000 to 200,000 Yes.
Предпочтительно амфотерный акриловый сополимер присутствует в количестве в диапазоне от 0,0001 до 3%, более предпочтительно от 0,001 до 1%, еще более предпочтительно от 0,008 до 0,1%, а наиболее предпочтительно от 0,01 до 0,05% в расчете на массу композиции.Preferably, the amphoteric acrylic copolymer is present in an amount ranging from 0.0001 to 3%, more preferably from 0.001 to 1%, even more preferably from 0.008 to 0.1%, and most preferably from 0.01 to 0.05%, based on on the weight of the composition.
Амфотерный модифицированный полисахарид, подходящий для использования в настоящем изобретении, предпочтительно представляет собой амфотерный модифицированный крахмал, более предпочтительно амфотерный модифицированный маисовый (кукурузный) крахмал. Предпочтительно амфотерный модифицированный полисахарид содержит элементарные звенья вышеупомянутого мономера (а). Более предпочтительно амфотерный модифицированный полисахарид содержит элементарные звенья вышеупомянутых мономеров (а) и (b). Еще более предпочтительно амфотерный модифицированный полисахарид содержит элементарные звенья, по меньшей мере, мономера (а) и мономера (b), где мономер (а) представляет собой хлорид 3-триметиламмонийпропилметакриламида, а мономер (b) представляет собой акриловую кислоту или соли щелочных металлов и акриловой кислоты. Еще более предпочтительно амфотерный модифицированный полисахарид модифицируют с использованием хлорида 3триметиламмонийпропилметакриламида и акрилата натрия.Amphoteric modified polysaccharide suitable for use in the present invention is preferably an amphoteric modified starch, more preferably amphoteric modified maize starch. Preferably, the amphoteric modified polysaccharide contains the elementary units of the aforementioned monomer (a). More preferably, the amphoteric modified polysaccharide contains the building blocks of the aforementioned monomers (a) and (b). Even more preferably, the amphoteric modified polysaccharide contains at least monomer (a) and monomer (b) units, wherein monomer (a) is 3-trimethylammonium propylmethacrylamide chloride and monomer (b) is acrylic acid or alkali metal salts, and acrylic acid. Even more preferably, the amphoteric modified polysaccharide is modified using 3trimethylammoniumpropylmethacrylamide chloride and sodium acrylate.
Наиболее предпочтительно амфотерный модифицированный полисахарид имеет наименование по номенклатуре МНКИ (INCI) поликватерниум-95. Поликватерниум-95 доступен на коммерческих условиях в компании BASF под наименованием Polyquart® Ecoclean.Most preferably, the amphoteric modified polysaccharide has the INCI name Polyquaternium-95. Polyquaternium-95 is commercially available from BASF under the name Polyquart® Ecoclean.
Предпочтительно амфотерный модифицированный полисахарид присутствует в количестве в диапазоне от 0,0001 до 3%, более предпочтительно от 0,001 до 1%, еще более предпочтительно от 0,008 до 0,1%, а наиболее предпочтительно от 0,01 до 0,05% в расчете на массу композиции.Preferably, the amphoteric modified polysaccharide is present in an amount ranging from 0.0001 to 3%, more preferably from 0.001 to 1%, even more preferably from 0.008 to 0.1%, and most preferably from 0.01 to 0.05%, based on on the weight of the composition.
Предпочтительно массовое соотношение между амфотерным акриловым сополимером и амфотерным модифицированным полисахаридом находится в диапазоне от 0,85:1 до 2:1, а наиболее предпочтительно от 0,9:1 до 1,3:1.Preferably, the weight ratio between the amphoteric acrylic copolymer and the amphoteric modified polysaccharide ranges from 0.85: 1 to 2: 1, and most preferably from 0.9: 1 to 1.3: 1.
Предпочтительно композиция дополнительно содержит неионное поверхностно-активное вещество. Неионное поверхностно-активное вещество предпочтительно содержит соединения, полученные в результате конденсации простых алкиленоксидов с алифатическим или алкилароматическим гидрофобным соединением, предпочтительно с алифатическим или алкилароматическим спиртом; алкилполиглюкозидами; или их смесью. Более предпочтительно неионное поверхностно-активное вещество содержит этоксилированные алкиловые спирты, алкилполиглюкозиды или их смесь. Еще более предпочтительно неионные поверхностно-активные вещества представляют собой этоксилированные алкиловые спирты, алкилполиглюкозиды или их смесь. Еще более предпочтительно неионные поверхностно-активные вещества представляют собой этоксилированные C8-C16 алкиловые спирты, С5-С20 алкилполиглюкозиды или их смесь.Preferably, the composition further comprises a nonionic surfactant. The nonionic surfactant preferably contains compounds resulting from the condensation of simple alkylene oxides with an aliphatic or alkyl aromatic hydrophobic compound, preferably an aliphatic or alkyl aromatic alcohol; alkyl polyglucosides; or a mixture of them. More preferably, the nonionic surfactant contains ethoxylated alkyl alcohols, alkyl polyglucosides, or mixtures thereof. Even more preferably, nonionic surfactants are ethoxylated alkyl alcohols, alkyl polyglucosides, or mixtures thereof. Even more preferably, the nonionic surfactants are ethoxylated C 8 -C 16 alkyl alcohols, C 5 -C 20 alkyl polyglucosides, or mixtures thereof.
Этоксилированные алкиловые спирты предпочтительно являются этоксилированными C8-Ci2 алкиловыми спиртами, при этом еще более предпочтительно средняя степень этоксилирования находится в диапазоне от 5 до 8. Одним примером особенно эффективных (и поэтому предпочтительных) поверхностно-активных веществ являются этоксилированные С9-Сп алкиловые спирты, характеризующиеся средней степенью этоксилирования 8, в том числе, например, доступное на коммерческих условиях поверхностно-активное вещество Neodol 91-8.The ethoxylated alkyl alcohols are preferably ethoxylated C 8 -Ci 2 alkyl alcohols, with an even more preferred average degree of ethoxylation ranging from 5 to 8. One example of particularly effective (and therefore preferred) surfactants are ethoxylated C 9 -Ci alkyl alcohols. alcohols having an average degree of ethoxylation of 8, including, for example, the commercially available surfactant Neodol 91-8.
Предпочтительные алкилполиглюкозиды описываются формулой RO-(G)n, где R представляет собой разветвленно- или прямоцепочечную алкильную группу, которая может быть насыщенной или ненасыщенной, G представляет собой сахаридную группу, и степень полимеризации n может иметь значение в диапазоне от 1 до 10. Предпочтительно R характеризуется средней длиной алкильной цепочки в диапазоне от C5 до С20, G выбирают из С5 или С6 моносахаридных остатков и n имеет значение в диапазоне от 1 до 6; более предпочтительно R характеризуется средней длиной алкильной цепочки в диапазоне от С6 до C16, G представляет собой глюкозу, а n имеет значение в диапазоне от 1 до 2. Подходящие для использования алкилполиглюкозиды включают соответствующие соединения из линейки Glucopon®, например продукты Glucopon®425 N/HH и Glucopon®215 UP от компании BASF.Preferred alkyl polyglucosides are described by the formula RO- (G) n , where R is a branched or straight chain alkyl group which may be saturated or unsaturated, G is a saccharide group, and the degree of polymerisation n may be in the range from 1 to 10. Preferably R is characterized by an average alkyl chain length in the range from C5 to C20, G is selected from C5 or C6 monosaccharide residues and n has a value in the range from 1 to 6; more preferably R has an average alkyl chain length in the range of C 6 to C 16 , G is glucose and n is in the range of 1 to 2. Suitable alkyl polyglucosides include the corresponding compounds from the Glucopon® line, for example the products Glucopon®425 N / HH and Glucopon®215 UP from BASF.
Предпочтительно композиция содержит этоксилированные алкиловые спирты, алкилполиглюкозиды или их смесь. Более предпочтительно композиция содержит этоксилированные C8-C16 алкиловые спирты, С5-С20 алкилполиглюкозиды или их смесь.Preferably, the composition contains ethoxylated alkyl alcohols, alkyl polyglucosides, or a mixture thereof. More preferably, the composition comprises ethoxylated C 8 -C 16 alkyl alcohols, C 5 -C 20 alkyl polyglucosides, or a mixture thereof.
Предпочтительно количество неионного поверхностно-активного вещества находится в диапазоне от 0,01 до 20%, более предпочтительно от 0,1 до 15%, еще более предпочтительно от 0,3 до 7%, а наиболее предпочтительно от 1 до 5% в расчете на массу композиции, в случае присутствия такового.Preferably, the amount of nonionic surfactant is in the range from 0.01 to 20%, more preferably from 0.1 to 15%, even more preferably from 0.3 to 7%, and most preferably from 1 to 5%, based on weight of the composition, if present.
- 3 038572- 3 038572
Для установления pH композиция предпочтительно содержит органическую кислоту, характеризующуюся среднечисленной молекулярной массой, составляющей не более чем 400, более предпочтительно композиция содержит органическую кислоту, характеризующуюся среднечисленной молекулярной массой, составляющей не более чем 200, еще более предпочтительно композиция содержит лимонную кислоту, молочную кислоту, малеиновую кислоту, яблочную кислоту, гликолевую кислоту или их смесь, и еще более предпочтительно композиция содержит лимонную кислоту, молочную кислоту или их смесь. В случае присутствия органической кислоты ее количество предпочтительно будет находиться в диапазоне от 0,1 до 15%, более предпочтительно от 1 до 5% в расчете на массу композиции.To adjust the pH, the composition preferably contains an organic acid having a number average molecular weight of not more than 400, more preferably the composition contains an organic acid having a number average molecular weight of not more than 200, even more preferably the composition contains citric acid, lactic acid, maleic acid, malic acid, glycolic acid, or a mixture thereof, and even more preferably the composition comprises citric acid, lactic acid, or a mixture thereof. If an organic acid is present, the amount will preferably be in the range from 0.1 to 15%, more preferably from 1 to 5%, based on the weight of the composition.
Композиция для обработки твердых поверхностей по настоящему изобретению предпочтительно содержит по меньшей мере 30% воды в расчете на массу композиции. Более предпочтительно композиция содержит по меньшей мере 50%, еще более предпочтительно от 70 до 99%, еще более предпочтительно от 77 до 97%, а наиболее предпочтительно от 84 до 93% воды в расчете на массу композиции.The composition for treating hard surfaces of the present invention preferably contains at least 30% water based on the weight of the composition. More preferably, the composition contains at least 50%, even more preferably 70 to 99%, even more preferably 77 to 97%, and most preferably 84 to 93% water, based on the weight of the composition.
Композиция предпочтительно содержит органические растворители, выбранные из С1-8 спирта, простого эфира, содержащего от 2 до 16 атомов углерода, сложного эфира C2-24 органической кислоты, С6-18 циклического терпена и их смеси. Более предпочтительно композиция содержит этанол, изопропиловый спирт, н-бутанол, изобутанол, н-бутоксипропанол, дипропиленгликоль, диэтиленгликольмонобутиловый простой эфир, дипропиленгликольмонобутиловый простой эфир, пропиленгликольмонометиловый простой эфир, пропиленгликольмонопропиловый простой эфир, метиловый сложный эфир каприловой кислоты, метиловый сложный эфир гептиловой кислоты, диметил-2-метилглутарат, сложные эфиры полиглицерина, метиловый сложный эфир соевого масла, лимонен или их смесь. Еще более предпочтительно композиция содержит этанол, изопропиловый спирт, дипропиленгликоль, диэтиленгликольмонобутиловый простой эфир, дипропиленгликольмонобутиловый простой эфир, пропиленгликольмонометиловый простой эфир, пропиленгликольмонопропиловый простой эфир, метиловый сложный эфир каприловой кислоты, метиловый сложный эфир гептиловой кислоты, диметил-2-метилглутарат, сложные эфиры полиглицерина, метиловый сложный эфир соевого масла, лимонен или их смесь. Наиболее предпочтительно композиция содержит изопропиловый спирт, дипропиленгликольмонобутиловый простой эфир, пропиленгликольмонометиловый простой эфир, пропиленгликольмонопропиловый простой эфир или их смесь. Органический растворитель в композиции может присутствовать при концентрации в диапазоне от 0 до 20%, предпочтительно 0,5-15% в расчете на массу композиции.The composition preferably comprises organic solvents selected from C1-8 alcohol, an ether containing 2 to 16 carbon atoms, ester of C 2 - 24, organic acid C 6-18 cyclic terpene and mixtures thereof. More preferably, the composition contains ethanol, isopropyl alcohol, n-butanol, isobutanol, n-butoxypropanol, dipropylene glycol, diethylene glycol monobutyl ether, dipropylene glycol monobutyl ether, propylene glycol monomethyl ester, propylene glycol mono ether -2-methylglutarate, polyglycerol esters, soybean oil methyl ester, limonene, or a mixture thereof. Even more preferably, the composition comprises ethanol, isopropyl alcohol, dipropylene glycol, diethylene glycol monobutyl ether, dipropylene glycol monobutyl ether, propylene glycol monomethyl ether, propylene glycol monopropyl ether, caprylic acid methyl ester, methyl dimethyl ether methyl ester soybean oil methyl ester, limonene, or a mixture thereof. Most preferably, the composition comprises isopropyl alcohol, dipropylene glycol monobutyl ether, propylene glycol monomethyl ether, propylene glycol monopropyl ether, or a mixture thereof. The organic solvent in the composition may be present at a concentration ranging from 0 to 20%, preferably 0.5-15%, based on the weight of the composition.
Композиция может содержать от 0,2 до 1,2% загустителя в расчете на массу композиции. Это обеспечивает получение оптимальных реологических свойств композиции. Подходящие для использования загустители включают модифицированные целлюлозы, например гидроксиэтилцеллюлозу.The composition may contain from 0.2 to 1.2% of a thickening agent based on the weight of the composition. This ensures that optimal rheological properties of the composition are obtained. Suitable thickeners include modified celluloses such as hydroxyethyl cellulose.
Композиция для обработки твердых поверхностей по изобретению может, кроме того, содержать красители, душистое вещество и/или консерванты. В случае присутствия таких веществ их количество может находиться в диапазоне от 0,001 до 5% в расчете на массу композиции.The composition for treating hard surfaces according to the invention may further contain colorants, fragrances and / or preservatives. If such substances are present, their amount can range from 0.001 to 5% based on the weight of the composition.
Композиция предпочтительно характеризуется значением pH в диапазоне от 1 до 4,5, более предпочтительно от 1,5 до 4, еще более предпочтительно от 2,0 до 3,0.The composition preferably has a pH in the range from 1 to 4.5, more preferably from 1.5 to 4, even more preferably from 2.0 to 3.0.
Для достижения внешнего вида, благоприятного для потребителей, композиция предпочтительно характеризуется светопропусканием, составляющим по меньшей мере 20%, более предпочтительно по меньшей мере 40%, еще более предпочтительно по меньшей мере 60% и еще более предпочтительно находящимся в диапазоне от 70 до 95%. Значения светопропускания, приведенные в настоящем документе, представляют собой процентную величину, характеризующую пропускание света в ближней инфракрасной области, характеризующегося длиной волны 880 нм, через образец композиции толщиной 2,5 см при 25°С. Испытание на светопропускание композиции может быть проведено с использованием устройства Turbiscan Lab Expert (от компании Formulation, France).To achieve a consumer-friendly appearance, the composition preferably has a light transmission of at least 20%, more preferably at least 40%, even more preferably at least 60%, and even more preferably in the range of 70 to 95%. The light transmittances reported herein are percentages of the transmittance of near infrared light, characterized by a wavelength of 880 nm, through a 2.5 cm thick sample of the composition at 25 ° C. The light transmission test of the composition can be performed using a Turbiscan Lab Expert device (from Formulation, France).
Композиция может быть упакована в любой форме, но предпочтительно ее упаковывают в виде обычного продукта для обработки или очистки твердых поверхностей. Предпочтительная упаковка представляет собой устройство для распылительного нанесения. Также возможны дозаторы насосного типа (либо распыляющие, либо нераспыляющие насосы) и устройства для нанесения обливанием (бутылки и тому подобное). Также возможно пропитывание композицией салфетки. Предпочтительно композиция представляет собой средство для очистки туалета или ванной комнаты.The composition can be packaged in any form, but is preferably packaged as a conventional product for treating or cleaning hard surfaces. The preferred packaging is a spray applicator. Pump-type dispensers (either spray or non-spray pumps) and pour applicators (bottles and the like) are also possible. It is also possible to impregnate the wipes with the composition. Preferably, the composition is a toilet or bathroom cleaner.
Настоящее изобретение также предлагает способ обеспечения блеска, быстрого высыхания, легкой повторной очистки, или долговременного очищения поверхности, или комбинации этих эффектов, включающий стадию введения твердой поверхности в контакт с композицией по настоящему изобретению; и применение композиции по настоящему изобретению для обеспечения блеска, быстрого высыхания, легкой повторной очистки, или долговременного очищения поверхности, или комбинации этих эффектов.The present invention also provides a method of providing shine, fast drying, easy re-cleaning, or long-term surface cleaning, or a combination of these effects, comprising the step of contacting a hard surface with a composition of the present invention; and using the composition of the present invention to provide shine, fast drying, easy re-cleaning, or long-term surface cleaning, or a combination of these effects.
Далее изобретение будет описано со ссылкой на следующие далее неограничивающие примеры.The invention will now be described with reference to the following non-limiting examples.
- 4 038572- 4 038572
Таблица 1Table 1
ПримерыExamples of
Пример 1.Example 1.
Данный пример демонстрирует получение составов.This example demonstrates the preparation of formulations.
а: этоксилат С9-С11 спирта (8ЕО) b: C8-C16 алкилполиглюкозид с: сополимер хлорида акриламидопропилтриметиламмония/акрилата натрия/Nизопропиламида/2-акриламидо-2-метилпропансульфоновой кислоты d: поликватерниум-95: сополимер маисового (кукурузного) крахмала, мономерных акриловой кислоты и хлорида акриламидопропилтриметиламмонияa: C 9 -C 11 alcohol ethoxylate (8EO) b: C 8 -C 16 alkylpolyglucoside c: copolymer of acrylamidopropyltrimethylammonium chloride / sodium acrylate / Nisopropylamide / 2-acrylamido-2-methylpropanesulfonic acid d: polyquaternium-95: copolymer-95 starch, monomeric acrylic acid and acrylamidopropyltrimethylammonium chloride
В соответствии с табл. 1 получали серию образцов.In accordance with the table. 1 received a series of samples.
Пример 2.Example 2.
В данном примере продемонстрированы эксплуатационные характеристики по быстрому высыханию и уменьшению остатков.This example demonstrates fast drying performance and reduced residue.
Плитки из черной глазурованной керамики (15 смх15 см) предварительно промывали и высушивали, после этого располагали на решетке с рисунком 3х3. 4 г образца размещали на решетке с плитками по кругу по часовой стрелке. Незамедлительно использовали влажную ткань (с массой, в 4 раза превышающей массу первоначальной сухой ткани) для протирки решетки с плитками по зигзагообразной траектории в одном цикле ополаскивания. После этого цикл ополаскивания повторяли два раза с заменой увлажненной ткани в каждом цикле ополаскивания. Центральную плитку вынимали для дополнительной оценки эксплуатационных характеристик в том, что касается остатков и быстрого высыхания.Tiles made of black glazed ceramics (15 cm x 15 cm) were pre-washed and dried, after which they were placed on a grid with a 3x3 pattern. 4 g of the sample was placed on a grid with tiles in a clockwise circle. Immediately, a damp cloth (4 times the weight of the original dry cloth) was used to wipe the grid of tiles in a zigzag pattern in one rinse cycle. Thereafter, the rinsing cycle was repeated twice, replacing the wetted cloth in each rinsing cycle. The center tile was removed to further evaluate the performance in terms of residue and fast drying.
Остаток тщательно изучали под источником точечной подсветки и/или невооруженным глазом человека. Также оценивали эксплуатационные характеристики по быстрому высыханию. Плитки располагали под углом наклона 60°, а после этого омывали струей водопроводной воды при расходе, составляющем приблизительно 60 л/ч, на протяжении 10 с. Эксплуатационные характеристики по быстрому высыханию и уменьшению остатков для каждого из образцов обобщенно представили в табл. 2.The residue was carefully examined under a spot light source and / or with the naked eye of a person. Fast drying performance was also evaluated. The tiles were positioned at an angle of 60 °, and then washed with a stream of tap water at a flow rate of approximately 60 l / h for 10 seconds. Performance characteristics for fast drying and reduction of residues for each of the samples are summarized in table. 2.
Таблица 2table 2
- 5 038572- 5 038572
Табл. 2 демонстрирует результаты по быстрому высыханию и остатку для исследованных образцов. Как было неожиданно обнаружено, композиции по настоящему изобретению оказались способны обеспечить хорошее быстрое высыхание без образования явно выраженных остатков/пятен на твердой поверхности. Также было неожиданно обнаружено, что плитка, подвергнутая обработке с использованием образца 2, не имела видимых разводов даже под точечным источником подсветки. В противоположность этому на плитке, подвергнутой обработке с использованием образца 1, под источником точечной подсветки могло быть обнаружено несколько крапинок.Tab. 2 shows the fast drying and residue results for the samples tested. It was surprisingly found that the compositions of the present invention were able to provide good fast drying without the formation of pronounced residues / stains on the hard surface. It was also surprisingly found that tiles treated with Sample 2 had no visible streaks even under the spotlight. In contrast, on a tile treated with Sample 1, several specks could be found under the spotlight.
Claims (12)